JP5249875B2 - インクジェット記録材料 - Google Patents
インクジェット記録材料 Download PDFInfo
- Publication number
- JP5249875B2 JP5249875B2 JP2009187414A JP2009187414A JP5249875B2 JP 5249875 B2 JP5249875 B2 JP 5249875B2 JP 2009187414 A JP2009187414 A JP 2009187414A JP 2009187414 A JP2009187414 A JP 2009187414A JP 5249875 B2 JP5249875 B2 JP 5249875B2
- Authority
- JP
- Japan
- Prior art keywords
- receiving layer
- ink
- ink receiving
- recording material
- silica
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
1)支持体上に平均二次粒子径が500nm以下の無機微粒子を主体として含有するインク受容層を少なくとも2層有し、支持体に近いインク受容層が真珠光沢顔料を含有し、支持体に近いインク受容層中における真珠光沢顔料の添加量が、平均二次粒子径が500nm以下の無機微粒子の固形分量に対して10〜30質量%の範囲であることを特徴とするインクジェット記録材料。
2)前記支持体が紙基材の少なくとも一方の面に樹脂層を有する樹脂被覆紙であることを特徴とする上記1)記載のインクジェット記録材料。
本発明のインクジェット記録材料は、支持体上に平均二次粒子径が500nm以下の無機微粒子を主体として含有するインク受容層を少なくとも2層有し、支持体に近いインク受容層が真珠光沢顔料を含有する。なお以下の説明において、支持体に近いインク受容層をインク受容層Aと称する。また該インク受容層Aよりも支持体から離れた位置に設けられるインク受容層をインク受容層Bと称する。
[Al(OH)3]nAlCl3 ・・式2
Aln(OH)mCl(3n−m) 0<m<3n ・・式3
<ポリオレフィン樹脂被覆紙1の作製>
広葉樹晒クラフトパルプ(LBKP)と広葉樹晒サルファイトパルプ(LBSP)の1:1混合物をカナディアン スタンダード フリーネスで300mlになるまで叩解し、パルプスラリーを調製した。これにサイズ剤としてアルキルケテンダイマーを対パルプ0.5%、強度剤としてポリアクリルアミドを対パルプ1.0%、カチオン化澱粉を対パルプ2.0%、ポリアミドエピクロロヒドリン樹脂を対パルプ0.5%添加し、水で希釈して0.2%スラリーとした。このスラリーを長網抄紙機で坪量170g/m2になるように抄造し、乾燥調湿してポリオレフィン樹脂被覆紙の基紙とした。抄造した基紙に、密度0.918g/cm3の低密度ポリエチレンの樹脂に対して、10%のアナターゼ型チタンを均一に分散したポリエチレン樹脂組成物を320℃で溶融し、厚さ35μmになるように押出被覆し、微粗面加工されたクーリングロールを用いて押出被覆し表面とした。もう一方の面には密度0.962g/cm3の高密度ポリエチレン樹脂70部と密度0.918g/cm3の低密度ポリエチレン樹脂30部のブレンド樹脂組成物を同様に320℃で溶融し、厚さ30μmになるように押出コーティングし、粗面加工されたクーリングロールを用いて押出被覆し裏面とした。
石灰処理ゼラチン 100部
スルフォコハク酸−2−エチルヘキシルエステル塩 2部
クロム明ばん 10部
水にジメチルジアリルアンモニウムクロライドホモポリマー(分子量9000)4部と気相法シリカ(平均一次粒径7nm、BET法による比表面積300m2/g)100部を添加し予備分散液を作製した後、高圧ホモジナイザー処理して、固形分濃度20%の気相法シリカ分散液を作製した。気相法シリカの平均二次粒子径は135nmであった。
水に真珠光沢顔料(日本光研工業(株)製、MM−100R)を添加し予備分散液を作製した後、700rpmで5分間プロペラ撹拌して、固形分濃度25%の真珠光沢顔料分散液を作製した。
気相法シリカ分散液1 (気相法シリカの固形分として)100部
ホウ酸 4部
ポリビニルアルコール 23部
(ケン化度88%、平均重合度3500)
真珠光沢顔料分散液1 (真珠光沢顔料の固形分として)26.5部
塗布液の固形分濃度 13.9%
気相法シリカ分散液1 (気相法シリカの固形分として)100部
ホウ酸 4部
ポリビニルアルコール 23部
(ケン化度88%、平均重合度3500)
塗布液の固形分濃度 12.8%
実施例1の真珠光沢顔料分散液1を下記の真珠光沢顔料分散液2に変えた以外は実施例1と同様にして実施例2のインクジェット記録材料を得た。
