JP3928970B2 - Method for producing laminated transparent conductive film - Google Patents
Method for producing laminated transparent conductive film Download PDFInfo
- Publication number
- JP3928970B2 JP3928970B2 JP2004279680A JP2004279680A JP3928970B2 JP 3928970 B2 JP3928970 B2 JP 3928970B2 JP 2004279680 A JP2004279680 A JP 2004279680A JP 2004279680 A JP2004279680 A JP 2004279680A JP 3928970 B2 JP3928970 B2 JP 3928970B2
- Authority
- JP
- Japan
- Prior art keywords
- transparent conductive
- film
- thin film
- ito
- conductive film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
本発明は透明導電膜にかかり、特に、抵抗値の小い積層型透明導電膜に関する。 The present invention relates to a transparent conductive film, and more particularly to a laminated transparent conductive film having a small resistance value.
最近では、主としてノートパソコン向けにカラーLCD表示装置が普及しているが、一般に用いられるカラーLCD表示装置は、TFT方式とSTN方式とに大別することができる。両方式を比べた場合、TFT方式では、各画素電極をトランジスタによって独立に駆動するため、CRTに匹敵する高画質が得られるが、高価であるという問題点がある。他方、STN方式は単純マトリクス駆動であるため、安価ではあるがクロストークにより画質が劣化しやすいという問題がある。 Recently, a color LCD display device has been widely used mainly for notebook personal computers, but generally used color LCD display devices can be broadly classified into a TFT method and an STN method. When both systems are compared, in the TFT system, since each pixel electrode is independently driven by a transistor, a high image quality comparable to that of a CRT can be obtained, but there is a problem that it is expensive. On the other hand, since the STN method is simple matrix driving, there is a problem that the image quality is liable to deteriorate due to crosstalk although it is inexpensive.
現状で、カラー表示装置に用いられている透明導電膜のうち、特に、単純マトリクス駆動型LCDパネルの配線電極には、酸化インジウム(In2O3)にSnを添加したITO膜(indium tin oxide)が広く使用されているが、STN方式の表示装置のクロストークについては、ITO膜配線の低抵抗化によって改善できることが知られている。しかしながらノートパソコン向けの表示装置については、大型化、高精細化の傾向にあり、より微細な加工が求められていることから、むしろ、透明導電膜の抵抗値は増加する傾向にある。 At present, among transparent conductive films used in color display devices, in particular, an ITO film (indium tin oxide) in which Sn is added to indium oxide (In 2 O 3 ) for wiring electrodes of a simple matrix drive type LCD panel. However, it is known that the crosstalk of the STN display device can be improved by reducing the resistance of the ITO film wiring. However, display devices for notebook computers tend to be larger and higher in definition and require finer processing. Rather, the resistance value of the transparent conductive film tends to increase.
特に、高精細化の要求については、現状は640×480画素の規格が主流であるが、近い将来、より表示能力の大きな800×600画素の規格が主流になるものと考えられている。その場合、カラーのRGB表示のために必要な画素数は、モノクロの3倍になることから、透明導電膜の抵抗値の問題は一層深刻になっている。 In particular, regarding the demand for higher definition, the standard of 640 × 480 pixels is currently the mainstream, but in the near future, the standard of 800 × 600 pixels having a larger display capability will be mainstream. In that case, since the number of pixels necessary for color RGB display is three times that of monochrome, the problem of the resistance value of the transparent conductive film becomes more serious.
このようなITO膜は、通常、ITO酸化物ターゲットを用いた直流マグネトロンスパッタ法により、インライン装置またはバッチ装置を用いて生産されているが、例えば640×480画素の10型パネルについては5〜7Ω/□のシート抵抗値が要求されており、更に、800×600画素ではそれを下回る3〜5Ω/□のシート抵抗値すら要求されているのに対し、現状で得られているITO膜の比抵抗から算出してみると、シート抵抗を5Ω/□以下にするためには、ITO膜を最低でも3000Å〜4000Å程度の膜厚に成膜する必要があることになる。 Such an ITO film is normally produced by a direct current magnetron sputtering method using an ITO oxide target using an in-line device or a batch device. For example, a 10-type panel of 640 × 480 pixels is 5 to 7Ω. A sheet resistance value of / □ is required, and even 800 × 600 pixels require even a sheet resistance value of 3 to 5Ω / □, which is lower than that. When calculated from the resistance, in order to reduce the sheet resistance to 5 Ω / □ or less, it is necessary to form the ITO film to a thickness of about 3000 to 4000 mm.
しかしながらITO膜の膜厚を3000Å以上にした場合には、光の干渉効果が生じるため、わずかな膜厚変動があった場合でも色合いが変化してしまい、表示素子としては不適当なものになってしまうという問題点がある。 However, when the film thickness of the ITO film is 3000 mm or more, a light interference effect occurs, so that even if there is a slight film thickness variation, the hue changes, making it unsuitable as a display element. There is a problem that.
ところで、透明導電膜には、ITO膜ばかりでなく、SnO2やZnOなどの半導体の酸化物透明導電薄膜があり、更にはAu、Ag、Cu、Alなどの金属薄膜も透明導電膜に含める場合もあるが、前述したITO膜は酸化物透明導電薄膜のうちで最も低い比抵抗を持つのにもかかわらず、最近のカラーSTNからの要求に対しては、そのシート抵抗の値は大きすぎると言われている。他方、金属薄膜については、100Å程度のごく薄いものであっても10Ω/□以下の低いシート抵抗が得られるが、金属膜表面の光反射が大きく透過率が悪いため、実際には透明導電膜としては用いられていなかった。
本発明は上記従来技術の不都合に鑑みて創作されたもので、その目的は、シート抵抗値が小さく、透過率の高い透明導電膜を提供することにある。 The present invention was created in view of the disadvantages of the prior art described above, and an object thereof is to provide a transparent conductive film having a small sheet resistance value and a high transmittance.
