JP3328974B2 - Unique sheet - Google Patents
Unique sheetInfo
- Publication number
- JP3328974B2 JP3328974B2 JP34277692A JP34277692A JP3328974B2 JP 3328974 B2 JP3328974 B2 JP 3328974B2 JP 34277692 A JP34277692 A JP 34277692A JP 34277692 A JP34277692 A JP 34277692A JP 3328974 B2 JP3328974 B2 JP 3328974B2
- Authority
- JP
- Japan
- Prior art keywords
- pile
- sheet
- region
- different color
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【0001】[0001]
【産業上の利用分野】本発明は、ループパイル領域(以
下L領域という)とカットパイル領域(以下C領域とい
う)とが濃淡差異色で、かつ鮮明な異色効果を発揮する
自動車内装用の異色シートに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a different color for an automobile interior in which a loop pile area (hereinafter referred to as an L area) and a cut pile area (hereinafter referred to as a C area) have different shades of color and exhibit a clear different color effect. Regarding the sheet.
【0002】[0002]
【従来の技術】従来の自動車内装用のパイルシートは、
パイルの段階でケン縮を抑制する工夫がないまま、ただ
単にカットするだけで、ループパイルの側面とカットパ
イルの端面との、光の反射の大小などによって、濃淡差
異色を出す試みがなされている。しかしながら、これら
の方法によって得られた異色シートは、両領域間の明度
差(以下△L値という)が5未満で十分な異色効果が得
られておらず、特にL領域またはC領域のいずれかで柄
を出そうとした場合、両領域の境界がボケてしまい品位
の劣るものであった。また実用上では、使用回数を重ね
る内に、両パイル領域が更に不明瞭になり、例えばL領
域またはC領域のいずれかで細い線や文字を柄出しした
場合、線や文字が消失する問題があり、全体として品位
の劣るものであった。2. Description of the Related Art A conventional pile sheet for an automobile interior is
Attempts have been made to produce different shades of color due to the degree of light reflection between the side of the loop pile and the end face of the cut pile, without cutting in the pile stage, without any means to suppress shrinkage. I have. However, in the different color sheet obtained by these methods, the lightness difference between the two regions (hereinafter referred to as ΔL value) is less than 5, and a sufficient different color effect is not obtained. When the pattern was attempted to be displayed by using, the boundary between the two regions was blurred and the quality was inferior. In practice, both pile areas become more unclear as the number of uses increases, and for example, when a thin line or character is patterned in either the L area or the C area, the line or character disappears. Yes, the overall quality was poor.
【0003】また、カットパイル単独シートまたは、ル
ープパイル単独シートにおいては、異色を得るためにパ
イル長の長短で陰影模様を出したり、プリントによって
多色模様を出すことで、市場に提供している。陰影模様
によるシートは、パイル長の長短によって、光が直接当
たる部分と当たり難い部分との差によって模様を出そう
とするものであるが、△L値は5以下と低く、色調が単
調で品位の劣るものであった。また実用上においても使
用頻度が高くなるにつれてパイル長の長いほうがヘタ
リ、模様が消えてしまう。[0003] In addition, a cut pile single sheet or a loop pile single sheet is provided to the market by providing a shading pattern with a long or short pile length or a multicolor pattern by printing to obtain a different color. . The shaded sheet is intended to produce a pattern due to the difference between the part directly hit by light and the part that is hard to hit due to the length of the pile, but the ΔL value is as low as 5 or less, the color tone is monotonous, and the quality is high. Was inferior. Also, in practical use, as the frequency of use increases, the pile length becomes longer and the pattern disappears.
【0004】一方、プリントによる多色模様は、濃淡、
色相などの異色を自由に表現することができ、品位も優
れたものが多いが、L領域とC領域の組合わせによる異
色効果は得られていない。パイルシートのプリントは、
工程が繁雑でありコストも高くなるという問題があっ
た。[0004] On the other hand, multi-colored patterns by printing include shading,
Although different colors such as hue can be freely expressed and the quality is excellent in many cases, the different color effect by the combination of the L region and the C region is not obtained. The print of the pile sheet
There is a problem that the process is complicated and the cost is high.
