JPH10305656A - Information-recording paper - Google Patents

Abstract

PROBLEM TO BE SOLVED: To obtain an information-recording paper having both xerography suitability and ink-jet suitability, by adding a specific amount of an inorganic filler into a supporting body, applying a water-soluble substance including a cationic polymer to both faces of the supporting body, and holding a Stoeckigt sizing degree in a specific range. SOLUTION: A cationic polymer is applied to a front face by a sizing press of a paper machine. A blend ratio of an inorganic filler is set to be 10-20 wt.%. A Stoeckigt sizing degree is adjusted in a range of 10-40 seconds. Although a mechanical pulp(MP) is blended by 10-40 wt.% of pulp components into a supporting body, the paper exhibits superior image quality and run smoothness to suit xerography. Moreover, the paper limits ink not to ooze much and has good drying characteristics as ink-jet suitability.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【産業上の利用分野】本発明は、ゼログラフィー方式や
インクジェット方式の画像印字装置に使用される情報記
録用紙に関し、特に環境保全に有利なメカニカルパルプ
（ＭＰ）を含有し、しかも優れたゼログラフィー適性と
インクジェット適性を併せもつ情報記録用紙に係る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an information recording paper used in an xerographic or ink-jet type image printing apparatus, and more particularly to an excellent xerographic containing mechanical pulp (MP) which is advantageous for environmental protection. The present invention relates to information recording paper having both suitability and inkjet suitability.

【０００２】[0002]

【従来の技術】近年、コンピューターやワードプロセッ
サーなどの普及によりオフィスやパーソナル向けにイン
クジェット方式を用いた画像印字装置が急速な成長を遂
げ、産業界においても一般的になりつつある。これによ
り、オフィスなどではゼログラフィー方式、インクジェ
ット方式など複数の画像印字装置が設置されており、ユ
ーザーはこれらの各機種に対応する記録用紙をそれぞれ
用意して使用していた。しかし、最近ではユーザーの利
便性を考慮して、ゼログラフィー方式、インクジェット
方式の両方式に適用出来る新規な情報記録用紙が求めら
れている。2. Description of the Related Art In recent years, with the spread of computers, word processors, and the like, image printing apparatuses using the ink jet system for offices and personal computers have rapidly grown, and are becoming popular in the industrial world. Accordingly, in an office or the like, a plurality of image printing apparatuses such as a xerographic system and an inkjet system are installed, and a user prepares and uses recording paper corresponding to each of these models. However, recently, in consideration of user's convenience, a new information recording paper applicable to both the xerography method and the ink jet method has been demanded.

【０００３】一方、資源保護、環境保全などの立場か
ら、特開平３−２４３９５３、特開平３−２８７８９
５、特開平４−８２９９１、特開平４−１８１８８など
で新聞古紙を主体とした古紙パルプを使用し、ゼログラ
フィー方式の画像印字装置に使用できる情報記録用紙の
検討がなされているが、インクジェット方式の画像形成
装置を同時に満足させることについては未検討の状況に
ある。On the other hand, from the standpoint of resource protection and environmental protection, Japanese Patent Application Laid-Open Nos.
5, Japanese Patent Application Laid-Open Nos. 4-82991, 4-18188, and the like have been studying information recording paper that can be used in a xerographic image printing apparatus using waste paper pulp mainly composed of newspaper waste paper. It is not yet studied to satisfy the above image forming apparatuses at the same time.

【０００４】一般的に、インクジェットプリンタに使用
されるインクは、水をベースに水溶性の酸性染料、直接
染料などの着色剤や、湿潤剤としてグリコール類やアル
コール、助剤にｐＨ調整剤やキレート剤、ヌレ性の改善
に界面活性剤などが使用されており、アニオン性の性質
を有するところから陽電化を帯びたカチオン性サイズ剤
との定着性は良い。しかし、化学的処理が施されていな
いメカニカルパルプ（ＭＰ）は、セルロース以外に、剛
直で太いヘミセルロースやリグニンなどのアニオン性物
質を多く含有しており、化学的にも不安定である。この
ＭＰは、パルプのほとんどが細かくフィブリル化され、
比表面積の大きいセルロース繊維で形成されているケミ
カルパルプ（ＣＰ）と比較してサイズ剤の定着性が悪
い。そのため、メカニカルパルプ（ＭＰ）を配合した用
紙をインクジェット方式の画像印字装置で印字した際に
は、インクが紙面上に留まらず、剛直で太い繊維に沿っ
て流れ出し、フェザリングと呼ばれるひげ状のインク滲
みが多発する傾向にある。In general, inks used in ink-jet printers include water-based colorants such as water-soluble acid dyes and direct dyes, glycols and alcohols as wetting agents, pH adjusters and chelates as auxiliaries. A surfactant and the like are used for improving the agent and wetting properties, and since it has an anionic property, it has good fixability to a cationic sizing agent having a positive charge. However, mechanical pulp (MP) that has not been subjected to chemical treatment contains a large amount of anionic substances such as hemicellulose and lignin that are rigid and thick in addition to cellulose, and is chemically unstable. In this MP, most of the pulp is finely fibrillated,
The fixing property of the sizing agent is poor as compared with chemical pulp (CP) formed of cellulose fibers having a large specific surface area. Therefore, when paper containing mechanical pulp (MP) is printed by an ink jet image printing device, the ink does not stay on the paper surface but flows out along rigid and thick fibers, forming a beard-like ink called feathering. Bleeding tends to occur frequently.

