JP5005264B2 - 粘着剤組成物、粘着シート及び粘着剤付着型機能性フィルム - Google Patents
粘着剤組成物、粘着シート及び粘着剤付着型機能性フィルム Download PDFInfo
- Publication number
- JP5005264B2 JP5005264B2 JP2006157505A JP2006157505A JP5005264B2 JP 5005264 B2 JP5005264 B2 JP 5005264B2 JP 2006157505 A JP2006157505 A JP 2006157505A JP 2006157505 A JP2006157505 A JP 2006157505A JP 5005264 B2 JP5005264 B2 JP 5005264B2
- Authority
- JP
- Japan
- Prior art keywords
- weight
- pressure
- sensitive adhesive
- component
- polymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
(1)下記(a)、(b)、(c)及び(d)成分を単量体単位として含み、重量平均分子量が300,000以上の第1の重合体と、メタクリル酸アルキルエステルを単量体単位として含み、重量平均分子量が100,000以下の第2の重合体とを含有し、第2の重合体の含有量が第1の重合体100重量部に対して1〜40重量部である、粘着剤組成物。
(a)下記式(I);
CH2=C(Rl)COOR2 (I)
(式中、Rlは水素原子又はメチル基を示し、R2は炭素数2〜14のアルキル基を示す。)
で表される(メタ)アクリル系単量体:40〜98重量%
(b)(a)成分と共重合可能であり、かつ芳香環を有する(メタ)アクリル系単量体:1〜59.9重量%
(c)(a)成分及び(b)成分と共重合可能であり、かつ反応性官能基を含有する重合性単量体:0.1〜5重量%
(d)(a)成分、(b)成分及び(c)成分と共重合可能な重合性単量体:0〜59.9重量%
(2)第1の重合体をフィルム化した場合における屈折率(nd 1)と、第2の重合体をフィルム化した場合における屈折率(nd 2)との比(nd 1/nd 2)が0.98〜1.02である、上記(1)記載の粘着剤組成物。
(3)(c)成分がカルボキシ基を含有する重合性単量体である、上記(1)又は(2)記載の粘着剤組成物。
(4)上記(1)〜(3)のいずれか一つに記載の粘着剤組成物からなる、粘着シート。
(5)基材の少なくとも片面に、上記(1)〜(3)のいずれか一つに記載の粘着剤組成物からなる粘着剤層を有する、粘着シート。
(6)機能性フィルムの少なくとも片面に、上記(1)〜(3)のいずれか一つに記載の粘着剤組成物からなる粘着剤層を有する、粘着剤付着型機能性フィルム。
(7)機能性フィルムの少なくとも片面に、上記(4)又は(5)記載の粘着シートが積層されている、粘着剤付着型機能性フィルム。
まず、本発明の粘着剤組成物について説明する。
本発明の粘着剤組成物は、特定の単量体成分から構成され、かつ特定範囲の重量平均分子量を有する第1の重合体と、特定の単量体成分から構成され、かつ特定範囲の重量平均分子量を有する第2の重合体とを含有し、第2の重合体の含有量が第1の重合体100重量部に対して1〜40重量部であることを特徴とする。
具体的には、(メタ)アクリル酸フェノキシエチル、(メタ)アクリル酸ベンジル、(メタ)アクリル酸フェノキシジエチレングリコール、(メタ)アクリル酸エチレンオキサイド変性ノニルフェノール、(メタ)アクリル酸エチレンオキサイド変性クレゾール等が挙げられる。中でも、下記式(II)で表されるアクリル酸フェノキシエチルが特に好適である。なお、(b)成分は、1種を単独で又は2種以上組み合わせて使用することができる。
