JP4385147B2 - Sheet-like stress light emitting structure including stress light emitting material and use thereof - Google Patents
Sheet-like stress light emitting structure including stress light emitting material and use thereof Download PDFInfo
- Publication number
- JP4385147B2 JP4385147B2 JP2004203834A JP2004203834A JP4385147B2 JP 4385147 B2 JP4385147 B2 JP 4385147B2 JP 2004203834 A JP2004203834 A JP 2004203834A JP 2004203834 A JP2004203834 A JP 2004203834A JP 4385147 B2 JP4385147 B2 JP 4385147B2
- Authority
- JP
- Japan
- Prior art keywords
- stress
- sheet
- emitting structure
- light
- bonding agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、機械的な外力の強度に応じて発光する応力発光材料を含む、効率よく発光することができるシート状応力発光構造物、および、当該シート状応力発光構造物を用いて作製される構造体に関するものである。 The present invention includes a stress-stimulated luminescent material that emits light according to the strength of a mechanical external force, a sheet-like stress luminescent structure capable of efficiently emitting light, and the sheet-like stress-luminescent structure. It relates to a structure.
従来、外部から刺激を与えられた物質が、低温（例えば、室温）で可視光および／または可視域付近の光を発する現象は、いわゆる蛍光現象としてよく知られている。このような蛍光現象を生じる物質、すなわち蛍光体は、蛍光ランプなどの照明灯や、ＣＲＴ（Ｃａｔｈｏｄｅ Ｒａｙ Ｔｕｂｅ）いわゆるブラウン管などのディスプレイなどとして利用されている。この蛍光現象を生じさせる外部からの刺激は、通常、紫外線、電子線、Ｘ線、放射線、電界、化学反応などによって与えられる。 Conventionally, a phenomenon in which an externally stimulated substance emits visible light and / or light in the vicinity of the visible range at a low temperature (for example, room temperature) is well known as a so-called fluorescence phenomenon. A substance that generates such a fluorescent phenomenon, that is, a phosphor is used as an illumination lamp such as a fluorescent lamp or a display such as a cathode ray tube (CRT) so-called cathode ray tube. The external stimulus that causes this fluorescence phenomenon is usually given by ultraviolet rays, electron beams, X-rays, radiation, electric fields, chemical reactions, and the like.
近年、機械的な外力等の刺激によって発光する材料、または機械的な外力などの刺激を加えて変形させることによって強く発光する材料が開発されている。このように外力などの機械的な刺激によって発光する材料は、応力発光材料と呼ばれている。 In recent years, materials that emit light when stimulated by a mechanical external force or the like, or materials that emit light strongly when deformed by applying a stimulus such as a mechanical external force have been developed. Such a material that emits light by a mechanical stimulus such as an external force is called a stress luminescent material.
日本古来からの伝統芸能である折り紙は、紙を折ることによって構造を構成し特徴的な形を創り出すものであり、その過程や最終的な完成物を楽しむものである。紙には本来発光機能が存在しないが、応力発光材料を含ませると、紙を折るときの外力に応じて折り目の部分に発光を生じさせることができる。さらに、このような応力発光材料を含ませた紙を用いて作製した紙風船などの構造体において、手で弄んだ場合にさらに発光させることができるため、より情緒的な効果を奏することができる。このように、娯楽分野に用いられる素材として、応力発光材料を紙のようなシート状にすることは、さまざまな用途を生み出すものである。 Origami, a traditional performing art from ancient Japan, is a structure that creates a distinctive shape by folding paper and enjoys the process and the final finished product. Paper does not originally have a light emitting function, but if a stress light emitting material is included, light emission can be generated at a fold portion in accordance with an external force when the paper is folded. Furthermore, in a structure such as a paper balloon manufactured using paper containing such a stress-stimulated luminescent material, it can be further lit when tampered with by hand, so that a more emotional effect can be achieved. . As described above, forming a stress-stimulated luminescent material into a sheet like paper as a material used in the entertainment field creates various uses.
本発明者らは、種々の応力発光材料をこれまで開発してきた（例えば、特許文献１〜４を参照のこと）。また他のグループによって、いくつかの応力発光材料および応力発光材料の応用技術が報告されている（例えば、特許文献５〜８を参照のこと）。 The present inventors have developed various stress luminescent materials so far (see, for example, Patent Documents 1 to 4). Other groups have reported several stress-stimulated luminescent materials and applied technologies of stress-stimulated luminescent materials (see, for example, Patent Documents 5 to 8).
特許文献５〜８には、弾性を有する樹脂などに応力発光材料からなる微粒子を混入させた人工発光布地のようなシート状の応力発光構造物が開示されている。これらの文献に開示される微粒子の発光は、シートの基材となる樹脂などに作用した応力が、応力発光材料からなる微粒子に作用することに基づいている。
しかしながら、これまでに報告された応力発光材料は、機械的な刺激に伴った発光レベルの変化が小さく、反復して外力を加えると発光強度の減衰が激しく、さらに、機械的な外力による発光強度の再現性がないという問題を有している。 However, the stress-stimulated luminescent materials reported so far have little change in the luminescence level due to mechanical stimulation, and when external force is applied repeatedly, the luminescence intensity decays drastically. There is a problem that there is no reproducibility.
応力発光材料の発光特性は、外部から加えられた歪みエネルギーに比例する。すなわち、外力の大きさおよび／または時間変化率に比例する。シート状の応力発光構造物において強い発光を発生させるためには、応力発光材料そのものの発光レベルを強める以外に、シート内で応力発光材料の微粒子へ応力を効率よく作用させて発光効率を高める構造が非常に重要である。 The light emission characteristic of the stress light emitting material is proportional to the strain energy applied from the outside. That is, it is proportional to the magnitude of the external force and / or the time change rate. In order to generate strong light emission in a sheet-like stress light emitting structure, in addition to increasing the light emission level of the stress light emitting material itself, a structure in which stress is efficiently applied to the fine particles of the stress light emitting material in the sheet to increase the light emission efficiency Is very important.