【０００５】従来、メカニカルパルプ（ＭＰ）を配合し
た用紙に対しては、ＰＶＡやデンプンなどの表面サイズ
剤を多く塗布して前記の不具合を減殺しようとする方法
が採られてきたが、上記のフェザリングは改善されるも
のの、この方法の欠点としてインクの吸収性低下による
乾燥性の悪化や、製造時に抄紙機のドライヤーパートで
キャンバスが汚染するという問題が生じていた。また、
サイズ剤の添加量を少なくすれば、インクが用紙内部に
速く浸透するため、乾燥性やフェザリングは解消される
が、印字濃度が低く、裏抜けが発生しやすくなると同時
に横方向にも拡がるので、ラインや文字が太くなり解像
度が低下するという問題があった。かかる状況から、メ
カニカルパルプ（ＭＰ）を配合した用紙で、ゼログラフ
ィー適性とインクジェット適性を併せもつ用紙の開発は
困難であった。Conventionally, a method has been adopted in which a large amount of a surface sizing agent such as PVA or starch is applied to paper containing mechanical pulp (MP) to reduce the above-mentioned problems. Although feathering is improved, disadvantages of this method include a problem that drying properties are deteriorated due to a decrease in ink absorbency, and that canvas is contaminated by a dryer part of a paper machine during production. Also,
If the amount of the sizing agent is reduced, the ink quickly penetrates into the paper, eliminating the drying property and feathering.However, the print density is low, strike-through easily occurs, and the ink spreads in the horizontal direction. However, there has been a problem that lines and characters become thicker and the resolution is reduced. Under such circumstances, it has been difficult to develop a paper containing mechanical pulp (MP) and having both xerographic suitability and ink jet suitability.

【０００６】これを要するにメカニカルパルプ（ＭＰ）
を配合する際、配合率が概ね１０重量％未満であれば、
従来技術でも表面サイズ剤の塗布量増加などにより改善
可能であったが、配合率が１０重量％を上廻ると剛直で
太いヘミセルロース繊維やリグニンが多くなり、フェザ
リングが発生しやすくなるという問題が生じていた。[0006] In short, mechanical pulp (MP)
When compounding, if the compounding ratio is generally less than 10% by weight,
In the prior art, it could be improved by increasing the amount of the surface sizing agent applied. However, if the mixing ratio exceeds 10% by weight, rigid and thick hemicellulose fibers and lignin increase and feathering tends to occur. Had occurred.

【０００７】[0007]

【発明が解決しようとする課題】本発明者等は前記のメ
カニカルパルプを相当量含有し、ゼログラフィー方式と
インクジェット方式に共用でき、しかもゼログラフィー
適性としての優れた画質と走行性を持ち、かつ、インク
ジェット適性においても、インクの滲みが少なく、乾燥
性の良い用紙を開発するべく検討を重ねた結果、カチオ
ン性ポリマーの添加と填料の配合を工夫することにより
従来の欠点を改善する方法を見出した。SUMMARY OF THE INVENTION The inventors of the present invention contain a considerable amount of the above-mentioned mechanical pulp and can be used for both xerographic and ink jet systems, and have excellent image quality and running properties as xerographic aptitude, and As a result of repeated studies to develop paper with good ink drying and low ink bleeding even in ink jet suitability, we found a method to improve the conventional disadvantages by adding a cationic polymer and blending fillers. Was.

【０００８】[0008]

【課題を解決する手段】本発明は、ゼログラフィー方式
やインクジェット方式の画像印字装置に使用される情報
記録用紙であり、環境保全に有利なメカニカルパルプ
（ＭＰ）を含有しながら、優れたゼログラフィー適性と
インクジェット適性を併せもつ情報記録用紙を提供せん
としたものである。すなわち、本発明は、カチオン性ポ
リマーを抄紙機のサイズプレスで表面塗工し、さらに填
料の配合率を１０〜２０重量％になし、その上ではステ
キヒトサイズ度を１０〜４０秒の範囲に調整することに
より、相当量のメカニカルパルプ（ＭＰ）を配合したに
もかかわらず、前記した従来の欠点を改善して、優れた
ゼログラフィー適性とインクジェット適性を併用する情
報記録用紙を提供し得るようにしたものである。SUMMARY OF THE INVENTION The present invention relates to an information recording paper for use in an xerographic or ink-jet type image printing apparatus. It is an object of the present invention to provide information recording paper having both suitability and ink jet suitability. That is, in the present invention, the cationic polymer is surface-coated by a size press of a paper machine, and the compounding ratio of the filler is reduced to 10 to 20% by weight. By adjusting, despite the fact that a considerable amount of mechanical pulp (MP) is blended, it is possible to improve the above-mentioned conventional drawbacks and to provide an information recording paper which combines excellent xerographic suitability and ink jet suitability. It was made.