具体的には、ヒドロキシル基含有重合性単量体としては、(メタ)アクリル酸2−ヒドロキシエチル、(メタ)アクリル酸2−ヒドロキシプロピル、(メタ)アクリル酸3−ヒドロキシプロピル、(メタ)アクリル酸3−ヒドロキシブテル、(メタ)アクリル酸6−ヒドロキシヘキシル、(メタ)アクリル酸8−ヒドロキシオクチル、(メタ)アクリル酸10−ヒドロキシデシル、(メタ)アクリル酸12−ヒドロキシラウリル、グリセリンジメタクリレート、ポリエチレングリコール(メタ)アクリレート、ポリプロピレングリコール(メタ)アクリレート等が挙げられる。カルボキシル基含有重合性単量体としては、(メタ)アクリル酸、カルボキシエチルアクリレート、カルボキシペンチルアクリレート、イタコン酸、マレイン酸、フマル酸、クロトン酸等が挙げられる。カルボキシル基含有重合性単量体の無水物としては、無水マレイン酸、無水イタコン酸等が挙げられる。スルホン酸基含有重合性単量体としては、スチレンスルホン酸、アリルスルホン酸、2−(メタ)アクリルアミド−2−メチルプロバンスルホン酸、(メタ)アクリルアミドプロバンスルホン酸、スルホプロピル(メタ)アクリレート、(メタ)アクリロイルオキシナフタレンスルホン酸等が挙げられる。リン酸含有重合性単量体としては、2−ヒドロキシエチルアクリロイルホスフェート等が挙げられる。アミノ基含有重合性単量体としては、(メタ)アクリル酸アミノエチル等が挙げられる。エポキシ基含有重合性単量体としては、(メタ)アクリル酸グリシジル等が挙げられる。中でも、カルボキシ基含有重合性単量体が好ましく、アクリル酸がより好ましい。
アルコキシ基含有重合性単量体としては(メタ)アクリル酸メトキシエチル等が挙げられ、アミド基含有重合性単量体としては(メタ)アクリルアミド等が挙げられる。N−ビニル窒素含有複素環化合物としてはN−ビニルピロリドン等が挙げられ、モルホリン系重合性単量体としてはアクリロイルモルホリン等が挙げられる。イミド基含有共重合性単量体としては、N−シクロヘキシルマレイミド等が挙げられる。
過酸化物系開始剤としては、例えば、ジベンゾイルペルオキシド、tert−ブチルペルマレート等が挙げられる。また、光開始剤として、例えば、4−(2−ヒドロキシエトキシ)フェニル(2−ヒドロキシ−2−プロピル)ケトン、α−ヒドロキシ−α,α’−ジメチルアセトフェノン、メトキシアセトフェノン等のアセトフェノン系開始剤;ベンゾインエチルエーテル等のベンゾインエーテル系開始剤;ベンジルジメチルケタール等のケタール系開始剤;ハロゲン化ケトン;アシルホスフィノキシド;アシルホスフォナート等が挙げられる。
なお、重合開始剤の使用量は特に限定されないが、例えば、単量体の総量100重量部に対して0.01〜2重量部、好ましくは0.02〜1重量部程度である。
GPCの測定条件
・サンプル濃度:0.2重量%(テトラヒドロフラン溶液)
・サンプル注入量:10μl
・容離液:テトラヒドロフラン(THF)
・流量(流速):0.6mL/min
・カラム温度(測定温度):40℃
・カラム:サンプルカラム:商品名[TSKguardcolumn SuperHZ−H](1本)+商品名[TSKgel SuperHZM−H](2本)(以上、東ソー株式会社製)
リファレンスカラム:商品名[TSKgel SuperH−RC](1本)(東ソー株式会社製)
・検出器:示差屈折計(RI)
有機系架橋剤としては、エポキシ系架橋剤、イソシアネート系架橋剤、アミン化合物等が挙げられる。中でも、エポキシ系架橋剤を用いることが好ましい。
イソシアネート系架橋剤としては、例えば、トリレンジイソシアネート、ヘキサメチレンジイソシアネート、イソホロンジイソシアネート、ポリメチレンポリフェニルイソシアネート、ジフェニルメタンジイソシアネート、ジフェニルメタンジイソシアネートの2量体、トリメチロールプロパンとトリレンジイソシアネートとの反応生成物、ポリエーテルポリイソシアネート、ポリエステルポリイソシアネート等が挙げられる。
アミン化合物としては、例えば、ヘキサメチレンジアミン、トリエチルジアミン、ポリエチレンイミン、ヘキサメチレンテトラミン、ジエチレントリアミン、トリエチルテトラミン、イソホロンジアミン、アミノ樹脂、メチレン樹脂等が挙げられる。
多官能性化合物の含有量は特に限定されないが、第1の重合体100重量部に対して0.01〜6重量部であることが好ましく、より好ましくは0.02〜3重量部である。
次に、本発明の粘着シートについて説明する。
本発明の粘着シートは前述した粘着剤組成物からなる粘着剤層を備えていればその形態は特に限定されるものではなく、例えば、使用目的に応じて以下の形態を採用することができる。
(i)粘着剤層のみからなる両面粘着シート、
(ii)粘着剤層の片面又は両面に剥離ライナーを有する両面粘着シート、
(iii)基材の片面に粘着剤層を有する粘着シート、
(iv)基材の両面に粘着剤層を有し、少なくとも一方の粘着剤層が本発明の粘着剤組成物からなる両面粘着シート
次に、本発明の粘着剤付着型機能性フィルムについて説明する。
