JP5458478B2 - High refractive index and high strength resin composition - Google Patents
High refractive index and high strength resin composition Download PDFInfo
- Publication number
- JP5458478B2 JP5458478B2 JP2007201769A JP2007201769A JP5458478B2 JP 5458478 B2 JP5458478 B2 JP 5458478B2 JP 2007201769 A JP2007201769 A JP 2007201769A JP 2007201769 A JP2007201769 A JP 2007201769A JP 5458478 B2 JP5458478 B2 JP 5458478B2
- Authority
- JP
- Japan
- Prior art keywords
- resin composition
- compound
- optical material
- optical
- material according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は光学材料用樹脂組成物に関し、更には、それを用いたプラスチックレンズ、プリズム、光ファイバー、情報記録基盤、フィルター等の光学材料に関する。中でも本発明はプラスチックレンズとして好適に使用される。 The present invention relates to a resin composition for an optical material, and further relates to an optical material such as a plastic lens, a prism, an optical fiber, an information recording substrate, and a filter using the resin composition. Among these, the present invention is suitably used as a plastic lens.
プラスチック材料は軽量かつ靭性に富み、また染色が容易であることから、各種光学材料、特に眼鏡レンズに近年多用されている。光学材料、中でも眼鏡レンズに特に要求される性能は、物理的性質としては、低比重、高透明性及び低黄色度、高耐熱性、高強度等であり、光学性能としては高屈折率と高アッベ数である。高屈折率はレンズの薄肉化を可能とし、高アッベ数はレンズの色収差を低減するが、屈折率が上昇するほどアッベ数は低くなるため、両者を同時に向上させる検討が実施されている。これらの検討の中で最も代表的な方法は、特許文献1に示されるエピスルフィド化合物を使用する方法である。 In recent years, plastic materials have been widely used in various optical materials, particularly eyeglass lenses, because they are light and tough and easy to dye. The performance required particularly for optical materials, especially spectacle lenses, is low specific gravity, high transparency and low yellowness, high heat resistance, high strength, etc. as physical properties, and high refractive index and high optical performance. Abbe number. A high refractive index makes it possible to reduce the thickness of the lens, and a high Abbe number reduces chromatic aberration of the lens. However, as the refractive index increases, the Abbe number decreases, and studies are being made to improve both simultaneously. Among these studies, the most typical method is a method using an episulfide compound disclosed in Patent Document 1.
一方、高屈折率化にともない薄肉化したレンズに対しては、安全性等の観点から従来に増して高強度が望まれる。レンズに望まれる強度は大きく分けて三種ある。第一に落球強度である。レンズに物が当たった際あるいはレンズを落とした際に簡単に破壊しない強度が必要である。第二に耐ドリル強度である。ドリルでレンズに穴をあける際に欠けや割れが生じないこと、すなわちドリル加工性が良好なことである。いわゆるツーポイントと呼ばれるフレームを装着する場合に穴を開ける必要があるが、この際に欠けや割れが生じない強度が必要である。第三に引張強度である。ツーポイントフレームの使用に耐えるためにはフレームが撓んでもレンズが破壊されない強度が必要である。
同時に、耐熱性も必要である。プラスチックレンズは表面を保護するためにハードコートを付ける事が標準となっているが、ハードコートをかける際に熱がかかるため、耐熱性が必要となっている。
On the other hand, for lenses that have become thinner with higher refractive index, higher strength is desired than in the past from the viewpoint of safety and the like. There are three types of strength desired for lenses. The first is falling ball strength. It is necessary to have strength that does not easily break when an object hits the lens or when the lens is dropped. Second is the drilling resistance. When a hole is made in a lens with a drill, no chipping or cracking occurs, that is, drilling workability is good. When mounting a so-called two-point frame, it is necessary to make a hole, but at this time, a strength that does not cause chipping or cracking is required. Third is the tensile strength. In order to withstand the use of the two-point frame, it is necessary to have a strength that prevents the lens from being destroyed even if the frame is bent.
At the same time, heat resistance is also necessary. It is standard that a plastic lens is provided with a hard coat to protect the surface, but heat resistance is required because heat is applied when the hard coat is applied.
従来からエピスルフィド化合物を用いた材料については、特許文献2、特許文献3、特許文献4、特許文献5、特許文献6、特許文献7、および特許文献8に示されるようにさまざまな高強度化の検討が行われてきているが、これらの検討では一部の強度試験のみを評価するに終わり、すべての強度試験を満足するものは得られていなかった。更には、より一層の高強度が望ましいことは言うまでも無い。また、高強度のレンズを得ようとした場合、耐熱性の低下が見られる場合があり(特許文献2、特許文献3、および特許文献4)、強度と耐熱性の両立は必須であるが困難であった。また、硬化物が白濁、あるいは硬化が十分でなく、眼鏡用レンズとして実用性に欠けるもの(特許文献5、特許文献6、および特許文献7)もあった。さらには合成困難な材料を用いているため実用化しにくいもの(特許文献8)もあった。
したがって、エピスルフィド化合物を用いたレンズは高屈折率、高アッベ数を有するが、さらに優れた強度と耐熱性を付与したレンズの開発が求められていた。
Therefore, a lens using an episulfide compound has a high refractive index and a high Abbe number, but there has been a demand for development of a lens imparted with superior strength and heat resistance.
本発明が解決しようとする課題は、優れた光学物性を有し、優れた強度と耐熱性を有する光学材料を提供し得る光学材料用樹脂組成物を提供することにある。 The problem to be solved by the present invention is to provide a resin composition for an optical material that has excellent optical properties and can provide an optical material having excellent strength and heat resistance.
本発明者らは、このような状況に鑑み、鋭意研究を重ねた結果、本課題を解決し、本発明に至った。
すなわち、本発明の一実施形態は、(a)下記一般式(1)で表されるエピスルフィド化合物、(b)キシリレンジチオール化合物および(c)キシリレンジイソシアネート化合物を含有する光学材料用樹脂組成物である。
式中、mは0〜4の整数、nは0〜2の整数を示す。
本発明の好ましい態様は、上記(a)エピスルフィド化合物が、ビス(β−エピチオプロピル)スルフィド又はビス(β−エピチオプロピル)ジスルフィドである光学材料用樹脂組成物である。また、本発明の別の好ましい態様は、上記(b)キシリレンジチオール化合物が、m−キシリレンジチオール又はp−キシリレンジチオールである光学材料用樹脂組成物である。また、本発明の別の好ましい態様は、上記(c)キシリレンジイソシアネート化合物が、m−キシリレンジイソシアネートである光学材料用樹脂組成物である。また、本発明の別の好ましい態様は、上記(c)キシリレンジイソシアネート化合物が、1、3−ビス(1−イソシアナート−1−メチルエチル)ベンゼンである光学材料用樹脂組成物である。
In view of such a situation, the present inventors have intensively studied, and as a result, solved the problem and arrived at the present invention.
That is, in one embodiment of the present invention, a resin composition for an optical material comprising (a) an episulfide compound represented by the following general formula (1), (b) a xylylene dithiol compound, and (c) a xylylene diisocyanate compound. It is.