【０００９】[0009]

【発明の実施の形態】以下、本発明の具体的な構成につ
いて説明する。まず、本発明にいうＭＰについて述べる
と、このＭＰは木材またはチップを機械的にパルプ化し
たグランドパルプ（ＧＰ）、木材またはチップに薬品を
染み込ませた後、機械的にパルプ化したケミグランドパ
ルプ（ＣＧＰ）、ケミメカニカルパルプ（ＣＭＰ）、お
よびチップを柔らかくなるまで蒸解した後、リファイナ
ーでパルプ化したセミメカニカルパルプなどで代表され
るメカニカルパルプ（ＭＰ）をいい、それ以外に古紙パ
ルプ（ＤＩＰ）からくるメカニカルパルプ（ＭＰ）を含
むもので、その種類は特に限定されない。また、前記Ｍ
Ｐに対してクラフトパルプ（ＫＰ）などの化学パルプ
（ＣＰ）が配合されていても差し支えなく、要するに全
パルプ成分中１０〜４０重量％のＭＰが配合されていれ
ばよい。DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, a specific configuration of the present invention will be described. First, the MP according to the present invention will be described. This MP is ground pulp (GP) obtained by mechanically pulping wood or chips, or chemically ground pulp obtained by impregnating wood or chips with a chemical and then mechanically pulping. (CGP), mechanical pulp (CMP), and mechanical pulp (MP) typified by semi-mechanical pulp obtained by pulverizing chips to be softened and then pulping with a refiner, and waste paper pulp (DIP) It contains mechanical pulp (MP) coming from the plant, and its type is not particularly limited. In addition, the M
Chemical pulp (CP) such as kraft pulp (KP) may be blended with P. In short, MP may be blended in an amount of 10 to 40% by weight of all pulp components.

【００１０】なお、本発明に使用される古紙パルプの原
料としては、（財）古紙再生促進センターの古紙標準規
格表に記載されている上白、罫白、クリーム白、カー
ド、特白、中白、模造、色白、ケント、白アート、特上
切、新聞、雑誌などを挙げることができる。さらに、具
体例としては、情報関連用紙である非塗工コンピュータ
用紙、感熱紙、感圧紙などのプリンター用紙およびＰＰ
Ｃ用紙などのＯＡ古紙、アート紙、コート紙、微塗工
紙、マット紙などの塗被紙、あるいは上質紙、色上質、
ノート、便箋、包装紙、ファンシーペーパー、中質紙、
新聞紙、更紙、スーパー掛け紙、模造紙、純白ロール
紙、ミルクカートンなどや板紙の古紙で、化学パルプ
紙、高歩留パルプ含有紙などが使用されるが、印字、複
写、非印刷を問わず、すべて使用でき、特に限定される
ものではない。[0010] The raw materials of the used paper pulp used in the present invention include the above-mentioned white, ruled white, cream white, card, special white, medium white and the like described in the used paper standard specification table of the Used Paper Recycling Promotion Center. White, imitation, fair-skinned, Kent, white art, extraordinary cutting, newspaper, magazine, etc. Further, as specific examples, printer paper such as uncoated computer paper, heat-sensitive paper, and pressure-sensitive paper, which are information-related paper;
OA waste paper such as C paper, art paper, coated paper, lightly coated paper, coated paper such as matte paper, or high-quality paper,
Notebook, stationery, wrapping paper, fancy paper, medium paper,
Used pulp paper, high-yield pulp-containing paper, etc. is used for newsprint, paper change, super wrapping paper, imitation paper, pure white roll paper, milk carton, and paperboard. And can be used without any particular limitation.

【００１１】本発明で使用される内添サイズ剤は、ロジ
ン系サイズ剤、合成サイズ剤、石油樹脂系サイズ剤、中
性サイズ剤などが使用できるが、用紙の保存性、ゼログ
ラフィー適性における画質や走行性などの観点からアル
ケニル無水コハク酸、アルキルケテンダイマー、中性ロ
ジンサイズ剤などの中性サイズ剤が好ましい。As the internal sizing agent used in the present invention, a rosin sizing agent, a synthetic sizing agent, a petroleum resin sizing agent, a neutral sizing agent, and the like can be used. Neutral sizing agents such as alkenyl succinic anhydride, alkyl ketene dimer, and neutral rosin sizing agent are preferred from the viewpoints of water resistance and runnability.

