JP5004482B2 - Water-soluble fullerene / polysaccharide complex - Google Patents

Description

本発明は、フラーレンの可溶化方法およびそれによって得られる水溶性フラーレン／多糖複合体に関する。   The present invention relates to a method for solubilizing fullerene and a water-soluble fullerene / polysaccharide complex obtained thereby.

C₆₀に代表されるフラーレンは、炭素のみからなる化合物であり、その半導体としての性質や高い電子受容能を持つことから注目されているナノ物質の一つである。しかし、フラーレンは水に難溶であるため、材料として用いるにはその水溶化が課題であった。その水溶化を解決する方法としては、フラーレンに水溶性置換基を直接導入する方法が挙げられる（特許文献１〜３）。しかし、この方法は、置換基の導入によりフラーレンのもつπ系が破壊され、フラーレンの本来もつ性質が失われるため、好ましい方法とは言えない。
特開２０００−２９０２７８ 特開２００５−２６３７９５ 特開２００５−２７０８０４ Fullerene represented by C ₆₀ is a compound consisting of carbon, which is one of nanomaterials has attracted attention because of its nature and high electron accepting ability as a semiconductor. However, since fullerene is hardly soluble in water, its water solubilization has been a problem for use as a material. As a method for solving the water solubilization, there is a method of directly introducing a water-soluble substituent to fullerene (Patent Documents 1 to 3). However, this method is not a preferable method because the introduction of a substituent destroys the π system of fullerene and loses the inherent properties of fullerene.
JP 2000-290278 A JP 2005-26395 A JP 2005-270804 A

また、別の水溶化法として、水溶性分子にフラーレンを包接させるという方法がある（非特許文献１）。例えば、水溶性分子にγ−シクロデキストリン（γ−ＣＤ）を用い、混合の手段として高速振動粉砕法を採用することにより、未修飾のＣ₆₀を簡便に、しかも高濃度で水溶化できることが知られている（非特許文献１）。しかしながら、このフラーレンを包接するγ−ＣＤには官能基を選択的に付加することが難しく、また、その修飾によりフラーレンへの錯化能が落ちることから、水溶化フラーレンの機能化という点では問題が残る。
KoichiKomatsu, Koichi Fujiwara, Yasujiro Murata and Tibor Braun；J. Chem. Soc., Perkin Trans. 1, 1999, 2963-2966 As another water-solubilization method, there is a method in which fullerene is included in water-soluble molecules (Non-patent Document 1). For example, it is known that γ-cyclodextrin (γ-CD) is used as a water-soluble molecule, and the high-speed vibration pulverization method is employed as a means of mixing, whereby unmodified C ₆₀ can be easily water-solubilized at a high concentration. (Non-Patent Document 1). However, it is difficult to selectively add a functional group to γ-CD that includes this fullerene, and the complexing ability to fullerene is reduced by the modification, so that there is a problem in terms of functionalization of water-soluble fullerene. Remains.
Koichi Komatsu, Koichi Fujiwara, Yasujiro Murata and Tibor Braun; J. Chem. Soc., Perkin Trans. 1, 1999, 2963-2966

本発明者らは、フラーレンと類似の物質であるカーボンナノチューブ（ＣＮＴ）を水溶化する方法として、多糖の一種；β-1,3-グルカンとＣＮＴとを複合体化させることによる水溶化法を見出している（非特許文献２）。その方法では、一旦、β-1,3-グルカンを溶媒中ランダムコイル状に解離させてＣＮＴと超音波混合した後、中性の水を加えることにより、ＣＮＴの外側にβ-1,3-グルカンを螺旋状にラッピングさせることで水溶性複合体が形成されるものである。
MunenoriNumata, Masayoshi Asai, Kenji Kaneko, Teruaki Hasegawa, Kazuo Sakurai, SeijiShinkai；J. Am. Chem. Soc..2005, 127(16), 5875-5884 As a method for water-solubilizing carbon nanotubes (CNT), which is a substance similar to fullerene, the present inventors have proposed a water-solubilization method by complexing a kind of polysaccharide; β-1,3-glucan and CNT. (Non-Patent Document 2). In that method, β-1,3-glucan is once dissociated in a random coil form in a solvent and mixed ultrasonically with CNT, and then neutral water is added to the outside of CNT to form β-1,3- A water-soluble complex is formed by helically wrapping glucan.
MunenoriNumata, Masayoshi Asai, Kenji Kaneko, Teruaki Hasegawa, Kazuo Sakurai, SeijiShinkai; J. Am. Chem. Soc .. 2005, 127 (16), 5875-5884

また、β-1,3-グルカンとは異なる種類の多糖；スターチやアミロースなどを用いても、水溶化が可能との報告がなされている（非特許文献３および４）
AlexanderStar, David W. Steuerman, James R. Heath and J. Fraser Stoddart; Angew. Chem.Int. Ed., 2002, 41, No.14, 2508-2512 Oh-Kil Kim,Jongtae Je, Jeffrey W. Baldwin, Steven Kooi, Pehr E.Pehrsson, and Leonard J.Buckley；J.Am.Chem.Soc., 2003,125, 4426-4427 In addition, it has been reported that even if a polysaccharide different from β-1,3-glucan; starch or amylose is used, water-solubilization is possible (Non-patent Documents 3 and 4).
AlexanderStar, David W. Steuerman, James R. Heath and J. Fraser Stoddart; Angew. Chem. Int. Ed., 2002, 41, No. 14, 2508-2512 Oh-Kil Kim, Jongtae Je, Jeffrey W. Baldwin, Steven Kooi, Pehr E. Pehrsson, and Leonard J. Buckley; J. Am. Chem. Soc., 2003, 125, 4426-4427