In the formula, m represents an integer of 0 to 4, and n represents an integer of 0 to 2.
A preferred embodiment of the present invention is the resin composition for optical materials, wherein the (a) episulfide compound is bis (β-epithiopropyl) sulfide or bis (β-epithiopropyl) disulfide. Another preferred embodiment of the present invention is a resin composition for an optical material, wherein the (b) xylylenedithiol compound is m-xylylenedithiol or p-xylylenedithiol. Another preferred embodiment of the present invention is a resin composition for an optical material, wherein the (c) xylylene diisocyanate compound is m-xylylene diisocyanate. Another preferred embodiment of the present invention is a resin composition for optical materials, wherein the (c) xylylene diisocyanate compound is 1,3-bis (1-isocyanato-1-methylethyl) benzene.
また、本発明の別の好ましい態様は、さらに(d)エステル基とメルカプト基の両方を有する化合物を含む光学材料用樹脂組成物である。また、本発明の別の好ましい態様は、上記(d)エステル基とメルカプト基の両方を有する化合物が、トリメチロールプロパントリスチオグリコレート、ペンタエリスリトールテトラキスチオグリコレート、トリメチロールプロパントリスチオプロピオネートおよびペンタエリスリトールテトラキスチオプロピオネートからなる群より選択される1種以上である光学材料用樹脂組成物である。また、本発明の別の好ましい態様は、さらに(e)硫黄原子を有する無機化合物を含む光学材料用樹脂組成物である。
また、本発明の別の好ましい態様は、光学材料用樹脂組成物中に含まれるNCO基の数に対して光学材料用樹脂組成物中に含まれるSH基の数(SH基数/NCO基数)が1〜2である光学材料用樹脂組成物である。また、本発明の別の好ましい態様は、上記(a)エピスルフィド化合物が、光学材料用樹脂組成物に対して40重量%〜90重量%含まれる光学材料用樹脂組成物である。また、本発明の別の好ましい態様は、さらに(f)重合触媒としてオニウム塩および/又はホスフィン類を光学材料用樹脂組成物に対して0.001重量%〜5重量%含有する光学材料用樹脂組成物である。
Another preferred embodiment of the present invention is a resin composition for an optical material further comprising (d) a compound having both an ester group and a mercapto group. In another preferred embodiment of the present invention, the compound (d) having both an ester group and a mercapto group may be trimethylolpropane tristhioglycolate, pentaerythritol tetrakisthioglycolate, trimethylolpropane tristhiopropionate. And a resin composition for optical materials, which is at least one selected from the group consisting of pentaerythritol tetrakisthiopropionate. Another preferred embodiment of the present invention is a resin composition for an optical material further comprising (e) an inorganic compound having a sulfur atom.
In another preferred embodiment of the present invention, the number of SH groups contained in the resin composition for optical materials (SH group number / number of NCO groups) with respect to the number of NCO groups contained in the resin composition for optical materials is It is the resin composition for optical materials which is 1-2. Another preferred embodiment of the present invention is a resin composition for optical materials in which the (a) episulfide compound is contained in an amount of 40% by weight to 90% by weight with respect to the resin composition for optical materials. Another preferred embodiment of the present invention is that the resin for optical materials further comprises (f) 0.001% by weight to 5% by weight of an onium salt and / or phosphine as a polymerization catalyst with respect to the resin composition for optical materials. It is a composition.
本発明の他の実施形態は、上記光学材料用樹脂組成物を硬化して得られる光学材料である。
本発明の好ましい態様によれば、高強度、高耐熱性などの優れた特性を有する光学材料用樹脂組成物及び光学材料を提供することができる。
Other embodiment of this invention is an optical material obtained by hardening | curing the said resin composition for optical materials.
According to the preferable aspect of this invention, the resin composition for optical materials and optical material which have the outstanding characteristics, such as high intensity | strength and high heat resistance, can be provided.
以下、本発明について更に詳細に説明する。
本発明は、(a)下記一般式(1)で表されるエピスルフィド化合物、(b)キシリレンジチオール化合物および(c)キシリレンジイソシアネート化合物を含有する光学材料用樹脂組成物である。
式中、mは0〜4の整数、nは0〜2の整数を示す。
本発明では、高い屈折率と良好なアッベ数のバランスを有する光学材料を提供するために、上記一般式(1)で表されるエピスルフィド化合物が用いられる。
(a)の一般式(1)で表されるエピスルフィド化合物の具体例としては、ビス(β−エピチオプロピル)スルフィド、ビス(β−エピチオプロピル)ジスルフィド、ビス(β−エピチオプロピル)トリスルフィド、ビス(β−エピチオプロピルチオ)メタン、1,2−ビス(β−エピチオプロピルチオ)エタン、1,3−ビス(β−エピチオプロピルチオ)プロパン、1,4−ビス(β−エピチオプロピルチオ)ブタン、ビス(β−エピチオプロピルチオエチル)スルフィド、などが好ましく挙げられる。一般式(1)で表されるエピスルフィド化合物は単独でも、2種類以上を混合して用いてもよい。中でも好ましいエピスルフィド化合物は、下記構造式で表されるビス(β−エピチオプロピル)スルフィド、ビス(β−エピチオプロピル)ジスルフィドであり、最も好ましいエピスルフィド化合物は、ビス(β−エピチオプロピル)スルフィドである。
The present invention is a resin composition for an optical material containing (a) an episulfide compound represented by the following general formula (1), (b) a xylylene dithiol compound and (c) a xylylene diisocyanate compound.
In the formula, m represents an integer of 0 to 4, and n represents an integer of 0 to 2.
In the present invention, an episulfide compound represented by the above general formula (1) is used in order to provide an optical material having a balance between a high refractive index and a good Abbe number.
Specific examples of the episulfide compound represented by the general formula (1) in (a) include bis (β-epithiopropyl) sulfide, bis (β-epithiopropyl) disulfide, and bis (β-epithiopropyl) tris. Sulfide, bis (β-epithiopropylthio) methane, 1,2-bis (β-epithiopropylthio) ethane, 1,3-bis (β-epithiopropylthio) propane, 1,4-bis (β Preferred examples include -epithiopropylthio) butane and bis (β-epithiopropylthioethyl) sulfide. The episulfide compounds represented by the general formula (1) may be used alone or in combination of two or more. Among them, preferred episulfide compounds are bis (β-epithiopropyl) sulfide and bis (β-epithiopropyl) disulfide represented by the following structural formula, and the most preferred episulfide compound is bis (β-epithiopropyl) sulfide. It is.
