JP4724598B2 - Agricultural coating - Google Patents
Agricultural coating Download PDFInfo
- Publication number
- JP4724598B2 JP4724598B2 JP2006127205A JP2006127205A JP4724598B2 JP 4724598 B2 JP4724598 B2 JP 4724598B2 JP 2006127205 A JP2006127205 A JP 2006127205A JP 2006127205 A JP2006127205 A JP 2006127205A JP 4724598 B2 JP4724598 B2 JP 4724598B2
- Authority
- JP
- Japan
- Prior art keywords
- light
- agricultural
- less
- wavelength
- covering material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、農作物栽培用の農業用ハウス、トンネル等に好適な遮熱性能を有する農業用被覆材に関する。 The present invention relates to an agricultural covering material having heat shielding performance suitable for agricultural houses, tunnels and the like for crop cultivation.
従来、農業用ハウス等の農作物栽培用施設にはポリオレフィン系樹脂フィルムやポリ塩化ビニル系樹脂フィルム等の農業用被覆材が用いられてきた。しかしながら、このような農業用フィルムを農業用ハウスにおける農作物の栽培に用いた場合に、太陽の日射によってハウス内の温度が高温となって農作物の育成に障害を生じるといった問題があった。また、抵抗力の弱いイチゴ苗などの育苗は、濃色の育苗ポットで行われるために、過温状態は育苗にとって好ましくない物であった。このような問題を解消するために、農業用被覆材の上に寒冷紗や遮光ネットをかけたり、農業用被覆材自体に、光線遮断層や反射層を設ける等の対応が取られていた。 Conventionally, agricultural coating materials such as polyolefin resin films and polyvinyl chloride resin films have been used in agricultural crop cultivation facilities such as agricultural houses. However, when such an agricultural film is used for cultivating crops in an agricultural house, there is a problem that the temperature in the house becomes high due to solar sunshine and the cultivation of the crops is hindered. Moreover, since raising seedlings, such as a strawberry seedling with weak resistance, is performed with a dark-colored seedling pot, the overheated state was not preferable for raising seedlings. In order to solve such problems, countermeasures such as applying a cold chill or a light-shielding net on the agricultural covering material, or providing a light blocking layer or a reflecting layer on the agricultural covering material itself have been taken.
例えば、特開昭６１−１１１３５０号公報（特許文献１）においては、塩化ビニル系樹脂にアルミニウム粉末と、白色顔料（酸化チタン）又は白色顔料と、カーボンブラックとを配合してなる農業用遮光性フィルムが開示されている。また、特開２００４−３１４３６３号公報（特許文献２）においては、ポリエチレン系樹脂１００質量部及び酸化チタン顔料１０〜５０質量部を含有してなる白色樹脂層を少なくとも１層含んでなるポリエチレン系多層フィルムであり、多層フィルム全体においてポリエチレン系樹脂１００質量部に対し酸化チタン顔料が１０〜５０質量部であり、フィルムの厚さが７０〜２００μｍ、遮光率が８０％以上である農業用被覆材が開示されている。しかしながら、特許文献１〜２に記載の農業用被覆材においては、含有させる酸化チタンに太陽光を効率よく遮蔽させるために重量平均粒子径が一般に５００ｎｍ以下（好ましくは１００ｎｍ〜３００ｎｍ）程度の細かな粒子径の酸化チタンを用いていた。そのため、酸化チタン顔料を少量含有させたとしても農業用被覆材自体が白くなって外観や透明性が損なわれるという問題や、光合成に必要な可視光領域の光線の平均透過率が低くなって農作物の育成に影響を及ぼすという問題が生じていた。 For example, in Japanese Patent Application Laid-Open No. 61-111350 (Patent Document 1), a light shielding property for agriculture comprising a vinyl chloride resin and an aluminum powder, a white pigment (titanium oxide) or a white pigment, and carbon black. A film is disclosed. In JP 2004-314363 A (Patent Document 2), a polyethylene multilayer comprising at least one white resin layer containing 100 parts by mass of a polyethylene resin and 10 to 50 parts by mass of a titanium oxide pigment. Agricultural covering material that is a film, 10 to 50 parts by mass of titanium oxide pigment with respect to 100 parts by mass of polyethylene resin in the entire multilayer film, a film thickness of 70 to 200 μm, and a light shielding rate of 80% or more. It is disclosed. However, in the agricultural coating materials described in Patent Documents 1 and 2, in order to efficiently shield sunlight from the titanium oxide to be contained, the weight average particle diameter is generally about 500 nm or less (preferably 100 nm to 300 nm). Particle size titanium oxide was used. Therefore, even if a small amount of titanium oxide pigment is contained, the agricultural coating itself becomes white and the appearance and transparency are impaired, and the average transmittance of light in the visible light region necessary for photosynthesis is lowered and There has been a problem of affecting the development of
また、特開平１１−２９２９９６号公報（特許文献３）においては、金属酸化物の結晶構造中に該金属酸化物を構成する金属の酸化数以下の酸化数を有する他の金属が固溶した金属酸化物を、チタンの酸化物又は含水酸化物で被覆した物質を含んでなる熱可塑性樹脂フィルムが開示されている。しかしながら、特許文献３に記載の熱可塑性樹脂フィルムにおいても、重量平均粒子径が１〜５００ｎｍと細かな粒子径の酸化チタンが用いられていたため、透明性が損なわれるという問題や光合成に必要な可視光領域の光線までも大きく遮断してしまって農作物の育成に影響を及ぼすという問題が生じていた。 In Japanese Patent Application Laid-Open No. 11-292996 (Patent Document 3), a metal in which another metal having an oxidation number equal to or lower than the oxidation number of the metal constituting the metal oxide is dissolved in the crystal structure of the metal oxide. A thermoplastic resin film comprising a substance obtained by coating an oxide with a titanium oxide or a hydrous oxide is disclosed. However, in the thermoplastic resin film described in Patent Document 3, titanium oxide having a fine particle diameter of 1 to 500 nm is used, and thus the problem that transparency is impaired and the visibility necessary for photosynthesis are required. There was a problem that even the light in the light region was largely blocked, affecting the cultivation of crops.
また、特開平１１−１８５８９号公報（特許文献４）においては、光触媒機能を有する酸化チタンを含有する塗膜を塗工した農業用合成樹脂フィルムが開示されている。ここに添加される酸化チタンは遮熱性能のために添加されたものではなく、光触媒機能を塗膜にもたせるものであるために、５〜５０ｎｍと粒径が小さなものであり、遮熱性能を有するものではない。
本発明は、上記従来技術の有する課題に鑑みてなされたものであり、酸化チタンを含有する塗膜を備える農業用被覆材であるにも拘らず、波長が近赤外光領域にある光線を過度に透過させることなく波長が可視光領域にある光線を十分に透過させることができ、しかも十分な透明性と優れた遮熱性とを有することを可能とし、作物の根の部分に影響する地温の上昇を抑制し、また、直接光の照射による葉焼けを軽減できる農業用被覆材を提供することを目的とする。 The present invention has been made in view of the above-described problems of the prior art, and is a light having a wavelength in the near infrared region despite being an agricultural coating material having a coating film containing titanium oxide. Ground temperature that can sufficiently transmit light having a wavelength in the visible light range without excessive transmission, and has sufficient transparency and excellent heat shielding properties, and affects the root part of the crop. An object of the present invention is to provide an agricultural covering material that can suppress the increase in the amount of light and reduce the burning of leaves caused by direct light irradiation.
