JP5362285B2 - Adsorption roll - Google Patents
Adsorption roll Download PDFInfo
- Publication number
- JP5362285B2 JP5362285B2 JP2008203202A JP2008203202A JP5362285B2 JP 5362285 B2 JP5362285 B2 JP 5362285B2 JP 2008203202 A JP2008203202 A JP 2008203202A JP 2008203202 A JP2008203202 A JP 2008203202A JP 5362285 B2 JP5362285 B2 JP 5362285B2
- Authority
- JP
- Japan
- Prior art keywords
- roll
- sintered body
- porous ceramic
- ceramic sintered
- web
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、薄い帯状の有機物フィルムや金属箔など、繊細な取り扱いが必要なウェブを吸着状態で搬送案内、各種処理をするための吸着ロールに関する。
The present invention relates to a suction roll for conveying and guiding a web that requires delicate handling, such as a thin band-shaped organic film or a metal foil, in a suction state and performing various treatments.
ウェブを吸着状態で搬送案内する吸着ロールとしては、吸着ロールの内部を減圧状態にして、そこから連通した吸着ロール表面に設けた多数の穴を用いて吸着を行なう「スルーホール型」が一般的である。特許文献1にはこのスルーホール型の吸着ロールが示されている。スルーホール型は、ウェブがホール部と接する部分が凹になり、その周囲は引っ張られることになるために、皺も生じやすく、ウェブに処理をすることに適していない。
As a suction roll that conveys and guides the web in the suction state, the "through-hole type" is generally used in which the inside of the suction roll is decompressed and suction is performed using a number of holes provided on the surface of the suction roll communicating therewith. It is.
特許文献2には吸着ロールのウェブに接する部分の一部に多数の多孔質セラミックスを埋設したロールが示されている。この技術は、吸着ロールの長方向にウェブが揃うように提案されたものである。多孔質セラミックスの部分と吸着ロール本体の金属部分は材質も面粗度も異なるために、均一な吸着や、多孔質セラミックス面からの転写により、ウェブ表面の凹凸をなくすことはできない。また、代表図面の27,28に示されるような、吸着ロールの一部分だけを吸着する機構が必要となる。これは、吸引に必要としない部分の多孔質セラミックスからの空気の流入(リーク)が大きいために必要な機構であり、費用もかさむ。
特許文献3にはロール表面に多孔質セラミックスを溶射にて形成し、さらにその上から樹脂製の膜を形成したロールである。この発明は、多孔質セラミックスがロール表面に形成されるものの、ロール内部から吸着するわけではなく、溶射で形成された面は面粗さも十分低いとはいえない。
近年、吸着ロールを用いての送りの状態にて、ウェブへの印刷、塗布、転写、検査などの処理を行なう装置は増加傾向にある。例として図2中のAで示す箇所に、前記処理を行なうための装置を設置して、吸着ロールに吸着されている部分のウェブに処理を行なう、または検査するものである。
近年、前記処理の精度、均一性は大幅な改善が求められている。先行文献に示されている技術では、ウェブを吸着されている面と考えた場合に、その中でのロール材質の違いや、スルーホール部分の存在により、ウェブが均一に吸着され、搬送案内や各種処理をすることは難しく、従来技術ではいずれも解決することができない。
本発明が解決しようとする課題は、吸着ロールを改善することにより、ウェブの吸着、搬送案内、処理において、ウェブを極めて均一に平滑性を保った状態とすることである。
In recent years, there is an increasing number of apparatuses that perform processing such as printing, coating, transfer, and inspection on a web while being fed using an adsorption roll. As an example, an apparatus for performing the above-described processing is installed at a position indicated by A in FIG. 2 to perform processing or inspection on a portion of the web adsorbed by the suction roll.
In recent years, the accuracy and uniformity of the processing are required to be greatly improved. In the technique shown in the prior art, when the web is considered to be a sucked surface, the web is uniformly sucked due to the difference in the roll material and the presence of the through-hole portion, It is difficult to perform various processes, and none of them can be solved by the prior art.
The problem to be solved by the present invention is to improve the suction roll so that the web is kept in a very uniform and smooth state in web suction, transport guidance and processing.
吸着ロールを一定の連通した微細開気孔を持つ筒状多孔質セラミック焼結体とすることにより、前 記課題を解決した。またウェブと接する面の面粗度を十分低くすることができ、スルーホールタイプのような大きな凹凸が無いために、ウェブを均一な状態で保持、搬送、処理をすることができる。
本発明はロール内部を大気圧以下に減圧することによりロール表面で帯状のウェブを吸着して搬送案内する吸着ロールであって、少なくとも帯状のウェブと接する部分が筒状多孔質セラミック焼結体からなる吸着ロールである。ウェブと接する 部分が筒状多孔質セラミック焼結体であり、ウェブと接する微細気孔のすべてから均等に吸着ができるために、送り中のウェブを均一な状態で送ることが可能に なる。このことは、一部を多孔体で製作したロールや、スルーホールタイプの吸着ロールでは不可能であった。また、セラミック質であるために、長期に渡る使用でも磨耗や腐食の影響がほとんどない。さらに、高温中の用途でもセラミックスは耐熱性に優れるために好適する。
The problem described above was solved by making the adsorbing roll a cylindrical porous ceramic sintered body having fine open pores that are in constant communication. Further, the surface roughness of the surface in contact with the web can be made sufficiently low, and since there is no large unevenness as in the through-hole type, the web can be held, transported and processed in a uniform state.
The present invention is an adsorption roll that adsorbs and conveys a belt-like web on the roll surface by reducing the pressure inside the roll to below atmospheric pressure, and at least a portion in contact with the belt-like web is formed from a cylindrical porous ceramic sintered body. It is an adsorption roll. Since the portion in contact with the web is a cylindrical porous ceramic sintered body and can be uniformly adsorbed from all the fine pores in contact with the web, the web being fed can be fed in a uniform state. This is not possible with a roll partially made of a porous body or a through-hole type adsorption roll. Moreover, since it is ceramic, there is almost no influence of wear and corrosion even if it is used for a long time. Furthermore, ceramics are suitable for high temperature applications because of their excellent heat resistance.
