JP4278540B2 - Optical functional film, article, method for producing optical functional film, and method for coating article - Google Patents
Optical functional film, article, method for producing optical functional film, and method for coating article Download PDFInfo
- Publication number
- JP4278540B2 JP4278540B2 JP2004070123A JP2004070123A JP4278540B2 JP 4278540 B2 JP4278540 B2 JP 4278540B2 JP 2004070123 A JP2004070123 A JP 2004070123A JP 2004070123 A JP2004070123 A JP 2004070123A JP 4278540 B2 JP4278540 B2 JP 4278540B2
- Authority
- JP
- Japan
- Prior art keywords
- optical functional
- functional film
- heat
- layer
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は、視覚的な効果により物品の真贋性(真正性)を識別する技術に関し、物品を覆い、あるいは物品に貼り付けて使用することに適した真贋性の識別機能を有する光学機能フィルムに関する。 The present invention relates to a technique for identifying the authenticity (authenticity) of an article by a visual effect, and relates to an optical functional film having an authenticity identification function suitable for covering or attaching to an article for use. .
乾電池のような円筒形状の物品において、その表面に製品のロゴ、注意書きあるいは装飾等を行う技術として、熱収縮フィルム(シュリンクフィルム)を用いる方法が知られている。 In a cylindrical article such as a dry battery, a method of using a heat shrink film (shrink film) is known as a technique for applying a product logo, a cautionary note, or decoration on the surface of the article.
この方法においては、熱を加えると収縮するフィルムに任意の印刷を行い、円筒形状の物品にこのフィルムを巻き付け、さらに熱を加えることで収縮させ、フィルムを物品に密着させる。この方法は、熱収縮フィルムに所定の表示内容を印刷すればよいので、多様な表示内容に対応させることが容易である。また物品を覆い、その後に熱収縮させればよいだけなので、低コスト・大量生産に適している。また物品の形状や大きさの相違にも容易に対応することができる。このような優位性から、各種パッケージや飲料水を詰めたPETボトル等の包装に広く利用されている。この技術に関しては、例えば特許文献1に記載されている。 In this method, arbitrary printing is performed on a film that shrinks when heat is applied, the film is wound around a cylindrical article, and the film is shrunk by applying heat, and the film is adhered to the article. In this method, a predetermined display content may be printed on the heat-shrink film, so that it is easy to cope with various display contents. Moreover, since it is only necessary to cover the article and then heat shrink, it is suitable for low cost and mass production. In addition, it is possible to easily cope with differences in the shape and size of articles. Because of such advantages, it is widely used for packaging of various packages and PET bottles filled with drinking water. This technique is described in Patent Document 1, for example.
他方で、日用品や電化製品等の多くの物品において、見た目を本物に似せて製造した偽物が市場に出回り問題となっている。このような状況において、性能、信頼性あるいは安全性の保証やブランド力の維持のために、物品の真贋性を識別することができる技術が求められている。 On the other hand, in many articles such as daily necessities and electrical appliances, fake products that look like real items appear on the market and become a problem. Under such circumstances, there is a need for a technology that can identify the authenticity of an article in order to guarantee performance, reliability, safety, or maintain brand power.
物品の真贋性を識別する技術として、物品に特殊なインクを用いて印刷を行う方法、あるいは、特殊な光学反射特性を有する小片を物品に貼り付けたりする方法が知られている。 As a technique for identifying the authenticity of an article, a method of performing printing using special ink on the article, or a method of attaching a small piece having special optical reflection characteristics to the article is known.
特殊なインクを塗布する方法としては、紫外線に対して蛍光するインクを用いて、所定の文字や図柄を印刷し、紫外線を照射した際にその図柄や文字を浮かび上がらせることで、真正性を確認する方法がある。また、磁性体の粒子や磁性を帯びた粒子を混ぜたインクを塗布し、磁気センサで真正性を識別する方法が知られている。 As a method of applying special ink, the authenticity is confirmed by printing a predetermined character or design using ink that fluoresces against ultraviolet light, and then highlighting the design or character when irradiated with ultraviolet light. There is a way to do it. In addition, a method is known in which authenticity is identified by a magnetic sensor by applying ink mixed with magnetic particles or magnetic particles.
また、光学反射特性を有する小片としては、コレステリック液晶が示す光学特性を利用したものが知られている。この技術に関しては、例えば特許文献2に示されている。 As small pieces having optical reflection characteristics, those utilizing optical characteristics exhibited by cholesteric liquid crystals are known. This technique is disclosed in Patent Document 2, for example.
上述した熱収縮フィルムを用いた包装技術においても、偽造品であるか否かを判定できる機能を持たせることが求められている。しかしながら、上述した熱収縮フィルムを用いた技術の優位性を失わずに、真贋判定機能を付与することは困難であった。 Even in the packaging technology using the heat-shrinkable film described above, it is required to have a function capable of determining whether or not it is a counterfeit product. However, it has been difficult to provide an authenticity determination function without losing the superiority of the technology using the heat shrink film described above.
例えば、熱収縮フィルムに特殊なインクによる印刷方法を行い、真贋識別機能を付与する方法が考えられる。しかしながら、このような特殊なインクは高価であり、低コストであるという熱収縮フィルムを用いる技術の優位性を生かせない。またそのインクを入手され、悪用することが比較的容易であり、偽造を防止する能力はさほど高くない。 For example, a method of printing a heat-shrinkable film with a special ink and imparting an authenticity identification function can be considered. However, such special ink is expensive and cannot take advantage of the superiority of the technology using a heat shrink film that is low cost. Also, it is relatively easy to obtain and abuse the ink, and its ability to prevent counterfeiting is not so high.
また、コレステリック液晶を用いた光学機能フィルムを用いる方法も考えられる。しかしながら、コレステリック液晶を用いた光学機能フィルムを別に用意しなければならず、やはりコスト高になる。特にコレステリック液晶は、大量生産される安価な製品に利用するには、コストの面から不利である。また、コレステリック液晶が熱収縮の影響で所定の光学機能を示さなくなるという根本的に解決困難な問題がある。 A method using an optical functional film using cholesteric liquid crystal is also conceivable. However, an optical functional film using cholesteric liquid crystal must be prepared separately, which also increases the cost. In particular, cholesteric liquid crystals are disadvantageous in terms of cost in order to be used for inexpensive products that are mass-produced. Further, there is a problem that is fundamentally difficult to solve because the cholesteric liquid crystal does not exhibit a predetermined optical function due to the influence of heat shrinkage.
本発明は、熱収縮フィルムを用いた包装技術において、低コスト性を損なわずに真贋判定のための光学機能フィルムとしての機能が得られる技術を提供することを目的とする。 An object of the present invention is to provide a technique that can provide a function as an optical functional film for authenticity determination without impairing low cost in a packaging technique using a heat shrinkable film.