上記課題を解決するために、請求項1記載の発明は、銀と金からなる金属薄膜であって、腐食防止剤として金を6質量%以上35質量%以下の範囲で含有する透明な金属薄膜を基板上に形成し、前記金属薄膜上に上層側酸化物透明導電薄膜を形成した後、前記上層側酸化物透明導電薄膜と前記金属薄膜とを200℃以上の温度で大気中でアニールする積層型透明導電膜の製造方法である。
請求項2記載の発明は、請求項1項記載の積層型透明導電膜の製造方法であって、前記上層側酸化物透明導電薄膜としてITO膜を形成する積層型透明導電膜の製造方法である。
請求項3記載の発明は、請求項2記載の積層型透明導電膜の製造方法であって、前記上層側酸化物透明導電薄膜は、ITOターゲットをスパッタリングして形成する積層型透明導電膜の製造方法である。
請求項4記載の発明は、請求項1乃至請求項3のいずれか1項記載の積層型透明導電膜の製造方法であって、前記基板上に下層側酸化物透明導電膜を形成した後、該下層側酸化物透明導電膜上に前記金属薄膜を形成する積層型透明導電膜の製造方法である。
請求項5記載の発明は、請求項4記載の積層型透明導電膜の製造方法であって、前記下層側酸化物透明導電薄膜としてITO膜を形成する積層型透明導電膜の製造方法である。
請求項6記載の発明は、請求項5記載の積層型透明導電膜の製造方法であって、前記下層側酸化物透明導電薄膜は、ITOターゲットをスパッタリングして形成する積層型透明導電膜の製造方法である。
In order to solve the above-mentioned problems, the invention described in
Invention of
Invention of Claim 3 is a manufacturing method of the lamination type transparent conductive film of
Invention of Claim 4 is a manufacturing method of the lamination | stacking type transparent conductive film of any one of
Invention of Claim 5 is a manufacturing method of the laminated type transparent conductive film of Claim 4, Comprising: It is a manufacturing method of the laminated type transparent conductive film which forms an ITO film | membrane as the said lower layer side oxide transparent conductive thin film.
Invention of
本発明の積層型透明導電膜は上述したような構成を有するが、スパッタ法によってITO膜等の酸化物透明導電薄膜を形成する場合には、負イオンがカソード表面の電界で加速されて透明基板表面に入射し、成膜しようとする酸化物透明導電薄膜がダメージを受け、それにより比抵抗が増大することが知られている。そのような負イオンの入射を低下させるためには、低電圧でターゲットをスパッタすればよいと言われている。 The laminated transparent conductive film of the present invention has the above-described configuration. However, when an oxide transparent conductive thin film such as an ITO film is formed by sputtering, negative ions are accelerated by the electric field on the cathode surface, and the transparent substrate It is known that the oxide transparent conductive thin film which is incident on the surface and is to be deposited is damaged, thereby increasing the specific resistance. In order to reduce the incidence of such negative ions, it is said that the target may be sputtered at a low voltage.
しかしながら、単にスパッタ電圧を低電圧にするだけでは、酸化物ターゲットを安定にスパッタすることができない。 However, the oxide target cannot be stably sputtered simply by reducing the sputtering voltage.
通常では、マグネトロンカソードの磁場強度は200〜300Gであり、その場合のスパッタ電圧の下限はおよそ400V程度となるが、マグネトロン磁場強度を1000G程度まで増加させれば低いスパッタ電圧でも安定なプラズマを維持することができるので、今回は、250Vという低電圧でITO膜を成膜することができた。 Usually, the magnetic field strength of the magnetron cathode is 200 to 300 G, and the lower limit of the sputtering voltage in that case is about 400 V. However, if the magnetron magnetic field strength is increased to about 1000 G, a stable plasma can be maintained even at a low sputtering voltage. This time, the ITO film could be formed at a voltage as low as 250 V this time.
但し、磁場強度を増加させただけでは250Vが下限であったので、1000Gの強磁場でDCマグネトロンカソードにRF電圧を重畳したところ、250V以下の低電圧でもITO膜を成膜することができた。 However, 250 V was the lower limit only by increasing the magnetic field strength, so when an RF voltage was superimposed on the DC magnetron cathode with a strong magnetic field of 1000 G, an ITO film could be formed even at a low voltage of 250 V or less. .
ところで、酸化物透明導電薄膜をスパッタリング法によって成膜する場合には、得られる薄膜のシート抵抗の大きさには、酸化物透明導電薄膜の膜厚の他、スパッタリングの際のO2ガス添加量、基板温度、放電電圧などの成膜パラメーターが多数関係することが知られている。特に、ITO膜等の酸化物透明導電膜については、基板加熱を行って高温で成膜するほど低抵抗にできると言われているため、成膜温度も重要なパラメーターである。 By the way, when the oxide transparent conductive thin film is formed by the sputtering method, the sheet resistance of the obtained thin film includes the film thickness of the oxide transparent conductive thin film and the amount of O 2 gas added during sputtering. It is known that many film formation parameters such as substrate temperature and discharge voltage are related. In particular, with regard to an oxide transparent conductive film such as an ITO film, it is said that the resistance can be lowered as the film is heated at a higher temperature and the film forming temperature is also an important parameter.
