JP3225097B2 - Transfer paper for electrophotography - Google Patents
Transfer paper for electrophotographyInfo
- Publication number
- JP3225097B2 JP3225097B2 JP19540092A JP19540092A JP3225097B2 JP 3225097 B2 JP3225097 B2 JP 3225097B2 JP 19540092 A JP19540092 A JP 19540092A JP 19540092 A JP19540092 A JP 19540092A JP 3225097 B2 JP3225097 B2 JP 3225097B2
- Authority
- JP
- Japan
- Prior art keywords
- paper
- sizing agent
- neutral
- rosin
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【０００１】[0001]
【産業上の利用分野】本発明は、サイズ性と電子写真適
性を改良した電子写真用転写紙に関するものである。更
に詳しくは、サイズ性とトナー定着性、及び重送のすぐ
れた電子写真用転写紙に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an electrophotographic transfer paper having improved size and electrophotographic suitability. More specifically, the present invention relates to an electrophotographic transfer paper excellent in size, toner fixability, and multifeed.
【０００２】[0002]
【従来の技術】近年、填料として炭酸カルシウムの使用
による白色度や不透明度の改良、紙の保存性の向上など
を目的として、電子写真用転写紙を中性抄紙にて製造す
る場合が増してきている。また、正極性トナーを用いる
電子写真方式の複写機においても、ハイバックグランド
（転写工程で感光体に付着した紙粉中の填料が現像部で
現像剤に混入すると、トナーと填料が逆極性の場合、凝
集体が非画線部に現像される）、及びディリーション
（感光体の暗所での電気抵抗の低下により、正常な静電
潜像が得られない）と呼ばれる現象対策として摩擦帯電
列が正極性であり、高湿条件で表面電気抵抗の高い炭酸
カルシウムの使用が提案されている（特公昭６３−４０
３１２号公報、及び特公平２−５４５４３号公報）。2. Description of the Related Art In recent years, the use of calcium carbonate as a filler to improve whiteness and opacity, and to improve the storage stability of paper, and the like, has increased the production of transfer paper for electrophotography using neutral papermaking. ing. Also, in an electrophotographic copying machine using a positive polarity toner, a high background (when the filler in the paper powder adhering to the photoreceptor in the transfer process is mixed into the developer in the developing section, the toner and the filler have opposite polarities) , Aggregates are developed on non-image areas), and triboelectric charging as countermeasures against phenomena called deletion (a normal electrostatic latent image cannot be obtained due to a decrease in electrical resistance of the photoconductor in a dark place). Has a positive polarity, and the use of calcium carbonate having high surface electric resistance under high humidity conditions has been proposed (Japanese Patent Publication No. 63-40 / 1988)
No. 312, and Japanese Patent Publication No. 2-54543).
【０００３】電子写真用転写紙には、筆記特性を中心と
するサイズ性を向上させる目的で内添サイズ剤を用いる
が、従来の酸性ロジンサイズ剤は、中性条件で紙を製造
する際に、酸性雰囲気、かつ硫酸バンドの存在化で性能
を発揮するものの、ロジンの溶出、及び硫酸バンドと炭
酸カルシウムとの競合反応が起こり使用することができ
なかった。[0003] An internal sizing agent is used in electrophotographic transfer paper for the purpose of improving the sizing property mainly on writing characteristics, whereas the conventional acidic rosin sizing agent is used when producing paper under neutral conditions. Although it exhibited its performance in an acidic atmosphere and in the presence of a sulfate band, the rosin was eluted and a competitive reaction between the sulfate band and calcium carbonate occurred, so that it could not be used.
【０００４】これに代わって、一般に中性サイズ剤と呼
ばれる内添サイズ剤が使用されてきた。ここで言う中性
サイズ剤とは、アルキルケテンダイマー（以下、ＡＫＤ
と略す）や、アルケニルコハク酸無水物（以下、ＡＳＡ
と略す）のことを言う。ＡＫＤは、取扱いの容易さ、あ
るいは少量の添加で優れたサイズ性の得られる特徴を生
かし、又、ＡＳＡは、サイズ性の立ち上がりの良好な特
徴を生かして使用されてきた。[0004] Instead of this, an internal sizing agent generally called a neutral sizing agent has been used. The neutral sizing agent referred to herein is an alkyl ketene dimer (hereinafter, AKD)
Abbreviated), alkenyl succinic anhydride (hereinafter, ASA)
Abbreviated). AKD takes advantage of the characteristics of obtaining excellent sizing properties with ease of handling or addition of a small amount, and ASA has been used taking advantage of the characteristics of good rise of sizing properties.