本発明の光学機能フィルムは、異なる屈折率を有する光透過性のフィルムを多層に積層した積層構造を有し、熱収縮により物品を包装する熱収縮性を備え、前記熱収縮性は異方性を有し、前記熱収縮性の異方性により、面内における視野角の増加に従うブルーシフト現象に異方性が付与されていることを特徴とする。 The optical functional film of the present invention has a laminated structure in which light transmissive films having different refractive indexes are laminated in multiple layers, and has heat shrinkability for wrapping an article by heat shrinkage, and the heat shrinkability is anisotropic. And the anisotropy is imparted to the blue shift phenomenon according to the increase in viewing angle in the plane due to the heat-shrinkable anisotropy .
熱収縮により物品を包装する熱収縮性とは、熱収縮が起こる前の状態で物品を覆い、その後に加熱することで、物品の形状に沿って熱収縮し、物品に密着する機能のことをいう。したがって、加熱により単に収縮するだけでは、熱収縮により物品を包装する熱収縮性を有しているとはいえない。ここで、包装という概念には、物品の全体を完全に覆う包装の状態、および物品の一部を覆う包装の状態が含まれる。 The heat shrinkability of packaging an article by heat shrinkage is a function of covering the article in a state before the heat shrinkage occurs and then heating it to heat shrink along the shape of the article and adhere to the article. Say. Therefore, it cannot be said that it has the heat shrinkability which wraps articles | goods by heat contraction only by shrinking only by heating. Here, the concept of packaging includes a state of packaging completely covering the entire article and a state of packaging covering a part of the article.
次に、異なる屈折率を有する光透過性薄膜フィルムを多層に積層した積層構造が示す光学的な性質について説明する。図8は、多層薄膜フィルム層における光の反射状態を示す概念図である。図8には、第1の屈折率を有する光透過性の薄膜フィルム801(A層)と第2の屈折率を有する光透過性の薄膜フィルム802(B層)とを交互に多層に積層した多層薄膜フィルム層803の例が示されている。
Next, the optical properties of the laminated structure in which light transmissive thin film films having different refractive indexes are laminated in a multilayer manner will be described. FIG. 8 is a conceptual diagram showing a light reflection state in the multilayer thin film layer. In FIG. 8, light transmissive thin film films 801 (A layer) having a first refractive index and light transmissive thin film films 802 (B layer) having a second refractive index are alternately laminated in multiple layers. An example of a multilayer
多層薄膜フィルム層803に白色光を当てると、フレネルの反射則に従って、各層の界面において光の反射が発生する。すなわち、A層とB層との間の界面において、入射光の一部が反射し、その他は透過する。A層とB層との間の界面において、入射光の一部が反射するのは、A層の屈折率とB層の屈折率とが異なるからである。
When white light is applied to the multilayer
A層とB層との間の界面は、繰り返し現れるので、各界面で生じた反射光は干渉する。入射光の入射角を徐々に大きくすると、各界面で生じた反射光の光路差は、徐々に小さくなり、より短波長の光が干渉し強め合うようになる。従って、白色光が当たっている多層薄膜フィルム層803をより斜め(面に平行に近い角度)から見る程、より短波長の光が強く反射しているように見える。例えば、白色光が当たっている多層薄膜フィルム層803を傾けて行くと反射光がだんだん青っぽく見えるようになる。この現象をブルーシフトという。なお、入射角は、入射面への垂線と入射光の光軸とがなす角度として定義される。
Since the interface between the A layer and the B layer appears repeatedly, reflected light generated at each interface interferes. When the incident angle of incident light is gradually increased, the optical path difference of the reflected light generated at each interface gradually decreases, and light of shorter wavelengths interferes and strengthens each other. Therefore, as the multilayer thin
異なる屈折率を有する光透過性薄膜フィルムを多層に積層した構造というのは、屈折率の異なる少なくとも2種類の光透過性薄膜フィルムを積層し、屈折率の異なる光透過性薄膜フィルム同士の界面が少なくとも一つ存在する多層構造のことをいう。この多層薄膜の具体的な構造としては、異なる屈折率を有する2種類の光透過性薄膜フィルムを交互に多層に重ねた構成、第1〜第N(Nは自然数)の屈折率を有した第1〜第Nの光透過性薄膜フィルムを順に積層したものを1単位として、それを任意の数で積層した構造等が挙げられる。 The structure in which light transmissive thin film films having different refractive indexes are laminated in multiple layers means that at least two kinds of light transmissive thin film films having different refractive indexes are laminated, and the interface between the light transmissive thin film films having different refractive indexes is This refers to a multi-layer structure in which at least one exists. As a specific structure of the multilayer thin film, a structure in which two types of light-transmitting thin film films having different refractive indexes are alternately stacked in a multilayer structure, and a first to Nth (N is a natural number) refractive index. The structure etc. which laminated | stacked the 1st-Nth light transmissive thin film film in order as 1 unit as what was laminated | stacked by the arbitrary number are mentioned.
本発明の光学機能フィルムで覆われる物品は、何ら限定されるものではない。このような物品としては、乾電池、各種日用品、食料品、商品パッケージ、電化製品、事務用品、電子部品等が挙げられる。また、真贋判定が重要となる、パスポート、書類、各種カード、パス、紙幣、金券、証券、証書、商品券、絵画、切符、公共競技投票券、音楽や映像が記録された記録媒体、コンピュータソフトウェアが記録された記録媒体、それらの各種製品およびそのパッケージ等も本発明における物品として挙げることができる。 The article covered with the optical functional film of the present invention is not limited at all. Examples of such articles include dry batteries, various daily necessities, foodstuffs, merchandise packages, electrical appliances, office supplies, electronic parts, and the like. In addition, passports, documents, various cards, passes, banknotes, vouchers, securities, certificates, gift certificates, pictures, tickets, public competition voting tickets, music and video recording media, computer software, where authentication is important The recording medium on which is recorded, their various products, their packages and the like can also be cited as articles in the present invention.
本発明の光学機能フィルムは、従来の熱収縮フィルムと同様の取扱によって、物品の包装を行うことができる。したがって、これまで利用されてきた設備を利用することができ、包装作業におけるコストアップを抑えることができる。また、光学機能フィルム自体も特殊な材料は必要とせず、大きなコストアップにはつながらない。 The optical functional film of the present invention can be packaged by the same handling as a conventional heat-shrinkable film. Therefore, the facilities that have been used so far can be used, and the cost increase in the packaging work can be suppressed. Further, the optical functional film itself does not require a special material, and does not lead to a large cost increase.
また、ブルーシフトの見え方は、積層構造に対する延伸条件を調整することで容易に制御することができる。 The appearance of the blue shift can be easily controlled by adjusting the stretching conditions for the laminated structure.
したがって、コスト増を招かずに、物品の包装に用いることができる熱収縮性と、真贋判定のために光学機能とを有する包装材料を提供することができる。 Therefore, it is possible to provide a packaging material having heat shrinkability that can be used for packaging an article and an optical function for authenticity determination without causing an increase in cost.
