JP3984629B2 - Copper-based composite substrate for electronic parts and electronic parts - Google Patents

Copper-based composite substrate for electronic parts and electronic parts Download PDF

Info

Publication number
JP3984629B2
JP3984629B2 JP2005361881A JP2005361881A JP3984629B2 JP 3984629 B2 JP3984629 B2 JP 3984629B2 JP 2005361881 A JP2005361881 A JP 2005361881A JP 2005361881 A JP2005361881 A JP 2005361881A JP 3984629 B2 JP3984629 B2 JP 3984629B2
Authority
JP
Japan
Prior art keywords
copper
base material
based composite
substrate
silicon
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
JP2005361881A
Other languages
Japanese (ja)
Other versions
JP2007162094A (en
Inventor
靖 真砂
和志 林
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kobe Steel Ltd
Original Assignee
Kobe Steel Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kobe Steel Ltd filed Critical Kobe Steel Ltd
Priority to JP2005361881A priority Critical patent/JP3984629B2/en
Priority to KR1020087009569A priority patent/KR20080050518A/en
Priority to CN2006800370267A priority patent/CN101297066B/en
Priority to PCT/JP2006/322625 priority patent/WO2007069419A1/en
Priority to TW095143779A priority patent/TW200735304A/en
Publication of JP2007162094A publication Critical patent/JP2007162094A/en
Application granted granted Critical
Publication of JP3984629B2 publication Critical patent/JP3984629B2/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Description

本発明は、電子部品に用いられる電子部品用銅系複合基材、それを用いた電子部品及び前記電子部品用銅系複合基材の製造方法に関する。   The present invention relates to a copper-based composite substrate for electronic components used for electronic components, an electronic component using the same, and a method for producing the copper-based composite substrate for electronic components.

従来から、各種半導体装置における回路基板やリードフレーム，電極，端子部分等（以下、単に回路基板等ともいう）には、銅系の金属材料が用いられている。   Conventionally, copper-based metal materials have been used for circuit boards, lead frames, electrodes, terminal portions, etc. (hereinafter also simply referred to as circuit boards) in various semiconductor devices.

前記銅系の金属材料としては、電気配線と連結する際の端子部における接触抵抗を低くするために、銅基材又は銅合金基材の表面に錫又は錫系合金からなる被覆層が形成された複合材（以下、単に、銅系複合基材ともいう）が好ましく用いられている。このような被覆層は、銅の酸化を抑制する層であり、電気配線と連結する際の端子部における接触抵抗を低くする働きをする。   As the copper-based metal material, a coating layer made of tin or a tin-based alloy is formed on the surface of the copper base material or the copper alloy base material in order to reduce the contact resistance at the terminal portion when connecting to the electrical wiring. A composite material (hereinafter also simply referred to as a copper-based composite base material) is preferably used. Such a coating layer is a layer that suppresses copper oxidation and serves to lower the contact resistance at the terminal portion when connecting to the electrical wiring.

前記銅系複合基材からなる回路基板等は、通常、樹脂封止材で封止されるが、信頼性の観点から、回路基板等の表面と樹脂成分との密着性（接着性）は非常に重要である。前記密着性が乏しい場合には、回路基板等と樹脂封止材との間で剥離が生じ、その剥離した部分から水分や腐食性ガスが侵入することにより、回路基板等を腐食して、その結果、半導体装置の信頼性を低下させる恐れがある。   The circuit board made of the copper-based composite base material is usually sealed with a resin sealing material, but from the viewpoint of reliability, the adhesion (adhesion) between the surface of the circuit board and the resin component is very high. Is important to. When the adhesion is poor, peeling occurs between the circuit board and the resin sealing material, and moisture or corrosive gas enters from the peeled portion, thereby corroding the circuit board and the like. As a result, the reliability of the semiconductor device may be reduced.

前記銅系複合基材と樹脂成分との密着性を高める方法としては、シランカップリング剤で基材表面を表面処理して、密着性を向上させる、従来から知られている方法が挙げられる（例えば、特許文献１）。   Examples of a method for improving the adhesion between the copper-based composite substrate and the resin component include a conventionally known method in which the substrate surface is surface-treated with a silane coupling agent to improve the adhesion ( For example, Patent Document 1).

しかしながら、高温多湿下で使用され、また、高電圧が使用される自動車に搭載される電装部品や、電装部品を制御する制御ユニット等の半導体装置のように、より高い信頼性が求められる半導体装置においては、前記方法により得られる密着性向上効果の程度は不充分であり、更なる密着性の向上が求められていた。
特開２００２−２７０７４０号公報 However, semiconductor devices that are used under high temperature and high humidity, and are required to have higher reliability, such as semiconductor devices such as electrical components mounted on automobiles that use high voltages and control units that control electrical components. However, the degree of adhesion improvement obtained by the above method is insufficient, and further improvement in adhesion has been demanded.
JP 2002-270740 A

本発明者らは、前記のように半導体装置、特に、自動車に搭載されるような制御ユニット等の半導体装置において用いられる銅系複合基材において、銅系複合基材と樹脂成分との密着性をより高めることができる電子部品用銅系複合基材、それを用いた電子部品及び前記電子部品用銅系複合基材の製造方法を提供することを課題とする。   In the copper-based composite base material used in the semiconductor device as described above, particularly in a semiconductor device such as a control unit mounted on an automobile, the adhesion between the copper-based composite base material and the resin component It is an object of the present invention to provide a copper-based composite base material for electronic components, an electronic component using the same, and a method for producing the copper-based composite base material for electronic components.

本発明の電子部品用銅系複合基材は、銅基材又は銅合金基材の表面に錫又は錫系合金からなる被覆層が形成されてなる銅系複合基材において、前記被覆層表面に、炭化水素基及び／又は水酸基を含有するシリコン酸化物薄膜が形成されていることを特徴とするものである。   The copper-based composite base material for electronic components of the present invention is a copper-based composite base material in which a coating layer made of tin or a tin-based alloy is formed on the surface of a copper base material or a copper alloy base material. A silicon oxide thin film containing a hydrocarbon group and / or a hydroxyl group is formed.

ここで、本発明に用いられる銅系複合基材とは、純銅の他、各種銅合金、具体的には例えば、Ｃｕ-Ｆｅ-Ｐ系合金、Ｃｕ-Ｎｉ-Ｓｉ系合金、Ｃｕ-Ｃｒ-Ｚｒ系、Ｃｕ−Ｚｎ系合金、Ｃｕ−Ｓｎ系合金等の各種銅及び銅合金からなる基材（以下、銅系基材ともいう）の表面に、電気めっき、無電解めっき、溶融めっき、プラズマＣＶＤ等の方法により錫又は錫系合金からなる被覆層が形成された、電子部品の分野で用いられている公知のものが用いられる。   Here, the copper-based composite substrate used in the present invention is not only pure copper but also various copper alloys, specifically, for example, Cu-Fe-P-based alloys, Cu-Ni-Si-based alloys, Cu-Cr- Electroplating, electroless plating, hot dipping, plasma on the surface of various copper and copper alloys such as Zr-based, Cu-Zn-based alloys, Cu-Sn-based alloys (hereinafter also referred to as copper-based substrates) The well-known thing used in the field | area of the electronic component in which the coating layer which consists of tin or a tin-type alloy was formed by methods, such as CVD, is used.

また、必要に応じて、前記銅系基材と前記被覆層との間には、その他の層が介在しても良い。具体的には、例えば、銅系基材と前記被覆層との間に銅系金属、ニッケル系金属等からなる層が一層、あるいは、複数層介在しても良い。   Moreover, another layer may intervene between the said copper-type base material and the said coating layer as needed. Specifically, for example, a layer made of a copper-based metal, a nickel-based metal, or the like may be interposed between the copper-based substrate and the coating layer, or a plurality of layers may be interposed.

前記被覆層が、電気めっきされた錫又は錫系合金から形成される場合（電気光沢めっき）には、めっき層の残留応力によりウィスカが発生する場合がある。このような場合には、残留応力を除去してウィスカの発生を抑制するために、更に、１００〜６００℃の温度でリフロー処理（熱処理）しても良い。このようにして得られる錫めっきは、通常、リフロー錫めっきとも呼ばれる。このようにリフロー処理した場合には、Ｃｕ−Ｓｎ系合金や、銅系基材にニッケル系金属が含有される場合には、Ｃｕ-Ｎｉ-Ｓｎ系合金が被覆層中に形成される。   When the coating layer is formed from electroplated tin or a tin-based alloy (electrobright plating), whiskers may be generated due to residual stress of the plating layer. In such a case, reflow treatment (heat treatment) may be performed at a temperature of 100 to 600 ° C. in order to remove residual stress and suppress the generation of whiskers. The tin plating obtained in this way is usually called reflow tin plating. When the reflow treatment is performed in this manner, a Cu—Ni—Sn alloy is formed in the coating layer when a Cu—Sn alloy or a nickel-based metal is contained in the copper substrate.

前記被覆層の厚みは、特に限定されないが０．１〜１０μｍ、更には０．５〜５μｍ、特には、０．５〜３μｍ程度であることが好ましい。前記被覆層が厚すぎる場合には、銅系基材に対する酸化抑制効果は変わらない反面、耐熱性が低下し、また、経済的に不利になる傾向があり、更に、本発明の電子部品用銅系複合基材を、挿抜式の端子に用いる場合には、オス端子とメス端子の挿抜力高くなりすぎる傾向がある。一方、薄すぎる場合には、前記酸化抑制効果が不充分になる傾向がある。   The thickness of the coating layer is not particularly limited, but is preferably 0.1 to 10 μm, more preferably 0.5 to 5 μm, and particularly preferably about 0.5 to 3 μm. If the coating layer is too thick, the oxidation suppression effect on the copper-based substrate is not changed, but the heat resistance tends to be lowered, and it tends to be economically disadvantageous. Further, the copper for electronic parts of the present invention When the system composite substrate is used for an insertion / extraction type terminal, the insertion / extraction force of the male terminal and the female terminal tends to be too high. On the other hand, when it is too thin, the oxidation inhibiting effect tends to be insufficient.

