JP5421531B2 - モリブデン金属粉末およびその製造 - Google Patents
モリブデン金属粉末およびその製造 Download PDFInfo
- Publication number
- JP5421531B2 JP5421531B2 JP2007537984A JP2007537984A JP5421531B2 JP 5421531 B2 JP5421531 B2 JP 5421531B2 JP 2007537984 A JP2007537984 A JP 2007537984A JP 2007537984 A JP2007537984 A JP 2007537984A JP 5421531 B2 JP5421531 B2 JP 5421531B2
- Authority
- JP
- Japan
- Prior art keywords
- metal powder
- molybdenum metal
- heating
- ammonium molybdate
- intermediate product
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は概してモリブデンに関し、より具体的にはモリブデン金属粉末とその製造に関する。
モリブデン(Mo)は銀白色または白金色の金属化学元素で、硬質であることや可鍛性、展延性および高い融点を有するという特性を、その他の望ましい特性とともに有している。モリブデンは自然界では純粋な形態ではなく化合物の状態で見出される。モリブデン鉱石は自然界では輝水鉛鉱(二硫化モリブデン、MoS2)として存在する。
モリブデン金属粉末は、BET分析で測定して約1.0メートル2/グラム(m2/g)と約3.0m2/gの間の範囲の表面積対質量比(surface-area-to-mass-ratio)を有し、これと組合わせて粒子の少なくとも30%がサイズ+100の標準タイラーメッシュふるい(standard Tyler mesh sieve)よりも大きい粒度となるような粒度を有する。モリブデン金属粉末はさらに、ホール流量計(Hall Flowmeter)で測定して約29秒/50グラム(s/50g)と約64s/50gの間の範囲の流動性によって特徴づけることができる。モリブデン金属粉末はまた、その比較的低い焼結温度によって特徴づけることができて、このときモリブデン金属粉末は約950℃で焼結し始める。モリブデン金属粉末は約0.2%未満の酸素の最終重量パーセントを有する。
新規なモリブデン金属粉末10は、BET分析で測定して約1.0メートル2/グラム(m2/g)と約3.0m2/gの間の範囲の表面積対質量比を有し、これと組合わせて粒子の少なくとも30%がサイズ+100の標準タイラーメッシュふるいよりも大きい粒度となるような粒度を有する。加えて、モリブデン金属粉末10は、ホール流量計で測定して約29秒/50グラム(s/50g)と約64s/50gの間の範囲の流動性;焼結が始まる温度;および最終製品中に存在する酸素の重量パーセントによってさらに特徴づけることができる。
装置12(上で説明したもの)を用いてモリブデン金属粉末10(上で説明したもの)を製造するための方法80がここで開示され、そして図2に示されている。本発明に従ってモリブデン金属粉末10を製造するための方法80の態様は、図2に示す流れ図における工程として示すことができる。
これらの実施例において、モリブデン酸アンモニウム先駆物質24はヘプタモリブデン酸アンモニウム(AHM)であった。この実施例においてモリブデン酸アンモニウム先駆物質24として用いられるAHMの粒子はClimax Molybdenum Company(Fort Madison、アイオワ州)によって製造されていて、そこから商業的に入手できる。
実施例3〜6において、モリブデン酸アンモニウム先駆物質24はヘプタモリブデン酸アンモニウム(AHM)であった。実施例3〜6においては、実施例1および2において上で詳細に説明したものと同じモリブデン酸アンモニウム先駆物質24、同じ装置、および同じプロセスパラメーターの設定を用いた。実施例3〜6においては最終の帯域の温度だけを変えた。実施例3〜6について得られた結果を下の表5に示す。
実施例7〜12において、モリブデン酸アンモニウム先駆物質24はヘプタモリブデン酸アンモニウム(AHM)であった。実施例7〜12においては、実施例1および2において上で詳細に説明したものと同じモリブデン酸アンモニウム先駆物質24、同じ装置、および同じプロセスパラメーターの設定を用いた。実施例7〜12においては中間の帯域と最終の帯域の温度を変えた。中間の帯域と最終の帯域の温度および実施例7〜12について得られた結果を下の表6に示す。
