JP3298217B2 - Ink composition for moisture indicator and recording medium using the same - Google Patents
Ink composition for moisture indicator and recording medium using the sameInfo
- Publication number
- JP3298217B2 JP3298217B2 JP07322793A JP7322793A JP3298217B2 JP 3298217 B2 JP3298217 B2 JP 3298217B2 JP 07322793 A JP07322793 A JP 07322793A JP 7322793 A JP7322793 A JP 7322793A JP 3298217 B2 JP3298217 B2 JP 3298217B2
- Authority
- JP
- Japan
- Prior art keywords
- acid
- water
- ink composition
- color
- moisture indicator
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本発明は、大気中においては有色
であるが、水中または水を付着することにより消色する
水分インジケータに関するものである。例として挙げる
と、不織布のシーツの尿の判定、紙オムツの尿の判定、
水分表示体、水濡れ履歴検査等に利用される。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a moisture indicator which is colored in the atmosphere but is decolored by being attached to water or water. As examples, determination of urine of non-woven sheets, determination of urine of disposable diapers,
It is used for moisture indicator, water history inspection, etc.
【０００２】[0002]
【従来の技術】代表的な水分インジケータとしては、コ
バルト塩が挙げられる。コバルト塩による水分検知は、
コバルト塩が水と反応して水和物を作り色調変化を生じ
ることに基づいている。すなわち、コバルトイオンに配
位している水分子の数が多いほど赤色、少ないほど青色
に変化することを利用している。例えば、ＣｏＣｌ2 ・
６Ｈ2 Ｏ（淡赤色）、ＣｏＣｌ2 ・４Ｈ2 Ｏ（桃色）、
ＣｏＣｌ2 ・２Ｈ2 Ｏ（淡赤紫色）、２ＣｏＣｌ2 ・３
Ｈ2 Ｏ（赤紫色）、ＣｏＣｌ2 ・２Ｈ2 Ｏ（暗青紫
色）、ＣｏＣｌ2 （淡青色）のように変わる。2. Description of the Related Art As a representative moisture indicator, a cobalt salt is exemplified. Moisture detection with cobalt salt
It is based on the fact that cobalt salts react with water to form hydrates and cause color changes. In other words, it utilizes the fact that the larger the number of water molecules coordinated to the cobalt ion, the more the color changes to red, and the smaller the number, the more the color changes to blue. For example, CoCl 2.
6H 2 O (light red), CoCl 2 .4H 2 O (pink),
CoCl 2 · 2H 2 O (pale red-purple), 2CoCl 2 · 3
It changes like H 2 O (red-purple), CoCl 2 .2H 2 O (dark blue-purple), CoCl 2 (light blue).
【０００３】しかしながらコバルト塩は水和物を作りや
すく、大気中の湿度に敏感に反応し、大気中に置いてお
くだけで呈色状態が青色から赤色に変化する。また、こ
の呈色状態は可逆的であり、乾燥により再使用が可能で
ある反面、メモリ−性が乏しく、水濡れ履歴等を必要と
する際には、不都合であるという問題点があった。[0003] However, the cobalt salt easily forms a hydrate, reacts sensitively to the humidity in the atmosphere, and changes its color state from blue to red just by being placed in the atmosphere. Further, this coloration state is reversible and can be reused by drying, but has poor memory properties and is disadvantageous when water wet history or the like is required.
【０００４】[0004]
【発明が解決しようとする課題】本発明は、上記の如き
不都合、欠点を解消して、水中または水を付着すること
により消色し、その消色時の状態変化を乾燥後も保持
し、かつ耐環境保存性、すなわち大気中の湿度に抗する
保存安定性を有する水分インジケータを提供することを
目的とする。SUMMARY OF THE INVENTION The present invention solves the above-mentioned disadvantages and drawbacks, erases the color by adhering to water or water, and retains the state change at the time of the erase after drying. It is another object of the present invention to provide a moisture indicator having environmental storage resistance, that is, storage stability that resists atmospheric humidity.