そこで、上記のＣＮＴに有効であった方法をフラーレンに適用し、多糖によって水溶性複合体を形成させるということが考えられるが、単純に同じ操作をフラーレンに行っても、水溶化は困難である。   Therefore, it is conceivable that the above-mentioned method effective for CNT is applied to fullerene to form a water-soluble complex with a polysaccharide. However, even if the same operation is simply performed on fullerene, water-solubilization is difficult. .

本発明の目的は、安全な物質を用いて、簡便且つ効果的にフラーレンを水溶性複合体へ変換し、フラーレンの水溶液を得る技術を提供することにある。   An object of the present invention is to provide a technique for easily and effectively converting a fullerene into a water-soluble complex by using a safe substance to obtain an aqueous solution of fullerene.

本発明者らは、フラーレンを多糖と固相のまま強力に混合した後、水を加えて攪拌・混合することによって、フラーレンを含む水溶性複合体が形成することを見出したものである。
かくして、本発明に従えば、フラーレンと多糖とを固相状態で予備混合する工程、および、前記予備混合工程の後に、水を加えて攪拌・混合する工程を含むことを特徴とする水溶性フラーレン／多糖複合体の製造方法が提供される。
さらに、本発明は、別の視点から、上記の方法で得られる水溶性フラーレン／多糖複合体、またはフラーレン含有水溶液を提供する。 The present inventors have found that a water-soluble complex containing fullerene is formed by strongly mixing fullerene with a polysaccharide in a solid phase, and then adding water and stirring and mixing.
Thus, according to the present invention, a water-soluble fullerene comprising a step of premixing fullerene and polysaccharide in a solid state, and a step of adding water and stirring and mixing after the premixing step. A method for producing a polysaccharide complex is provided.
Furthermore, the present invention provides a water-soluble fullerene / polysaccharide complex or a fullerene-containing aqueous solution obtained by the above method from another viewpoint.

本発明に従えば、生体に安全な多糖を使ってフラーレンを水に可溶化できるため、広範な用途、特に医療およびバイオテクノジーの分野で、フラーレンを使った新規な技術の開発が期待される。   According to the present invention, fullerenes can be solubilized in water using polysaccharides that are safe for living organisms, and therefore, development of new technologies using fullerenes is expected in a wide range of applications, particularly in the fields of medicine and biotechnology.

また、本発明により得られる複合体化されたフラーレンは、多糖の形成する疎水性空間内に一次元状に配列していると考えられ（図１参照）、単一のフラーレン粒子には認められない新たな機能の付与が期待される。即ち、一次元状に配列したＣ₆₀は、単体のＣ₆₀に比べて長寿命電荷分離状態を形成できると考えられ、電子プールとしての利用が期待される。これは、緑色植物における光合成アンテナ捕集体Ｂ８５０（ＬＨ２）で見られる、クロロフィルの配列と同様、Ｃ₆₀配列間を電子が移動可能なため逆電子移動が抑制されることによる。この一次元配列したＣ₆₀を基板上に集積できれば、Ｃ₆₀の高密度集積化と高効率な光電変換素子の開発が可能になると考えられる。 In addition, the complexed fullerene obtained by the present invention is considered to be one-dimensionally arranged in the hydrophobic space formed by the polysaccharide (see FIG. 1), and is recognized by a single fullerene particle. It is expected that new functions will be added. That is, it is considered that C ₆₀ arranged in a one-dimensional form can form a long-lived charge separation state as compared with a single C ₆₀ and is expected to be used as an electron pool. This can be seen in photosynthetic antenna collecting body B850 (LH2) in green plants, similar to the arrangement of chlorophyll due to the fact that electrons between C ₆₀ sequences because it can move back electron transfer is inhibited. If this one-dimensionally arranged C ₆₀ can be integrated on the substrate, it is considered that high-density integration of C ₆₀ and development of a highly efficient photoelectric conversion element can be made.

また、水溶化されたＣ₆₀は光励起されることにより高い一重項酸素発生効率を有するため、光線力学治療法への応用が期待される。超音波照射法により準備したＣ₆₀は大きな会合体を形成しており、その表面積が小さく、十分に一重項酸素を発生できないものと考えられる。一方、今回の一次元配列を形成したＣ₆₀では、表面積が大きく、より効率的に酸素分子との間でエネルギー移動や電子移動を行なえるものと期待される。また、今回用いた可溶化剤は天然多糖であるため、その安全性は高く、生体への応用に関して有利である。 Further, water-solubilized C ₆₀ has high singlet oxygen generation efficiency when photoexcited, and therefore, application to photodynamic therapy is expected. C ₆₀ prepared by the ultrasonic irradiation method forms a large aggregate, and its surface area is small, and it is considered that singlet oxygen cannot be generated sufficiently. On the other hand, C ₆₀ formed in this one-dimensional array has a large surface area and is expected to perform energy transfer and electron transfer with oxygen molecules more efficiently. Moreover, since the solubilizer used this time is a natural polysaccharide, its safety is high and it is advantageous for application to living bodies.