特に、娯楽分野に用いられる素材としてシート状の応力発光構造物を利用するためには、外部照明などの利用環境に依存しない強い発光強度が必要である。さらに、人の手で力を作用させた場合に同じ力によって発光強度がより強まるように、シート状の応力発光構造物全体としての発光効率を高める必要がある。 In particular, in order to use a sheet-like stress light-emitting structure as a material used in the entertainment field, a strong light emission intensity that does not depend on the use environment such as external illumination is required. Furthermore, it is necessary to increase the light emission efficiency of the sheet-like stress light emitting structure as a whole so that the light emission intensity is increased by the same force when a force is applied by human hands.
しかしながら、これまでには応力発光材料の微粒子へ応力を効率よく作用させる構造は開示されておらず、上記従来の構成では、シート状応力発光構造物において応力発光材料の微粒子へ効率よく応力を作用させることができないという問題を生じる。 However, there has been no disclosure of a structure that efficiently applies stress to the fine particles of the stress luminescent material, and in the conventional configuration, the stress is effectively applied to the fine particles of the stress luminescent material in the sheet-like stress luminescent structure. The problem that it cannot be made arises.
例えば、特許文献５には、応力発光材料を混入させたシートが人の力によって発光したと記載されるが、そのシート内での応力分布について全く記載されておらず、応力に対する発光特性についてもなんら言及されていない。また、特許文献５〜８には、発光強度を強めるための構造についてが全く記載されておらず、これらの文献に記載されるシート状の応力発光構造物は、単に応力発光材料の微粒子を均質な媒質中に分散させたものにすぎない。 For example, Patent Document 5 describes that a sheet mixed with a stress luminescent material emits light by human power, but does not describe the stress distribution in the sheet at all. No mention is made. Further, Patent Documents 5 to 8 do not describe any structure for increasing the light emission intensity, and the sheet-like stress light-emitting structure described in these documents simply homogenizes fine particles of the stress light-emitting material. It is only dispersed in a simple medium.
また、特許文献５〜８には、応力発光性物質と複合化する物質は、有機物質（例えば、樹脂）、無機物質（例えば、無機ガラス）のいずれであっても、両者を一緒に用いてもよく、場合によっては有機・無機複合物質であってもよいと記載されるが、両者を共存させることの利点、すなわち、シート形状の応力発光構造物において両者を共存させることが好ましいことについて何ら記載も示唆もされていない。 In Patent Documents 5 to 8, the substance to be combined with the stress luminescent substance is either an organic substance (for example, resin) or an inorganic substance (for example, inorganic glass). In some cases, it may be an organic / inorganic composite material, but there is no advantage about the coexistence of both, that is, it is preferable to coexist both in a sheet-shaped stress light emitting structure. Neither listed nor suggested.
このように、いずれの従来技術も、シート状の応力発光構造物において強い応力を効率よく作用させるという技術課題を全く認識しておらず、よって、シート状の応力発光構造物において応力発光材料の微粒子へ応力を効率よく作用させるための構成を想到することは、非常に困難であった。 As described above, none of the conventional techniques recognizes the technical problem of efficiently applying strong stress in the sheet-like stress light-emitting structure, and therefore, the stress-light-emitting material of the sheet-like stress light-emitting structure is not recognized. It has been very difficult to conceive a configuration for efficiently applying stress to fine particles.
本発明は、上記の問題点に鑑みてなされたものであり、その目的は、発光効率をより高めたシート状の応力発光構造物を提供することである。換言すれば、本発明の目的は、シート内において応力発光材料の微粒子に対して応力を集中させて、応力発光材料の微粒子の発光効率をより高めたシート状の応力発光構造物を供給することである。 This invention is made | formed in view of said problem, The objective is to provide the sheet-like stress light-emitting structure which improved luminous efficiency more. In other words, an object of the present invention is to provide a sheet-like stress light emitting structure in which stress is concentrated on the fine particles of the stress light emitting material in the sheet to further increase the light emission efficiency of the fine particles of the stress light emitting material. It is.
すなわち、本発明に係るシート状応力発光構造物は、応力発光材料の微粒子を含有する接合剤と当該接合剤より大きな弾性率を有する微細構造物とを含むことを特徴としている。 That is, the sheet-like stress luminescent structure according to the present invention is characterized by including a bonding agent containing fine particles of a stress luminescent material and a microstructure having a larger elastic modulus than the bonding agent.
本発明に係るシート状応力発光構造物において、上記応力発光材料の微粒子が外力の強度に比例して発光強度を変化させることが好ましい。 In the sheet-like stress light-emitting structure according to the present invention, it is preferable that the fine particles of the stress-stimulated light material change the light emission intensity in proportion to the strength of the external force.
本発明に係るシート状応力発光構造物において、上記接合剤が上記応力発光材料の微粒子を分散して含有することが好ましい。 In the sheet-like stress light-emitting structure according to the present invention, it is preferable that the bonding agent contains dispersed particles of the stress-luminescent material.
本発明に係るシート状応力発光構造物において、上記微細構造物が金属、ガラス、セラミクス、プラスチック、人工繊維または天然繊維であることが好ましい。 In the sheet-like stress-emitting structure according to the present invention, the fine structure is preferably a metal, glass, ceramics, plastic, artificial fiber, or natural fiber.
本発明に係るシート状応力発光構造物において、上記天然繊維がセルロースであることが好ましい。 In the sheet-like stress-emitting structure according to the present invention, the natural fiber is preferably cellulose.
本発明に係るシート状応力発光構造物において、上記人工繊維がナイロン、アクリルまたはポリエステルであることが好ましい。 In the sheet-like stress light-emitting structure according to the present invention, the artificial fiber is preferably nylon, acrylic or polyester.
本発明に係るシート状応力発光構造物において、上記微細構造物が球状、繊維状または針状であることが好ましい。 In the sheet-like stress light-emitting structure according to the present invention, the fine structure is preferably spherical, fibrous, or needle-shaped.
本発明に係るシート状応力発光構造物において、上記接合剤が高分子有機材料であることが好ましい。 In the sheet-like stress light-emitting structure according to the present invention, the bonding agent is preferably a polymer organic material.