(b)のキシリレンジチオール化合物の具体例としては、o−、m−、およびp−キシリレンジチオールが好ましく挙げられる。中でも好ましいキシリレンジチオール化合物は、下記構造式で表されるm−キシリレンジチオール、p−キシリレンジチオールであり、特に好ましいキシリレンジチオール化合物はm−キシリレンジチオールである。
(c)のキシリレンジイソシアネート化合物の具体例としては、o−、m−およびp−キシリレンジイソシアネート、1,2−、1,3−、および1,4−ビス(1−イソシアナート−1−メチルエチル)ベンゼンなどが好ましく挙げられる。これらは単独でも、2種類以上を混合して用いてもよい。中でも好ましいキシリレンジイソシアネート化合物は、下記構造式で表されるm−キシリレンジイソシアネート、1,3−ビス(1−イソシアナート−1−メチルエチル)ベンゼンであり、特に好ましいキシリレンジイソシアネート化合物はm−キシリレンジイソシアネートである。
また、(c)キシリレンジイソシアネート化合物は単独で用いることが望ましいが、キシリレンジイソシアネートと1,3−ビス(1−イソシアナート−1−メチルエチル)ベンゼンを任意の割合で混合しても良い。混合して用いる場合、好ましい混合の割合を、NCO基のモル数の比で表すならば次のとおりになる。キシリレンジイソシアネート中のNCO基のモル数をz、1,3−ビス(1−イソシアナート−1−メチルエチル)ベンゼン中のNCO基のモル数をuとした場合、z/uが0.01以上10以下であることが好ましい。より好ましくは0.05以上2以下、更に好ましくは0.1以上1以下である。 Moreover, although it is desirable to use (c) xylylene diisocyanate compound alone, xylylene diisocyanate and 1,3-bis (1-isocyanato-1-methylethyl) benzene may be mixed in an arbitrary ratio. When mixed and used, a preferable mixing ratio is expressed as follows by the ratio of the number of moles of NCO groups. When the number of moles of NCO groups in xylylene diisocyanate is z and the number of moles of NCO groups in 1,3-bis (1-isocyanato-1-methylethyl) benzene is u, z / u is 0.01. It is preferable that it is 10 or less. More preferably, it is 0.05 or more and 2 or less, More preferably, it is 0.1 or more and 1 or less.
また、キシリレンジチオール化合物と、エステル基とメルカプト基の両方を有する化合物との混合の割合は任意であるが(ただし、キシリレンジチオール化合物は必ず用いる)、より優れた物性を発現させるためにはキシリレンジチオール化合物を主成分とし、エステル基とメルカプト基の両方を有する化合物を副成分として用いることが好ましい。好ましい混合の割合を、SH基のモル数の比で表すならば次のとおりになる。エステル基とメルカプト基の両方を有する化合物中のSH基のモル数をx、キシリレンジチオール化合物中のSH基のモル数をyとしたときにx/yが0.01以上2以下であることが好ましい。より好ましくは0.1以上1.2以下、更に好ましくは0.2以上1.0以下、最も好ましくは0.3以上0.8以下である。 In addition, the mixing ratio of the xylylene dithiol compound and the compound having both an ester group and a mercapto group is arbitrary (however, the xylylene dithiol compound is always used), but in order to develop more excellent physical properties. A compound having a xylylene dithiol compound as a main component and having both an ester group and a mercapto group is preferably used as an accessory component. A preferable mixing ratio is expressed as follows by the ratio of the number of moles of SH groups. X / y is 0.01 or more and 2 or less, where x is the number of moles of SH group in the compound having both ester group and mercapto group, and y is the number of moles of SH group in xylylene dithiol compound. Is preferred. More preferably, it is 0.1 or more and 1.2 or less, More preferably, it is 0.2 or more and 1.0 or less, Most preferably, it is 0.3 or more and 0.8 or less.
(d)のエステル基とメルカプト基の両方を有する化合物の具体例としては、エチレングリコールビスチオグリコレート、ブタンジオールビスチオグリコレート、ヘキサンジオールビスチオグリコレート、トリメチロールプロパントリスチオグリコレート、ペンタエリスリトールテトラキスチオグリコレート、エチレングリコールビスチオプロピオネート、ブタンジオールビスチオプロピオネート、トリメチロールプロパントリスチオプロピオネート、ペンタエリスリトールテトラキスチオプロピオネートなどが好ましく挙げられる。中でも好ましい化合物は、下記構造式で表されるトリメチロールプロパントリスチオグリコレート、ペンタエリスリトールテトラキスチオグリコレート、トリメチロールプロパントリスチオプロピオネート、ペンタエリスリトールテトラキスチオプロピオネートであり、最も好ましい化合物は、ペンタエリスリトールテトラキスチオプロピオネートである。これらは単独でも、2種類以上を混合して用いてもよい。
(e)の硫黄原子を有する無機化合物の具体例としては、硫黄、硫化水素、二硫化炭素、硫化セレン、セレノ硫化炭素、硫化アンモニウム、二酸化硫黄、三酸化硫黄等の硫黄酸化物、チオ炭酸塩、硫酸およびその塩、硫酸水素塩、亜硫酸塩、次亜硫酸塩、過硫酸塩、チオシアン酸塩、チオ硫酸塩、二塩化硫黄、塩化チオニル、チオホスゲン等のハロゲン化物、硫化ホウ素、硫化窒素、硫化珪素、硫化リン、硫化砒素、金属硫化物、金属水硫化物等が好ましく挙げられる。これらの中でも好ましい無機化合物は硫黄、二硫化炭素、硫化セレンであり、特に好ましい無機化合物は硫黄である。これらは単独でも、2種類以上を混合して用いてもよい。(e)無機化合物の添加量は全樹脂量に対して0.01〜30重量%、好ましくは、0.1〜20重量%、更に好ましくは、1〜10重量%である。 Specific examples of the inorganic compound having a sulfur atom of (e) include sulfur, hydrogen sulfide, carbon disulfide, selenium sulfide, carbon selenosulfide, ammonium sulfide, sulfur dioxide, sulfur trioxide, and other sulfur oxides, thiocarbonates. , Sulfuric acid and its salts, hydrogen sulfate, sulfite, hyposulfite, persulfate, thiocyanate, thiosulfate, sulfur dichloride, thionyl chloride, thiophosgene, halides, boron sulfide, nitrogen sulfide, silicon sulfide Preferred examples include phosphorus sulfide, arsenic sulfide, metal sulfide, metal hydrosulfide and the like. Among these, preferred inorganic compounds are sulfur, carbon disulfide, and selenium sulfide, and particularly preferred inorganic compounds are sulfur. These may be used alone or in combination of two or more. (E) The addition amount of the inorganic compound is 0.01 to 30% by weight, preferably 0.1 to 20% by weight, and more preferably 1 to 10% by weight with respect to the total resin amount.
本発明の目的の一つである高強度を発現させるためには、光学材料用樹脂組成物中に含まれるNCO基の数に対して光学材料用樹脂組成物中に含まれるSH基の数(SH基数/NCO基数)が1以上であることが望ましい。より好ましくは1.1以上、更に好ましくは1.2以上である。一方、高い耐熱性を維持するためには光学材料用樹脂組成物中に含まれるNCO基の数に対して光学材料用樹脂組成物中に含まれるSH基の数(SH基数/NCO基数)が2以下であることが望ましい。より好ましくは1.9以下、更に好ましくは1.8以下である。 In order to develop high strength, which is one of the objects of the present invention, the number of SH groups contained in the optical material resin composition relative to the number of NCO groups contained in the optical material resin composition ( (SH group number / NCO group number) is preferably 1 or more. More preferably, it is 1.1 or more, More preferably, it is 1.2 or more. On the other hand, in order to maintain high heat resistance, the number of SH groups contained in the optical material resin composition (SH group number / NCO group number) is smaller than the number of NCO groups contained in the optical material resin composition. It is desirable that it is 2 or less. More preferably, it is 1.9 or less, More preferably, it is 1.8 or less.