本発明においては、単独ではほとんど水に溶解することがないフラーレンを、多くの水素結合サイトを有する多糖が内部に形成する疎水性空間に、一次元配列的に取り込むことによって、水溶性の複合体が形成するものと考えられる（図１参照）。   In the present invention, a water-soluble complex is obtained by incorporating fullerene, which hardly dissolves in water alone, into a hydrophobic space formed by a polysaccharide having many hydrogen bonding sites in a one-dimensional array. (See FIG. 1).

本発明において用いられるのに特に好適な多糖はβ-1,3-グルカンである。β-1,3-グルカンは、天然の状態では３重螺旋構造をとっているが、強アルカリ性の溶液中やジメチルスルホキシド（ＤＭＳＯ）などの非プロトン性極性溶媒中では、１本鎖に解かれており、それを中性の水中に移すと、３重螺旋状態に戻ることが知られている。また、その際、１本鎖のＤＮＡやＲＮＡを共存させると、多糖２本と核酸１本が水素結合および疎水性相互作用の働きによって３重螺状の複合体となることが本発明者らによって見出されている。多糖単独で３重螺旋状に戻るか、または核酸やカーボンナノチューブ、フラーレンのような他の物質と複合体化するかの選択は、接触・混合の方法やＤＭＳＯ水溶液の組成などの要因によっても影響を受ける。
櫻井、新海; J. Am.Chem. Soc., 2000, 122, 4520 木村、甲元、櫻井、新海;Chem. Lett., 2000, 1242 PCT/JP00/07875 PCT/JP02/02228 A particularly preferred polysaccharide for use in the present invention is β-1,3-glucan. β-1,3-glucan has a triple helix structure in the natural state, but it is dissolved into a single chain in a strongly alkaline solution or in an aprotic polar solvent such as dimethyl sulfoxide (DMSO). It is known that when it is transferred to neutral water, it returns to a triple spiral state. In addition, in this case, when a single-stranded DNA or RNA coexists, two polysaccharides and one nucleic acid become a triple screw complex by the action of hydrogen bonding and hydrophobic interaction. It is found by. The choice of whether a polysaccharide alone will return to a triple helix or be complexed with other substances such as nucleic acids, carbon nanotubes, and fullerenes will also be affected by factors such as the contact / mixing method and the composition of the DMSO aqueous solution. Receive.
Sakurai, Shinkai; J. Am. Chem. Soc., 2000, 122, 4520 Kimura, Komoto, Sakurai, Shinkai; Chem. Lett., 2000, 1242 PCT / JP00 / 07875 PCT / JP02 / 02228

本発明においては、フラーレンと多糖とを固相状態のままで予め混合する。したがって、通常３重螺旋状態にあるβ-1,3-グルカンを、上記のように複合体化する前にランダムコイル状に解離させる必要がないため、本発明は工程的に有利である。
本発明に従いフラーレンと多糖とを予め固相状態で混合するための適用される手法（装置）は、当初は黒色のフラーレンと当初は白色の多糖とが混合されて全体として均一な褐色を呈するようにフラーレンと多糖とが充分に混合、粉砕されれば、特に制限なく、従来から知られた各種の混合・粉砕法（装置）を用いることができる。例えば、遊星式や遠心回転式のボールミルなども使用できるが、特に、好ましいのは高速振動粉砕装置を用いて行われる高速振動粉砕（法）である。すなわち、固相のまま、フラーレンおよび可溶化剤としての多糖を硬球と共に容器内に入れ、該容器を高速で振動させる。 In the present invention, fullerene and polysaccharide are mixed in advance in a solid phase state. Therefore, since it is not necessary to dissociate β-1,3-glucan, which is normally in a triple helical state, into a random coil before complexing as described above, the present invention is advantageous in terms of process.
The method (apparatus) applied to preliminarily mix fullerene and polysaccharide in the solid state according to the present invention is such that initially black fullerene and initially white polysaccharide are mixed to give a uniform brown color as a whole. If the fullerene and the polysaccharide are sufficiently mixed and pulverized, various conventionally known mixing and pulverizing methods (apparatuses) can be used without particular limitation. For example, a planetary or centrifugal rotating ball mill can be used. Particularly preferred is a high-speed vibration pulverization method using a high-speed vibration pulverization apparatus. That is, fullerene and a polysaccharide as a solubilizing agent are placed in a container together with hard spheres in a solid phase, and the container is vibrated at high speed.