吸着ロールはロールの半径と前記筒状多孔質セラミック焼結体の厚さの比が10以上であり、かつ、筒状多孔質セラミック焼結体の厚さが0.5mm以上であることが好ましい。筒状多孔質セラミック焼結体で内部の減圧によりウェブを吸着する場合は、その厚さが厚いほど吸着力は下がり、逆に薄ければ吸着力は上がる。吸着ロール半径と筒状多孔質セラミック焼結体の比を10以上とし、筒状多孔質セラミック焼結体の厚さを一定以下の厚さとする ことにより、微細気孔を有する筒状多孔質セラミック焼結体で十分な吸引力が得られる。比が10未満であれば、吸着力が落ちる場合がある。また、厚さが0.5mmより薄い場合は筒状多孔質セラミック焼結体の製造が難しくなるばかりでなく、剛性がそれに応じて下がるために破損しやすい。そのために少なくとも0.5mm以上の厚さがより望ましい。
Suction roll ratio of the thickness of the radius and the cylindrical porous ceramic sintered body of the roll is not less than 10, and it is preferable that the thickness of the cylindrical porous ceramic sintered body is 0.5mm or more . When a web is adsorbed by a reduced pressure inside the cylindrical porous ceramic sintered body, the adsorption force decreases as the thickness increases, and conversely, the adsorption force increases as the thickness decreases. By setting the ratio of the radius of the adsorption roll and the cylindrical porous ceramic sintered body to 10 or more and the thickness of the cylindrical porous ceramic sintered body to a certain thickness or less, the cylindrical porous ceramic sintered body having fine pores is obtained. Sufficient suction power can be obtained by ligation. If the ratio is less than 10, the adsorptive power may decrease. In addition, when the thickness is less than 0.5 mm, not only is it difficult to produce a cylindrical porous ceramic sintered body, but the rigidity is lowered accordingly, so that it is easily damaged. Therefore, a thickness of at least 0.5 mm or more is more desirable.
前記筒状多孔質セラミック焼結体の少なくともウェブと接する部分の面粗さは、算術平均粗さRaが1.5μm以下かつ最大高さRzが15μm以下である前記吸着ロールであることが特によい。ウェブを吸着し、その面を平滑かつ均一に保つためには、中心線平均粗さRaが 1.5μm以下、最大面粗さRzが15μm以下とすることにより、よりその効果が高まる。これは、ウェブの厚さが薄くなると、吸着時の吸着ロールの面状態がウェブに転写されるために、十分低い面粗さが必要となるためである。薄いフィルムを吸着する場合はRaが1.5μm以下でRz15μm以下が望ましい。なお、前記RaおよびRzの値は、JIS規格2001年度版に準じた値である。
Surface roughness of at least a portion in contact with the web of the tubular porous ceramic sintered body, it is particularly good arithmetic average roughness Ra of said suction roll 1.5μm or less and the maximum height Rz is 15μm or less . In order to adsorb the web and keep the surface smooth and uniform, the effect is further enhanced by setting the center line average roughness Ra to 1.5 μm or less and the maximum surface roughness Rz to 15 μm or less. This is because when the thickness of the web is reduced, the surface state of the suction roll at the time of suction is transferred to the web, so that a sufficiently low surface roughness is required. When adsorbing a thin film, Ra is preferably 1.5 μm or less and Rz is 15 μm or less. The values of Ra and Rz are values according to the JIS standard 2001 version.
また、筒状多孔質セラミック焼結体の少なくともウェブと接する外周部の平均気孔径が
2μm以下(0は含まず)で気孔率が15〜40%であり、気孔により少なくとも外周面と内周面で通気可能である前記吸着ロールであることが好ましい。多孔質セラミックス焼結体の気孔率は、15%未満であれば、連続した開気孔が得るのが難しく、吸着力を上げるためには、より性能の高い真空ポンプなどが必要となる。反対に40%よりも大きければ、ウェブと接していない部分からの圧力のリークが起こりやすくなり、吸着面の外周面に対する面積比率を、一定以上に高くする必要が生じる。また、筒状多孔質セラミック焼結体は、連続した開気孔が焼結体全体に均一に存在することにより、表面全体を均等に吸着することができる。また、この場合の平均気孔径が2.0μm以下と十分に小さい場合は、表面全面にウェブを吸着した状態でなくとも、たとえば表面積の1/10程度の面積を吸着した場合においても、それ以外の部分からのリークが極めて少なく、ほとんど無視できる。一般に、吸着ロールの場合は筒状多孔質セラミック焼結体表面積の1/3〜1/2程度の面積にウェブが吸着されるために、十分な吸着力が確保できる。これが平均気孔径が2.0μmを越えると、ウェブを吸着していない部分からのリークが起こるために、十分な吸着力を得るのが難しくなる。なお、前記平均気孔径および気孔率は水銀圧入法にて測定した値である。
The cylindrical porous ceramic sintered body has an average pore diameter of 2 μm or less (excluding 0) at the outer peripheral portion in contact with the web and a porosity of 15 to 40%. At least the outer peripheral surface and the inner peripheral surface are formed by the pores. it is preferable in that said suction roll is breathable. If the porosity of the porous ceramic sintered body is less than 15%, it is difficult to obtain continuous open pores, and a higher performance vacuum pump or the like is required to increase the adsorption power. On the other hand, if it is larger than 40%, pressure leaks easily from a portion not in contact with the web, and the area ratio of the suction surface to the outer peripheral surface needs to be higher than a certain level. In addition, the cylindrical porous ceramic sintered body can uniformly adsorb the entire surface because the continuous open pores exist uniformly in the entire sintered body. Further, in this case, when the average pore diameter is sufficiently small as 2.0 μm or less, even when the web is not adsorbed on the entire surface, for example, even when an area of about 1/10 of the surface area is adsorbed, There is very little leakage from this part and it can be almost ignored. Generally, in the case of an adsorbing roll, the web is adsorbed in an area of about 1/3 to 1/2 of the surface area of the cylindrical porous ceramic sintered body, so that a sufficient adsorbing force can be secured. If the average pore diameter exceeds 2.0 μm, leakage from a portion where the web is not adsorbed occurs, making it difficult to obtain a sufficient adsorbing force. The average pore diameter and porosity are values measured by mercury porosimetry.