【0005】[0005]
【発明が解決しようとする課題】本発明は、かかる従来
技術の問題点に鑑み、L領域とC領域との明確な濃淡差
異色が極めて明確で、かつ高級感のある異色シートを提
供せんとするものである。SUMMARY OF THE INVENTION The present invention has been made in view of the above-mentioned problems of the prior art, and it is necessary to provide a different-color sheet in which the distinct shades of color between the L region and the C region are extremely clear and have a high-class feeling. Is what you do.
【0006】[0006]
【課題を解決するための手段】本発明は、上記課題を達
成するため、次の構成を有する。すなわち、基布とパイ
ルとからなるシートにおいて、該パイルがループパイル
領域とカットパイル領域を構成し、かつ、該パイルのケ
ン縮率が15%以下、該パイルに含まれる酸化チタン量
が1.0重量%以下であることを特徴とする異色シート
である。The present invention has the following configuration to achieve the above object. That is, in a sheet composed of a base fabric and a pile, the pile constitutes a loop pile region and a cut pile region, the shrinkage of the pile is 15% or less, and the amount of titanium oxide contained in the pile is 1. It is a different color sheet characterized by being 0% by weight or less.
【0007】以下、本発明を図面を参照しながら詳細に
説明する。図1は、本発明に係る異色シートの一例を示
す模式図である。図1において、ループパイルBとカッ
トパイルCは、基材シート(基布)Aに面を成してタフ
ティングされ、それぞれL領域とC領域を形成してい
る。Hereinafter, the present invention will be described in detail with reference to the drawings. FIG. 1 is a schematic view showing an example of a different color sheet according to the present invention. In FIG. 1, a loop pile B and a cut pile C are tufted on a base sheet (base cloth) A so as to form an L region and a C region, respectively.
【0008】図2は、従来のカット・アンド・ループパ
イル布帛の断面を示す模式図である。図2では、カット
パイルCは先端で極端に屈曲した形状となっている。FIG. 2 is a schematic view showing a cross section of a conventional cut and loop pile fabric. In FIG. 2, the cut pile C has an extremely bent shape at the tip.
【0009】本発明は、L領域とC領域とを有するシー
トにおいて、パイルのケン縮率を15%以下とし、パイ
ルに含まれる酸化チタン量を1.0重量%以下にする
と、L領域とC領域との△L値が拡大される事実を究明
し、それによって明確な濃淡差異色を達成することに成
功したものである。本発明において異色シートを構成す
るパイルは、同一シート上にループパイル部とカットパ
イル部とがそれぞれ領域(L領域、C領域)を構成する
ことが重要である。これらの領域は、線(帯)状と面、
面と面などの構成からなり、線(帯)状であれば太さが
3mm以上、面であれば9mm2 以上の面が好ましい。それ
に対し、ループパイル1個の曲面とカットパイル1本の
端面とが交互に隣あってミックスされた場合は、視覚的
には混合されるため異色効果が得られない。上記パイル
は、基布の地肌が見えない程度に構成することが好まし
い。According to the present invention, in a sheet having an L region and a C region, when the shrinkage ratio of the pile is set to 15% or less and the amount of titanium oxide contained in the pile is set to 1.0% by weight or less, the L region and the C region are reduced. The inventors investigated the fact that the ΔL value with the region was enlarged, and thereby succeeded in achieving a distinct shade difference color. In the present invention, it is important that the piles constituting the different color sheets constitute the regions (L region, C region) of the loop pile portion and the cut pile portion on the same sheet. These areas consist of lines (bands) and surfaces,
It is composed of a surface and a surface, and preferably a line (band) having a thickness of 3 mm or more, and a surface having a thickness of 9 mm 2 or more. On the other hand, when the curved surface of one loop pile and the end face of one cut pile are alternately adjacent to each other, they are visually mixed, so that a different color effect cannot be obtained. It is preferable that the pile is configured so that the background of the base cloth is not visible.