【０００５】しかし、電子写真用転写紙にサイズ剤とし
て、ＡＫＤ、あるいはＡＳＡを使用した場合、サイズ度
を高くする目的でサイズ剤の添加量を増すと紙の表面エ
ネルギーが低下し、電子写真方式の複写機で転写したト
ナーの定着性が悪化する傾向にある。またＡＫＤを使用
して、サイズ度を高くする目的でサイズ剤の添加量を増
すと紙の摩擦係数が低下し紙がスベリ易くなり、結果と
して複写機で重送が発生するという問題があった。これ
らの問題に対する対策として、ＡＫＤあるいはＡＳＡの
添加量の削減、スチレン−ジメチルアミノエーテル（メ
タ）アクリレート−エピハロヒドリン変成物に代表され
るカチオンポリマータイプの中性サイズ剤との併用（特
開昭５５−１３２７８９、及び特開昭５７−１１２４９
７）、及び表面サイズ澱粉塗布量の増加などが試みられ
ている。However, when AKD or ASA is used as a sizing agent for electrophotographic transfer paper, if the amount of the sizing agent added is increased for the purpose of increasing the sizing degree, the surface energy of the paper decreases, and the electrophotographic method , There is a tendency that the fixability of the toner transferred by the copying machine is deteriorated. Also, when the amount of the sizing agent added is increased by using AKD to increase the degree of sizing, the friction coefficient of the paper is reduced, and the paper is liable to slip. As a result, there is a problem that double feeding occurs in a copying machine. . As measures against these problems, reduction of the amount of AKD or ASA added, combined use with a cationic polymer type neutral sizing agent represented by a styrene-dimethylaminoether (meth) acrylate-epihalohydrin modified product (Japanese Patent Application Laid-Open No. 132789, and JP-A-57-11249
7) and an increase in the amount of surface-size starch applied.
【０００６】[0006]
【発明が解決しようとしている課題】サイズ性とトナー
定着性、及び重送のすぐれた電子写真用転写紙を得るた
めに適用できる技術としては、前述のような、ＡＫＤや
ＡＳＡの添加量の削減、カチオンポリマータイプの中性
サイズ剤との併用、及び表面サイズ澱粉塗布量の増加が
ある。しかし、ＡＫＤやＡＳＡの添加量の削減では、ト
ナーの定着性は良好なものの十分なサイズ度の紙は得ら
れない。更に、カチオンポリマータイプの中性サイズ剤
との併用系では損紙の離解性の悪さや蛍光染料の蛍光強
度を低下させるという問題が残る。一方、表面サイズ澱
粉付着量の増加では、紙のカール性が悪化するなど、い
ずれにおいても十分な品質の電子写真用転写紙を得るこ
とはできなかった。As a technique which can be applied to obtain an electrophotographic transfer paper excellent in size, toner fixability and double feeding, reduction of the addition amount of AKD or ASA as described above is known. , A combination with a cationic polymer type neutral sizing agent, and an increase in the amount of surface size starch applied. However, when the amount of AKD or ASA added is reduced, paper having a sufficient degree of sizing cannot be obtained although the fixability of the toner is good. Further, the combined use of the cationic polymer type with a neutral sizing agent has a problem that poor disintegration of broke and a decrease in the fluorescence intensity of the fluorescent dye remain. On the other hand, when the amount of starch adhering to the surface increased, the curl of the paper deteriorated, and transfer paper for electrophotography of sufficient quality could not be obtained in any case.
【０００７】従って、本発明の目的は、中性紙であり、
かつサイズ性とトナー定着性、及び重送のすぐれた電子
写真用転写紙を提供することにある。Accordingly, an object of the present invention is a neutral paper,
Another object of the present invention is to provide an electrophotographic transfer paper excellent in size, toner fixing property, and double feeding.
【０００８】[0008]
【課題を解決するための手段】本発明者は、上記の課題
を解決すべく、中性紙であり、かつサイズ性とトナー定
着性、及び重送のすぐれた電子写真用転写紙について鋭
意検討した結果、填料として炭酸カルシウムを含有し、
内添サイズ剤としてアニオン性の中性ロジンサイズ剤を
用いた場合に、公知の技術では到達できなかったような
顕著なサイズ度、及び電子写真適性が得られることを見
出し、本発明を完成するに至ったものである。In order to solve the above-mentioned problems, the present inventors have intensively studied a transfer paper for electrophotography which is a neutral paper and has excellent size, toner fixability, and multifeed. As a result, containing calcium carbonate as a filler,
It has been found that when an anionic neutral rosin sizing agent is used as an internal sizing agent, a remarkable sizing degree and electrophotographic aptitude that cannot be achieved by known techniques can be obtained, and the present invention is completed. It has been reached.