前記銅系複合基材の被覆層表面に形成される炭化水素基及び／又は水酸基を含有するシリコン酸化物薄膜としては、例えば、後述するプラズマＣＶＤ法において、その原料ガスとしてシリコン系アルコキシドを含有するシリコン含有反応ガスを用いて形成される薄膜が挙げられる。   As a silicon oxide thin film containing a hydrocarbon group and / or a hydroxyl group formed on the surface of the coating layer of the copper-based composite base material, for example, in a plasma CVD method described later, a silicon-based alkoxide is included as a raw material gas. Examples include a thin film formed using a silicon-containing reaction gas.

本発明におけるシリコン酸化物薄膜は、Ｓｉ-Ｏ結合からなるシリコン酸化物薄膜中にシリコン系アルコキシドのプラズマ分解物又はシリコン系アルコキシドと酸素含有分子とのプラズマ分解物に由来する炭化水素基及び／又は水酸基を含有する。   The silicon oxide thin film according to the present invention is a silicon oxide thin film composed of Si—O bonds, a hydrocarbon group derived from a plasma decomposition product of silicon alkoxide or a plasma decomposition product of silicon alkoxide and oxygen-containing molecules, and / or Contains a hydroxyl group.

前記炭化水素基及び／又は水酸基は、樹脂成分と銅系複合基材との密着性を向上させる成分であり、具体的には、例えば、テトラメトキシシラン、ヘキサメチルジシロキサン、ヘキサメチルジシラザン等のプラズマ分解物に由来するメチル基（―ＣＨ３）やテトラエトキシシラン等のエチル基（―Ｃ２Ｈ５）を有するシリコン系アルコキシドのプラズマ分解物に由来する炭化水素基及び前記シリコン系アルコキシドのプラズマ分解物と酸素含有分子のプラズマ分解物が再結合して形成されるような水酸基が挙げられる。また、γ-グリシドキシプロピルトリメトキシシラン、γ-グリシドキシプロピルトリエトキシシラン、β―（３，４エポキシシクロヘキシル）エチルトリメトキシシランや、γ―アミノプロピルトリエトキシシラン等の反応性官能基を有するシリコン系アルコキシドのプラズマ分解物に由来する炭化水素基及び／又は水酸基等も挙げられる。これらは１種のみで用いても、２種以上を組合せて用いてもよい。 The hydrocarbon group and / or hydroxyl group is a component that improves the adhesion between the resin component and the copper-based composite substrate. Specifically, for example, tetramethoxysilane, hexamethyldisiloxane, hexamethyldisilazane, etc. The hydrocarbon group derived from the plasma decomposition product of a silicon-based alkoxide having an ethyl group (—C 2 H 5 ) such as a methyl group (—CH 3 ) or tetraethoxysilane derived from the plasma decomposition product of Examples include hydroxyl groups formed by recombination of plasma decomposition products and plasma decomposition products of oxygen-containing molecules. In addition, reactive functional groups such as γ-glycidoxypropyltrimethoxysilane, γ-glycidoxypropyltriethoxysilane, β- (3,4-epoxycyclohexyl) ethyltrimethoxysilane, and γ-aminopropyltriethoxysilane Also included are hydrocarbon groups and / or hydroxyl groups derived from plasma-decomposed products of silicon-based alkoxides. These may be used alone or in combination of two or more.

前記含有される炭化水素基及び／又は水酸基の割合としては、特に限定されないが、銅系複合基材上に薄膜を形成する場合と同一の条件でシリコン基板上に成膜された膜についてＦＴ-ＩＲで測定した場合の吸光度表示におけるピーク強度比において、Ｓｉ―Ｏのピーク（１０７０〜１０８０ｃｍ-１）の強度に対するＳｉ-ＯＨのピーク（３０００〜３４００ｃｍ-１）の強度又は前記Ｓｉ―Ｏのピーク強度に対するＳｉ-ＣＨ３、Ｓｉ-Ｃ２Ｈ５及びＳｉ-Ｃ３Ｈ８のピーク（２８００〜２９００ｃｍ-１）の強度比は、０．０１〜０．５、さらには０．０５〜０．２であることが好ましい。前記ピーク強度比が小さすぎる場合には、樹脂成分との密着性改良効果が低い傾向があり、大きすぎる場合には膜強度が低く、耐久性が小さくなる傾向がある。なお、銅系基材上に成膜された薄膜を測定せずに、シリコン基板上に成膜された薄膜を測定した理由は、最も、一般的に用いられている透過型のＦＴ−ＩＲ法においては、不透明な銅系基材上に形成されたシリコン系薄膜のピーク強度は測定できず、また、銅系基材の成膜条件と同様の条件では同様のシリコン薄膜が形成されるためであり、更に、シリコン基板は赤外線領域で透明で、且つ、表面が比較的平坦であるため正確な測定ができるためである。 The ratio of the hydrocarbon group and / or hydroxyl group contained is not particularly limited, but FT- is a film formed on a silicon substrate under the same conditions as those for forming a thin film on a copper-based composite substrate. In the peak intensity ratio in the absorbance display when measured by IR, the intensity of the Si—OH peak (3,000 to 3400 cm −1 ) relative to the intensity of the Si—O peak (1070 to 1080 cm −1 ) or the Si—O peak The intensity ratio of Si—CH 3 , Si—C 2 H 5 and Si—C 3 H 8 peaks (2800 to 2900 cm −1 ) with respect to the intensity is 0.01 to 0.5, and further 0.05 to 0. 2 is preferable. When the peak intensity ratio is too small, the effect of improving the adhesion with the resin component tends to be low, and when it is too large, the film strength tends to be low and the durability tends to be low. In addition, the reason for measuring the thin film formed on the silicon substrate without measuring the thin film formed on the copper base material is the most commonly used transmission type FT-IR method. In this case, the peak intensity of the silicon-based thin film formed on the opaque copper-based substrate cannot be measured, and the same silicon thin film is formed under the same conditions as the film-forming conditions of the copper-based substrate. In addition, the silicon substrate is transparent in the infrared region and has a relatively flat surface, so that accurate measurement can be performed.

本発明におけるシリコン酸化物薄膜の厚みは特に限定されないが、1〜２００ｎｍ、さらには５〜１００ｎｍ程度であることが好ましい。前記膜厚が厚すぎる場合には成膜に時間がかかるためにコストアップの要因になるとともに、銅系複合基材に対する密着性、特に高温多湿環境下における密着性が低下し、また、薄すぎる場合には密着性改良効果が充分に得られないおそれがある。 Although the thickness of the silicon oxide thin film in this invention is not specifically limited, It is preferable that it is about 1-200 nm, Furthermore, about 5-100 nm. If the film thickness is too thick, it takes a long time to form the film, resulting in an increase in cost, and the adhesion to the copper-based composite substrate, particularly the adhesion in a high-temperature and high-humidity environment is reduced, and is too thin. In some cases, the adhesion improving effect may not be sufficiently obtained.

特に半導体装置に本発明の電子部品用銅系複合基材を用いる場合においては、膜厚が厚すぎる場合には、リフローはんだ工程における実装時の熱履歴等により吸湿し、銅系複合基材と薄膜との付着強度が低下する場合があるために１００ｎｍ以下の膜厚が好ましい。   In particular, when using the copper-based composite substrate for electronic parts of the present invention in a semiconductor device, if the film thickness is too thick, it absorbs moisture due to the heat history during mounting in the reflow soldering process, and the copper-based composite substrate and A film thickness of 100 nm or less is preferable because the adhesion strength with the thin film may decrease.

なお、前記薄膜は必ずしも連続膜に形成されている必要はなく、例えば、不連続で縞状にシリコン酸化物薄膜が形成されている場合には、樹脂成分のアンカー効果により密着強度を向上させることができる点から好ましい。   The thin film is not necessarily formed as a continuous film. For example, when the silicon oxide thin film is formed in a discontinuous and striped manner, the adhesion strength is improved by the anchor effect of the resin component. It is preferable because of

以上説明した本発明の電子部品用銅系複合基材は、樹脂成分との高い密着性とダイシェア強度値が得られるものであり、樹脂成分と本発明の電子部品用銅系複合基材とを接着した後に剥離した場合の樹脂破壊モードも、従来の銅系基材においては界面破壊で剥離していた場合にも本発明の電子部品用銅系複合基材においては、凝集破壊で剥離する傾向がある。   The copper-based composite base material for electronic parts of the present invention described above has high adhesion to the resin component and a die shear strength value, and the resin component and the copper-based composite base material for electronic parts of the present invention are combined. The resin failure mode when peeling after bonding is also a tendency to peel due to cohesive failure in the copper-based composite substrate for electronic parts of the present invention even when peeling is caused by interfacial failure in the conventional copper-based substrate There is.