本発明に係るシート状応力発光構造物において、上記高分子有機材料が透明性および柔軟性を有することが好ましい。 In the sheet-like stress light emitting structure according to the present invention, it is preferable that the polymer organic material has transparency and flexibility.
本発明に係るシート状応力発光構造物において、上記高分子有機材料がゴムまたは樹脂であることが好ましい。 In the sheet-like stress-emitting structure according to the present invention, the polymer organic material is preferably rubber or resin.
本発明に係るシート状応力発光構造物において、上記樹脂がエポキシ系樹脂またはアクリル樹脂であることが好ましい。 In the sheet-like stress light-emitting structure according to the present invention, the resin is preferably an epoxy resin or an acrylic resin.
本発明に係るシート状応力発光構造物において、上記応力発光材料がセラミクスであることが好ましい。 In the sheet-like stress luminescent structure according to the present invention, the stress luminescent material is preferably ceramics.
本発明に係るシート状応力発光構造物において、上記応力発光材料がアルミン酸塩またはケイ酸塩であることが好ましい。 In the sheet-like stress-luminescent structure according to the present invention, the stress-luminescent material is preferably an aluminate or a silicate.
すなわち、本発明に係るシート状応力発光構造物の作製方法は、応力発光材料の微粒子を含有する接合剤を、当該接合剤より大きな弾性率を有する微細構造物と混合した後にシートを形成する工程を包含することを特徴としている。 That is, in the method for producing a sheet-like stress luminescent structure according to the present invention, the step of forming a sheet after mixing a bonding agent containing fine particles of a stress luminescent material with a microstructure having a larger elastic modulus than the bonding agent. It is characterized by including.
すなわち、本発明に係るシート状応力発光構造物の作製方法は、接合剤より大きな弾性率を有しかつ表面に応力発光微粒子をコーティングした微細構造物を当該接合剤に混合した後にシートを形成する工程を包含することを特徴としている。 That is, in the method for producing a sheet-like stress luminescent structure according to the present invention, a sheet is formed after a microstructure having a larger elastic modulus than the bonding agent and having a surface coated with stress luminescent particles is mixed with the bonding agent. It is characterized by including a process.
すなわち、本発明に係るシート状応力発光構造物の作製方法は、応力発光材料の微粒子を含有する接合剤を、当該接合剤より大きな弾性率を有する微細構造物からなるシート状構造物に含浸させる工程を包含することを特徴としている。 That is, in the method for producing a sheet-like stress luminescent structure according to the present invention, a sheet-like structure made of a fine structure having a larger elastic modulus than that of the bonding agent is impregnated with a bonding agent containing fine particles of a stress-luminescent material. It is characterized by including a process.
本発明に係るシート状応力発光構造物の作製方法において、上記シート構造物が紙であることが好ましい。 In the method for producing a sheet-like stress light-emitting structure according to the present invention, the sheet structure is preferably paper.
本発明に係るシート状応力発光構造物は、上記の方法によって作製されることが好ましい。 The sheet-like stress light-emitting structure according to the present invention is preferably produced by the above method.
すなわち、本発明に係る構造体は、上記のシート状応力発光構造物からなることを特徴としている。 That is, the structure according to the present invention is characterized by comprising the above sheet-like stress light emitting structure.
本発明に係る構造体は、じゃばら構造を有することが好ましい。 The structure according to the present invention preferably has a loose structure.
本発明に係る構造体は、巻き取り笛、紙風船、ハリセン、グリーテイングカードまたは絵本であることが好ましい。 The structure according to the present invention is preferably a winding whistle, a paper balloon, a harsen, a greeting card or a picture book.
本発明に係るシート状応力発光構造物は、応力発光材料の微粒子を含む接合剤が、接合剤自体よりも大きな弾性率を有する微細構造物に挟み込まれており、その結果、外力を受けた場合に効率よく発光することができるという効果を奏する。つまり、本発明に係るシート状応力発光構造物は、上記の構成を採ることによって、外部からの機械的エネルギーを受けて発光する応力発光材料に、当該エネルギーを効率よく注入することができる。 In the sheet-like stress-stimulated luminescent structure according to the present invention, the bonding agent containing fine particles of the stress-luminescent material is sandwiched between the microstructures having a larger elastic modulus than the bonding agent itself, and as a result, receives external force. In addition, it is possible to emit light efficiently. That is, the sheet-like stress light emitting structure according to the present invention can efficiently inject the energy into a stress light emitting material that emits light by receiving mechanical energy from the outside by adopting the above configuration.
本発明に係るシート状応力発光構造物は、上記の構成を採ることによって、柔軟性および可塑性を有し、種々の形状に変化することができるという効果を奏する。また、本発明に係るシート状応力発光構造物において、上記接合剤は透明性が高い場合、応力発光材料の微粒子の発光を効率よく周囲に伝達することができるという効果を奏する。 The sheet-like stress light-emitting structure according to the present invention has the effect of having flexibility and plasticity and being able to change into various shapes by adopting the above-described configuration. Moreover, in the sheet-like stress light emitting structure according to the present invention, when the bonding agent has high transparency, there is an effect that the light emission of the fine particles of the stress light emitting material can be efficiently transmitted to the surroundings.
本発明に係るシート状応力発光構造物において、上記微細構造物が球状の場合、上記接合剤と混合しやすくなり、発光シートを均質に仕上げることができるという効果を奏する。また、本発明に係るシート状応力発光構造物において、上記微細構造物が針状の場合、微細構造物の端部においてより大きな応力集中が発生し、その結果発光強度を高めることができるという効果を奏する。また、本発明に係るシート状応力発光構造物において、上記微細構造物が繊維状の場合、シート状応力発光構造物の強度を高めることができるという効果を奏する。 In the sheet-like stress light-emitting structure according to the present invention, when the fine structure is spherical, it is easy to mix with the bonding agent, and the light-emitting sheet can be finished uniformly. Further, in the sheet-like stress light-emitting structure according to the present invention, when the fine structure is needle-shaped, a larger stress concentration occurs at the end of the fine structure, and as a result, the light emission intensity can be increased. Play. Moreover, in the sheet-like stress light-emitting structure according to the present invention, when the fine structure is fibrous, there is an effect that the strength of the sheet-like stress light-emitting structure can be increased.