【0010】また、本発明においてパイルのケン縮率を
15%以下とすることが重要である。ケン縮率が11%
以下であることは好ましい。ケン縮を全く有しないスト
レート糸も本発明に含まれる。一方、パイルのケン縮率
が15%を越えると異色効果が小さくなるので好ましく
ない。In the present invention, it is important to reduce the shrinkage of the pile to 15% or less. 11% reduction
It is preferred that: Straight yarns having no sagging are also included in the present invention. On the other hand, when the shrinkage of the pile exceeds 15%, the effect of different colors is reduced, which is not preferable.
【0011】ここでいうケン縮率とは、単繊維単位で次
のようにして求めた値をいう。 ケン縮率(%)=100×(a−b)/a ここで、aは50cm長さの試料に0.1 g/dの荷重をか
けた時の繊維長(mm)、bは50cm長さの試料に2mg/dの
荷重をかけた時の繊維長(mm)を示す。The term "shrinkage ratio" as used herein means a value determined in the following manner in a unit of single fiber. Saponification shrinkage (%) = 100 × (ab) / a Here, a is a fiber length (mm) when a load of 0.1 g / d is applied to a 50 cm long sample, and b is a 50 cm length The fiber length (mm) when a load of 2 mg / d was applied to the sample was shown.
【0012】従来の通常のカットパイルでは、図2に示
すように、パイルの先端が極端に屈曲して密集してい
る。このように屈曲した繊維は光を受けた時にその光を
反射する面が多いため反射光が多くなり、L領域とC領
域との十分な異色が得られない。本発明はケン縮率を1
5%以下とすることにより、C領域では単繊維単位で先
端が比較的屈曲することなく上方を向いているため、繊
維端面において光が反射される割合が少なく、効率的に
光が吸収され、深みのある濃色を呈する。In a conventional ordinary cut pile, as shown in FIG. 2, the tip of the pile is extremely bent and dense. The fiber bent in this manner has many surfaces that reflect the light when receiving the light, so that the amount of reflected light increases, and a sufficient different color between the L region and the C region cannot be obtained. The present invention reduces the shrinkage ratio to 1
By setting the content to 5% or less, in the C region, since the tip of the single fiber unit faces upward without relatively bending, the ratio of light reflected at the fiber end face is small, and light is efficiently absorbed, It has a deep dark color.
【0013】また、本発明において、パイルは、単繊維
単位で繊維に含まれる酸化チタン量が繊維重量に対し
1.0重量%以下であることが重要である。好ましく
は、0.5重量%以下である。1.0重量%を越える場
合には、C領域の繊維の先端において、反射光が多くな
り目的とする△L値が得られず結果として品粗なものに
なる。[0013] In the present invention, it is important that the amount of titanium oxide contained in the fiber in a single fiber unit is 1.0% by weight or less based on the weight of the fiber. Preferably, it is 0.5% by weight or less. If the content exceeds 1.0% by weight, the amount of reflected light increases at the tip of the fiber in the C region, and the desired ΔL value cannot be obtained, resulting in a coarse product.
【0014】従来のカットパイルは、繊維に含まれる酸
化チタン量が繊維重量に対し、1.0%以上含まれてお
り、さらにパイルの先端が極端に屈曲して密集している
ため、光を受けた時に反射光が多くなり、十分な異色が
得られない。In a conventional cut pile, the amount of titanium oxide contained in the fiber is 1.0% or more based on the weight of the fiber, and the tip of the pile is extremely bent and dense. When received, the reflected light increases, and a sufficient different color cannot be obtained.
【0015】本発明においては、パイルを構成する繊維
に含まれる酸化チタン量を繊維重量に対し1.0%以下
とし、さらにケン縮率を15%以下に抑えることによっ
てパイルの先端において光が吸収され、反射が抑えられ
てループパイル部との明確な異色が実現される。In the present invention, light is absorbed at the tip of the pile by controlling the amount of titanium oxide contained in the fibers constituting the pile to 1.0% or less with respect to the fiber weight, and further suppressing the shrinkage to 15% or less. Thus, reflection is suppressed, and a clear different color from the loop pile portion is realized.