従って、本発明の電子部品用銅系複合基材は、半導体装置をはじめとする各種電子部品の樹脂成分で封止や接着される金属部分、具体的には半導体装置のリードフレーム部分や電極，端子部分等に好ましく用いられる。更に、好ましい用途としては、特に、自動車のエンジンルームに代表されるような高温高湿にさらされる環境で使用される電装部品、具体的には、高電圧が用いられるエンジンコントロールユニットや電動パワーステアリング等の電装部品に用いられる電子部品が挙げられる。これらの電装部品は、ジャンクションブロック（ＪＢ）を経由し、エレクトリックコントロールユニット（ＥＣＵ）で制御されているが、近年、これらの電装品の集約化、一体化が進み、数種類の電装品を一体化したパワーディストリビュータ（ＰＤ）が開発され、ＥＣＵがエンジンルームに搭載される場合があるが、このような、高温高湿にさらされる環境において用いられる電子部品に好ましく用いられる。   Therefore, the copper-based composite base material for electronic parts of the present invention is a metal part that is sealed or bonded with a resin component of various electronic parts including a semiconductor device, specifically, a lead frame part or an electrode of a semiconductor device, It is preferably used for the terminal portion. Furthermore, preferred applications include electrical parts used in environments exposed to high temperatures and high humidity, as represented by the engine room of automobiles, specifically, engine control units and electric power steering systems that use high voltages. Electronic parts used for electrical parts such as These electrical components are controlled by an electric control unit (ECU) via a junction block (JB). In recent years, these electrical components have been integrated and integrated, and several types of electrical components have been integrated. The power distributor (PD) has been developed, and the ECU may be mounted in the engine room. However, the power distributor (PD) is preferably used for electronic parts used in such an environment exposed to high temperature and high humidity.

次に、本発明の電子部品用銅系複合基材の製造方法を具体的に説明する。   Next, the manufacturing method of the copper-type composite base material for electronic components of this invention is demonstrated concretely.

本発明の電子部品用銅系複合基材の製造方法は、放電によりプラズマを発生させるために備えられた少なくとも一対の電極対間にシリコン含有反応ガスを導入し、前記電極対間にプラズマを発生させることにより前記シリコン含有反応ガスを分解し、前記シリコン含有反応ガスの分解物に銅基材又は銅合金基材の表面に錫又は錫系合金からなる被覆層が形成されてなる銅系複合基材を接触させて、前記被覆層表面にシリコン酸化物薄膜を形成させることを特徴とする。   The method for producing a copper-based composite substrate for electronic parts according to the present invention introduces a silicon-containing reaction gas between at least a pair of electrodes provided to generate plasma by electric discharge, and generates plasma between the electrode pairs. The silicon-containing reaction gas is decomposed, and a decomposed product of the silicon-containing reaction gas is formed with a coating layer made of tin or a tin-based alloy on the surface of a copper base material or a copper alloy base material. A material is contacted to form a silicon oxide thin film on the surface of the coating layer.

具体的な一例としては、互いに対向する電極対を備え、前記電極対の一方の電極上に銅系複合基材を載置して、前記電極間にシリコン含有反応ガスを導入し、これをプラズマ化して銅系複合基材の被覆層表面に薄膜を形成させる方法等が用いられる。   As a specific example, a pair of electrode pairs facing each other is provided, a copper-based composite base material is placed on one electrode of the electrode pair, a silicon-containing reaction gas is introduced between the electrodes, and this is converted into plasma. And a method of forming a thin film on the surface of the coating layer of the copper-based composite substrate.

さらに具体的には、例えば、１０〜１０００Ｐａ程度の減圧条件下でグロー放電することによりプラズマを発生させて、基材上に薄膜を形成させる減圧プラズマＣＶＤ法（減圧プラズマ気相蒸着法）や、大気圧付近の圧力下でグロー放電することによりプラズマを発生させて基材上に薄膜を形成させる特開平６-２１４９号公報等で提案されている方法、対向する電極の少なくとも一方に誘電体を形成し、ＤＣパルスなどにより大気圧でプラズマを発生させるとともに、ガスの圧力で基材に原料ガスを吹き付ける特開２００２-２３７４８０号公報に記載の方法、さらには、例えば特開平９-１０４９８５号公報に開示されているような回転電極を用いて成膜する方法等が用いられる。   More specifically, for example, a low-pressure plasma CVD method (low-pressure plasma vapor deposition method) in which a plasma is generated by glow discharge under a reduced pressure condition of about 10 to 1000 Pa to form a thin film on a substrate, A method proposed in Japanese Patent Laid-Open No. 6-2149 or the like in which plasma is generated by glow discharge under a pressure near atmospheric pressure to form a thin film on a substrate, and a dielectric is applied to at least one of opposing electrodes A method described in Japanese Patent Laid-Open No. 2002-237480, in which a plasma is generated at atmospheric pressure by a DC pulse or the like, and a raw material gas is blown onto a substrate with a gas pressure. And a method of forming a film using a rotating electrode as disclosed in the above.

前記各種方法の中でも、電界の集中がないためにアーク放電がおきにくく、回転する電極に沿ってガス流が幅方向で均一になる等により連続的に生産性良く薄膜を形成することができる点から回転電極を用いたプラズマＣＶＤ法により成膜する方法が好ましい。   Among the various methods described above, arc discharge is difficult to occur because there is no concentration of electric field, and a thin film can be continuously formed with high productivity by making the gas flow uniform in the width direction along the rotating electrode. A method of forming a film by a plasma CVD method using a rotating electrode is preferable.

以下に、チャンバー内に回転電極を備えたプラズマＣＶＤ成膜装置を用いた成膜方法により本発明の電子部品用銅系複合基材を製造する方法を一例として詳しく説明する。なお、本発明の実施は以下の方法以外にも、例えば、チャンバーを備えない回転電極を用いたプラズマＣＶＤ成膜装置を用いた成膜方法等によっても実施可能である。   Hereinafter, a method for producing a copper-based composite substrate for electronic parts of the present invention by a film forming method using a plasma CVD film forming apparatus provided with a rotating electrode in a chamber will be described in detail as an example. In addition to the following method, the present invention can be implemented by, for example, a film forming method using a plasma CVD film forming apparatus using a rotating electrode without a chamber.

回転電極を用いたプラズマＣＶＤ法により銅系複合基材上にシリコン酸化物薄膜を成膜する方法は、チャンバー内部に対向する電極対を備え、放電電極を回転電極とし、その対向電極上に銅系複合基材を載置し、チャンバー内部にシリコン含有反応ガスを導入し、回転電極と銅系複合基材間（以下、「狭隙間」と呼ぶ）に大気圧付近の圧力下でグロー放電によるプラズマを発生させて、プラズマを狭隙間におけるライン状のプラズマとし、プラズマ空間を横切るように銅系複合基材をスキャンさせる方法である。前記方法によれば、装置の大型化を図ることなく大面積の成膜や表面処理を行うことができる。   A method of forming a silicon oxide thin film on a copper-based composite base material by a plasma CVD method using a rotating electrode includes an electrode pair facing the inside of a chamber, a discharge electrode serving as a rotating electrode, and a copper electrode on the counter electrode. A silicon-based reaction gas is introduced into the chamber, and glow discharge is performed between the rotating electrode and the copper-based composite substrate (hereinafter referred to as “narrow gap”) under a pressure near atmospheric pressure. In this method, plasma is generated, the plasma is changed to a line-shaped plasma in a narrow gap, and the copper-based composite substrate is scanned so as to cross the plasma space. According to the method, it is possible to perform film formation and surface treatment of a large area without increasing the size of the apparatus.

チャンバー内部に備えられる対向する電極対としては、一方の放電電極側を回転電極とし、その対向電極側を平面電極にして、前記対向電極上に銅系複合基材を載置する。   As a pair of opposing electrodes provided in the chamber, one discharge electrode side is a rotating electrode, and the opposing electrode side is a planar electrode, and a copper-based composite substrate is placed on the opposing electrode.

回転電極としては後に詳しく説明する図１に示すＣＶＤ成膜装置の構成例に示されているような円筒状回転電極のほか、図２に示されているような無端状ベルト電極等を用いることができる。   As the rotating electrode, in addition to the cylindrical rotating electrode as shown in the configuration example of the CVD film forming apparatus shown in FIG. 1 described in detail later, an endless belt electrode as shown in FIG. 2 is used. Can do.

回転電極の表面形状は特に限られず、平滑面の他、その表面に凹凸形状が形成されていてもよい。凹凸形状は、銅系複合基材上の所望の位置における回転電極と銅系複合基材との距離を調整することに用いられ、例えば、回転方向に沿って凹凸形状を形成した場合には、銅系複合基材上の凸部に対向する部分においてのみ優先的にプラズマを発生させることができ、その部分のみに優先的にシリコン酸化物薄膜を形成させることができる。従って、形成されるシリコン酸化物薄膜の表面に凹凸を形成することができる。
また、回転電極上に前記凹凸形状を設けた場合には、大気圧近傍で層流（粘性流）であるシリコン含有反応ガスを拡散させる効果もある。 The surface shape of the rotating electrode is not particularly limited, and an uneven shape may be formed on the surface in addition to the smooth surface. The concavo-convex shape is used to adjust the distance between the rotating electrode and the copper-based composite substrate at a desired position on the copper-based composite substrate. For example, when the concavo-convex shape is formed along the rotation direction, Plasma can be preferentially generated only in the portion facing the convex portion on the copper-based composite substrate, and the silicon oxide thin film can be formed preferentially only in that portion. Accordingly, irregularities can be formed on the surface of the formed silicon oxide thin film.
Further, when the uneven shape is provided on the rotating electrode, there is an effect of diffusing a silicon-containing reaction gas that is a laminar flow (viscous flow) near atmospheric pressure.

前記対向電極上には、具体的な用途に応じた所望の形状の銅系複合基材が載置される。   On the counter electrode, a copper-based composite base material having a desired shape according to a specific application is placed.

