JP4664711B2 - セメント系材料の被覆養生剤及び当該被膜養生剤の施工方法 - Google Patents
セメント系材料の被覆養生剤及び当該被膜養生剤の施工方法 Download PDFInfo
- Publication number
- JP4664711B2 JP4664711B2 JP2005070203A JP2005070203A JP4664711B2 JP 4664711 B2 JP4664711 B2 JP 4664711B2 JP 2005070203 A JP2005070203 A JP 2005070203A JP 2005070203 A JP2005070203 A JP 2005070203A JP 4664711 B2 JP4664711 B2 JP 4664711B2
- Authority
- JP
- Japan
- Prior art keywords
- curing agent
- cement
- coating curing
- coating
- curing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
特に気温が高い時や、湿度の低い時等においては、水分の蒸発が早いためひび割れが生じやすい。
また、道路舗装等の工期を短縮する場合や、二次製品工場での型枠の回転を早くする場合には、硬化初期の水分蒸発量を抑制することで、強度発現性が良く、強度も高くなり、その目的を達成することができる。
シート養生については、長期に養生する際には、シートを現場にそのまま放置することが必要であり、また、施工面積が増大するにつれて使用するシートも増加し、作業が面倒で管理に手間がかかり、硬化後はシートの撤去が必要であるため、作業が煩雑で、広い面積範囲の養生には適さない。
更に、当該シート養生においても、気温が高い時等には、セメント系材料の表面の乾燥状態によって、散水する必要があり、シートが風で飛ばされる等のトラブルも発生する。
かかる養生剤は、モルタルやコンクリートの施工直後から養生を行うことができるとされており、水分の蒸発抑制効果がある程度得られるものであるが、水分の補給をすることができないため、表層部においてセメントの水和に必要な水分が不足し、セメントの水和反応が十分に進行しないため、強度発現が低くなり、脆弱層が形成されてしまう。
しかし、セルロースを用いており、当該セルロースは保水性能があり水分蒸発を抑制できる一方、セメントに対して硬化遅延作用を引き起こす場合があり、強度の早期発現が困難となる場合がある。
このような表面改質剤としては、珪酸ソーダや珪酸リチウムのような珪酸アルカリ金属水溶液のものが多く使用されており、例えば、特開昭60−108384号公報には、珪酸アルカリ水溶液にポリマーエマルションを添加した処理液を、すでに硬化したセメント系材料の表面から含浸させ、これを乾燥させることで表面層を改質して強化する方法が提案されている。
しかし、上記特開昭60−108384号公報記載の方法は、セメント系材料が水硬反応によって硬化した後に使用するものであり、また硬化後に使用した場合の表面強度発現効果も低い。
また本発明の他の目的は、取り扱いが容易で、上記被覆養生剤の特性を有効に発現させることができ、高強度で耐久性の高い構造物を得ることができる簡便な施工方法を提供することである。
すなわち、本発明のセメント系材料の被膜養生剤は、セメント系材料の打設から凝結が始まるまでの間に、セメント系材料の表面に塗布又は散布する被覆養生剤であって、ポリマーエマルション及びリチウム塩及びセメント水和用硬化促進剤を含む(但し、顔料は含まない)ことを特徴とするものである。
更に好適には、上記本発明のセメント系材料の被覆養生剤は、硬化促進剤を0.1〜2.0質量%含有することを特徴とする。
さらに、硬化促進剤を配合することにより、より水分抑止効果を高めて表面層を強化させることを可能とする。