【００１２】本発明で使用されるカチオン性ポリマー
は、ポリアクリルアミン塩などのアミン系高分子やその
第４級塩の他、アクリル系化合物とアンモニウム塩との
共重合体などからなるカチオン性高分子などで、これら
を例示すると、次のとおりである。すなわち、ポリアク
リルアミン塩、ポリエチレンイミン、ポリジメチルジア
リルアンモニウムクロライド、ポリアルキレンポリアミ
ンジシアンジアミドアンモニウム縮合物、ポリビニール
ビリジウムハライド、（メタ）アクリル酸アルキル四級
アンモニウム塩、（メタ）アクリルアミドアルキル四級
アンモニウム塩、ω−クロロ−ポリ（オキシエチレン−
ポリメチレン−アルキル四級アンモニウム塩）、ポリビ
ニールベンジルトリメチルアンモニウム塩、などを挙げ
ることができる。カチオン性ポリマーは、従来のサイズ
剤では定着性の悪かったヘミセルロースやリグニンを被
覆する働きがあり、良好なサイズ効果が得られるのと同
時に、インクジェット方式の画像形成装置で印字した場
合、アニオン性のインクとカチオン性の物質が反応し、
メカニカルパルプを配合した場合でも、従来の表面サイ
ズ剤では得られなかったサイズの発現性が得られる。ま
た、上記にあげたカチオン性ポリマーは、デンプンやＰ
ＶＡなどの表面サイズ剤と併用して使用することも可能
である。The cationic polymer used in the present invention includes an amine-based polymer such as a polyacrylamine salt and a quaternary salt thereof, and a cationic polymer comprising a copolymer of an acrylic compound and an ammonium salt. These are exemplified as follows by molecules and the like. That is, polyacrylamine salt, polyethyleneimine, polydimethyldiallylammonium chloride, polyalkylene polyamine dicyandiamidammonium condensate, polyvinyl viridium halide, (meth) acrylic acid alkyl quaternary ammonium salt, (meth) acrylamidoalkyl quaternary ammonium salt , Ω-chloro-poly (oxyethylene-
Polymethylene-alkyl quaternary ammonium salt), polyvinylbenzyltrimethylammonium salt, and the like. Cationic polymer has the function of coating hemicellulose and lignin, which had poor fixability with conventional sizing agents, and at the same time, good sizing effect can be obtained. The ink reacts with the cationic substance,
Even when mechanical pulp is blended, expression of a size that cannot be obtained with a conventional surface sizing agent can be obtained. In addition, the above-mentioned cationic polymers include starch and P.
It can be used in combination with a surface sizing agent such as VA.

【００１３】本発明に使用される填料は、軽質炭酸カル
シウム、重質炭酸カルシウム、カオリン、焼成クレー、
バイオフェライト、セリサイト、タルク、二酸化チタ
ン、微粉末シリカなどの無機填料が使用できるが、古紙
原料に含まれている填料を勘案して添加する必要があ
る。填料の種類について述べると、ゼログラフィー適性
での画質、走行性などの観点から、好ましくは軽質炭酸
カルシウムを使用するのがよく、また填料の配合率は用
紙に対して重量比で１０〜２０重量％の範囲が良い。The filler used in the present invention includes light calcium carbonate, heavy calcium carbonate, kaolin, calcined clay,
Inorganic fillers such as bioferrite, sericite, talc, titanium dioxide, and finely divided silica can be used, but need to be added in consideration of the fillers contained in the raw material of waste paper. In terms of the type of filler, light calcium carbonate is preferably used from the viewpoints of image quality at xerography suitability, running properties, and the like, and the compounding ratio of the filler is 10 to 20% by weight based on paper. Good range of%.

【００１４】填料の配合率が１０重量％を下廻ると、イ
ンクジェット適性でインクの吸収性が悪くなりフェザリ
ングの発生や、乾燥性が悪化する。また、填料の配合率
が２０重量％を上廻ると、ゼログラフィー適性で紙粉の
発生量が多くなり、画像形成装置内を汚染して画像悪化
につながり、さらには給紙部の部材に付着して給紙不良
などの問題を発生させる他、インクジェット方式の画像
形成装置でインクノズルの目詰まりや、印字濃度低下、
ラインや文字の太りによる解像度低下という問題につな
がる。If the compounding ratio of the filler is less than 10% by weight, the ink absorbability is deteriorated due to the suitability for ink jet, and the occurrence of feathering and the drying property are deteriorated. On the other hand, if the content of the filler is more than 20% by weight, the amount of paper dust generated increases due to the suitability of xerography, contaminating the inside of the image forming apparatus, leading to deterioration of the image, and furthermore, adhering to the members of the paper feeding section. Causes problems such as poor paper feed, and clogging of ink nozzles, lowering of print density,
This leads to a problem of a reduction in resolution due to thick lines and characters.

