JP3170620B2 - Moxibustion pack and its heating method - Google Patents
Moxibustion pack and its heating methodInfo
- Publication number
- JP3170620B2 JP3170620B2 JP04173696A JP4173696A JP3170620B2 JP 3170620 B2 JP3170620 B2 JP 3170620B2 JP 04173696 A JP04173696 A JP 04173696A JP 4173696 A JP4173696 A JP 4173696A JP 3170620 B2 JP3170620 B2 JP 3170620B2
- Authority
- JP
- Japan
- Prior art keywords
- moxibustion
- heating
- ceramic particles
- pack
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、温灸パックとその
加熱方法に関する。The present invention relates to a hot moxibustion pack and a method for heating the same.
【０００２】[0002]
【従来の技術】皮膚の特定部位（つぼ）に熱刺激を与
え、これによって生体の違和を除いて、自然治癒力を向
上させることにより病気を治す温灸療法は、東洋医学の
重要な分野として長い歴史を有している。近年西洋医学
がもたらした種々の薬害などに対する反省の結果とし
て、温灸療法の有用性が見直されている。温灸の適用範
囲は、神経痛、頭痛、リュウマチ、腹痛などの消化器系
疾患、風邪などの呼吸器系疾患、婦人科系疾患などの広
い範囲に及ぶ。2. Description of the Related Art Hot moxibustion therapy, which gives a thermal stimulus to a specific part (pot) of the skin, thereby eliminating the discomfort of the living body and improving the natural healing power to cure the disease, has long been an important field of Oriental medicine. Has a history. In recent years, the usefulness of hot moxibustion therapy has been reviewed as a result of reflecting on various phytotoxicities caused by western medicine. The application range of hot moxibustion covers a wide range such as digestive diseases such as neuralgia, headache, rheumatism and abdominal pain, respiratory diseases such as colds, and gynecological diseases.
【０００３】従来温灸療法は、皮膚の特定部位にもぐさ
を直接（有痕灸或いは知熱灸）或いは間接的に（無痕
灸）付着させ、これを燃焼させて、熱刺激を行ってい
る。しかしながら、もぐさを使用する旧来の方法では、
温灸による施術を行い得るのは、所定の教育を受け、都
道府県知事の免許を受けた灸師に限られている。しか
も、皮膚上でのもぐさの燃焼による温灸療法は、見栄え
の悪さの故に、特に子供および若年齢者層に嫌われ、そ
の利用は、比較的高年齢者層に限られているのが現状で
ある。Conventionally, in hot moxibustion therapy, a muzzle is directly (inscribed moxibustion or intellectual moxibustion) or indirectly (invisible moxibustion) adhered to a specific part of the skin and burned to stimulate heat. However, with the traditional method of using moxa,
Moxibustion can only be performed by moxibustion practitioners who have received the required education and are licensed by the prefectural governor. Moreover, hot moxibustion therapy by burning mushrooms on the skin is particularly disliked by children and young people due to its poor appearance, and its use is currently limited to relatively elderly people. is there.
【０００４】[0004]
【発明が解決しようとする課題】従って、本発明は、も
ぐさの燃焼を行うことなく、簡便に温灸療法を実施しう
る新たな手段を提供することを主な目的とする。SUMMARY OF THE INVENTION Accordingly, it is a main object of the present invention to provide a new means for easily performing hot moxibustion therapy without burning moxa.
【０００５】[0005]
【課題を解決するための手段】本発明者は、上記のよう
な課題を解決するために種々研究を重ねた結果、急速な
加熱が可能であり、且つ長時間にわたり加熱効果を発揮
する新たな温灸パックを開発することに成功した。すな
わち、本発明は、下記の温灸パックとその加熱方法を提
供するものである： １．アラミド繊維製の収容具に多孔質セラミック粒を収
容してなる温灸パック。The inventor of the present invention has conducted various studies to solve the above-mentioned problems, and as a result, a new heating device capable of rapid heating and exhibiting a heating effect for a long time has been developed. Successfully developed a hot moxibustion pack. That is, the present invention provides the following moxibustion pack and the heating method thereof: A moxibustion pack that contains porous ceramic particles in a container made of aramid fiber.
【０００６】２．アラミド繊維製の収容具に多孔質セラ
ミック粒を収容してなる温灸パックを電磁波により加熱
することを特徴とする温灸パックの加熱方法。[0006] 2. A method for heating a moxibustion pack, comprising heating a moxibustion pack containing porous ceramic particles in a container made of aramid fiber with electromagnetic waves.
【０００７】３．電磁波による加熱手段が、電子レンジ
である上記項３に記載の温灸パックの加熱方法。[0007] 3. Item 4. The method for heating a moxibustion pack according to Item 3, wherein the heating means using electromagnetic waves is a microwave oven.
【０００８】[0008]
【発明の実施の形態】以下添付の図面を参照しつつ、本
発明をさらに詳細に説明する。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will be described below in more detail with reference to the accompanying drawings.
【０００９】図１は、本発明による温灸パックの一例を
示す断図面である。本発明による温灸パックは、基本的
に、多孔質セラミック粒３を耐熱性のアラミド繊維製の
袋乃至収容具１に収容した構造を有している。FIG. 1 is a sectional view showing an example of a hot moxibustion pack according to the present invention. The moxibustion pack according to the present invention basically has a structure in which the porous ceramic particles 3 are accommodated in a heat-resistant aramid fiber bag or container 1.
【００１０】本発明で使用するアラミド繊維は、構造式The aramid fiber used in the present invention has a structural formula
【００１１】[0011]
【化１】 Embedded image
【００１２】で表される主鎖にベンゼン環を有する芳香
族ポリアミドからなる高分子繊維であり、例えば、“ケ
ブラー”（Kevlar）という商標名で米国デュポン社から
市販されている。Is a polymer fiber made of an aromatic polyamide having a benzene ring in the main chain, and is commercially available, for example, from DuPont, USA under the trade name "Kevlar" (Kevlar).