本発明の光学機能フィルムが示すブルーシフトは、積層構造を構成する各光学フィルムの材質、厚さ、屈折率の違いおよび屈折率の異方性が複雑に関係している。また積層構造は、延伸が施されることで一体になっており、単層を剥がすようなことは不可能である。したがって、完成品を解析しても、同様な光学的な性質を再現することは極めて困難である。このため、偽造が困難であり、真贋判定手段に適したものとなる。 The blue shift exhibited by the optical functional film of the present invention is complicatedly related to the material, thickness, refractive index difference, and refractive index anisotropy of each optical film constituting the laminated structure. Further, the laminated structure is integrated by being stretched, and it is impossible to peel off a single layer. Therefore, even if the finished product is analyzed, it is extremely difficult to reproduce similar optical properties. For this reason, forgery is difficult, and it is suitable for authenticity determination means.
また、本発明の光学機能フィルムは、包装対象となる物品(基材)の形状に合わせて熱収縮するので、包装された物品を視認した際、視野角を動かさなくても曲面部分にブルーシフトに従う虹のようなグラデーションの変化が現れる。この曲面部分の見え方は、物品の形状に依存したものであり、特異なものとなる。 In addition, since the optical functional film of the present invention is thermally shrunk in accordance with the shape of the article (base material) to be packaged, when viewing the packaged article, the blue shift is made to the curved surface portion without moving the viewing angle. A gradation change like a rainbow appears. The appearance of the curved surface portion depends on the shape of the article and is unique.
本発明の光学機能フィルムにおける積層構造は、延伸処理により熱収縮性が付与され、そして調整される。また、光透過性のフィルムの材料としてPETやアクリル等の高分子樹脂材料を用いた場合、延伸処理によりフィルムの屈折率も変化する。このことを利用すると、光学機能フィルムが示す熱収縮性と光学機能(ブルーシフト機能)とを延伸処理によって同時に調整することができる。 The laminated structure in the optical functional film of the present invention is imparted with heat shrinkability by the stretching treatment and is adjusted. Further, when a polymer resin material such as PET or acrylic is used as the material for the light transmissive film, the refractive index of the film also changes due to the stretching treatment. By utilizing this fact, the heat shrinkability and the optical function (blue shift function) exhibited by the optical functional film can be simultaneously adjusted by the stretching process.
例えば、フィルムを一軸延伸すると、その延伸した方向における屈折率と熱収縮性が同時に変化する。なお、延伸した方向における屈折率とは、その方向に偏光した直線偏光の光に対して当該フィルムが示す屈折率のことをいう。また、フィルムに対して2軸延伸を加えると、フィルム面内の2次元方向における熱収縮性と屈折率とを調整することができる。 For example, when the film is uniaxially stretched, the refractive index and the heat shrinkability in the stretched direction change simultaneously. Note that the refractive index in the stretched direction refers to the refractive index of the film with respect to linearly polarized light polarized in that direction. Moreover, when biaxial stretching is applied to the film, the heat shrinkability and the refractive index in the two-dimensional direction in the film plane can be adjusted.
また、この2軸延伸において、直交する2方向における延伸状態を意図的に異ならせることで、熱収縮性と屈折率とに異方性を付与することができる。つまり、熱収縮する方向に異方性を付与させた場合、屈折率も平面内において異方性を示すように調整することができる。このことを利用すると、物品の形状に合わせた熱収縮が発生するように調整され、さらに物品を包装した状態において、見る方向によってブルーシフトの状態が異なる特異な見え方をする包装構造を得ることができる。 In this biaxial stretching, anisotropy can be imparted to the heat shrinkability and the refractive index by intentionally changing the stretched state in two orthogonal directions. That is, when anisotropy is imparted in the direction of heat shrinkage, the refractive index can also be adjusted to exhibit anisotropy in the plane. By utilizing this, a packaging structure is obtained that is adjusted so that thermal contraction according to the shape of the article occurs, and in which the article is wrapped, the blue shift state varies depending on the viewing direction. Can do.
このように本発明の光学機能フィルムにおいて、延伸処理は、1軸延伸であり、この1軸延伸が施された方向における熱収縮性が制御されていることは好ましい。この場合、延伸した方向における熱収縮性とブルーシフトの状態とを延伸条件により制御することができる。 Thus, in the optical functional film of the present invention, the stretching treatment is uniaxial stretching, and it is preferable that the heat shrinkability in the direction in which the uniaxial stretching is performed is controlled. In this case, the heat shrinkability and the blue shift state in the stretched direction can be controlled by the stretching conditions.
また、本発明において、延伸処理として2軸延伸を行ってもよい。この場合、2次元平面内における収縮とブルーシフトの状態とを制御することができる。たとえば、X軸方向とそれに直交するY軸方向における熱収縮率を意図的に異ならせた熱収縮性の制御、さらにX軸方向とそれに直交するY軸方向におけるブルーシフトの見え方を意図的に異ならせた光学特性の制御を2軸延伸の延伸具合の調整によって実現することができる。 In the present invention, biaxial stretching may be performed as the stretching process. In this case, the contraction and the blue shift state in the two-dimensional plane can be controlled. For example, control of heat shrinkability by intentionally changing the heat shrinkage rate in the X-axis direction and the Y-axis direction perpendicular to the X-axis direction, and further intentional appearance of the blue shift in the X-axis direction and the Y-axis direction perpendicular thereto Control of the different optical characteristics can be realized by adjusting the stretching condition of biaxial stretching.
本発明の光学機能フィルムは、曲面形状に沿った状態において、曲面の湾曲方向に向かって色彩変化を観察することができる。すなわち、本発明の光学機能素子を曲面に沿って湾曲させた状態において、所定の曲面部分を垂直方向から見ると、その注視した部分から少し外れた部分(つまり曲面の湾曲方向に少し移動した部分)は、曲面の性質から、ブルーシフトが発現する程度の視野角を有した方向からの視認になる。この結果、注視部分から離れるにしたがって、短波長方向への色変化が連続的に発生するような色彩のグラデーションを観察することができる。 The optical functional film of the present invention can observe a color change toward the curved direction of the curved surface in a state along the curved surface shape. That is, in a state where the optical functional element of the present invention is curved along a curved surface, when a predetermined curved surface portion is viewed from the vertical direction, a portion slightly deviated from the gaze portion (that is, a portion slightly moved in the curved direction of the curved surface) ) Is visually recognized from a direction having a viewing angle such that a blue shift appears due to the nature of the curved surface. As a result, it is possible to observe a color gradation in which a color change in the short wavelength direction continuously occurs as the distance from the gaze portion increases.
このような特異な光学的な性質は、光学機能フィルムが熱収縮し、基材の形状にそって変形することによっても発生する。 Such a unique optical property also occurs when the optical functional film is thermally contracted and deformed along the shape of the substrate.