【0016】繊維に含まれる酸化チタン量は、繊維重量
に対し1.0重量%以下であり、このましくは0.5重
量%以下である。1.0重量%を上回る場合には、C領
域の繊維の先端において、反射光が多くなり目的とする
△L値が得られず結果として品粗なものになる。[0016] The amount of titanium oxide contained in the fiber is 1.0% by weight or less, preferably 0.5% by weight or less based on the weight of the fiber. If the content exceeds 1.0% by weight, the amount of reflected light increases at the tip of the fiber in the C region, and the desired ΔL value cannot be obtained, resulting in a coarse product.
【0017】パイルを構成する繊維の断面形状は特に限
定されず、酸化チタン量が1.0%以下であれば、いか
なる断面形状でもよい。The cross-sectional shape of the fibers constituting the pile is not particularly limited, and any cross-sectional shape may be used as long as the amount of titanium oxide is 1.0% or less.
【0018】また、曲玉形、多葉形、H形など、一か所
以上の凹部を有する異形断面形状の繊維、さらに該形状
の中空の繊維などを用いた場合には、ループパイル領域
ではカーペット独特のふくらみのある風合いを得ること
ができ、カットパイル領域ではパイルの先端において花
火のごとき広がりを得ることができ、結果として高級感
が得られるので好ましく用いられる。When a fiber having an irregular cross-sectional shape having one or more concave portions such as a curved ball shape, a multilobe shape, and an H shape, and a hollow fiber having such a shape, is used, the loop pile region has It is preferably used because a swelling texture unique to a carpet can be obtained, and in the cut pile area, a spread such as fireworks can be obtained at the tip of the pile, and as a result, a high-class feeling can be obtained.
【0019】本発明の異色シートは、ループパイル領域
が淡色系で、カットパイル領域が濃色系の濃淡差異色シ
ートを構成し、両領域の△L値が5以上であると、特に
優れた異色効果を発揮する。The different color sheet of the present invention is particularly excellent when the loop pile region is a light color system and the cut pile region is a dark color system with a dark and light color difference sheet, and the ΔL value of both regions is 5 or more. Exhibits a unique color effect.
【0020】次に、本発明の異色シートの製造方法を説
明する。ケン縮率15%以下であるパイルを得る方法
は、例えば、染色工程あるいは乾燥工程で潜在ケン縮が
発現しないように、パイルをチーズまたはドラムに巻い
た状態で染色前にスチーム熱処理する方法、染色と同時
に熱固定する方法などを用いることによって得ることが
できる。Next, the method for producing a different color sheet of the present invention will be described. Methods for obtaining a pile having a shrinkage ratio of 15% or less include, for example, a method in which the pile is wound around a cheese or a drum and steam-heat-treated before dyeing so that latent shrinkage does not occur in the dyeing step or the drying step. At the same time, it can be obtained by using a method of heat setting.
【0021】例えば、スチーム熱処理の方法において、
温度は95℃以上130℃以下で行なうことが好まし
い。95℃未満であると後の染色工程あるいは乾燥工程
でケン縮発現により異色効果が低減する。130℃を越
えると繊維の風合いが損なわれ、製品の品位が低下す
る。For example, in the method of steam heat treatment,
The temperature is preferably from 95 ° C to 130 ° C. When the temperature is lower than 95 ° C., a different color effect is reduced due to the development of shrinkage in the subsequent dyeing step or drying step. If the temperature exceeds 130 ° C., the texture of the fiber is impaired, and the quality of the product is reduced.
【0022】上記の様にして用意されたパイルを基布に
打ち込んでループパイルとなし、その一部をカットして
カット領域を形成し、ループパイル領域とカットパイル
領域とから構成されるシートとする。The pile prepared as described above is driven into a base cloth to form a loop pile, a part of which is cut to form a cut area, and a sheet comprising a loop pile area and a cut pile area. I do.
【0023】シートを製造するに際し、酸化チタン含有
量が1.0重量%以下の繊維を用いることにより本願発
明の効果を得ることができる。In producing a sheet, the effect of the present invention can be obtained by using a fiber having a titanium oxide content of 1.0% by weight or less.