本発明者らは、上記目的を達成すべく鋭意研究を重ねた結果、農業用被覆材において、重量平均粒子径が０．６〜１．５μｍである酸化チタンを含有させた塗膜を少なくとも一方の面に設けることにより、驚くべきことに波長が近赤外光領域にある光線を過度に透過させることなく波長が可視光領域にある光線を十分に透過させることができること、並びに、十分な透明性と優れた遮熱性を有し、直達光透過率を減少させることが可能となることを見出し、本発明を完成するに至った。 As a result of intensive studies to achieve the above object, the present inventors have found that at least one coating film containing titanium oxide having a weight average particle diameter of 0.6 to 1.5 μm in an agricultural coating material. Surprisingly, the light having the wavelength in the near-infrared light region can be sufficiently transmitted without excessively transmitting the light having the wavelength in the near-infrared light region, and sufficiently transparent. The present invention has been completed by discovering that the direct light transmittance can be reduced by reducing the direct light transmittance.
すなわち、本発明の農業用被覆材は、少なくとも１層の熱可塑性樹脂フィルムからなり、少なくとも一方の面に塗膜が設けられた農業用被覆材であって、前記塗膜組成中に重量平均粒子径が０．６〜１．５μｍである酸化チタンを含有しており、波長が４００ｎｍ以上７００ｎｍ未満の可視光領域にある光線の平均透過率が７５%以上であり、且つ、波長が７００ｎｍ以上２０００ｎｍ未満の近赤外光領域にある光線の平均透過率が８５％以下であることを特徴とするものである。 That is, the agricultural coating material of the present invention is an agricultural coating material comprising at least one layer of a thermoplastic resin film, and a coating film is provided on at least one surface, and the weight average particle in the coating film composition Titanium oxide having a diameter of 0.6 to 1.5 μm is contained, the average transmittance of light in the visible light region having a wavelength of 400 nm or more and less than 700 nm is 75% or more, and the wavelength is 700 nm or more and 2000 nm. The average transmittance of light rays in the near-infrared light region of less than 85% is 85% or less .
さらに、本発明の農業用被覆材としては、波長が７００ｎｍ以上２０００ｎｍ未満の近赤外光領域にある透過光線において直達光透過率が４０％以上７５％以下であることが好ましい。 Furthermore, as the agricultural covering material of the present invention, it is preferable that the direct light transmittance is 40% or more and 75% or less in the transmitted light in the near infrared light region having a wavelength of 700 nm or more and less than 2000 nm.
本発明における直達光とは、被覆材を透過する光線が内部に直線的に到達する光線のことであり、直達光透過率とは透過する光線のうち直達光として透過する光線の割合を示す物である。 The direct light in the present invention is a light beam that linearly passes through the coating material, and the direct light transmittance is a thing that indicates the ratio of the light beam that is transmitted as direct light to the transmitted light beam. It is.
本発明によれば、酸化チタンを含有する塗膜を備える農業用被覆材であるにも拘らず、波長が近赤外光領域にある光線を過度に透過させることなく波長が可視光領域にある光線を十分に透過させることができ、しかも十分な透明性と優れた遮熱性とを有することを可能とする農業用被覆材を提供することが可能となる。 According to the present invention, the wavelength is in the visible light region without excessively transmitting the light having the wavelength in the near infrared light region, even though it is an agricultural covering material having a coating film containing titanium oxide. It is possible to provide an agricultural covering material that can sufficiently transmit light and that has sufficient transparency and excellent heat shielding properties.
また、波長が４００ｎｍ以上７００ｎｍ未満の可視光領域にある光線の平均透過率が７５％以上であり、且つ、波長が７００ｎｍ以上２０００ｎｍ未満の近赤外光領域にある光線の平均透過率が８５％以下であり、ハウス内の温度上昇を抑制することが可能となるために、過温障害による農作物の育成不良を防ぐことが可能となる。 The average transmittance of light in the visible light region having a wavelength of 400 nm or more and less than 700 nm is 75% or more, and the average transmittance of light in the near infrared light region having a wavelength of 700 nm or more and less than 2000 nm is 85%. Since it is possible to suppress an increase in the temperature in the house, it is possible to prevent poor crop growth due to an overheat failure.
またさらに、波長が７００ｎｍ以上２０００ｎｍ未満の近赤外光領域にある透過光線において直達光透過率が４０％以上７５％以下であるために、農作物の葉の直達光による焼けや変色を防止することが可能になると共に、特に育苗ポット内の温度の上昇を抑制することが可能となるために、イチゴ苗等の育苗時の苗の成長に適したものとなる。 Furthermore, since the direct light transmittance is 40% or more and 75% or less in the transmitted light in the near-infrared light region having a wavelength of 700 nm or more and less than 2000 nm, the burning or discoloration of the crop leaves by the direct light is prevented. In addition, since it becomes possible to suppress an increase in temperature particularly in the seedling pot, it is suitable for growing seedlings such as strawberry seedlings.
以下、本発明をその好適な実施形態に即して詳細に説明する。 Hereinafter, the present invention will be described in detail with reference to preferred embodiments thereof.
本発明の農業用被覆材は、少なくとも１層の熱可塑性樹脂フィルムからなり、少なくとも一方の面に塗膜が設けられた農業用被覆材であって、前記塗膜組成中に重量平均粒子径が０．６〜１．５μｍである酸化チタンを含有していることを特徴とするものである。 The agricultural coating material of the present invention is an agricultural coating material comprising at least one layer of a thermoplastic resin film, and a coating film is provided on at least one surface, wherein the coating film composition has a weight average particle diameter. It contains titanium oxide having a thickness of 0.6 to 1.5 μm.
本発明にかかる酸化チタンは、重量平均粒子径が０．６〜１．５μｍのものである。このような重量平均粒子径が０．６未満では、波長が４００ｎｍ以上７００ｎｍ未満にある可視光領域の光線の平均透過率が低下するとともに波長が７００ｎｍ以上２０００ｎｍ未満の近赤外光領域における光線の平均透過率が高くなるとともに、得られる農業用被覆材が白くなって透明性が低下することで、農業用被覆材で覆われたハウス内における農作物の光合成の効率が低下し、更には遮熱性も低下する。他方、前記重量平均粒子径が１．５を超えると近赤外領域における光線の散乱効率が低下し、結果として近赤外光領域における光線の平均透過率が高くなり遮熱性が低下する。さらに、塗膜組成物への分散性も低下して、均一な塗膜の塗布ができず、成形性が低下する。 The titanium oxide according to the present invention has a weight average particle diameter of 0.6 to 1.5 μm. When the weight average particle diameter is less than 0.6, the average transmittance of light in the visible light region having a wavelength of 400 nm or more and less than 700 nm is lowered and the light in the near infrared light region having a wavelength of 700 nm or more and less than 2000 nm is reduced. As the average transmittance increases, the resulting agricultural covering material becomes white and the transparency decreases, which reduces the efficiency of photosynthesis in the house covered with the agricultural covering material, and further provides heat insulation. Also decreases. On the other hand, when the weight average particle diameter exceeds 1.5, the light scattering efficiency in the near infrared region decreases, and as a result, the average light transmittance in the near infrared region increases and the heat shielding property decreases. Furthermore, the dispersibility to a coating-film composition also falls, a uniform coating film cannot be applied, and a moldability falls.
また、本発明にかかる熱可塑性樹脂としては、塩化ビニル系樹脂、オレフィン系樹脂、エチレン−酢酸ビニル系共重合樹脂、ポリエステル系樹脂、フッ素系樹脂、アクリル系樹脂、ポリウレタン系樹脂が挙げられる。 Examples of the thermoplastic resin according to the present invention include vinyl chloride resin, olefin resin, ethylene-vinyl acetate copolymer resin, polyester resin, fluorine resin, acrylic resin, and polyurethane resin.