高い屈折率と良好なアッベ数のバランスを有する光学材料であるためには、高い屈折率と良好なアッベ数のバランスを有する(a)エピルスルフィド化合物の割合が光学材料用樹脂組成物に対して40重量%以上であることが望ましい。より好ましくは50重量%以上、更に好ましくは60重量%以上である。一方、高強度を維持するためには、(a)エピルスルフィド化合物の割合が光学材料用樹脂組成物に対して90重量%以下であることが望ましく、より好ましくは85重量%以下、更に好ましくは80重量%以下である。
(b)キシリレンジチオール化合物の割合が、光学材料用樹脂組成物に対して1重量%以上50重量%以下であることが好ましく、より好ましくは3重量%以上30重量%以下、更に好ましくは5重量%以上20重量%以下である。
(c)キシリレンジイソシアネート化合物の割合が、光学材料用樹脂組成物に対して1重量%以上50重量%以下であることが好ましく、より好ましくは2重量%以上30重量%以下、更に好ましくは3重量%以上20重量%以下である。
In order to be an optical material having a high refractive index and a good Abbe number balance, the proportion of the (a) episulfide compound having a high refractive index and a good Abbe number balance is compared to the resin composition for optical materials. It is desirable that it is 40 weight% or more. More preferably, it is 50 weight% or more, More preferably, it is 60 weight% or more. On the other hand, in order to maintain high strength, it is desirable that the proportion of (a) episulfide compound is 90% by weight or less, more preferably 85% by weight or less, and still more preferably, with respect to the resin composition for optical materials. 80% by weight or less.
(B) The ratio of the xylylene dithiol compound is preferably 1% by weight or more and 50% by weight or less, more preferably 3% by weight or more and 30% by weight or less, and still more preferably 5% with respect to the resin composition for optical materials. % By weight or more and 20% by weight or less.
(C) The proportion of the xylylene diisocyanate compound is preferably 1% by weight or more and 50% by weight or less, more preferably 2% by weight or more and 30% by weight or less, and still more preferably 3% with respect to the resin composition for optical materials. % By weight or more and 20% by weight or less.
本発明では、更に(f)重合触媒としてオニウム塩やホスフィン化合物が好ましく用いられる。具体例としては第4級アンモニウム塩、第4級ホスホニウム塩、第3級スルホニウム塩、第2級ヨードニウム塩、ホスフィン化合物などが好ましく挙げられる。中でも光学材料用樹脂組成物との相溶性の良好な第4級アンモニウム塩および第4級ホスホニウム塩、ホスフィン化合物がより好ましく、さらに好ましくは第4級ホスホニウム塩である。より好ましい化合物の具体例としては、テトラ−n−メチルアンモニウムクロライド、テトラ−n−エチルアンモニウムクロライド、テトラ−n−ブチルアンモニウムクロライド、テトラオクチルアンモニウムクロライド、テトラフェニルアンモニウムクロライド、テトラ−n−メチルアンモニウムブロマイド、テトラ−n−エチルアンモニウムブロマイド、テトラ−n−ブチルアンモニウムブロマイド、テトラオクチルアンモニウムブロマイド、テトラフェニルアンモニウムブロマイド、トリエチルベンジルアンモニウムクロライド、セチルジメチルベンジルアンモニウムクロライド、1−n−ドデシルピリジニウムクロライド等の第4級アンモニウム塩、テトラ−n−メチルホスホニウムクロライド、テトラ−n−エチルホスホニウムクロライド、テトラ−n−ブチルホスホニウムクロライド、テトラオクチルホスホニウムクロライド、テトラフェニルホスホニウムクロライド、テトラ−n−メチルホスホニウムブロマイド、テトラ−n−エチルホスホニウムブロマイド、テトラ−n−ブチルホスホニウムブロマイド、テトラオクチルホスホニウムブロマイド、テトラフェニルホスホニウムブロマイド等の第4級ホスホニウム塩、トリフェニルホスフィン等のホスフィン化合物が挙げられる。これらの中で、さらに好ましい化合物は、トリエチルベンジルアンモニウムクロライド、テトラ−n−ブチルホスホニウムブロマイド、トリフェニルホスフィンであり、最も好ましい化合物は、テトラ−n−ブチルホスホニウムブロマイドである。 In the present invention, an onium salt or a phosphine compound is preferably used as the polymerization catalyst (f). Specific examples include quaternary ammonium salts, quaternary phosphonium salts, tertiary sulfonium salts, secondary iodonium salts, and phosphine compounds. Of these, quaternary ammonium salts, quaternary phosphonium salts, and phosphine compounds having good compatibility with the resin composition for optical materials are more preferable, and quaternary phosphonium salts are more preferable. Specific examples of more preferable compounds include tetra-n-methylammonium chloride, tetra-n-ethylammonium chloride, tetra-n-butylammonium chloride, tetraoctylammonium chloride, tetraphenylammonium chloride, and tetra-n-methylammonium bromide. Tetra-n-ethylammonium bromide, tetra-n-butylammonium bromide, tetraoctylammonium bromide, tetraphenylammonium bromide, triethylbenzylammonium chloride, cetyldimethylbenzylammonium chloride, 1-n-dodecylpyridinium chloride, etc. Ammonium salt, tetra-n-methylphosphonium chloride, tetra-n-ethylphosphonium chloride Ride, tetra-n-butylphosphonium chloride, tetraoctylphosphonium chloride, tetraphenylphosphonium chloride, tetra-n-methylphosphonium bromide, tetra-n-ethylphosphonium bromide, tetra-n-butylphosphonium bromide, tetraoctylphosphonium bromide, tetra Examples include quaternary phosphonium salts such as phenylphosphonium bromide and phosphine compounds such as triphenylphosphine. Among these, further preferred compounds are triethylbenzylammonium chloride, tetra-n-butylphosphonium bromide and triphenylphosphine, and the most preferred compound is tetra-n-butylphosphonium bromide.
(f)重合触媒の添加量は、光学材料用樹脂組成物の成分、混合比および重合硬化方法によって変化するため一概には決められないが、通常は光学材料用樹脂組成物に対して0.001重量%以上5重量%以下が好ましく、より好ましくは、0.01重量%以上1重量%以下、最も好ましくは、0.01重量%以上0.5重量%以下である。(f)重合触媒の添加量が5重量%より多いと硬化物の屈折率、耐熱性が低下し、着色する場合がある。また、0.001重量%より少ないと十分に硬化せず耐熱性が不十分となる場合がある。 (F) Although the addition amount of the polymerization catalyst varies depending on the components of the resin composition for optical materials, the mixing ratio, and the polymerization curing method, it is not generally determined. It is preferably 001 wt% or more and 5 wt% or less, more preferably 0.01 wt% or more and 1 wt% or less, and most preferably 0.01 wt% or more and 0.5 wt% or less. (F) When the addition amount of the polymerization catalyst is more than 5% by weight, the refractive index and heat resistance of the cured product may be lowered and coloring may occur. On the other hand, if it is less than 0.001% by weight, it may not be sufficiently cured and heat resistance may be insufficient.