【００１５】[0015]

【実施例】以下に、本発明を実施例に基づいて詳細に説
明するが、本発明はこれらの実施例に限定されるもので
はない。実施例および比較例による用紙の評価は、下記
の要領で行った。 ステキヒトサイズ度：ＪＩＳ Ｐ−８１２２に準拠して
測定した。 填 料 の 含 有 量 ：抄紙された用紙をＪＩＳ Ｐ−８
１２８に従って測定した。 インクジェット適性：プリンタにＣａｎｏｎ ＢＪ−３
００Ｊを使用して、縦横の罫線、ソリッドパッチ、文字
を印字してのフェザリング、乾燥性、印字濃度、文字・
ラインの再現性を評価した。 フェザリング評価 ：Ａ４判の紙に横罫線のパターンお
よびアルファベット文字を印字し、それを目視にてJAPA
N TAPPI紙パルプ試験方法Ｎｏ．１２のペン書サイズ度
試験方法に使用する標準にじみ見本を参考にして、０か
ら６級までの範囲で判定した。その結果についての評価
は、現実に使用する上から判断して５級以上を「○」、
４級を「△」、４級未満を「×」として表示した。 乾 燥 性：印字後、ソリッド・パッチ部に綿
棒を押し当てたときに、インクが綿棒に転移しなくなる
までの時間を測定し、９秒以下を「○」、１０〜１９秒
を「△」、２０秒以上を「×」とした。 印 字 濃 度 ：反射濃度計Ｘ−Ｒｉｔｅ４０４を
使用してソリッドパッチ部の濃度を測定した。１．００
以上を「○」、０．７０〜０．９９を「△」、０．６９
以下を「×」とした。 文字・ラインの再現性：良好なものを「○」、標準的な
ものを「△」、不十分なものを「×」とした。 『ＰＰＣ適性』複写機に富士ゼロックス社製Ｖｉｖａｃ
ｅ８００を使用し、電子写真学会テストチャートをコピ
ーしてモトルを中心とした画質および用紙１０００枚を
連続コピーしたときの給紙性（走行性）を評価した。 画質評価：良好なものを「○」、標準的なものを
「△」、不十分なものを「×」とした。 走行評価：給紙不良の生じないものを「○」、給紙不良
枚数１〜５枚を「△」、給紙不良枚数６枚以上を「×」
とした。 以下に実施例を説明する。EXAMPLES The present invention will be described in detail below with reference to examples, but the present invention is not limited to these examples. The evaluation of the paper according to the examples and the comparative examples was performed in the following manner. Stockigt sizing degree: Measured according to JIS P-8122. Filler content: JIS P-8
128. Inkjet aptitude: Canon BJ-3 for printer
Using 00J, vertical and horizontal ruled lines, solid patches, feathering by printing characters, drying, printing density,
The reproducibility of the line was evaluated. Feathering evaluation: A pattern of horizontal ruled lines and alphabetic characters are printed on A4 size paper, and JAPA is visually observed.
N TAPPI paper pulp test method No. References were made to a standard bleeding sample used in the pen size sizing test method of No. 12, and the judgment was made in the range of 0 to 6 grades. As for the evaluation of the result, if it is judged from the actual use, grade 5 or higher is "○",
Grade 4 was indicated as “△”, and less than 4 was indicated as “×”. Drying property: After printing, when the cotton swab is pressed against the solid patch part, the time until the ink stops transferring to the cotton swab is measured. 9 seconds or less are indicated by “○”, and 10 to 19 seconds are indicated by “△”. , And 20 seconds or more were evaluated as “×”. Print density: The density of the solid patch portion was measured using a reflection densitometer X-Rite404. 1.00
The above is “○”, 0.70 to 0.99 is “△”, 0.69
The following was set as "x". Reproducibility of characters and lines: "Good" for good, "、" for standard, and "x" for poor. Fuji Xerox Vivac for "PPC suitability" copier
Using the e800, the electrophotographic society test chart was copied to evaluate the image quality centered on the mottle and the paper feeding property (running property) when 1000 sheets of paper were continuously copied. Image quality evaluation: Good was evaluated as “○”, standard was evaluated as “Δ”, and insufficient was evaluated as “X”. Running evaluation: "○" indicates that no defective paper feed occurs, "△" indicates 1-5 defective paper feeds, and "x" indicates 6 or more defective paper feeds.
And Examples will be described below.