前記塩化ビニル系樹脂としては、塩化ビニルの単独重合体であるポリ塩化ビニルの他、塩化ビニルと他のモノマー、例えば、エチレン、プロピレン、酢酸ビニル、アクリル酸、メタクリル酸、アクリル酸エステル、メタクリル酸エステル、マレイン酸、マレイン酸エステル、フマール酸、イタコン酸、塩化ビニリデン、アクリロニトリル、高級ビニルエーテル等との共重合樹脂が挙げられる。このような塩化ビニル系樹脂は１種を単独で又は２種以上を混合して使用することができる。 Examples of the vinyl chloride resin include polyvinyl chloride, which is a homopolymer of vinyl chloride, and vinyl chloride and other monomers, such as ethylene, propylene, vinyl acetate, acrylic acid, methacrylic acid, acrylic ester, methacrylic acid. Examples thereof include copolymers with esters, maleic acid, maleic esters, fumaric acid, itaconic acid, vinylidene chloride, acrylonitrile, higher vinyl ethers, and the like. Such vinyl chloride resins can be used singly or in combination of two or more.
前記オレフィン系樹脂としては、低密度ポリエチレン、線状低密度ポリエチレン、中密度ポリエチレン、高密度ポリエチレン、メタロセン触媒を用いて重合したポリエチレン等のポリエチレン；ランダム重合ポリプロピレン、ブロック重合ポリプロピレン、アイソタクチックポリプロピレン、シンジオタクチックポリプロピレン等のポリプロピレン；エチレン−酢酸ビニル、エチレン−アクリル酸、エチレン−アクリル酸エステル、エチレン−メタクリル酸、エチレン−メタクリル酸エステル等のエチレン系共重合体等のオレフィン系樹脂が挙げられる。このようなオレフィン系樹脂は１種を単独で又は２種以上を混合して使用することができる。 Examples of the olefin resin include low density polyethylene, linear low density polyethylene, medium density polyethylene, high density polyethylene, polyethylene such as polyethylene polymerized using a metallocene catalyst; random polymerized polypropylene, block polymerized polypropylene, isotactic polypropylene, Examples thereof include polypropylene such as syndiotactic polypropylene; and olefin resins such as ethylene-vinyl acetate, ethylene-acrylic acid, ethylene-acrylic acid ester, ethylene-methacrylic acid, ethylene-methacrylic acid ester, and other ethylene-based copolymers. Such olefin resin can be used individually by 1 type or in mixture of 2 or more types.
また、前記エチレン−酢酸ビニル共重合体（ＥＶＡ）系樹脂としては特に制限されないが、酢酸ビニル（ＶＡ）の含有量が５〜２０質量％程度のものを好適に使用することができる。また、このようなエチレン−酢酸ビニル系共重合樹脂は１種を単独で又はエチレン含有量等が異なる２種以上のものを混合して用いることもできる。 The ethylene-vinyl acetate copolymer (EVA) -based resin is not particularly limited, but those having a vinyl acetate (VA) content of about 5 to 20% by mass can be preferably used. Further, such ethylene-vinyl acetate copolymer resins may be used alone or in combination of two or more different ethylene contents.
また、前記ポリエステル系樹脂としては特に制限されないが、ポリエチレンテレフタレートが好ましく、また、生分解性を有する脂肪族ポリエステル、芳香族−脂肪族ポリエステル等を使用することもできる。 The polyester-based resin is not particularly limited, but polyethylene terephthalate is preferable, and biodegradable aliphatic polyesters, aromatic-aliphatic polyesters, and the like can also be used.
さらに、前記フッ素系樹脂としては、四フッ化エチレン、三フッ化塩化エチレン、フッ化ビニリデン、フッ化ビニル、六フッ化プロピレン、パーフルオロビニルエーテル、その他のフッ素含有モノマーの単独重合体又は共重合体、或いはこれらのフッ素含有モノマーとフッ素を含有しないモノマーとの共重合体、例えばエチレン−四フッ化エチレン共重合体，エチレン−三フッ化塩化エチレン共重合体等が挙げられる。このようなフッ素系樹脂は１種を単独で又は２種以上を混合して使用することができる。 Further, as the fluororesin, homopolymers or copolymers of ethylene tetrafluoride, ethylene trifluoride chloride, vinylidene fluoride, vinyl fluoride, hexafluoropropylene, perfluorovinyl ether, and other fluorine-containing monomers Alternatively, copolymers of these fluorine-containing monomers and monomers not containing fluorine, such as ethylene-tetrafluoroethylene copolymer and ethylene-trifluorotrifluoroethylene copolymer, can be mentioned. Such a fluorine-type resin can be used individually by 1 type or in mixture of 2 or more types.
また、前記アクリル系樹脂としては、アクリル酸エステル、メタクリル酸エステル、アクリル酸、メタクリル酸、アクリルアミド、アクリロニトリル等の化合物の単独重合体又は前記化合物の共重合体、更には、前記化合物と、前記化合物と共重合可能な他の単量との共重合体等が挙げられる。このようなアクリル系樹脂は１種を単独で又は２種以上を混合して使用することができる。 In addition, as the acrylic resin, a homopolymer of a compound such as acrylic acid ester, methacrylic acid ester, acrylic acid, methacrylic acid, acrylamide, acrylonitrile, or a copolymer of the compound, further, the compound and the compound Copolymers with other monomers that can be copolymerized with styrene. Such acrylic resins can be used singly or in combination of two or more.
さらに、前記ポリウレタン系樹脂としては、適宜公知の二官能性ポリオールと、適宜公知のジイソシアネートとを主成分として反応させて得られる分子構造中にウレタン基を有する樹脂が挙げられる。このようなポリウレタン系樹脂は１種を単独で又は２種以上を混合して使用することができる。 Furthermore, examples of the polyurethane-based resin include resins having a urethane group in a molecular structure obtained by appropriately reacting a known bifunctional polyol and a known diisocyanate as appropriate as main components. Such polyurethane resins can be used singly or in combination of two or more.
また、本発明の効果を損ねない範囲において、前記熱可塑性樹脂を２種以上混合して使用することもできる。また、上記の熱可塑性樹脂を２層以上の多層構造として本発明の農業用被覆材を構成してもよい。例えば、熱可塑性樹脂をオレフィン系樹脂で構成した場合は、ウェルダー等の加工性を考慮して多層構造とすることが好ましい。 Moreover, in the range which does not impair the effect of this invention, the said thermoplastic resin can also be used in mixture of 2 or more types. Moreover, you may comprise the agricultural coating | covering material of this invention by making said thermoplastic resin into a multilayered structure of two or more layers. For example, when the thermoplastic resin is composed of an olefin resin, a multilayer structure is preferable in consideration of processability such as a welder.
本発明の農業用被覆材の少なくとも一方の面に設けられる塗膜は、重量平均粒子径が０．６〜１．５μｍである酸化チタンを含有する塗料を塗布することによって設けられる。塗膜の厚みとしては、１〜２０μｍが好ましい。塗膜の厚みが１μｍ未満であると、酸化チタンの重量平均粒径が０．６μｍ以上であるために、酸化チタン粒子が表面に露出して平面平滑な塗膜が形成されにくいとともに、表面が傷つきやすく農業用被覆材の透明性を低下させる可能性があり好ましくなく、２０μｍを超えると農業用被覆材を折り曲げたときに白化が発生する可能性があり好ましくない。 The coating film provided on at least one surface of the agricultural covering material of the present invention is provided by applying a paint containing titanium oxide having a weight average particle diameter of 0.6 to 1.5 μm. As thickness of a coating film, 1-20 micrometers is preferable. When the thickness of the coating film is less than 1 μm, the weight average particle diameter of titanium oxide is 0.6 μm or more. It is easy to be damaged and may reduce the transparency of the agricultural covering material, which is not preferable. If it exceeds 20 μm, whitening may occur when the agricultural covering material is bent.
