JP5485729B2 - 導電性パターン作製方法 - Google Patents
導電性パターン作製方法 Download PDFInfo
- Publication number
- JP5485729B2 JP5485729B2 JP2010017718A JP2010017718A JP5485729B2 JP 5485729 B2 JP5485729 B2 JP 5485729B2 JP 2010017718 A JP2010017718 A JP 2010017718A JP 2010017718 A JP2010017718 A JP 2010017718A JP 5485729 B2 JP5485729 B2 JP 5485729B2
- Authority
- JP
- Japan
- Prior art keywords
- silver
- mass
- concentration
- water
- polymer latex
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
1.水性媒体中に、平均粒径が0.1μm以下の銀超微粒子、ポリマーラテックス、および水溶性ハロゲン化物を含有する銀超微粒子含有組成物を基材表面に塗布・乾燥させることによりパターンを作製し、該パターンに紫外線の照射および/または水分の再付与を行うことにより導電性を発現させることを特徴とする導電性パターン作製方法。
2.前記銀超微粒子含有組成物が、ポリマーラテックスおよび水溶性ハロゲン化物を、下記の式を満足する範囲で含有することを特徴とする上記1記載の導電性パターン作製方法。
2.93<A/B<168
A:銀超微粒子含有組成物中のポリマーラテックス固形分濃度(単位:質量%)
B:水溶性ハロゲン化物質量モル濃度(単位:mol/kg)
2.93<A/B<168
A:銀超微粒子含有組成物中のポリマーラテックス固形分濃度(単位:質量%)
B:水溶性ハロゲン化物質量モル濃度(単位:mol/kg)
ここで水溶性ハロゲン化物質量モル濃度とは、水溶性ハロゲン化物の物質量を、銀超微粒子含有組成物の全質量から銀、ポリマーラテックス固形分、水溶性ハロゲン化物等の溶質の質量を差し引いた値で除した値を意味する。
2Lのステンレスビーカーに平均分子量が約30000の焙焼デキストリン(日澱化学(株)製、デキストリンNo.1−A)を54.4gと純水860gを加え、約30分間撹拌した。その後、硝酸銀131.8gを加え、更に約30分間撹拌し、完全に溶解した。この液に水酸化カリウム60.9gを純水83.9gに溶解した液を添加し、撹拌回転数400rpmの状態で60分間還元反応を実施した。還元反応が終了した銀超微粒子分散液を続いて、酢酸にてpH=5.6に調整した後、ビオザイムF10SD(天野エンザイム(株)製)を200mg添加し45℃で1時間撹拌し、残留しているデキストリンを低分子化し、7質量%の銀超微粒子分散液を得た。次に、得られた銀超微粒子分散液の精製工程として、遠心分離を実施することで、銀超微粒子と上澄み液を綺麗に分離させ、上澄み液を廃棄した。残った銀超微粒子を再分散させ、繰り返し遠心分離を実施し、上澄み液を廃棄した。その後、純水を加えて再分散し、銀超微粒子の平均粒径が0.03μm、銀濃度が47.2質量%の銀超微粒子分散液1を110g得た。
銀超微粒子含有組成物1〜4を、コート紙(三菱製紙(株)製、坪量157.0g/m2)上にワイヤーバーを用いて、銀の塗布量が1m2あたり2.0gとなるよう塗布・乾燥し、その後紫外線(253.7nm、365.0nmの輝線を有する)を1.1J/m2照射し、続いて50℃80%RH(重量絶対湿度H=0.067kg/kgD.A.)の高湿条件下にて5分間放置し、導電性パターン20〜23を得た。
上記導電性パターン1〜19、20〜23それぞれについて、(株)ダイアインスツルメンツ製ロレスターGPを用いて電気抵抗値を測定した。各パターンのA/B値および試験結果を表1および表2に示す。A、Bはそれぞれ該銀超微粒子含有組成物中のポリマーラテックス固形分濃度(単位:質量%)、水溶性ハロゲン化物質量モル濃度(単位:mol/kg)である。
Claims (2)
- 水性媒体中に、平均粒径が0.1μm以下の銀超微粒子、ポリマーラテックス、および水溶性ハロゲン化物を含有する銀超微粒子含有組成物を基材表面に塗布・乾燥させることによりパターンを作製し、該パターンに紫外線の照射および/または水分の再付与を行うことにより導電性を発現させることを特徴とする導電性パターン作製方法。
- 前記銀超微粒子含有組成物が、ポリマーラテックスおよび水溶性ハロゲン化物を、下記の式を満足する範囲で含有することを特徴とする請求項1記載の導電性パターン作製方法。
2.93<A/B<168
A:銀超微粒子含有組成物中のポリマーラテックス固形分濃度(単位:質量%)
B:水溶性ハロゲン化物質量モル濃度(単位:mol/kg)