【００１６】[0016]

【実施例１】表１の実施例１に示す通り、パルプ材料と
してケミカルパルプ（広葉樹晒クラフトパルプ）９０
％、メカニカルパルプとしてＧＰ（グランドパルプ）１
０％を使用し、坪量６６ｇ／ｍ²、厚さ９５μｍとし、
インクジェット適性での乾燥性を考慮して、填料の軽質
炭酸カルシウムが対用紙あたり１０重量％となるよう調
整し、得られた用紙の填料はＪＩＳ Ｐ−８１２８に従
って測定した結果、１０．５重量％であった。内添サイ
ズにはアルケニル無水コハク酸を０．１％（対パルプ重
量）配合し、これに、ゼログラフィー適性を付与するた
めにサイズプレス処方により、澱粉を１ｇ／ｍ²、塩化
ナトリウムを０．２ｇ／ｍ²塗布し、さらに、インクジ
ェット適性でのフェザリングを考慮してポリアクリルア
ミン塩を０．２ｇ／ｍ²塗布した。この用紙のステキヒ
トサイズ度は３５秒であった。Example 1 As shown in Example 1 of Table 1, a chemical pulp (hardwood bleached kraft pulp) 90 was used as a pulp material.
%, GP (ground pulp) 1 as mechanical pulp
Using 0%, a basis weight of 66 g / m ² and a thickness of 95 μm,
Taking into account the drying property of the ink jet, the light calcium carbonate of the filler was adjusted to 10% by weight per paper, and the filler of the obtained paper was measured in accordance with JIS P-8128. As a result, 10.5% by weight was obtained. Met. For the internal size, 0.1% (by weight of pulp) of alkenyl succinic anhydride was blended, and 1 g / m ^{2 of} starch and 0.1 g of sodium chloride were added thereto by a size press formulation to impart xerographic aptitude. 2 g / m ^{2 was} applied, and further, 0.2 g / m ^{2 of} a polyacrylamine salt was applied in consideration of feathering for inkjet suitability. The Stockigt sizing degree of this paper was 35 seconds.

【００１７】[0017]

【実施例２】表１の実施例２に示す通り、填料としては
軽質炭酸カルシウムを対用紙あたり２０重量％となるよ
う調整し、得られた用紙の填料はＪＩＳ Ｐ−８１２８
に従って測定した結果、１９．３重量％であった。上記
以外は、実施例１と同一の処理方法で作成した。この用
紙のステキヒトサイズ度は１４秒であった。Example 2 As shown in Example 2 of Table 1, as a filler, light calcium carbonate was adjusted to 20% by weight per sheet, and the filler of the obtained sheet was JIS P-8128.
Was 19.3% by weight. Except for the above, it was created by the same processing method as in Example 1. The Stockigt sizing degree of this paper was 14 seconds.

【００１８】[0018]

【実施例３】表１の実施例３に示す通り、パルプ材料と
してケミカルパルプ（広葉樹晒クラフトパルプ）８０
％、メカニカルパルプとしてＧＰ（グランドパルプ）１
０％、ＣＭＰ（ケミメカニカルパルプ）１０％を使用
し、インクジェット適性でのフェザリングを考慮してポ
リアクリルアミン塩を０．３ｇ／ｍ²塗布し、また、填
料としては軽質炭酸カルシウムが対用紙あたり１５重量
％となるよう調整した。得られた用紙の填料をＪＩＳ
Ｐ−８１２８に従って測定した結果、１４．８重量％で
あった。それ以外は、実施例１と同一の処理方法で作成
した。この用紙のステキヒトサイズ度は２９秒であっ
た。Example 3 As shown in Example 3 of Table 1, as a pulp material, chemical pulp (hardwood bleached kraft pulp) 80
%, GP (ground pulp) 1 as mechanical pulp
Using 0% and 10% of CMP (chemi-mechanical pulp), 0.3 g / m ^{2 of} polyacrylamine salt is applied in consideration of feathering in ink jet suitability, and light calcium carbonate is used as a filler for paper. Per 15% by weight. Fill the obtained paper with JIS
As a result of measurement according to P-8128, it was 14.8% by weight. Other than that, it was created by the same processing method as in Example 1. The Stockigt sizing degree of this paper was 29 seconds.

【００１９】[0019]

【実施例４】表１の実施例４に示す通り、パルプ材料と
してケミカルパルプ（広葉樹晒クラフトパルプ）６０
％、メカニカルパルプとしてＧＰ（グランドパルプ）３
０％、ＣＭＰ（ケミメカニカルパルプ）１０％を使用
し、インクジェット適性でのフェザリングを考慮して、
ポリビニルビリジウムハライドを０．４ｇ／ｍ²塗布
し、填料としては、軽質炭酸カルシウムが対用紙あたり
１０重量％となるよう調整し、得られた用紙の填料をＪ
ＩＳ Ｐ−８１２８に従って測定した結果、１１．１重
量％であった。上記以外は、実施例１と同一の処理方法
で作成した。この用紙のステキヒトサイズ度は２６秒で
あった。Example 4 As shown in Example 4 of Table 1, a chemical pulp (hardwood bleached kraft pulp) 60 was used as a pulp material.
%, GP (Grand Pulp) 3 as mechanical pulp
Using 0% and 10% of CMP (chemi-mechanical pulp), considering feathering with ink jet suitability,
Polyvinyl viridium halide was applied at 0.4 g / m ^2, and the filler was adjusted so that light calcium carbonate was 10% by weight per paper.
As a result of measurement according to ISP-8128, it was 11.1% by weight. Except for the above, it was created by the same processing method as in Example 1. The degree of Stekigt sizing of this paper was 26 seconds.

