JP3911332B2 - Laying floor board - Google Patents
Laying floor board Download PDFInfo
- Publication number
- JP3911332B2 JP3911332B2 JP35620097A JP35620097A JP3911332B2 JP 3911332 B2 JP3911332 B2 JP 3911332B2 JP 35620097 A JP35620097 A JP 35620097A JP 35620097 A JP35620097 A JP 35620097A JP 3911332 B2 JP3911332 B2 JP 3911332B2
- Authority
- JP
- Japan
- Prior art keywords
- board
- recycled wood
- wood board
- olefin
- floorboard
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【0001】
【発明の属する技術分野】
本発明は、置敷き用床板に関する。
【0002】
【従来の技術】
通常、床板を下地に接着剤や釘により固着しているが、このような方法では床板の張り替え作業が困難であるばかりか、施工に手間を要する。そのため、下地上に床板を単に置いて敷き詰める置敷き用床板が提案されている。
従来の置敷き用床板は、自重により施工後の安定性を図ることを目的として、基材としての合板の裏面に比重の大きい塩化ビニル樹脂からなるシートを貼着した構成となっている。
【0003】
【発明が解決しようとする課題】
しかしながら、前記従来の置敷き用床板においては、シートが塩化ビニル樹脂であるため、火災時に燃えると、有毒な塩素ガスを発生するという問題があった。また、合板も高価であるため、繊維板やパーティクルボード等の再生木質板を代替基材としたものも提案されているが、伸縮率が大きく、反りが発生し易い問題もあった。
【0004】
本発明はこのような事情に鑑みてなされたもので、反りが少なく、また低コストで安全な置敷き用床板を提供することを目的とする。
【0005】
【課題を解決するための手段】
前記目的に沿う請求項1記載の置敷き用床板は、繊維板、パーティクルボード、ストランドボード等からなる再生木質板の裏面にオレフィン系シートを介してガラス繊維マットを積層している。
【0006】
【発明の実施の形態】
続いて、添付した図面を参照しつつ、本発明を具体化した実施の形態につき説明し、本発明の理解に供する。
ここに、図1は本発明の一実施の形態に係る置敷き用床板が床下地上に配置された状態の断面図である。
図1に示すように、本発明の一実施の形態に係る置敷き用床板10は、基材の一例である再生木質板11の表面に化粧材12が積層され、再生木質板11の裏面にオレフィン系シート13を介して裏面材としてガラス繊維マット14が積層されている。以下、詳細に説明する。
【0007】
再生木質板11としては、厚さ2〜5mm程度の繊維板、パーティクルボード、ストランドボード等を単体あるいは複合したものを使用できる。再生木質板11の断面形状は、図1に示すように、再生木質板11の両端下部にそれぞれ突起部15、切欠き部16が形成されている。また、床下地21の凸凹になじませるために、再生木質板11の裏面から短手方向に多数本のスリットを形成することもできる。
再生木質板11の上面に積層された化粧材12は、突板、印刷化粧紙、化粧合成樹脂シート等が貼着されたり、さらに、この表面にウレタン樹脂塗料等により塗装されたりして構成されている。
【0008】
オレフィン系シート13としては、ポリエチレンやポリプロピレン、エチレンビニルアルコール等の水分非透過性合成樹脂を用いることができる。オレフィン系シート13の断面形状は、図1に示すように、オレフィン系シート13の両端上部にそれぞれ突起部17、切欠き部18が形成されている。なお、突起部15及び突起部17によって雄実19が、また、切欠き部16及び切欠き部18によって雌実20が形成され、雄実19と雌実20の掛合により隣接して配置される置敷き用床板10が連結されるようになっている。なお、厚さは2〜4mmの範囲でよい。
ガラス繊維マット14として、ガラス繊維を直交に束ねた厚さ1〜3mm程度のマット状物を使用することができる。厚さが1mm未満であれば、そり防止効果が少なく、一方厚さが3mmを超えるとコストが高くつく。
【0009】
置敷き用床板10を床下地21に配置した場合、基材を構成する再生木質板11は合板と比較して、水分の吸放出により反り易いが、オレフィン系シート13により床下地21からの水分が遮断されるので、反りが抑制される。
さらに、オレフィン系シート13の下面に積層されたガラス繊維マット14によってより効果的に反りが防止されると共に、燃えにくく、例え燃えたとしても、従来の塩化ビニル樹脂に比べて有毒ガスの発生は少なくて済む。
また、基材としての再生木質板11は、従来の合板に比較して安価なため、低コストの置敷き用床板10を製造できる。
【0010】
本実施の形態においては、両端部には、隣接する置敷き用床板10を掛合可能な対となる雄、雌実19、20を形成したが、必要に応じて雄、雌実を形成しない場合もある。
また、雄、雌実19、20は、再生木質板11とオレフィン系シート13に跨がって形成されているが、これに限定されず、再生木質板又はオレフィン系シートに単独で形成することもできる。
【0011】
【発明の効果】
請求項1記載の置敷き用床板においては、繊維板、パーティクルボード、ストランドボード等からなる再生木質板の裏面にオレフィン系シートを介してガラス繊維マットを積層しており、基材を再生木質板としているため、低コストで製造可能であると共に、再生木質板が合板と比較して水分の吸放出により反り易いとしても、オレフィン系シートによって床下地からの水分が遮断されるため、反りが効果的に抑制される。また、有害ガスが発生しないので安全である。
【図面の簡単な説明】
【図1】本発明の一実施の形態に係る置敷き用床板の断面図である。
【符号の説明】
10 置敷き用床板 11 再生木質板
12 化粧材 13 オレフィン系シート
14 ガラス繊維マット 15 突起部
16 切欠き部 17 突起部
18 切欠き部 19 雄実
20 雌実 21 床下地[0001]
BACKGROUND OF THE INVENTION
The present invention relates to a floorboard for installation.
[0002]
[Prior art]
Usually, the floor board is fixed to the base with an adhesive or a nail. However, such a method not only makes it difficult to replace the floor board, but also requires labor. For this reason, floorboards have been proposed that simply place the floorboard on the ground and spread it.