【０００５】[0005]
【課題を解決するための手段】本発明は、有機酸、有機
酸により発色する呈色性有機化合物、吸水性粉末、及び
高分子結着剤から成る組成物が、非水溶媒中に溶解もし
くは分散されて成る水分インジケ−タ用インキ組成物
と、そのインキ組成物を支持体上に塗布して成る水分イ
ンジケータである。また、実施様態として、前記有機酸
として安息香酸及びその誘導体であることを特徴とする
上記の消色型水分インジケータ用インキ組成物である。
以下、各成分について具体的に説明する。According to the present invention, a composition comprising an organic acid, a color-forming organic compound which develops a color with the organic acid, a water-absorbing powder, and a polymer binder is dissolved or dissolved in a non-aqueous solvent. A water indicator ink composition dispersed and a water indicator formed by applying the ink composition on a support. According to an embodiment, there is provided the above-described ink composition for a decolorable moisture indicator, wherein the organic acid is benzoic acid or a derivative thereof.
Hereinafter, each component will be described specifically.
【０００６】（イ）呈色性有機化合物 本発明に使用される有機酸により発色する呈色性有機化
合物としては、酸性で発色あるいは色変化を起こすよう
なｐＨ指示薬、トリアリールメタン誘導体、フルオラン
誘導体などが使用される。その代表的な例を具体例をも
って示せば、クリスタルバイオレットラクトン、３−イ
ンドリノ−３−ｐ−ジメチルアミノフェニル−６−ジメ
チルアミノフタリド、３−ジエチルアミノ−７−クロロ
フルオラン、２−（２−フルオロフェニルアミノ）−６
−ジエチルアミノフルオラン、２−（２−フルオロフェ
ニルアミノ）−６−ジ−ｎ−ブチルアミノフルオラン、
３−ジエチルアミノ−７−シクロヘキシルアミノフルオ
ラン、３−ジエチルアミノ−５−メチル−７−ｔ−ブチ
ルフルオラン、３−ジエチルアミノ−６−メチル−７−
アニリノフルオラン、３−ジエチルアミノ−６−メチル
−７−ｐ−ブチルアニリノフルオラン、３−シクロヘキ
シルアミノ−６−クロロフルオラン、２−アニリノ−３
−メチル−６−（Ｎ−エチル−ｐ−トルイジノ）−フル
オラン、３−ピロリジノ−６−メチル−７−アニリノフ
ルオラン、３−ピロリジノ−７−シクロヘキシルアミノ
フルオラン、３−Ｎ−メチルシクロヘキシルアミノ−６
−メチル−７−アニリノフルオラン、３−Ｎ−エチルペ
ンチルアミノ−６−メチル−７−アニリノフルオラン等
をあげることができる。但し、これらの代表例は本発明
を限定するものではない。(A) Color-forming organic compound The color-forming organic compound used in the present invention, which develops a color with an organic acid, includes a pH indicator, a triarylmethane derivative, and a fluoran derivative which cause color development or color change under acidic conditions. Are used. Typical examples thereof are as follows: crystal violet lactone, 3-indolino-3-p-dimethylaminophenyl-6-dimethylaminophthalide, 3-diethylamino-7-chlorofluoran, 2- (2- Fluorophenylamino) -6
-Diethylaminofluoran, 2- (2-fluorophenylamino) -6-di-n-butylaminofluoran,
3-diethylamino-7-cyclohexylaminofluoran, 3-diethylamino-5-methyl-7-tert-butylfluoran, 3-diethylamino-6-methyl-7-
Anilinofluoran, 3-diethylamino-6-methyl-7-p-butylanilinofluoran, 3-cyclohexylamino-6-chlorofluoran, 2-anilino-3
-Methyl-6- (N-ethyl-p-toluidino) -fluoran, 3-pyrrolidino-6-methyl-7-anilinofluoran, 3-pyrrolidino-7-cyclohexylaminofluoran, 3-N-methylcyclohexylamino -6
-Methyl-7-anilinofluoran, 3-N-ethylpentylamino-6-methyl-7-anilinofluoran and the like. However, these representative examples do not limit the present invention.