水に真珠光沢顔料(日本光研工業(株)製、ME−100R)を添加し予備分散液を作製した後、700rpmで5分間プロペラ撹拌して、固形分濃度25%の真珠光沢顔料分散液を作製した。
実施例1の真珠光沢顔料分散液1を下記の真珠光沢顔料分散液3に変えた以外は実施例1と同様にして実施例3のインクジェット記録材料を得た。
水に真珠光沢顔料(メルク(株)製、Iriodin123 Bright Lustre Satin)を添加し予備分散液を作製した後、700rpmで5分間プロペラ撹拌して、固形分濃度25%の真珠光沢顔料分散液を作製した。
実施例1の真珠光沢顔料分散液1を下記の真珠光沢顔料分散液4に変えた以外は実施例1と同様にして実施例4のインクジェット記録材料を得た。
水に真珠光沢顔料(メルク(株)製、Xirallic T50−10 Crystal Silver)を添加し予備分散液を作製した後、700rpmで5分間プロペラ撹拌して、固形分濃度25%の真珠光沢顔料分散液を作製した。
実施例1と同様にして作製したポリオレフィン樹脂被覆紙の下引き層を設けた面に、下記組成のインク受容層塗布液3をインク受容層Aとして、及び下記組成のインク受容層塗布液4をインク受容層Bとしてスライドビードコーターで重層塗布した。インク受容層塗布液3の乾燥塗布量は13.8g/m2であり、インク受容層塗布液4の乾燥塗布量は26.2g/m2である。塗布後の乾燥条件は、10℃で20秒間冷却後、30〜55℃の加熱空気を吹き付けて乾燥した。
水に解膠剤としてアルミナ水和物固形分100gに対して硝酸20mmolになるように予め添加しておき、分散装置(特殊機化工業(株)製、ハイビスディスパーミックス)により撹拌しながら、この溶液に擬ベーマイト粉末(DISPERALHP14、Sasol社製)を添加し、添加後更に60分撹拌を続け、固形分濃度25%のアルミナ水和物分散液を得た。アルミナ水和物の平均二次粒子径は160nmであった。
アルミナ水和物分散液1 (アルミナ水和物の固形分として)100部
ホウ酸 0.5部
ポリビニルアルコール 10部
(ケン化度88%、平均重合度3500)
真珠光沢顔料分散液1 (真珠光沢顔料の固形分として)12.5部
塗布液の固形分濃度 18.5%
アルミナ水和物分散液1 (アルミナ水和物の固形分として)100部
ホウ酸 0.5部
ポリビニルアルコール 10部
(ケン化度88%、平均重合度3500)
塗布液の固形分濃度 18.0%
実施例1のインク受容層塗布液2を下記組成のインク受容層塗布液5に変えた以外は実施例1と同様にして参考例1のインクジェット記録材料を得た。
気相法シリカ分散液1 (気相法シリカの固形分として)100部
ホウ酸 4部
ポリビニルアルコール 23部
(ケン化度88%、平均重合度3500)
真珠光沢顔料分散液1 (真珠光沢顔料の固形分として)0.8部
塗布液の固形分濃度 12.8%
実施例1のインク受容層塗布液1を下記組成のインク受容層塗布液6に変えた以外は実施例1と同様にして実施例6のインクジェット記録材料を得た。
気相法シリカ分散液1 (気相法シリカの固形分として)100部
ホウ酸 4部
ポリビニルアルコール 23部
(ケン化度88%、平均重合度3500)
真珠光沢顔料分散液1 (真珠光沢顔料の固形分として)10部
塗布液の固形分濃度 13.2%
実施例1のインク受容層塗布液1を下記組成のインク受容層塗布液7に変えた以外は実施例1と同様にして実施例7のインクジェット記録材料を得た。
気相法シリカ分散液1 (気相法シリカの固形分として)100部
ホウ酸 4部
ポリビニルアルコール 23部
(ケン化度88%、平均重合度3500)
真珠光沢顔料分散液1 (真珠光沢顔料の固形分として)20部
塗布液の固形分濃度 13.7%
実施例1のインク受容層塗布液1を下記組成のインク受容層塗布液8に変えた以外は実施例1と同様にして実施例8のインクジェット記録材料を得た。
気相法シリカ分散液1 (気相法シリカの固形分として)100部
ホウ酸 4部
ポリビニルアルコール 23部
(ケン化度88%、平均重合度3500)
真珠光沢顔料分散液1 (真珠光沢顔料の固形分として)30部
塗布液の固形分濃度 14.1%
実施例1のインク受容層塗布液1を下記組成のインク受容層塗布液9に変えた以外は実施例1と同様にして参考例2のインクジェット記録材料を得た。
気相法シリカ分散液1 (気相法シリカの固形分として)100部
ホウ酸 4部
ポリビニルアルコール 23部
(ケン化度88%、平均重合度3500)
真珠光沢顔料分散液1 (真珠光沢顔料の固形分として)40部
塗布液の固形分濃度 14.4%
実施例1のインク受容層塗布液1及びインク受容層塗布液2からなるインク受容層A及びBに代えて、下記インク受容層塗布液10の乾燥塗布量を25g/m2となるようにインク受容層を単層で設けた以外は実施例1と同様にして比較例1のインクジェット記録材料を得た。