【0024】シートは、最終パイル製品においてパイル
のケン縮率が15%以下が保持されるように着色すれば
よい。着色の方法は、原着、糸染め、反染めなど特に限
定されず、適宜選択することができる。[0024] The sheet may be colored so that the shrinkage of the pile in the final pile product is maintained at 15% or less. The coloring method is not particularly limited, such as original dyeing, yarn dyeing, and anti-dyeing, and can be appropriately selected.
【0025】また、本発明においてパイルを構成する繊
維は、特に限定されないが、ポリアミド系、ポリエステ
ル系、ポリアクリルニトリル系およびこれらの改質繊維
などからなる合成繊維が好ましい。パイルを構成する単
繊維の太さ、長さ、断面形状は、最終目的の品位に合っ
たものを使用することができる。The fibers constituting the pile in the present invention are not particularly limited, but synthetic fibers composed of polyamide-based, polyester-based, polyacrylonitrile-based and modified fibers thereof are preferred. The thickness, length, and cross-sectional shape of the single fibers constituting the pile may be those that match the quality of the final purpose.
【0026】パイルの単糸繊度は、50デニールを越え
るようになるとカットパイル、ループパイルとも風合い
が粗硬になるが、細くなりすぎるとヘタリが出るなど実
用上問題になることから、2〜50デニールが好まし
く、10〜30デニールがさらに好ましい。When the single fiber fineness of the pile exceeds 50 denier, the texture of both the cut pile and the loop pile becomes coarse and hard, but when it becomes too thin, practical problems such as settling occur. Denier is preferred, and 10 to 30 denier is more preferred.
【0027】パイル長は、カットパイル長とループパイ
ル長が揃っていることが好ましい。全体としての長さ
は、5〜20mmの範囲のものが好ましく使用される。パ
イル長が揃わない場合、例えば、ループパイル長に比べ
カットパイル長が極端に長い場合は、L領域とC領域と
の境界が不明瞭になるため、模様がボケてしまう傾向が
あり、また、長期間の使用によりパイルがヘタり、品位
の劣るものになり易い。また、逆にループパイル長が長
い場合には、表面のタッチが粗硬になるばかりでなく、
全体として白けた色合いになる傾向がある。従って、パ
イル長は、ループパイル長に比べカットパイル長は±5
mm程度のものが好ましく使用される。The pile length is preferably the same as the cut pile length and the loop pile length. The overall length is preferably in the range of 5 to 20 mm. When the pile lengths are not uniform, for example, when the cut pile length is extremely long compared to the loop pile length, the boundary between the L region and the C region becomes unclear, and the pattern tends to be blurred. The pile is liable to be broken due to long-term use, and the quality tends to be poor. On the other hand, when the loop pile length is long, not only the touch on the surface becomes coarse but also hard,
There is a tendency for the color to be whitish as a whole. Therefore, the cut pile length is ± 5 compared to the loop pile length.
Those having a size of about mm are preferably used.
【0028】本発明におけるシートの基材は、用途によ
って適宜選定すればよいが、木綿、絹、麻などの天然繊
維、または、ポリエステル、ポリアクリルニトリル、ポ
リエチレン、ポリプロピレン、ポリアミドなどの合成繊
維からなる高分子シートを使用することができるが、敷
物の場合ではポリプロピレンが好ましい。The base material of the sheet in the present invention may be appropriately selected according to the intended use, and is made of natural fibers such as cotton, silk, hemp, or synthetic fibers such as polyester, polyacrylonitrile, polyethylene, polypropylene, and polyamide. Polymer sheets can be used, but in the case of rugs, polypropylene is preferred.