光学材料用樹脂組成物を重合硬化させる際に、ポットライフの延長や重合発熱の分散化などを目的として、必要に応じて重合調整剤を添加することができる。重合調整剤は、長期周期律表における第13〜16族のハロゲン化物を挙げることができる。これらのうち好ましい化合物は、ケイ素、ゲルマニウム、スズ、アンチモンのハロゲン化物であり、より好ましい化合物はアルキル基を有するゲルマニウム、スズ、アンチモンの塩化物である。さらに好ましい化合物は具体的にはジブチルスズジクロライド、ブチルスズトリクロライド、ジオクチルスズジクロライド、オクチルスズトリクロライド、ジブチルジクロロゲルマニウム、ブチルトリクロロゲルマニウム、ジフェニルジクロロゲルマニウム、フェニルトリクロロゲルマニウム、トリフェニルアンチモンジクロライドであり、最も好ましい化合物の具体例は、ジブチルスズジクロライドである。重合調整剤は単独でも2種類以上を混合して使用してもよい。 When the resin composition for optical materials is polymerized and cured, a polymerization regulator can be added as necessary for the purpose of extending the pot life or dispersing the polymerization heat. Examples of the polymerization regulator include halides of Groups 13 to 16 in the long-term periodic table. Of these, preferred compounds are halides of silicon, germanium, tin and antimony, and more preferred compounds are chlorides of germanium, tin and antimony having an alkyl group. More preferred compounds are specifically dibutyltin dichloride, butyltin trichloride, dioctyltin dichloride, octyltin trichloride, dibutyldichlorogermanium, butyltrichlorogermanium, diphenyldichlorogermanium, phenyltrichlorogermanium, triphenylantimony dichloride, and the most preferred compound A specific example of is dibutyltin dichloride. The polymerization regulator may be used alone or in combination of two or more.
また、他の重合調整剤としてホスフェートやフェニルホウ酸を挙げることができる。これらのうち好ましい化合物は、ジメチルホスフェート、ジエチルホスフェート、ジブチルホスフェート、ジブトキシエチルホスフェート、ジ(2−エチルヘキシル)ホスフェート、ジイソデシルホスフェート、ジラウリルホスフェート、ジステアリルホスフェート、ジ−n−ヘキサデシルホスフェート、ジオレイルホスフェート、ジテトラコシルホスフェート、ジフェニルホスフェート、ジエチレングリコールホスフェート、フェニルホウ酸であり、さらに好ましい化合物はジフェニルホスフェート、フェニルホウ酸であり、最も好ましい化合物はジフェニルホスフェートである。これらは単独でも2種類以上を混合して使用してもよい。
重合調整剤の添加量は、通常、光学材料用樹脂組成物に対して、0.0001〜5.0重量%であり、好ましくは0.0005〜3.0重量%であり、より好ましくは0.001〜2.0重量%である。
Examples of other polymerization regulators include phosphate and phenylboric acid. Among these, preferred compounds are dimethyl phosphate, diethyl phosphate, dibutyl phosphate, dibutoxyethyl phosphate, di (2-ethylhexyl) phosphate, diisodecyl phosphate, dilauryl phosphate, distearyl phosphate, di-n-hexadecyl phosphate, dioleyl. Phosphate, ditetracosyl phosphate, diphenyl phosphate, diethylene glycol phosphate, and phenylboric acid are preferred. Diphenyl phosphate and phenylboric acid are more preferred, and the most preferred compound is diphenyl phosphate. These may be used alone or in admixture of two or more.
The addition amount of the polymerization regulator is usually 0.0001 to 5.0% by weight, preferably 0.0005 to 3.0% by weight, and more preferably 0 to the resin composition for an optical material. 0.001 to 2.0% by weight.
本発明の光学材料用樹脂組成物において、硬化物の屈折率等の諸物性を調節するために、(a)化合物以外のエピスルフィド化合物、(b)化合物以外のチオール化合物、(c)化合物以外のイソシアネート化合物、エポキシ化合物、不飽和基を有するアルコール類を併用することも可能である。 In the resin composition for an optical material of the present invention, in order to adjust various physical properties such as the refractive index of the cured product, an episulfide compound other than the compound (a), a thiol compound other than the compound (b), and a compound other than the compound (c) It is also possible to use an isocyanate compound, an epoxy compound, and an alcohol having an unsaturated group in combination.
また、本発明の光学材料用樹脂組成物を重合硬化して光学材料を得る際、周知の酸化防止剤、紫外線吸収剤、ブルーイング剤等の添加剤を加えて、得られる材料の実用性をより向上せしめることはもちろん可能である。 In addition, when the optical material resin composition of the present invention is polymerized and cured to obtain an optical material, additives such as well-known antioxidants, ultraviolet absorbers, and bluing agents are added to make the resulting material practical. Of course, it can be improved further.
酸化防止剤の好ましい例としてはフェノール誘導体が挙げられる。中でも好ましい化合物は多価フェノール類、ハロゲン置換フェノール類であり、より好ましい化合物はカテコール、ピロガロール、アルキル置換カテコール類であり、最も好ましい化合物はカテコール、ピロガロールである。紫外線吸収剤の好ましい例としてはベンゾトリアゾール系化合物、ベンゾフェノン系化合物が挙げられる。中でも好ましい化合物はベンゾトリアゾール系化合物であり、特に好ましい化合物の具体例は2−(2−ヒドロキシ−5−メチルフェニル)−2H−ベンゾトリアゾール、5−クロロ−2−(3,5−ジ−tert−ブチル−2−ヒドロキシフェニル)−2H−ベンゾトリアゾール、2−(3−tert−ブチル−2−ヒドロキシ−5−メチルフェニル)−5−クロロ−2H−ベンゾトリアゾール、2−(3,5−ジ−tert−ペンチル−2−ヒドロキシフェニル)−2H−ベンゾトリアゾール、2−(3,5−ジ−tert−ブチル−2−ヒドロキシフェニル)−2H−ベンゾトリアゾール、2−(2−ヒドロキシ−4−オクチルオキシフェニル)−2H−ベンゾトリアゾール、2−(2−ヒドロキシ−5−tert−オクチルフェニル)−2H−ベンゾトリアゾールである。ブルーイング剤の好ましい例としてはアントラキノン系化合物が挙げられる。これらの酸化防止剤、紫外線吸収剤およびブルーイング剤の添加量は、通常、光学材料用樹脂組成物に対してそれぞれ0.000001〜5重量%である。 Preferable examples of the antioxidant include phenol derivatives. Among them, preferred compounds are polyhydric phenols and halogen-substituted phenols, more preferred compounds are catechol, pyrogallol, and alkyl-substituted catechols, and most preferred compounds are catechol and pyrogallol. Preferred examples of the ultraviolet absorber include benzotriazole compounds and benzophenone compounds. Among them, preferred compounds are benzotriazole compounds, and specific examples of particularly preferred compounds are 2- (2-hydroxy-5-methylphenyl) -2H-benzotriazole, 5-chloro-2- (3,5-di-tert. -Butyl-2-hydroxyphenyl) -2H-benzotriazole, 2- (3-tert-butyl-2-hydroxy-5-methylphenyl) -5-chloro-2H-benzotriazole, 2- (3,5-di -Tert-pentyl-2-hydroxyphenyl) -2H-benzotriazole, 2- (3,5-di-tert-butyl-2-hydroxyphenyl) -2H-benzotriazole, 2- (2-hydroxy-4-octyl) Oxyphenyl) -2H-benzotriazole, 2- (2-hydroxy-5-tert-octylphenyl) A -2H- benzotriazole. Preferable examples of the bluing agent include anthraquinone compounds. The addition amount of these antioxidant, ultraviolet absorber and bluing agent is usually 0.000001 to 5% by weight with respect to the resin composition for optical materials.