容器は、容器内のフラーレン、多糖および硬球を外界雰囲気から遮断して密閉するものであることが好ましい。さらに容器は、好ましくは、ステンレス等の硬い材料から主として形成され、振動により生じる衝撃、例えば、容器本体中空部で往復運動する硬球が容器内壁と衝突することで生じる衝撃に耐え得るものであれば、いずれの種類の材料から形成してもよい。なお一般的に、容器は、振動に付される間で密閉状態を維持するものが好ましい。従って、適当な密閉が供されるように、容器本体と蓋とを外部からホルダーで固定してもよい。   The container is preferably one that seals off fullerenes, polysaccharides and hard balls in the container from the ambient atmosphere. Furthermore, the container is preferably formed mainly from a hard material such as stainless steel, and can withstand an impact caused by vibration, for example, an impact caused by a hard ball reciprocating in the hollow portion of the container body colliding with the inner wall of the container. , Any kind of material may be used. In general, the container is preferably one that maintains a sealed state while being subjected to vibration. Therefore, the container body and the lid may be fixed with a holder from the outside so as to provide an appropriate seal.

容器中空部は、例えば円筒形状を有し、振動に付される間、当該円筒形中空部の一方の端部から他方の端部へと硬球が中空部の長手方向に往復運動できる形状およびサイズを有している。しかしながら、振動に付される間、硬球が中空部の長手方向に往復運動できるものであれば、容器中空部はいずれの形状およびサイズであってもよい。   The container hollow portion has, for example, a cylindrical shape, and a shape and size that allows a hard ball to reciprocate in the longitudinal direction of the hollow portion from one end of the cylindrical hollow portion to the other end while being subjected to vibration. have. However, as long as the hard sphere can reciprocate in the longitudinal direction of the hollow portion while being subjected to vibration, the container hollow portion may have any shape and size.

高速振動粉砕における特に重要な操作条件は振動数である。すなわち、容器中空部で硬球が往復運動し、その結果、フラーレンと可溶化剤とが混ざるような振動数および／または往復運動する硬球と中空部壁部との間でフラーレンが粉砕されるような振動数で容器を振動させる。具体的には、振動数１０〜１２０ｓ^−１（１０〜１２０Ｈｚ）、好ましくは振動数１０〜６０ｓ^−１（１０〜６１Ｈｚ）より好ましくは振動数２０〜５０ｓ^−１（２０〜５０Ｈｚ）で容器を振動させる。 A particularly important operating condition in high-speed vibration grinding is the frequency. That is, the hard sphere reciprocates in the hollow portion of the container, and as a result, the frequency at which the fullerene and the solubilizer are mixed and / or the fullerene is crushed between the reciprocating hard sphere and the hollow portion wall. Vibrate container at frequency. Specifically, the container is at a frequency of 10 to 120 s ⁻¹ (10 to 120 Hz), preferably a frequency of 10 to 60 s ⁻¹ (10 to 61 Hz), more preferably a frequency of 20 to 50 s ⁻¹ (20 to 50 Hz). Vibrate.

なお、容器を振動させる方向は、一般的に容器中空部の長手方向であり、容器中空部の長手方向が水平方向となるように容器を振動機に設置する場合には、その水平方向にて容器を左右に往復するように振動させることが好ましい。ただし、硬球が中空部で往復運動するのであれば、容器自体の振動方向に制限はなく、容器および／もしくはその中空部の形態または容器の振動機への設置の仕方等に応じて振動させる方向を適宜変更してよい。   The direction in which the container is vibrated is generally the longitudinal direction of the container hollow portion, and when the container is installed in the vibrator so that the longitudinal direction of the container hollow portion is the horizontal direction, It is preferable to vibrate the container so as to reciprocate left and right. However, if the hard sphere reciprocates in the hollow part, there is no restriction on the vibration direction of the container itself, and the direction of vibration depends on the form of the container and / or its hollow part or how the container is installed on the vibrator. May be changed as appropriate.

振動時間は、５〜６０分、より好ましくは１０〜３０分程度である。振動時間が長すぎると分散液中のフラーレン濃度が低下する結果となる。ただし、振動時間は、振動数や振幅等によって変動するものである。このような振動数、振動方向および振動時間に加えて更に、容器中空部で硬球が往復運動し、その結果、好ましくは乾燥したフラーレンと可溶化剤とが粉砕、混合されるような振幅および／または往復運動する硬球と中空部壁部との間でフラーレンが粉砕されるような振幅でもって容器を振動させる。従って、具体的には、例えば底面直径２０ｍｍ、長手方向長さ６５ｍｍの容器（中空部の底面直径１２ｍｍ、中空部の長手方向長さ５０ｍｍ）を用いる場合、振幅５〜１００ｍｍ、好ましくは振幅１０〜８０ｍｍ、より好ましくは振幅２０〜５０ｍｍでもって中空部長手方向に容器を振動させる。なお、ここでいう「振幅」とは、振動に付される容器が振動の中心点を基準にして最大に変位した場合において、中心点から最大変位点までの長さをいう。   The vibration time is about 5 to 60 minutes, more preferably about 10 to 30 minutes. If the vibration time is too long, the fullerene concentration in the dispersion will decrease. However, the vibration time varies depending on the frequency and amplitude. In addition to the frequency, vibration direction and vibration time, the hard sphere reciprocates in the hollow portion of the container, and as a result, preferably the amplitude and / or so that the dried fullerene and the solubilizer are ground and mixed. Alternatively, the container is vibrated with such an amplitude that the fullerene is crushed between the reciprocating hard sphere and the hollow wall portion. Therefore, specifically, for example, when a container having a bottom diameter of 20 mm and a longitudinal length of 65 mm (a bottom diameter of the hollow portion of 12 mm and a longitudinal length of the hollow portion of 50 mm) is used, the amplitude is 5 to 100 mm, preferably the amplitude is 10 to 10. The container is vibrated in the longitudinal direction of the hollow portion with an amplitude of 80 mm, more preferably 20 to 50 mm. Here, the “amplitude” refers to the length from the center point to the maximum displacement point when the container to be subjected to vibration is displaced to the maximum with respect to the vibration center point.