なお、本方法によって、銅系複合基材に対するシリコン酸化物薄膜の密着性を向上させるためには、銅系複合基材を加熱することも有効な手段である。前記加熱温度としては錫又は錫系合金が溶融せず、後述するシリコン含有反応ガスが結露しない７０℃以上、２３２℃以下が好ましいが、錫又は錫系合金の酸化が進まない２００℃以下、より望ましくは１５０℃以下であることが望ましい。   In addition, in order to improve the adhesiveness of the silicon oxide thin film with respect to a copper-type composite base material by this method, heating a copper-type composite base material is also an effective means. The heating temperature is preferably 70 ° C. or more and 232 ° C. or less at which tin or a tin-based alloy does not melt and the silicon-containing reaction gas described later does not condense. The temperature is desirably 150 ° C. or lower.

前記回転電極と対向電極に載置された銅系複合基材との間隔（前記狭隙間の間隔）は、回転電極に印加する高周波電力や、用いられるシリコン含有反応ガスの種類、組成比等によって適宜調整されるが、通常０．５〜５ｍｍ、さらには、１〜３ｍｍ程度とすることが好ましい。前記間隔が狭すぎる場合には、その狭隙間へのシリコン含有反応ガスの安定供給が図れず、回転電極の幅方向における狭隙間バラツキが顕著になり、均一な成膜が困難になり、また、狭隙間の狭化に伴って、安定なプラズマ生成を実現するには、電子・イオンのプラズマ荷電粒子の捕捉が必要になり、１００ＭＨｚ以上の高周波が必要になりコスト的に不利になる傾向がある。一方、前記間隔が広すぎる場合には、電界の減少やプラズマ密度の減少による成膜速度の低下を招いたり、回転電極の回転にて発生する層流によって成膜の前駆体が銅系複合基材上から排出されることによる成膜速度の低下およびチャンバー内の汚染等の問題が生じることがある。   The interval between the rotating electrode and the copper-based composite substrate placed on the counter electrode (the interval between the narrow gaps) depends on the high-frequency power applied to the rotating electrode, the type of silicon-containing reaction gas used, the composition ratio, etc. Although it adjusts suitably, it is usually 0.5-5 mm, Furthermore, it is preferable to set it as about 1-3 mm. When the interval is too narrow, the stable supply of the silicon-containing reaction gas to the narrow gap cannot be achieved, the narrow gap variation in the width direction of the rotating electrode becomes remarkable, and uniform film formation becomes difficult. Accompanying the narrowing of the narrow gap, in order to realize stable plasma generation, it is necessary to capture plasma charged particles of electrons and ions, and a high frequency of 100 MHz or more is required, which tends to be disadvantageous in terms of cost. . On the other hand, if the interval is too wide, the film formation rate may be reduced due to a decrease in the electric field or plasma density, or the film formation precursor may be caused by the laminar flow generated by the rotation of the rotating electrode. Problems such as a decrease in film formation speed and contamination in the chamber may occur due to the discharge from the material.

前記回転電極の周速度としては３０００ｃｍ／ｍｉｎ以上であることが好ましい。前記周速度が３０００ｃｍ／ｍｉｎ未満の場合には、成膜速度が遅くなる傾向があり、好ましくは１００００ｃｍ／ｍｉｎ以上とするのが良いが、収率の向上ということを考慮すると１０００００ｃｍ／ｍｉｎ以下であることが好ましい。   The peripheral speed of the rotating electrode is preferably 3000 cm / min or more. When the peripheral speed is less than 3000 cm / min, the film forming speed tends to be low, and preferably 10,000 cm / min or more. However, considering the improvement in yield, the film forming speed is less than 100,000 cm / min. Preferably there is.

そして、チャンバーにはシリコン含有反応ガスが導入され、また、好ましくは大気圧近傍の圧力に調整されている。
前記大気圧近傍の圧力とは、０．０１〜０．１ＭＰａ程度の圧力を意味し、この圧力範囲のうち、圧力調整が容易で装置構成機構が簡易になるという観点からして好ましい圧力範囲は０．０８〜０．１ＭＰａ程度であることが好ましい。 A silicon-containing reaction gas is introduced into the chamber and is preferably adjusted to a pressure close to atmospheric pressure.
The pressure in the vicinity of the atmospheric pressure means a pressure of about 0.01 to 0.1 MPa. Among these pressure ranges, a preferable pressure range is from the viewpoint that pressure adjustment is easy and the device configuration mechanism is simplified. It is preferably about 0.08 to 0.1 MPa.

前記シリコン含有反応ガスはシリコン系アルコキシドの他、好ましくは不活性ガス及び酸素等が含有される原料ガスである。
前記シリコン系アルコキシドとしては、例えば、テトラエトキシシラン、テトラメトキシシラン、メチルトリエトキシシラン、ヘキサメチルジシロキサン、ヘキサメチルジシラザン、γ-グリシドキシプロピルトリメトキシシラン、γ-グリシドキシプロピルトリエトキシシラン、β―（３，４エポキシシクロヘキシル）エチルトリメトキシシランや、γ―アミノプロピルトリエトキシシランが挙げられる。これらは単独でまたは２種以上を組合せて用いることができる。これらの中ではテトラエトキシシランが工業的に入手可能な点から好ましい。
なお、シリコン系アルコキシドは、大気圧近傍の圧力下でのプラズマＣＶＤを適用するに際して、プラズマＯＦＦ時において高圧下においてもＯ２との反応性が低いという理由で安全な物質である。 The silicon-containing reaction gas is preferably a raw material gas containing an inert gas and oxygen in addition to the silicon-based alkoxide.
Examples of the silicon alkoxide include tetraethoxysilane, tetramethoxysilane, methyltriethoxysilane, hexamethyldisiloxane, hexamethyldisilazane, γ-glycidoxypropyltrimethoxysilane, and γ-glycidoxypropyltriethoxy. Examples thereof include silane, β- (3,4 epoxycyclohexyl) ethyltrimethoxysilane, and γ-aminopropyltriethoxysilane. These can be used alone or in combination of two or more. Of these, tetraethoxysilane is preferred because it is industrially available.
Silicon-based alkoxide is a safe substance because it has low reactivity with O 2 even under high pressure when the plasma is turned off when applying plasma CVD under a pressure near atmospheric pressure.

また、前記不活性ガスは反応性のラジカルを発生しない雰囲気で安定なグロー放電を発生させるために用いられる成分であり、Ｈｅ、Ａｒ、Ｘｅ、Ｋｒ等の希ガスやＮ２等のガスが挙げられ、これらの１種以上を用いることができる。前記不活性ガスとしては、準安定励起状態の寿命が長いＨｅを用いることが好ましい。 The inert gas is a component used to generate a stable glow discharge in an atmosphere that does not generate reactive radicals, and examples thereof include rare gases such as He, Ar, Xe, and Kr, and gases such as N 2. One or more of these can be used. As the inert gas, it is preferable to use He having a long life in a metastable excited state.

さらに、本発明におけるシリコン含有反応ガス中には、その他の成分、具体的にはシリコン系アルコキシド以外のシリコン化合物や酸素（Ｏ2）、酸化窒素（Ｎ２Ｏ）等の窒素酸化物、水等が含有されてもよい。
特にシリコン含有反応ガス中に酸素を含有する場合には、シリコン系アルコキシドの酸化・架橋反応を促進するとともに、比較的高い割合で酸素を含有する場合にはシリコン酸化物薄膜に凹凸を形成させるためのパーティクルライクなシリコン酸化物薄膜を形成することができる。
前記酸素の含有割合としては、シリコン系アルコキシドとの体積比（酸素／シリコン系アルコキシド）で０．１〜２程度であることが好ましい。この比が０．１未満の場合には充分に酸化・架橋反応を促進する効果が少ないとともに、シリコン酸化物微粒子が充分に成長せず、また、２を超える場合にはパーティクルとなって堆積する傾向がある。 Further, in the silicon-containing reaction gas in the present invention, other components, specifically, silicon compounds other than silicon-based alkoxides, nitrogen oxides such as oxygen (O 2 ) and nitrogen oxide (N 2 O), water, etc. May be contained.
In particular, when oxygen is contained in the silicon-containing reaction gas, the oxidation / crosslinking reaction of the silicon-based alkoxide is promoted, and when oxygen is contained at a relatively high rate, unevenness is formed on the silicon oxide thin film. The particle-like silicon oxide thin film can be formed.
The oxygen content is preferably about 0.1 to 2 by volume ratio (oxygen / silicon alkoxide) to silicon alkoxide. When this ratio is less than 0.1, the effect of sufficiently promoting the oxidation / crosslinking reaction is small, and the silicon oxide fine particles do not grow sufficiently, and when it exceeds 2, the particles are deposited as particles. Tend.

前記シリコン含有反応ガス中の各成分の好ましい割合は、シリコン系アルコキシドが１気圧中に０．１〜５体積％、さらに好ましくは１〜５体積％で、酸素が０〜１０体積％程度含有されることが好ましい。   A preferable ratio of each component in the silicon-containing reaction gas is that the silicon-based alkoxide is 0.1 to 5% by volume, more preferably 1 to 5% by volume in 1 atm, and oxygen is contained in an amount of about 0 to 10% by volume. It is preferable.