また本発明の被覆養生剤の施工方法は、取り扱いが容易であり、簡便に施工でき、硬化前のフレッシュな状態のセメント系材料の塗布等することで、上記本発明の被覆養生剤の効果を一層有効に発現させることができる。
本発明のセメント系材料の被覆養生剤は、ポリマーエマルション及びリチウム塩及びセメント水和用硬化促進剤を含む(但し、顔料は含まない)養生剤であり、セメント系材料の打設から凝結が始まるまでの間に、セメント系材料の表面に塗布又は散布する被覆養生剤である。
当該ポリマーエマルションは、水にポリマーを分散させた状態であるので、被膜養生剤の水分が蒸発し、ポリマー粒子同士が結合しポリマーフィルムを形成するため、セメント系材料表面から水分蒸発を抑制することができる。
また、酢酸ビニル系樹脂としては、ポリ酢酸ビニル、酢酸ビニル・エチレン共重合樹脂、変性酢酸ビニル樹脂、酢酸ビニル・ベオバ共重合樹脂、酢酸ビニル・アクリル酸エステル共重合樹脂等が挙げられる。
また、ポリビニルアルコール系樹脂としては、完全ケン化型、中間ケン化型、部分ケン化型のいずれの型のものも使用できる。
これは被覆養生剤中のポリマー固形分が50質量%を超えると、ポリマー被膜が厚くなり過ぎ、また5質量%未満となるとポリマー被膜が薄くなり過ぎ、被覆養生剤としての性能が低下する場合があるからである。
これらのリチウム塩は、リチウムイオンが空気中の水分と結合しやすい性質を有しており、この空気中の水分が集まってくることにより、セメント系材料の水分蒸発が抑制され、良好な強度発現性が得られ高強度となる。
また、リチウムイオンは、セメントの水和に対して、凝結遅延作用はなく、逆に硬化促進効果を有する。
かかる硬化促進剤としては、無機塩系硬化促進剤と有機塩系硬化促進剤とのいずれのものも使用でき、これを単独でまたは複数混合して用いることができる。
無機塩系硬化促進剤としては、カルシウム、ナトリウム、カリウム等の硝酸塩、亜硝酸塩、チオ硫酸塩、チオシアン酸塩等が例示できる。
また、有機塩系硬化促進剤としては、ジエタノールアミン、トリエタノールアミン等のアミン類、ギ酸、酢酸、アクリル酸などの有機酸のカルシウム塩等があり、セメントの水和反応を促進する化合物として公知のこれらの化合物を用いることができる。
その配合量としては、使用される硬化促進剤の種類に応じて異なり、特に限定されるものではないが、上記被覆養生剤中、好適には0.1〜2.0質量%、より好適には0.5〜1.5質量%の量で混入させることが好ましい。
これは、2.0質量%を超えて多量に混入した場合、逆に遅延作用により表面層の強度を低下させることがあるからである。
また、本発明の効果に悪影響を及ぼさない限り、乾燥収縮低減剤等の添加剤を添加することもできる。
本発明においては、本発明の被覆養生剤は、セメント系材料がまだ硬化しないフレッシュな状態、すなわちセメント系材料の打設から凝結が始まるまでの間に、塗布または散布する。
このようにセメント系材料が硬化しないうちに、被覆養生剤を塗布または散布することにより、含有されるポリマーの被膜がセメント系材料の表面に均一に形成されるとともに、リチウムイオンの吸湿性能により、空気中の水分が集まる作用を利用することで、水分蒸発抑制と水分補給により、良好な強度発現性が得られ高強度となる。
かかる被覆養生剤をセメント系材料に塗布または散布する方法としては、セメント系材料に均一に塗布または散布できるのであれば、手段は限定されず、刷毛やローラー等の通常の塗布手段や、公知のスプレー噴霧及びポンプ吹付け機等による散布等、通常行なわれる方法を任意に選択することにより、施工することができる。
使用材料
被覆養生剤を調製し、試験するにあたり、以下の材料を使用した。
・ポリマーセメント:ライオンGRLC−SP(住友大阪セメント社製)
・ポリマーエマルション原料:モビニール701(アクリル共重合体 固形分46質量% クラリアントポリマー社製)
・リチウム塩:リチウムシリケート45(珪酸リチウム SiO2/Li2Oモル比:4.5 日産化学社製)
・硬化促進剤:ギ酸カルシウム(試薬:キシダ化学社製)