本発明の光学機能フィルムにおいて、収縮が行えない状態において加熱を加える熱固定処理を予め加えることにより、熱収縮性を制御させておくことは好ましい。収縮しないように例えば面圧を加えた状態で加熱を行うと、熱収縮は発生しないが分子構造に変化が生じ、後に加熱した際の熱収縮が抑制される。この現象を利用すると、熱収縮処理の際にどの程度の熱収縮を行わせるかを予め制御することができる。この予め行う熱処理を熱固定処理という。 In the optical functional film of the present invention, it is preferable to control the heat shrinkability by preliminarily applying a heat setting treatment in which heating is performed in a state where shrinkage cannot be performed. For example, if heating is performed in a state where surface pressure is applied so as not to shrink, thermal shrinkage does not occur, but the molecular structure changes, and thermal shrinkage when heated later is suppressed. If this phenomenon is utilized, it is possible to control in advance how much heat shrinkage is performed in the heat shrink process. This heat treatment performed in advance is called heat setting treatment.
本発明の光学機能フィルムにおいて、光吸収層を備えていることは好ましい。ブルーシフトは、多層構造中の複数の界面からの反射光の干渉を利用するので、この界面からの反射光以外の光が極力反射しないようにすることが、ブルーシフトを観察する際のS/N比を高くする上で有利となる。 The optical functional film of the present invention preferably includes a light absorption layer. Since the blue shift uses interference of reflected light from a plurality of interfaces in the multilayer structure, it is necessary to prevent light other than the reflected light from the interfaces from being reflected as much as possible. This is advantageous in increasing the N ratio.
光吸収層は、観察面側と反対の面に配置される。光吸収層は、黒あるいは濃い色を有し、なるべく広い可視光帯域の光を吸収する機能を有することが好ましい。光吸収層としては、カーボン粒子等を分散させた樹脂層や黒等の濃い色を有するフィルム、黒等の濃い色の塗料を塗ることで構成された層等が挙げられる。 The light absorption layer is disposed on the surface opposite to the observation surface side. The light absorption layer preferably has a black or dark color and has a function of absorbing light in a visible light band as wide as possible. Examples of the light absorbing layer include a resin layer in which carbon particles and the like are dispersed, a film having a dark color such as black, a layer formed by applying a dark color paint such as black, and the like.
本発明の光学機能フィルムにおいて、積層構造の少なくとも一部にホログラム加工が施されていることは好ましい。この態様によれば、ブルーシフトに加えて、ホログラム効果による識別機能を得ることができる。ホログラム加工は、積層構造の少なくとも一部にエンボス加工や凹凸加工を施すことで得ることができる。 In the optical functional film of the present invention, it is preferable that hologram processing is applied to at least a part of the laminated structure. According to this aspect, in addition to the blue shift, an identification function based on the hologram effect can be obtained. Hologram processing can be obtained by embossing or uneven processing at least a part of the laminated structure.
ホログラム機能を付加する方法として、ホログラム加工を施した被ホログラム加工層を備えてもよい。ホログラムは、層自体にエンボス加工や凹凸加工を施す必要があるので、使用する材料の材質によっては効果的な構造を付与することが困難な場合がある。特に本発明は、多層薄膜が示すブルーシフトと熱収縮性を優先する必要があるので、ホログラム加工に適したものとならない場合も考慮する必要がある。このような場合は、ホログラム加工を行うのに適した層を積層構造に付加し、この層にホログラム加工を施せばよい。こうすることで、ブルーシフトと熱収縮性を犠牲にすることなく、ホログラムの機能を追求することができる。 As a method of adding a hologram function, a hologram processing layer subjected to hologram processing may be provided. Since the hologram needs to be embossed or concavo-convex on the layer itself, it may be difficult to impart an effective structure depending on the material used. In particular, the present invention needs to give priority to the blue shift and heat shrinkability exhibited by the multilayer thin film, and therefore needs to be considered even if it is not suitable for hologram processing. In such a case, a layer suitable for performing hologram processing may be added to the laminated structure, and hologram processing may be performed on this layer. In this way, the function of the hologram can be pursued without sacrificing blue shift and heat shrinkability.
本発明の光学機能フィルムが示す熱収縮性は、加熱した際の収縮率が寸法比で25%以上であることが好ましい。収縮率が寸法比で25%を下回る値であると、物品の形状に対する追従性や密着性が不足し、包装材料として好ましくない。寸法比で考えた収縮率は、収縮前の寸法をA、収縮後の寸法をBとして、((A−B)/A)×100で算出される。 The heat shrinkability exhibited by the optical functional film of the present invention is preferably such that the shrinkage ratio when heated is 25% or more in terms of dimensional ratio. When the shrinkage ratio is less than 25% in terms of the dimensional ratio, the followability and adhesion to the shape of the article are insufficient, which is not preferable as a packaging material. The shrinkage rate in terms of the size ratio is calculated as ((A−B) / A) × 100, where A is the size before shrinkage and B is the size after shrinkage.
本発明は、上述したような本発明の光学機能フィルムの少なくとも一部が熱収縮することで、当該光学機能フィルムで包装された物品として把握することもできる。このような物品は、包装材料である熱収縮フィルムに、ブルーシフトによる識別性が付与され、識別機能を備えている。そのため、物品自体にブルーシフトによる識別機能を備えたものとなる。また、本発明の光学機能フィルムによる包装は、熱収縮機能により物品の曲面や凹凸に追従して密着するので、包装状態にあるフィルムを破らずにフィルムを外すこと(つまり包装状態を解くこと)は困難である。 This invention can also be grasped | ascertained as an article | item packaged with the said optical functional film because at least one part of the optical functional film of this invention as mentioned above heat-shrinks. Such an article is provided with a discriminating function due to blue shift to a heat-shrinkable film as a packaging material. Therefore, the article itself is provided with an identification function by blue shift. Moreover, since the packaging with the optical functional film of the present invention closely adheres to the curved surface and unevenness of the article by the heat shrinkage function, the film is removed without breaking the packaging film (that is, the packaging state is unraveled). It is difficult.
また、収縮した光学機能フィルムを無理矢理引き剥がそうとして破ると、光学機能に深く関係している多層構造が引き裂かれた状態になり、その引き裂かれた部分が目視で確認できないように修復することは困難となる。したがって、一旦包装による封印が破られると、その履歴を消せない状態となる。このことは、包装の再利用を防止する点で有用な機能となる。また、この性質を利用することで、本発明の光学機能フィルムを封印が解かれていないことを識別する封印材料として利用することもできる。 Also, if the optical functional film that has shrunk is torn apart by force, the multilayer structure deeply related to the optical function is torn, and it is impossible to repair the torn part so that it cannot be visually confirmed. It becomes difficult. Therefore, once the seal by packaging is broken, the history cannot be erased. This is a useful function in preventing reuse of packaging. In addition, by utilizing this property, the optical functional film of the present invention can also be used as a sealing material for identifying that the seal is not released.