そして本方法においては、放電電極に高周波電力を印加することにより、大気圧近傍の圧力でグロー放電させてプラズマを発生させる。
この場合、グロー放電によりプラズマ化されたシリコン含有反応ガス分子の電離後の再結合までの寿命が短く、また電子の平均自由工程も短いので、対向する狭隙電極間にグロー放電を安定に発生させるためには、狭隙間にて電子・イオンの荷電粒子を捕捉する必要がある。
従って、回転電極に高周波電力を印加する際には、１００ＫＨｚ以上の周波数が利用可能であるが、特に１０ＭＨｚ以上の高周波であることが好ましい。１０ＭＨｚ以上の高周波、例えば最も入手の容易な商用周波数である１３．５６ＭＨｚや電源として入手可能な７０ＭＨｚや１００ＭＨｚ、１５０ＭＨｚを用いることによりプラズマ密度が向上し、安定なプラズマを発生させることが可能になる。 In this method, plasma is generated by glow discharge at a pressure near atmospheric pressure by applying high-frequency power to the discharge electrode.
In this case, the lifetime of the silicon-containing reactive gas molecules that have been turned into plasma by glow discharge has a short lifetime until recombination after ionization, and the mean free path of electrons is short, so that glow discharge is stably generated between opposing narrow gap electrodes. In order to achieve this, it is necessary to capture charged particles of electrons and ions in a narrow gap.
Therefore, when high frequency power is applied to the rotating electrode, a frequency of 100 KHz or higher can be used, but a high frequency of 10 MHz or higher is particularly preferable. By using a high frequency of 10 MHz or higher, for example, 13.56 MHz, which is the most readily available commercial frequency, and 70 MHz, 100 MHz, and 150 MHz available as a power source, the plasma density is improved and stable plasma can be generated. .

本発明によれば、半導体装置、特に、自動車に搭載されるような制御ユニット等の半導体装置において用いられる銅系複合基材において、その構成要素である、銅系複合基材と樹脂成分との密着性をより高めることができる電子部品用銅系複合基材、それを用いた電子部品及び前記電子部品用銅系複合基材の製造方法を提供することができる。   According to the present invention, in a copper-based composite base material used in a semiconductor device, in particular, a semiconductor device such as a control unit mounted on an automobile, the constituent elements of the copper-based composite base material and the resin component The copper-type composite base material for electronic components which can improve adhesiveness more, the electronic component using the same, and the manufacturing method of the said copper-type composite base material for electronic components can be provided.

図１は、本発明の電子部品用銅系複合基材の製造方法として好適に用いられる、シリコン酸化物薄膜を形成するためのＣＶＤ成膜装置の構成例を示す概略説明図であり、図中１は成膜チャンバー、２ａは基材導入用ロードロック室、２ｂは基材搬出用ロードロック室、３ａ〜３ｄはゲートバルブ、４ａ〜４ｄはガス導入口、５ａ，５ｂはリーク口、５ｃは排気口、６は基材ホルダー、７は銅系複合基材からなる基材、８はベアリング、９は回転電極、１０は架台、１１ａ〜１１ｃは回転電極支持用絶縁体、１２は合成石英ガラス、１３は近赤外線ランプ、１４は覗き窓、１５は放射温度計、１６，１９は高周波電源、１７，２０は整合器、１８は基材ホルダーに内蔵されたヒータ、２１はグロー放電領域（プラズマ発生領域）をそれぞれ示す。   FIG. 1 is a schematic explanatory view showing a configuration example of a CVD film forming apparatus for forming a silicon oxide thin film, which is preferably used as a method for producing a copper-based composite base material for electronic parts according to the present invention. 1 is a film forming chamber, 2a is a load lock chamber for introducing a substrate, 2b is a load lock chamber for carrying out a substrate, 3a to 3d are gate valves, 4a to 4d are gas inlets, 5a and 5b are leak ports, and 5c is Exhaust port, 6 is a base material holder, 7 is a base material made of a copper-based composite base material, 8 is a bearing, 9 is a rotating electrode, 10 is a mount, 11a to 11c are insulators for supporting a rotating electrode, and 12 is a synthetic quartz glass , 13 is a near infrared lamp, 14 is a viewing window, 15 is a radiation thermometer, 16 and 19 are high-frequency power supplies, 17 and 20 are matching units, 18 is a heater built in the substrate holder, and 21 is a glow discharge region (plasma). Each occurrence area)

図１に示した装置構成において、成膜チャンバー１には、基材導入用ロードロック室２ａおよび基材搬出用ロードロック室２ｂが、それぞれゲートバルブ３ｂ，３ｃを介して接続されている。そして、ロードロック室２ａ，２ｂには、それぞれガス導入口４ａ，４ｂからＨｅ等の不活性ガスが常時導入されており（Ｖ１，Ｖ２は流量調整バルブ）、ロードロック室２ａ，２ｂのそれぞれに設けられたリーク口５ａ，５ｂによって圧力調整がされ（Ｖ３，Ｖ４は流量調整バルブ）、ロードロック室２ａ，２ｂは常圧（０．１ＭＰａ程度）に保持されている。   In the apparatus configuration shown in FIG. 1, a substrate introduction load lock chamber 2a and a substrate carry-out load lock chamber 2b are connected to the film forming chamber 1 through gate valves 3b and 3c, respectively. An inert gas such as He is constantly introduced into the load lock chambers 2a and 2b from the gas inlets 4a and 4b (V1 and V2 are flow rate adjusting valves), and the load lock chambers 2a and 2b are respectively supplied to the load lock chambers 2a and 2b. The pressure is adjusted by the provided leak ports 5a and 5b (V3 and V4 are flow rate adjusting valves), and the load lock chambers 2a and 2b are held at normal pressure (about 0.1 MPa).

前記成膜チャンバー１内には、ガス導入口４ｃからＨｅ等の不活性ガスと必要に応じて酸素（Ｏ２）の混合ガスがマスフロー（図示せず）を介して流量調整されつつ導入されている。また、ガス導入口４ｄからは、マスフロー（図示せず）を介して流量調整されたＨｅ等の不活性ガスによるバプリングによって希釈されたシリコン系アルコキシド等が導入される。尚、チャンバー１内の圧力調整は、排気口５ｃからの流量を調整することによって行われる。 A mixed gas of an inert gas such as He and oxygen (O 2 ) as needed is introduced into the film forming chamber 1 through a mass flow (not shown) through a gas inlet 4c. Yes. Further, silicon-based alkoxide diluted by bubbling with an inert gas such as He whose flow rate is adjusted is introduced from the gas inlet 4d through a mass flow (not shown). The pressure in the chamber 1 is adjusted by adjusting the flow rate from the exhaust port 5c.

基材ホルダー６の上には銅系複合基材である基材７が載置されており、この基材ホルダー６は、まずゲートバルブ３ａを開状態としてロードロック室２ａに移送・格納される。その後、ゲートバルブ３ａを閉の状態とすると共に、ゲートバルブ３ｂを開の状態として、基材ホルダー７は矢印Ａの方向にスキャン移動されて、チャンバー１内に格納され、その後ゲートバルブ３ｂは閉の状態になる。   A base material 7 that is a copper-based composite base material is placed on the base material holder 6. The base material holder 6 is first transferred and stored in the load lock chamber 2 a with the gate valve 3 a opened. . Thereafter, the gate valve 3a is closed, the gate valve 3b is opened, the base material holder 7 is scanned in the direction of arrow A and stored in the chamber 1, and then the gate valve 3b is closed. It becomes the state of.

基材ホルダー６はチャンバー１内に格納された状態で、基材ホルダー６上に載置された基材７の表面にシリコン酸化物薄膜が形成される。基材７の表面にシリコン酸化物薄膜が形成された後は、ゲートバルブ３ｃが開状態とされ、基材ホルダー６は、ロードロック室２ｂに格納される。引き続き、ゲートバルブ３ｃを閉状態とすると共に、ゲートバルブ３ｄを開の状態とし、基材ホルダー７およびその上に載置されている基材７は、ロードロック室２ｂ外に搬出される。これら一連の動作は、連続的に行われ、基材ホルダー６の停止および進行を自由に制御することができる。   In the state in which the substrate holder 6 is stored in the chamber 1, a silicon oxide thin film is formed on the surface of the substrate 7 placed on the substrate holder 6. After the silicon oxide thin film is formed on the surface of the base material 7, the gate valve 3c is opened, and the base material holder 6 is stored in the load lock chamber 2b. Subsequently, the gate valve 3c is closed and the gate valve 3d is opened, and the substrate holder 7 and the substrate 7 placed thereon are carried out of the load lock chamber 2b. These series of operations are continuously performed, and the stop and progress of the base material holder 6 can be freely controlled.

常温では液体原料であるシリコン系アルコキシドの成膜チャンバー１内壁等での液体吸収を防止する為に、成膜チャンバー１、ロードロック室２ａ，２ｂ等の外壁にはヒータ（図示せず）を取り付け、各壁面温度が１００℃程度の高温になるようにすることが好ましい。また、これと同じ理由で、成膜チャンバー１内の回転電極９を支える架台１０および絶縁体１１ａ〜１１ｃ等は内蔵ヒータによって１００℃程度に温度調整することが好ましい。更に、回転電極９については、合成石英ガラス１２を介して近赤外線ランプ１３から放射される赤外線によって加熱され、１５０℃程度に昇温されることが好ましい。尚、回転電極９の温度モニターは、例えばＢａＦ２からなる覗き窓１４を介して放射温度計１５によって行われる。 At room temperature, a heater (not shown) is attached to the outer walls of the film forming chamber 1 and the load lock chambers 2a and 2b in order to prevent liquid absorption of the silicon alkoxide, which is a liquid raw material, on the inner wall of the film forming chamber 1 It is preferable that each wall surface temperature is as high as about 100 ° C. For the same reason, it is preferable to adjust the temperature of the gantry 10 and the insulators 11a to 11c that support the rotating electrode 9 in the film forming chamber 1 to about 100 ° C. with a built-in heater. Further, the rotating electrode 9 is preferably heated by infrared rays emitted from the near-infrared lamp 13 through the synthetic quartz glass 12 and heated to about 150 ° C. The temperature monitor rotating electrode 9 is performed by the radiation thermometer 15 via the observation window 14 made of, for example, BaF 2.

