JP4530670B2 - 防曇性ポリ乳酸系二軸延伸フィルムおよびその製造方法 - Google Patents
防曇性ポリ乳酸系二軸延伸フィルムおよびその製造方法 Download PDFInfo
- Publication number
- JP4530670B2 JP4530670B2 JP2004002001A JP2004002001A JP4530670B2 JP 4530670 B2 JP4530670 B2 JP 4530670B2 JP 2004002001 A JP2004002001 A JP 2004002001A JP 2004002001 A JP2004002001 A JP 2004002001A JP 4530670 B2 JP4530670 B2 JP 4530670B2
- Authority
- JP
- Japan
- Prior art keywords
- film
- polylactic acid
- biaxially stretched
- aqueous
- stretched film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
500mlのガラス容器に50℃の温湯を300ml入れ、フィルムの塗布面を内側にして密封し、5℃の冷蔵庫中に静置し、フィルムの表面状態を経時的に観察した。防曇性は次の4段階で評価した。なお静置時間は1時間、8時間、1日、3日、7日とした。
◎:表面が均一透明で水滴の付着がない。
○:表面は透明で水滴の付着はないが、不均一でゆがんで見える。
△:表面に大きめの水滴が部分的に付着している。
×:全面に微細な水滴が付着し、底が見えない。
フィルムの塗布面と非塗布面とを重ね合わせて、10kg/cm2の荷重下、40℃×80%RHにて24時間処理した後、フィルム同志の剥離力を測定し、その剥離荷重から耐ブロッキング性を下記基準により評価した。
◎:剥離荷重10g未満
○:剥離荷重10g以上30g未満
△:剥離荷重30g以上100g未満
×:剥離荷重100g以上
塗布面にカッターで格子状に切れ込みを100等分入れた後、ニチバン社製粘着テープを用いて剥離試験を行い、塗布層の剥離状況を下記基準により判定した。
◎:剥離部がない
○:剥離部が20個未満
△:剥離部が20個以上80個未満
×:剥離部が80個以上
上記の各特性値を総合して次の基準に従い4段階評価を行った。
◎:非常に良好
○:良好
△:やや問題有り
×:問題有り
非イオン系界面活性剤としてポリオキシエチレンソルビタンモノラウレート(A−1)(東邦化学社製 ソルボンT−20)60質量%と、水分散ポリウレタン樹脂として自己乳化型ポリウレタン樹脂(B−1)(大日本インキ化学工業社製 ハイドランKU−400SF)40質量%とからなる混合物100質量部に対して、アミノ樹脂(大日本インキ化学工業社製 ベッカミンPMN)10質量部を加え、総固形分濃度が5質量%となるよう水で濃度調整して水分散液を調製した。
表1に示す非イオン系界面活性剤、水性ポリウレタン樹脂、水性ポリエステル樹脂を用い、質量比、塗布量を変更する以外は実施例1と同様にして逐次二軸延伸フィルムを得た。
ポリ乳酸系樹脂(カーギルダウポリマー社製 L−乳酸/D−乳酸=96.0/4.0(モル比)、融点150℃、数平均分子量105,000)と、表1に示す非イオン系界面活性剤を用い、質量比、塗布量を変更する以外は実施例1と同様にして逐次二軸延伸フィルムを得た。
非イオン系界面活性剤と水性ポリウレタン樹脂及び/又は水性ポリエステル樹脂とからなる塗布層を設けることなく、実施例1と同様にして逐次二軸延伸フィルムを得た。
非イオン系界面活性剤の代わりに、アニオン系界面活性剤(A−4)(アルキルスルホン酸ナトリウム塩、三洋化成工業社製 ケミスタット3033N)を用いる以外は、実施例1と同様にして二軸延伸フィルムを得た。
表1に示す非イオン系界面活性剤を用い、質量比を変更する以外は実施例1と同様にして逐次二軸延伸フィルムを得た。
水性樹脂としてポリエチレンオキサイド(B−3)(明成化学工業社製 アルコックスR−150、分子量15万)と、表1に示す非イオン系界面活性剤とを用い、質量比、塗布量を変更する以外は実施例1と同様にして逐次二軸延伸フィルムを得た。
Claims (4)
- 少なくとも片面に非イオン系界面活性剤(A)と水性ポリウレタン樹脂及び/又は水性ポリエステル樹脂(B)とからなる塗布層を有するポリ乳酸系二軸延伸フィルムであって、前記塗布層の非イオン系界面活性剤(A)と水性ポリウレタン樹脂及び/又は水性ポリエステル樹脂(B)との質量比(A/B)が90/10〜10/90であることを特徴とする防曇性ポリ乳酸系二軸延伸フィルム。
- 非イオン系界面活性剤(A)が、ポリオキシエチレンソルビタン脂肪酸エステル、ポリグリセリン脂肪酸エステル、ショ糖脂肪酸エステルより選ばれる少なくとも1種類の非イオン系界面活性剤であることを特徴とする請求項1記載の防曇性ポリ乳酸系二軸延伸フィルム。
- 未延伸ポリ乳酸系フィルムの少なくとも片面に、非イオン系界面活性剤(A)と水性ポリウレタン樹脂及び/又は水性ポリエステル樹脂(B)とからなる水溶液又は水分散液を塗布し、続いて二軸方向に延伸し、熱固定することを特徴とする請求項1または2記載の防曇性ポリ乳酸系二軸延伸フィルムの製造方法。
- 一軸方向のみに延伸されたポリ乳酸系フィルムの少なくとも片面に、非イオン系界面活性剤(A)と水性ポリウレタン樹脂及び/又は水性ポリエステル樹脂(B)とからなる水溶液又は水分散液を塗布し、続いて最初の延伸方向と直角方向に延伸し、熱固定することを特徴とする請求項1または2記載の防曇性ポリ乳酸系二軸延伸フィルムの製造方法。