本発明は、光学機能フィルムの製造方法として把握することもできる。すなわち、本発明の光学機能フィルムの製造方法は、異なる屈折率を有する光透過性のフィルムを多層に積層した構造を有する光学機能フィルムの製造方法であって、異なる屈折率を有する光透過性のフィルムを多層に積層する積層ステップと、前記積層ステップによって得た積層構造に対して延伸処理を施し、熱収縮性を付与する延伸ステップとを備え、前記延伸処理は異方性を有し、前記延伸処理の異方性により、面内における視野角の増加に従うブルーシフト現象に異方性が付与されることを特徴とする。 This invention can also be grasped | ascertained as a manufacturing method of an optical function film. That is, the method for producing an optical functional film of the present invention is a method for producing an optical functional film having a structure in which light transmissive films having different refractive indexes are laminated in multiple layers, and having a light transmissive property having different refractive indexes. A lamination step of laminating a film in multiple layers, and a stretching step for imparting heat shrinkability to the laminated structure obtained by the laminating step, and the stretching treatment has anisotropy, the anisotropy of the stretching process, the anisotropy is imparted to the blue shift phenomenon according to the increase of the viewing angle in a plane and wherein the Rukoto.
また本発明は、以上説明した光学機能フィルムで物品を覆う被覆ステップと、加熱し、前記光学機能フィルムの少なくとも一部を熱収縮させる熱収縮ステップとを備える光学機能フィルムで覆われた物品の被覆方法として把握することもできる。 The present invention also provides a coating of an article covered with an optical functional film comprising a coating step of covering the article with the optical functional film described above and a heat shrinking step of heat-shrinking at least a part of the optical functional film. It can also be grasped as a method.
本発明の光学機能フィルムは、熱収縮により基材の形状に合わせて熱収縮するので、凹凸や曲面を覆い、光学的な機能を発現するフィルムとして利用することができる。 Since the optical functional film of the present invention is thermally shrunk in accordance with the shape of the substrate by heat shrinkage, it can be used as a film that covers unevenness and curved surfaces and exhibits optical functions.
本発明によれば、異なる屈折率を有する光透過性フィルムを積層した積層体に物品の包装に利用できる程度の熱収縮性を付与することで、コスト増を招かずに熱収縮作用によって物品を包装することができる光学機能フィルムが提供される。この光学機能フィルムは、従来から物品の包装用や表示用に用いられている熱収縮フィルムと同じように取り扱うことができ、光学的に高い識別機能を有しているのにもかかわらず、低コストなものとできる。このため、任意の物品にコスト増加を招かずに真贋判定機能を付与することができる。 According to the present invention, by providing a heat-shrinkable property that can be used for packaging an article to a laminate in which light-transmitting films having different refractive indexes are laminated, the article can be obtained by a heat shrinking action without causing an increase in cost. An optical functional film that can be packaged is provided. This optical functional film can be handled in the same way as a heat-shrinkable film conventionally used for packaging and display of articles and has a high optical identification function. It can be costly. For this reason, the authenticity determination function can be given to any article without increasing the cost.
(第1の実施の形態)
1−1.第1の実施形態の構成
図1は、本実施形態の光学機能フィルムの概要を示す断面図である。図2は、図1の光学機能フィルムの概要を示す斜視図である。図1に示すように、光学機能フィルム101は、接着層102、光吸収層103、多層薄膜フィルム層104および印刷表示層105が積層された断面構造を有している。また、図2に示すように光学機能フィルム101は薄い可撓性を有するフィルム状を有している。
(First embodiment)
1-1. Configuration of First Embodiment FIG. 1 is a cross-sectional view showing an outline of an optical functional film of the present embodiment. FIG. 2 is a perspective view showing an outline of the optical functional film of FIG. As shown in FIG. 1, the optical
接着層102は、光学機能フィルム101を物品に貼り付けるための接着機能を有する。この例では、接着層102として、感熱ホットメルト剤を塗布したものが採用されている。感熱ホットメルトは、所定の熱を加えるとメルトし、接着機能を発現する接着材料である。接着層としては、シールに利用される粘着材料を利用してもよい。この場合、使用前は離型紙を粘着層に貼り付けておき、貼付時に離型紙を剥がし、貼付対象物に粘着材料の機能により貼り付けを行う。
The
光吸収層103は、可視光帯域の光を吸収する層である。この例では、黒色インクの印刷により光吸収層103が構成されている。光吸収層103は、カーボンブラックを分散させた樹脂フィルムによって構成してもよい。光吸収層としては、濃い青や緑といった可視光帯域の光がある程度吸収される色を有しているインクや材料を利用することができる。光吸収層は、カーボンブラック等の可視光帯域の光を吸収する材料を分散させた接着剤を塗布し、硬化させたものを利用してもよい。
The
また、接着層と光吸収層とを兼ねた構造を採用してもよい。例えば、カーボンブラック等の可視光を吸収する材料の粉末を混ぜた接着剤を塗布し、接着層102を形成した場合、接着層102が光吸収層としても機能する。この場合、光吸収層103を省くことができる。
Moreover, you may employ | adopt the structure which served as the contact bonding layer and the light absorption layer. For example, when an adhesive mixed with powder of a material that absorbs visible light such as carbon black is applied to form the
多層薄膜フィルム層104は、2種類の屈折率を有する可視光を透過する光透過性の樹脂フィルムを交互に積層した構造を有する。この例では、添加物により屈折率に違いを持たせた2種類のPET(ポリエチレンテレフタレート)フィルムを交互に201層積層した積層構造を採用している。この例では、一方のPETフィルムとして、添加物であるイソフタル酸を15モル%共重合したものを用い、PETフィルム間における屈折率の違いを設定している。ここで、多層薄膜フィルム層104が、熱収縮性とブルーシフトを示す層として機能する。
The multilayer
屈折率を制御する目的で使用される添加物としては、イソフタル酸、2,6−ナフタレンジカルボン酸のような芳香族カルボン酸、あるいはアジピン酸、アゼライン酸のような脂肪族ジカルボン酸等が挙げられる。 Additives used for the purpose of controlling the refractive index include aromatic carboxylic acids such as isophthalic acid and 2,6-naphthalenedicarboxylic acid, and aliphatic dicarboxylic acids such as adipic acid and azelaic acid. .