【０００９】本発明でいう中性ロジンサイズ剤とは、ｐ
Ｈ６〜９の中性領域において使用される各種界面活性剤
もしくは水溶性高分子で乳化してなるエマルジョン型ロ
ジンサイズ剤である。ここで、ロジン物質としては、ガ
ムロジン、ウッドロジン、トール油ロジン、水素化ロジ
ン、不均化ロジン、重合ロジン、アルデヒド変成ロジ
ン、ロジンエステルなどのロジン類、更には該ロジン類
とアクリル酸、無水マレイン酸、フマール酸、イタコン
酸などのα、β−不飽和カルボン酸との加熱反応物を例
示できるが、中性領域でのロジン物質の溶出を抑える目
的で重合、耐水化等の不溶化処理を行なうことができ
る。The neutral rosin sizing agent referred to in the present invention is p
Emulsified rosin sizing agent emulsified with various surfactants or water-soluble polymers used in the neutral region of H6-9. Here, as the rosin substance, gum rosin, wood rosin, tall oil rosin, hydrogenated rosin, disproportionated rosin, polymerized rosin, aldehyde modified rosin, rosin ester and other rosins, furthermore, the rosin and acrylic acid, maleic anhydride Examples of the heat-reacted product with an α, β-unsaturated carboxylic acid such as an acid, fumaric acid, and itaconic acid can be given, but in order to suppress the elution of a rosin substance in a neutral region, polymerization, insolubilization treatment such as water resistance is performed. be able to.
【００１０】中性ロジンサイズ剤のイオン性は、乳化時
に用いる各種界面活性剤もしくは水溶性高分子によりア
ニオン性、カチオン性の選択は可能である。本発明で
は、従来から使用されている各種のアニオン性、ノニオ
ン性、カチオン性あるいは両性の歩留り向上剤、ポリエ
チレンオキサイド、ポリアミド樹脂、親水性架橋ポリマ
ー粒子分散物等又はその誘導体あるいは変成物などとコ
ロイダルシリカ、ベントナイト等の化合物が適宜組み合
わされて使用される歩留りシステムを検討した結果、ア
ニオン性の中性ロジンサイズ剤とカチオン性、あるいは
両性の親水性架橋ポリマー粒子分散物等又はその誘導体
あるいは変成物を構成要素の一つとする歩留り向上剤、
あるいは歩留りシステムを組み合わせた時に顕著なサイ
ズ効果がでる事を確認した。[0010] The ionicity of the neutral rosin sizing agent can be selected from anionic and cationic types depending on various surfactants or water-soluble polymers used during emulsification. In the present invention, various anionic, nonionic, cationic or amphoteric retention enhancers conventionally used, polyethylene oxide, polyamide resin, hydrophilic cross-linked polymer particle dispersion or the like or colloidal with its derivatives or denatured products As a result of examining a retention system in which compounds such as silica and bentonite are used in combination as appropriate, an anionic neutral rosin sizing agent and a cationic or amphoteric hydrophilic crosslinked polymer particle dispersion or a derivative or modified product thereof A yield improver with one of the constituent elements,
Alternatively, it was confirmed that a remarkable size effect was obtained when the yield system was combined.
【００１１】また、中性ロジンサイズ剤のサイズ性を発
現させる目的で、Ａｌの多価金属化合物（例えば、硫酸
バンド、ポリ塩化アルミニウム、ポリアルミニウムシリ
ケートサルフェイト、アルミン酸ソーダなど）を配合す
ることは勿論である。For the purpose of expressing the sizing properties of the neutral rosin sizing agent, a polyvalent metal compound of Al (for example, a sulfate band, polyaluminum chloride, polyaluminum silicate sulfate, sodium aluminate, etc.) is blended. Of course.
【００１２】本発明の中性抄紙でアニオン性の中性ロジ
ンサイズ剤がサイズ性を発現できる機構としては、アニ
オン性のパルプ繊維上にカチオン澱粉等の水溶性カチオ
ン高分子を介してアニオン性の中性ロジンサイズ剤が定
着し、ドライヤー上でアルミニウムイオンと反応するこ
とによりサイズ性が発現するものと推定される。また、
歩留り向上剤は微細繊維に定着したサイズ剤、及び遊離
のサイズ剤などを捕集する効果によりサイズ性を向上さ
せるものと考えられる。The mechanism by which the anionic neutral rosin sizing agent can exhibit sizing properties in the neutral papermaking of the present invention is as follows: the anionic neutral rosin sizing agent is formed on the anionic pulp fiber via a water-soluble cationic polymer such as cationic starch. It is presumed that the neutral rosin sizing agent is fixed and reacts with aluminum ions on the dryer to develop sizing properties. Also,
It is considered that the retention aid improves the sizing property by the effect of collecting the sizing agent fixed to the fine fibers and the free sizing agent.
