JP5159016B2 - 重合体組成物 - Google Patents
重合体組成物 Download PDFInfo
- Publication number
- JP5159016B2 JP5159016B2 JP2003357830A JP2003357830A JP5159016B2 JP 5159016 B2 JP5159016 B2 JP 5159016B2 JP 2003357830 A JP2003357830 A JP 2003357830A JP 2003357830 A JP2003357830 A JP 2003357830A JP 5159016 B2 JP5159016 B2 JP 5159016B2
- Authority
- JP
- Japan
- Prior art keywords
- copolymer
- ethylene
- weight
- ionomer
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
(1)エチレン・メタクリル酸共重合体(EMAA)
メタクリル酸含量9重量%、メルトフローレート3g/10分
(2)亜鉛アイオノマー(Zn−IO)
メタクリル酸含量15重量%のエチレン・メタクリル酸共重合体の亜鉛アイオノマー(中和度59%、メルトフローレート0.9g/10分)
(3)アイオノマー組成物(IO組成物)
エチレン・グリシジルメタクリレート共重合体(グリシジルメタクリレート含量12重量%、メルトフローレート(190℃)3.0g/10分)2重量部とプロピレン・エチレンランダム共重合体(三井・住友ポリオレフィン(株)製、三井・住友ポリプロF−219DA、密度910kg/m3、メルトフロレート(230℃)8.5g/10分)15重量部を予め溶融混合して得たメルトブレンド物とアイオノマー(メタクリル酸含量10重量%のエチレン・メタクリル酸共重合体の亜鉛アイオノマー、中和度80%、メルトフローレート(190℃)0.9g/10分)83重量部を溶融ブレンドしたもの
(4)ポリテトラフルオロエチレン粉末(PTFE粉末)
低分子量ポリテトラフルオロエチレンモールディングパウダー(デュポン(株)製ゾニールMP1300、見掛密度450kg/m3、融点325℃、平均粒径9μm、表面積3m2/g)
2.物性評価項目
(1)メルトフローレート(MFR):JIS K6760(190℃、2160g荷重)
(2)引張試験:JIS K6760準拠(引張速度200m/分)
(3)硬度(ショアD):JIS K7215準拠
(4)曲げ剛性率(オルゼン式):JIS K7106準拠
(5)テーバー摩耗:厚さ1mmのT−ダイシート又は厚さ3mmのプレスシートを用い、摩耗輪H−18,荷重1kg、回転数2000回転の条件での摩耗量を測定した。
(6)学振摩耗
東洋精機(株)製摩耗試験機により、綿帆布10号を使用し、荷重450g(1.92g/mm2)、往復回数100回の条件で行なった。傷が観察されなかった面積を残存率で表示した。また耐磨耗性の序列を◎、○、△により表示した。
前記したエチレン・メタクリル酸共重合体(EMAA)又は亜鉛アイオノマー(Zn−IO)100重量部にポリテトラフルオロエチレン粉末(PTFE粉末)2.5重量部を添加し、溶融混練して得られた重合体組成物の物性評価を行った。また比較のため、EMAA又はZn−IOのみの物性評価を行った。結果を表1に示す。
前記したアイオノマー組成物(IO組成物)100重量部に対し、ポリテトラフルオロエチレン粉末(PTFE粉末)を表2に示す割合で配合した重合体組成物につき、同様の物性評価を行なった。結果を表2に示す。
Claims (3)
- エチレン・不飽和カルボン酸共重合体又はそのアイオノマー60〜96.7重量部、エチレン・グリシジルモノマー共重合体0.3〜10重量部、及びオレフィン同士の共重合体、オレフィンと不飽和カルボン酸以外の他の極性モノマーとの共重合体から選ばれるポリオレフィン3〜30重量部からなる樹脂成分100重量部に対し、平均粒径が1〜400μmのフッ素系樹脂粉末を1〜5重量部の割合で配合してなる重合体組成物であって、上記フッ素系樹脂が、テトラフルオロエチレンの単独重合体又はテトラフルオロエチレンに少量の他のモノマーを共重合した共重合体である、重合体組成物。
- エチレン・不飽和カルボン酸共重合体又はそのアイオノマーが、エチレン・(メタ)アクリル酸共重合体又はそのアイオノマーである請求項1に記載の重合体組成物。
- 前記フッ素系樹脂が、ポリテトラフルオロエチレン、テトラフルオロエチレン・エチレン共重合体、テトラフルオロエチレン・ヘキサフルオロプロピレン共重合体、テトラフルオロエチレン・パーフルオロアルキルビニルエーテル共重合体、及びテトラフルオロエチレン・ヘキサフルオロプロピレン・パーフルオロアルキルビニルエーテル共重合体から選ばれる樹脂である請求項1又は2に記載の重合体組成物。