JP5141796B2 - インクジェット印刷物及びその製造方法 - Google Patents
インクジェット印刷物及びその製造方法 Download PDFInfo
- Publication number
- JP5141796B2 JP5141796B2 JP2011138362A JP2011138362A JP5141796B2 JP 5141796 B2 JP5141796 B2 JP 5141796B2 JP 2011138362 A JP2011138362 A JP 2011138362A JP 2011138362 A JP2011138362 A JP 2011138362A JP 5141796 B2 JP5141796 B2 JP 5141796B2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- resin
- ink
- printed matter
- ink receiving
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
バーコーターでA4サイズのフィルムに10g/m2となるように受理剤を塗工し、目視にてはじきの数を計測した。
○:はじきが無い。
×:はじきが一箇所以上ある。
受理剤を塗工した後、80℃で5分間乾燥させた時のフィルムの外観について目視にて評価した。
○:よれ、皺、フィルムの変形等の外観不良がほとんど無い。
△:若干のよれ、皺、フィルムの変形等の外観不良が見られる。
×:著しいよれ、皺、フィルムの変形等の外観不良が見られる。
インク受容層に対して安定したインク転移(印刷)が行われたか否かを目視にて評価した。
○:印刷がかすれたり、印字できない部分等が無く、良好に印刷された。
×:印刷がかすれたり、印字できない部分等が有り、印刷不良がある。
セロハンテープ(ニチバン製)剥離試験を行い、目視にて評価した。
○:剥離無し。
×:剥離有り。
得られたインクジェット印刷物を水に45分間浸し、室温にて1日乾燥させた後、セロハンテープ(ニチバン製)剥離試験を行い、目視にて評価した。
○:インクの滲み、かすれ、脱落、剥離もしくはインク受容層の剥離が何れも無い。
×:インクの滲み、かすれ、脱落、剥離もしくはインク受容層の剥離の何れか若しくは2以上の異常が有る。
ハイドラン CP−7020(DIC株式会社製、カチオン性ポリウレタン樹脂水分散体)と、PVA205〔株式会社クラレ製、ケン化度87モル%〜89モル%、重合度500のポリビニルアルコール〕の25質量%水溶液と、塩化マグネシウムの6水和物の53.5質量%水溶液、及びDK−6830〔星光PMC株式会社製、エピクロルヒドリンポリアミド樹脂〕の25質量%水溶液を、[水分散体(I):PVA205の25質量%水溶液:塩化マグネシウムの6水和物の53.5質量%水溶液:DK−6830の25質量%水溶液]の質量割合が、48.2:35.9:3.0:12.9となるように、プロペラ翼を取り付けた攪拌機にて十分に混合し、カチオン性ポリウレタン樹脂を含有するインク受理剤(b−1)を調製した。
塩化マグネシウム10部、ハイドランHW−970(DIC株式会社製、ポリカーボネート鎖と親水基としてスルホン酸基を有するポリウレタン樹脂水分散体、不揮発分40%)30部、ゴーセファイマー Z−100(日本合成化学株式会社製、アセトアセチル化ポリビニルアルコール)の20%水溶液を30部、WS525(星光PMC株式会社製、エピクロルヒドリンポリアミド樹脂)30部を配合し、不揮発分が15質量%のアニオン性ポリウレタン樹脂を含有するインク受理剤(b−2)を調製した。
樹脂層(A1)用樹脂として、ホモポリプロピレン〔MFR:10g/10分(230℃、21.18N)、融点:163℃;以下、「HOPP」と記載〕を用いた。また、樹脂層(A2)用樹脂として、エチレン−(メタ)アクリル酸メチル共重合体〔密度:0.940g/cm3、MA含有量18%;以下、「MA1」と記載〕を用いた。これらの樹脂をそれぞれ、樹脂層(A1)用押出機(口径50mm)及び樹脂層(A2)用押出機(口径50mm)に供給して200〜250℃で溶融し、その溶融した樹脂をフィードブロックを有するTダイ・チルロール法の共押出多層フィルム製造装置(フィードブロック及びTダイ温度:250℃)にそれぞれ供給して共溶融押出を行って、フィルムの層構成が(A1)/(A2)の2層構成で、各層の厚さが96μm/24μm(合計120μm)である共押出多層フィルムを得た。この支持体の(A2)層の面に濡れ張力が40mN/mとなるようコロナ放電処理をした後、調製例1で得られたインク受理剤(b−1)を塗布し、インクジェット記録媒体を作製した。得られたインクジェット記録媒体の受理層(B)に対してインクジェット印刷機にて印刷を行い、実施例1のインクジェット印刷物を作製した。