前記筒状多孔質セラミック焼結体の材質はアルミナ、ジルコニア、シリカ、炭化珪素、イットリア、マグネシア、炭化チタン、窒化チタン、炭化チタン、炭化タングステン、窒化珪素、窒化アルミのいずれか1種または2種以上を基とするセラミックスより選択できる。これらのセラミックスは入手の容易さ、製造費用の低さ、剛性、耐摩耗性、耐食性、耐熱性などの観点より、本発明の吸着ロールの筒状多孔質セラミック焼結体に用いるのに特に適している。製造については、原料粉末に有機物を分散させて焼結する方法や、完全に緻密化が起こらないように原料粉末、組成、焼結温度などを調整することなどがあげられる。
The cylindrical porous ceramic sintered body is made of one or two of alumina, zirconia, silica, silicon carbide, yttria, magnesia, titanium carbide, titanium nitride, titanium carbide, tungsten carbide, silicon nitride, and aluminum nitride. It can be selected from ceramics based on the above . These ceramics are particularly suitable for use in the cylindrical porous ceramic sintered body of the suction roll of the present invention from the viewpoints of availability, low manufacturing cost, rigidity, wear resistance, corrosion resistance, heat resistance, etc. ing. As for the production, there are a method in which an organic substance is dispersed in a raw material powder and sintering, and a raw material powder, a composition, a sintering temperature and the like are adjusted so that complete densification does not occur.
また、筒状多孔質セラミック焼結体の筒内に、略円筒状の補強体が嵌合し、筒状多孔質セラミック焼結体の内周部と補強体の外周部とが一体に接合されている前述の吸着ロールはより望ましい。また、さらに本発明は補強体の材質が筒状多孔質セラミック焼結体よりも気孔率または平均気孔径の少なくとも一方、もしくは両方が高い多孔質セラミック焼結体前記吸着ロールとすることが特に好ましい。これまでに述べてきた筒状多孔質セラミック焼結体の厚さが、吸引力の必要性、ロールの大きさ、剛性、製造費用、設計の面などから十分な強度が得られない場合に用いることができる。筒状多孔質セラミック焼結体の内面(ロールの中心)側に略円筒状の補強体を設けることにより、その欠点を解消することができる。この模式図を図1に示す。略円筒状の補強体には、減圧をウェブと接する面まで伝えるための溝や切欠部分を設けるか、補強体そのものを多孔質体とすることにより、負圧をウェブとの接触面まで及ぼすことができる。補強体そのものを多孔体質とする場合は、筒状多孔質セラミック焼結体よりも、少なくとも気孔率か平均気孔径のいずれかが大きい、できれば両方が大きい材質が好ましい。このことにより、補強体を流れる気体の流量が筒状多孔質セラミック焼結体よりも大きくなるために、溝や切 欠部分を設けることなく、内部の加減圧が支障なく筒状多孔質セラミック焼結体まで伝わる。気孔率も平均気孔径も筒状多孔質セラミック焼結体より小さい材質を補強体とした場合は、図1に示すように溝や切欠部分を設ける必要がある。
前記補強体の熱膨張係数と前記筒状多孔質セラミック焼結体の熱膨張係数との差が1.0×106(K−1)以下であることが望ましい。使用温度が常温でない場合や、環境によって変化する場合、筒状多孔質セラミック焼結体と補強体はその熱膨張係数の差によっては、接合が外れたり、応力により破壊したりする。本発明のように熱膨張係数の差を1×10−6(K−1)以下と小さい組合せにすることにより、これらの不具合は起こりにくくなる。
Further, in the cylinder of the cylindrical porous ceramic sintered body, a substantially cylindrical reinforcing body is fitted, the inner peripheral portion of the cylindrical porous ceramic sintered body and the outer peripheral portion of the reinforcing member is joined together The aforementioned adsorbing roll is more desirable . It is particularly preferred invention further to at least one, or both a high porous ceramic sintered body the suction roll of the porosity or average pore diameter than the material the tubular porous ceramic sintered body of the reinforcement member . Used when the thickness of the cylindrical porous ceramic sintered body described so far cannot provide sufficient strength due to the necessity of suction force, roll size, rigidity, manufacturing cost, design, etc. be able to. By providing a substantially cylindrical reinforcing body on the inner surface (center of roll) side of the cylindrical porous ceramic sintered body, the disadvantage can be solved. This schematic diagram is shown in FIG. The substantially cylindrical reinforcing body is provided with a groove or notch for transmitting reduced pressure to the surface in contact with the web, or the reinforcing body itself is made porous so that negative pressure is exerted on the contact surface with the web. Can do. When the reinforcing body itself is made porous, a material having at least either a porosity or an average pore diameter larger than that of the cylindrical porous ceramic sintered body is preferable. As a result, since the flow rate of the gas flowing through the reinforcing body is larger than that of the cylindrical porous ceramic sintered body, the internal porous pressure can be reduced without any trouble without providing grooves and notches. It is transmitted to the union. In the case where the reinforcing body is made of a material whose porosity and average pore diameter are smaller than the cylindrical porous ceramic sintered body, it is necessary to provide grooves and notches as shown in FIG.
Wherein it is desired difference in thermal expansion coefficient of the reinforcing member and the thermal expansion coefficient of the tubular porous ceramic sintered body is 1.0 × 10 6 (K -1) or less. When the operating temperature is not room temperature or changes depending on the environment, the cylindrical porous ceramic sintered body and the reinforcing body are disconnected or broken by stress depending on the difference in thermal expansion coefficient. By making the difference in thermal expansion coefficient as small as 1 × 10 −6 (K −1 ) or less as in the present invention, these problems are less likely to occur.