【0029】本発明の異色シートは、L領域では光がル
ープ側面で乱反射されるため淡色を呈し、C領域では単
繊維単位で繊維に含まれる酸化チタン量が繊維重量に対
して1.0重量%以下であるため透明感があり、光を吸
収しやすく、加えて、繊維がループを形成せず上方を向
き、ケン縮率が低いため先端が屈曲していないので繊維
端面において光が吸収され、深みのある濃色を呈するの
である。すなわち、L領域とC領域における光の吸収と
反射による色の違いが生じるのである。The different color sheet of the present invention exhibits a light color in the region L because light is diffusely reflected on the side of the loop, and the amount of titanium oxide contained in the fiber per unit fiber in the region C is 1.0 wt. % Or less, it is transparent and easily absorbs light. In addition, light is absorbed at the fiber end face because the fiber faces upward without forming a loop and the tip does not bend due to low shrinkage. It has a deep, deep color. That is, a color difference occurs between light absorption and reflection in the L region and the C region.
【0030】製品品位の観点から、L領域とC領域にお
ける明度の差(△L値)が5以上であることが好まし
く、10以上であることはさらに好ましい。From the viewpoint of product quality, the difference in lightness (ΔL value) between the L region and the C region is preferably 5 or more, and more preferably 10 or more.
【0031】[0031]
【実施例】以下、実施例を挙げて本発明をさらに具体的
に説明する。なお、実施例で使用する測色法は次の方法
で行なった。The present invention will now be described more specifically with reference to examples. The colorimetry used in the examples was performed by the following method.
【0032】測色法 スガ試験機株式会社製の多光源分光測色計のC光源を使
って、異色シートのL領域とC領域のL値を測色比較し
て、△L値を求めた。Colorimetric method Using a C light source of a multi-light source spectrophotometer manufactured by Suga Test Instruments Co., Ltd., the L value of the L region and the L value of the C region of the different color sheet were colorimetrically compared to obtain a ΔL value. .
【0033】実施例1〜3 酸化チタンを0.1重量%含有するポリアミドを通常の
方法により溶融紡糸して断面形状が丸であるポリアミド
フィラメントを得、次いでギヤケン縮法によってケン縮
をかけて、単糸繊度20デニールのバルクド・コンティ
ニュアス・フィラメント(BCF)を得た。Examples 1 to 3 A polyamide containing 0.1% by weight of titanium oxide was melt-spun by a conventional method to obtain a polyamide filament having a round cross-sectional shape. A bulked continuous filament (BCF) having a single yarn fineness of 20 denier was obtained.
【0034】得られたBCFを、紙管に約500g巻取
り、100℃に熱しられた箱型のスチーマの中で30分
間処理し、ケン縮率3%のBCFとした。次に、得られ
たBCFを、L領域とC領域とを自動的に形成するよう
セットされた、タフトマシンを使ってポリプロピレンか
らなる基布に700g/m2 の目付けになるようにタフ
ティングしてL領域とC領域を構成し、パイルシートを
得た。パイル長は、ループパイルが8mm、カットパイル
が10mmであった。L領域とC領域の模様の面積比は
1:1で、C領域は全体の50%であり、シート上で糸
断面が占める割合(パイル密度)は約70%であった。About 500 g of the obtained BCF was wound around a paper tube and treated in a box-shaped steamer heated to 100 ° C. for 30 minutes to obtain a BCF having a shrinkage factor of 3%. Next, the obtained BCF was tufted to a base fabric made of polypropylene using a tufting machine set to automatically form the L region and the C region so as to have a basis weight of 700 g / m 2. Thus, a pile sheet was obtained by forming an L region and a C region. The pile length was 8 mm for the loop pile and 10 mm for the cut pile. The pattern area ratio between the L region and the C region was 1: 1, the C region was 50% of the whole, and the ratio (pile density) occupied by the yarn cross section on the sheet was about 70%.