【０００７】（ロ）有機酸 本発明に使用する有機酸は、常温で固体であることが望
ましく、その具体例を以下に示すが、これらの代表例は
本発明を限定するものではない。(B) Organic acid The organic acid used in the present invention is desirably a solid at ordinary temperature, and specific examples thereof are shown below, but these typical examples do not limit the present invention.
【０００８】安息香酸、メチル安息香酸、エチル安息香
酸、プロピル安息香酸、ブチル安息香酸、ペンチル安息
香酸、ヘキシル安息香酸、ヘプチル安息香酸、オクチル
安息香酸、デシル安息香酸、ドデシル安息香酸、テトラ
デシル安息香酸、ヘキサデシル安息香酸、オクタデシル
安息香酸、メトキシ安息香酸、エトキシ安息香酸、プロ
ポキシ安息香酸、ブトキシ安息香酸、ペンチルオキシ安
息香酸、ヘキシルオキシ安息香酸、ヘプチルオキシ安息
香酸、オクチルオキシ安息香酸、ドデシルオキシ安息香
酸、テトラデシルオキシ安息香酸、ヘキサデシルオキシ
安息香酸、オクタデシルオキシ安息香酸、ヒドロキシ安
息香酸、アミノ安息香酸、メチルアミノ安息香酸、エチ
ルアミノ安息香酸、プロピルアミノ安息香酸、ブチルア
ミノ安息香酸、ペンチルアミノ安息香酸、ヘキシルアミ
ノ安息香酸、ヘプチルアミノ安息香酸、オクチルアミノ
安息香酸、デシルアミノ安息香酸、ドデシルアミノ安息
香酸、テトラデシルアミノ安息香酸、ヘキサデシルアミ
ノ安息香酸、オクタデシルアミノ安息香酸、ジメチルア
ミノ安息香酸、ジエチルアミノ安息香酸、ジヒドロキシ
安息香酸、ジヒドロキシアミノ安息香酸、トリヒドロキ
シ安息香酸。Benzoic acid, methylbenzoic acid, ethylbenzoic acid, propylbenzoic acid, butylbenzoic acid, pentylbenzoic acid, hexylbenzoic acid, heptylbenzoic acid, octylbenzoic acid, decylbenzoic acid, dodecylbenzoic acid, tetradecylbenzoic acid, Hexadecylbenzoic acid, octadecylbenzoic acid, methoxybenzoic acid, ethoxybenzoic acid, propoxybenzoic acid, butoxybenzoic acid, pentyloxybenzoic acid, hexyloxybenzoic acid, heptyloxybenzoic acid, octyloxybenzoic acid, dodecyloxybenzoic acid, tetra Decyloxybenzoic acid, hexadecyloxybenzoic acid, octadecyloxybenzoic acid, hydroxybenzoic acid, aminobenzoic acid, methylaminobenzoic acid, ethylaminobenzoic acid, propylaminobenzoic acid, butylaminobenzoic acid, PE Tylaminobenzoic acid, hexylaminobenzoic acid, heptylaminobenzoic acid, octylaminobenzoic acid, decylaminobenzoic acid, dodecylaminobenzoic acid, tetradecylaminobenzoic acid, hexadecylaminobenzoic acid, octadecylaminobenzoic acid, dimethylaminobenzoic acid, Diethylaminobenzoic acid, dihydroxybenzoic acid, dihydroxyaminobenzoic acid, trihydroxybenzoic acid.
【０００９】（ハ）高分子結着剤 本発明に使用される高分子結着剤は、支持体と呈色性有
機化合物、有機酸、および吸水性粉末を固着するために
用いられ、有機溶剤に可溶な熱可塑性樹脂であれば、い
ずれをも使用できる。具体例を以下に示すが、これらの
代表例は本発明を限定するものではない。(C) Polymer binder The polymer binder used in the present invention is used for fixing a color-forming organic compound, an organic acid, and a water-absorbing powder to a support, and an organic solvent. Any thermoplastic resin soluble in water can be used. Specific examples are shown below, but these representative examples do not limit the present invention.