【００１３】また、本発明では、ロジンサイズ剤の特徴
として、紙中への配合量が増加するとともに、紙の摩擦
係数が増加するため、ＡＫＤを使用した場合に問題にな
ったようなサイズ性向上に伴うスベリは発生せず、これ
に伴い複写機上で転写用紙が複数枚給紙される、いわゆ
る重送問題も解決される。さらに、本発明では中性抄紙
を行なうことにより、填料として炭酸カルシウムを配合
できることから紙の摩擦係数、及びコントロール性の格
段の向上とともに、従来、相反する特性であったハイバ
ックグランド、及びディリーションと呼ばれる現象問題
も同時に解決しうる。In the present invention, the rosin sizing agent is characterized in that the amount of rosin compounded in the paper increases and the coefficient of friction of the paper increases. No sliding occurs due to the improvement, and the so-called double feeding problem in which a plurality of transfer sheets are fed on a copying machine is solved. Furthermore, in the present invention, by performing neutral papermaking, calcium carbonate can be blended as a filler, so that the coefficient of friction of the paper, and the controllability are significantly improved, and, in the past, the high background, which had contradictory characteristics, and the release. The so-called phenomenon problem can be solved at the same time.
【００１４】また、本発明に使用されるパルプとして
は、ＮＢＫＰ、ＬＢＫＰ、ＮＢＳＰ、ＬＢＳＰ、ＧＰ、
ＴＭＰなどの他に古紙パルプが挙げられる。使用に当た
っては、それらを数種類目的に応じた比率で混合して用
いる。全パルプ中の古紙パルプの混合比率は、電子写真
複写機の転写後のカール対策から４０％以下が好まし
い。The pulp used in the present invention includes NBKP, LBKP, NBSP, LBSP, GP,
Waste paper pulp may be used in addition to TMP. In use, they are mixed and used at a ratio according to several purposes. The mixing ratio of waste paper pulp in the whole pulp is preferably 40% or less from the viewpoint of curling after transfer by an electrophotographic copying machine.
【００１５】なお、本発明で言う古紙パルプの原料とし
ては、（財）古紙再生促進センターの古紙標準品質規格
表に示されている、上白、罫白、クリーム白、カード、
特白、中白、模造、色白、ケント、白アート、特上切、
別上切、新聞、雑誌等が挙げられる。更に具体例として
は、情報関連用紙である非塗工コンピュータ用紙、感熱
紙、感圧紙などのプリンター用紙、及びＰＰＣ用紙等の
ＯＡ古紙、アート紙、コート紙、微塗工紙、マット紙等
の塗被紙、あるいは上質紙、色上質、ノート、便箋、包
装紙、ファンシーペーパー、中質紙、新聞用紙、更紙、
スーパー掛け紙、模造紙、純白ロール紙、ミルクカート
ン等の非塗被紙等の紙や板紙の古紙で、化学パルプ紙、
高歩留りパルプ含有紙等が使用されるが、印字、複写、
印刷、非印刷を問わず特に限定されるものではない。The raw materials for waste paper pulp referred to in the present invention include: top white, ruled white, cream white, card, and the like shown in the waste paper standard quality standard table of the Waste Paper Recycling Promotion Center.
Special white, medium white, imitation, fair white, Kent, white art, special top cut,
Other examples include newspapers and magazines. Further specific examples include information-related papers such as uncoated computer papers, thermal papers, printer papers such as pressure-sensitive papers, and OA waste papers such as PPC papers, art papers, coated papers, lightly coated papers, mat papers and the like. Coated paper or high quality paper, color high quality, notebook, stationery, wrapping paper, fancy paper, medium quality paper, newsprint, paper change,
Used paper such as super coated paper, imitation paper, pure white roll paper, uncoated paper such as milk carton and paperboard, chemical pulp paper,
High yield pulp-containing paper is used, but printing, copying,
There is no particular limitation on printing or non-printing.
【００１６】また、古紙パルプは一般的に、 （１）離解……古紙をパルパーにて機械力と薬品で処理
して繊維状にほぐし、印刷インキを繊維より剥離する。 （２）除塵……古紙に含まれる異物（プラスチックな
ど）及びゴミをスクリーン、クリーナー等により除去す
る。 （３）脱墨……繊維より界面活性剤を用いて剥離された
印刷インキをフローテーション法、または洗浄法で系外
に除去する。 （４）漂白……酸化作用や還元作用を用いて、繊維の白
色度を高める。 の４工程の組み合わせから作られる。In addition, waste paper pulp is generally (1) disintegrated .... The waste paper is treated with a mechanical force and a chemical by a pulp to loosen it into a fibrous form, and the printing ink is peeled from the fiber. (2) Dust removal: Foreign matter (such as plastic) and dust contained in the used paper are removed by a screen, a cleaner, or the like. (3) Deinking: The printing ink removed from the fiber using a surfactant is removed out of the system by a flotation method or a washing method. (4) Bleaching: The degree of whiteness of the fiber is increased by using an oxidizing action or a reducing action. It is made from a combination of the four steps.
