JP5032106B2 - セルロース繊維含有成形体の製造方法 - Google Patents
セルロース繊維含有成形体の製造方法 Download PDFInfo
- Publication number
- JP5032106B2 JP5032106B2 JP2006343215A JP2006343215A JP5032106B2 JP 5032106 B2 JP5032106 B2 JP 5032106B2 JP 2006343215 A JP2006343215 A JP 2006343215A JP 2006343215 A JP2006343215 A JP 2006343215A JP 5032106 B2 JP5032106 B2 JP 5032106B2
- Authority
- JP
- Japan
- Prior art keywords
- cellulose fiber
- mass
- cellulose
- resin composition
- ethylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本実施形態に係るセルロース繊維含有成形体は、無延伸ポリオレフィンフィルムの少なくとも一方の面に、セルロース繊維、エチレン・α‐オレフィン共重合体及びエチレン・プロピレンランダム共重合体を含有するポリオレフィン系樹脂組成物層が形成された複層構造を有し、延伸されている。ポリオレフィン系樹脂組成物層は無延伸ポリオレフィンフィルムの片面又は両面に形成される。
次に、本実施形態に係るセルロース繊維含有成形体の製造方法について説明する。セルロース繊維含有成形体の製造方法は、セルロース繊維及びエチレン・α‐オレフィン共重合体を含む混合物を混練してセルロース繊維含有ペレットを製造する工程と、セルロース繊維含有ペレット及びエチレン・プロピレンランダム共重合体を混合してシート化し、無延伸ポリオレフィンフィルムに前記シートを重ねてセルロース繊維含有複層構造体を形成する工程と、セルロース繊維含有複層構造体を延伸して成形する工程と、を有する。
とする。
前記のセルロース繊維含有成形体の製造方法において、次に示す条件で実施例1のセルロース繊維含有成形体を製造した。まず、混練工程で、粉砕セルロース繊維100質量部に対して、エチレン・α‐オレフィン共重合体を10質量部、不飽和カルボン酸変性ポリオレフィン「商品名:MODIC−AP ER333F−2 MFR(JIS K 7210 190℃ 2.16kg荷重)=7.5g/10min 融点(JIS K 7121 DSC融解ピーク温度)=134℃ 三菱化学製」を4質量部、白色顔料としての酸化チタンを4質量部及び滑剤を8質量部を加え、ヘンシェルミキサーで混練し混練物を形成した。使用した酸化チタンは、商品名 タイペークA−220 石原産業製である。使用した滑材は、商品名 エクセレックス30200B 三井化学製/商品名 リケマールEW‐90 理研ビタミン製=50/50質量%混合物である。
*1 ISO白色度90%、パルプ粘度1.5、長さ加重平均繊維長0.15mm、ファイン量87.9質量%、LBP100質量%の紙粉砕物
*2 ISO白色度80%、パルプ粘度2.5、長さ加重平均繊維長0.22mm、ファイン量65.6質量%、LBP100質量%の紙粉砕物
*3 ISO白色度80%、パルプ粘度6.5、長さ加重平均繊維長0.32mm、ファイン量26.9質量%、LBP90質量% 炭酸カルシウム10質量%の紙粉砕物
*4 ISO白色度64%、パルプ粘度9.0、長さ加重平均繊維長0.55mm、ファイン量8.1質量%、LBP60質量% GP(砕木パルプ)30質量% 炭酸カルシウム10質量%の紙粉砕物
*5 ファイン量:カヤニ社 FS−2000 JAPAN TAPPI No52−2000に順じて長さ加重平均繊維長、0.2mm以下のファイン量を算出した。