【0035】次に、上記作成したパイルシートを、染料
(SANDZ社製のNylosan BlueN-GFL 167%)を
1%owf、染色助剤(日華化学株式会社製のニューボ
ンTS)を3%owf、硫酸アンモン3%owfをそれ
ぞれ配合した染浴中に投入し、100℃で30分間浴中
染色した。次いで、水洗いして、乾燥し、異色シート
(実施例1)を作成した。また、酸化チタンを0.05
重量%含有するポリアミドを通常の方法により溶融紡糸
して得られた断面形状が丸で中空のポリアミドフィラメ
ントからなるBCFを用いた以外は実施例1と同様の方
法により、異色シート(実施例2)を得た。さらにま
た、酸化チタンを0.05重量%含有するポリアミドを
実施例1と同様の方法により単糸繊度20デニールの断
面形状が三葉で中空のポリアミドフィラメントからなる
BCFを用いた以外は実施例1と同様の方法により異色
シート(実施例3)を作成した。Next, the pile sheet prepared above was prepared by adding 1% owf of a dye (Nylosan Blue N-GFL 167% manufactured by Sandz) and 3% owf of a dyeing aid (New Bonn TS manufactured by Nichika Chemical Co., Ltd.). 3% owf of ammonium sulfate was placed in each of the dyeing baths, and dyed in the bath at 100 ° C. for 30 minutes. Next, the sheet was washed with water and dried to prepare a sheet of a different color (Example 1). In addition, titanium oxide is 0.05
A different-color sheet (Example 2) in the same manner as in Example 1 except that a BCF composed of polyamide filaments having a round and hollow cross section obtained by melt-spinning a polyamide containing by weight in a usual manner was used. I got Further, Example 1 was repeated except that a polyamide containing 0.05% by weight of titanium oxide was used in the same manner as in Example 1 except that BCF made of hollow polyamide filaments having a three-lobed cross section of 20 denier single yarn was used. A sheet of a different color (Example 3) was prepared in the same manner as described above.
【0036】得られた異色シートの△L値を表めた結果
を表1に示す。表1に示すように、本発明に係る異色シ
ート(実施例1〜3)は、△L値が5以上であり、濃淡
差が明確で高級感のある異色シートが得られた。また、
6ケ月間使用後の△L値を測定すると、およそ1〜2%
低下するものの△L値は5以上あり、耐久性にも優れて
いた。Table 1 shows the ΔL values of the obtained sheets of different colors. As shown in Table 1, the sheets of different colors according to the present invention (Examples 1 to 3) had ΔL values of 5 or more, and the sheets of different colors with distinct shades of light and high quality were obtained. Also,
△ L value after use for 6 months is about 1-2%
Although decreased, the ΔL value was 5 or more, and the durability was excellent.
【0037】比較例1 酸化チタンを1.5重量%含有するポリアミドを実施例
1と同様の方法により単糸繊度20デニールの断面形状
が丸のポリアミドフィラメントからなるBCFを得、1
00℃スチーマの中で30分間熱処理を施さない以外は
実施例1と同様の方法により異色シートを作成した。ケ
ン縮率は25%であった。得られた異色シートの△L値
を求めたところ、表1に示すように、△L値が0.5と
低く異色効果が小さいものであった。COMPARATIVE EXAMPLE 1 A BCF comprising a polyamide filament having a roundness of 20 denier and having a round cross section was obtained in the same manner as in Example 1 using a polyamide containing 1.5% by weight of titanium oxide.
A different color sheet was prepared in the same manner as in Example 1 except that the heat treatment was not performed in a steamer at 00 ° C. for 30 minutes. The shrinkage was 25%. When the ΔL value of the obtained different color sheet was determined, as shown in Table 1, the ΔL value was as low as 0.5 and the different color effect was small.
【0038】比較例2 酸化チタンを1.5重量%含有するポリアミドを実施例
2と同様の方法により単糸繊度20デニールの断面形状
が丸で中空のポリアミドフィラメントからなるBCFを
得、100℃スチーマの中で30分間熱処理を施さない
以外は実施例1と同様の方法により異色シートを作成し
た。ケン縮率は20%であった。得られた異色シートの
△L値を求めたところ、表1に示すように、△L値が
1.8であり、十分な異色効果は得られず品粗なもので
あった。Comparative Example 2 A polyamide containing 1.5% by weight of titanium oxide was obtained in the same manner as in Example 2 to obtain a BCF consisting of hollow polyamide filaments having a single-filament fineness of 20 denier and a round cross-section, and steaming at 100 ° C. A different color sheet was prepared in the same manner as in Example 1 except that the heat treatment was not performed for 30 minutes. The shrinkage was 20%. When the ΔL value of the obtained different color sheet was determined, as shown in Table 1, the ΔL value was 1.8, and a sufficient different color effect was not obtained, and the sheet was rough.