【００１０】ポリエステル系樹脂、ポリ塩化ビニル、塩
化ビニル−酢酸ビニル共重合体、ポリメタクリル酸メチ
ル、ポリメタクリル酸エチル、ポリメタクリル酸ブチ
ル、メタクリル酸メチルとメタクリル酸アルキル（但
し、アルキル基の炭素数は２〜６個）の共重合体などの
アクリル系樹脂、ポリスチレン、ポリアミド系樹脂、ポ
リビニルブチラール、ポリビニルアセタールなどのポリ
アセタール系樹脂、ポリウレタン樹脂、エポキシ樹脂、
石油系樹脂、メチルセルロース、エチルセルロース、ニ
トロセルロース等のセルロース誘導体、及びこれらの混
合物。Polyester resin, polyvinyl chloride, vinyl chloride-vinyl acetate copolymer, polymethyl methacrylate, polyethyl methacrylate, polybutyl methacrylate, methyl methacrylate and alkyl methacrylate (however, Are 2 to 6) acrylic resins such as copolymers, polyacetal resins such as polystyrene, polyamide resins, polyvinyl butyral, and polyvinyl acetal, polyurethane resins, epoxy resins,
Petroleum-based resins, cellulose derivatives such as methylcellulose, ethylcellulose, nitrocellulose, and mixtures thereof.
【００１１】（ニ）吸水性粉末 本発明に使用される吸水性粉末は、水分インジケータ組
成物に添加することにより、多孔質構造を形成し、水分
と呈色性組成物との接触を推進し、呈色性有機化合物の
色調変化を促進する働きをする。(D) Water-absorbing powder The water-absorbing powder used in the present invention forms a porous structure by being added to the moisture indicator composition to promote contact between moisture and the color-forming composition. It functions to promote the color change of the color-forming organic compound.
【００１２】この為、吸水性粉末は親水性を有していた
方が好ましい。具体的には、デンプン、カオリン、タル
ク、微粉末セルロース、ケイ酸アルミニウム、酸化ケイ
素、炭酸カルシウム等が使用されるが、上記代表例は本
発明を限定するものではない。For this reason, it is preferable that the water-absorbing powder has a hydrophilic property. Specifically, starch, kaolin, talc, finely powdered cellulose, aluminum silicate, silicon oxide, calcium carbonate and the like are used, but the above representative examples do not limit the present invention.
【００１３】（ホ）非水溶媒 非水溶媒としては、以上に示したインキ組成物、特に高
分子結着剤を溶解することが必要である。具体的には、
芳香族炭化水素、脂肪族炭化水素、エステル類、ケトン
類、アルコール類等の中から適宜選択し使用する。上記
した溶剤は単独もしくは二種以上混合してもかまわな
い。(E) Non-aqueous solvent As a non-aqueous solvent, it is necessary to dissolve the above-described ink composition, particularly a polymer binder. In particular,
It is appropriately selected from aromatic hydrocarbons, aliphatic hydrocarbons, esters, ketones, alcohols and the like. The above solvents may be used alone or in combination of two or more.
【００１４】以上、（イ）〜（ホ）のインキ組成物を支
持体に塗布して測定領域を形成するわけであるが、塗布
にあたっては印刷法、コーティング法（たとえば、ロー
ルコーティング、スプレーコーティング、ディップコー
ティング、ベタコーティング）等が用いられる。As described above, the ink composition of (a) to (e) is applied to a support to form a measurement area. In the application, a printing method, a coating method (for example, roll coating, spray coating, Dip coating, solid coating) and the like are used.