*6 不飽和カルボン酸変性ポリオレフィン樹脂:商品名 MODIC−AP ER333F−2 MFR(JIS K 7210 190℃ 2.16kg荷重)=7.5g/10min 融点(JIS K 7121 DSC融解ピーク温度)=134℃ 三菱化学製
*7 酸化チタン:商品名 タイペークA‐220 石原産業製
*8 滑材:商品名 エクセレックス30200B 三井化学製/商品名 リケマールEW‐90 理研ビタミン製=50/50質量%混合物
*9 ヘンシェルミキサー温度:攪拌終了時の材料温度を示す。
*10 見掛け嵩比重:2Lのメスシリンダーにセルロース繊維含有ペレットを入れ質量を測定し、容積当りの質量を算出した。
*11 貼合フィルム:無延伸ポリプロプレンフィルム 60μm
*12 重量フィダー計量性
○:全く問題なし。
×:安定した供給ができず、実用上問題あり。
*13 Tダイ押出性:同方向二軸押出機(TEM104BS 東芝機械製)を用い厚さ1.2mmのシートを作製した。
○:全く問題なし。
△:引取速度の調整が必要で、実用上問題あり。
×:安定した引き取りができず、実用上問題あり。
*14 シート色相:ミノルタ社製の色差計 CR−300を用いL*値、a*値及びb*値を測定した。
*15 真空成形性:開口部1に対して深さ0.6の容器、16ヶ取りの成形を行った。
◎:予熱時にシートのたれ下がりがなく、成形作業性が良好であり、良好なセルロース繊維含有成形体が得られ、実用上全く問題がない。
○: 予熱時にシートのたれ下がりが大きく成形作業性は劣るが、良好なセルロース繊維含有成形体は得られるので、実用上問題ない。
×:時々穴があき深絞りできず、実用上問題あり。
*16 焼け着色:シートを視感にて次の基準で判定した。
○:黄色身がない。
×:黄色味ややあり、実用上問題あり。
*17 水黄変:成形品50gを蒸留水30mlに浸漬し、35℃で2日間保持した。その後、ろ過し水層について着色度合いを視感で評価した。視感評価は、下記の基準で判定した。
○:無色で実用上の問題なし。
×:淡黄色で実用上の問題あり。
*18 外観:真空成形後の表面状態から評価した。
○:光沢がなく均一な白い表面状態で独特な風合いと質感を表現している。
△:光沢がなく均一であるが黄色味が強く、実用上問題あり。
×:従来のプラスチック様表面である。
*19 表面粗さ(Ra):レーザ顕微鏡(VK−9700 キーエンス社製)を用いて、JIS B 0601:2001「製品の幾何特性仕様(GPS)−表面性状:輪郭曲線方式−用語,定義及び表面性状パラメータ」に準じて測定した。
*20 成形不良のため未評価である。
セルロース繊維含有ペレットに含まれる粉砕セルロース繊維100質量部に対してエチレン・プロピレンランダム共重合体を63質量部加えた以外は実施例1と同様にして、セルロース繊維含有成形体を作製した。
セルロース繊維の白色度を80%とし、セルロース繊維含有ペレットに含まれる粉砕セルロース繊維100質量部に対してエチレン・プロピレンランダム共重合体を100質量部加えた以外は実施例1と同様にして、セルロース繊維含有成形体を作製した。ここに、セルロース繊維は、ISO白色度80%、パルプ粘度2.5、長さ加重平均繊維長0.22mm、ファイン量65.6質量%、LBP100質量%の紙粉砕物を使用した。
エチレン・α‐オレフィン共重合体を26質量部とし、また、セルロース繊維含有ペレットに含まれる粉砕セルロース繊維100質量部に対してエチレン・プロピレンランダム共重合体を129質量部加え、更に、ヘンシェルミキサー温度を145℃とした以外は実施例1と同様にして、セルロース繊維含有成形体を作製した。