【0039】比較例3 酸化チタンを1.5重量%含有するポリアミドを実施例
1と同様の方法により単糸繊度20デニールの断面形状
が丸のポリアミドフィラメントからなるBCFを得、実
施例1と同様の方法により異色シートを作成した。ケン
縮率は3%であった。得られた異色シートの△L値は
3.5と低く異色効果の小さいものであった。COMPARATIVE EXAMPLE 3 A BCF comprising a polyamide filament having a roundness of 20 denier and having a round cross section was obtained in the same manner as in Example 1 by using a polyamide containing 1.5% by weight of titanium oxide in the same manner as in Example 1. A sheet of a different color was prepared by the method described above. The shrinkage was 3%. The ΔL value of the obtained sheet of a different color was as low as 3.5, and the sheet had a small different color effect.
【0040】比較例4 酸化チタンを0.1重量%含有するポリアミドを実施例
1と同様の方法により単糸繊度20デニールの断面形状
が丸のポリアミドフィラメントからなるBCFを得、1
00℃スチーマの中で30分間熱処理を施さない以外は
実施例1と同様の方法により異色シートを作成した。ケ
ン縮率は25%であった。得られた異色シートの△L値
は2.7と低く異色効果の小さいものであった。COMPARATIVE EXAMPLE 4 A BCF comprising a polyamide filament having a roundness of 20 deniers and a round cross-sectional shape of a polyamide filament was obtained in the same manner as in Example 1 by using a polyamide containing 0.1% by weight of titanium oxide.
A different color sheet was prepared in the same manner as in Example 1 except that the heat treatment was not performed in a steamer at 00 ° C. for 30 minutes. The shrinkage was 25%. The ΔL value of the obtained sheet of a different color was as low as 2.7, and the sheet had a small different color effect.
【0041】[0041]
【表1】 [Table 1]
【0042】[0042]
【発明の効果】本発明に係る異色シートは、従来の異色
シートに比べ、著しく改良された濃淡差異色を有し、か
つ高級感を有する。The different color sheet according to the present invention has remarkably improved light and shade difference color as compared with the conventional different color sheet and has a sense of quality.
【図1】本発明に係る異色シートの一例を示す模式図で
ある。FIG. 1 is a schematic view showing an example of a different color sheet according to the present invention.
【図2】従来のカット・アンド・ループパイル布帛の断
面を示す模式図である。FIG. 2 is a schematic view showing a cross section of a conventional cut and loop pile fabric.
【符号の説明】 A:シート B:ループパイル領域 C:カットパイル領域[Description of Signs] A: Sheet B: Loop pile area C: Cut pile area
───────────────────────────────────────────────────── フロントページの続き (56)参考文献 特開 昭60−126355(JP,A) 特開 平4−328037(JP,A) 特開 昭56−63056(JP,A) (58)調査した分野(Int.Cl.7,DB名) B60N 3/00 A47G 27/00 D03D 27/00 ──────────────────────────────────────────────────続 き Continuation of the front page (56) References JP-A-60-126355 (JP, A) JP-A-4-328037 (JP, A) JP-A-56-63056 (JP, A) (58) Field (Int.Cl. 7 , DB name) B60N 3/00 A47G 27/00 D03D 27/00
Claims (2)
該パイルがループパイル領域とカットパイル領域を構成
し、かつ、該パイルのケン縮率が15%以下、該パイル
に含まれる酸化チタン量が1.0重量%以下であること
を特徴とする異色シート。1. A sheet comprising a base cloth and a pile,
The pile comprises a loop pile area and a cut pile area, and the shrinkage of the pile is 15% or less, and the amount of titanium oxide contained in the pile is 1.0% by weight or less. Sheet.
パイル領域が濃色系であって、かつ両領域の明度差△L
値が5以上であることを特徴とする請求項1記載の異色
シート。2. The loop pile area is of a light color type, the cut pile area is of a dark color type, and the brightness difference ΔL between the two areas is 2.
2. The different color sheet according to claim 1, wherein the value is 5 or more.