そこで、今回は予備実験として、室温、200℃、350℃の成膜温度でITO膜を形成し、比抵抗を測定した。スパッタ電圧を横軸、比抵抗を縦軸にとって、図3に、各成膜温度での比抵抗の値を、■、◆、●のプロットを結んだグラフで示す。 Therefore, as a preliminary experiment, an ITO film was formed at room temperature, 200 ° C., and 350 ° C., and the specific resistance was measured. With the horizontal axis of the sputtering voltage and the vertical axis of specific resistance, FIG. 3 shows the value of specific resistance at each film forming temperature as a graph connecting plots of ■, ◆, and ●.
350℃の場合が最も比抵抗が小さくなるが、ITO膜をカラーSTNに用いる場合には、透明基板に形成されているカラーフィルタやオーバーコート材の耐熱性の限界から、ITO膜の成膜温度も180〜230℃程度に制限されてしまう。 When the temperature is 350 ° C., the specific resistance is the smallest. However, when the ITO film is used for the color STN, the film forming temperature of the ITO film is limited by the heat resistance limit of the color filter and overcoat material formed on the transparent substrate. Is also limited to about 180 to 230 ° C.
この場合、図3から分かるように、成膜温度200℃、スパッタ電圧400Vでは、形成されるITO膜の比抵抗はおよそ4×10-4Ωcmである。それに対して、スパッタ電圧を250Vという低電圧にすると、200℃の成膜温度でも、比抵抗をスパッタ電圧が400Vのときの二分の一の2×10-4Ωcmといいう低抵抗にできた。更に、110Vのスパッタ電圧ではITO膜の比抵抗を1.3×10-4Ωcmという低抵抗にできた。このように、低いスパッタ電圧で酸化物透明導電薄膜の形成を行えば、膜中のダメージが低減され、シート抵抗値も小さくすることができる。本発明の積層型透明導電膜の酸化物透明導電薄膜を形成する際にも、低いスパッタ電圧を用いると、積層型透明導電膜全体のシート抵抗を低減できて望ましい。 In this case, as can be seen from FIG. 3, at a film forming temperature of 200 ° C. and a sputtering voltage of 400 V, the specific resistance of the formed ITO film is approximately 4 × 10 −4 Ωcm. On the other hand, when the sputtering voltage was set to a low voltage of 250 V, the specific resistance could be as low as 2 × 10 −4 Ωcm even when the sputtering voltage was 400 V, even at a film forming temperature of 200 ° C. Furthermore, the specific resistance of the ITO film was reduced to 1.3 × 10 −4 Ωcm at a sputtering voltage of 110 V. Thus, if the oxide transparent conductive thin film is formed at a low sputtering voltage, damage in the film can be reduced and the sheet resistance value can be reduced. When forming the oxide transparent conductive thin film of the laminated transparent conductive film of the present invention, it is desirable to use a low sputtering voltage because the sheet resistance of the entire laminated transparent conductive film can be reduced.
低抵抗で透過率の高い透明導電薄膜が得られたので、配線抵抗を低減できる。
パターン性も良好であるので、高密度の表示装置に用いることができる。
透過率ピークが可視領域に位置するようにできるので、効率の良い表示装置を作成することができる。
耐腐食性に優れているので透明導電膜の信頼性が向上し、ひいては本発明の積層型透明導電膜が用いられる製品の信頼性も向上する。
Since a transparent conductive thin film having low resistance and high transmittance is obtained, wiring resistance can be reduced.
Since the pattern property is also good, it can be used for a high-density display device.
Since the transmittance peak can be positioned in the visible region, an efficient display device can be created.
Since it is excellent in corrosion resistance, the reliability of the transparent conductive film is improved, and as a result, the reliability of products using the laminated transparent conductive film of the present invention is also improved.
<積層型透明導電膜の製造方法>
最初に、本発明の積層型透明導電膜の製造方法について説明する。
図1を参照し、符号10はスパッタ装置であり、本発明の積層型透明導電膜を製造できる装置の一例を示したものである。
<Method for producing laminated transparent conductive film>
Initially, the manufacturing method of the lamination type transparent conductive film of the present invention is explained.
Referring to FIG. 1, reference numeral 10 denotes a sputtering apparatus, which shows an example of an apparatus that can manufacture the laminated transparent conductive film of the present invention.