前記した装置は、回転電極９と基材７間の狭隙間にグロー放電２１によるプラズマを形成することによって、基材７上にシリコン酸化物薄膜を形成するものであるが、この成膜の原理について説明する。回転電極９は、例えばアルミニウム製で構成されており、そのサイズは例えば幅：１２０ｍｍ、直径：１００ｍｍ程度の円筒状であり、そのエッジ部は電界集中を防止するために、Ｒ５（ｍｍ）の曲率半径で丸く形成されている。また、回転電極９の表面は、アーキングを防止するために、誘電体コーティングがなされている。このときの誘電体コーティングとしては、例えばホワイトアルミナが溶射コート（厚み：１５０μｍ程度）されることによって構成される。   The above-described apparatus forms a silicon oxide thin film on the base material 7 by forming plasma by the glow discharge 21 in a narrow gap between the rotating electrode 9 and the base material 7. Will be described. The rotating electrode 9 is made of, for example, aluminum, and its size is, for example, a cylindrical shape having a width of about 120 mm and a diameter of about 100 mm, and its edge portion has a curvature of R5 (mm) to prevent electric field concentration. It is rounded with a radius. In addition, the surface of the rotating electrode 9 is coated with a dielectric to prevent arcing. As the dielectric coating at this time, for example, white alumina is formed by thermal spray coating (thickness: about 150 μm).

回転電極９において、基材７との狭隙を形成する面は研磨仕様となっており、必要に応じて凹凸形状が形成されている。また、回転電極９はベアリング８と架台１０とによって支持されている。回転電極９の一方の軸端はマグネットカップリングとなっており、成膜チャンバー１の外側に配置されているモータ端のマグネット（図示せず）とカップリングし、回転電極９を０〜３０００ｒｐｍの範囲で回転させることができる。   The surface of the rotating electrode 9 that forms a narrow gap with the base material 7 has a polishing specification, and an uneven shape is formed as necessary. The rotating electrode 9 is supported by the bearing 8 and the gantry 10. One shaft end of the rotating electrode 9 is a magnet coupling, which is coupled to a motor end magnet (not shown) arranged outside the film forming chamber 1 so that the rotating electrode 9 is rotated at 0 to 3000 rpm. Can be rotated in range.

架台１０は例えばステンレス鋼製で構成されており、この架台１０に整合器１７を介して、高周波電源１６からの高周波電力が印加できるようにされている。基材ホルダー６のスキャン先端部が回転電極９の直下に到着したときに、前記高周波電力が印加され、まず回転電極９と基材ホルダー６（即ち、基材ホルダー６は対向電極に相当する）の狭隙間でグロー放電が開始される。次いで、基材ホルダー６が順次スキャンされ、基材ホルダー６上に載置された基材７が回転電極９の直下に到着した後に、狭隙は回転電極９と基材７との間となる。   The gantry 10 is made of, for example, stainless steel, and high frequency power from a high frequency power source 16 can be applied to the gantry 10 via a matching unit 17. When the scanning tip of the substrate holder 6 arrives directly under the rotating electrode 9, the high-frequency power is applied. First, the rotating electrode 9 and the substrate holder 6 (that is, the substrate holder 6 corresponds to the counter electrode). Glow discharge starts in the narrow gap. Next, after the base material holder 6 is sequentially scanned and the base material 7 placed on the base material holder 6 arrives immediately below the rotary electrode 9, the narrow gap is between the rotary electrode 9 and the base material 7. .

基材ホルダー６の内部にはヒータ１８が埋設されており、このヒータ１８によって基材ホルダー６の温度を室温から３００℃程度にまで加熱できるように構成されている。また、基材ホルダー６の表面にはホワイトアルミナが厚み：１００μｍ程度で溶射コ―ティングされており、基本的には電気的にアース（接地）された状態でもよいが、図１に示すように整合器２０を介して高周波電源１９からの高周波電力を印加するように構成されていてもよい。このように基材ホルダー６にも高周波電力を印加することによって、プラズマ密度の増加やプラズマの封じ込め効果等が発揮されることになる。高周波電源１９からの電力を基材ホルダー６に印加する時期については、回転電極９への高周波電源１６からの電力を印加後、直ちに高周波電力を印加するようにすればよい。   A heater 18 is embedded in the base material holder 6, and the heater 18 is configured so that the temperature of the base material holder 6 can be heated from room temperature to about 300 ° C. The surface of the substrate holder 6 is thermally sprayed with white alumina having a thickness of about 100 μm, and basically may be electrically grounded, but as shown in FIG. The high frequency power from the high frequency power supply 19 may be applied via the matching unit 20. In this way, by applying the high frequency power to the substrate holder 6, an increase in plasma density, a plasma containment effect, and the like are exhibited. About the time to apply the power from the high frequency power source 19 to the substrate holder 6, the high frequency power may be applied immediately after the power from the high frequency power source 16 is applied to the rotating electrode 9.

尚、整合器１７は、高周波電源１６側と整合器１７を含めた負荷側をマッチングさせるため周波数の同調とインピーダンスの調整を行うこと、整合器１７を含めた負荷回路全体での消費電力を最大にすること、および高周波電源１６や高周波発振回路を保護すること等の役目を担うものである（整合器２０と高周波電源１９の関係についても同じ）。   The matching unit 17 performs frequency tuning and impedance adjustment to match the high frequency power source 16 side and the load side including the matching unit 17, and maximizes power consumption in the entire load circuit including the matching unit 17. And protecting the high-frequency power supply 16 and the high-frequency oscillation circuit (the relationship between the matching unit 20 and the high-frequency power supply 19 is the same).

図２は、本発明を実施するためのＣＶＤ成膜装置の他の例を示す概略説明図であり、その基本的な構成は前記図１に示した装置構成に類似し、対応する部分には同一の参照符号を付すことによって重複説明を回避する。また図２では、説明の便宜上図面では示していないが、この装置においても前記図１に示した装置と同様に、基材導入用ロードロック室２ａ、基材搬出用ロードロック室２ｂおよびそれに付随する部材が配置されるものである。   FIG. 2 is a schematic explanatory view showing another example of a CVD film forming apparatus for carrying out the present invention. The basic structure is similar to the apparatus structure shown in FIG. Duplicate description is avoided by assigning the same reference numerals. In FIG. 2, although not shown in the drawing for convenience of explanation, in this apparatus as well as the apparatus shown in FIG. 1, the substrate introduction load lock chamber 2a, the substrate carry-out load lock chamber 2b, and the accompanying lock chamber 2b. The member to be arranged is arranged.

そして、図２に示した装置構成においては、前記円筒状回転電極９の代わりに無端状ベルト電極２２が設けられており、この無端状ベルト電極２２は、例えば薄肉鋼製の導電性部材からなり、２つのローラ２３，２４に掛け回されて走行するように構成されている。   In the apparatus configuration shown in FIG. 2, an endless belt electrode 22 is provided instead of the cylindrical rotating electrode 9, and the endless belt electrode 22 is made of a conductive member made of, for example, thin steel. It is configured to run around two rollers 23 and 24.

ローラ２３，２４は、円筒状外周面を有しており、これらはプラズマ発生領域Ｐにおいて無端状ベルト電極２２表面と水平に延びる基材７表面とが平行をなし、両者の狭隙間距離が一定となるように配置されている。無端状ベルト電極２２は、その回転方向がプラズマ発生領域Ｐにおいて基材７の移動方向と同方向に走行するようになっている。   Each of the rollers 23 and 24 has a cylindrical outer peripheral surface, and in the plasma generation region P, the surface of the endless belt electrode 22 and the surface of the substrate 7 extending horizontally are parallel to each other, and the narrow gap distance between them is constant. It is arranged to become. The endless belt electrode 22 travels in the same direction as the movement direction of the substrate 7 in the plasma generation region P.

前記２つのローラ２３，２４のうち、図２における右側に位置するものが金属性の駆動兼給電用ローラ２４である。このローラ２４をベルト駆動用モータ（図示せず）によって回転させることによって、ローラ２４が回転するように構成されている。また、成膜チャンバー１内において、基材ホルダー６上に載置された基材７は、基材搬送機構２５によって水平方向（矢印Ｂ方向）に移動されるようになされている。   Of the two rollers 23 and 24, the one located on the right side in FIG. The roller 24 is configured to rotate by rotating the roller 24 with a belt driving motor (not shown). In the film forming chamber 1, the base material 7 placed on the base material holder 6 is moved in the horizontal direction (arrow B direction) by the base material transport mechanism 25.

図２に示したプラズマＣＶＤ成膜装置では、ガス導入口４ｅより成膜チャンバー１内にシリコン含有反応ガスを導入すると共に、排気用ダクト５ｅを介して排気し、成膜チャンバー１内を所定の雰囲気圧力に維持する。そして、ローラ２３，２４により無端状ベルト電極２２を走行させ、該ベルト電極２２と基材７との狭隙間にグロー放電により比較的広いライン状のプラズマを発生させ、基材７を移動させながらガスの化学反応により基材７上にシリコン酸化物薄膜を形成するものである。   In the plasma CVD film forming apparatus shown in FIG. 2, the silicon-containing reaction gas is introduced into the film forming chamber 1 from the gas inlet 4e and exhausted through the exhaust duct 5e, and the film forming chamber 1 is evacuated to a predetermined state. Maintain atmospheric pressure. Then, the endless belt electrode 22 is caused to travel by the rollers 23 and 24, and a relatively wide line-shaped plasma is generated by glow discharge in a narrow gap between the belt electrode 22 and the base material 7, and the base material 7 is moved. A silicon oxide thin film is formed on the base material 7 by a chemical reaction of gas.

