JP4819410B2 - サイドウォール用ゴム組成物 - Google Patents
サイドウォール用ゴム組成物 Download PDFInfo
- Publication number
- JP4819410B2 JP4819410B2 JP2005178243A JP2005178243A JP4819410B2 JP 4819410 B2 JP4819410 B2 JP 4819410B2 JP 2005178243 A JP2005178243 A JP 2005178243A JP 2005178243 A JP2005178243 A JP 2005178243A JP 4819410 B2 JP4819410 B2 JP 4819410B2
- Authority
- JP
- Japan
- Prior art keywords
- rubber
- white filler
- component constituting
- weight
- rubber component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
以下に、実施例1〜5および比較例1〜4にて使用した各種薬品について詳細に説明する。
NR:RSS♯3(ムーニー粘度(ML1+4100℃)100、SP値8.2)
BR:宇部興産(株)製のBR150B(ムーニー粘度(ML1+4100℃)43、SP値8.2)
エポキシ化天然ゴム1(ENR1):GUTHRIE POLYMER SDN.BHD製のENR25(エポキシ化率25モル%、ムーニー粘度(ML1+4100℃)75、SP値9)
エポキシ化天然ゴム2(ENR2):GUTHRIE POLYMER SDN.BHD製のENR50(エポキシ化率50モル%、ムーニー粘度(ML1+4100℃)65、SP値10)
シリカ:Degussa社製のUltrasil VN3(BET比表面積175m2/g)
シランカップリング剤:Degussa社製のSi69
カーボンブラック:昭和キャボット(株)製のショウブラックN330(HAF)
アロマオイル:(株)ジャパンエナジー製のプロセスX140
レジン:(株)日本触媒製のSP1068レジン
ステアリン酸:日本油脂(株)製のステアリン酸「桐」
酸化亜鉛:三井金属鉱業(株)製の酸化亜鉛2種
老化防止剤:大内新興化学工業(株)製のノクラック6c
ワックス:日本精蝋(株)製のオゾエース0355
EPDM:住友化学(株)製のエスプレン586(ムーニー粘度(ML1+4100℃)85、SP値7.9)
硫黄:鶴見化学工業(株)製の粉末硫黄
加硫促進剤BBS:大内新興化学工業(株)製のノクセラーNS(N−tert−ブチル−2−ベンゾチアゾリルスルファンアミド)
加硫促進剤CBS:大内新興化学工業(株)製のノクセラーCZ(N−シクロヘキシル−2−ベンゾチアゾリルスルファンアミド)
表1の工程(1)に示す配合量にしたがって、ゴム成分、フィラー、軟化剤、レジン、ワックス、老化防止剤、ステアリン酸および酸化亜鉛を、充填率が58%になるように(株)神戸製鋼製の1.7Lバンバリーに充填し、80rpmで140℃に到達するまで混練した。
(粘弾性試験)
粘弾性スペクトロメータVES((株)岩本製作所製)を用いて、温度70℃、初期歪10%、動歪2%および周波数10Hzの条件において、実施例1〜5および比較例1〜4の加硫ゴムスラブシートのtanδを測定した。そして、測定したtanδから、以下の式により転がり抵抗指数を算出した。指数が大きいほど、転がり抵抗が低減され、転がり抵抗特性に優れることを示す。
(転がり抵抗指数)=(比較例1のtanδ)/(各配合のtanδ)×100
JIS−K6252の「加硫ゴムおよび熱可塑性ゴム−引裂強さの求め方」の試験方法に準じて、切り込み無しのアングル形試験片を使うことにより引き裂き強さ(N/mm)を測定した。そして、測定した引き裂き強さから、以下の式により引き裂き強さ指数を算出した。指数が大きいほど、引き裂き強さが大きいことを示す。