この塗料は、上記粒径の酸化チタンとバインダー樹脂成分と、必要に応じて水又は有機溶媒からなる希釈溶媒から構成されている。 This paint is composed of titanium oxide having the above particle size, a binder resin component, and, if necessary, a diluting solvent composed of water or an organic solvent.
希釈溶媒は、塗料の塗布性やバインダー樹脂成分によって適宜選定される。また、酸化チタンの塗料への添加量は、形成される塗膜の厚みにより適宜決定される。例えば、塗膜厚２．０μｍの場合は、樹脂固形分１００質量部に対して、酸化チタンの添加量は１０〜３５質量部であり、塗膜厚１０μｍの場合は、樹脂固形分１００質量部に対して、酸化チタンの添加量は２〜７質量部程度である。酸化チタンの添加量が少ないと波長が７００ｍ以上２０００ｎｍ未満の近赤外光領域にある光線の平均透過率が８５％を超えてしまい、遮熱効果の面で好ましくなく、酸化チタンの添加量が多いと波長が４００ｎｍ以上７００ｎｍ未満の可視光領域にある光線の平均透過率が７５％未満となり、作物の育成が阻害される可能性が高くなり、透明性も低下してしまう。 The dilution solvent is appropriately selected depending on the coating property of the paint and the binder resin component. Further, the amount of titanium oxide added to the paint is appropriately determined depending on the thickness of the coating film to be formed. For example, when the coating thickness is 2.0 μm, the addition amount of titanium oxide is 10 to 35 parts by mass with respect to 100 parts by mass of the resin solid content, and when the coating thickness is 10 μm, the resin solid content is 100 parts by mass. On the other hand, the addition amount of titanium oxide is about 2 to 7 parts by mass. If the addition amount of titanium oxide is small, the average transmittance of light in the near-infrared light region having a wavelength of 700 m or more and less than 2000 nm exceeds 85%, which is not preferable in terms of the heat shielding effect. If the amount is too large, the average transmittance of light in the visible light region having a wavelength of 400 nm or more and less than 700 nm is less than 75%, which increases the possibility of hindering crop growth and decreases transparency.
本発明において使用されるバインダー樹脂成分としては、具体的には、アクリル樹脂（パーフルオロアクリル樹脂等も含む）系、フッ素樹脂系、塩化ビニル樹脂系、セルロース樹脂系、ポリアミド樹脂系、ウレタン樹脂系、エポキシ樹脂系、シリコーン樹脂系、ポリエステル樹脂系等の有機溶剤系（好ましくはアルコール系）塗料や水系（エマルジョン系）塗料；或いは、樹脂バインダーを含まず、水、メタノール、イソプロピルアルコール、ｎ−ブチルアルコール、イソブチルアルコール、エチレングリコール、キシレン等を分散媒とした塗料のいずれであっても使用可能である。 Specific examples of the binder resin component used in the present invention include acrylic resins (including perfluoroacrylic resins), fluororesins, vinyl chloride resins, cellulose resins, polyamide resins, and urethane resins. , Epoxy resin-based, silicone resin-based, polyester resin-based organic solvent-based (preferably alcohol-based) paints or water-based (emulsion-based) paints; or water, methanol, isopropyl alcohol, n-butyl without a resin binder Any coating material using alcohol, isobutyl alcohol, ethylene glycol, xylene or the like as a dispersion medium can be used.
前記塗料を農業用被覆材の少なくとも一方の面に塗工する方法としては、ロールコーター等の一般的に行われている方法を使用できる。 As a method for applying the paint to at least one surface of the agricultural covering material, a generally performed method such as a roll coater can be used.
また、本発明にかかる酸化チタンを含有する塗料においては、前記酸化チ
タン及びバイダー樹脂の他に、光安定剤、酸化防止剤、紫外線吸
収剤、滑剤、顔料、防滴剤、防霧剤等の各種添加剤を添加することができる。
In addition, in the paint containing titanium oxide according to the present invention, in addition to the titanium oxide and the binder resin, a light stabilizer, an antioxidant, an ultraviolet absorber, a lubricant, a pigment, a drip-proof agent, an anti-fogging agent, etc. Various additives can be added.
前記光安定剤としては、２，２，６，６−テトラメチル−４−ピペリジルステアレー、１，２，２，６，６−ペンタメチル−４−ピペリジルステアレート、２，２，６，６−テトラメチル−４−ピペリジルベンゾエート、Ｎ−（２，２，６，６−テトラメチル−４−ピペリジル）ドデシルコハク酸イミド、１−［（３，５−ジ−ｔｅｒｔ−ブチル−４−ヒドロキシフェニル）プロピオニルオキシエチル］−２，２，６，６−テトラメチル−４−ピペリジル（３，５−ジ−ｔｅｒｔ−ブチル−４−ヒドロキシフェニル）プロピオネート、ビス（２，２，６，６−テトラメチル−４−ピペリジル）セバケート、ビス（１，２，２，６，６−ペンタメチル−４−ピペリジル）セバケート、ビス（１，２，２，６，６，−ペンタメチル−４−ピペリジル）−２−ブチル−２−（３，５−ジ−ｔｅｒｔ−ブチル−４−ヒドロキシベンジル）マロネート、Ｎ，Ｎ’−ビス（２，２，６，６−テトラメチル−４−ピペリジル）ヘキサメチレンジアミン、テトラ（２，２，６，６−テトラメチル−４−ピペリジル）ブタンテトラカルボキシレート、ビス（２，２，６，６−テトラメチル−４−ピペリジル）ジ（トリデシル）ブタンテトラカルボキシレート、ビス（１，２，２，６，６−ペンタメチル−４−ピペリジル）ジ（トリデシル）ブタンテトラカルボキシレート、３，９−ビス｛１，１−ジメチル−２−［トリス（２，２，６，６−テトラメチル−４−ピペリジルオキシカルボニルオキシ）ブチルカルボニルオキシ］エチル｝−２，４，８，１０−テトラオキシサスピロ［５，５］ウンデカン、３，９−ビス｛１，１−ジメチル−２−［トリス（１，２，２，６，６−ペンタメチル−４−ピペリジルオキシカルボニルオキシ）ブチルカルボニルオキシ］エチル｝−２，４，８，１０−テトラオキサスピロ［５，５］ウンデカン、１，５，８，１２−テトラキス｛４，６−ビス［Ｎ−（２，２，６，６−テトラメチル−４−ビペリジル）ブチルアミノ］−１，３，５−トリアジン−２−イル｝−１，５，８，１２−テトラアザドデカン、１−（２−ヒドロキシエチル）−２，２，６，６−テトラメチル−４−ピペリジノール／コハク酸ジメチル縮合物、２−ｔｅｒｔ−オクチルアミノ−４，６−ジクロロ−ｓ−トリアジン／Ｎ，Ｎ’−ビス（２，２，６，６−テトラメチル−４−ピペリジル）ヘキサメチレンジアミン縮合物、Ｎ，Ｎ’−ビス（２，２，６，６−テトラメチル−４−ピペリジル）ヘキサメチレンジアミン／ジブロモエタン縮合物等のヒンダードアミン系光安定剤等が挙げられる。このようなヒンダードアミン系光安定剤の中でも、平均分子量が８００〜２０００程度のヒンダードアミン系光安定剤が好ましい。また、このような光安定剤の添加量としては、バインダー樹脂１００質量部に対して０．０１〜０．