【００１７】また、本発明の電子写真用転写紙は、サイ
ズプレス工程で成紙の表面に澱粉、ポリビニールアルコ
ール、ラテックス、無水マレイン酸系サイズ、α−オレ
フィン系サイズ、スチレン−アクリル酸系等の各種の表
面サイズ剤、エチレン−尿素樹脂等の寸法安定化剤、塩
化ナトリウム、塩化カリウム等の無機導電剤、有機導電
剤、界面活性剤、顔料、染料を塗布するが、サイズプレ
ス工程で塗抹する方式としては、コンベンショナルサイ
ズプレス、ゲートロールサイズプレス、あるいはメタリ
ングブレード方式のサイズプレス、ビルブレード、ショ
ートドウェルコーター等の装置を用いることは勿論可能
である。Further, the transfer paper for electrophotography of the present invention is obtained by applying a starch, polyvinyl alcohol, latex, maleic anhydride type size, α-olefin type size, styrene-acrylic acid type, etc. Apply various surface sizing agents, dimensional stabilizers such as ethylene-urea resin, inorganic conductive agents such as sodium chloride and potassium chloride, organic conductive agents, surfactants, pigments and dyes. As a method for carrying out the method, it is of course possible to use a device such as a conventional size press, a gate roll size press, a size press of a metering blade system, a bill blade, a short dwell coater and the like.
【００１８】紙料中にはこの他に、本発明の所望の効果
を損なわない範囲で、従来から使用されている前述のよ
うな歩留り向上剤、各種のアニオン性、ノニオン性、カ
チオン性あるいは両性のろ水向上剤、紙力向上剤や内添
サイズ剤等の抄紙用内添助剤が必要に応じて適宜選択し
て使用される。例えば、各種澱粉、及びポリアクリルア
ミド、ポリエチレンイミン、ポリアミン、ポリアミド・
ポリアミン、尿素ホルマリン樹脂、メラミンホルマリン
樹脂、植物ガム、ポリビニールアルコール、ラテック
ス、ポリエチレンオキサイド、ポリアミド樹脂の内の１
種あるいは２種以上が適宜組み合わされて使用される。In the paper stock, other than the above, the above-mentioned retention improvers, various anionic, nonionic, cationic or amphoteric substances which have been conventionally used may be used as long as the desired effects of the present invention are not impaired. An internal additive for papermaking such as a drainage improver, a paper strength improver and an internal sizing agent is appropriately selected and used as needed. For example, various starches, polyacrylamide, polyethyleneimine, polyamine, polyamide
1 of polyamine, urea formalin resin, melamine formalin resin, vegetable gum, polyvinyl alcohol, latex, polyethylene oxide, polyamide resin
Species or two or more kinds are used in appropriate combination.
【００１９】なお、染料、ｐＨ調節剤、消泡剤、ピッチ
コントロール剤、スライムコントロール剤等の抄紙用内
添助剤を目的に応じて適宜添加することも可能である。It is also possible to appropriately add an internal additive for papermaking such as a dye, a pH adjuster, an antifoaming agent, a pitch control agent and a slime control agent according to the purpose.
【００２０】本発明の抄紙方法については、抄紙ｐＨが
６〜９の中性抄紙に限定されるが、抄紙機は、長網抄紙
機、ツインワイヤー抄紙機、コンビネーション抄紙機、
丸網抄紙機、ヤンキー抄紙機等を適宜使用できる。The papermaking method of the present invention is limited to neutral papermaking at a papermaking pH of 6 to 9, but papermaking machines include fourdrinier paper machines, twin wire paper machines, combination paper machines,
A round mesh paper machine, a Yankee paper machine or the like can be used as appropriate.
【００２１】[0021]
【作用】本発明で規定したように、填料として、炭酸カ
ルシウムを含有し、内添サイズ剤としてアニオン性中性
ロジンサイズ剤を含有した中性紙を抄造することによ
り、ｐＨ６〜９の中性領域においても、ロジンの溶出が
最小限に抑えられ、従来の歩留りシステムを用いても十
分なサイズ性を得ることができる。また、ロジンサイズ
剤は紙の表面エネルギーを低下させることが無いので、
トナーの定着性に優れるとともに、摩擦係数の減少によ
る複写機上の走行性の問題である重送が改善される。As described in the present invention, neutral paper containing calcium carbonate as a filler and an anionic neutral rosin sizing agent as an internal sizing agent is formed into a paper having a neutral pH of 6 to 9. Also in the region, elution of rosin is minimized, and sufficient sizing can be obtained even with a conventional yield system. Also, since rosin sizing agents do not lower the surface energy of paper,
In addition to excellent toner fixability, double feeding, which is a problem of running property on a copying machine due to a decrease in friction coefficient, is improved.