(引き裂き強さ指数)=(各配合の引き裂き強さ)/(比較例1の引き裂き強さ)×100
JIS−K6260の「加硫ゴムおよび熱可塑性ゴムのデマッチャ屈曲亀裂成長試験方法」の試験方法に準じて、室温23℃、相対湿度55%の条件でゴム組成物サンプルに1mmの亀裂成長が生じるまでの回数、あるいは100万回試験後の亀裂成長長さを測定した。そして、得られた回数および亀裂長さをもとに、ゴム試験片サンプルに1mmの亀裂成長までの屈曲回数を対数で表す。なお、70%および110%とは、もとのゴム組成物サンプルの長さに対する伸び率を表す。
走査型プローブ顕微鏡(SPM)の位相モード測定により、実施例2および比較例2のテストサンプルについてのモルフォルジーを測定した。ポリマー分散の評価結果を図3および4に示す。
ENR2>ENR1>NR>BR≧EPDM
2 白色充填剤が偏在している非連続相
3 白色充填剤が偏在している非連続相以外の非連続相
4 天然ゴム
5 エポキシ化天然ゴム
6 白色充填剤を主として含むフィラー
Claims (9)
- ゴム成分および白色充填剤を含有するサイドウォール用ゴム組成物であって、
連続相および1相以上の非連続相が海−島構造を呈し、
該非連続相の少なくとも1相に、該白色充填剤が偏在しており、
白色充填剤がシリカであり、
白色充填剤が偏在している非連続相を構成するゴム成分が、天然ゴムまたは極性基を有するジエン系ゴムであり、
連続層を構成するゴム成分が、水素化天然ゴム、ブタジエンゴムおよび/または天然ゴムであり、
白色充填剤が偏在している非連続相を構成するゴム成分として天然ゴムを用いる場合、連続層を構成するゴム成分が水素化天然ゴムおよび/またはブタジエンゴムであり、
白色充填剤が偏在している非連続相を構成するゴム成分として極性基を有するジエン系ゴムを用いる場合、連続層を構成するゴム成分が天然ゴムであるサイドウォール用ゴム組成物。 - 白色充填剤の含有量が、ゴム成分100重量部に対して5〜80重量部である請求項1記載のサイドウォール用ゴム組成物。
- 極性基を有するジエン系ゴムが、極性基含有天然ゴム、極性基含有ブタジエンゴムおよび極性基含有スチレンブタジエンゴムからなる群から選ばれる1種以上である請求項1記載のサイドウォール用ゴム組成物。
- 白色充填剤が偏在している非連続相以外の非連続相を構成するゴム成分が、白色充填剤と親和性の低い低極性ゴムであり、
低極性ゴムがエチレンプロピレンジエン共重合ゴムである請求項1、2または3記載のサイドウォール用ゴム組成物。 - 連続層を構成するゴム成分が、ブタジエンゴムまたは天然ゴムであり、
白色充填剤が偏在している非連続相を構成するゴム成分として天然ゴムを用いる場合、連続層を構成するゴム成分がブタジエンゴムであり、
白色充填剤が偏在している非連続相を構成するゴム成分として極性基を有するジエン系ゴムを用いる場合、連続層を構成するゴム成分が天然ゴムである
請求項1、2、3または4記載のサイドウォール用ゴム組成物。 - 全ゴム成分中において、白色充填剤が偏在している非連続相を構成するゴム成分の含有率が5〜75重量%、および連続相を構成するゴム成分の含有率が95〜25重量%である請求項1、2、3、4または5記載のサイドウォール用ゴム組成物。
- (a)非連続相を構成するゴム成分と白色充填剤とを混練する工程、ならびに
(b)工程(a)で得られた混練物に、連続相を構成するゴム成分を混練する工程からなる請求項1、2、3、4、5または6記載のサイドウォール用ゴム組成物の製造方法。 - 請求項1、2、3、4、5または6記載のサイドウォール用ゴム組成物からなる空気入りタイヤ。
- 請求項7記載の製造方法により得られたサイドウォール用ゴム組成物からなる空気入りタイヤ。