【００１５】本発明においては、インキ組成物の塗布量
が比較的多く、かつ塗布量が一定であることが好ましい
ため、シルクスクリーン印刷法、凹版印刷法、グラビア
印刷法等により、インキ組成物を支持体上に設けること
が好ましい。In the present invention, since the coating amount of the ink composition is preferably relatively large and the coating amount is preferably constant, the ink composition is prepared by a silk screen printing method, an intaglio printing method, a gravure printing method, or the like. It is preferably provided on a support.
【００１６】支持体は、インキ組成物と反応せずしかも
試薬の呈色を阻害しないものであることが望ましい。具
体的には、紙、合成紙、不織布または合成樹脂フィルム
等が用いられる。以下、本発明の実施例を述べるが、本
発明はこれに限定されるものではない。The support preferably does not react with the ink composition and does not inhibit the coloration of the reagent. Specifically, paper, synthetic paper, nonwoven fabric, synthetic resin film, or the like is used. Hereinafter, examples of the present invention will be described, but the present invention is not limited thereto.
【００１７】[0017]
【作用】本発明において、インキ組成物中の酸は、乾燥
後色素と接触した形をとるため、未使用時のインジケー
タでは、色素が呈色状態を取っていると考えられる。水
濡れ時には、酸である安息香酸誘導体と色素との相互作
用に水が働きかけ、安息香酸誘導体は水との水素結合や
非解離型へ移行し、一方、色素は呈色のツビッターイオ
ン型からニュートラルの非イオン型へと移行することに
より、インジケータは消色すると推定される。また、色
素の水への溶解性が低いことから、水濡れ後の乾燥過程
で再び安息香酸誘導体と接触することができず、一度消
色した状態が保持されるものと推定される。In the present invention, since the acid in the ink composition is in contact with the dye after drying, it is considered that the dye is in a colored state in the indicator when not used. At the time of water wetting, water acts on the interaction between the acid, a benzoic acid derivative, and the dye, and the benzoic acid derivative shifts to a hydrogen bond or non-dissociated form with water, while the dye changes from a colored zwitter ion form. By transitioning to the neutral non-ionic form, the indicator is presumed to fade. In addition, since the solubility of the dye in water is low, it is presumed that the dye cannot be brought into contact with the benzoic acid derivative again in the drying process after wetting with water, and the state once decolored is maintained.
【００１８】[0018]
＜実施例１＞ 呈色性有機化合物 １部 <Example 1> Color-forming organic compound 1 part
【００１９】[0019]
【化１】 Embedded image
【００２０】 有機酸 アミノ安息香酸 ４部 吸水性粉末 米デンプン １０部 高分子結着剤 ポリエステル樹脂（東洋紡（株）製バイロン＃２００） ５部 トルエン／２−ブタノン（２：１） ４５部Organic acid Aminobenzoic acid 4 parts Water-absorbing powder Rice starch 10 parts Polymer binder Polyester resin (Vylon # 200 manufactured by Toyobo Co., Ltd.) 5 parts Toluene / 2-butanone (2: 1) 45 parts
【００２１】上記組成物を分散機（サンドミル）にて１
時間均一分散し，水分インジケータ用インキ組成物を得
た。これを、厚さ１５０μｍの白色ポリエステルシート
上にワイヤーバーを用いて塗布し、７０℃で１０分間乾
燥して乾燥膜厚１０μｍの記録層を形成して黒色の水分
インジケータシートを作製した。The above composition was dispersed in a dispersing machine (sand mill) for 1 hour.
This was dispersed uniformly over time to obtain an ink composition for a moisture indicator. This was applied on a 150 μm-thick white polyester sheet using a wire bar and dried at 70 ° C. for 10 minutes to form a recording layer having a dry film thickness of 10 μm, thereby producing a black moisture indicator sheet.