本発明に係るシート状応力発光構造物において、上記微細構造物が上記の構成を採ることによって、応力発光材料の微粒子を含む接合剤より弾性率が高くなり、応力集中が発生しやすくなるという効果を奏する。さらに、本発明に係るシート状応力発光構造物において、上記微細構造物が上記の構成を採ることによって、応力集中がシート内部の微細構造だけでなくシートを折り曲げて構成する構造体にも発生するという効果を奏する。 In the sheet-like stress light emitting structure according to the present invention, the above-described fine structure adopts the above-described configuration, so that the elastic modulus is higher than that of the bonding agent containing the fine particles of the stress light emitting material, and stress concentration is likely to occur. Play. Furthermore, in the sheet-like stress light emitting structure according to the present invention, when the fine structure adopts the above-described configuration, stress concentration occurs not only in the fine structure inside the sheet but also in a structure formed by folding the sheet. There is an effect.
本発明に係るシート状応力発光構造物を用いて稜線と谷線を交互に折り返して形成したじゃばら様構造体において、じゃばらを折りたたむかまたは広げる力を加えた場合、稜線と谷線の部分で強い曲げ応力の集中が発生して稜線と谷線の部分で強く発光するという効果を奏する。 In a rose-like structure formed by alternately folding a ridge line and a valley line using the sheet-like stress light-emitting structure according to the present invention, when a force is applied to fold or spread the rose, the ridge line and the valley line are strong. There is an effect that bending stress is concentrated and light is emitted strongly at the ridge line and the valley line.
本発明に係るシート状応力発光構造物によれば、応力発光材料の微粒子を含む接合剤と、接合剤より大きな弾性率を有する微細構造物とが存在することに起因して、外力に応じて当該微細構造物間に応力集中が発生して、応力発光材料の微粒子に対してより強い応力が作用し、その結果、より強い発光を発生させることができるという効果を奏する。 According to the sheet-like stress light-emitting structure according to the present invention, due to the presence of the bonding agent containing fine particles of the stress-luminescent material and the fine structure having a larger elastic modulus than the bonding agent, depending on the external force Stress concentration occurs between the microstructures, and a stronger stress acts on the fine particles of the stress luminescent material. As a result, there is an effect that stronger luminescence can be generated.
また、シート状応力発光構造物を折り曲げて構造体を形成した場合、折り曲げ部分に曲げ応力の集中が発生し、その他の部分より強く発光させることができるという効果を奏する。従って、本発明に係るシート状応力発光構造物を用いて形成した巻き取り笛または紙風船は、より強い発光を発生させることができるので、より情緒的な効果を高めることができるという効果を奏する。 Further, when the sheet-like stress light emitting structure is bent to form a structure, the bending stress is concentrated at the bent portion, and the light can be emitted more strongly than the other portions. Therefore, the winding whistle or the paper balloon formed using the sheet-like stress light-emitting structure according to the present invention can generate more intense light emission, and thus has the effect of enhancing the emotional effect.
応力発光材料は、機械的な力を加えることによって発光する性質を有する。微粒子状にした応力発光材料を混入させた透明樹脂などの媒質を加工生成したシートは、力を加えたり変形させることによって、応力発光材料の微粒子に応力が作用して発光する。 The stress-stimulated luminescent material has a property of emitting light when a mechanical force is applied. A sheet formed by processing a medium such as a transparent resin mixed with a stress light-emitting material in the form of fine particles emits light when stress is applied to the fine particles of the stress light-emitting material by applying or deforming a force.
このようなシート状応力発光構造物の発光強度は、加えられた外力の大きさ（強度）と時間的な変化率に比例する。応力発光材料の微粒子を均質な媒質に混入させた場合、外力は、媒質によって分散されてしまうので、応力発光材料の微粒子に強い発光を発生させる程度の応力を生じない。 The light emission intensity of such a sheet-like stress light-emitting structure is proportional to the magnitude (intensity) of the applied external force and the temporal change rate. When the fine particles of the stress-stimulated luminescent material are mixed in a homogeneous medium, the external force is dispersed by the medium, so that no stress is generated to the extent that strong light emission is generated in the fine particles of the stress-luminescent material.
本発明者らは、上述したような外力の分散を防止する方法を探索した結果、従来方法の問題点を解決できることを見出した。すなわち、本発明者らは、応力発光材料の微粒子を含む均質な接合剤を、接合剤より大きな弾性率を有する微細構造物と共存させると、微細構造物間に存在する接合剤に応力集中が発生し、その結果、接合剤中に含まれる応力発光材料の微粒子に大きな応力が作用して強い発光が発生することを見出して、本発明を完成するに至った。 As a result of searching for a method for preventing the dispersion of the external force as described above, the present inventors have found that the problems of the conventional method can be solved. That is, when the present inventors coexist a homogeneous bonding agent containing fine particles of a stress-luminescent material with a microstructure having a larger elastic modulus than the bonding agent, stress concentration occurs in the bonding agent existing between the microstructures. As a result, it was found that a large stress acts on the fine particles of the stress-stimulated luminescent material contained in the bonding agent to generate strong luminescence, and the present invention was completed.
さらに本発明者らは、応力発光材料の微粒子を含む接合剤を細かい繊維が織り成すシート状構造物（例えば、紙）に含浸させた場合に、繊維間に応力発光材料の微粒子が効率よく浸透するので応力発光材料の微粒子が繊維間に発生する応力集中によってより強い発光を発することができることを見出した。 Furthermore, the present inventors efficiently impregnate the fine particles of the stress-luminescent material between the fibers when the bonding agent containing the fine particles of the stress-luminescent material is impregnated into a sheet-like structure woven with fine fibers (for example, paper). Therefore, it has been found that the fine particles of the stress-stimulated luminescent material can emit more intense light due to the stress concentration generated between the fibers.