気相法シリカ分散液1 (気相法シリカの固形分として)100部
ホウ酸 4部
ポリビニルアルコール 23部
(ケン化度88%、平均重合度3500)
真珠光沢顔料分散液1 (真珠光沢顔料の固形分として)7.7部
塗布液の固形分濃度 13.1%
実施例1のインク受容層Aの塗布液をインク受容層塗布液2にして、その乾燥塗布量を18.7g/m2とし、インク受容層Bの塗布液をインク受容層塗布液1にして、その乾燥塗布量を6.3g/m2に変えた以外は実施例1と同様にして比較例2のインクジェット記録材料を得た。
実施例1において、下引き層上に下記組成の真珠光沢顔料塗布液1を乾燥塗布量が2.6g/m2となる様に塗布して下塗り層を設け、その後インク受容層塗布液2を乾燥塗布量が25g/m2となる様に塗布した以外は実施例1と同様にして比較例3のインクジェット記録材料を得た。
ポリビニルアルコール 100部
(ケン化度88%、平均重合度3500)
真珠光沢顔料分散液1 (真珠光沢顔料の固形分として)9.2部
塗布液の固形分濃度 12.6%
実施例1のインク受容層塗布液1を下記組成のインク受容層塗布液11に変えた以外は実施例1と同様にして比較例4のインクジェット記録材料を得た。
気相法シリカ分散液1 (気相法シリカの固形分として)100部
ホウ酸 4部
ポリビニルアルコール 23部
(ケン化度88%、平均重合度3500)
マット剤(水澤化学工業(株)製、ミズカシルP78A、平均粒子径3μm)1部
塗布液の固形分濃度 12.8%
実施例1のポリオレフィン樹脂被覆紙1を下記組成のポリオレフィン樹脂被覆紙2に変更し、更にインク受容層塗布液2の乾燥塗布量を25g/m2としてインク受容層を単層で設けた以外は実施例1と同様にして比較例5のインクジェット記録材料を得た。
ポリオレフィン樹脂被覆紙1と同様にして抄造した基紙に、密度0.918g/cm3の低密度ポリエチレン樹脂に対して、10%のアナターゼ型チタンと4.5%の真珠光沢顔料(日本光研工業(株)製、MM−100R)を均一に分散したポリエチレン樹脂組成物を320℃で溶融し、厚さ35μmになるように押出被覆し、微粗面加工されたクーリングロールを用いて押出被覆し表面とした。もう一方の面にはポリオレフィン樹脂被覆紙1と同様に密度0.962g/cm3の高密度ポリエチレン樹脂70部と密度0.918g/cm3の低密度ポリエチレン樹脂30部のブレンド樹脂組成物を同様に320℃で溶融し、厚さ30μmになるように押出コーティングし、粗面加工されたクーリングロールを用いて押出被覆し裏面とした。
実施例1のインク受容層塗布液1及びインク受容層塗布液2からなるインク受容層に代えて、インク受容層塗布液2の乾燥塗布量を25g/m2となるようにインク受容層を単層で設けた以外は実施例1と同様にして比較例6のインクジェット記録材料を得た。
インクジェットプリンター(セイコーエプソン(株)製、G860)でレッド、ブルー、グリーン、ブラックのベタ印字を行い、印字直後にPPC用紙を印字部に重ねて軽く圧着し、PPC用紙に転写したインク量の程度を目視で観察した。下記の基準で評価した。
○:転写しない。
△:わずかに転写するが問題とならないレベル。
×:印字部に転写が観察され、インク吸収性が劣る。
塗布・乾燥したインク受容層の塗布面を目視観察し、以下の基準で評価した。
○:基紙の面シボ感が目立たない。
×:基紙の面シボ感が目立つ。
記録材料の印字前の光沢性を斜光で観察し、下記の基準で評価した。
◎:カラー写真を上回る高い光沢性がある。
○:カラー写真並の高い光沢性がある。
×:光沢性がない。
塗布・乾燥させたインクジェット記録材料のインク受容層に蛍光灯を映し、その映りこみ像を目視観察して以下の基準で評価した。
○:蛍光灯の映りこみ像が鮮明に確認できる。
△:蛍光灯の映りこみ像が確認できる。
×:蛍光灯の映りこみ像がぼやけている。
××:蛍光灯の映りこみ像が著しくぼやけている。
市販のインクジェットプリンター(セイコーエプソン(株)製、G860)にて、C、M、Yの混色からなるコンポジットブラックのくすみ具合とC、M、Y各色の発色濃度を目視で観察した。下記の基準で評価した。
○:くすみがなく、発色性が良好。
△:ややくすみが認められるが良好。
×:くすみが認められ、発色性に劣る。
××:強いくすみが認められ、発色性に劣る。
Claims (2)
- 支持体上に平均二次粒子径が500nm以下の無機微粒子を主体として含有するインク受容層を少なくとも2層有し、支持体に近いインク受容層が真珠光沢顔料を含有し、支持体に近いインク受容層中における真珠光沢顔料の添加量が、平均二次粒子径が500nm以下の無機微粒子の固形分量に対して10〜30質量%の範囲であることを特徴とするインクジェット記録材料。
- 前記支持体が、紙基材の少なくとも一方の面に樹脂層を有する樹脂被覆紙であることを特徴とする請求項1に記載のインクジェット記録材料。