【００２２】[0022]
【実施例】以下に実施例を示し本発明を詳細に説明す
る。なお、本発明はこれに限定されるものではない。以
下における部、％はすべて重量によるものである。The present invention will be described in detail below with reference to examples. Note that the present invention is not limited to this. All parts and percentages in the following are by weight.
【００２３】実施例１ １．原紙配合； ＬＢＫＰ（ろ水度；３５０ｍｌ、ｃ．ｓ．ｆ） ７０部 ＮＢＫＰ（ろ水度；４００ｍｌ、ｃ．ｓ．ｆ） ３０部 炭酸カルシウム（奥多摩工業製；ＴＰ−１２１） １０部 アニオン性中性ロジンサイズ剤（荒川化学社製；ＫＳ−７６７） １部 硫酸バンド １部 両性澱粉（王子ナショナル社製；Ｃａｔｏ３２１０） １部 歩留り向上剤（ハイモ社製；ＮＲ−１１ＬＳ） ０．０２部 上記配合の０．３％スラリーを抄幅１，３００ｍｍ、抄
紙速度１５０ｍ／ｍｉｎ．で長網抄紙機により６４ｇ／
ｍ2の原紙の抄造を行なった。この原紙に、以下の配合
でサイズプレスを行ない、固形分付着量１．２ｇ／ｍ2
の電子写真用転写紙を得た。 ２．サイズプレス液配合； 酸化澱粉（日本食品加工社製；ＭＳ−３８００） ５部 塩化ナトリウム ０．１５部スチレン -アクリル酸系表面サイズ剤（荒川化学社製；ポリマロン１３０８Ｓ） ０．１５部 水 ９４．７０部Embodiment 1 1. LBKP (freeness: 350 ml, csf) 70 parts NBKP (freeness: 400 ml, csf) 30 parts Calcium carbonate (Okutama Kogyo; TP-121) 10 parts Anionic Neutral rosin sizing agent (Arakawa Chemical Co., Ltd .; KS-767) 1 part Sulfuric acid band 1 part Amphoteric starch (Oji National Co., Ltd .; Cato3210) 1 part Yield improver (Himo Co., Ltd .; NR-11LS) 0.02 part A 0.3% slurry with a blending width of 1,300 mm and a papermaking speed of 150 m / min. With a Fourdrinier paper machine at 64g /
It was carried out papermaking of m 2 of the base paper. The base paper was subjected to a size press with the following composition to obtain a solid content of 1.2 g / m 2.
Was obtained. 2. Compounding of a size press solution; oxidized starch (manufactured by Nippon Shokuhin Kabushiki Kaisha; MS-3800) 5 parts Sodium chloride 0.15 part Styrene-acrylic acid-based surface sizing agent (Arakawa Chemical Co .; polymalon 1308S) 0.15 parts Water 94. 70 copies
【００２４】上記の電子写真用転写紙の用紙特性は、Ａ
４判縦目にて裁断されたサンプルで以下の方法にて評価
を行なった。 １．ステキヒトサイズ度；ステキヒトサイズ度はＪＩＳ
Ｐ−８１１２に準じて測定を行なった。電子写真用転
写紙においては上質紙同様に、坪量６４ｇ／ｍ2の場合
１８秒以上のサイズ性が必要とされている。 ２．静摩擦係数；静摩擦係数はＪＩＳ Ｐ−８１４７に
準じて、測定を行なった。本評価では紙の組み合わせと
して、表と裏、横と横を用いた。電子写真用転写紙にお
いては、静摩擦係数として、０．４５〜０．７５が望ま
しい値とされている。The paper characteristics of the above electrophotographic transfer paper are as follows.
The samples cut in the 4th dimension were evaluated by the following method. 1. Stigecht sizing degree;
The measurement was performed according to P-8112. Electrophotographic transfer paper requires a size of 18 seconds or more in the case of a basis weight of 64 g / m 2 , similarly to high quality paper. 2. Static friction coefficient: The static friction coefficient was measured according to JIS P-8147. In this evaluation, front and back, side and side were used as combinations of paper. For electrophotographic transfer paper, a desirable value of the static friction coefficient is 0.45 to 0.75.