３質量部であることが好ましい。 Examples of the light stabilizer include 2,2,6,6-tetramethyl-4-piperidyl stearate, 1,2,2,6,6-pentamethyl-4-piperidyl stearate, 2,2,6,6- Tetramethyl-4-piperidylbenzoate, N- (2,2,6,6-tetramethyl-4-piperidyl) dodecylsuccinimide, 1-[(3,5-di-tert-butyl-4-hydroxyphenyl) Propionyloxyethyl] -2,2,6,6-tetramethyl-4-piperidyl (3,5-di-tert-butyl-4-hydroxyphenyl) propionate, bis (2,2,6,6-tetramethyl- 4-piperidyl) sebacate, bis (1,2,2,6,6-pentamethyl-4-piperidyl) sebacate, bis (1,2,2,6,6, -pentamethyl-4-piperidi ) -2-Butyl-2- (3,5-di-tert-butyl-4-hydroxybenzyl) malonate, N, N′-bis (2,2,6,6-tetramethyl-4-piperidyl) hexamethylene Diamine, tetra (2,2,6,6-tetramethyl-4-piperidyl) butanetetracarboxylate, bis (2,2,6,6-tetramethyl-4-piperidyl) di (tridecyl) butanetetracarboxylate, Bis (1,2,2,6,6-pentamethyl-4-piperidyl) di (tridecyl) butanetetracarboxylate, 3,9-bis {1,1-dimethyl-2- [tris (2,2,6, 6-tetramethyl-4-piperidyloxycarbonyloxy) butylcarbonyloxy] ethyl} -2,4,8,10-tetraoxysaspiro [5,5] undecane 3,9-bis {1,1-dimethyl-2- [tris (1,2,2,6,6-pentamethyl-4-piperidyloxycarbonyloxy) butylcarbonyloxy] ethyl} -2,4,8,10 -Tetraoxaspiro [5,5] undecane, 1,5,8,12-tetrakis {4,6-bis [N- (2,2,6,6-tetramethyl-4-biperidyl) butylamino] -1 , 3,5-triazin-2-yl} -1,5,8,12-tetraazadodecane, 1- (2-hydroxyethyl) -2,2,6,6-tetramethyl-4-piperidinol / succinic acid Dimethyl condensate, 2-tert-octylamino-4,6-dichloro-s-triazine / N, N′-bis (2,2,6,6-tetramethyl-4-piperidyl) hexamethylenediamine condensate, N , N′− Examples thereof include hindered amine light stabilizers such as bis (2,2,6,6-tetramethyl-4-piperidyl) hexamethylenediamine / dibromoethane condensate. Among such hindered amine light stabilizers, hindered amine light stabilizers having an average molecular weight of about 800 to 2000 are preferable. Moreover, as an addition amount of such a light stabilizer, it is preferable that it is 0.01-0.3 mass part with respect to 100 mass parts of binder resin.
前記酸化防止剤としては、アルキルフェノール、アルキレンビスフェノール、アルキルフェノールチオエーテル、β，β’−チオプロピオン酸エステル、有機亜リン酸エステル、芳香族アミン、フェノール・ニッケル複合体等が挙げられる。このような酸化防止剤は、１種を単独で又は２種以上を混合して使用することができる。 Examples of the antioxidant include alkylphenols, alkylene bisphenols, alkylphenol thioethers, β, β'-thiopropionic acid esters, organic phosphites, aromatic amines, phenol / nickel composites, and the like. Such antioxidant can be used individually by 1 type or in mixture of 2 or more types.
前記紫外線吸収剤としては、サリチル酸エステル、ベンゾトリアゾール、ヒドロキシベンゾフェノン、アクリロニトリル置換体等が挙げられる。このような紫外線吸収剤は、１種を単独で又は２種以上を混合して使用することができる。具体的には、２，４−ジヒドロキシベンゾフェノン、２−ヒドロキシ−４−メトキシベンゾフェノン、２−ヒドロキシ−４−エトキシベンゾフェノン、２−ヒドロキシ−４−オクトキシベンゾフェノン、５，５’−メチレンビス（２−ヒドロキシ−４−メトキシベンゾフェノン）等の２−ヒドロキシベンゾフェノン類；２−（２’−ヒドロキシ−５’−メチルフェニル）ベンゾトリアゾール、２−（２’−ヒドロキシ−３’，５’−ジ−ｔｅｒｔ−ブチルフェニル）−５−クロロベンゾトリアゾール、２−（２’−ヒドロキシ−３’−ｔｅｒｔ−ブチル−５’−メチルフェニル）−５−クロロベンゾトリアゾール、２−（２’−ヒドロキシ−５’−ｔｅｒｔ−オクチルフェニル）ベンゾトリアゾール、２−（２’−ヒドロキシ−３’，５’−ジクミルフェニル）ベンゾトリアゾール、２，２’−メチレンビス（４−ｔｅｒｔ−オクチル−６−ベンゾトリアゾール）フェノール等の２−（２’−ヒドロキシフェニル）ベンゾトリアゾール類；フェニルサリチレート、レゾルシノールモノベンゾエート、２，４−ジ−ｔｅｒｔ−ブチルフェニル−３’，５’−ジ−ｔｅｒｔ−ブチル−４’−ヒドロキシベンゾエート、ヘキサデシル−３，５−ジ−ｔｅｒｔ−ブチル−４−ヒドロキシベンゾエート等のベンゾエート類；２−エトキシ−４’−ドデシルオキザニリド等のオキザニリド類；エチル−α−シアノ−β，β−ジフェニルアクリレート、メチル−２−シアノ−３−メチル−３−（ｐ−メトキシフェニル）アクリレート等のシアノアクリレート類が挙げられる。 Examples of the ultraviolet absorber include salicylic acid esters, benzotriazoles, hydroxybenzophenones, acrylonitrile substituted products, and the like. Such an ultraviolet absorber can be used individually by 1 type or in mixture of 2 or more types. Specifically, 2,4-dihydroxybenzophenone, 2-hydroxy-4-methoxybenzophenone, 2-hydroxy-4-ethoxybenzophenone, 2-hydroxy-4-octoxybenzophenone, 5,5′-methylenebis (2-hydroxy 2-hydroxybenzophenones such as -4-methoxybenzophenone); 2- (2′-hydroxy-5′-methylphenyl) benzotriazole, 2- (2′-hydroxy-3 ′, 5′-di-tert-butyl) Phenyl) -5-chlorobenzotriazole, 2- (2′-hydroxy-3′-tert-butyl-5′-methylphenyl) -5-chlorobenzotriazole, 2- (2′-hydroxy-5′-tert-) Octylphenyl) benzotriazole, 2- (2′-hydroxy-3 ′, 5′- 2- (2′-hydroxyphenyl) benzotriazoles such as cumylphenyl) benzotriazole, 2,2′-methylenebis (4-tert-octyl-6-benzotriazole) phenol; phenyl salicylate, resorcinol monobenzoate, 2, Benzoates such as 4-di-tert-butylphenyl-3 ′, 5′-di-tert-butyl-4′-hydroxybenzoate, hexadecyl-3,5-di-tert-butyl-4-hydroxybenzoate; Oxanilides such as ethoxy-4'-dodecyloxanilide; Cyanoacrylates such as ethyl-α-cyano-β, β-diphenylacrylate, methyl-2-cyano-3-methyl-3- (p-methoxyphenyl) acrylate Kind.