また、本発明の光学材料用樹脂組成物は重合中に型から剥がれやすい場合は、周知の外部および/または内部密着性改善剤を使用または添加して、得られる硬化物と型の密着性を向上せしめることも可能である。密着性改善剤としては、周知のシランカップリング剤やチタネート化合物類などが挙げられ、これらは単独でも、2種類以上を混合して用いてもよい。添加量は通常、光学材料用樹脂組成物に対して0.0001〜5重量%である。逆に、本発明の光学材料用樹脂組成物は重合後に型から剥がれにくい場合は、周知の外部および/または内部離型剤を使用または添加して、得られる硬化物の型からの離型性を向上せしめることも可能である。離型剤としては、フッ素系ノニオン界面活性剤、シリコン系ノニオン界面活性剤、燐酸エステル、酸性燐酸エステル、オキシアルキレン型酸性燐酸エステル、酸性燐酸エステルのアルカリ金属塩、オキシアルキレン型酸性燐酸エステルのアルカリ金属塩、高級脂肪酸の金属塩、高級脂肪酸エステル、パラフィン、ワックス、高級脂肪族アミド、高級脂肪族アルコール、ポリシロキサン類、脂肪族アミンエチレンオキシド付加物などが挙げられ、これらは単独でも、2種類以上を混合して用いてもよい。添加量は通常、光学材料用樹脂組成物に対して0.0001〜5重量%である。 In addition, when the resin composition for optical materials of the present invention is easily peeled off from the mold during polymerization, a known external and / or internal adhesion improver is used or added to improve the adhesion between the obtained cured product and the mold. It is also possible to improve. Examples of the adhesion improving agent include known silane coupling agents and titanate compounds, and these may be used alone or in combination of two or more. The addition amount is usually 0.0001 to 5% by weight with respect to the resin composition for optical materials. On the contrary, when the resin composition for optical materials of the present invention is difficult to peel off from the mold after polymerization, a known external and / or internal mold release agent is used or added to release the cured product from the mold. It is also possible to improve. Release agents include fluorine-based nonionic surfactants, silicon-based nonionic surfactants, phosphate esters, acidic phosphate esters, oxyalkylene-type acidic phosphate esters, alkali metal salts of acidic phosphate esters, and alkalis of oxyalkylene-type acidic phosphate esters. Examples include metal salts, metal salts of higher fatty acids, higher fatty acid esters, paraffins, waxes, higher aliphatic amides, higher aliphatic alcohols, polysiloxanes, aliphatic amine ethylene oxide adducts, and these may be used alone or in combination of two or more. May be used in combination. The addition amount is usually 0.0001 to 5% by weight with respect to the resin composition for optical materials.
本発明の光学材料用樹脂組成物を重合硬化して光学材料を製造する方法は、さらに詳しく述べるならば以下の通りである。前述した各組成成分、酸化防止剤、紫外線吸収剤、重合触媒、ラジカル重合開始剤、密着性改善剤、離型剤などの添加剤を、全て同一容器内で同時に撹拌下に混合しても、各原料を段階的に添加混合しても、数成分を別々に混合後さらに同一容器内で再混合しても良い。各原料および副原料はいかなる順序で混合してもかまわない。混合にあたり、設定温度、これに要する時間等は基本的には各成分が十分に混合される条件であれば良い。 The method for producing an optical material by polymerizing and curing the resin composition for an optical material of the present invention is as follows. Additives such as the above-mentioned composition components, antioxidants, ultraviolet absorbers, polymerization catalysts, radical polymerization initiators, adhesion improvers, mold release agents, etc., all mixed together in the same container under stirring, Each raw material may be added and mixed in stages, or several components may be mixed separately and then remixed in the same container. Each raw material and auxiliary raw material may be mixed in any order. In mixing, the set temperature, the time required for this, and the like may basically be the conditions under which each component is sufficiently mixed.
本発明では光学材料用樹脂組成物に対し、あらかじめ脱気処理を行うことが好ましく、これにより光学材料の高度な透明性が達成される場合がある。脱気処理は、組成成分の一部もしくは全部と反応可能な化合物、重合触媒、添加剤の混合前、混合時あるいは混合後に、減圧下に行うことが好ましい。好ましくは、混合時あるいは混合後に、減圧下に行う。処理条件は、0.001〜50torrの減圧下、1分〜24時間、0℃〜100℃で行う。減圧度は、好ましくは0.005〜25torrであり、より好ましくは0.01〜10torrであり、これらの範囲で減圧度を可変してもよい。脱気時間は、好ましくは5分〜18時間であり、より好ましくは10分〜12時間である。脱気の際の温度は、好ましくは5℃〜80℃であり、より好ましくは10℃〜60℃であり、これらの範囲で温度を可変してもよい。脱気処理の際は、撹拌、気体の吹き込み、超音波などによる振動などによって、樹脂組成物の界面を更新することは、脱気効果を高める上で好ましい操作である。脱気処理により、除去される成分は、主に硫化水素等の溶存ガスや低分子量のチオール等の低沸点物等である。さらには、これらの樹脂組成物および/または混合前の各原料を0.05〜10μm程度の孔径を有するフィルターで固形物等を濾過し精製することは本発明の光学材料の品質をさらに高める上からも好ましい。
このようにして得られた光学材料用樹脂組成物は、ガラスや金属製の型に注入し、加熱や紫外線などの活性エネルギー線の照射によって重合硬化反応を進めた後、型から外される。好ましくは、加熱によって重合硬化する。この場合、硬化時間は0.1〜200時間、通常1〜100時間であり、硬化温度は−10〜160℃、通常−10〜140℃である。重合は所定の重合温度で所定時間ホールドし、0.1℃〜100℃/時間で昇温し、0.1℃〜100℃/時間で降温およびこれらの組み合わせで行う。また、重合終了後、硬化物を50〜150℃の温度で10分〜5時間程度アニール処理を行う事は、本発明の光学材料の歪を除くために好ましい処理である。さらに必要に応じて染色、ハードコート、耐衝撃性コート、反射防止、防曇性付与等表面処理を行うことができる。
こうして得られた重合体は、3次元架橋しているため不溶、不融化した樹脂状物である。
In the present invention, the resin composition for optical materials is preferably subjected to a deaeration treatment in advance, and thereby high transparency of the optical material may be achieved. The deaeration treatment is preferably performed under reduced pressure before, during or after mixing the compound, polymerization catalyst, and additive capable of reacting with some or all of the composition components. Preferably, it is performed under reduced pressure during or after mixing. The treatment conditions are 0 to 100 ° C. under reduced pressure of 0.001 to 50 torr for 1 minute to 24 hours. The degree of vacuum is preferably 0.005 to 25 torr, more preferably 0.01 to 10 torr, and the degree of vacuum may be varied within these ranges. The deaeration time is preferably 5 minutes to 18 hours, more preferably 10 minutes to 12 hours. The temperature at the time of deaeration is preferably 5 ° C. to 80 ° C., more preferably 10 ° C. to 60 ° C., and the temperature may be varied within these ranges. In the deaeration process, renewing the interface of the resin composition by stirring, blowing of gas, vibration by ultrasonic waves, or the like is a preferable operation for enhancing the deaeration effect. Components removed by the deaeration treatment are mainly dissolved gases such as hydrogen sulfide, and low boiling point substances such as low molecular weight thiols. Furthermore, filtering and purifying these resin compositions and / or raw materials before mixing with a filter having a pore size of about 0.05 to 10 μm further improves the quality of the optical material of the present invention. Is also preferable.