振動工程にて容器内に供される硬球は好ましくは球形を有するものの、容器が振動に付される間、中空部にて往復運動するのに適した形状であればいずれの形状であってもよい。
また、例えば底面直径１２ｍｍ、長手方向長さ５０ｍｍの中空部サイズを容器が有する場
合、硬球は、直径２〜１０ｍｍ、好ましくは直径４〜６ｍｍ、より好ましくは直径５ｍｍ
のサイズを有する球体である。また、容器が振動に付される間、当該中空部にて硬球が往
復運動し、その結果、好ましくは当該硬球と中空部壁部との間でフラーレンが
粉砕されるような硬さを硬球が有することが好ましい。従って、例えば、硬球はメノウ、
スレンレス、アルミナ、ジルコニア、タングステンカーバイド、クロム鋼およびテフロン
（登録商標）からなる群から選択される材料から形成される。容器に供される硬球の数は
、１〜６個、好ましくは１〜４個、より好ましくは２個であるものの、容器が振動に付さ
れる間、中空部にて硬球が往復運動し、その結果、好ましくは乾燥したフラーレンと可溶化剤とが混ざるのに適した個数および／または往復運動する硬球と中空部壁部との間でフラーレンが粉砕されるのに適した個数であれば、いずれの個数を用いてもかまわない。なお、２個以上の硬球が容器に供される場合は、往復運動する硬球間でもフラーレンが粉砕されることになる。 The hard sphere provided in the container in the vibration process preferably has a spherical shape, but any shape is suitable as long as the container is suitable for reciprocating movement in the hollow portion while being subjected to vibration. Good.
For example, when the container has a hollow part size having a bottom diameter of 12 mm and a longitudinal length of 50 mm, the hard sphere has a diameter of 2 to 10 mm, preferably a diameter of 4 to 6 mm, more preferably a diameter of 5 mm.
A sphere having a size of Further, while the container is subjected to vibration, the hard sphere reciprocates in the hollow portion, and as a result, the hard sphere preferably has such a hardness that the fullerene is crushed between the hard ball and the hollow wall portion. It is preferable to have. Thus, for example, hard balls are agate,
It is formed from a material selected from the group consisting of slenless, alumina, zirconia, tungsten carbide, chromium steel and Teflon. The number of hard spheres provided to the container is 1 to 6, preferably 1 to 4, more preferably 2, but while the container is subjected to vibration, the hard sphere reciprocates in the hollow part, As a result, preferably the number suitable for mixing the dried fullerene and the solubilizer and / or the number suitable for pulverizing the fullerene between the reciprocating hard sphere and the hollow wall, Any number may be used. In addition, when two or more hard balls are provided to the container, fullerenes are crushed even between the reciprocating hard balls.

本発明に従えば、以上のようにして予め混合したフラーレン／多糖混合物に、次に、水を加えて攪拌・混合する。この攪拌・混合工程は、室温下に少なくとも２日間、例えば、４〜７日間行うことが好ましい。   According to the present invention, water is then added to the fullerene / polysaccharide mixture previously mixed as described above, followed by stirring and mixing. This stirring and mixing step is preferably performed at room temperature for at least 2 days, for example, 4 to 7 days.

本発明で使用する多糖には、各種のβ-1,3-グルカン、およびアミロース、プルランなどのα-1,4-グルカン、ならびにα-1,4-グルカンとα-1,3-グルカンの混合系であるデキストランなどがある。そのなかでより好ましいのはβ-1,3-グルカンである。この多糖は、主鎖がβ1→3グルコシド結合により結合された多糖であり、側鎖に糖残基（グルコース残基）の存在する割合（側鎖の糖残基置換率）の異なる各種のものが知られている。側鎖がないカードランおよび側鎖の糖残基による置換率が数百分の１程度と小さいパーキマンとラミナランなど側鎖置換率が低いβ-1,3-グルカンは、水溶性に乏しく、使いづらいところがあるが、致命的なものではない。一方、シゾフィラン、スクレログルカンおよびレンチナンは側鎖の糖置換率が３３−４０％と比較的高く、水溶性で、一般に利用し易い。本発明において、フラーレンの可溶化剤として使用する場合も、側鎖の糖置換率が約３０％以上の後者のものが好適である。なお、平均分子量は広範囲のものが使用可能であるが、1本鎖の状態で、約２５０００程度以上のものが好適である。側鎖に官能基が導入されたβ-1,3-グルカンなども使用できる。   The polysaccharides used in the present invention include various β-1,3-glucans, α-1,4-glucans such as amylose and pullulan, and α-1,4-glucans and α-1,3-glucans. There are dextran, which is a mixed system. Of these, β-1,3-glucan is more preferred. These polysaccharides are polysaccharides whose main chains are linked by β1 → 3 glucoside bonds, and have various ratios of sugar residues (glucose residues) in the side chains (side chain sugar residue substitution rates). It has been known. Β-1,3-glucans with low side-chain substitution rates such as perchiman and laminalane, which have a side chain-free curdlan and a side chain sugar residue substitution rate of about one-hundredth, have poor water solubility. It is difficult but not fatal. On the other hand, schizophyllan, scleroglucan and lentinan have a relatively high side chain sugar substitution rate of 33-40%, are water-soluble and are generally easy to use. In the present invention, the latter having a side chain sugar substitution rate of about 30% or more is also preferred when used as a fullerene solubilizer. A wide range of average molecular weights can be used, but a molecular weight of about 25,000 or more in a single-stranded state is preferable. Β-1,3-glucan having a functional group introduced in the side chain can also be used.