印刷表示層105は、アルミニウム箔の一方の面に図2に示すような図柄が印刷され、金属光沢面に任意のロゴが表示されるようになっている。印刷表示層105は、多層薄膜フィルム層104の全体を覆っているわけでなく、領域106の部分においては、多層薄膜フィルム104が露出した状態となっている。すなわち、図2に示されるように、光学機能フィルム101の印刷表示層105の側の面を見た場合、領域107において印刷表示層105の金属光沢面および印刷内容が視認され、領域106において多層薄膜フィルム層104が視認される。
The printed
したがって、印刷表示層105側の面を見た場合、領域107の部分の印刷内容と領域106の部分のブルーシフトを視認することができる。この場合、光学機能フィルム101に対する視野角を大きくすると(つまりより面に平行な方向から見るような見方をすると)、領域107の部分の印刷内容は通常の印刷面を斜めからみる場合と同じように見えるのであるが、領域106の部分は視野角が大きくなる程、より短波長側の色に反射して見えるように見え方が変化する。例えば、視野角を大きくしてゆくに従い、領域106の部分が赤→緑→青といった具合に色調が変化して見える。
Therefore, when the surface on the
印刷表示層105は、多層薄膜フィルム層104の表面にアルミニウム箔を蒸着することで形成される。また、印刷表示層105としてアルミニウム箔を用いるのではなく、多層薄膜フィルム層104に直接印刷により文字や図柄を形成し、それを印刷表示層としてもよい。
The printed
熱収縮性およびブルーシフトを示す多層薄膜フィルム層を得るための材料の組合せとしては、ポリエチレン−2,6−ナフタレートからなる第1のフィルムと、コポリエチレンテレフタレートからなる第2のフィルムとを交互に積層した構造のものを採用することもできる。また、多層薄膜フィルム層を構成する他の材料としては、ポリスチレン、ポリプロピレン、塩化ビニル、ポリエチレン等を利用することができる。また、以上例示した材料の2種以上の組合せを利用することもできる。本発明を実施する場合には、ブルーシフトが現れるように、異なる屈折率を有するフィルム間の界面が多層に存在するように、屈折率の異なる光透過性フィルムを積層する点が重要となる。 As a combination of materials for obtaining a multilayer thin film layer exhibiting heat shrinkability and blue shift, a first film made of polyethylene-2,6-naphthalate and a second film made of copolyethylene terephthalate are alternately used. A layered structure can also be employed. In addition, polystyrene, polypropylene, vinyl chloride, polyethylene, and the like can be used as other materials constituting the multilayer thin film layer. A combination of two or more of the materials exemplified above can also be used. In practicing the present invention, it is important to laminate light-transmitting films having different refractive indexes so that the interfaces between films having different refractive indexes exist in multiple layers so that a blue shift appears.
1−2.実施形態の製造方法
以下、図1および図2に示す光学機能フィルム101の製造方法の一例を説明する。まず多層薄膜フィルム層104の製造方法について説明する。多層薄膜フィルム層104は、PET材料からなる第1の層と、PET材料に屈折率を調整するための添加物であるイソフタル酸を15モル%添加した第2の層とを交互に201層積層し、圧力を加えることで、各層を密着させ一体化させることで得る。
1-2. Manufacturing Method of Embodiment Hereinafter, an example of a manufacturing method of the optical
そして、90℃の温度を加えながら1軸延伸処理を加えることで、熱収縮性を付与する。この延伸条件によって得た多層薄膜フィルム層104は、150℃の温度を加えると寸法比で約60%に収縮する性質を有したものとなる。
And heat shrinkability is provided by adding a uniaxial stretching process, adding the temperature of 90 degreeC. The multilayer
多層薄膜フィルム層104を得たら、その一方の面に黒色のインクを印刷し、光吸収層103を形成する。さらに、光吸収層103の露出した面に感熱ホットメルト剤を塗布し、接着層102を形成する。また、他方の面にアルミニウム箔を蒸着し、さらに印刷を施して印刷表示層105を形成する。
When the multilayer
なお、印刷を行う被印刷面にインクの密着性を向上させ、また被印刷面を保護するためにプライマー層を形成してもよい。プライマー層は、塩化ビニル・酢酸ビニル共重合体樹脂、ポリエステル系樹脂、あるいはポリウレタン系樹脂等の樹脂材料を主成分とした溶剤希釈タイプのコート剤を塗布し、乾燥させることで形成すればよい。このプライマー層は、被印刷面として多層薄膜フィルム等の他の層を選択する場合においても利用することができる。 A primer layer may be formed to improve the adhesion of the ink to the printing surface on which printing is performed and to protect the printing surface. The primer layer may be formed by applying a solvent dilution type coating agent mainly composed of a resin material such as a vinyl chloride / vinyl acetate copolymer resin, a polyester resin, or a polyurethane resin and drying it. This primer layer can also be used when another layer such as a multilayer thin film is selected as the printing surface.
こうして、図1および図2に示す光学機能フィルム101を得る。各層の厚さは任意に設定可能であるが、本実施形態では、接着層102の厚さを10μm、光吸収層103の厚さを10μm、多層薄膜フィルム層104の厚さを20μm、印刷表示層105の厚さを5μmとした。なお接着層102として、70℃の温度でメルトし接着力を発揮するものを使用した。
Thus, the optical
なお、熱収縮性を制御する目的で、多層薄膜フィルム層104に対して熱固定処理を加えても良い。熱固定処理は、面圧を加えた状態で加熱を行うことで、その後の加熱における収縮を抑制する処理である。熱固定処理を行うことで、後の工程における熱収縮の具合を調整することができる。
In addition, you may add a heat setting process with respect to the multilayer thin
1−3.実施形態の応用
以下、図1および図2に示す光学機能フィルム101を用いて乾電池を包装する例を説明する。図3は、光学機能フィルムにより乾電池を包装する作業工程を示す模式図である。まず、図1および図2に示す光学機能フィルム101を用意し、80℃の熱を加えることで、接着層102に接着機能を発現させる。この状態のものを図3(a)に示すように乾電池305の周囲に巻き付け、図3(b)に示す状態を得る。これにより乾電池305と光学機能フィルム101とが密着する。この際、光学機能フィルム101の幅を乾電池101の長さより長いものとし、乾電池305の両端において光学機能フィルム101が少しはみ出すようにする。図3(b)には、このはみ出した部分306および307が示されている。
1-3. Application of Embodiments Hereinafter, an example of packaging a dry battery using the optical
なお図3(a)において、光学機能フィルム101の多層薄膜フィルム層104(図1参照)に対して行われた一軸延伸処理の方向と、乾電池305の円周方向(円筒表面の周方向)とを一致させた状態とする。こうすることで、乾電池両端の縁部分における熱収縮を乾電池305の形状に合わせてスムーズに行わせることができる。
3A, the direction of uniaxial stretching performed on the multilayer thin film layer 104 (see FIG. 1) of the optical
次に乾電池305の両端部分にはみ出した符号306および307により示される部分を選択的に155℃の温度に加熱する。この加熱により符号306および307の部分が熱収縮し、図3(c)の符号309によって示されるように乾電池305の端面の縁部分が光学機能フィルム101によって包み込まれる。こうして、光学機能フィルム101によって包装された乾電池308が得られる。
Next, the portions indicated by
この乾電池308は、符号310で示される部分において、通常の商品名等の印刷表示が行われ、符号311で示される部分がブルーシフトによる識別機能を示す。
In the
乾電池は円筒なので、符号311の部分が円周方向に向かってブルーシフトに従うグラデーションを示す特異な見え方をする。この見え方は、多層薄膜フィルム層104に加える延伸条件によって微妙に調整されたものとなる。従って、詳細な製造条件が分からなければ、完成品からこの特異な見え方を再現することは困難である。特に多層薄膜フィルム層104は、一体化しており、構成するPET層を単層に分離することは極めて困難であるので、リバースエンジニアリングによってブルーシフトの見え方を再現することは容易ではない。したがって、真贋の見極めが困難な乾電池308の偽造品を製造することは極めて困難なものとなる。