前記補強体を用いる場合は、補強体の材質が筒状多孔質セラミック焼結体と同種のセラミックスを基とすることが望ましい。筒状多孔質セラミック焼結体と補強体が同種のセラミックス基で製作することにより、両者の熱膨張差をより小さくすることができる。熱膨張差が小さければ、常温以外の環境下で使用した場合でも、両者の剥離や破損、変形などをより抑えることが可能である。
例としては、たとえば筒状多孔質セラミック焼結体が微細で連通した開気孔を持つアルミナセラミックスと、補強体である緻密なアルミナセラミックスと組み合わせたり、筒状多孔質セラミック焼結体を微細な気孔を有する炭化珪素セラミックスとし、補強体が比較的大きな連通した気孔を有する多孔質炭化珪素セラミックスという組み合わせなども可能である。
また前記一体に接合する方法では、ガラス系または有機物系いずれかの接着剤にて接着することが望ましい。筒状多孔質セラミック焼結体と補強体とを一体とするには、焼きば め、冷やしばめ、一体焼結、拡散接合などの手段が取れるが、最も適しているのはガラス系、セラミック系または有機物系の接着剤を使った一体化である。他の方法と比較して、一体化工程での失敗が少なく、費用面や製造のしやすさでも最も好ましい。また、使用上では使用温度がたとえば200℃と高い場合でも、ガラス系の接着剤や高温まで使用できる有機物系の接着剤であれば使用することができる。
When the reinforcing body is used, it is desirable that the material of the reinforcing body is based on the same kind of ceramic as the cylindrical porous ceramic sintered body. By manufacturing the cylindrical porous ceramic sintered body and the reinforcing body with the same kind of ceramic base, the difference in thermal expansion between them can be further reduced. If the difference in thermal expansion is small, even when used in an environment other than room temperature, it is possible to further suppress peeling, breakage, deformation, etc. of both.
For example, for example, a cylindrical porous ceramic sintered body is combined with alumina ceramics having fine pores and fine pores and a dense alumina ceramic as a reinforcing body, or a cylindrical porous ceramic sintered body is combined with fine pores. A combination of silicon carbide ceramics having a porous structure and porous silicon carbide ceramics having relatively large communicating pores is also possible.
Further, in the method of joining together, it is desirable to bond with either a glass-based or organic-based adhesive . In order to integrate the cylindrical porous ceramic sintered body and the reinforcing body, methods such as shrink fitting, cold fitting, integral sintering, and diffusion bonding can be taken, but the most suitable are glass-based, ceramic Integration using organic or organic adhesives. Compared to other methods, there are few failures in the integration process, and it is most preferable in terms of cost and ease of manufacturing. In use, even when the use temperature is as high as 200 ° C., for example, a glass-based adhesive or an organic-based adhesive that can be used up to a high temperature can be used.
前記補強体は、円筒形状の一部を削り取った形状であり、その削り取った部分の少なくとも一部が、ロール内部の減圧を筒状多孔 質セラミック焼結体のウェブと接する部分に及ぼし吸着する経路の一部であることが望ましい。補強体に緻密質の 材料を使った場合は、略円筒状の補強体をたとえば図1に示すように外周部を一部削り取り、スリットを入れることにより、ロール内部から筒状多孔質セラミック焼結体のウェブと接する面に負圧を及ぼすことができる。 The reinforcing body has a shape obtained by scraping a part of a cylindrical shape, and at least a part of the shaved part applies a reduced pressure inside the roll to a part in contact with the web of the cylindrical porous ceramic sintered body and adsorbs the path. It is desirable to be a part of When a dense material is used for the reinforcing body, a cylindrical porous ceramic sintered body is sintered from the inside of the roll by cutting off a part of the substantially cylindrical reinforcing body, for example, as shown in FIG. Negative pressure can be exerted on the surface of the body that contacts the web.
ウェブを吸着して搬送案内する吸着ロールに、本発明の吸着ロールを用いることにより、下記1.〜3.の少なくとも1つの課題を解決できる。
1.吸着した部分のウェブ全体を均一に吸着することができる。そのために、ウェブに皺が生じたり、変形するといった問題が解決できる。また、吸着するウェブがロールの表面をすべて覆う必要がなく、ウェブ形状や吸着形態の自由度が高い。
2.従来の多孔質セラミックを用いた吸着ロールなどと比較して、吸着ロール表面の面粗さを低くすることができる。そのため、吸着面の凹凸(面粗度)が、ウェブに転写される現象を、小さく抑えることができる。
3.前記1及び2の特徴より、ウェブの吸着、送りの際に変形が無く、面粗度もよく均一な吸着ができる。そのために、吸着、搬送案内の際に印刷、光学的な検査、塗布、転写などの処理を高品位にて行なうことができる。
By using the suction roll of the present invention for the suction roll that sucks and guides the web, the following 1. ~ 3. Can solve at least one of the following issues.
1. The entire web of the adsorbed part can be adsorbed uniformly. As a result, problems such as wrinkles and deformations in the web can be solved. Moreover, the web to adsorb | suck does not need to cover all the surfaces of a roll, and the freedom degree of a web shape and an adsorption | suction form is high.
2. The surface roughness of the surface of the suction roll can be reduced as compared with a suction roll using a conventional porous ceramic. Therefore, the phenomenon that the unevenness (surface roughness) of the suction surface is transferred to the web can be suppressed to a small level.
3. Due to the
本発明を実施するための最良の形態を以下に示す。
まず、吸着部および補強体以外の端部5は、図3を用いて説明するが、鉄材をはじめとする金属材料やセラミック材料にて製作することができる。その際には図4のように両端が一体化している構造も含めて、一般的な形態で製作すればよい。
ロールの内部を負圧とすることに関しては、従来用いられている一般的な方法をいずれも用いることができる。代表的な形態としては図3〜図6に示すように、ロールの中心部付近の空孔部分から、ロールの端部の任意の位置に、真空ポンプなどの減圧装置で内部の気体が移動できる状態に設ければよい。
The best mode for carrying out the present invention will be described below.
First, the
As for the negative pressure inside the roll, any conventionally used general method can be used. As a typical form, as shown in FIGS. 3 to 6, the internal gas can be moved from the hole portion near the center of the roll to an arbitrary position at the end of the roll by a decompression device such as a vacuum pump. What is necessary is just to provide in a state.
筒状多孔質セラミック焼結体の端部への固定は、接着剤による固定、ボルト締めなどの機械的手段による固定など、特に制限はない。端部と筒状多孔質セラミック焼結体が使用中に動かないよう固定されていれば問題ない。 There are no particular limitations on the fixing of the cylindrical porous ceramic sintered body to the end, such as fixing with an adhesive or fixing by mechanical means such as bolting. There is no problem if the end portion and the cylindrical porous ceramic sintered body are fixed so as not to move during use.