また、天然のβ-1,3-グルカンの一つであるシゾフィラン（ＳＰＧ）は筋肉内注射製剤の臨床薬として実際に使用されており、婦人科癌に対する免疫増強法の筋肉内注射薬として２０年以上の使用実績がある。さらに、免疫系の抗原提示細胞への親和性が知られており、生体内での安全性が確認されている。それらの特性は、フラーレンを水溶化して、例えば、バイオテクノロジーにおけるデバイスとしての応用などを考慮する場合には重要な特性であると考えられる。そして、溶液で所定の部位にフラーレンを送達した後に、使用した多糖を除く必要がある場合は、分解酵素処理などの方法で目的を達成することも可能である。
McIntire, T.M., Brant, D. A.; J. Am. Chem. Soc., 1998, 120, 6909 清水、陳、荷見、増淵;Biotherapy, 1990, 4, 1390 長谷川; Oncologyand Chemotherapy, 1992, 8, 225 Further, schizophyllan (SPG), which is one of natural β-1,3-glucans, is actually used as a clinical drug for intramuscular injection preparations, and is used as an intramuscular injection for immune enhancement for gynecological cancer. Has been used for more than a year. Furthermore, the affinity of the immune system for antigen-presenting cells is known, and safety in vivo has been confirmed. These characteristics are considered to be important characteristics when fullerene is solubilized and considered for application as a device in biotechnology, for example. And when it is necessary to remove the used polysaccharide after delivering fullerene to a predetermined site | part with a solution, it is also possible to achieve the objective by methods, such as a degradation enzyme process.
McIntire, TM, Brant, DA; J. Am. Chem. Soc., 1998, 120, 6909 Shimizu, Chen, Luggage, Enlargement; Biotherapy, 1990, 4, 1390 Hasegawa; Oncology and Chemotherapy, 1992, 8, 225

本発明が適用されるフラーレンは現在期待されている実用性からは主としてＣ₆₀であるが、本発明はＣ₆₀に限らず、他のいずれのフラーレン（例えば、Ｃ₇₀、Ｃ₇₆など）にも同様に適用できる。
以下、高速振動粉砕法を採用し、ＳＰＧでＣ₆₀を可溶化する方法および生成したＣ₆₀／ＳＰＧ水溶液の特性に沿って本発明の特徴を実施例で詳細に示が、本発明は、この実施例によって制限されるものではない。 The fullerene to which the present invention is applied is mainly C ₆₀ from the practicality expected at present, but the present invention is not limited to C ₆₀ but also to any other fullerene (for example, C ₇₀ , C _76, etc.). The same applies.
Hereinafter, the features of the present invention will be described in detail along with the characteristics of the method of solubilizing C ₆₀ with SPG and the characteristics of the produced C ₆₀ / SPG aqueous solution by adopting the high-speed vibration pulverization method. It is not limited by the examples.

高速振動粉砕法によるシゾフィランを用いたＣ₆₀の可溶化Ｃ₆₀ 1.0mg、シゾフィラン（ＳＰＧ）3.0mg
(一本鎖当りのMw=150,000、n=231、三井製糖株式会社提供)を高速振動粉砕容器に入れ、高速振動粉砕を20分、30Hzで行った。なお、用いた振動粉砕装置は、レッチェ（Retsch）製MM200であり、Ｃ₆₀およびシゾフィランとともに、２個のメノウボール（球直径5mm）を20mmの底面直径、65mmの長手方向長さを有する円筒形状の密閉容器（当該容器に形成される円筒形中空部：底面直径12mm、長手方向長さ50mm）に入れて高速振動粉砕した。その後、Ｄ₂Ｏを加え、室温で6日間攪拌した。遠心分離（14000rpm、5min）にて不溶成分を取り除き、褐色の上澄み液（Ｃ₆₀/SPG溶液）を採取した。 Fast solubilized C ₆₀ 1.0 mg of C ₆₀ with schizophyllan by vibration grinding method, schizophyllan (SPG) 3.0 mg
(Mw = 150,000 per chain, n = 231, provided by Mitsui Sugar Co., Ltd.) was placed in a high-speed vibration pulverization vessel, and high-speed vibration pulverization was performed at 30 Hz for 20 minutes. Incidentally, the vibration grinding apparatus used, Lecce (Retsch) manufactured by a MM200, together with C ₆₀ and schizophyllan, two agate balls base diameter of (spherical diameter 5mm) to 20 mm, cylinder has a longitudinal length of 65mm shape In a closed container (cylindrical hollow portion formed in the container: bottom diameter 12 mm, longitudinal length 50 mm) and pulverized at high speed. Thereafter, D ₂ O was added, and the mixture was stirred at room temperature for 6 days. Insoluble components were removed by centrifugation (14000 rpm, 5 min), and a brown supernatant (C ₆₀ / SPG solution) was collected.