このスパッタ装置10は、酸化物透明導電薄膜を成膜するスパッタ室1と、金属薄膜を成膜するスパッタ室2とを有している。前記スパッタ室1、2の間はバルブ32で仕切られており、各スパッタ室1、2の両側は、バルブ31、33がそれぞれ設けられ、大気が侵入しないように構成されている。
The sputtering apparatus 10 has a
また、前記スパッタ室1、2には、それぞれバルブ41、42を介して真空ポンプ51、52が接続されており、前記各バルブ31〜33を閉じて前記バルブ41、42を開け、各真空ポンプ51、52を起動すると個別に真空排気できるように構成されている。
Further, vacuum pumps 5 1 and 5 2 are connected to the
前記スパッタ室1内の底面にはマグネトロンカソード6が配置されており、このマグネトロンカソード6上には、酸化物透明導電薄膜の材料であるITO焼結体ターゲット(In2O3−10wt%SnO2)が、その裏面に配置された磁石によって、表面の水平磁場強度が約1000 Oeになるように設けられている(図示せず)。また、このスパッタ室1内の天井には、キャリアー13が水平移動可能に設けられており、該キャリアー13に基板を取り付けるとその成膜面が前記ITO焼結体ターゲットに対して平行に向くように構成されている。
A
前記スパッタ室2内にはカソード9が配置されており、このカソード9上には金属ターゲットが設けられている(図示せず)。
前記キャリアー13に透明な基板12を取り付け、前記スパッタ室1を真空排気して高真空状態とした後、スパッタ室1に設けられたノズル8から、マスフローコントローラーで流量制御されたArガスとO2ガスとを0.67Paの圧力まで導入し、前記マグネトロンカソード6に接続された直流電源71(RF電圧が重畳できるように構成してもよい)を起動すると前記ITO焼結体ターゲットのスパッタリングが開始される。
A
A
このスパッタリングの際、前記キャリアー13を動かして前記基板12を前記ITOターゲット上で等速度で通過させると、酸化物透明導電薄膜であるITO膜を所定膜厚で形成することができる。
During the sputtering, when the
前記真空ポンプ52を動作させ、予め前記スパッタ室2内を高真空状態にしておくと、前記バルブ32を介して、前記ITO膜が形成された基板をスパッタ室2内に搬入することができる。搬入後、このバルブ32を閉じ、該スパッタ室2に設けられたノズル11からマスフローコントローラーで流量制御されたArガスを0.27Paの圧力まで導入し、前記カソード9に接続された直流電源72を起動すると前記金属ターゲットのスパッタリングが開始される。
このとき、前記基板12を金属ターゲット上で等速度で通過させると、ITO膜上に所定膜厚の金属薄膜を形成することができる。
Wherein operating the vacuum pump 5 2 and advance the
At this time, if the
次に、ITO膜と金属薄膜とがこの順で成膜された基板を、前記バルブ32を介して再度スパッタ室1に搬入すると、前記金属薄膜上にITO膜を形成することができる。そして大気中に取り出すと、図2(a)に示すように、透明な基板12上に、ITO膜28/金属薄膜26/ITO膜27の3層構造で構成された積層型透明導電膜22を得ることができる。
Next, the substrate on which the ITO film and the metal thin films are deposited in this order, when carried into the sputtering
また、未成膜基板12を前記スパッタ室1に搬入した後、ITO膜を成膜せずにそのままスパッタ室2に搬送し、基板12表面に直接金属薄膜を形成した後、スパッタ室1内に戻してITO膜を成膜すれば、図2(b)に示すように、透明基板12上に金属薄膜36とITO膜37がこの順で成膜された2層構造の積層型透明導電膜32が得られる。
Further, after the
<積層型透明導電膜の透過率>
上記スパッタ装置10の金属ターゲットに金ターゲットを使用し、基板としてコーニング(株)製の製品番号#7059の透明基板(以下、この透明基板を用いる)を用い、その表面にITO膜/金薄膜/ITO膜をこの順で形成し、前述の図2(a)に示したような、3層構造の積層型透明導電膜を作製した。このとき、ITO膜一層当たりについては300Åの一定膜厚とし、金薄膜については、80、100、150Åの膜厚の3種類の積層型透明導電膜を作製した。それらについて、2波長型分光光時計を用いて大気リファレンスで透明基板を含めた透過率スペクトルを測定した。
<Transmissivity of laminated transparent conductive film>
A gold target is used as the metal target of the sputtering apparatus 10 and a transparent substrate of product number # 7059 (hereinafter, this transparent substrate) manufactured by Corning Co., Ltd. is used as the substrate, and an ITO film / gold thin film / An ITO film was formed in this order to produce a laminated transparent conductive film having a three-layer structure as shown in FIG. At this time, three types of laminated transparent conductive films having a constant film thickness of 300 mm per ITO film and 80, 100, and 150 mm thickness for the gold thin film were prepared. About these, the transmittance | permeability spectrum including a transparent substrate was measured by the atmospheric reference using the 2 wavelength type | mold spectroscopic clock.
測定波長を横軸に、透過率を縦軸にとって、前記金薄膜が80、100、150Åの膜厚に形成された各積層型透明導電膜について、●、◆、■の各プロットを結んだグラフで示す。 A graph connecting the plots of ●, ◆, and ■ for each of the laminated transparent conductive films in which the gold thin film is formed to a thickness of 80, 100, and 150 mm, with the measurement wavelength on the horizontal axis and the transmittance on the vertical axis It shows with.
次に、前記スパッタ装置10の、上記金ターゲットに替えて銀ターゲットを使用し、透明基板上にITO膜/銀薄膜/ITO膜の3層構造の積層型透明導電膜を形成した。 Next, a silver target was used in place of the gold target of the sputtering apparatus 10, and a laminated transparent conductive film having a three-layer structure of ITO film / silver thin film / ITO film was formed on a transparent substrate.
一層当たりのITO膜を450Åの一定膜厚とし、銀薄膜を80、130、180Åの膜厚の3種類の積層型透明導電膜を作製した。図6に、各積層型透明導電膜の透過率スペクトルを、●、◆、■の各プロットを結んだグラフで示す。80Åと130Åの銀薄膜の場合は透過率は良好であるが、180Åになると透過率は低下している。これは、銀薄膜表面の反射が大きくなるためである。 Three types of laminated transparent conductive films having a constant film thickness of 450 mm per layer and a silver thin film of 80, 130, and 180 mm were prepared. FIG. 6 shows the transmittance spectrum of each laminated transparent conductive film as a graph connecting the plots of ●, ◆, and ■. In the case of the silver thin films of 80 mm and 130 mm, the transmittance is good, but at 180 mm, the transmittance is lowered. This is because the reflection on the surface of the silver thin film is increased.