筒状多孔質セラミック焼結体は図7に示すような筒状のものを用いる。筒状多孔質セラミック焼結体を得るには、まずセラミックスの原料粉末と成形用バインダーとを乾式または湿式にて混合し、所望の粉末を得た上で、円筒状に成形する。この成形は、円柱状の中芯の周りに粉末をつめてラバープレスまたは冷間静水圧プレスすることにより得られるが、このほかに押し出し成形を行なうことができる。形状によっては金型プレスでもよい。
次に、プレス体に中間加工を施した後、脱脂、焼結を行なう。脱脂は前記成型用バインダーを除去するためであり、脱脂だけを行なってその後に焼結を行なっても、脱脂と焼結を連続的に行なってもどちらでもかまわない。そのセラミック材料に合わせた焼結温度で焼結を行なう。
得られた焼結体を、所望の形状、寸法となるように機械加工を行なう。外径、内径、端部と大きく分けて3箇所の加工が必要となるが、これらは円筒研削盤、内面研削盤、平面研削盤、マシニングセンタなど各種の加工機械にて行なう。この際に、外形は所望の寸法より若干大きめに仕上げておく。
次に、別に準備したロール端部の部材と、筒状多孔質セラミック焼結体を一体化する。このロール端部の部材は、負圧を生じさせる真空ポンプなどとロール中央部を接続するための部分を少なくとも一箇所含む。一体化にはどのような方法も取れるが、筒状多孔質セラミック焼結体端部およびその周辺を接着剤による固定を行なうか、またはボルトなどを使って機械的に固定してもよい。
A cylindrical porous ceramic sintered body as shown in FIG. 7 is used. In order to obtain a cylindrical porous ceramic sintered body, first, a ceramic raw material powder and a molding binder are mixed in a dry or wet manner to obtain a desired powder, and then molded into a cylindrical shape. This molding can be obtained by packing the powder around the cylindrical core and pressing it with a rubber press or cold isostatic pressing. However, it is possible to perform extrusion molding. Depending on the shape, a die press may be used.
Next, after intermediate processing is performed on the pressed body, degreasing and sintering are performed. Degreasing is for removing the molding binder. Either degreasing and subsequent sintering may be performed, or degreasing and sintering may be performed continuously. Sintering is performed at a sintering temperature suitable for the ceramic material.
The obtained sintered body is machined so as to have a desired shape and size. Three major parts are required for the outer diameter, inner diameter, and end, and these are performed by various processing machines such as a cylindrical grinder, an internal grinder, a surface grinder, and a machining center. At this time, the outer shape is finished slightly larger than the desired dimension.
Next, a separately prepared roll end member and a cylindrical porous ceramic sintered body are integrated. The member at the end of the roll includes at least one portion for connecting the central portion of the roll with a vacuum pump that generates a negative pressure. Any method can be used for the integration, but the end of the cylindrical porous ceramic sintered body and its periphery may be fixed with an adhesive or may be fixed mechanically using a bolt or the like.
最後に、ロール端部部材などの部材と一体化した後に、ロール全体を回転させながら、筒状多孔質セラミック焼結体外周部分の研削加工を行なう。こうすることにより、ロール全体と筒状多孔質セラミック焼結体の真円度、円筒度および同軸度を十分高くすることができる。
Finally, after integrating with a member such as a roll end member, the outer peripheral portion of the cylindrical porous ceramic sintered body is ground while rotating the entire roll. By doing so, the roundness, cylindricity and coaxiality of the entire roll and the cylindrical porous ceramic sintered body can be made sufficiently high.
前記補強体を別に用いる場合には、若干工程が異なる。筒状多孔質セラミック焼結体の内面研削を行った後に、別に準備しておいた補強体と一体化する工程が増える。一体化には焼きばめ、冷やしばめ、拡散接合、一体焼結などの手段をとることができるが、接着剤にて一体化する方法が最も簡単に行なうことができる。 When the reinforcing body is used separately, the process is slightly different. After the internal grinding of the cylindrical porous ceramic sintered body, the number of steps for integrating with a separately prepared reinforcing body increases. For integration, means such as shrink fitting, cold fitting, diffusion bonding, and integral sintering can be used, but the method of integrating with an adhesive can be most easily performed.
一体化した後に、筒状多孔質セラミック焼結体と合わせて端部や内面の加工を行なう。この後は補強体を用いない場合と同様である。
After the integration, the end portion and the inner surface are processed together with the cylindrical porous ceramic sintered body. After this, it is the same as the case where a reinforcing body is not used.
以下実施例において、発明の具体例を数例示すが、製造方法や使用方法などについては、これらに限定されるものではない。
In the following examples, several specific examples of the invention will be described, but the production method, usage method, and the like are not limited thereto.
(実施例1)
1.筒状多孔質セラミック焼結体の製造
原料粉末として0.25%のマグネシア成分を含むアルミナ粉末を2種用意した。それぞれの平均粒子径は(a)2μmと(b)0.3μmである。
Example 1
1. Production of Cylindrical Porous Ceramic Sintered Body Two types of alumina powder containing 0.25% magnesia component were prepared as raw material powders. The average particle diameter of each is (a) 2 μm and (b) 0.3 μm.
これらの粉末を(a)が80質量%、(b)が20質量%の比率で、メタノールを溶媒と成型用バインダーであるポリエチレングリコールをボールミルにて均一に混合し、混合粉末を得た。乾燥後に、ゴム袋に鋼鉄の中芯と、その回りに前記混合粉末を充填し、密封した後に冷間静水圧プレス成形を行い、円筒状のプレス体を得た。 These powders were mixed at a ratio of 80% by mass for (a) and 20% by mass for (b), and methanol was uniformly mixed with a solvent and polyethylene glycol, which was a molding binder, to obtain a mixed powder. After drying, the rubber core was filled with the steel core and the mixed powder around it, and after sealing, cold isostatic pressing was performed to obtain a cylindrical press body.
プレス体を脱脂、焼結兼用炉に投入し、大気雰囲気にて1、400℃にて脱脂、焼結を行なった。焼結体を観察したところ、微細な開気孔が均一に存在していた。気孔を測定したところ、平均気孔径は0.5μmであった。また、気孔率は20%であった。 The press body was put into a degreasing and sintering furnace, and degreased and sintered at 1,400 ° C. in an air atmosphere. When the sintered body was observed, fine open pores existed uniformly. When the pores were measured, the average pore diameter was 0.5 μm. The porosity was 20%.