本明細書中で使用される場合、用語「シート」は、平面状の薄い構造物であって折り曲げ等の加工が容易である構造物（例えば、紙）が意図される。本明細書中で意図されるシートの厚さは特に限定されないが、好ましくは０．５ｍｍ以下、より好ましくは０．１ｍｍ以下である。５〜５０μｍの厚さのいわゆる薄膜もまたシートであることが当業者に容易に理解される。 As used herein, the term “sheet” is intended to be a planar thin structure that can be easily folded or otherwise processed (eg, paper). Although the thickness of the sheet | seat intended in this specification is not specifically limited, Preferably it is 0.5 mm or less, More preferably, it is 0.1 mm or less. Those skilled in the art will readily understand that so-called thin films having a thickness of 5 to 50 μm are also sheets.
本明細書中で使用される場合、用語「応力発光材料」は、外部から加えられた歪みエネルギーによって発光する材料が意図され、「応力発光性材料」または「応力発光性物質」と相互交換可能に使用される。即ち、応力発光材料は、外部から加えられた歪みエネルギーによって材料自体が発光するという性質を有し、かつその歪みエネルギーに比例して発光強度を変化させるという性質を有する。よって、応力発光構造物は応力発光材料を含んでなる構造体であるということが、当業者に容易に理解される。応力発光材料としては、例えば、上述の特許文献１〜４に記載の応力発光材料や、特許第３２７３３１７号公報、特許第２９９２６３１号公報に記載のもの（例えば、β−アルミナ構造を有するセラミクスまたはアルミン酸ストロンチウムなど）が挙げられ、一般に、アルミン酸塩またはケイ酸塩などのような無機化合物が用いられる。応力発光微粒子は、接合材中に分散させて微細構造物間の隙間に効率よく充填させるために、その形状は球状で、直径は２ｎｍ〜１０μｍの範囲にあることが好ましい。 As used herein, the term “stress luminescent material” is intended to be a material that emits light by externally applied strain energy and is interchangeable with “stress luminescent material” or “stress luminescent material”. Used for. That is, the stress-stimulated luminescent material has the property that the material itself emits light by strain energy applied from the outside, and has the property of changing the luminescence intensity in proportion to the strain energy. Therefore, it will be easily understood by those skilled in the art that the stress light emitting structure is a structure including a stress light emitting material. Examples of the stress-stimulated luminescent material include the stress-stimulated luminescent materials described in Patent Documents 1 to 4 described above, and those described in Japanese Patent No. 3273317 and Japanese Patent No. 2999631 (for example, ceramics or alumina having a β-alumina structure). In general, inorganic compounds such as aluminates or silicates are used. In order to disperse the stress-stimulated fine particles in the bonding material and efficiently fill the gaps between the fine structures, the shape is spherical and the diameter is preferably in the range of 2 nm to 10 μm.
「弾性率」は、外力を適用された物質（弾性体）が変形する際に生じる歪みと外力の割合（力／歪み）である。一般に「弾性率」は、ヤング率、体積弾性率、剛性率またはポアゾン比で表されるが、本明細書中で使用される場合、用語「弾性率」は、体積弾性率が意図される。 “Elastic modulus” is a ratio (force / strain) between strain and external force generated when a substance (elastic body) to which an external force is applied is deformed. In general, “elastic modulus” is expressed in terms of Young's modulus, bulk modulus, stiffness, or Poisson's ratio, but as used herein, the term “elastic modulus” is intended to be bulk modulus.
本明細書中で使用される場合、用語「接合剤」は、応力発光微粒子を分散させる媒体が意図される。好ましい接合剤としては、高分子有機材料が挙げられる。応力発光材料の微粒子を分散させるための接合剤は、透明性および／または柔軟性を有する高分子有機材料であることが好ましい。特に、接合剤に応力発光材料の微粒子を混合してシート状応力発光構造物を作製する場合、接合剤は、種々の揮発性溶媒によって希釈可能であることが好ましい。好ましい接合剤は、ゴムまた樹脂であり、より好ましくは、エポキシ系樹脂およびアクリル樹脂などである。 As used herein, the term “bonding agent” intends a medium in which the stress-stimulated luminescent particles are dispersed. As a preferable bonding agent, a polymer organic material can be used. The bonding agent for dispersing the fine particles of the stress-stimulated luminescent material is preferably a polymer organic material having transparency and / or flexibility. In particular, when a sheet-like stress light emitting structure is prepared by mixing fine particles of a stress light emitting material in a bonding agent, the bonding agent is preferably dilutable with various volatile solvents. A preferable bonding agent is rubber or resin, and more preferable are epoxy resin and acrylic resin.
本明細書中で使用される場合、用語「微細構造物」は、球状、針状または繊維状の形態を有する任意の物質であって、これらの形態の特徴を現わすパラメータ（例えば、粒径および直径）が小さい構造を有する物質が意図される。本発明において使用される微細構造物は、上記接合剤より大きな弾性率を有することを特徴としており、接合剤の種類によって任意に選択され得る。好ましい微細構造物としては、金属、ガラス、セラミクス、プラスチック、人工繊維（例えば、セルロース）または天然繊維（例えば、ナイロン、アクリルまたはポリエステル）が挙げられる。微細構造物の形状は、繊維状、針状または球状であることが好ましい。微細構造物の大きさは、最終生成品であるシート状応力発光構造物中に含まれる大きさであれば特に限定されないが、シート状応力発光構造物内に応力集中を発生させるために、その直径は応力発光材料の微粒子より大きいことが好ましい。従って、微細構造物の大きさは、用途に応じたシートの厚みおよび応力発光材料の微粒子の大きさによって変動し得るが、１μｍ〜０．２ｍｍであることが好ましく、２０μｍ〜１００μｍであることがより好ましい。微細構造物の形状が針状である場合は、そのアスペクト比が２０〜１００であることが好ましい。なぜなら、針状の微細構造物においてその端部での応力集中が球状の場合と比較して大きくなるからである。 As used herein, the term “microstructure” is any material having a spherical, acicular or fibrous morphology, and parameters that characterize these morphology (eg, particle size And materials having a structure with a small diameter) are contemplated. The microstructure used in the present invention is characterized by having a larger elastic modulus than the above-mentioned bonding agent, and can be arbitrarily selected depending on the type of bonding agent. Preferred microstructures include metals, glasses, ceramics, plastics, artificial fibers (eg cellulose) or natural fibers (eg nylon, acrylic or polyester). The shape of the fine structure is preferably fibrous, acicular or spherical. The size of the fine structure is not particularly limited as long as it is a size contained in the sheet-like stress light-emitting structure that is the final product, but in order to generate stress concentration in the sheet-like stress light-emitting structure, The diameter is preferably larger than the fine particles of the stress luminescent material. Therefore, the size of the fine structure may vary depending on the thickness of the sheet and the fine particles of the stress-stimulated luminescent material depending on the application, but is preferably 1 μm to 0.2 mm, and preferably 20 μm to 100 μm. More preferred. When the fine structure has a needle shape, the aspect ratio is preferably 20 to 100. This is because the stress concentration at the end of the needle-like microstructure is larger than that of the spherical shape.
