JP4925390B2 - フェノール樹脂発泡体の製造方法 - Google Patents
フェノール樹脂発泡体の製造方法 Download PDFInfo
- Publication number
- JP4925390B2 JP4925390B2 JP2004207120A JP2004207120A JP4925390B2 JP 4925390 B2 JP4925390 B2 JP 4925390B2 JP 2004207120 A JP2004207120 A JP 2004207120A JP 2004207120 A JP2004207120 A JP 2004207120A JP 4925390 B2 JP4925390 B2 JP 4925390B2
- Authority
- JP
- Japan
- Prior art keywords
- curing
- foam
- post
- phenol resin
- resin foam
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
このフェノール樹脂発泡体は、通常レゾール型フェノール樹脂、界面活性剤、発泡剤、硬化剤などを含む発泡性フェノール樹脂成形材料を、連続的に移動するキャリア上に吐出し、吐出物を加熱ゾーンを経由して発泡、硬化させると共に成形して一次発泡体を得たのち、後硬化処理することにより、製造されている。
しかしながら、これらの方法においては、多段乾燥炉を必要とし、製造コストが高くつくのを免れない上、連続生産には向かないなどの問題がある。
(1) (A)レゾール型フェノール樹脂、(B)界面活性剤、(C)炭素数3〜7の脂肪族炭化水素化合物および炭素数5〜7の脂環式炭化水素化合物の中から選ばれる少なくとも1種の発泡剤、および(D)硬化剤を含む発泡性フェノール樹脂成形材料を発泡硬化させてなる一次発泡体を、単一構造の熱風硬化炉中にて、80〜90℃の温度で1.5〜4.5時間の範囲で後硬化処理することにより、寸法変化率を1%未満に、かつ厚さ30mmにおける圧縮強さを14.0N/cm2以上とすることを特徴とするフェノール樹脂発泡体の製造方法、
(2) 熱風硬化炉における風速が0.5m/min以上である上記(1)項に記載のフェノール樹脂発泡体の製造方法、および
(3) それぞれスペーサを介して20mm以上の間隔を開けて重ねられた複数の一次発泡体を、熱風硬化炉中にて後硬化処理する上記(1)または(2)項に記載のフェノール樹脂発泡体の製造方法、
を提供するものである。
また、後硬化処理温度が上記の範囲にあれば、気泡壁の損傷が抑制されると共に、膨れ、収縮、変色などが抑制された外観の良好なフェノール樹脂発泡体を得ることができる。
さらに、この後硬化処理は、熱風硬化炉中で、複数の一次発泡体を重ねて行うことが生産性の面から有利である。この場合、各一次発泡体同士が接触しないように、それぞれスペーサを介して20mm以上の間隔を開けて重ねることが好ましい。
〈寸法変化率〉
200mm角のサンプルを用い、EN1604に従い、70℃、48時間後の寸法変化を測定した。
〈厚さ30mmにおける圧縮強さ〉
100mm角のサンプルを用い、JISK7220に従い、変形10%時の圧縮応力を求めた。但し、試験片の数は3個とした。
〈初期熱伝導率(20℃)〉
300mm角のサンプルを用い、低温板10℃、高温板30℃に設定し、JIS A 1412の熱流計法に従い、熱伝導率測定装置HC−074 304(英弘精機株式会社製)を使用して測定した値である。
なお、各例で得られた発泡体の物性は、以下に示す方法に従って評価した。
(1)寸法変化率
明細書本文記載の方法に従って測定した。
(2)圧縮強さ
明細書本文記載の方法に従って測定した。
(3)初期熱伝導率(20℃)
明細書本文記載の方法に従って測定し、初期熱伝導率(20℃)が0.02W/m・K以下を○、0.02W/m・Kを超えるものを×とした。
(4)外観
目視により、爆裂、膨れ、収縮、変色の有無を観察した。
レゾール型フェノール樹脂[旭有機材工業(株)製「PF−329」、フェノール:ホルムアルデヒド モル比=1:2]100重量部に、シリコーン系界面活性剤3重量部、ポリエステル系可塑剤2.5重量部を加えて混合し、このフェノール樹脂混合物に、発泡剤としてペンタン8重量部、硬化剤としてパラトルエンスルホン酸:キシレンスルホン酸 重量比=2:1の混合物20重量部をピンミキサーにて供給して混合物を攪拌した。
その後、攪拌した混合物を連続的に送行するキャリア上に吐出し、この吐出物を75℃加熱ゾーンを経由して発泡させると同時に成形して厚さ30mm、幅910mm、長さ1820mmのフェノール樹脂発泡体を得た。次いで、直ちに台車上に取り、1枚ごとに厚さ30mm、幅80mm、長さ1820mmのスペーサーを3本置き、該フェノール樹脂発泡体を30枚積載し、図1に示す単一構造の熱風硬化炉(風速1m/min)に挿入し、後硬化温度が85℃、後硬化時間が3時間の条件で、後硬化処理を行った。なお、図1において、符号1は熱風硬化炉、2は台車、3はフェノール樹脂発泡体、4は温度計である。
後硬化処理発泡体の物性を表1に示す。
実施例1において、後硬化温度を82℃に変更した以外は、実施例1と同様にして実施した。後硬化処理発泡体の物性を表1に示す。
実施例1において、後硬化温度を88℃に変更した以外は、実施例1と同様にして実施した。後硬化処理発泡体の物性を表1に示す。
実施例1において、後硬化温度を65℃に変更した以外は、実施例1と同様にして実施した。後硬化処理発泡体の物性を表1に示す。
実施例1において、後硬化温度を75℃に変更した以外は、実施例1と同様にして実施した。後硬化処理発泡体の物性を表1に示す。
実施例1において、後硬化温度を95℃に変更した以外は、実施例1と同様にして実施した。後硬化処理発泡体の物性を表1に示す。
実施例1において、後硬化温度を105℃に変更した以外は、実施例1と同様にして実施した。後硬化処理発泡体の物性を表1に示す。
実施例1において、後硬化時間を1時間に変更した以外は、実施例1と同様にして実施した。後硬化処理発泡体の物性を表1に示す。
実施例1において、後硬化時間を5時間に変更した以外は、実施例1と同様にして実施した。後硬化処理発泡体の物性を表1に示す。
2 台車
3 フェノール樹脂発泡体
4 温度計
Claims (3)
- (A)レゾール型フェノール樹脂、(B)界面活性剤、(C)炭素数3〜7の脂肪族炭化水素化合物および炭素数5〜7の脂環式炭化水素化合物の中から選ばれる少なくとも1種の発泡剤、および(D)硬化剤を含む発泡性フェノール樹脂成形材料を発泡硬化させてなる一次発泡体を、単一構造の熱風硬化炉中にて、80〜90℃の温度で1.5〜4.5時間の範囲で後硬化処理し、寸法変化率を1%未満に、かつ厚さ30mmにおける圧縮強さを14.0N/cm2以上とすることを特徴とするフェノール樹脂発泡体の製造方法。
- 熱風硬化炉における風速が0.5m/min以上である請求項1に記載のフェノール樹脂発泡体の製造方法。
- それぞれスペーサを介して20mm以上の間隔を開けて重ねられた複数の一次発泡体を、熱風硬化炉中にて後硬化処理する請求項1または2に記載のフェノール樹脂発泡体の製造方法。