この焼結体の端面、内面、外面をそれぞれ円筒研削盤、内面研削盤、円筒研削盤を用いて所望の円筒形状のアルミナ基の多孔質セラミック焼結体を得た。
2. ロールの端部
前記1.とは別に図3の5に示すように、クロムモリブデン鋼でロールの端部の部材を準備した。部材には一箇所の真空引き用の穴6を設けた。
3. 組み立て
前記1.及び2.にて準備した筒状多孔質セラミック焼結体1およびロール端部の部材5をエポキシ系の接着剤にて、筒状多孔質セラミック焼結体の端部をロール端部の部材に接着した後に1日間乾燥させた。両者は強固に一体化しており、模式図3に示す吸着ロールを得た。この後、一体化した状態で円筒研削盤にて筒状多孔質セラミック焼結体の外周部を仕上げ研削し、本発明の吸着ロールを得た。この吸着ロールをNo.1とした。
A desired cylindrical alumina-based porous ceramic sintered body was obtained by using a cylindrical grinder, an internal grinder, and a cylindrical grinder on the end face, inner face, and outer face of the sintered body, respectively.
2. End of roll Separately, as shown in 5 of FIG. 3, a member at the end of the roll was prepared from chromium molybdenum steel. The member was provided with one
3.
本発明の吸着ロールに対する比較用のロールとして、多数の0.5mmのスルーホールを表面からロール内面に設けた「スルーホール」タイプの吸着ロールを用い、これをNo.11とした。 As a comparative roll for the suction roll of the present invention, a “through hole” type suction roll in which a number of through holes of 0.5 mm are provided from the surface to the inner surface of the roll is used. It was set to 11.
また、金属ロール表面に多数の多孔質セラミックス(アルミナを使用)を設けた特許文献2に相当するロールをNo.12とした。
Further, a roll corresponding to Patent
No.1、No.11およびNo.12のロールを用いて、図2に示すように、厚さ0.025mmのポリイミドをウェブ9として、吸着、搬送案内中に別のロールによるポリイミドへの金属含有インクでパターン印刷処理を行なった。この場合の図2中のAで示される部分には、印刷用のロールが入る。この印刷の形態を図8に示す。
No. 1, no. 11 and no. As shown in FIG. 2, using 12 rolls, a pattern printing process was performed with a metal containing ink on polyimide by another roll during suction and conveyance guidance, using polyimide having a thickness of 0.025 mm as a
本発明のNo.1のロールは、全体を均一に保持するために、印刷されたパターンに不具合はなく、正確なパターン印刷を長時間にわたり変わらず得ることができた。 No. of the present invention. In order to keep the entire roll uniformly, the roll No. 1 had no defect in the printed pattern, and an accurate pattern printing could be obtained over a long period of time.
比較例であるNo.11のロールは、スルーホールにあたる部分を中心に印刷に数〜10μm程度のパターンのゆがみが発生しており、高精度な印刷には適していないことが分かった。スルーホールの周辺はスルーホールに引き込まれて引っ張られるために、このゆがみが起こったと考えられる。 No. which is a comparative example. It was found that the roll No. 11 was not suitable for high-precision printing because a pattern distortion of about several tens to 10 μm occurred in printing around the portion corresponding to the through hole. It is thought that this distortion occurred because the periphery of the through hole was pulled into the through hole and pulled.
同じく比較例であるNo.12では、多孔質セラミックスに吸引されている部分と、そうでない部分にウェブの進行方向に波打ったような印刷ムラが見られた。これは、多孔質セラミックに吸着されている部分がそうでない部分を引っ張るために起こったと考えられる。
(実施例2)
吸着ロールの半径及び、筒状多孔質セラミック焼結体の厚さを以下の表1に示すよう設定し、ロールを得た。筒状多孔質セラミック焼結体の材質はすべてアルミナ−20質量%炭化チタンとした。いずれも気孔率は40%、平均気孔径は2μmである。
Similarly, in the comparative example No. In No. 12, printing unevenness such as waving in the advancing direction of the web was observed in the portion sucked by the porous ceramic and the portion not. This is thought to have occurred because the portion adsorbed by the porous ceramic pulled the portion that was not.
(Example 2)
The radius of the adsorption roll and the thickness of the cylindrical porous ceramic sintered body were set as shown in Table 1 below to obtain a roll. All the materials of the cylindrical porous ceramic sintered body were alumina-20 mass% titanium carbide. In both cases, the porosity is 40%, and the average pore diameter is 2 μm.
ロール端部の部材や他の寸法は同じ条件であり、ロールの半径と筒状多孔質セラミック焼結体の厚さの設定を表1に示す。これらのロールを用いて厚さ10μmの金箔を吸着、搬送案内し、その吸着状態を調べた。 The roll end members and other dimensions are the same, and Table 1 shows the setting of the roll radius and the thickness of the cylindrical porous ceramic sintered body. Using these rolls, a gold foil having a thickness of 10 μm was adsorbed, conveyed and guided, and the adsorbed state was examined.
表1の結果に示すように、ロールの半径と筒状多孔質セラミック焼結体の厚さの比が10以上であるロールNo.2、No.3、No.4、No.6、No.7は良好な吸着力が得られた。
As shown in the results of Table 1, a roll No. having a ratio of the roll radius to the thickness of the cylindrical porous ceramic sintered body of 10 or more was used. 2, No. 3, no. 4, no. 6, no. For No. 7, good adsorption force was obtained.
これに対して、その比が10未満であるロールNo.5は、筒状多孔質セラミック焼結体の厚さが厚いために、吸着力は吸着、搬送案内可能な程度ではあったものの、他のロールには及ばなかった。 On the other hand, the roll No. whose ratio is less than 10. No. 5 has a thickness of the cylindrical porous ceramic sintered body, so that the adsorbing force was able to adsorb and convey and guide, but did not reach other rolls.