3層構造の積層型透明導電膜の銀薄膜の膜厚を130Åの一定膜厚とし、ITO膜の膜厚を変化させて透過率のピークを測定した。但し、銀薄膜の表裏に位置する2層のITO膜の膜厚は同じにした。横軸にITO膜の膜厚x、縦軸に透過率のピークの波長をとって、図4に各積層型透明導電膜の透過率ピーク波長を、●のプロットを結んだグラフで示す。 The film thickness of the silver thin film of the laminated transparent conductive film having a three-layer structure was set to a constant film thickness of 130 mm, and the peak of transmittance was measured by changing the film thickness of the ITO film. However, the film thicknesses of the two ITO films located on the front and back of the silver thin film were the same. Taking the film thickness x of the ITO film on the horizontal axis and the wavelength of the transmittance peak on the vertical axis, FIG. 4 shows the transmittance peak wavelength of each laminated transparent conductive film as a graph connecting the plots of ●.
この図4から分かる通り、銀薄膜単層を透明基板上に130Åの厚みに成膜した場合に比べて、透過率は向上している。銀薄膜表面の大きな反射光がITO膜層での干渉効果で低減されるためであるが、ITO膜の膜厚が増加すると、透過率のピーク波長も長波長側にシフトしてしまっている。特に、130Åの銀薄膜を用いた積層型透明導電膜について、可視域550nmの透過率を最大にするためには、膜厚450ÅのITO膜のが必要となることが分かる。 As can be seen from FIG. 4, the transmittance is improved as compared with the case where the silver thin film single layer is formed on the transparent substrate to a thickness of 130 mm. This is because the large reflected light on the surface of the silver thin film is reduced by the interference effect on the ITO film layer, but when the thickness of the ITO film increases, the peak wavelength of the transmittance also shifts to the longer wavelength side. In particular, for a laminated transparent conductive film using a 130 mm silver thin film, an ITO film having a thickness of 450 mm is required to maximize the transmittance in the visible region of 550 nm.
また、同様に、前記スパッタ装置10の金属ターゲットに銅ターゲットを使用し、透明基板上にITO膜/銅薄膜/ITO膜の3層構造(300/100/300Å)の積層型透明導電膜を作製し、透過率スペクトルを測定した。測定結果を、図7に、●のプロットを結んだグラフで示す。 Similarly, a copper target is used as the metal target of the sputtering apparatus 10 to produce a laminated transparent conductive film having a three-layer structure (300/100/300 mm) of ITO film / copper thin film / ITO film on a transparent substrate. Then, the transmittance spectrum was measured. The measurement results are shown in FIG. 7 as a graph connecting the ● plots.
図5〜図7の、各積層型透明導電膜の透過率スペクトルのグラフを比較すると、銀薄膜を有する積層型透明導電膜が最も透過率が高い。それに対し、金薄膜を用いた積層型透明導電膜と銅薄膜を用いた積層型透明導電膜では短波長側の吸収が大きく、また、それぞれの金属色を反映した色合いになっていた。 Comparing the graphs of transmittance spectra of the respective laminated transparent conductive films in FIGS. 5 to 7, the laminated transparent conductive film having a silver thin film has the highest transmittance. On the other hand, in the laminated transparent conductive film using a gold thin film and the laminated transparent conductive film using a copper thin film, the absorption on the short wavelength side is large, and the color reflects each metal color.
比較のため、図8に、透明基板上に形成した、膜厚1000Åと1500Åの単層のITO膜の透過率スペクトルのグラフを示す。このグラフと図6のグラフとから、膜厚1000ÅのITO膜の透過率スペクトルと、ITO膜/銀薄膜/ITO膜の、膜厚450/80/450Åの場合の積層型透明導電膜の透過率スペクトルとがよく似ていることが分かる。また、膜厚1500ÅのITO膜の透過率スペクトルについては、ITO膜/銀薄膜/ITO膜の、膜厚450/130/450Åの場合の積層型透明導電膜の透過率スペクトルとがよく似ていることが分かる。見た目の色合いにおいても、それぞれよく似ていた。
For comparison, FIG. 8 shows a graph of the transmittance spectrum of single-layer ITO films having a thickness of 1000 mm and 1500 mm formed on a transparent substrate. From this graph and the graph of FIG. 6, the transmittance spectrum of the ITO film having a film thickness of 1000 mm and the transmittance of the laminated transparent conductive film in the case of the film thickness of 450/80/450 mm of ITO film / silver thin film / ITO film. It can be seen that the spectrum is very similar. Further, the transmittance spectrum of the ITO film having a thickness of 1500 mm is very similar to the transmittance spectrum of the laminated transparent conductive film in the case of the
<積層型透明導電膜のシート抵抗>
前記スパッタ装置10と透明基板を用い、基板加熱を行わずに、ITO膜/金薄膜/ITO膜の3層構造と、ITO膜/銀薄膜/ITO膜の3層構造と、ITO膜/銅薄膜/ITO膜の3層構造と、及び銀薄膜/ITO膜の2層構造との積層型透明導電膜を形成した。各積層型透明導電膜について、成膜直後のシート抵抗値と、200℃で1時間の大気アニールを行った後のシート抵抗の値とを測定した。各層の膜厚とシート抵抗の関係を下記表1に示す。
<Sheet resistance of laminated transparent conductive film>
Using the sputtering apparatus 10 and a transparent substrate, without heating the substrate, a three-layer structure of ITO film / gold thin film / ITO film, a three-layer structure of ITO film / silver thin film / ITO film, and an ITO film / copper thin film A laminated transparent conductive film having a three-layer structure of / ITO film and a two-layer structure of silver thin film / ITO film was formed. For each laminated transparent conductive film, the sheet resistance value immediately after film formation and the value of sheet resistance after atmospheric annealing at 200 ° C. for 1 hour were measured. Table 1 below shows the relationship between the film thickness of each layer and the sheet resistance.