本発明の粘着剤付着型機能性フィルムは、機能性フィルムの少なくとも片面に本発明の粘着剤組成物からなる粘着剤層が形成されているもの、あるいは機能性フィルムの少なくとも片面に前述した(i)〜(iv)のうちの少なくとも1種の粘着シートが積層されているものである。
機能性フィルムとは、プラズマディスプレイ、液晶表示装置、有機EL表示装置等の画像表示装置のディスプレイ等に用いられるものであり、例えば、反射防止フィルム、電磁波遮蔽フィルム、近赤外線遮蔽フィルム、偏光フィルム、防眩フィルム、位相差フィルム、光学補償フィルム、精度向上フィルム等の光学フィルムが挙げられる。機能性フィルムの材質としては、ポリエチレンテレフタレートフィルム、易接着処理されたポリエチレンテレフタレートフィルムが挙げられる。機能性フィルムを貼着すべき被着体としては、例えば、フィルターガラス、パネルガラスが挙げられ、ガラスの種類としては、例えば、ソーダ石灰ガラス、鉛ガラス、ほうけい酸ガラス等が挙げられる。
このように、本発明の粘着剤付着型機能性フィルムを使用すれば、被着体から機能性フィルムを剥離する際に、被着体を破損することなく容易に剥離することができ、しかも被着体表面に糊残りが発生することもない。したがって、被着体との貼合面に異物を噛み込んだり、貼合せ位置を誤ったとしても、被着体から機能性フィルムを剥離し再利用することができ、また透明性にも優れているので、プラズマディスプレイ、液晶表示装置、有機EL表示装置等の画像表示装置の製造に有用である。
(製造例1)
冷却管、窒素導入管、温度計、滴下ロート及び撹拝装置を備えた反応容器に、重合開始剤として2,2’−アゾビスイソブチロニトリル0.2重量部、溶媒として酢酸エチル150重量部、単量体成分としてアクリル酸2−エチルヘキシル99重量部、アクリル酸1重量部を入れ、窒素還流を室温にて1時間行った後、反応容器内のモノマー組成物溶液の温度を63℃に昇温し、窒素気流中で5.5時間重合を行い、重量平均分子量が47万の重合体の溶液を得た。
単量体成分として、アクリル酸2−エチルヘキシル79重量部、アクリル酸フェノキシエチル20重量部及びアクリル酸1重量部を用いたこと以外は、製造例1と同様の条件にて、重量平均分子量が106万の重合体の溶液を得た。
単量体成分として、アクリル酸2−エチルへキシル59重量部、アクリル酸フェノキシエチル40重量部及びアクリル酸1重量部を用いたこと以外は、製造例1と同様の条件にて、重量平均分子量110万の重合体の溶液を得た。
冷却管、窒素導入管、温度計、滴下ロート及び撹拝装置を備えた反応容器に、重合開始剤として2,2’−アゾビスイソブチロニトリル10重量部、連鎖移動剤としてα−メチルスチレン二量体10重量部、溶媒としてトルエン120重量部を入れ、反応容器内の温度を85℃に昇温した後、窒素気流中で、単量体成分としてメタクリル酸メチル100重量部を2時間かけて滴下した。その後、1時間反応を行い、重量平均分子量が3,800の重合体の溶液を得た。
製造例2で得た重合体100重量部(固形分換算)に、製造例4で得た重合体5重量部(固形分換算)を加え、架橋剤としてエポキシ系架橋剤(商品名:テトラッドC、三菱瓦欺化学社製)を0.25重量部添加して粘着剤組成物を得た。この粘着剤組成物を、アプリケーターを用いて、厚さが50μmのシリコーン処理したポリエチレンテレフタレートフィルム上に塗布し、130℃で3分間乾燥して、厚さが25μmの粘着剤層を形成した。この粘着剤層上に厚さが38μmのシリコーン処理したポリエチレンテレフタレートフィルムを貼り合せて粘着シートを得た。
製造例3で得た重合体100重量部(固形分換算)に、製造例4で得た重合体5重量部(固形分換算)を加え、架橋剤としてエポキシ系架橋剤(商品名:テトラッドC)を0.25重量部添加したこと以外は、実施例1と同様の方法により粘着シートを作製した。
製造例1で得た重合体100重量部(固形分換算)に、製造例4で得た重合体5重量部(固形分換算)を加え、架橋剤としてエポキシ系架橋剤(商品名:テトラッドC)を0.15重量部添加したこと以外は、実施例1と同様の方法により粘着シートを作製した。
製造例2で得た重合体100重量部(固形分換算)に、架橋剤としてエポキシ系架橋剤(商品名:テトラッドC)を0.075重量部添加したこと以外は、実施例1と同様の方法により粘着シートを作製した。
製造例で得られた重合体、実施例及び比較例で得られた各粘着シートを用いて以下の方法により各種評価を行った。その結果を表1に示す。
製造例で得られた重合体溶液を130℃にて3分間乾燥してフィルムを形成した後、得られたフィルムに25℃の雰囲気下でナトリウムD線を照射しアッベ屈折率計(DR−M2、アタゴ社製)にて屈折率を測定した。