【００２５】上記の電子写真用転写紙の電子写真適性
は、シャープ社製の電子写真式複写機（ＳＦ−９４０
０）を用いてＡ４判縦目にて裁断されたサンプルで以下
の方法にて評価を行なった。 １．トナー定着性；上記複写機にて複写した光学濃度が
約１．４の画像部に、市販の１８ｍｍ幅セロハン粘着テ
ープ（ニチバン社製；セロテープ）を３００ｇ／ｃｍの
線圧で貼り付け、１ｃｍ／ｓｅｃ．の速度で剥離した際
の、剥離前の画像濃度に対する剥離後の画像濃度の比
（以下、ＯＤ比と略す）を指標として評価した。 ＯＤ比＝剥離後の画像濃度／剥離前の画像濃度 電子写真用転写紙としては、ＯＤ比で０．７以上のトナ
ー定着性が必要とされている。なお、画像濃度の測定に
はマクベス反射型濃度計（Ｍａｃｂｅｔｈ社製；ＲＤ−
９１８）を使用した。 ２．重送；Ａ４判の紙を抄紙と直角方向（ＣＤ方向）に
２，５００枚片面通紙した時の、重送の発生枚数で評価
した。電子写真用転写紙としては、７枚以下が必要とさ
れている。 ３．カール；Ａ４判の紙をＣＤ方向に通紙して片面複写
をした後、カール面を上にして平らな台の上に置き、四
隅の中で最も台の面より高い値を測定し、１０枚の平均
値で評価した。電子写真用転写紙としては、３ｍｍ以下
が望ましい。The electrophotographic transfer paper described above is suitable for electrophotography using an electrophotographic copying machine (SF-940) manufactured by Sharp Corporation.
0) was evaluated by the following method using a sample cut in an A4 size square. 1. Toner fixing property: A commercially available 18 mm-wide cellophane adhesive tape (Nichiban; cellophane tape) was adhered to an image portion having an optical density of about 1.4 copied by the above copying machine at a linear pressure of 300 g / cm and 1 cm / cm sec. The evaluation was performed using the ratio of the image density after peeling to the image density before peeling (hereinafter abbreviated as OD ratio) when peeling at a speed of as an index. OD ratio = image density after peeling / image density before peeling The electrophotographic transfer paper is required to have a toner fixing property with an OD ratio of 0.7 or more. The image density was measured using a Macbeth reflection densitometer (manufactured by Macbeth; RD-
918) was used. 2. Double feed: Evaluation was made based on the number of double feeds when 2,500 sheets of A4 size paper were passed on one side in a direction perpendicular to the papermaking (CD direction). Seven or less electrophotographic transfer papers are required. 3. Curl: A4 size paper is passed in the CD direction to make a single-sided copy, then placed on a flat table with the curled side up, and the highest value among the four corners is measured. Evaluation was made based on the average value of the sheets. The transfer paper for electrophotography is desirably 3 mm or less.
【００２６】実施例２ 実施例１で歩留り向上剤として、コロイダルシリカ（エ
カ社製；ＢＭＡ）を０．１部とした以外は同様にしてサ
ンプルを調整し、実施例２とした。Example 2 A sample was prepared in the same manner as in Example 1, except that 0.1 parts of colloidal silica (manufactured by Eka; BMA) was used as a retention aid in Example 1.
【００２７】実施例３ 実施例１で歩留り向上剤として、カチオン性ポリアクリ
ルアミド（アライト゛コロイト゛社製；パーコール４７）０．０３
部、ベントナイト（アライト゛コロイト゛社製；ハイト゛ロコールO）０．
１部とした以外は同様にしてサンプルを調整し、実施例
３とした。Example 3 In Example 1, cationic polyacrylamide (manufactured by Allite Coroit; Percoll 47) as a retention aid was 0.03.
Part, bentonite (manufactured by Alite Koroit Co., Ltd .; Hytorocoll O)
A sample was prepared in the same manner as in Example 3, except that one part was used.
【００２８】実施例４ 実施例１でアニオン性中性ロジンサイズ剤を２．０部と
した以外は同様にしてサンプルを調整し、実施例４とし
た。Example 4 A sample was prepared in the same manner as in Example 1 except that the amount of the anionic neutral rosin sizing agent was changed to 2.0 parts.
【００２９】実施例５ 実施例１で原紙のＬＢＫＰを４０部、ＮＢＫＰを２０
部、模造古紙パルプを４０部、アニオン性中性ロジンサ
イズ剤を１．２部とした以外は同様にしてサンプルを調
整し、実施例５とした。Example 5 In Example 1, 40 parts of base paper LBKP and 20 parts of NBKP were used.
, A sample was prepared in the same manner as in Example 5 except that the amount of the imitation waste paper pulp was 40 parts and the amount of the anionic neutral rosin sizing agent was 1.2 parts.
【００３０】実施例６ 実施例１で原紙のＬＢＫＰを４０部、ＮＢＫＰを２０
部、新聞古紙パルプを２０部、模造古紙パルプを２０
部、アニオン性中性ロジンサイズ剤を１．５部とした以
外は同様にしてサンプルを調整し、実施例６とした。Example 6 In Example 1, 40 parts of base paper LBKP and 20 parts of NBKP were used.
Copies, 20 copies of used newspaper pulp and 20 copies of imitation used pulp
A sample was prepared in the same manner as in Example 6, except that the amount of the anionic neutral rosin sizing agent was changed to 1.5 parts.