大気アニールを行う必要性は、実際のLCDパネルの製造工程において、液晶の封入工程などで熱処理が加えられる場合があるので、耐熱性の確認のためであったが、アニールを行った方がシート抵抗は2割程度低下した。 The necessity of performing atmospheric annealing was to confirm heat resistance because heat treatment may be applied during the liquid crystal encapsulation process in the actual LCD panel manufacturing process. The resistance dropped by about 20%.
また、上記表2には示さないが、300℃の大気アニールを行うとシート抵抗値はさらに低下した。いずれの場合も、懸念された熱処理による劣化は発生しなかった。 Further, although not shown in Table 2 above, the sheet resistance value was further reduced by performing atmospheric annealing at 300 ° C. In either case, the deterioration due to the heat treatment concerned was not generated.
このようなアニールによるシート抵抗の低下は、ITO膜の結晶化による比抵抗の低下だけでは説明がつかず、その低下割合からは、むしろ金属層の比抵抗が低下したことに起因すると推定できる。 Such a decrease in sheet resistance due to annealing cannot be explained only by a decrease in specific resistance due to crystallization of the ITO film, and it can be presumed that the decrease in specific resistance of the metal layer is rather based on the reduction ratio.
表1に記載した積層型透明導電膜のシート抵抗を比較すると、バルク比抵抗の一番低い銀を金属薄膜に用いたものが最も低い抵抗値が得られており、各積層型透明導電膜のシート抵抗値は、用いられた金属膜の種類と膜厚に依存していることが分かる。銀薄膜を用いたものに注目してみると、ITO膜/銀薄膜/ITO膜(450/180/450Å)では、成膜直後(as depo.)で2.59Ω/□のシート抵抗値、200℃1時間の大気アニール後で2.10Ω/□のシート抵抗値であり、この値は、透明導電膜としては超低抵抗と言える。 When the sheet resistance of the laminated transparent conductive film described in Table 1 is compared, the lowest resistance value is obtained when silver having the lowest bulk specific resistance is used for the metal thin film. It can be seen that the sheet resistance value depends on the type and thickness of the metal film used. When attention is paid to those using a silver thin film, in the case of ITO film / silver thin film / ITO film (450/180/450 mm), a sheet resistance value of 2.59 Ω / □ immediately after film formation (as depo.), 200 The sheet resistance value is 2.10 Ω / □ after atmospheric annealing at 1 ° C., and this value can be said to be an extremely low resistance for a transparent conductive film.
なお、予備実験において、透明基板を200℃に加熱して金属薄膜を形成しようと試みたところ、金属が粒状に凝集して分離してしまい、得られた金属薄膜では導電性がなかった。 In a preliminary experiment, when an attempt was made to form a metal thin film by heating the transparent substrate to 200 ° C., the metal agglomerated and separated, and the obtained metal thin film was not conductive.
<積層型透明導電膜の耐食性>
前記図5〜図7の透過率の測定に使用した積層型透明導電膜を、長時間(1〜2週間)大気中で放置したところ、銀薄膜を用いたものと銅薄膜を用いたものとに腐食が発生していることが観察された。これはITO膜の中間に位置する金属層が酸化したためと考えられる。
<Corrosion resistance of laminated transparent conductive film>
When the laminated transparent conductive film used for the measurement of the transmittance in FIGS. 5 to 7 is left in the air for a long time (1 to 2 weeks), a silver thin film and a copper thin film are used. It was observed that corrosion occurred. This is considered because the metal layer located in the middle of the ITO film was oxidized.
このように、銀薄膜を用いた積層型透明導電膜はシート抵抗が小さく、透過率が高く、特性的には優れており、カラーSTNへの応用に対し一番有望である。しかし、耐食性に劣っているため、エッチング方法の検討とともに、この膜腐食の問題を解決することが望ましい。
一方、金薄膜を用いたものは、耐食性の点では優れているが、シート抵抗が高く、透過率も低いため、特性的には不充分である。
Thus, a laminated transparent conductive film using a silver thin film has a low sheet resistance, a high transmittance, and excellent characteristics, and is most promising for application to color STN. However, since it is inferior in corrosion resistance, it is desirable to solve this film corrosion problem together with the examination of the etching method.
On the other hand, those using a gold thin film are excellent in terms of corrosion resistance, but are insufficient in characteristics because of high sheet resistance and low transmittance.