また、筒状多孔質セラミック焼結体の厚さが、1mmより薄いロールNo.2については、吸着状態は良好であったが、薄いために製造時に割れや欠けが起こりやすく、それを解消するために加工能率を落として加工する必要があった。製造費用の面では1mm以上のものが安価に製作可能であった。
(実施例3)
本発明の、筒状多孔質セラミック焼結体を気孔率が15%で外周表面の開気孔の平均気孔径が0.4μmである窒化珪素とした吸着ロールを製作した。筒状多孔質セラミック焼結体のウェブを吸着する部分の面粗さを加工時の砥石の番手などを変えることによって表2に示すよう、それぞれに変えて試験を行なった。この吸着ロールにて、ポリエチレン系で厚さ10μmのウェブを吸着、送り中に図9に示すような形態でスクリーン印刷処理を行なった。棒状の塗布工具10は、先端から速乾性のスラリー11がウェブの幅方向に対して均等に出てくるようにしてある。
Also, the roll porous ceramic sintered body having a thickness of roll No. For No. 2, the adsorbed state was good, but since it was thin, cracks and chips were likely to occur during production, and it was necessary to process with reduced processing efficiency to eliminate it. In terms of manufacturing cost, a product of 1 mm or more could be manufactured at a low cost.
(Example 3)
An adsorbing roll made of silicon nitride having a porosity of 15% and an average pore diameter of open pores on the outer peripheral surface of the cylindrical porous ceramic sintered body of the present invention was manufactured. The test was performed by changing the surface roughness of the portion of the cylindrical porous ceramic sintered body that adsorbs the web as shown in Table 2 by changing the count of the grindstone during processing. A screen printing process was performed in the form shown in FIG. 9 while sucking and feeding a polyethylene-based web having a thickness of 10 μm with this suction roll. The rod-shaped
乾燥後のウェブを細かく切り、AFM(原子間力顕微鏡)にて表面の状態を観察した。 The dried web was cut into small pieces, and the surface condition was observed with an AFM (atomic force microscope).
表2に示す結果のように、中心線平均粗さRa≦1.5μm、最大高さRz≦15μmの吸着ロールがムラの見られない、良好な塗布が行なえることがわかった。面粗さがこれよりも大きいと、筒状多孔質セラミック焼結体の表面の凹凸が、ウェブにも転写されることで、塗布後のウェブの状態に差ができたと考えられる。
本発明の吸着ロールで請求項3の条件を満たすものは、極めて微小な面の状態を制御したい場合に特に有効であった。ただし、一般的な精度の塗布や印刷の場合は試料No.28、No.29程度でも使用に問題ない場合が多い。
(実施例4)
実施例1では0.25%のマグネシア成分を含むアルミナを筒状多孔質セラミック焼結体として用いたが、請求項5に示すいずれのセラミック材料(アルミナ、ジルコニア、シリカ、炭化珪素、イットリア、マグネシア、炭化チタン、窒化チタン、炭化タングステン)でも、気孔の状態を制御することにより同様の吸着ロールを得ることができた。
(実施例5)
アルミナ基の筒状多孔質セラミック焼結体1の厚さを1mmとし、その内面側に補強体2を一体に接合した吸着ロールを製作した。アルミナ基の筒状多孔質セラミック焼結体1の気孔率は30%、平均気孔径は1.0μmである。この模式図を図1に示す。
補強体2として用いたのは円筒状の緻密質(密度99%)のアルミナ焼結体であり、その外形は筒状多孔質セラミック焼結体1の内径より20μm小さくした。この円筒状の補強体の外周にあたる部分は、一部を除いて研削にて削り取り、各角に円弧が残った5角筒形状とし、さらに内面からの減圧を筒状多孔質セラミック焼結体に伝達できるように、内面から外面まで複数のスリット13を設けた。この補強体の5つの円弧12にそれぞれに有機接着剤を塗布し、筒状多孔質セラミック焼結体1の内面に接着し、乾燥した。
一体化したものに、焼入れ鋼製の端部をさらに接着することにより、補強体を有する吸着ロールを得た。
補強体を有する吸着ロールの利点を以下に示す。
1.補強体により補強されているために、吸着ロールに生じるたわみなどの変形が少ない。そのために、吸着ロールが長い場合でも、たわみを最小限に抑えることができる。また、補強があるために、更なる吸着力を必要とする場合などは、筒状多孔質セラミック焼結体を薄くすることも可能となる。
2.補強体と筒状多孔質セラミック焼結体の熱膨張係数が小さいために、温度変化などによる変形や破壊が起こらない。本実施例では筒状多孔質セラミック焼結体の熱膨張係数は7.5×10−6(K−1)であり、補強体のそれは7.4×10−6(K−1)とほぼ同じであった。そのために、吸着ロールの焼入れ鋼端部が温度変化により収縮するのを妨げ、熱膨張差によって生じる変形や筒状多孔質セラミック焼結体の割れを大幅に緩和することができる。逆に熱膨張差が1.0×10−6(K−1)以上と大きくなれば、補強体と筒状多孔質セラミック焼結体の熱膨張差により、両者の分離や、筒状多孔質セラミック焼結体の割れなどにつながるために、熱膨張差は1.0×10−6(K−1)以下がより望ましい。
3.補強体は緻密質のセラミックスも用いることができるために、曲げやねじれなどの応力から筒状多孔質セラミック焼結体を保護するのが容易になる。
As shown in the results in Table 2, it was found that the adsorbing roll having the center line average roughness Ra ≦ 1.5 μm and the maximum height Rz ≦ 15 μm can be satisfactorily applied with no unevenness. If the surface roughness is larger than this, it is considered that the unevenness on the surface of the cylindrical porous ceramic sintered body is also transferred to the web, thereby making a difference in the state of the web after coating.
The suction roll of the present invention that satisfies the conditions of
Example 4
In Example 1, alumina containing 0.25% magnesia component was used as the cylindrical porous ceramic sintered body. However, any ceramic material shown in claim 5 (alumina, zirconia, silica, silicon carbide, yttria, magnesia) was used. , Titanium carbide, titanium nitride, tungsten carbide), the same adsorption roll could be obtained by controlling the state of the pores.
(Example 5)
An adsorption roll in which the thickness of the alumina-based cylindrical porous ceramic
A cylindrical dense alumina sintered body (density 99%) was used as the reinforcing
By adhering the end made of hardened steel to the integrated one, an adsorbing roll having a reinforcing body was obtained.