図３は、本発明を実施するための回転電極を用いたＣＶＤ成膜装置の他の例を示す概略説明図である。この例はガスの排気・置換工程を省略することにより生産性を高めるとともに、高価な真空容器の使用を避けるために大気からの直接的な基板の挿入と搬出が可能となっている。なお、基本的な回転電極部分の構成は図１と同様であり、同様の部分については説明を省略する。
この装置では、基材７はベルトコンベア２６によって一方向に搬送される。基材７は、基板ハンドリングロボット（図示せず）により、一定間隔でベルトコンベアの一方の端に載せられる。その後、基材７はベルトコンベアの移動に伴い、反応容器内に誘導される。
本装置では、入り口／出口を基材７の搬送に最低限必要な大きさに開口部に限るとともに、エアーカーテン２７が備え付けられており、ガス流れを利用して外気の遮断を行なっている。反応空間は、不活性ガスに満たされており、別途導入される原料ガスを回転電極９の流れによりプラズマ空間に導き、銅系複合基材上にシリコン酸化物薄膜を形成する。 FIG. 3 is a schematic explanatory view showing another example of a CVD film forming apparatus using a rotating electrode for carrying out the present invention. In this example, productivity is improved by omitting the gas evacuation / replacement step, and the substrate can be directly inserted and removed from the atmosphere in order to avoid the use of an expensive vacuum vessel. The basic structure of the rotating electrode portion is the same as that in FIG. 1, and the description of the same portion is omitted.
In this apparatus, the base material 7 is conveyed in one direction by the belt conveyor 26. The substrate 7 is placed on one end of the belt conveyor at regular intervals by a substrate handling robot (not shown). Thereafter, the base material 7 is guided into the reaction container as the belt conveyor moves.
In this apparatus, the inlet / outlet is limited to the opening necessary for the conveyance of the base material 7 and the air curtain 27 is provided to block outside air using a gas flow. The reaction space is filled with an inert gas, and a separately introduced raw material gas is guided to the plasma space by the flow of the rotating electrode 9 to form a silicon oxide thin film on the copper-based composite substrate.

図４は本発明を実施するための回転電極を用いたＣＶＤ成膜装置の更に別の例を示す概略説明図である。
この装置では、銅系複合基材からなる基材７をコイル状として、送出しロール２９から基材７を送出し、巻き取りロール３０で基材７を巻き取る。反応容器とは入り口／出口に設置されたガス遮断ロール３１により外気と分離される。このような構成にすることで基材７の連続処理が可能となり、生産性を著しく向上させることが可能である。 FIG. 4 is a schematic explanatory view showing still another example of a CVD film forming apparatus using a rotating electrode for carrying out the present invention.
In this apparatus, the base material 7 made of a copper-based composite base material is coiled, the base material 7 is sent out from the feed roll 29, and the base material 7 is wound up by the take-up roll 30. The reaction vessel is separated from the outside air by a gas blocking roll 31 installed at the entrance / exit. With such a configuration, the base material 7 can be continuously processed, and the productivity can be remarkably improved.

次に、実施例によって本発明の作用効果をより具体的に示すが、下記実施例は本発明を限定する性質のものではなく、前・後記の趣旨を逸脱しない範囲で変更実施することはいずれも本発明の技術範囲に含まれるものである。   Next, the working effects of the present invention will be described more specifically by way of examples. However, the following examples are not of a nature that limits the present invention, and any modifications may be made without departing from the spirit of the preceding and following descriptions. Is also included in the technical scope of the present invention.

（実施例１〜１０）
前記図１に示した回転電極型ＣＶＤ成膜装置を用いて、シリコン酸化物薄膜の形成を行った。
図中、基材ホルダー６としては、幅：１７０ｍｍ、長さ（スキャン方向長さ）：１７０ｍｍのものを使用し、この基材ホルダー６上に銅系複合基材からなる基材７を載置してチャンバー１内に収納した。
銅系複合基材からなる基材７としては、幅：１００ｍｍ、長さ（スキャン方向長さ）：１５０ｍｍ、厚さ：０．４ｍｍのＣｕ-０．１質量％Ｆｅ-０．０３質量％Ｐ（Ｃ１９２１０）からなる銅合金基材に錫の電気光沢めっきにより膜厚０．６〜５．１μｍの被覆層が形成された銅系複合基材を用いた。 (Examples 1 to 10)
A silicon oxide thin film was formed using the rotating electrode type CVD film forming apparatus shown in FIG.
In the figure, as the substrate holder 6, a substrate having a width of 170 mm and a length (scanning direction length) of 170 mm is used, and a substrate 7 made of a copper-based composite substrate is placed on the substrate holder 6. And stored in the chamber 1.
As the base material 7 made of a copper-based composite base material, the width: 100 mm, the length (scan direction length): 150 mm, and the thickness: 0.4 mm, Cu-0.1 mass% Fe-0.03 mass% P A copper-based composite base material in which a coating layer having a film thickness of 0.6 to 5.1 μm was formed on a copper alloy base material made of (C19210) by electro-gloss plating of tin was used.

そして、基材ホルダー６の先端が回転電極９の直下に到達した後、回転電極９に高周波電源１６から高周波電力（周波数：１３．５６ＭＨｚ、５００Ｗ）を印加した。なお、基材ホルダー６はアースに接続した。
このとき基材ホルダー６の設定温度を１００〜２５０℃、回転電極９の温度を１５０℃、成膜チャンバー１およびその部材は１００℃に設定した。
また回転電極９の回転数は５００〜１５００ｒｐｍ（周速度：１５０００〜４５０００ｃｍ／ｍｉｎ）とし、回転電極９と基材７との狭隙間は１ｍｍに設定した。このとき基材７のスキャン速度は３．３〜１７ｍｍ／ｓｅｃとしたので、基材７のスキャン方向における端間での放電時間は約８〜５１ｓｅｃとなった。 And after the front-end | tip of the base-material holder 6 reached right under the rotating electrode 9, the high frequency electric power (frequency: 13.56 MHz, 500W) was applied to the rotating electrode 9 from the high frequency power supply 16. FIG. The substrate holder 6 was connected to ground.
At this time, the set temperature of the substrate holder 6 was set to 100 to 250 ° C., the temperature of the rotary electrode 9 was set to 150 ° C., and the film forming chamber 1 and its members were set to 100 ° C.
The rotational speed of the rotary electrode 9 was 500 to 1500 rpm (peripheral speed: 15000 to 45000 cm / min), and the narrow gap between the rotary electrode 9 and the substrate 7 was set to 1 mm. Since the scanning speed of the base material 7 was 3.3 to 17 mm / sec at this time, the discharge time between the ends in the scanning direction of the base material 7 was about 8 to 51 seconds.

成膜チャンバー１の圧力は、排気口５ｃに設置されたオートプレシャーコントロール（図示せず）によって行い、この製造例では全圧１０１ＫＰａ（０．１ＭＰａ）に調整した。成膜チャンバー１に導入した反応ガスは、ヘリウムおよびテトラエトキシシラン（ＴＥＯＳ）の混合ガスとし、それぞれ流量調整によって分圧を調整した。
このとき、ＴＥＯＳの分圧は０．０１３〜２．６６ＫＰａとし（分圧比換算で０．０１３／１０１〜２．６６／１０１：０．０１〜２．６（％））まで変化させてシリコン酸化物薄膜を形成させた。 The pressure in the film forming chamber 1 was controlled by an auto pressure control (not shown) installed in the exhaust port 5c, and was adjusted to a total pressure of 101 KPa (0.1 MPa) in this production example. The reaction gas introduced into the film forming chamber 1 was a mixed gas of helium and tetraethoxysilane (TEOS), and the partial pressure was adjusted by adjusting the flow rate.
At this time, the partial pressure of TEOS is set to 0.013 to 2.66 KPa (0.013 / 101 to 2.66 / 101: 0.01 to 2.6 (%) in terms of partial pressure ratio) to change the silicon oxide. A physical thin film was formed.

得られたシリコン酸化物薄膜の膜厚を予め銅系複合基材上に設置したマスク領域との差をデクタック触針式段差計により測定した結果、表１に示したような１〜１０００ｎｍの厚みのシリコン酸化物薄膜が前記銅系複合基材からなる基材上に形成された。   As a result of measuring the difference between the film thickness of the obtained silicon oxide thin film and the mask region previously set on the copper-based composite base material with a decack stylus profilometer, the thickness of 1-1000 nm as shown in Table 1 The silicon oxide thin film was formed on a substrate made of the copper-based composite substrate.

そして、前記シリコン酸化物薄膜の形成条件と同条件でＳｉ基板上に堆積し、透過型フーリエ変換赤外分光法（Ｆｏｕｒｉｅｒ Ｉｎｆｒａｒｅｄ；ＦＴ-ＩＲ法）によって有機成分の評価を行った。代表例として、実施例１について測定したＩＲチャートを図５に示す。図５（ａ）は８００〜４０００ｃｍ−１におけるＩＲチャートであり、図５（ｂ）は１５００〜４５００ｃｍ−1の部分を拡大したＩＲチャートである。
なお、図５において、周波数：３０００〜３４００ｃｍ-１付近のピーク強度は、薄膜中の-ＯＨ基を、周波数：２８００〜２９００ｃｍ-１付近のピーク強度はアルキル基（メチル基、エチル基）をそれぞれ示す。前記測定は透過型フーリエ変換赤外分光法により行ない、吸光度モードで解析した結果、いずれもＯＨ基及びメチル基、エチル基の存在が確認された。 And it deposited on Si substrate on the same conditions as the formation conditions of the said silicon oxide thin film, and evaluated the organic component by the transmission type Fourier-transform infrared spectroscopy (Fourier Infrared; FT-IR method). As a representative example, an IR chart measured for Example 1 is shown in FIG. FIG. 5A is an IR chart at 800 to 4000 cm −1 , and FIG. 5B is an IR chart in which a portion of 1500 to 4500 cm −1 is enlarged.
In FIG. 5, the peak intensity near the frequency: 3000 to 3400 cm −1 is the —OH group in the thin film, and the peak intensity near the frequency: 2800 to 2900 cm −1 is the alkyl group (methyl group, ethyl group). Show. The measurement was performed by transmission Fourier transform infrared spectroscopy, and the results were analyzed in the absorbance mode. As a result, the presence of OH groups, methyl groups, and ethyl groups was confirmed.