The resin composition for optical material thus obtained is poured into a glass or metal mold and subjected to a polymerization and curing reaction by heating or irradiation with active energy rays such as ultraviolet rays, and then removed from the mold. Preferably, it is polymerized and cured by heating. In this case, the curing time is 0.1 to 200 hours, usually 1 to 100 hours, and the curing temperature is −10 to 160 ° C., usually −10 to 140 ° C. The polymerization is carried out by holding at a predetermined polymerization temperature for a predetermined time, raising the temperature at 0.1 ° C. to 100 ° C./hour, lowering the temperature at 0.1 ° C. to 100 ° C./hour, and a combination thereof. Further, after the polymerization is completed, annealing the cured product at a temperature of 50 to 150 ° C. for about 10 minutes to 5 hours is a preferable treatment for removing the distortion of the optical material of the present invention. Furthermore, surface treatments such as dyeing, hard coating, impact resistant coating, antireflection and imparting antifogging properties can be performed as necessary.
The polymer thus obtained is a resinous material insoluble and infusible because it is three-dimensionally crosslinked.
以下、実施例により本発明を具体的に説明するが、本発明はこれらに限定されるものではない。なお、評価は以下の方法で行った。
落球強度:2.5mm厚の平板に127cmの高さから10gの鉄球を落下させて、順次鉄球の重量を10gずつ増加させて平板が破壊するまで試験を行い、破壊した時の鉄球の与えた衝撃エネルギー(J)を測定した。
耐ドリル強度:ドリルの回転数2500rpm、進入速度600mm/分で2.5mm厚の平板に直径2mmの穴を開けたときの周辺部の状態を測定した。周辺部に欠けが見られないものを○、見られたものを×とした。
引張強度:直径50mm、2mm厚のプラノーレンズの両端から4mmのところに直径2mmの穴を開けた。2つの穴にピンを差し込んで両端を固定し、10mm/分の速度で引っ張り、破壊時の強度(kgf)を測定した。
耐熱性:3mm厚の試料に直径1mmのピンを乗せて10gの荷重を与え、30℃から10℃/分で昇温してTMA測定を行い、熱膨張が変化したピークの値を測定した。80℃以上を○、80℃未満を×とした。
屈折率、アッベ数:アッベ屈折率計(株式会社アタゴ製アッベ屈折率測定機NAR−4T)を用い、25℃で測定した。
屈折率の測定では、d線(587.6nm、黄色)での屈折率を測定した。これは、一般的にndと表記される。
アッベ数の測定では、まずd線(587.6nm、黄色)、F線(486.1nm、青色)、C線(656.3nm、赤色)での屈折率を測定した。それぞれの数値をnd、nF、nCとした場合、アッベ数νdは以下の計算式で求められる。
νd=(nd−1)/(nF−nC)
EXAMPLES Hereinafter, the present invention will be specifically described with reference to examples, but the present invention is not limited thereto. Evaluation was performed by the following method.
Falling ball strength: Drop a 10 g iron ball from a height of 127 cm onto a 2.5 mm thick flat plate, increase the weight of the iron ball in increments of 10 g, and test until the flat plate breaks. The impact energy (J) applied was measured.
Drill strength: The state of the periphery when a 2 mm diameter hole was drilled in a 2.5 mm thick flat plate with a drill rotation speed of 2500 rpm and an entry speed of 600 mm / min was measured. The case where no chipping was observed in the peripheral portion was marked with ◯, and the case where chipping was seen was marked with ×.
Tensile strength: A hole having a diameter of 2 mm was formed at a position 4 mm from both ends of a planar lens having a diameter of 50 mm and a thickness of 2 mm. A pin was inserted into the two holes to fix both ends, and the wire was pulled at a speed of 10 mm / min, and the strength at break (kgf) was measured.
Heat resistance: A pin having a diameter of 1 mm was placed on a 3 mm thick sample, a load of 10 g was applied, the temperature was raised from 30 ° C. at 10 ° C./min, TMA measurement was performed, and the peak value at which the thermal expansion changed was measured. 80 degreeC or more was set to (circle) and less than 80 degreeC was set to x.
Refractive index, Abbe number: Measured at 25 ° C. using an Abbe refractometer (Abbago's Abbe refractometer NAR-4T).
In the measurement of the refractive index, the refractive index at the d-line (587.6 nm, yellow) was measured. This is denoted generally n d.
In the Abbe number measurement, first, the refractive index was measured for the d-line (587.6 nm, yellow), the F-line (486.1 nm, blue), and the C-line (656.3 nm, red). When the respective numerical values are n d , n F , and n C , the Abbe number ν d can be obtained by the following calculation formula.