Since the dry cell is a cylinder, the
また、符号311の部分における多層薄膜フィルム104の露出表面に文字や図柄を印刷してもよい。こうすると、印刷された文字や図柄の背景がブルーシフトを示す光学機能を得ることができる。
Moreover, you may print a character and a pattern on the exposed surface of the multilayer
また、符号311の部分における光吸収層103を利用して、文字や図柄を形成してもよい。つまり、印刷によって文字や図柄による部分的な光吸収層を形成してもよい。この場合、光吸収層103によって形成された文字や図柄がブルーシフトを示し、特異な色彩を従った表示として視認される。
Moreover, you may form a character and a pattern using the
また、光吸収層103上に光吸収層103とは異なる色に見える文字や図柄を印刷により形成してもよい。この場合、ブルーシフトを示す背景にこの背景とは異なる色合いのブルーシフトを示す印刷内容が浮かび上がって見える視覚効果を得ることができる。
Further, on the
さらに、図3(c)に示すように、光学機能フィルム101は、乾電池305の形状に合わせて収縮(シュリンク)しているので、乾電池305から取り外して再利用することは困難である。なぜなら、熱収縮は非可逆変化であり、一旦熱収縮したものを元に戻すことはできないからである。
Further, as shown in FIG. 3C, the optical
また、多層薄膜フィルム104の熱収縮した部分もブルーシフトを示す。このブルーシフトは、収縮した形状による影響を受けたものであるので、さらに特異な見え方を示すものとなる。このことは、偽造が困難で識別性の高い識別媒体として有利なこととなる。また、ここで例示したような熱収縮を利用して、光学機能フィルムで物品を包装する方法は、流れ作業的に大量生産が可能であり、コスト増を招かない優位性がある。
Further, the heat-shrinked portion of the multilayer
また、光学機能フィルム101の多層薄膜フィルム層104(図1参照)に対する延伸処理として、2軸延伸を行い、乾電池305の円筒軸方向における熱収縮性を付与してもよい。所定の方向による熱収縮の程度は延伸処理によって調整できるので、乾電池305の微妙な形状に合わせて、方向による熱収縮の程度を微調整してもよい。
1−4.他の包装方法
図4は、上述した光学機能フィルムを用いた乾電池の包装方法の他の例を示す模式図である。図4に示す方法では、長手形状の光学機能フィルム402を製造し、それをロール形状401に巻き取ったものを使用する。なお、光学機能フィルムとしては、図1に図示した構造において、接着層102を設けない構造のものを用意する。
Further, as a stretching process for the optical thin film layer 104 (see FIG. 1) of the optical
1-4. Other Packaging Methods FIG. 4 is a schematic diagram showing another example of a method for packaging a dry battery using the above-described optical functional film. In the method shown in FIG. 4, an optical
まず、図示されているように、ロール形状401に巻き取られた長手形状の光学機能フィルム402を引き出し、カッター403によって所定の長さに切断することで光学機能フィルム101を得る。次に切断された光学機能フィルム101を円筒形状405に丸め、その丸めたものを乾電池305に被せる。
First, as shown in the drawing, the optical
そして、熱収縮を行わせるための加熱を行い、円筒形状にした光学機能フィルムを熱収縮させる。この熱収縮により、円筒形状405が全体的に収縮し、さらに光学機能フィルム101の乾電池305の両端からはみ出した部分306および307が、乾電池305の端面の縁部分を覆うように内側に折れながら収縮する。こうして、光学機能フィルムで包装された乾電池308が得られる。この例では、接着材料の機能は利用されず、光学機能フィルムが熱収縮することで、乾電池305が締め付けられるようにして包装された状態が得られる。また、符号305および307の部分が乾電池の端面の縁部分を立体的に覆う構造になるので、接着剤を利用しなくても、光学機能フィルムによるしっかりとしたズレの生じない包装状態を得ることができる。
And the heating for performing heat contraction is performed, and the optical function film made into the cylindrical shape is heat contracted. Due to this thermal contraction, the
2−1.他の実施形態
以下、光学機能フィルムの構造のバリエーションについて説明する。図5〜図7は、他の実施形態の構造を示す断面図である。
2-1. Other Embodiments Hereinafter, variations of the structure of the optical functional film will be described. 5-7 is sectional drawing which shows the structure of other embodiment.
図5に示すのは、接着層501、光吸収層502および多層薄膜フィルム層503を備えた光学機能フィルム500である。この光学機能フィルム500も多層薄膜フィルム503が熱収縮性を有し、そのために加熱することで全体が収縮する。この例では、多層薄膜フィルム503の全体を視認し、ブルーシフトを観察することになる。
FIG. 5 shows an optical
この例において、多層薄膜フィルム503の露出した表面に文字や図柄等を印刷表示してもよい。この場合、多層薄膜フィルム503が示すブルーシフト表示を背景に印刷内容が浮かび上がる視覚効果を得ることができる。
In this example, characters, designs, etc. may be printed on the exposed surface of the multilayer
また、光吸収層502を利用して、文字や図柄を形成してもよい。つまり、印刷によって文字や図柄による部分的な光吸収層を形成してもよい。この場合、光吸収層502によって形成された文字や図柄がブルーシフトを示し、特異な色彩を従った表示として視認される。
Moreover, you may form a character and a pattern using the
また、光吸収層502上に光吸収層502とは異なる色に見える文字や図柄を印刷により形成してもよい。この場合、ブルーシフトを示す背景にこの背景とは異なる色合いのブルーシフトを示す印刷内容が浮かび上がって見える視覚効果を得ることができる。
Further, on the
図6に示すのは、接着層601、アルミニウム箔602、印刷表示層603および多層薄膜フィルム層605を備えた光学機能フィルム600である。ここで、印刷表示層603は光透過性フィルムであり、その表面には黒インクによる印刷表示604が印刷されている。
FIG. 6 shows an optical
この構成では、印刷表示604がブルーシフトによって際だって認識される。この構成では、印刷表示604以外の部分はアルミニウム箔602からの反射があるので、多層薄膜フィルム層605におけるブルーシフトは観察し難く(あるいは顕著でなく)、印刷表示604の部分では、印刷部分への到達光が吸収されるので、多層薄膜フィルム層605における反射光の干渉を観察し易い。このため、キラキラした反射光の背景の中に印刷表示604がブルーシフト現象によって浮かび上がって見える。
In this configuration, the
図7に示すのは、接着層701、光吸収層702、多層薄膜フィルム層703およびホログラム層704を備えた光学機能フィルム700である。
FIG. 7 shows an optical
ホログラム層704は、ホログラム705を構成する凹凸形状が付与し易い光透過性の材質で構成された層である。このような材質としては、ポリエステル樹脂、ポリスチレン樹脂、ポリプロピレン樹脂、ポリエチレン樹脂等が挙げられる。この構成によれば、ホログラム705がブルーシフトによって浮かび上がる視覚効果が得られる。また、ホログラムを視認する側の面に形成することで、ホログラムを認識し易くでき、ホログラムの機能を有効に活用することができる。なお、ホログラム層を光吸収層702と多層薄膜フィルム層703との間に設けてもよい。
The
ホログラム機能は、ホログラム層704を別に設ける構造とせず、ホログラム効果を得るための凹凸構造やエンボス構造を多層薄膜フィルム層703の上または下の一方の面、あるいは両方の面に直接形成することで得てもよい。
The hologram function does not have a structure in which the
2−2.他の物品への応用
本発明の光学機能フィルムで覆われる物品としては、乾電池以外の多様のものを挙げることができる。ここでは、飲料水のボトルや化粧品の容器(瓶)の包装に本発明の光学機能フィルムを利用する場合の例を説明する。図9は、瓶を光学機能フィルムで包装する手順を示す模式図である。
2-2. Application to other articles Examples of articles covered with the optical functional film of the present invention include various things other than dry batteries. Here, the example in the case of utilizing the optical function film of this invention for packaging of the bottle of drinking water and the container (bottle) of cosmetics is demonstrated. FIG. 9 is a schematic diagram showing a procedure for packaging a bottle with an optical functional film.