表1に示すような配合割合で、上記ポリマーエマルション原料(モビニール701)に水を添加してポリマーの固形分が、得られるセメント系被覆材料中20質量%となるように調整し、上記リチウム塩(珪酸リチウム)及び上記硬化促進剤を更に添加し、各材料を均一に混合して、各セメント系被覆養生剤を調製した。
一方、上記ポリマーセメント25kgに標準配合の水量を加え、30℃、25%RHの室内で均一に混練し、得られたモルタルを、20×15×3cmの簡易型枠を用いて打設した。
前記モルタル打設1時間後、まだ硬化していないモルタル供試体表面に、表1に示す配合の実施例1、参考例1で得られた当該各被覆養生剤を刷毛により200g/m2の量で均一に塗布した。
参考例1で用いたと同様の打設モルタルに、被覆養生剤を何も塗布しないものを比較例1とした。
比較例2
表1の配合割合で被覆養生剤を調製して用いた以外は、参考例1と同様にして、モルタル供試体表面に各被覆養生剤を塗布した。
比較例3
参考例1と同様にしてモルタルを打設し、そのまま30℃、25%RHの室内での条件下で3日間養生し、参考例1と同様の被覆養生剤をモルタル打設3日後に塗布した以外は、参考例1と同様に行って、被覆養生剤をモルタル硬化後に塗布したものを比較例3とした。
(モルタルの水分蒸発率の試験方法)
実施例1、参考例1及び比較例1〜2で得られた、各表面被覆養生剤を塗布した各モルタルについて、30℃、25%RHの室内で0時間、1時間後、3時間後、6時間後、24時間後、48時間放置した後のモルタル供試体の質量を測定した。
塗布後0時間の際のモルタルの質量と、各時間におけるモルタルの質量とを比較して、その質量減少を水分減少とし、その結果を表2に水分減少率(%)として示す。
(モルタルの表面強度)
実施例1、参考例1及び比較例1〜2で得られた各表面被覆養生剤を塗布した各モルタルを、そのまま30℃、25%RHの室内での条件下で養生し、材齢1日後、3日後、7日後まで養生したのち、各モルタルについて、当該試験実施の3時間前に4×4cmの鉄製アタッチメントをモルタル表面にエポキシ接着剤(クイックメンダー,コニシ株式会社製)で付着させ、建研式接着力試験機(LPT−3000,オックスジャッキ株式会社製)を用いて付着強度試験を行い、得られた付着強度試験の測定値を表面引張強度とした。
但し、比較例3で得られた表面被覆養生剤を塗布したモルタルは、材齢7日後(塗布から4日後)の表面強度のみを測定した以外は、実施例1と同様にして付着強度試験を行った。
その結果を表3に示す。
また、更に、ポリマーエマルションと珪酸リチウムを主成分とする表面被覆養生剤とすることにより、より水分抑止効果を高め表面層を強化させることができる。
また、その施工方法は簡便であるため、施工面積にかかわらず適用でき、また天井等の施工にも有効に適用できる。
従って、本発明の養生剤及び養生方法は、コンクリート舗装のみならず、コンクリート構造物や二次製品等の任意のセメント系構造体に適用することができる。
Claims (5)
- セメント系材料が硬化する前に塗布又は散布する被覆養生剤であって、ポリマーエマルション及びリチウム塩及びセメント水和用硬化促進剤を含む(但し、顔料は含まない)ことを特徴とする、セメント系材料の被膜養生剤。
- 請求項1記載のセメント系材料の被覆養生剤は、ポリマーエマルションをポリマー固形分として5〜50質量%含有し、リチウム塩を1〜30質量%含有することを特徴とする、セメント系材料の被膜養生剤。
- 請求項2記載のセメント系材料の被覆養生剤は、硬化促進剤を0.1〜2.0質量%含有することを特徴とする、セメント系材料の被膜養生剤。
- 請求項1〜3記載のセメント系材料の被膜養生剤を、セメント系材料表面に塗布又は散布することを特徴とする、被膜養生剤の施工方法。
- 請求項4記載の被覆養生剤の施工方法において、セメント系材料の被覆養生剤を100〜300g/m2量で塗布または散布することを特徴とする、被覆養生剤の施工方法。