各粘着シートの、一方の剥離ライナーを剥がし、厚さ25μmのポリエチレンテレフタレートフィルム(商品名:ルミラーS−10#25、東レ社製)に貼り合せ、20×120mmの試験片を採取した後、他方の剥離ライナーを剥がし、被着体としてのガラス(マイクロスライドガラス、厚さ1.3mm、水縁磨、松浪硝子工業社製)に、23℃の雰囲気下、加重19.6Nでローラを一往復させて貼り合せ、30分後にテンシロン型剥離試験機(TCM−1KNB、(株)タンスイ社製)により300mm/minの引張り速度で、180°方向の剥離粘着力を測定した。
各粘着シートの、一方の剥離ライナーを剥がし、厚さ125μmの易接着ポリエチレンテレフタレートフィルム(商品名:A4300#125、東洋紡社製)に貼り合せ、60×75mmの試験片を採取した後、他方の剥離ライナーを剥がし、被着体としてのガラスに、23℃の雰囲気下で貼り合せ、60℃の条件下に1hr投入した後、取り出して23℃の雰囲気下で45分放置した。その後、およそ300mm/minの速度で、かつ45°〜180°の角度で剥がした時のガラス面への糊残り具合(リワーク性)を、以下の基準により目視で評価した。
○:ガラス面に糊残りした部分が、目視で確認できないほど小さい。
×:ガラス面に糊残りした部分が、目視で確認できる。
各粘着シートから30×60mmの試験片を採取した後、一方の剥離ライナーを剥がしてガラス(マイクロスライドガラス、厚み0.8mm、白縁磨、松浪硝子工業社製)に貼り合せ、他方の剥離ライナーを剥がした。次いで、濁度計(ヘーズメータHM−150、村上色彩技術研究所製)を用いてJIS K7361及びJIS K7136に準じて拡散光線透過率(%)及び全光線透過率(%)を測定し、下記式によりヘーズ(%)を求めた。
ヘーズ(%)=拡散光線透過率(%)/全光線透過率(%)×100
そして、得られたヘーズに基づいて、以下の基準により透明性を評価した。
○:ヘーズが2%以下である。
×:ヘーズが2%を超えている。
一方、比較例1の粘着シートは、ポリエチレンテレフタレートフィルムとガラスを貼合した後に加熱処理すると、再剥離時にガラス面に糊残りなく剥がすことができるが、ヘーズが高く透明性に劣ることが確認された。また、比較例2の粘着シートは、ヘーズが低く透明性に優れるが、ポリエチレンテレフタレートフィルムとガラスを貼合した後に加熱処理すると、再剥離時にガラス面に糊残りが生ずることが確認された。
Claims (8)
- 下記(a)、(b)、(c)及び(d)成分を単量体単位として含み、重量平均分子量が300,000以上の第1の重合体と、
メタクリル酸アルキルエステルを単量体単位として含み、単量体全重量に占めるメタクリル酸アルキルエステルの比率が50重量%以上である、重量平均分子量が100,000以下の第2の重合体とを含有し、
第2の重合体の含有量が第1の重合体100重量部に対して1〜40重量部である、粘着剤組成物。
(a)下記式(I);
CH2=C(Rl)COOR2 (I)
(式中、Rlは水素原子又はメチル基を示し、R2は炭素数2〜14のアルキル基を示す。)
で表される(メタ)アクリル系単量体:40〜98重量%
(b)(a)成分と共重合可能であり、かつ芳香環を有する(メタ)アクリル系単量体:1〜59.9重量%
(c)(a)成分及び(b)成分と共重合可能であり、かつ反応性官能基を含有する重合性単量体:0.1〜5重量%
(d)(a)成分、(b)成分及び(c)成分と共重合可能な重合性単量体:0〜59.9重量% - 第1の重合体をフィルム化した場合における屈折率(nd 1)と、第2の重合体をフィルム化した場合における屈折率(nd 2)との比(nd 1/nd 2)が0.98〜1.02である、請求項1記載の粘着剤組成物。
- (c)成分がカルボキシ基を含有する重合性単量体である、請求項1又は2記載の粘着剤組成物。
- 多官能性化合物をさらに含有する、請求項1〜3のいずれか一項記載の粘着剤組成物。
- 請求項1〜4のいずれか一項に記載の粘着剤組成物からなる、粘着シート。
- 基材の少なくとも片面に、請求項1〜4のいずれか一項に記載の粘着剤組成物からなる粘着剤層を有する、粘着シート。
- 機能性フィルムの少なくとも片面に、請求項1〜4のいずれか一項に記載の粘着剤組成物からなる粘着剤層を有する、粘着剤付着型機能性フィルム。
- 機能性フィルムの少なくとも片面に、請求項5又は6記載の粘着シートが積層されている、粘着剤付着型機能性フィルム。