実施例1のフィルムの層構成(A1)/(A2)の各層の厚さを56μm/14μm(合計70μm)とした以外は実施例1と同様にしてインクジェット印刷物を作製した。
実施例1のフィルムの層構成(A1)/(A2)の各層の厚さを24μm/6μm(合計30μm)とした以外は実施例1と同様にしてインクジェット印刷物を作製した。
実施例1におけるインク受理剤(b−1)を、調製例2で得られたインク受理剤(b−2)とする以外は実施例1と同様にインクジェット印刷物を作製した。
実施例1の樹脂層(A2)の酸変性オレフィン系樹脂をエチレン−アクリル酸メチル共重合体〔MA含有量12%、密度:0.933g/cm3;以下、「MA2」と記載〕に置き換えた以外は実施例1と同様にしてインクジェット印刷物を作製した。
実施例1の樹脂層(A2)の酸変性オレフィン系樹脂をエチレン−アクリル酸メチル−無水マレイン酸共重合体〔密度:1.00g/cm3、コポリマー含有量15%;以下、「MA3」と記載〕に置き換えた以外は実施例1と同様にしてインクジェット印刷物を作製した。
実施例1の樹脂層(A2)用の樹脂MA1を50%とプロピレン−エチレン共重合体〔密度:0.900g/cm3、MFR:7〜9g/10分(230℃、21.18N)、融点:150℃;以下「COPP」と記載〕50%との配合物に置き換えた以外は実施例1と同様にしてインクジェット印刷物を作製した。
実施例1の樹脂層(A2)用の樹脂MA1を20%とCOPPを80%との配合物に置き換えた以外は実施例1と同様にしてインクジェット印刷物を作製した。
実施例7の樹脂層(A1)のHOPPを高密度ポリエチレン〔密度:0.963g/cm3、MFR:7g/10分(190℃、21.18N)、融点130℃;以下、「HDPE」と記載〕に置き換えた以外は実施例5と同様にしてインクジェット印刷物を作製した。
実施例7の樹脂層(A1)のHOPPを中密度ポリエチレン〔密度:0.934g/cm3、MFR:5.3g/10分(190℃、21.18N)、融点119℃;以下、「MDPE」と記載〕に置き換えた以外は実施例5と同様にしてインクジェット印刷物を作製した。
実施例1のアクリル酸変性樹脂をエチレン−(メタ)アクリル酸共重合体〔密度:0.940g/cm3、酸変性率12%;以下、「MA4」と記載〕に置き換えた以外は実施例1と同様にしてインクジェット印刷物を作製した。
実施例1のフィルムの層構成(A1)/(A2)の各層の厚さを114μm/6μm(合計120μm)とした以外は実施例1と同様にしてインクジェット印刷物を作製した。
実施例1のフィルムの層構成(A1)/(A2)の各層の厚さを90μm/30μm(合計120μm)とした以外は実施例1と同様にしてインクジェット印刷物を作製した。
実施例1の樹脂層(A2)の酸変性オレフィン系樹脂をCOPPに置き換えた以外は実施例1と同様にしてインクジェット印刷物を作製した。
比較例1のインク受理剤(b−1)を、インク受理剤(b−2)に置き換えた以外は比較例1と同様にインクジェット印刷物を作製した。
実施例1の樹脂層(A2)の酸変性オレフィン系樹脂をHDPEに置き換えた以外は実施例1と同様にしてインクジェット印刷物を作製した。
Claims (8)
- ポリオレフィン系樹脂(a1)を主成分とする層(A1)と、酸変性オレフィン系樹脂(a2)を含有する層(A2)とを共押出積層法を用いて積層した後、層(A2)上にインク受理剤(b)を塗布し、インク受理層(B)を形成させた後、当該インク受理層(B)上にインクジェット印刷を行なうことを特徴とするインクジェット印刷物の製造方法。
- 前記ポリオレフィン系樹脂(a1)の融点が110℃以上である請求項1記載のインクジェット印刷物の製造方法。
- 前記酸変性オレフィン系樹脂(a2)における変性率が3〜40%の範囲である請求項1又は2記載のインクジェット印刷物の製造方法。
- 前記層(A2)が更にポリオレフィン系樹脂を含有する請求項1〜3の何れか1項記載のインクジェット印刷物の製造方法。
- 前記層(A2)を形成する樹脂成分100質量部中に、前記酸変性オレフィン系樹脂(a2)を20質量部以上含有するものである請求項1〜4の何れか1項記載のインクジェット印刷物の製造方法。
- 前記インク受理剤(b)が、ポリウレタン系樹脂(b1)を含有するものである請求項1〜5の何れか1項記載のインクジェット印刷物の製造方法。
- 請求項1〜6の何れか1項記載の製造方法で得られたものであり、
ポリオレフィン系樹脂(a1)を主成分とする層(A1)と、酸変性オレフィン系樹脂(a2)を含有する層(A2)と、インク受理層(B)とが、(A1)/(A2)/(B)の順で積層されてなるインクジェット記録媒体の層(B)上にインクジェット印刷を施してなることを特徴とするインクジェット印刷物。 - 前記層(A1)と前記層(A2)との合計厚みに対する層(A2)の比率が5〜40%である請求項7記載のインクジェット印刷物。