本発明は、応力発光材料の微粒子を含有する接合剤と当該接合剤より大きな弾性率を有する微細構造物とを含むシート状応力発光構造物を提供する。 The present invention provides a sheet-like stress luminescent structure including a bonding agent containing fine particles of a stress luminescent material and a microstructure having a larger elastic modulus than the bonding agent.
本発明の一実施形態について図１に基づいて説明すると以下の通りである。 An embodiment of the present invention will be described with reference to FIG.
本実施形態に係るシート状応力発光構造物１０は、外力の強度に比例して発光強度を変化させる応力発光材料の微粒子２を含んで構成される。本実施形態に係るシート状応力発光構造物１０は、応力発光材料からなる微粒子２を分散させた接合剤３と、接合剤３より大きな弾性率を有する微細構造物１の複合構造物である。接合剤３中に含まれる応力発光材料の微粒子２は、微細構造物１が隣接している近傍に存在すると、シート状応力発光構造物１０に外力が作用した際に微細構造物１の存在による応力集中が発生して同じ外力でも大きな応力が微粒子２に作用するため、微粒子２の発光強度は微細構造物１が存在しない場合に比較して大きくなる。 The sheet-like stress light emitting structure 10 according to the present embodiment includes fine particles 2 of a stress light emitting material that changes the light emission intensity in proportion to the intensity of an external force. The sheet-like stress light emitting structure 10 according to the present embodiment is a composite structure of a bonding agent 3 in which fine particles 2 made of a stress light emitting material are dispersed and a microstructure 1 having a larger elastic modulus than the bonding agent 3. If the fine particles 2 of the stress-stimulated luminescent material contained in the bonding agent 3 are present in the vicinity where the fine structures 1 are adjacent, the presence of the fine structures 1 when an external force acts on the sheet-like stress-light-emitting structures 10. Since stress concentration occurs and a large stress acts on the fine particles 2 even with the same external force, the emission intensity of the fine particles 2 becomes larger than when the fine structure 1 is not present.
本発明に係るシート状応力発光構造物を折り紙の素材として用いることによって、シートを折り曲げる過程で折り曲げ部分での発光を楽しむことができる。また、シート状応力発光構造物を折り曲げて、稜線や谷線を交互に連続させてじゃばら状に加工すると、じゃばらを展開したり折りたたむ際に折り曲げ部分に応力が集中するので、その折り曲げ部分の発光強度をさらに高めることができる。特に、紙風船のように、本発明に係るシート状応力発光構造物を折り曲げて完成した構造体を手で弄ぶことにより、折り曲げ部分に応力集中が発生し、この部分が発光し、より情緒性を高めることができる。また、飛び出す絵本またはグリーティングカードのように、ページ間に立体構造体として折りたたんでおいて、ページの開閉に応じてその立体構造体が展開する際に、その立体形状の折り目が強く発光し、より情緒性豊かな表現を可能にする。 By using the sheet-like stress light emitting structure according to the present invention as a material for origami, it is possible to enjoy light emission at the folded portion in the process of folding the sheet. In addition, if a sheet-like stress light emitting structure is folded and processed into a loose shape by alternating ridge lines and valley lines, stress concentrates on the folded portion when the loose leaf is expanded or folded. The strength can be further increased. In particular, when a sheet-like stress light emitting structure according to the present invention is folded, such as a paper balloon, by flicking a completed structure by hand, stress concentration occurs in the bent portion, and this portion emits light, making it more emotional. Can be increased. Also, as a picture book or greeting card that pops out, it is folded as a three-dimensional structure between pages, and when the three-dimensional structure expands according to the opening and closing of the page, the three-dimensional shape crease strongly emits light, and more Enables expressive expression.
本発明はさらに、応力発光材料の微粒子を含有する接合剤と当該接合剤より大きな弾性率を有する微細構造物とを含むシート状応力発光構造物の作製方法を提供する。 The present invention further provides a method for producing a sheet-like stress-luminescent structure including a bonding agent containing fine particles of a stress-luminescent material and a microstructure having a larger elastic modulus than the bonding agent.