A conventional flooring board has a configuration in which a sheet made of a vinyl chloride resin having a large specific gravity is attached to the back surface of a plywood as a base material for the purpose of achieving stability after construction by its own weight.
[0003]
[Problems to be solved by the invention]
However, in the conventional flooring for flooring, since the sheet is made of vinyl chloride resin, there is a problem that toxic chlorine gas is generated when it is burned in a fire. Further, since plywood is also expensive, there has been proposed one using a recycled wood board such as a fiber board or a particle board as an alternative base material. However, there is a problem that warpage is likely to occur due to a large expansion / contraction rate.
[0004]
The present invention has been made in view of such circumstances, and an object of the present invention is to provide a floorboard for laying that is less warped and safe at a low cost.
[0005]
[Means for Solving the Problems]
The floorboard for laying down according to claim 1, which meets the object, has a glass fiber mat laminated on the back surface of a recycled wood board made of fiber board, particle board, strand board or the like via an olefin-based sheet.
[0006]
DETAILED DESCRIPTION OF THE INVENTION
Next, embodiments of the present invention will be described with reference to the accompanying drawings for understanding of the present invention.
Here, FIG. 1 is a cross-sectional view of a state in which a floorboard for installation according to an embodiment of the present invention is arranged on a floor base.
As shown in FIG. 1, in the
[0007]
As the recycled wood board 11, a fiber board having a thickness of about 2 to 5 mm, a particle board, a strand board, or the like can be used alone or in combination. As for the cross-sectional shape of the recycled wood board 11, as shown in FIG. 1, the
The
[0008]
As the olefin-based
As the glass fiber mat 14, a mat-like material having a thickness of about 1 to 3 mm in which glass fibers are bundled orthogonally can be used. If the thickness is less than 1 mm, the warping prevention effect is small, while if the thickness exceeds 3 mm, the cost is high.
[0009]
When the
Furthermore, the
Moreover, since the recycled wood board 11 as a base material is cheap compared with the conventional plywood, the low-
[0010]
In the present embodiment, the male and
Further, the male and
[0011]
【The invention's effect】
The floorboard for installation according to claim 1, wherein a glass fiber mat is laminated on the back surface of a recycled wood board made of fiberboard, particle board, strand board, etc. via an olefin-based sheet, and the base material is the recycled wood board. Therefore, it is possible to manufacture at low cost, and even if the recycled wood board is more likely to warp due to moisture absorption and release compared to the plywood, the olefin-based sheet blocks the moisture from the floor base, so the warping is effective. Is suppressed. Moreover, it is safe because no harmful gas is generated.
[Brief description of the drawings]
FIG. 1 is a cross-sectional view of a floorboard for laying according to an embodiment of the present invention.
[Explanation of symbols]
DESCRIPTION OF
Claims (1)