この例では、長手形状の光学機能フィルム902を製造し、それをロール形状901に巻き取ったものを使用する。なお、光学機能フィルムとしては、図1に図示した構造において、接着層102を備えていないものを使用する。
In this example, an optical
まず、ロール形状901に巻き取られた長手形状の光学機能フィルム902を引き出し、それをカッター903によって所定の長さに切断することで光学機能フィルム904を得る。次に切断された光学機能フィルム904を円筒形状905に丸め、その丸めたものを瓶906に被せる。
First, an optical
この際、光学機能フィルムの多層薄膜フィルム層に対する1軸延伸の方向が円筒形状905の周方向に一致するようにする。こうすることで、瓶906の形状に追従した熱収縮を行わすことができる。なお、瓶906の形状によっては、光学機能フィルムの多層薄膜フィルム層に対して2軸延伸を施し、2次元的な熱収縮を行わせてもよい。
At this time, the direction of uniaxial stretching with respect to the multilayer thin film layer of the optical functional film is made to coincide with the circumferential direction of the
そして、熱収縮をさせるための加熱を行い、円筒形状905に丸めた光学機能フィルムを収縮させる。この際、円筒形状905に丸められた光学機能フィルム904は、瓶906の曲面に沿って収縮する。こうして、光学機能フィルムで包装された瓶907が得られる。
Then, heating for causing heat shrinkage is performed, and the optical functional film rolled into the
この包装においては、瓶906の形状に沿って、円筒形状905に形成された光学機能フィルム904が収縮するので、接着剤による接着を行わなくても、外れることのない包装状態を得ることができる。また、このよう方法による包装は、流れ作業的に大量生産が可能であり、コスト的に極めて有利である。こうして、コスト増を招かずに効果的な真贋判定機能を付与することができる。
In this packaging, since the optical
本発明は、乾電池や日用品といった物品の包装に利用し、それらの商品に真贋判定機能を付与することができる。本発明は、真贋判定機能に限定されず、ブルーシフト効果を観察でき、熱収縮機能により物品の凹凸や曲面を覆うことができる光学機能フィルムとして、あらゆる物品の包装や被覆用途に利用することができる。 INDUSTRIAL APPLICABILITY The present invention can be used for packaging articles such as dry batteries and daily necessities, and can give an authenticity determination function to those articles. The present invention is not limited to the authenticity determination function, and can be used for packaging and coating of any article as an optical functional film that can observe the blue shift effect and can cover the unevenness and curved surface of the article by the heat shrink function. it can.
101…光学機能フィルム、102…接着層、103…光吸収層、104…多層薄膜フィルム層、105…印刷表示層、106…ブルーシフトを示す領域、107…印刷表示が見える領域、305…乾電池、306…乾電池の端部からはみ出した光学機能フィルムの部分、307…乾電池の端部からはみ出した光学機能フィルムの部分、308…光学機能フィルムによって包装された乾電池、309…熱収縮し乾電池の端面を覆った光学機能フィルムの部分、310…通常の印刷表示が行われる部分、311…ブルーシフトによる識別機能を発現する部分、401…ロール形状に巻き取られた長手形状の光学機能フィルム、402…長手形状の光学機能フィルム、403…カッター、405…円筒形状に丸められた光学機能フィルム、500…光学機能フィルム、501…接着層、502…光吸収層、503…多層薄膜フィルム層、600…光学機能フィルム、601…接着層、602…アルミニウム箔、603…印刷表示層、604…印刷表示、605…多層薄膜フィルム層、700…光学機能フィルム、701…接着層、702…光吸収層、703…多層薄膜フィルム層、704…ホログラム層、705…ホログラム、801…第1の屈折率を有する光透過性の薄膜フィルム、802…第2の屈折率を有する光透過性の薄膜フィルム、803…多層薄膜フィルム層、901…ロール形状に巻き取られた長手形状の光学機能フィルム、902…長手形状の光学機能フィルム、903…カッター、904…光学機能フィルム、905…円筒形状に丸められた光学機能フィルム、906…瓶、907…光学機能フィルムで包装された瓶、908…熱収縮処理が施される部分。
DESCRIPTION OF
Claims (11)
熱収縮により物品を包装する熱収縮性を備え、
前記熱収縮性は異方性を有し、
前記熱収縮性の異方性により、面内における視野角の増加に従うブルーシフト現象に異方性が付与されていることを特徴とする光学機能フィルム。 It has a laminated structure in which light transmissive films having different refractive indexes are laminated in multiple layers,
With heat shrinkability to wrap the goods by heat shrinkage,
The heat shrinkability has anisotropy,
An optical functional film characterized in that anisotropy is imparted to a blue shift phenomenon according to an increase in viewing angle in a plane due to the heat-shrinkable anisotropy .
曲面の湾曲方向に向かって色彩変化が観察されることを特徴とする請求項1〜6のいずれかに記載の光学機能フィルム。 In a state along the curved surface shape,
The optical function film according to any one of claims 1 to 6, toward the curve direction of the curved surface, characterized in that the color change is observed.
異なる屈折率を有する光透過性のフィルムを多層に積層する積層ステップと、
前記積層ステップによって得た積層構造に対して延伸処理を施し、熱収縮性を付与する延伸ステップと
を備え、
前記延伸処理は異方性を有し、
前記延伸処理の異方性により、面内における視野角の増加に従うブルーシフト現象に異方性が付与されることを特徴とする光学機能フィルムの製造方法。 A method for producing an optical functional film having a structure in which light transmissive films having different refractive indexes are laminated in a multilayer structure,
A laminating step of laminating light transmissive films having different refractive indexes in multiple layers;
Stretching the laminated structure obtained by the laminating step to provide heat shrinkability,
The stretching treatment has anisotropy,
The method for producing an optical functional film, wherein anisotropy is imparted to a blue shift phenomenon according to an increase in viewing angle in a plane due to the anisotropy of the stretching treatment .
加熱し、前記光学機能フィルムの少なくとも一部を熱収縮させる熱収縮ステップと
を備えることを特徴とする光学機能フィルムで覆われた物品の被覆方法。 A covering step of covering the article with the optical functional film according to any one of claims 1 to 8 ,
A method for covering an article covered with an optical functional film, comprising: a heat shrinking step of heating and heat shrinking at least a part of the optical functional film.