<金添加銀薄膜の積層型透明導電膜の諸特性>
上述のスパッタ装置10の金属ターゲットに、金が添加された銀ターゲットを使用し、透明基板の表面にITO膜/金添加銀薄膜/ITO膜(450/130/450Å)から成る積層型透明導電膜を形成した。このとき、銀薄膜中の金添加割合が6、11、30、35質量%である4種類の積層型透明導電膜を作製した。
<Characteristics of laminated transparent conductive film of gold-added silver thin film>
The above-mentioned sputtering target 10 uses a silver target to which gold is added as a metal target, and a transparent transparent conductive film comprising ITO film / gold-added silver thin film / ITO film (450/130/450 mm) on the surface of the transparent substrate. Formed. At this time, four types of laminated transparent conductive films having gold addition ratios of 6, 11, 30, and 35% by mass in the silver thin film were produced.
銀薄膜中の金添加割合と、各積層型透明導電膜のシート抵抗値、及び透過率(波長550nmでの値)との関係を測定した。耐腐食性を観察するために、各積層型透明導電膜を数日間大気中に放置した。パターン性を観察するために、HCl:HNO3:H2O(1:1:8)のエッチング液を用い(液温40℃)、各積層型透明導電膜をエッチングしてエッチング残渣の有無を検査した。
The relationship between the gold addition ratio in the silver thin film, the sheet resistance value of each laminated transparent conductive film, and the transmittance (value at a wavelength of 550 nm) was measured. In order to observe the corrosion resistance, each laminated transparent conductive film was left in the air for several days. In order to observe the pattern property, an etching solution of HCl: HNO 3 : H 2 O (1: 1: 8) was used (
比較のため、金を添加しなかった銀薄膜を有する積層型透明導電膜についても、同様な測定を行った。
これらの結果を下記表2に示す。
For comparison, the same measurement was performed on a laminated transparent conductive film having a silver thin film to which no gold was added.
These results are shown in Table 2 below.
各積層型透明導電膜ともシート抵抗は小さく、透過率を大きくできたが、金を添加しなかった積層型透明導電膜では腐食が観察された。それに対し、3%以上の金を添加した場合には腐食は観察されず、耐食性は良好であった。特に、金を6%以上添加した積層型透明導電膜については2ヶ月以上放置したが、腐食の発生はみられなかった。 Although the sheet resistance of each of the laminated transparent conductive films was small and the transmittance could be increased, corrosion was observed in the laminated transparent conductive film to which gold was not added. On the other hand, when 3% or more of gold was added, no corrosion was observed and the corrosion resistance was good. In particular, the laminated transparent conductive film added with 6% or more of gold was allowed to stand for 2 months or more, but no corrosion was observed.
パターン性については、各積層型透明導電膜ともに前記エッチング液でエッチングができ、良好であった。但し、35%の金を添加した場合には、エッチング終了後、金と思われるエッチング残渣が観察された。 As for the pattern property, each of the laminated transparent conductive films could be etched with the above etching solution, and was good. However, when 35% of gold was added, an etching residue considered to be gold was observed after the etching was completed.
<金添加銀薄膜を有する積層型透明導電膜のエッチング特性>
エッチング液に40℃のHCl:HNO3:H2O(1:1:8)を用い、他の金添加割合についてもエッチング特性とともに、シート抵抗値と透過率とを測定した。成膜直後、200℃アニール、250℃アニールの場合の測定結果について、下記表3に示す(一部の値は上記表2と重複する)。
<Etching characteristics of laminated transparent conductive film having gold-added silver thin film>
HCl: HNO 3 : H 2 O (1: 1: 8) at 40 ° C. was used as the etching solution, and the sheet resistance value and transmittance were measured along with the etching characteristics for other gold addition ratios. The measurement results in the case of 200 ° C. annealing and 250 ° C. annealing immediately after film formation are shown in the following Table 3 (some values overlap with Table 2 above).
このように、ITO膜/銀薄膜/ITO膜構造の積層型透明導電膜において、銀薄膜中に金を3%以上添加した場合に、高透過率、低抵抗であって耐腐食性を有する積層型透明導電膜が得られた。特に6%以上金を添加すると、一層耐腐食性が向上する。また、200℃以上のアニールを行うことで、充分低抵抗の積層型透明導電膜が得られた。特に、250℃のアニールを行った場合には、4.44Ω/□という、超低抵抗の積層型透明導電膜が得られた。 Thus, in the laminated transparent conductive film of ITO film / silver thin film / ITO film structure, when 3% or more of gold is added to the silver thin film, the laminated film has high transmittance, low resistance and corrosion resistance. A type transparent conductive film was obtained. Particularly when 6% or more of gold is added, the corrosion resistance is further improved. Moreover, a sufficiently low resistance laminated transparent conductive film was obtained by annealing at 200 ° C. or higher. In particular, when annealing at 250 ° C. was performed, an ultra-low resistance laminated transparent conductive film of 4.44 Ω / □ was obtained.
以上の積層型透明導電膜の成膜条件を、下記表に記載しておく。 The film forming conditions of the above laminated transparent conductive film are described in the following table.
<まとめ>
以上説明したように、ITO膜/金属薄膜/ITO膜の積層型透明導電膜では、特に、ITO膜/銀薄膜/ITO膜の構造で、ITO膜単層に匹敵する高透過率と、ITO膜単層に比べて大幅に低いシート抵抗値を有する積層型透明導電膜が得られた。
その積層型透明導電膜中の銀薄膜に金を添加すると腐食が防止できた。また、HCl/HNO3系のエッチング液を用いてパターンニングできることも分かった。
<Summary>
As described above, in the laminated transparent conductive film of ITO film / metal thin film / ITO film, in particular, the structure of ITO film / silver thin film / ITO film has high transmittance comparable to that of a single ITO film, and the ITO film. A laminated transparent conductive film having a sheet resistance value significantly lower than that of a single layer was obtained.