紫外-可視吸収スペクトル測定 実施例１で得られたＣ₆₀/SPG溶液の紫外-可視吸収スペクトルを1mmセルを用いて測定した。SPGの代わりにγ-CDを用いて可溶化したＣ₆₀/γ-CD溶液（0.16mM）および自己会合体のスペクトルを比較例として合わせて図2に示した。その結果、いずれにもＣ₆₀由来のスペクトルが観測された。SPGで可溶化されたＣ₆₀の濃度は、Ｃ₆₀/γ-CD溶液のスペクトルとの比較より、約0.16mMであることがわかった。またＣ₆₀/γ-CD溶液の紫外-可視吸収スペクトルと比べて、230 nm、260nm付近の吸光度の減少および330 nm付近のレッドシフト、および450nm付近の吸光度の増加が見られた。しかし、単分散Ｃ₆₀と会合体Ｃ₆₀のスペクトルの中間的なスペクトルを示した。Ｃ₆₀同士が接触することでこのスペクトルの変化は生じるので、可溶化されているC₆₀は、会合体ではなく、単分散C₆₀が接触しあっている状態にあると考えられる。 Ultraviolet-visible absorption spectrum measurement The ultraviolet-visible absorption spectrum of the C ₆₀ / SPG solution obtained in Example 1 was measured using a 1 mm cell. The C ₆₀ / γ-CD solution (0.16 mM) solubilized with γ-CD instead of SPG and the spectrum of the self-aggregate are shown in FIG. 2 together as a comparative example. As a result, the spectrum of the even C ₆₀ from any was observed. The concentration of C ₆₀ solubilized with SPG was found to be about 0.16 mM by comparison with the spectrum of the C ₆₀ / γ-CD solution. Further, as compared with the ultraviolet-visible absorption spectrum of the C ₆₀ / γ-CD solution, a decrease in absorbance near 230 nm and 260 nm, a red shift near 330 nm, and an increase in absorbance near 450 nm were observed. However, it showed intermediate spectra of monodisperse C ₆₀ and aggregate C _60. Since the change in the spectrum by C ₆₀ come into contact with each other occurs, C ₆₀ being solubilized, not the aggregate are considered to be state of monodispersed C ₆₀ are each other in contact.

円偏光二色性スペクトル測定 SPGは、不斉炭素を有している。よって、C₆₀がSPGと相互作用しているならば、誘起CDが確認できるのではないかと考え、円偏光二色性スペクトル測定を行った。実施例1で得られた溶液の10倍希釈溶液の円偏光二色性（CD）スペクトル測定を行った。測定条件は、1cmセル、積算回数200回とした。CDスペクトル測定の結果を図3に示した。また、C₆₀/γ-CD溶液（0.16mM）のスペクトルも合わせて示した。同濃度のC₆₀/γ-CD溶液のCDスペクトルと比較すると、同スケールのCD値であることより、C₆₀がγ-CDに包接された状態と同程度の相互作用を受けているものと考えられる。 The circular dichroism spectrum measurement SPG has an asymmetric carbon. Accordingly, C ₆₀ is if interacting with SPG, considered either induced CD is not able confirmation were circular dichroism spectroscopy. Circular dichroism (CD) spectrum measurement of a 10-fold diluted solution of the solution obtained in Example 1 was performed. The measurement conditions were a 1 cm cell and 200 integrations. The results of CD spectrum measurement are shown in FIG. The spectrum of the C ₆₀ / γ-CD solution (0.16 mM) is also shown. Compared with CD spectra of C ₆₀ / gamma-CD solution the same concentration, than it is a CD value of the scale, which C ₆₀ is undergoing interaction comparable to a state of being inclusion in gamma-CD it is conceivable that.

^１ H-NMRスペクトル測定 実施例1で得られたC₆₀/SPG溶液および比較例としてのSPG溶液（三重螺旋構造）の¹H-NMRスペクトル測定を行った。積算回数は256回である。測定結果を図4に示した。SPGのスペクトルでは、3.0〜4.5ppm付近に大きくブロード化したスペクトルが見られた。ブロード化の原因として、SPGが三重螺旋構造をとっていることが考えられる。一方、C₆₀/SPG溶液では、若干ブロード化しているものの、比較的シャープなスペクトルが見られ、C₆₀/SPG溶液中のSPGは三重螺旋構造でない、別の構造をとっていることが考えられる。 ¹ H-NMR spectrum ^{1 H-NMR} measurements obtained by the spectral measurement Example 1 C ₆₀ / SPG solution and SPG solution as a comparative example (triple helix structures) was carried out. The number of integration is 256 times. The measurement results are shown in FIG. In the SPG spectrum, a broad spectrum was observed around 3.0 to 4.5 ppm. As a cause of broadening, it is considered that SPG has a triple helical structure. On the other hand, although the C ₆₀ / SPG solution is slightly broad, a relatively sharp spectrum is seen, and it is considered that the SPG in the C ₆₀ / SPG solution has a different structure, not a triple helix structure. .