本発明に係るシート状応力発光構造物の作製方法の第１の実施形態において、本発明に係るシート状応力発光構造物の作製方法は、応力発光材料の微粒子を分散させた接合剤に上記微細構造物を混合し、これをシート状に加工することである。接合剤にはまず応力発光材料の微粒子を混入し撹拌などによって均質になるように分散させる。その後に混合する微細構造物を接合剤中に均質に分散させやすくするために、微細構造物の形状は球状であることが好ましい。また、表面に予め応力発光材料の微粒子をコーティングした微細構造物を接合剤中に混合した後にシート状に加工してもよい。この場合、応力発光材料の微粒子が必ず微細構造物の近傍に存在するため、応力集中がより発生しやすくなる。応力発光材料の微粒子をコーティングする方法は、噴霧法が好ましいがこれに限定されない。微細構造物は透明性を有していなくてもよいが、微細構造物間に存在する応力発光材料の微粒子の発光を効率よく周囲に放射するために透明であることが好ましい。例えば、微細構造物としては、ガラスビーズやアクリル樹脂粉末などを用いることができる。シート状に加工するための方法は、当該分野において周知の方法を使用すればよく、特に限定されない。例えば、押し出し機の先端に取り付けた金型から流動状態の材料を押し出し成形する押し出し法、または加熱した回転ローラーで材料を融かしつつ圧延し、さらにロールで冷却しつつ圧延してシートを形成するカレンダー加工法が好ましい。 In the first embodiment of the method for producing the sheet-like stress luminescent structure according to the present invention, the method for producing the sheet-like stress luminescent structure according to the present invention includes the above-described finely bonded fine particles of the stress-luminescent material. A structure is mixed and processed into a sheet. First, fine particles of a stress-stimulated luminescent material are mixed in the bonding agent and dispersed so as to be homogeneous by stirring or the like. In order to facilitate uniform dispersion of the fine structure to be mixed thereafter in the bonding agent, the shape of the fine structure is preferably spherical. Alternatively, a fine structure whose surface is coated with fine particles of a stress-stimulated luminescent material in advance may be mixed into a bonding agent and then processed into a sheet shape. In this case, since the fine particles of the stress luminescent material always exist in the vicinity of the fine structure, the stress concentration is more likely to occur. The method of coating the fine particles of the stress-stimulated luminescent material is preferably a spray method, but is not limited thereto. Although the fine structure may not have transparency, it is preferable that the fine structure is transparent in order to efficiently emit light emitted from the fine particles of the stress-stimulated luminescent material existing between the fine structures. For example, glass beads or acrylic resin powder can be used as the fine structure. A method for processing into a sheet shape may be any method known in the art, and is not particularly limited. For example, an extrusion method in which a fluid material is extruded from a die attached to the tip of an extruder, or a material is rolled while being melted with a heated rotating roller, and further cooled with a roll to form a sheet. A calendering method is preferred.
本発明に係るシート状応力発光構造物の作製方法の第２の実施形態において、本発明に係るシート状応力発光構造物の作製方法は、例えば、紙のようなシート状構造物、好ましくは、繊維状の構造物に、応力発光材料の微粒子を分散させた接合剤を含浸させて作製する方法である。繊維状の構造物としては、セルロースなどの天然繊維、ナイロン、アクリル、ポリエステルなどの人工繊維を用いることができる。また、本実施形態に係るシート状応力発光構造物の作製方法を用いる場合、応力発光材料の微粒子を繊維状の構造物の間隙に効率良く浸透させるために、接合剤の流動性が高いほうが好ましい。また、第２の実施形態に係る方法で作製したシート状応力発光構造物は、第１の実施形態に係る方法で作製したシート状応力発光構造物より優れた強度を有するので、折り曲げによって様々な形状に加工することが容易である。 In the second embodiment of the method for producing a sheet-like stress luminescent structure according to the present invention, the method for producing the sheet-like stress luminescent structure according to the present invention is, for example, a sheet-like structure such as paper, preferably, In this method, a fibrous structure is impregnated with a bonding agent in which fine particles of a stress luminescent material are dispersed. As the fibrous structure, natural fibers such as cellulose and artificial fibers such as nylon, acrylic and polyester can be used. In addition, when using the method for producing a sheet-like stress luminescent structure according to the present embodiment, it is preferable that the bonding agent has high fluidity in order to efficiently infiltrate the fine particles of the stress luminescent material into the gaps of the fibrous structure. . In addition, the sheet-like stress light-emitting structure produced by the method according to the second embodiment has a strength superior to that of the sheet-like stress light-emitting structure produced by the method according to the first embodiment. It is easy to process into a shape.
このように、本発明に係るシート状応力発光構造物は、応力発光材料の微粒子を含む接合剤以外に、少なくとも、接合剤より大きな弾性率を有する微細構造物を含めばよいといえる。すなわち、応力発光材料の微粒子を含む接合剤中に当該微細構造物を含有するシート状応力発光構造物、当該微細構造物によって形成されるシート状構造物中に応力発光材料の微粒子を含む接合剤を含有して構成されるシート状応力発光構造物、およびさらなる成分を含有するシート状応力発光構造物もまた本発明の技術的範囲に含まれる点に留意すべきである。 Thus, it can be said that the sheet-like stress light-emitting structure according to the present invention should include at least a fine structure having an elastic modulus larger than that of the bonding agent, in addition to the bonding agent containing fine particles of the stress-luminescent material. That is, a sheet-like stress luminescent structure containing the fine structure in a bonding agent containing fine particles of a stress luminescent material, and a bonding agent containing fine particles of a stress luminescent material in a sheet-like structure formed by the fine structure It should be noted that a sheet-like stress-light-emitting structure constituted by containing and a sheet-like stress-light-emitting structure containing further components are also included in the technical scope of the present invention.
上記微細構造物は、接合剤より大きな弾性率を有する性質に依存するので、用いる接合剤の種類に応じて適宜選択すればよいことを、当業者は容易に理解する。 Those skilled in the art can easily understand that the microstructure is dependent on the property of having a larger elastic modulus than the bonding agent, and may be appropriately selected depending on the type of bonding agent used.
つまり、本発明の目的は、発光効率をより高めたシート状応力発光構造物を提供することにあるのであって、本明細書中に具体的に記載した個々のシート状応力発光構造物の作製方法に存するのではない。したがって、例示したシートの加工方法以外の方法によって作製されたシート状応力発光構造物もまた本発明の範囲に属することに留意しなければならない。 That is, an object of the present invention is to provide a sheet-like stress-light-emitting structure with higher luminous efficiency, and the production of individual sheet-like stress-light-emitting structures specifically described in this specification. It doesn't exist in the way. Therefore, it should be noted that a sheet-like stress light emitting structure manufactured by a method other than the exemplified sheet processing method also belongs to the scope of the present invention.
本発明は、以下の実施例によってさらに詳細に説明されるが、これに限定されるべきではない。 The invention is illustrated in more detail by the following examples, but should not be limited thereto.