【００３１】実施例７ 実施例１で原紙のＬＢＫＰを３０部、ＮＢＫＰを１０
部、色上古紙パルプを６０部、アニオン性中性ロジンサ
イズ剤を１．５部とした以外は同様にしてサンプルを調
整し、実施例７とした。Example 7 In Example 1, 30 parts of base paper LBKP and 10 parts of NBKP were used.
, A sample was prepared in the same manner as in Example 7, except that the amount of used pulp was 60 parts and the amount of anionic neutral rosin sizing agent was 1.5 parts.
【００３２】比較例１ 実施例１で内添サイズ剤をアニオン性中性ロジンサイズ
剤からＡＫＤ０．１５部とした以外は同様にしてサンプ
ルを調整し、比較例１とした。Comparative Example 1 A sample was prepared in the same manner as in Example 1 except that the internal sizing agent was changed from an anionic neutral rosin sizing agent to AKD 0.15 parts.
【００３３】比較例２ 実施例１で内添サイズ剤をアニオン性中性ロジンサイズ
剤からＡＫＤ０．０８部とした以外は同様にしてサンプ
ルを調整し、比較例２とした。Comparative Example 2 A sample was prepared in the same manner as in Example 1 except that the internal sizing agent was changed from an anionic neutral rosin sizing agent to 0.08 parts of AKD.
【００３４】比較例３ 実施例１で内添サイズ剤をアニオン性中性ロジンサイズ
剤からＡＳＡ０．１２部とした以外は同様にしてサンプ
ルを調整し、比較例３とした。Comparative Example 3 A sample was prepared in the same manner as in Example 1 except that the internal sizing agent was changed from an anionic neutral rosin sizing agent to 0.12 parts of ASA.
【００３５】比較例４ 実施例４でアニオン性中性ロジンエマルジョンサイズ剤
をカチオン性中性ロジンエマルジョンサイズ剤（テ゛ィックハ
ーキュレス社製；Ｃ−１０）とした以外は同様にしてサンプ
ルを調整し、比較例４とした。Comparative Example 4 A sample was prepared in the same manner as in Example 4 except that the anionic neutral rosin emulsion sizing agent was changed to a cationic neutral rosin emulsion sizing agent (C-10, manufactured by Dick Hercules). Example 4 was used.
【００３６】比較例５ 実施例１で填料を炭酸カルシウムからインドネシアクレ
ー（P.T.ALTER ABADI社製；BRU-30）とした以外は同様
にしてサンプルを調整し、比較例５とした。Comparative Example 5 A sample was prepared in the same manner as in Example 1 except that the filler was changed from calcium carbonate to Indonesian clay (manufactured by PTALTER ABADI; BRU-30).
【００３７】比較例６ 実施例１で填料を炭酸カルシウムからタルク（兵庫クレ
ー社製、兵庫タルク）とした以外は同様にしてサンプル
を調整し、比較例６とした 。Comparative Example 6 A sample was prepared in the same manner as in Example 1 except that the filler was changed from calcium carbonate to talc (manufactured by Hyogo Clay Co., Hyogo Talc).
【００３８】以上の結果を表１にまとめて示した。The above results are summarized in Table 1.
【００３９】[0039]
【表１】 [Table 1]
【００４０】[0040]
【発明の効果】表１から明らかな様に、本発明は、填料
として、炭酸カルシウムを含有し、内添サイズ剤として
アニオン性中性ロジンサイズ剤を含有した中性紙を抄造
することにより、原紙サイズ性、及びトナーの定着性に
優れるとともに、複写機上の重送が改善された電子写真
用転写紙を製造する事が可能となる。As is evident from Table 1, the present invention provides a neutral paper containing calcium carbonate as a filler and an anionic neutral rosin sizing agent as an internal sizing agent. It is possible to manufacture an electrophotographic transfer paper which is excellent in base paper sizing properties and toner fixing properties and has improved double feeding on a copying machine.
───────────────────────────────────────────────────── フロントページの続き (58)調査した分野(Int.Cl.7，ＤＢ名) G03G 7/00 101 D21H 17/62 ──────────────────────────────────────────────────続 き Continued on the front page (58) Field surveyed (Int. Cl. 7 , DB name) G03G 7/00 101 D21H 17/62
Claims (2)
かつ内添サイズ剤としてアニオン性中性ロジンサイズ剤
を含有した中性紙であることを特徴とする電子写真用転
写紙。1. A filler containing calcium carbonate as a filler,
And a neutral paper containing an anionic neutral rosin sizing agent as an internal sizing agent.
とを特徴とする請求項１記載の電子写真用転写紙。2. The transfer paper for electrophotography according to claim 1, wherein the neutral paper contains waste paper pulp.