透過型電子顕微鏡（TEM）観察 C₆₀/SPG溶液5μlを炭素膜付、および膜なしマイクログリッド上に載せ、1分放置した。溶液をろ紙で吸い取り、1日常温常圧で乾燥させた。TEMにより得られた像を図5に示す。図5a)、b)は炭素膜ありグリッド、c)、d)は炭素膜なしグリッドの像である。炭素膜ありグリッドからは、ワイヤー状の数μm程度のC₆₀/SPGが観察された。また、拡大していくと、Y字状に分岐した像が見られた。スケールバーより、像の直径は約10nmであった。SPGの三重螺旋構造は、直径が2.6nmであるので、バンドル化して存在していることが示された。また、炭素膜なしグリッドからは、C₆₀/SPGが非常に大きくバンドル化した像が見られた。 Observation with Transmission Electron Microscope (TEM) 5 μl of a C ₆₀ / SPG solution was placed on a microgrid with and without a carbon film and left for 1 minute. The solution was blotted with filter paper and dried at room temperature and normal pressure for 1 day. An image obtained by TEM is shown in FIG. FIGS. 5a) and b) are images of a grid with a carbon film, and c) and d) are images of a grid without a carbon film. From the grid with carbon film, wire-like C ₆₀ / SPG of about several μm was observed. In addition, as it was enlarged, a Y-branched image was seen. From the scale bar, the image diameter was about 10 nm. Since the triple helical structure of SPG has a diameter of 2.6 nm, it was shown to exist in a bundle. In addition, from the grid without carbon film, a very large bundle of C ₆₀ / SPG was seen.

本発明は、フラーレンを水に可溶化することにより、フラーレンの各種用途、特に医療およびバイオテクノロジー分野における新規な用途開発に資するものと期待される。また、フラーレンは水中で一次元に配列していると考えられ、高効率な光電変換素子等への応用も期待される。   The present invention is expected to contribute to various uses of fullerenes, particularly development of new uses in the medical and biotechnology fields, by solubilizing fullerenes in water. In addition, fullerenes are considered to be arranged one-dimensionally in water, and application to highly efficient photoelectric conversion elements and the like is also expected.

高速振動粉砕法による、シゾフィラン（SPG）を用いたC₆₀/の可溶化のイメージを示す。The image of solubilization of C ₆₀ / using schizophyllan (SPG) by the high-speed vibration grinding method is shown. 本発明のC₆₀/SPG溶液と比較例のC₆₀/γ-CD溶液およびC₆₀自己会合体の紫外-可視吸収スペクトル（実施例２）を示す。C ₆₀ / SPG solution and Comparative Example C ₆₀ / gamma-CD solution and C ₆₀ Ultraviolet self association of the present invention - showing the visible absorption spectrum (Example 2). 本発明のC₆₀/SPG溶液および比較例のC₆₀/γ-CD溶液の円偏光二色性スペクトル（実施例３）を示す。Shows the C ₆₀ / SPG solution and Comparative Examples of C ₆₀ / γ-CD solutions circular dichroism spectra of the present invention (Example 3). 本発明のC₆₀/SPG溶液およびSPG溶液の¹H-NMRスペクトル（実施例４）を示す。C ₆₀ / SPG solution and SPG ¹ H-NMR spectrum of the solution of the present invention (Example 4) shows. 本発明のC₆₀/SPGのTEM像（実施例５）を示す。TEM images of C ₆₀ / SPG of the present invention (Example 5) shows.

Claims (3)

フラーレンと多糖とを固相状態で予備混合する工程、および、前記予備混合工程の後に、水を加えて攪拌・混合する工程を含む水溶性フラーレン／多糖複合体の製造方法であって、多糖としてβ−1,3−グルカンを用いることを特徴とする方法。 A step of pre-mixing the fullerene and the polysaccharide in a solid state, and, after the preliminary mixing step, a step of stirring and mixing by adding water to a manufacturing method of including a water-soluble fullerene / polysaccharide complex, a polysaccharide And β-1,3-glucan is used as a method. β−1,3−グルカンが、シゾフィラン、スクレログルカンおよびレンチナンから選ばれたものであることを特徴とする請求項１の水溶性フラーレン／多糖複合体の製造方法。The method for producing a water-soluble fullerene / polysaccharide complex according to claim 1, wherein β-1,3-glucan is selected from schizophyllan, scleroglucan and lentinan. 請求項１または２の方法で得られることを特徴とする水溶性フラーレン／多糖複合体。A water-soluble fullerene / polysaccharide complex obtained by the method according to claim 1 or 2.