［実施例１］
応力発光材料と紙を用いてシート状応力発光構造物を作製した。具体的には、上述の特許文献１に記載の方法に従って、Ｓｒ０．９Ａｌ２Ｏ４：Ｅｕ０．０５％の粉末（平均粒径２μｍ）を作製し、次いで、得られた応力発光材料の粉末を透明なスクリーン印刷用のインク（エポキシ系二液型）（帝国インキ製ＰＯＳスクリーンインキ、ＰＯＳメジウムおよび２１０硬化剤の混合物をＰ−００２溶剤で希釈）と均質に混合した後に、厚さ９０μｍ坪量６４ｇ／ｍ２のＰＰＣ用紙にスクリーン印刷し含浸させ、室温で乾燥させた。
[Example 1]
A sheet-like stress light emitting structure was produced using a stress light emitting material and paper. Specifically, in accordance with the method described in Patent Document 1 described above, a powder (average particle size: 2 μm) of Sr 0.9 Al 2 O 4 : Eu 0.05% was prepared, and then the stress-stimulated luminescent material obtained Thickness of 90 μm after the powder is homogeneously mixed with clear screen printing ink (epoxy two-pack type) (Teikoku POS screen ink, POS medium and 210 hardener mixture diluted with P-002 solvent) A PPC paper having a basis weight of 64 g / m 2 was screen-printed and impregnated, and dried at room temperature.
作製したシート状応力発光構造物の表面を、間接照明下においてプラスチック棒で摩擦すると、接触位置の移動に伴って発光し、図２に示すように光の軌跡を描いた。 When the surface of the produced sheet-like stress light emitting structure was rubbed with a plastic rod under indirect illumination, light was emitted with the movement of the contact position, and a light locus was drawn as shown in FIG.
［実施例２］
実施例１で作製したシート状応力発光構造物をじゃばら状に折りたたみ、発光構造体を作製した。じゃばらを折りたたんだり展開させて観察したところ、稜線付近ではその他の部分より強い発光を行うことを確認した。
[Example 2]
The sheet-like stress light emitting structure produced in Example 1 was folded into a loose shape to produce a light emitting structure. We observed that the roses were folded and unfolded, and it was confirmed that they emitted more light in the vicinity of the ridge than in the other parts.
本発明は上述した実施形態に限定されるものではなく、請求項に示した範囲で種々の変更が可能である。すなわち、請求項に示した範囲で適宜変更した技術的手段を組合わせて得られる実施形態についても本発明の技術的範囲に含まれる。 The present invention is not limited to the above-described embodiments, and various modifications can be made within the scope shown in the claims. That is, embodiments obtained by combining technical means appropriately changed within the scope of the claims are also included in the technical scope of the present invention.
本発明に係るシート状応力発光構造物は、歪みエネルギーなどの機械的エネルギーを外部から受けた場合に、機械的エネルギーによってシート内に生じた応力を当該シート状応力発光構造物に含まれる応力発光材料の微粒子に効率よく作用することができる内部構造を有している。さらに、このシート状応力発光構造物を折り曲げて構造体を生成した場合、折り曲げ部分に応力が集中し、より効率よくエネルギーを作用されることができる。このように、本発明に係るシート状応力発光構造物は、折り曲げ部分に局所的に強い発光を発生させることができるため、比較的明るい場所でも発光を視認することができる。本発明に係るシート状応力発光構造物を、折り紙、巻き取り笛、紙風船、扇子、または絵本の材料として利用すると、より情緒的な効果を高めることができる。 The sheet-like stress light-emitting structure according to the present invention, when mechanical energy such as strain energy is received from the outside, stress generated in the sheet due to mechanical energy is contained in the sheet-like stress light-emitting structure. It has an internal structure that can act efficiently on the fine particles of the material. Furthermore, when this sheet-like stress light-emitting structure is bent to produce a structure, stress concentrates on the bent portion and energy can be applied more efficiently. Thus, since the sheet-like stress light-emitting structure according to the present invention can generate strong light emission locally at the bent portion, light emission can be visually recognized even in a relatively bright place. When the sheet-like stress light-emitting structure according to the present invention is used as a material for origami, a winding whistle, a paper balloon, a fan, or a picture book, the emotional effect can be further enhanced.
１ 微細構造物
２ 応力発光材料の微粒子
３ 接合剤
１０ シート状応力発光構造物
DESCRIPTION OF SYMBOLS 1 Fine structure 2 Fine particle of stress luminescent material 3 Binder 10 Sheet-like stress luminescent structure
Claims (16)
前記微細構造物の形状が繊維状であることを特徴とするシート状応力発光構造物。 A bonding agent containing fine particles of a stress-stimulated luminescent material and a microstructure having a larger volume modulus of elasticity than the bonding agent;
A sheet-like stress-stimulated luminescent structure, wherein the microstructure has a fibrous shape.
前記微細構造物の形状が繊維状であることを特徴とするシート状応力発光構造物の作製方法。 Including a step of forming a sheet after mixing a bonding agent containing fine particles of a stress-stimulated luminescent material with a microstructure having a larger volume modulus of elasticity than the bonding agent;
The manufacturing method of the sheet-like stress light-emitting structure, wherein the microstructure has a fibrous shape.
前記微細構造物の形状が繊維状であることを特徴とするシート状応力発光構造物の作製方法。 Including a step of forming a sheet after mixing a fine structure having a volume modulus of elasticity larger than that of the bonding agent and having the surface coated with stress-luminescent particles on the bonding agent,
The manufacturing method of the sheet-like stress light-emitting structure, wherein the microstructure has a fibrous shape.
前記微細構造物の形状が繊維状であることを特徴とするシート状応力発光構造物の作製方法。 Including a step of impregnating a sheet-like structure composed of a fine structure having a volumetric modulus larger than that of the bonding agent, including a bonding agent containing fine particles of a stress luminescent material,
The manufacturing method of the sheet-like stress light-emitting structure, wherein the microstructure has a fibrous shape.
じゃばら構造を有することを特徴とする構造体。 It is produced using the sheet-like stress light-emitting structure according to claim 1 or 14 ,
A structure characterized by having a loose structure .
巻き取り笛、紙風船、ハリセン、グリーティングカードまたは絵本であることを特徴とする構造体。 It is produced using the sheet-like stress light-emitting structure according to claim 1 or 14 ,
A structure characterized by being a winding whistle, a paper balloon, a harsen, a greeting card or a picture book .