前記滑剤又は前記粘着防止剤としては、ステアリン酸亜鉛、ステアリン酸バリウム、ステアリン酸カルシウム等の金属石鹸；流動パラフィン、ポリエチレンワックス類、塩素化炭化水素類等の炭化水素類；ステアリン酸、ステアリン酸アミド、パルミチン酸アミド、メチレンビスステアロアミド、エチレンビスステアロアミド等の脂肪酸及び脂肪酸アミド；ステアリン酸ブチル、パルミチン酸セチル、ステアリン酸モノグリセリド等の脂肪酸エステル；ステアリン酸、イソステアリン酸、パルミチン酸等の脂肪酸系滑剤；バリウムイソデシルホスフェート、カルシウムオクタデシルホスフェート等の有機リン酸金属塩系滑剤等の滑剤が使用できる。このような滑剤又は粘着防止剤は、１種を単独で又は２種以上を混合して使用することができる。 Examples of the lubricant or the anti-adhesive agent include metal soaps such as zinc stearate, barium stearate, calcium stearate; hydrocarbons such as liquid paraffin, polyethylene waxes, chlorinated hydrocarbons; stearic acid, stearamide, Fatty acids and fatty acid amides such as palmitic acid amide, methylene bisstearamide, ethylene bisstearamide; Fatty acid esters such as butyl stearate, cetyl palmitate, monoglyceride stearate; Fatty acids such as stearic acid, isostearic acid, palmitic acid Lubricants: Lubricants such as organophosphate metal salt lubricants such as barium isodecyl phosphate and calcium octadecyl phosphate can be used. Such lubricants or anti-sticking agents can be used alone or in combination of two or more.
前記防滴剤としては、ソルビタン脂肪酸エステル、ソルビトール脂肪酸エステル、グリセリン脂肪酸エステル、ジグリセリン脂肪酸エステル、トリグリセリン脂肪酸エステル、テトラグリセリン脂肪酸エステル等のポリグリセリン脂肪酸エステル；ソルビタン脂肪酸・二塩基酸エステル、ソルビトール脂肪酸・二塩基酸エステル、ジグリセリン脂肪酸・二塩基酸エステル等の多価アルコールと脂肪酸とのエステルや多価アルコールと脂肪酸及び二塩基酸とのエステル；或いはこれらにエチレンオキサイド、プロピレンオキサイド、ブチレンオキサイド等のアルキレンオキサイドが付加された化合物等が挙げられ、具体的には、ソルビタンパルミテート、ソルビタンステアレート、ソルビタンステアレート・エチレンオキサイド２モル付加物、ソルビタンステアレート・プロピレンオキサイド３モル付加物、ソルビトールステアレート、ソルビトールステアレート・エチレンオキサイド３モル付加物、ジグリセリンパルミテート・エチレンオキサイド２モル付加物、ソルビタンステアレートアジペート・エチレンオキサイド２モル付加物、ジグリセリンパルミテートセバケート・プロピレンオキサイド３モル付加物、ソルビトールパルミテートアジペート・エチレンオキサイド３モル付加物等があげられる。このような防滴剤は、１種を単独で又は２種以上を混合して使用することができる。また、このような防滴剤の添加量としては、バインダー樹脂１００質量部に対し、０．５〜６質量部程度が好ましい。 Examples of the drip-proofing agent include sorbitan fatty acid ester, sorbitol fatty acid ester, glycerin fatty acid ester, diglycerin fatty acid ester, triglycerin fatty acid ester, tetraglycerin fatty acid ester, and the like; sorbitan fatty acid / dibasic acid ester, sorbitol fatty acid -Esters of polyhydric alcohols and fatty acids such as dibasic acid esters, diglycerin fatty acids and dibasic acid esters, esters of polyhydric alcohols and fatty acids and dibasic acids; or ethylene oxide, propylene oxide, butylene oxide, etc. In particular, sorbitan palmitate, sorbitan stearate, sorbitan stearate / ethylene oxide 2 mol adduct, Rubitan stearate / propylene oxide 3 mol adduct, sorbitol stearate, sorbitol stearate / ethylene oxide 3 mol adduct, diglycerin palmitate / ethylene oxide 2 mol adduct, sorbitan stearate adipate / ethylene oxide 2 mol adduct And diglycerin palmitate sebacate / propylene oxide 3 mol adduct, sorbitol palmitate adipate / ethylene oxide 3 mol adduct, and the like. Such drip-proofing agents can be used alone or in combination of two or more. Moreover, as addition amount of such a dripproofing agent, about 0.5-6 mass parts is preferable with respect to 100 mass parts of binder resin.
前記防霧剤としては、一分子中に含フッ素基と、水酸基及びアルキレンオキサイド基のうちの少なくとも一種の基とを有する含フッ素化合物が挙げられる。前記含フッ素基としては、パーフルオロアルキル基（ＣｎＦ２ｎ＋１基）、パーフルオロアルコキシル基（ＣｎＦ２ｎ＋１Ｏ基）、ポリフルオロアルキル基（ＨｍＣｎＦ２ｎ＋１−ｍ基）、パーフルオロアルケニル基（ＣｎＦ２ｎ−１基）、ポリフルオロアルケニル基（ＨｍＣｎＦ２ｎ−１−ｍ基）等が挙げられる。なお、前記含フッ素基の式中のｍは１〜３の整数を示し、ｎは３〜２０の整数を示す。また、前記アルキレンオキサイド基としては、一般式（Ｃ２Ｈ４Ｏ）ｘ又は（Ｃ３Ｈ６Ｏ）ｘで表される基が挙げられる。また、前記一般式中のｘは１〜３０の整数を示す。このような含フッ素化合物の添加量は、バインダー樹脂１００質量部に対して０．０１〜１質量部が好ましく、更に好ましくは０．０５〜０．５質量部程度で
ある。
Examples of the anti-fogging agent include a fluorine-containing compound having a fluorine-containing group and at least one group selected from a hydroxyl group and an alkylene oxide group in one molecule. Examples of the fluorine-containing group include a perfluoroalkyl group (C n F 2n + 1 group), a perfluoroalkoxyl group (C n F 2n + 1 O group), a polyfluoroalkyl group (H m C n F 2n + 1-m group), and perfluoro alkenyl group (C n F 2n-1 group), polyfluoroalkenyl group (H m C n F 2n- 1-m group). In the formula of the fluorine-containing group, m represents an integer of 1 to 3, and n represents an integer of 3 to 20. As examples of the alkylene oxide group, the general formula (C 2 H 4 O) x, or a group represented by (C 3 H 6 O) x and the like. Moreover, x in the said general formula shows the integer of 1-30. The addition amount of such a fluorine-containing compound is preferably 0.01 to 1 part by mass, more preferably about 0.05 to 0.5 part by mass with respect to 100 parts by mass of the binder resin.
また、他の添加剤としては、ハイドロタルサイトや長石等の鉱物系の添加剤や、グリシジルアクリレート及び／又はグリシジルメタアクリレートのホモポリマー及び／又はコポリマー等が挙げられる。このようなグリシジルアクリレート及び／又はグリシジルメタアクリレートのホモポリマー及び／又はコポリマーとしては、平均分子量が１０００以上のものが好ましい。特に、グリシジルメタアクリレートのホモポリマーが好適である。またグリシジルアクリレート及び／又はグリシジルメタアクリレートのホモポリマー及び／又はコポリマーの添加量としては、熱可塑性樹脂１００重量部に対し、０．１〜１０重量部
であり、好ましくは０．５〜５重量部である。熱可塑性樹脂１００重量部に対するグリシジルアクリレート及び／又はグリシジルメタアクリレートのホモポリマー及び／又はコポリマーの添加量が、前記下限未満では耐久性の向上が見られず、長時間混練りすると粘着する傾向にある。他方、熱可塑性樹脂１００重量部に対するグリシジルアクリレート及び／又はグリシジルメタアクリレートのホモポリマー及び／又はコポリマーの添加量が前記上限を超えると、コストが高くなる割には耐久性の向上が小さく、成形加工時の着色が起こる傾向にある。
Other additives include mineral additives such as hydrotalcite and feldspar, and homopolymers and / or copolymers of glycidyl acrylate and / or glycidyl methacrylate. As such a homopolymer and / or copolymer of glycidyl acrylate and / or glycidyl methacrylate, those having an average molecular weight of 1000 or more are preferable. In particular, a homopolymer of glycidyl methacrylate is preferable. The addition amount of the homopolymer and / or copolymer of glycidyl acrylate and / or glycidyl methacrylate is 0.1 to 10 parts by weight, preferably 0.5 to 5 parts by weight with respect to 100 parts by weight of the thermoplastic resin. It is. When the addition amount of the homopolymer and / or copolymer of glycidyl acrylate and / or glycidyl methacrylate is less than the lower limit relative to 100 parts by weight of the thermoplastic resin, no improvement in durability is observed, and there is a tendency to stick when kneaded for a long time. . On the other hand, when the addition amount of the homopolymer and / or copolymer of glycidyl acrylate and / or glycidyl methacrylate with respect to 100 parts by weight of the thermoplastic resin exceeds the above upper limit, the improvement in durability is small for the cost increase, and molding processing Coloring of time tends to occur.