そして、前記のようにして得られた、表面にシリコン酸化物薄膜が形成された電子部品用銅系複合基材についての樹脂密着性評価を以下の方法により行なった。
（ダイシェア強度評価）
得られた電子部品用銅系複合基材の表面に厚み１ｍｍで５×５ｍｍの大きさのシリコンチップ（（株）高純度化学研究所製）を熱硬化性ポリオレフィン系樹脂（住友３Ｍ社（株）製の品番１５９２）で接着し、１５０℃×２時間の硬化条件で硬化させた。
そして、電子部品用銅系複合基材の表面に接着されたシリコンチップを米国ＭＩＬ ＳＴＤ-８８３に準拠したダイシェア強度評価装置を用いてダイシェア強度を評価した。
また、耐湿性を評価するために、１０５℃・１００％ＲＨの条件で２４時間プレッシャークッカー装置に供した後のダイシェア強度も測定した。 And the resin adhesion evaluation about the copper type composite base material for electronic components by which the silicon oxide thin film was formed on the surface obtained as mentioned above was performed with the following method.
(Die share strength evaluation)
A silicon chip (manufactured by Kojundo Chemical Laboratory Co., Ltd.) having a thickness of 1 mm and a size of 5 × 5 mm is thermoset polyolefin resin (Sumitomo 3M Co., Ltd.) on the surface of the obtained copper-based composite substrate for electronic parts. ) And manufactured under the curing conditions of 150 ° C. × 2 hours.
And the die shear strength was evaluated using the die shear strength evaluation apparatus based on US MIL STD-883 about the silicon chip adhere | attached on the surface of the copper-type composite base material for electronic components.
In addition, in order to evaluate moisture resistance, the die shear strength after being subjected to a pressure cooker for 24 hours under the conditions of 105 ° C. and 100% RH was also measured.

結果を表１に示す。   The results are shown in Table 1.

Figure 0003984629
Figure 0003984629

（実施例１１〜２０）
基材７として、幅：１００ｍｍ、長さ（スキャン方向長さ）：１５０ｍｍ、厚さ：０．４ｍｍのＣｕ-０．１質量％Ｆｅ-０．０３質量％Ｐ（Ｃ１９２１０）からなる銅合金基材の表面に電気光沢めっきした後、リフロー処理を施した膜厚０．５〜５μｍの被覆層が形成された銅系複合基材を用いて、表２に記載の薄膜形成条件により薄膜を形成した以外は同様にして試料を作成し、評価した。結果を表２に示す。 (Examples 11 to 20)
As the base material 7, a copper alloy base made of Cu—0.1 mass% Fe—0.03 mass% P (C19210) with a width of 100 mm, a length (length in the scanning direction): 150 mm, and a thickness of 0.4 mm. After electroplating on the surface of the material, a thin film is formed according to the thin film formation conditions shown in Table 2 using a copper-based composite base material on which a reflow-treated coating layer having a thickness of 0.5 to 5 μm is formed. A sample was prepared and evaluated in the same manner as described above. The results are shown in Table 2.

Figure 0003984629
Figure 0003984629

（実施例２１〜３０）
薄膜形成の際に酸素を導入して、表３に記載の薄膜形成条件により薄膜を形成した以外は実施例１と同様にして試料を作成し、評価した。結果を表３に示す。 (Examples 21 to 30)
Samples were prepared and evaluated in the same manner as in Example 1 except that oxygen was introduced during thin film formation and a thin film was formed under the thin film formation conditions shown in Table 3. The results are shown in Table 3.

Figure 0003984629
Figure 0003984629

（比較例１）
比較例として、水酸基及びアルキル基を含まないシリコン酸化物薄膜を実施例１と同様の銅系複合基材上に成膜し、同様の比較を行なった。成膜はマグネトロンスパッタリング法を用い、ＲＦ電力を印加することによりプラズマを発生させ、ＳｉＯ2ターゲットをプラズマ化されたアルゴンイオンでスパッタリングすることでシリコン酸化物薄膜を作製した。膜厚は予め算出された成膜速度をもとにスパッタリング時間を変更することで１０〜２００ｎｍのものを形成した。
実施例と同様の評価を行なった結果、アンカー効果のためか、ダイシェア強度に若干の増加が見られた。しかしながら吸湿後、いずれの試料にもダイシェア強度の大幅な低下が見られるとともに、銅板―接着剤間での剥離が見られ、充分な効果が得られなかった。 (Comparative Example 1)
As a comparative example, a silicon oxide thin film containing no hydroxyl group or alkyl group was formed on the same copper-based composite base material as in Example 1, and the same comparison was performed. Film formation was performed using a magnetron sputtering method, plasma was generated by applying RF power, and a silicon oxide thin film was produced by sputtering a SiO 2 target with plasmad argon ions. A film thickness of 10 to 200 nm was formed by changing the sputtering time based on the film formation speed calculated in advance.
As a result of performing the same evaluation as in the example, a slight increase in die shear strength was observed due to the anchor effect. However, after moisture absorption, all samples showed a significant decrease in die shear strength and peeling between the copper plate and the adhesive, and sufficient effects were not obtained.

本発明方法を実施するためのＣＶＤ成膜装置の一構成例を示す概略説明図である。It is a schematic explanatory drawing which shows one structural example of the CVD film-forming apparatus for enforcing this invention method. 本発明方法を実施するためのＣＶＤ成膜装置の他の構成例を示す概略説明図である。It is a schematic explanatory drawing which shows the other structural example of the CVD film-forming apparatus for implementing this invention method. 本発明方法を実施するためのＣＶＤ成膜装置の他の構成例を示す概略説明図である。It is a schematic explanatory drawing which shows the other structural example of the CVD film-forming apparatus for implementing this invention method. 本発明方法を実施するためのＣＶＤ成膜装置の他の構成例を示す概略説明図である。It is a schematic explanatory drawing which shows the other structural example of the CVD film-forming apparatus for implementing this invention method. 実施例１で得られたシリコン酸化物薄膜のＦＴ―ＩＲによる反射スペクトルを示すチャートである。2 is a chart showing a reflection spectrum by FT-IR of the silicon oxide thin film obtained in Example 1. FIG.

符号の説明Explanation of symbols

１ 成膜チャンバー
２ａ 基材導入用ロードロック室
２ｂ 基材搬出用ロードロック室
３ａ〜３ｄ ゲートバルブ
４ａ〜４ｆ ガス導入口
５ａ，５ｂ リーク口
５ｃ 排気口
５ｅ 排気用ダクト
６ 基材ホルダー
７ 銅系複合基材からなる基材
８ ベアリング
９ 回転電極
１０ 架台
１１ａ〜１１ｃ 絶縁体
１２ 合成石英ガラス
１３ 近赤外線ランプ
１４ 覗き窓
１５ 放射温度計
１６，１９ 高周波電源
１７，２０ 整合器
１８ ヒータ
２１ グロー放電領域
２２ ベルト電極
２３,２４ ローラ
２５ 基材搬送機構
２６ ベルトコンベア
２７ エアーカーテン
２８ 対向電極
２９ 送り出しロール
３０ 巻き取りロール
３１ ガス遮断ロール DESCRIPTION OF SYMBOLS 1 Deposition chamber 2a Load lock chamber for substrate introduction 2b Load lock chamber for substrate removal 3a to 3d Gate valve 4a to 4f Gas introduction port 5a, 5b Leak port 5c Exhaust port 5e Exhaust duct 6 Base material holder 7 Copper system Base material composed of composite base material 8 Bearing 9 Rotating electrode 10 Base 11a to 11c Insulator 12 Synthetic quartz glass 13 Near infrared lamp 14 Viewing window 15 Radiation thermometer 16, 19 High frequency power source 17, 19 Matching unit 18 Heater 21 Glow discharge area 22 Belt electrode 23, 24 Roller 25 Base material conveyance mechanism 26 Belt conveyor 27 Air curtain 28 Counter electrode 29 Feeding roll 30 Winding roll 31 Gas cut-off roll

Claims (3)

銅基材又は銅合金基材の表面に錫又は錫系合金からなる被覆層が形成されてなる銅系複合基材において、前記被覆層表面に、シリコン系アルコキシドを含有する反応ガスのプラズマ分解物を被着させることにより形成されてなり、炭化水素基及び／又は水酸基を含有する厚さ１〜２００ｎｍのシリコン酸化物薄膜が形成されていることを特徴とする電子部品用銅系複合基材。 In a copper-based composite base material in which a coating layer made of tin or a tin-based alloy is formed on the surface of a copper base material or a copper alloy base material, a plasma decomposition product of a reaction gas containing a silicon-based alkoxide on the surface of the coating layer is formed by depositing a result, a hydrocarbon group and / or electronic components for copper-based composite groups, characterized in that divorced oxide thin film having a thickness of 1~200nm you containing a hydroxyl group is formed Wood. 前記炭化水素基がメチル基又はエチル基である請求項１に記載の電子部品用銅系複合基材。   The copper-based composite base material for electronic components according to claim 1, wherein the hydrocarbon group is a methyl group or an ethyl group. 請求項１または請求項２に記載の電子部品用銅系複合基材を用いて得られる電子部品。
An electronic component obtained by using the copper-based composite base material for electronic components according to claim 1 or 2 .
JP2005361881A 2005-12-15 2005-12-15 Copper-based composite substrate for electronic parts and electronic parts Expired - Fee Related JP3984629B2 (en)