JP4489618B2 - 半導体装置の製造方法 - Google Patents
半導体装置の製造方法 Download PDFInfo
- Publication number
- JP4489618B2 JP4489618B2 JP2005070788A JP2005070788A JP4489618B2 JP 4489618 B2 JP4489618 B2 JP 4489618B2 JP 2005070788 A JP2005070788 A JP 2005070788A JP 2005070788 A JP2005070788 A JP 2005070788A JP 4489618 B2 JP4489618 B2 JP 4489618B2
- Authority
- JP
- Japan
- Prior art keywords
- film
- wiring
- sioc
- sioc film
- bond
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
×100 (1)
図4に、SiOC膜のテープテストの結果をまとめる。テープテストには、Si−CH3/Si−O結合比が2.30%、2.40%、2.50%、2.55%および2.90%の5つのSiOC膜を用いた。テープ荷重は220g/cmであり、測定には半導体基板上にSiOC膜(厚さ500nm)、TEOS膜(厚さ50nm)、Ta/TaN積層膜(厚さ100nm)、Cu膜(厚さ600〜700nm)を下層から順に堆積した積層構造の試料を用いた。
2 素子分離部
3 pウェル
4 nウェル
5 ゲート絶縁膜
6 ゲート電極
7 キャップ絶縁膜
8 サイドウォール
9 n型半導体領域
10 p型半導体領域
11 層間絶縁膜
12 接続孔
13 プラグ
14 ストッパ絶縁膜
15 配線層間膜
15a SiOC膜
15b TEOS膜
16 配線溝
17 バリアメタル層
18 銅膜
19 配線
20 キャップ絶縁膜
21 ビア層間膜
22 ストッパ絶縁膜
23 配線層間膜
24 接続孔
25 配線溝
26 バリアメタル層
27 銅膜
28 配線
29 ダイシング装置
30 ダイシングテーブル
31 円形刃
32 チップ
33 ダイシングテープ
34 フレーム
Claims (7)
- 金属材料からなる単層または多層の配線を半導体基板上に形成する半導体装置の製造方法であって、
前記半導体基板上に層間膜としてSiOC膜を形成する工程と、
前記SiOC膜上にTEOS膜を形成する工程と、
前記SiOC膜およびTEOS膜の所定の領域に配線溝を形成する工程と、
前記配線溝内および前記配線溝の外の前記TEOS膜上に前記金属材料を堆積する工程と、
前記配線溝以外の前記TEOS膜上の前記金属材料をCMP法により研磨して除去する工程と、を有し、
前記SiOC膜は、FT−IRから求まる前記SiOC膜のSi−CH3結合とSi−O結合との結合比が2.05〜2.49%の範囲であることを特徴とする半導体装置の製造方法。 - 請求項1記載の半導体装置の製造方法において、前記SiOC膜の比誘電率は3以下であることを特徴とする半導体装置の製造方法。
- 請求項1記載の半導体装置の製造方法において、前記SiOC膜の硬度は2.8Gpa以上であることを特徴とする半導体装置の製造方法。
- 請求項1記載の半導体装置の製造方法において、前記SiOC膜の弾性率は18Gpa以上であることを特徴とする半導体装置の製造方法。
- 請求項1記載の半導体装置の製造方法において、前記SiOC膜はプラズマCVD法により形成されることを特徴とする半導体装置の製造方法。
- 請求項5記載の半導体装置の製造方法において、前記SiOC膜は、圧力400〜600Pa、DMDMOS流量200〜350sccm、He流量100〜200sccm、RFパワー3000〜4000W、基板温度350〜400℃の成膜条件により形成されることを特徴とする半導体装置の製造方法。
- 請求項1記載の半導体装置の製造方法において、前記配線は、銅を主導体層とするダマシン配線であることを特徴とする半導体装置の製造方法。