熱可塑性樹脂フィルムを成形する方法としては特に制限されず、カレンダー法、押出法、インフレーション法等の適宜公知の成形方法を採用することができる。また、熱可塑性樹脂としてオレフィン系樹脂を用いる場合には加工性や、得られる製品の幅（幅１２ｍ程度とする場合）等の観点から、インフレーション法を採用することが好ましい。 A method for molding the thermoplastic resin film is not particularly limited, and a known molding method such as a calendar method, an extrusion method, an inflation method, or the like can be appropriately employed. Further, when an olefin resin is used as the thermoplastic resin, it is preferable to adopt an inflation method from the viewpoints of processability and the width of the product to be obtained (when the width is about 12 m).
また、本発明の農業用被覆材としては、前記熱可塑性樹脂フィルムとしてポリオレフィン系樹脂フィルムを使用する場合には、ウェルダー等の加工性や物性を考慮すると、多層構造とすることが好ましく、例えば、少なくとも２層以上の熱可塑性樹脂フィルムを備え、該熱可塑性樹脂フィルムのうちの少なくとも１層がポリオレフィン系樹脂フィルムとすればよい。 Moreover, as an agricultural covering material of the present invention, when using a polyolefin resin film as the thermoplastic resin film, it is preferable to have a multilayer structure in consideration of processability and physical properties such as a welder. At least two or more thermoplastic resin films may be provided, and at least one of the thermoplastic resin films may be a polyolefin resin film.
また、本発明の農業用被覆材を多層構造とする場合においては、他の層を構成する樹脂の種類は前記熱可塑性樹脂フィルムと同じであっても異なるものであってもよい。更に本発明の農業用被覆材を多層構造とする場合においては、相隣接する層が相互に相溶性又は接着性の高い層とすることが好ましい。 In the case where the agricultural covering material of the present invention has a multilayer structure, the type of resin constituting the other layer may be the same as or different from that of the thermoplastic resin film. Further, when the agricultural coating material of the present invention has a multilayer structure, it is preferable that adjacent layers are layers having high compatibility or adhesiveness.
このような多層構造の農業用被覆材を製造する方法としては特に制限されず、適宜公知の方法を採用することができ、例えば、多層共押出インフレーション法等の成形方法で一度に多層構造のフィルムを製造してもよく、また、単層の熱可塑性樹脂フィルムを成形した後にラミネート等して多層構造のフィルムを製造してもよい。 A method for producing such a multi-layered agricultural covering material is not particularly limited, and a known method can be used as appropriate. For example, a film having a multi-layered structure at a time by a molding method such as a multi-layer coextrusion inflation method. Alternatively, a film having a multilayer structure may be produced by forming a single layer thermoplastic resin film and then laminating it.
また、本発明の農業用被覆材としては、波長が４００ｎｍ以上７００ｎｍ未満の可視光領域にある光線の平均透過率が７５％以上であり、且つ波長が７００ｎｍ以上２０００ｎｍ未満の近赤外光領域にある光線の平均透過率が８５％以下でることが好ましい。可視光領域にある光線の平均透過率が７５％未満では、得られる農業用被覆材が農作物の育成に必要な光線が十分に透過することができない傾向にあり、他方、近赤外光領域にある光線の平均透過率が８５％を超えると、得られる農業用被覆材で覆われた領域において十分な遮熱性が得られず、作物の外観不良や生育障害となる可能性があると共に、作物の成長阻害が発生するか、遮熱効果が得られず、過温による根の成長阻害が発生する可能性が高くなり好ましくない。 Moreover, as the agricultural covering material of the present invention, the average transmittance of light in the visible light region having a wavelength of 400 nm or more and less than 700 nm is 75% or more, and in the near infrared light region having a wavelength of 700 nm or more and less than 2000 nm. It is preferable that the average transmittance of a certain light beam is 85% or less. When the average transmittance of light rays in the visible light region is less than 75%, the obtained agricultural coating material tends not to sufficiently transmit the light rays necessary for growing crops, while in the near infrared light region. If the average transmittance of a certain light beam exceeds 85%, sufficient heat shielding properties cannot be obtained in the area covered with the resulting agricultural covering material, which may cause crop appearance defects and growth obstacles. This is not preferable because the growth inhibition of the root occurs or the heat shielding effect cannot be obtained and the possibility of the root growth inhibition due to overheating increases.
また、波長が７００ｎｍ以上２０００ｎｍ未満の近赤外光領域にある光線の透過光のうち直達光の平均透過率が４０％以上７５％以下であることが好ましく、これにより、ハウス内の作物の葉焼けなどの外観不良を防止することが可能となると共に、地中温度の上昇を抑制する事が可能となり、特に育苗ポット内の温度上昇を抑制することができるので、夏期に育苗されるイチゴ苗等の育苗に好適に使用することができる農業用被覆材である。 Moreover, it is preferable that the average transmittance of direct light among the transmitted light in the near-infrared light region having a wavelength of 700 nm or more and less than 2000 nm is 40% or more and 75% or less. It is possible to prevent appearance defects such as burning, and it is possible to suppress an increase in underground temperature, and in particular, it is possible to suppress an increase in temperature in the seedling pot, so that strawberry seedlings grown in summer An agricultural covering material that can be suitably used for raising seedlings.
本発明の農業用被覆材の厚みとしては特に制限されず、塗膜への酸化チタンの配合量と塗膜の厚みにより、所望の光線透過率に設定することが可能となるので、用途により適宜選定することができるが、例えば、５０〜２００μｍであることが好ましく、７５〜１５０μｍであることがより好ましい。本発明の農業用フィルムの厚みが前記下限未満では、得られる農業用被覆材の引張強度等の物性が低下し、使用時の展張作業が困難となる傾向にあり、他方、前記上限を超えると、得られた農業用フィルムが重くなるため、使用時の展張作業が困難となる傾向にある。なお、本発明の農業用被覆材を多層構造とする場合においては、本発明の効果を確実に発揮させるという観点から、本発明にかかる熱可塑性樹脂フィルムが５０〜１５０μｍの厚みを有することが好ましい。 The thickness of the agricultural coating material of the present invention is not particularly limited, and can be set to a desired light transmittance depending on the amount of titanium oxide added to the coating film and the thickness of the coating film. Although it can select, it is preferable that it is 50-200 micrometers, for example, and it is more preferable that it is 75-150 micrometers. If the thickness of the agricultural film of the present invention is less than the lower limit, physical properties such as tensile strength of the resulting agricultural covering material tend to decrease, and the stretching work during use tends to be difficult. Since the obtained agricultural film becomes heavy, it tends to be difficult to perform the expansion work at the time of use. In addition, when making the agricultural coating | covering material of this invention into a multilayer structure, it is preferable that the thermoplastic resin film concerning this invention has thickness of 50-150 micrometers from a viewpoint of exhibiting the effect of this invention reliably. .