【００２２】このシート上に水数滴を滴下した所、その
箇所の黒色が消失した。その後、６０℃で３０分間乾燥
し水分を蒸発させたが、黒色の消失した部分が元の黒色
に戻ることはなかった。また、上記シートを２５℃相対
湿度６０％雰囲下に１週間放置しても湿度の影響を受け
ることなく発色状態を維持し、徐々に消色する傾向は観
察されなかった。When a few drops of water were dropped on this sheet, the black color at that location disappeared. Thereafter, drying was performed at 60 ° C. for 30 minutes to evaporate water, but the portion where the black disappeared did not return to the original black. Further, even if the sheet was left for one week in an atmosphere of 25 ° C. and a relative humidity of 60%, the color-developed state was maintained without being affected by humidity, and no tendency to gradually erase the color was observed.
【００２３】＜実施例２＞ 呈色性有機化合物 １部Example 2 One part of a color-forming organic compound
【００２４】[0024]
【化２】 Embedded image
【００２５】 有機酸 ｔｅｒｔブチル安息香酸 ３部 吸水性粉末 カオリン １０部 高分子結着剤 エチルセルロース（ハーキュレス社製Ｎ−７） １０部 イソプロプルアルコール ７０部 トルエン ２０部Organic acid tert-butyl benzoic acid 3 parts Water-absorbing powder Kaolin 10 parts Polymer binder Ethyl cellulose (N-7 manufactured by Hercules) 10 parts Isopropyl alcohol 70 parts Toluene 20 parts
【００２６】上記組成を分散機（ペイントコンディショ
ナー）にて３０分間粉砕分散して、水分インジケータ用
インキ組成物を作製した。このインキをナイロンスパン
ボンド不織布（旭化成工業（株）製Ｎ５０５１）上にグ
ラビアベタ版（１００μｍ版線）にて印刷、乾燥して青
色ベタパターンの水分インジケータシートを作製した。
このシート上に水数滴を滴下した所、その青色箇所が消
失した。その後、８０℃で１０分間乾燥し水を蒸発させ
たが、青色の消失部分が元の青色に戻ることはなく，ま
た，水滴により流出部分が青色に着色することもなかっ
た。さらに、上記シートを室温雰囲気下に１週間放置し
ても大気中の水分の影響を受けず元の状態が維持でき，
徐々に消色する傾向は観察されなかった。The above composition was pulverized and dispersed by a disperser (paint conditioner) for 30 minutes to prepare an ink composition for a moisture indicator. This ink was printed on a nylon spunbond nonwoven fabric (N5051 manufactured by Asahi Kasei Kogyo Co., Ltd.) using a gravure solid plate (100 μm line) and dried to prepare a blue solid pattern moisture indicator sheet.
When a few drops of water were dropped on this sheet, the blue portion disappeared. Thereafter, drying was performed at 80 ° C. for 10 minutes to evaporate water, but the disappeared blue portion did not return to the original blue color, and the outflow portion was not colored blue by water droplets. Furthermore, even if the above sheet is left in a room temperature atmosphere for one week, the original state can be maintained without being affected by moisture in the air.
No tendency to fade was observed.
【００２７】＜実施例３＞ 呈色性有機化合物 １部<Example 3> Coloring organic compound 1 part
【００２８】[0028]
【化３】 Embedded image
【００２９】 有機酸 アミノサリチル酸 ２部 吸水性粉末 微粉末セルロース １０部 高分子結着剤 ポリメチルメタアクリレート ７．５部 （ロームアンドハウス社製パラロイドＡ−１１） トルエン ５０部Organic acid Aminosalicylic acid 2 parts Water-absorbing powder Fine powdered cellulose 10 parts Polymer binder Polymethyl methacrylate 7.5 parts (Rohm and House Co., Ltd. Paraloid A-11) Toluene 50 parts
【００３０】上記組成物を分散機（サンドミル）にて１
時間均一分散して水分インジケーター用インキ組成物を
得た。これをあらかじめ易接着層（大日本インキ化学工
業（株）製ハイドランＡＰ−４０）を塗布して成る１５
０μｍの白色ポリエステル上にワイヤーバーを用いて塗
布し、７０℃で１０分間乾燥して乾燥膜厚８．５μｍの
記録層を形成して赤色の水分インジケータシートを作製
した。The above composition was dispersed in a disperser (sand mill)
The mixture was uniformly dispersed over time to obtain an ink composition for a moisture indicator. This is formed by applying an easy-adhesion layer (Hydran AP-40 manufactured by Dainippon Ink and Chemicals, Inc.) in advance.