【００２０】[0020]

【実施例５】表１の実施例５に示す通り、パルプ材料と
してケミカルパルプ（広葉樹晒クラフトパル）６０％、
メカニカルパルプとしてＧＰ（グランドパルプ）３０
％、ＣＭＰ（ケミメカニカルパルプ）１０％を使用し、
インクジェット適性でのフェザリングを考慮してポリビ
ニルビリジウムハライドを０．５ｇ／ｍ²塗布し、填料と
しては軽質炭酸カルシウムが対用紙あたり２０重量％と
なるよう調整した。得られた用紙の填料をＪＩＳ Ｐ−
８１２８に従って測定した結果、１９．８重量％であっ
た。それ以外は、実施例４と同一の処理方法で作成し
た。この用紙のステキヒトサイズ度は２０秒であった。Example 5 As shown in Example 5 in Table 1, 60% of chemical pulp (hardwood bleached kraft pulp) was used as a pulp material.
GP (Grand Pulp) 30 as mechanical pulp
%, CMP (Chemical Mechanical Pulp) 10%
In consideration of feathering suitable for inkjet, polyvinyl glydium halide was applied at 0.5 g / m ^{2, and} as a filler, light calcium carbonate was adjusted to 20% by weight per paper. Fill the obtained paper with JIS P-
As a result of measurement according to 8128, it was 19.8% by weight. Other than that, it was created by the same processing method as in Example 4. The Stockigt sizing degree of this paper was 20 seconds.

【００２１】以下に比較例を説明する。A comparative example will be described below.

【比較例１】表１の比較例１に示す通り、パルプ材料と
してケミカルパルプ（広葉樹晒クラフトパルプ）９５
％、メカニカルパルプとしてＧＰ（グランドパルプ）５
％を使用し、坪量６６ｇ／ｍ²、厚さ９５μｍとし、填
料の軽質炭酸カルシウムが対用紙あたり５重量％となる
よう調整し、得られた用紙の填料はＪＩＳ Ｐ−８１２
８に従って測定した結果、５．５重量％であった。内添
サイズにはアルケニル無水コハク酸を０．１％（対パル
プ重量）配合し、これに、ゼログラフィー適性を付与す
るためにサイズプレス処方により、澱粉を１ｇ／ｍ²、
塩化ナトリウムを０．２ｇ／ｍ²塗布した。この用紙の
ステキヒトサイズ度は３５秒であった。Comparative Example 1 As shown in Comparative Example 1 in Table 1, as a pulp material, chemical pulp (hardwood bleached kraft pulp) 95 was used.
%, GP (ground pulp) 5 as mechanical pulp
%, The basis weight is 66 g / m ² , the thickness is 95 μm, the light calcium carbonate of the filler is adjusted to 5% by weight per paper, and the filler of the obtained paper is JIS P-812.
As a result of measurement according to No. 8, it was 5.5% by weight. For the internal size, 0.1% of alkenyl succinic anhydride (based on pulp) was blended, and starch was added thereto in an amount of 1 g / m ² by a size press formulation to impart xerographic aptitude.
Sodium chloride was applied at 0.2 g / m ² . The Stockigt sizing degree of this paper was 35 seconds.

【００２２】[0022]

【比較例２】表１の比較例２に示す通り、パルプ材料と
してケミカルパルプ（広葉樹晒クラフトパルプ）６０
％、メカニカルパルプとしてＧＰ（グランドパルプ）４
０％を使用し、填料の軽質炭酸カルシウムが対用紙あた
り８重量％となるよう調整し、得られた用紙の填料はＪ
ＩＳ Ｐ−８１２８に従って測定した。測定結果は７．
６重量％であった以外は、実施例１と同一の処理方法で
作成した。この用紙のステキヒトサイズ度は３５秒であ
った。Comparative Example 2 As shown in Comparative Example 2 in Table 1, a chemical pulp (hardwood bleached kraft pulp) 60 was used as a pulp material.
%, GP (grand pulp) 4 as mechanical pulp
Using 0%, the light calcium carbonate of the filler was adjusted to 8% by weight per paper, and the obtained paper had a filler of J
It was measured according to ISP-8128. The measurement result is 7.
Except for 6% by weight, it was prepared in the same manner as in Example 1. The Stockigt sizing degree of this paper was 35 seconds.