Advantages of the adsorption roll having the reinforcing body are shown below.
1. Since it is reinforced by the reinforcing body, deformation such as deflection generated in the suction roll is small. Therefore, even when the adsorbing roll is long, the deflection can be minimized. Further, since there is reinforcement, the cylindrical porous ceramic sintered body can be made thin when a further adsorption force is required.
2. Since the thermal expansion coefficient of the reinforcing body and the cylindrical porous ceramic sintered body is small, deformation and destruction due to temperature change do not occur. In this example, the thermal expansion coefficient of the cylindrical porous ceramic sintered body is 7.5 × 10 −6 (K −1 ), and that of the reinforcing body is approximately 7.4 × 10 −6 (K −1 ). It was the same. Therefore, the hardened steel end portion of the adsorption roll is prevented from shrinking due to temperature change, and deformation caused by a difference in thermal expansion and cracking of the cylindrical porous ceramic sintered body can be relieved greatly. On the other hand, if the difference in thermal expansion is as large as 1.0 × 10 −6 (K −1 ) or more, the separation between the reinforcing body and the cylindrical porous ceramic sintered body may cause separation or cylindrical porous In order to lead to cracking of the ceramic sintered body, the thermal expansion difference is more preferably 1.0 × 10 −6 (K −1 ) or less.
3. Since the reinforcing body can also be a dense ceramic, it is easy to protect the cylindrical porous ceramic sintered body from stresses such as bending and twisting.
また、この実施例では補強材を5角筒に削り取ったが、筒状多孔質セラミック焼結体と十分に接着できる形状であれば、どのような削り取り方をしてもかまわない。
(実施例6)
実施例5と同様に、アルミナ基の筒状多孔質セラミック焼結体1の厚さを1mmとし、その内面側に補強体2を一体に接合した吸着ロールを製作した。アルミナ基の筒状多孔質セラミック焼結体1の気孔率は30%、平均気孔径は1.0μmである。
この場合の補強体は円筒状の多孔質アルミナ焼結体22であり、この模式図を図10に示す。補強体の気孔率は50%で、平均気孔径は10μmであった。補強体のほうが気孔率、平均気孔径ともに高い。補強体内部の3より減圧を行なうことにより、筒状多孔質セラミック焼結体1は表面にウェブを良好に吸着することができた。
この場合は、緻密質セラミックスを用いた場合と異なり、外形の一部を削り取ることや、溝入れも省くことができる。
In this embodiment, the reinforcing material is cut into a pentagonal cylinder, but any shape may be used as long as it can be sufficiently bonded to the cylindrical porous ceramic sintered body.
(Example 6)
In the same manner as in Example 5, an adsorption roll in which the thickness of the alumina-based cylindrical porous ceramic
The reinforcing body in this case is a cylindrical porous alumina sintered body 22, and a schematic diagram thereof is shown in FIG. The porosity of the reinforcing body was 50%, and the average pore diameter was 10 μm. The reinforcing body has a higher porosity and average pore diameter. By reducing the pressure from 3 inside the reinforcing body, the cylindrical porous ceramic
In this case, unlike the case where dense ceramics are used, part of the outer shape can be cut off and grooving can be omitted.
1 筒状多孔質セラミック焼結体
2 補強体
3 ロール内部の空間
4 円筒状の補強体を削った部分
5 ロール端部
6 真空引き経路
7 ウェブの進行方向を変えるローラー
8 印刷用ロール
9 ウェブ
10 塗布工具
11 塗布されるスラリー
12 接着部
13 真空引き経路となるスリット
14 リング状のスリット(6と常時連通している)
15 印刷されたウェブの部分
22 補強体(多孔質セラミックス)
100 吸着ロール全体
A ウェブを処理する機構が設置される場所
DESCRIPTION OF
15 Printed web portion 22 Reinforcing body (porous ceramic)
100 Whole adsorption roll A Place where a mechanism for processing web is installed
Claims (6)
少なくとも帯状のウェブと接する部分が筒状多孔質セラミック焼結体からなり、
前記筒状多孔質セラミック焼結体の少なくともウェブと接する外周部の平均気孔径が2μm以下(0は含まず)で気孔率が15〜40%であり、
前記多孔質セラミックス焼結体はアルミナ、ジルコニア、炭化珪素、マグネシア、炭化チタン、窒化チタン、炭化チタン、炭化タングステン、窒化珪素、窒化アルミのいずれか1種または2種以上を基とするセラミックスであり、
前記筒状多孔質セラミック焼結体端部に前記筒状多孔質セラミック焼結体とともに回転
する端部部材を有し、
ロールの回転中心付近にロール内部減圧用の通路を有する吸着ロール。 An adsorbing roll that adsorbs and conveys a belt-shaped web on the roll surface by reducing the pressure inside the roll to below atmospheric pressure,
At least the portion in contact with the belt-shaped web is made of a cylindrical porous ceramic sintered body,
The cylindrical porous ceramic sintered body has an average pore diameter of 2 μm or less (excluding 0) and a porosity of 15 to 40% at least in contact with the web.
The porous ceramic sintered body is a ceramic based on one or more of alumina, zirconia, silicon carbide, magnesia, titanium carbide, titanium nitride, titanium carbide, tungsten carbide, silicon nitride, and aluminum nitride. ,
An end member that rotates together with the cylindrical porous ceramic sintered body at the end of the cylindrical porous ceramic sintered body,
An adsorbing roll having a passage for decompression inside the roll in the vicinity of the rotation center of the roll.
前記筒状多孔質セラミック焼結体の筒内で前記筒状多孔質セラミック焼結体の内周部と補強体の外周部とが一体に接合されており、 In the cylinder of the cylindrical porous ceramic sintered body, the inner peripheral part of the cylindrical porous ceramic sintered body and the outer peripheral part of the reinforcing body are integrally joined,
前記補強体の材質が前記筒状多孔質セラミック焼結体と同種のセラミックスを基とする材料である請求項1に記載の吸着ロール。 The suction roll according to claim 1, wherein a material of the reinforcing body is a material based on the same kind of ceramic as the cylindrical porous ceramic sintered body.