It was applied on a 0 μm white polyester using a wire bar and dried at 70 ° C. for 10 minutes to form a 8.5 μm dry recording layer to produce a red moisture indicator sheet.
【００３１】このシート上に水数滴を滴下した所、その
箇所の赤色呈色が消失した。その後、６０℃で１０分間
乾燥し、水分を蒸発させが、消失した赤色部分が元の呈
色状態に復元することはなかった。また、水滴により赤
色部分が流出したことによる消色でないことは、流失部
分が乾燥後も赤色に着色することがないこと、流失先も
乾燥後に赤色を呈しないこと、更に、滴下した水滴を保
持したまま乾燥しても赤色に復元しないことより確認し
た。When a few drops of water were dropped on this sheet, the red color at that point disappeared. Thereafter, drying was performed at 60 ° C. for 10 minutes to evaporate the water, but the disappeared red portion was not restored to the original color. Also, the fact that the red portion was not erased by the water droplets flowing out of the water droplets means that the spilled portion does not become red even after drying, the spilled portion does not show red after drying, and furthermore, holds the dropped water droplets It was confirmed from the fact that it did not restore red even if dried as it was.
【００３２】また、上記シートを室温雰囲気下に１週間
放置しても大気中の水分の影響を受けず元の状態が維持
でき、徐々に消色する傾向は観察されなかった。Further, even if the above-mentioned sheet was left in a room temperature atmosphere for one week, the original state could be maintained without being affected by moisture in the air, and no tendency to gradually erase the color was observed.
【００３３】[0033]
【発明の効果】以上のように、本発明は水を付着するこ
とにより呈色が消失し、その後、乾燥を施しても元の状
態に復元せず、メモリ−性を有すること、また、室温雰
囲気下、大気中の湿度に抗するため環境保存性が優れて
いる特徴を有していることから従来にない効果を有して
いる。As described above, according to the present invention, the coloration disappears due to the adhesion of water, and the present invention does not restore the original state even after drying, and has a memory property. It has an unprecedented effect because it has a characteristic of being excellent in environmental preservation because it withstands atmospheric humidity under an atmosphere.
───────────────────────────────────────────────────── フロントページの続き (56)参考文献 特開 昭59−184861（ＪＰ，Ａ) 特開 昭60−187860（ＪＰ，Ａ) (58)調査した分野(Int.Cl.7，ＤＢ名) G01N 31/22 G01N 31/00 ────────────────────────────────────────────────── ─── Continuation of front page (56) References JP-A-59-184861 (JP, A) JP-A-60-187860 (JP, A) (58) Fields investigated (Int. Cl. 7 , DB name) G01N 31/22 G01N 31/00
Claims (3)
により発色している呈色性有機化合物、吸水性粉末、お
よび高分子結着剤から成る組成物が非水溶媒中に溶解も
しくは分散されてなり、水に濡れることで消色すること
を特徴とする消色型水分インジケータ用インキ組成物。A composition comprising an organic acid, a color-forming organic compound which has low solubility in water and develops a color due to the presence of the organic acid, a water-absorbing powder, and a polymer binder is non-aqueous. Dissolve or disperse in water solvent and discolor by wetting with water
An ink composition for a decolorizable moisture indicator, comprising:
特徴とする請求項１記載の消色型水分インジケータ用イ
ンキ組成物。2. The ink composition for a decolorizable water indicator according to claim 1, wherein the organic acid is a benzoic acid derivative .
成物を支持体上に塗布してなることを特徴とする消色型
水分インジケータ記録媒体。3. A decolorizable moisture indicator recording medium obtained by applying the ink composition according to claim 1 on a support.