実施例13において、モリブデン酸アンモニウム先駆物質24はジモリブデン酸アンモニウム(ADM)であった。実施例13においては、実施例1および2において上で詳細に説明したものと同じ装置とプロセスパラメーターの設定を用いたが、ただし最初の加熱帯域、中間の加熱帯域および最終の加熱帯域の温度は600℃に維持された。実施例13について得られた結果を下の表7に示す。
実施例14において、モリブデン酸アンモニウム先駆物質24はオクタモリブデン酸アンモニウム(AOM)であった。実施例14においては、実施例1および2において上で詳細に説明したものと同じ装置とプロセスパラメーターの設定を用いたが、ただし中間の加熱帯域と最終の加熱帯域の温度を変えた。実施例14において、中間の加熱帯域は750℃〜800℃の間に設定され、そして最終の加熱帯域は900℃〜1000℃の間に設定された。実施例14について得られた結果を下の表8に示す。
Claims (16)
- モリブデン金属粉末であって、
BET分析で測定して1.0m2/gと3.0m2/gの間の表面積対質量比;
0.2%未満の酸素の重量パーセント;および
ホール流量計で測定して58s/50gと63s/50gの間の流動時間;
を有し、
モリブデン金属粉末粒子の少なくとも30%がサイズ+100の標準タイラーメッシュふるいよりも大きい粒度を有する前記モリブデン金属粉末。 - 表面積対質量比がBET分析で測定して1.32m2/gと2.56m2/gの間である、請求項1に記載のモリブデン金属粉末。
- モリブデン金属粉末は950℃で焼結し始める、請求項1に記載のモリブデン金属粉末。
- モリブデン金属粉末を製造する方法であって:
モリブデン酸アンモニウムの供給物を炉の中に用意すること;
モリブデン酸アンモニウムを還元ガスの存在下で最初の温度において加熱して中間生成物を前記炉の中に生成させること;および
前記炉の中で中間生成物を還元ガスの存在下で最終温度において加熱し、それによってBET分析で測定して1.0m2/gと3.0m2/gの間の表面積対質量比、0.2%未満の酸素の重量パーセント、およびホール流量計で測定して58s/50gと63s/50gの間の流動時間を有するモリブデン金属粉末を生成させること、ここでモリブデン金属粉末粒子の少なくとも30%がサイズ+100の標準タイラーメッシュふるいよりも大きい粒度を有する;
から本質的になる前記方法。 - モリブデン金属粉末の表面積対質量比がBET分析で測定して1.32m2/gと2.56m2/gの間である、請求項4に記載の方法。
- モリブデン酸アンモニウムを最初の温度において加熱することと中間生成物を最終温度において加熱することは、2時間にわたって加熱することを含む、請求項4に記載の方法。
- モリブデン酸アンモニウムを最初の温度において加熱することは、600℃において加熱することを含む、請求項4に記載の方法。
- モリブデン酸アンモニウムを最初の温度において加熱することは、40分間にわたって加熱することを含む、請求項4に記載の方法。
- 中間生成物を最終温度において加熱することは、950℃において加熱することを含む、請求項4に記載の方法。
- 中間生成物を最終温度において加熱することは、40分間にわたって加熱することを含む、請求項4に記載の方法。
- 中間生成物を最終温度において加熱する前に中間生成物を中間の温度において加熱することをさらに含む、請求項4に記載の方法。
- 中間生成物を中間の温度において加熱することは、750℃において加熱することを含む、請求項11に記載の方法。
- モリブデン金属粉末を製造する方法であって:
モリブデン酸アンモニウムの供給物を炉の中に用意すること;
モリブデン酸アンモニウムを還元ガスの存在下で最初の温度において加熱して中間生成物を前記炉の中に生成させること;
中間生成物を前記炉の中で最終温度において加熱する前に、中間生成物を中間の温度で40分間にわたって加熱すること;
および
前記炉の中で中間生成物を還元ガスの存在下で最終温度において加熱し、それによってBET分析で測定して1.0m 2 /gと3.0m 2 /gの間の表面積対質量比、0.2%未満の酸素の重量パーセント、およびホール流量計で測定して58s/50gと63s/50gの間の流動時間を有するモリブデン金属粉末を生成させること、ここでモリブデン金属粉末粒子の少なくとも30%がサイズ+100の標準タイラーメッシュふるいよりも大きい粒度を有する;
から本質的になる前記方法。 - モリブデン酸アンモニウムの供給物を用意することは、ジモリブデン酸アンモニウム(ADM)の供給物を用意することを含む、請求項13に記載の方法。
- モリブデン酸アンモニウムの供給物を用意することは、ヘプタモリブデン酸アンモニウム(AHM)の供給物を用意することを含む、請求項13に記載の方法。
- モリブデン酸アンモニウムの供給物を用意することは、オクタモリブデン酸アンモニウム(AOM)の供給物を用意することを含む、請求項13に記載の方法。