ν d = (n d −1) / (n F −n C )
実施例1
(a)エピスルフィド化合物としてビス(β−エピチオプロピル)スルフィドを67重量部、(b)キシリレンジチオール化合物としてm−キシリレンジチオールを16重量部、(c)キシリレンジイソシアネート化合物として1,3−ビス(1−イソシアナート−1−メチルエチル)ベンゼンを17重量部、内部離型剤としてポリオキシエチレンラウリルエーテルリン酸ナトリウム0.005重量部、重合調整剤としてジブチルスズジクロライド0.05重量部、重合触媒としてテトラブチルホスホニムブロマイド0.1重量部、抗酸化剤としてカテコール0.005重量部、および紫外線吸収剤として2−(2−ヒドロキシ−5−tert−オクチルフェニル)ベンゾトリアゾール0.5重量部を混合し、室温で攪拌して均一液とした。次に上記組成物を10torrの減圧下で30分脱気を行った後、レンズ用モールドに注入し、オーブン中で30℃から100℃まで22時間かけて昇温して重合硬化させた。その後、型から外し、110℃で1時間加熱してアニール処理を行った。得られたレンズは透明であり、良好な外観であった。光学物性、強度、耐熱性を測定し、その結果を表1に示した。
Example 1
(A) 67 parts by weight of bis (β-epithiopropyl) sulfide as the episulfide compound, (b) 16 parts by weight of m-xylylenedithiol as the xylylenedithiol compound, (c) 1,3- 17 parts by weight of bis (1-isocyanato-1-methylethyl) benzene, 0.005 parts by weight of sodium polyoxyethylene lauryl ether phosphate as an internal mold release agent, 0.05 parts by weight of dibutyltin dichloride as a polymerization regulator, polymerization Tetrabutylphosphonium bromide 0.1 parts by weight as a catalyst, 0.005 parts by weight of catechol as an antioxidant, and 0.5 parts by weight of 2- (2-hydroxy-5-tert-octylphenyl) benzotriazole as an ultraviolet absorber Were mixed and stirred at room temperature to obtain a uniform solution. Next, the composition was degassed for 30 minutes under a reduced pressure of 10 torr, then poured into a lens mold, and polymerized and cured by raising the temperature from 30 ° C. to 100 ° C. over 22 hours. Then, it removed from the type | mold and it annealed by heating at 110 degreeC for 1 hour. The obtained lens was transparent and had a good appearance. The optical properties, strength, and heat resistance were measured, and the results are shown in Table 1.
実施例2〜6
実施例1に示す操作を、表1に示す組成で実施した。得られたレンズはいずれも透明であり、良好な外観であった。光学物性、強度、耐熱性を測定し、その結果を表1に示した。
Examples 2-6
The operation shown in Example 1 was carried out with the composition shown in Table 1. All of the obtained lenses were transparent and had a good appearance. The optical properties, strength, and heat resistance were measured, and the results are shown in Table 1.
実施例7〜14
表1に示すように、(d)エステル基とメルカプト基の両方を有する化合物を併用した組成で実施した。得られたレンズはいずれも透明であり、良好な外観であった。光学物性、強度、耐熱性を測定し、その結果を表1に示した。
Examples 7-14
As shown in Table 1, (d) it implemented by the composition which used together the compound which has both an ester group and a mercapto group. All of the obtained lenses were transparent and had a good appearance. The optical properties, strength, and heat resistance were measured, and the results are shown in Table 1.
実施例15、16
表1に示すように、(e)硫黄原子を有する無機化合物を併用した組成で実施した。得られたレンズはいずれも透明であり、良好な外観であった。光学物性、強度、耐熱性を測定し、その結果を表1に示した。
Examples 15 and 16
As shown in Table 1, (e) It implemented by the composition which used together the inorganic compound which has a sulfur atom. All of the obtained lenses were transparent and had a good appearance. The optical properties, strength, and heat resistance were measured, and the results are shown in Table 1.
実施例17〜20
表1に示すように、(d)エステル基とメルカプト基の両方を有するおよび(e)硫黄原子を有する無機化合物を併用した組成で実施した。得られたレンズはいずれも透明であり、良好な外観であった。光学物性、強度、耐熱性を測定し、その結果を表1に示した。
Examples 17-20
As shown in Table 1, (d) it carried out by the composition which used together the inorganic compound which has both an ester group and a mercapto group, and (e) has a sulfur atom. All of the obtained lenses were transparent and had a good appearance. The optical properties, strength, and heat resistance were measured, and the results are shown in Table 1.
比較例1〜8
実施例1に示す操作を、表2に示す組成で実施した。(b)キシリレンジチオール化合物または(c)キシリレンジイソシアネート化合物を用いずに、他の化合物を用いた組成で重合硬化させたため、強度が十分に出なかった。さらには、耐熱性も不十分な例もみられた。
Comparative Examples 1-8
The operation shown in Example 1 was carried out with the composition shown in Table 2. Since (b) the xylylene dithiol compound or (c) the xylylene diisocyanate compound was used for polymerization and curing with a composition using other compounds, the strength was not sufficiently obtained. In addition, there were cases where heat resistance was insufficient.
(a)エピスルフィド化合物
a−1:ビス(β−エピチオプロピル)スルフィド
a−2:ビス(β−エピチオプロピル)ジスルフィド
(b)キシリレンジチオール化合物
b−1:m−キシリレンジチオール
b−2:p−キシリレンジチオール
(c)キシリレンジイソシアネート化合物
c−1:1,3−ビス(1−イソシアナート−1−メチルエチル)ベンゼン
c−2:m−キシリレンジイソシアネート
(d)エステル基とメルカプト基の両方を有する化合物
d−1:ペンタエリスリトールテトラキスチオプロピオネート
d−2:ペンタエリスリトールテトラキスチオグリコレート
d−3:トリメチロールプロパントリスチオプロピオネート
d−4:トリメチロールプロパントリスチオグリコレート
(e)硫黄原子を有する無機化合物
e−1:硫黄
a−1:ビス(β−エピチオプロピル)スルフィド
a−2:ビス(β−エピチオプロピル)ジスルフィド
b−1:m−キシリレンジチオール
b−2:p−キシリレンジチオール
DMDS:ビス(2−メルカプトエチル)スルフィド
DMMD:2,5−ビス(メルカプトメチル)−1,4−ジチアン
c−1:m−テトラメチルキシリレンジイソシアネート
c−2:m−キシリレンジイソシアネート
BIC:1,3−ビス(イソシアネートメチル)シクロヘキサン
DIMB:ジ(イソシアネートメチル)ビシクロヘプタン
BIND:2,5−ビス(イソシアネートメチル)−1,4−ジチアン
e−1:硫黄
本発明の好ましい態様である光学材料用樹脂組成物を重合硬化することにより、これまで従来の化合物を原料とする限り困難であった、十分に高い屈折率と良好なアッベ数を有し、更に高い強度と耐熱性を有する光学材料を提供することが可能となった。 By polymerizing and curing the resin composition for an optical material which is a preferred embodiment of the present invention, it has a sufficiently high refractive index and a good Abbe number, which has been difficult as long as conventional compounds are used as raw materials. It has become possible to provide an optical material having high strength and heat resistance.
Claims (14)
(式中、mは0〜4の整数、nは0〜2の整数を示す。) (A) episulfide compound represented by the following general formula (1), (b) xylylenedithiol compound, and 1, 2, 1,3, and 1,4-bis (1-isocyanato -1 -Resin composition for optical materials containing the compound (c) selected from the group consisting of methylethyl) benzene.
(In the formula, m represents an integer of 0 to 4, and n represents an integer of 0 to 2.)