以下、実施例及び比較例に基づいて本発明をより具体的に説明するが、本発明は以下の実施例に限定されるものではない。また、各実施例及び各比較例で得られた農業用被覆材は以下のようにして評価した。 EXAMPLES Hereinafter, although this invention is demonstrated more concretely based on an Example and a comparative example, this invention is not limited to a following example. Moreover, the agricultural coating | covering material obtained by each Example and each comparative example was evaluated as follows.
＜光線透過率の評価＞
各実施例及び各比較例で得られた農業用被覆材の全光線透過率を分光光度計（日本分光社製：商品名「Ｖ−５７０」）を用いて測定した。得られた結果のうち、波長３８０〜４００ｎｍの光線の平均透過率と、波長が４００ｎｍ以上７００ｎｍ未満の可視光領域の光線の平均透過率と、波長が７００ｎｍ以上２０００ｎｍ未満の近赤外光領域の光線の平均透過率と、波長が７００ｎｍ以上２０００ｎｍ未満の近赤外光領域の透過光線のうち直達光の平均透過率とをそれぞれ表１に示す。
<Evaluation of light transmittance>
The total light transmittance of the agricultural covering material obtained in each example and each comparative example was measured using a spectrophotometer (manufactured by JASCO Corporation: trade name “V-570”). Among the obtained results, the average transmittance of light having a wavelength of 380 to 400 nm, the average transmittance of light in the visible light region having a wavelength of 400 nm to less than 700 nm, and the near infrared light region having a wavelength of 700 nm to less than 2000 nm. Table 1 shows the average transmittance of light and the average transmittance of direct light among transmitted light in the near-infrared light region having a wavelength of 700 nm or more and less than 2000 nm.
［実施例１〜４及び比較例１〜５］
実施例１〜４及び比較例１〜５では、表１に示す配合量の塗膜組成物を酢酸エチル／イソプロピルアルコールが５０／５０からなる希釈混合液１００質量部に対して、各塗膜組成物を１５質量部になるように調整し、農業用被覆材（製品名：ノンキリーあすか、フィルム厚み０．１ｍｍ、アキレス株式会社）に、グラビアコート法により塗工し、次いで９０℃３０秒間乾燥を行い、厚さ２μｍの塗膜を有する各実施例の農業用被覆材を作成した。
[Examples 1 to 4 and Comparative Examples 1 to 5]
In Examples 1 to 4 and Comparative Examples 1 to 5, the coating composition having the blending amounts shown in Table 1 was used for each coating composition with respect to 100 parts by weight of a diluted mixed solution composed of 50/50 ethyl acetate / isopropyl alcohol. The product is adjusted to 15 parts by mass, coated on an agricultural covering material (product name: NON-KILLY Asuka, film thickness 0.1 mm, Achilles Co., Ltd.) by the gravure coating method, and then dried at 90 ° C. for 30 seconds. The agricultural coating material of each Example having a coating film with a thickness of 2 μm was prepared.
得られた農業用被覆材の光線透過率を測定しその結果を表１に示す。 The light transmittance of the obtained agricultural coating material was measured and the results are shown in Table 1.
表１に示す結果からも明らかなように、本発明の農業用被覆材の可視光領域の光線の平均透過率はいずれも７５％以上と高く、且つ近赤外光領域の光線の平均透過率がいずれも８５％以下と低く、さらに近赤外線領域の光線の透過光のうち直達光の平均透過率が７５％以下であるので、本発明の農業用被覆材は、波長が近赤外光領域にある光線を過度に透過させることなく波長が可視光領域にある光線を十分に透過させることができることが確認された。また、このような可視光領域の光線の平均透過率の値から本発明の農業用被覆材は透明性が高いことが確認された。したがって、本発明の農業用フィルムは、透明性が高く、遮熱効果に優れたものであることが確認された。 As is clear from the results shown in Table 1, the average transmittance of light in the visible light region of the agricultural coating material of the present invention is as high as 75% or more, and the average transmittance of light in the near infrared light region. Are both as low as 85% or less, and the average transmittance of direct light among the transmitted light of the light in the near infrared region is 75% or less. Therefore, the agricultural coating material of the present invention has a wavelength in the near infrared region. It was confirmed that a light beam having a wavelength in the visible light region can be sufficiently transmitted without excessively transmitting the light beam in the region. Moreover, from the value of the average transmittance | permeability of the light ray of such a visible light area | region, it was confirmed that the agricultural coating | covering material of this invention has high transparency. Therefore, it was confirmed that the agricultural film of the present invention has high transparency and an excellent heat shielding effect.
他方、酸化チタンの含有量がバインダー樹脂１００質量部に対して１０質量部未満の比較例１，２においては、近赤外線領域の光線の平均透過率が８５％以上となり、遮熱効果の面で不足していることが確認され、近赤外光領域の直達光の平均透過率が７５％を超えてしまい、作物の成長阻害の可能性があると思われる。比較例３，４において、酸化チタンの含有量がバインダー樹脂１００質量部に対して３５質量部を超えているので、可視光領域の光線の平均透過率が７５％未満になってしまい作物の生育に支障をきたす可能性が有り好ましくない。 On the other hand, in Comparative Examples 1 and 2 in which the content of titanium oxide is less than 10 parts by mass with respect to 100 parts by mass of the binder resin, the average transmittance of light in the near-infrared region is 85% or more. The shortage is confirmed, and the average transmittance of direct light in the near-infrared light region exceeds 75%, which seems to possibly inhibit the growth of crops. In Comparative Examples 3 and 4, since the content of titanium oxide exceeds 35 parts by mass with respect to 100 parts by mass of the binder resin, the average transmittance of light in the visible light region becomes less than 75%, and the growth of the crop It is not preferable because it may cause trouble.
比較例５において、酸化チタンの重量平均粒子径が０．６μｍ以下であるので、実施例２と当量添加したものでも、全ての光線透過率で問題のあるものであった。 In Comparative Example 5, since the weight average particle diameter of titanium oxide was 0.6 μm or less, even when added in an equivalent amount to Example 2, there was a problem in all light transmittances.
以上説明したように、本発明によれば、酸化チタンを含有する塗膜を有する農業用被覆材であるにも拘らず、波長が赤外光領域にある光線を過度に透過させることなく波長が可視光領域にある光線を十分に透過させることができ、しかも十分な透明性と優れた遮熱性とを有することを可能とする農業用被覆材を提供することが可能となる。 As described above, according to the present invention, although the coating material for agriculture has a coating film containing titanium oxide, the wavelength is not excessively transmitted through the light beam in the infrared region. It is possible to provide an agricultural covering material that can sufficiently transmit light rays in the visible light region and that has sufficient transparency and excellent heat shielding properties.
従って、本発明の農業用被覆材は、例えば農業用ハウスに用いた場合にはハウス内の温度上昇を抑えつつ農作物の育成に必要な波長が可視光領域にある光線を十分に透過させることが可能となり、地温に対しても直達光を減少させているので、育苗ポットを使用した育苗にも優れている等、農業用ハウスやトンネル等の農業用施設に用いる農業用被覆材として有用である。 Therefore, when the agricultural covering material of the present invention is used for, for example, an agricultural house, it can sufficiently transmit light having a wavelength necessary for growing crops in the visible light region while suppressing temperature rise in the house. It is possible to reduce the direct light with respect to the ground temperature, so it is also excellent for raising seedlings using seedling pots and is useful as an agricultural covering material for agricultural facilities such as agricultural houses and tunnels. .
Claims (3)