Corrosion could be prevented by adding gold to the silver thin film in the laminated transparent conductive film. It was also found that patterning can be performed using an HCl / HNO 3 -based etching solution.
ITO膜/銀薄膜/ITO膜の構造では、各層の膜厚が450/130/450Å、銀薄膜中の金の添加量が6%である場合に、透過率82.8%(550nm、透明基板込みの測定値)、シート抵抗4.44Ω/□(250℃アニール後)という、高透過率で超低抵抗の積層型透明導電膜が得られた。 In the structure of ITO film / silver thin film / ITO film, when the thickness of each layer is 450/130/450 mm and the amount of gold added in the silver thin film is 6%, the transmittance is 82.8% (550 nm, transparent substrate A laminated transparent conductive film having a high transmittance and an ultra-low resistance of sheet resistance 4.44Ω / □ (after annealing at 250 ° C.) was obtained.
<本発明の他の実施の形態>
上記積層型透明導電膜ではITO膜(インジウム錫酸化物)を酸化物透明導電薄膜として使用したが、インジウム酸化物に添加する物質は、錫に限定されるものではない。
<Other embodiments of the present invention>
In the laminated transparent conductive film, an ITO film (indium tin oxide) is used as the oxide transparent conductive thin film, but the material added to the indium oxide is not limited to tin.
更に、インジウム酸化物(In2O3)に限定されるものではなく、例えば、SnO2、ZnO等の酸化物半導体膜を広く用いることが可能である。この場合、酸化物半導体に添加する物質には、ドナーとなることができる元素を広く含む。さらには薄膜にしたときに透明となる各種の導電薄膜を広く用いることが可能である。 Furthermore, the present invention is not limited to indium oxide (In 2 O 3 ), and for example, oxide semiconductor films such as SnO 2 and ZnO can be widely used. In this case, the substance added to the oxide semiconductor includes a wide range of elements that can serve as donors. Further, various conductive thin films that become transparent when formed into a thin film can be widely used.
また、本発明の積層型透明導電膜に用いられる金属薄膜は、金、銀、銅に限定されるものではなく、薄膜にし、酸化物透明導電薄膜との積層構造としたときに透過率の良い金属薄膜や合金薄膜を広く用いることができる。腐食防止剤も金に限定されるものではなく、各種貴金属やその他化合物等、要するに、金属薄膜や合金薄膜の比抵抗(シート抵抗)や透過率を大きく劣化させることなく腐食を防止できる物質を広く含む。この腐食防止剤の添加については、予め成膜したい金属薄膜のターゲット材料中に添加してもよいし、金属薄膜材料ターゲットとは別に金等の腐食防止剤ターゲットを用意し、両方のターゲットを一緒にスパッタしても良い。この場合には、ターゲットの面積比や投入電力を異ならせることで、添加割合を調節することが可能となる。 Moreover, the metal thin film used for the laminated transparent conductive film of the present invention is not limited to gold, silver, and copper, but has a good transmittance when formed into a thin film and a laminated structure with an oxide transparent conductive thin film. Metal thin films and alloy thin films can be widely used. Corrosion inhibitors are not limited to gold, but a wide range of substances that can prevent corrosion without greatly degrading the specific resistance (sheet resistance) and transmittance of metal thin films and alloy thin films such as various precious metals and other compounds. Including. As for the addition of this corrosion inhibitor, it may be added in advance to the target material of the metal thin film to be deposited, or a corrosion inhibitor target such as gold is prepared separately from the metal thin film material target, and both targets are combined together. Sputtering may be used. In this case, the addition ratio can be adjusted by changing the area ratio of the target and the input power.
また、金属薄膜は一層のものに限定されず、また、酸化物透明導電薄膜も一層や二層のものに限定されるものではなく、2層以上の金属薄膜と一層又は2層以上の酸化物透明導電薄膜が積層されて構成された積層型透明導電膜が広く含まれる。要するに、本発明の積層型透明導電膜の構造には、金属薄膜層の反射を酸化物透明導電薄膜層で低減できるようにすればよい。 Further, the metal thin film is not limited to a single layer, and the oxide transparent conductive thin film is not limited to a single layer or two layers, but two or more layers of metal thin film and one layer or two layers of oxide. A wide range of laminated transparent conductive films constituted by laminating transparent conductive thin films is widely included. In short, the structure of the laminated transparent conductive film of the present invention may be such that the reflection of the metal thin film layer can be reduced by the oxide transparent conductive thin film layer.
22、32……積層型透明導電膜 25、35……基板
26、36……金属薄膜 27及び28、37……酸化物透明導電薄膜
22, 32 ... Laminated transparent conductive film 25, 35 ...
Claims (6)
前記金属薄膜上に上層側酸化物透明導電薄膜を形成した後、
前記上層側酸化物透明導電薄膜と前記金属薄膜とを200℃以上の温度で大気中でアニールする積層型透明導電膜の製造方法。 A metal thin film composed of silver and gold , wherein a transparent metal thin film containing gold in a range of 6 mass % to 35 mass % as a corrosion inhibitor is formed on a substrate;
After forming the upper layer side oxide transparent conductive thin film on the metal thin film,
The manufacturing method of the laminated type transparent conductive film which anneals the said upper layer side oxide transparent conductive thin film and the said metal thin film in the air at the temperature of 200 degreeC or more.