【００２３】[0023]

【比較例３】表１の比較例３に示す通り、パルプ材料と
してケミカルパルプ（広葉樹晒クラフトパルプ）６０
％、メカニカルパルプとしてＧＰ（グランドパルプ）４
０％を使用し、填料が対用紙あたり２５重量％となるよ
う調整し、得られた用紙の填料はＪＩＳ Ｐ−８１２８
に従って測定した結果、２５．５重量％であった。上記
以外は、比較例１と同一の処理方法で作成した。この用
紙のステキヒトサイズ度は９秒であった。Comparative Example 3 As shown in Comparative Example 3 in Table 1, a chemical pulp (hardwood bleached kraft pulp) 60 was used as a pulp material.
%, GP (grand pulp) 4 as mechanical pulp
0% is used, and the filler is adjusted to 25% by weight per sheet, and the obtained sheet filler is JIS P-8128.
Was 25.5% by weight. Except for the above, it was prepared by the same processing method as Comparative Example 1. The Stockigt sizing degree of this paper was 9 seconds.

【００２４】[0024]

【比較例４】表１の比較例４に示す通り、パルプ材料と
してケミカルパルプ（広葉樹晒クラフトパルプ）５５
％、メカニカルパルプとしてＧＰ（グランドパルプ）４
５％を使用し、インクジェット適性でのフェザリングを
考慮してポリアクリルアミン塩を０．５ｇ／ｍ²塗布
し、填料が対用紙あたり１５重量％となるよう調整し、
得られた用紙の填料はＪＩＳ Ｐ−８１２８に従って測
定した結果１５．３重量％であった。それ以外は、比較
例１と同一の処理方法で作成した。この用紙のステキヒ
トサイズ度は４１秒であった。Comparative Example 4 As shown in Comparative Example 4 in Table 1, as a pulp material, chemical pulp (hardwood bleached kraft pulp) 55 was used.
%, GP (grand pulp) 4 as mechanical pulp
5%, a polyacrylamine salt was applied at 0.5 g / m ² in consideration of feathering in inkjet suitability, and the filler was adjusted to 15% by weight per paper,
The filler of the obtained paper was 15.3% by weight as measured according to JIS P-8128. Other than that, it was prepared by the same processing method as Comparative Example 1. The Steckigt sizing degree of this paper was 41 seconds.

【００２５】[0025]

【表１】 [Table 1]

【００２６】[0026]

【発明の効果】本発明は、１０〜４０重量％ものメカニ
カルパルプを含有しているにもかかわらず、カチオン性
ポリマーを抄紙機のサイズプレスで表面塗工し、さらに
填料の配合率を１０〜２０重量％にすることにより、ス
テキヒトサイズ度が１５〜３０秒となり、その結果、従
来の欠点が改善され、ゼログラフィー方式とインクジェ
ット方式の画像印字装置に共用できる情報記録用紙を提
供することが可能となった。According to the present invention, the cationic polymer is surface-coated with a size press of a paper machine even though it contains as much as 10 to 40% by weight of mechanical pulp. By setting the content to 20% by weight, the degree of stiffness becomes 15 to 30 seconds. As a result, the conventional disadvantages are improved, and an information recording paper which can be used in both xerographic and inkjet image printing apparatuses can be provided. It has become possible.

───────────────────────────────────────────────────── フロントページの続き (72)発明者 石田 博巳 東京都千代田区神田小川町２−12 富士ゼ ロックスオフィスサプライ株式会社内 (72)発明者 大橋 耐二 東京都千代田区神田小川町２−12 富士ゼ ロックスオフィスサプライ株式会社内 ──────────────────────────────────────────────────続 き Continuing on the front page (72) Inventor Hiromi Ishida 2-12 Kanda Ogawacho, Chiyoda-ku, Tokyo Inside Fuji Xerox Office Supply Co., Ltd. (72) Inventor Taiji Ohashi 2-12 Kanda Ogawacho, Chiyoda-ku, Tokyo Fuji Xerox Office Supply Co., Ltd.

Claims (1)

【特許請求の範囲】[Claims] 【請求項１】 パルプ成分のうちメカニカルパルプ（Ｍ
Ｐ）を１０〜４０重量％配合した支持体において、該支
持体中に無機填料を１０〜２０重量％含有させると共
に、前記支持体の両面にカチオン性ポリマーを含む水溶
性物質を塗布し、かつステキヒトサイズ度を１０〜４０
秒の範囲に保持したことを特徴とするゼログラフィー方
式とインクジェット方式の画像印字装置の出力に共用で
きる情報記録用紙。1. The pulp component comprising mechanical pulp (M
A support containing 10 to 40% by weight of P), containing 10 to 20% by weight of an inorganic filler in the support, and applying a water-soluble substance containing a cationic polymer to both sides of the support; Stekihito size degree 10-40
An information recording sheet that can be used for the output of xerographic and ink jet type image printing devices characterized by being held in the range of seconds.