セルロース繊維の白色度を80%とし、エチレン・α‐オレフィン共重合体を55質量部とし、また、セルロース繊維含有ペレットに含まれる粉砕セルロース繊維100質量部に対してエチレン・プロピレンランダム共重合体を100質量部加えた以外は実施例1と同様にして、セルロース繊維含有成形体を作製した。ここに、セルロース繊維は、ISO白色度80%、パルプ粘度6.5、長さ加重平均繊維長0.32mm、ファイン量26.9質量%、LBP90質量% 炭酸カルシウム10質量%の紙粉砕物を使用した。
セルロース繊維を添加せず、エチレン・α‐オレフィン共重合体10質量部に対して、不飽和カルボン酸変性ポリオレフィンを4質量部、エチレン・プロピレンランダム共重合体100質量部、酸化チタン4質量部、滑剤を8質量部を加えて、シート化した。表面粗さは0.9μmであった。続いて、真空成形によって成形体を得た。表面粗さは0.9μmであり、従来のプラスチック様の外観であった。
ヘンシェルミキサー温度を90℃としたこと及びセルロース繊維100質量部に対してエチレン・プロピレンランダム共重合体71質量部を加えたこと以外は実施例3と同様にして、セルロース繊維含有成形体の作製を試みた。
ディスクペレッターでペレット化しなかった以外は実施例4と同様にして、セルロース繊維含有成形体の作製を試みた。
セルロース繊維としてISO白色度64%、パルプ粘度9.0、長さ加重平均繊維長0.55mm、ファイン量8.1質量%、LBP60質量% GP30質量% 炭酸カルシウム10質量%の紙粉砕物を使用したこと及びセルロース繊維100質量部に対してエチレン・プロピレンランダム共重合体を71質量部加えたこと以外は実施例2と同様にして、セルロース繊維含有ペレットを作製した。そして、貼合フィルムなしとして実施例2と同様にしてシートを作製し、更にセルロース繊維含有成形体を得た。
ヘンシェルミキサー温度を180℃としたこと以外は実施例3と同様にして、セルロース繊維含有成形体を作製した。
Claims (4)
- JIS P 8148:2001「紙,板紙及びパルプ−ISO白色度(拡散青色光反射率)の測定方法」で規定されるISO白色度が70%以上の粉砕されたセルロース繊維とエチレン・α‐オレフィン共重合体とを含み、前記セルロース繊維100質量部に対してエチレン・α‐オレフィン共重合体が10質量部以上55質量部以下で加えられた混合物を材料温度130℃以上150℃以下で混練して含有水分1.0質量%以下の混練物を形成する混練工程と、
前記混練物を非スクリュータイプ圧縮造粒機で見かけ比重0.5以上のセルロース繊維含有ペレットとするペレット工程と、
前記セルロース繊維含有ペレットとエチレン・プロピレンランダム共重合体との混合物をシート化してポリオレフィン系樹脂組成物シートを得るシート化工程と、
無延伸ポリオレフィンフィルムに前記ポリオレフィン系樹脂組成物シートを重ねてセルロース繊維含有複層構造体とする工程と、
前記セルロース繊維含有複層構造体を延伸して、前記ポリオレフィン系樹脂組成物シート側の表面をつや消し調とする工程と、を有し、
該つや消し調とする工程において、前記ポリオレフィン系樹脂組成物シート側の表面粗さ(Ra)が2.0〜10.0μmとなるように前記セルロース繊維含有複層構造体を真空成形又は真空圧空成形で延伸させることを特徴とするセルロース繊維含有成形体の製造方法。 - 前記セルロース繊維は、JIS P 8148:2001「紙,板紙及びパルプ−ISO白色度(拡散青色光反射率)の測定方法」で規定されるISO白色度が90%以上であり、且つ、0.2mm以下の微細セルロース繊維を80質量%以上含有することを特徴とする請求項1に記載のセルロース繊維含有成形体の製造方法。
- 前記セルロース繊維の含有率が51質量%以上であることを特徴とする請求項1又は2に記載のセルロース繊維含有成形体の製造方法。
- 前記セルロース繊維に熱黄変が生じていないことを特徴とする請求項1〜3のいずれか一つに記載のセルロース繊維含有成形体の製造方法。