【００１３】アラミドは、高分子材料として、耐熱性、
強度、弾性率、耐磨耗性、断熱性などに傑出しておりい
る。例えば、その熱分解開始温度は（空気中）約500
℃、熱収縮開始温度は約400℃、200℃での引張強さ保持
率は常温値の約70％である。特に、耐熱性に関して、本
発明による多孔質セラミック粒を内部に収容した温灸パ
ックを240℃で長時間保持しても、変化は全く生じない
し、300〜350℃では20分間保持しても、変化しない。Aramid is a heat-resistant polymer material.
It excels in strength, elasticity, abrasion resistance, heat insulation, etc. For example, its thermal decomposition onset temperature (in air) is about 500
° C, the thermal shrinkage onset temperature is about 400 ° C, and the tensile strength retention at 200 ° C is about 70% of the normal temperature value. In particular, with respect to heat resistance, no change occurs when the moxibustion pack containing the porous ceramic particles according to the present invention is held at 240 ° C. for a long time, and no change occurs when held at 300 to 350 ° C. for 20 minutes. do not do.
【００１４】アラミド材料の形態としては、平織りなど
の織布、トリコットなどの編物布、不織布、フェルト、
ペーパー、ステープル、テープ、スパン糸、パルプ状品
などがある。本発明においては、これらの形態を有する
アラミド材料により後述のセラミック粒を収容しうる袋
を形成し、この袋にアラミド材料のひもなどの取付具を
取り付ける。Examples of the form of the aramid material include a woven fabric such as a plain weave, a knitted fabric such as a tricot, a nonwoven fabric, a felt,
Paper, staples, tapes, spun yarns, pulp-like products, etc. In the present invention, a bag capable of accommodating the ceramic particles described later is formed from the aramid material having these forms, and a fitting such as a string of the aramid material is attached to the bag.
【００１５】本発明で使用するセラミック粒の材質は、
特に限定されるものではないが、ホルンフェルス、トル
マリン、カオリン、アルミナ、炭化珪素、蛙目粘土、麦
飯石、陶土などが例示される。セラミック粒の製造に際
しては、材料の特性を阻害しない範囲で鉄などの金属の
酸化物或いはその他の化合物を配合しても良い。セラミ
ック粒は、多孔質であることが必須である。セラミック
粒中の孔径は、特に限定されず、数Å〜数百μｍの範囲
に及ぶ。セラミック粒の空隙率は、10〜20％程度である
ことが好ましく、30〜50％程度であることがより好まし
い。The material of the ceramic particles used in the present invention is:
Although not particularly limited, hornfels, tourmaline, kaolin, alumina, silicon carbide, frog-eye clay, barley stone, clay, and the like are exemplified. In the production of the ceramic particles, an oxide of a metal such as iron or other compounds may be added as long as the characteristics of the material are not impaired. It is essential that the ceramic particles be porous. The pore size in the ceramic grains is not particularly limited, and ranges from several millimeters to several hundred micrometers. The porosity of the ceramic particles is preferably about 10 to 20%, and more preferably about 30 to 50%.
【００１６】本発明による温灸パックを繰り返し使用す
る場合には、銀化合物などの抗菌性分、脱臭成分などを
多孔質セラミック粒の調製時に添加しておいたり、製造
後の多孔質セラミック粒に含浸させたり、或いは多孔質
セラミック粒とともにアラミド繊維袋に充填しておくこ
ともできる。When the moxibustion pack according to the present invention is used repeatedly, an antibacterial component such as a silver compound, a deodorizing component, etc. are added during the preparation of the porous ceramic particles, or the porous ceramic particles after production are impregnated. Alternatively, the aramid fiber bag may be filled together with the porous ceramic particles.
【００１７】本発明による多孔質セラミック粒に代えて
非多孔質セラミック粒を使用する場合には、重いので実
用上不利である。また、加熱時に温度のバラツキが生じ
やすく、最高温度の部分は、アラミド繊維の袋を介して
も手を触れることが出来ない程にもなり、さらに保温力
が低いので、使用時に短時間内に温度が低下して、温灸
効果が十分に発揮できない。The use of non-porous ceramic particles in place of the porous ceramic particles according to the present invention is practically disadvantageous because of its heavy weight. In addition, the temperature tends to fluctuate during heating, and the highest temperature part cannot be touched even through the aramid fiber bag. The temperature drops, and the effect of moxibustion cannot be fully exhibited.
【００１８】セラミック粒の粒径は、特に限定されるも
のではないが、アラミド繊維製の袋状収容具に収容して
電磁波により加熱することを考えると、１〜10mm程度と
することが好ましく、3〜6mm程度とすることがより好ま
しい。必要に応じて、セラミック粒に所定の孔特性を付
与する方法は、公知である。例えば、常法に従って、上
記のセラミック材料を所定の粒径に造粒し、乾燥し、発
泡成分の存在下に焼成することにより、所望のセラミッ
ク粒を形成することが出来る。Although the particle size of the ceramic particles is not particularly limited, it is preferably about 1 to 10 mm in consideration of heating in an aramid fiber bag-shaped container and heating by electromagnetic waves. More preferably, it is about 3 to 6 mm. Methods for imparting predetermined pore characteristics to the ceramic grains, if necessary, are known. For example, a desired ceramic particle can be formed by granulating the above ceramic material to a predetermined particle size, drying and firing in the presence of a foaming component according to a conventional method.
【００１９】本発明において使用するセラミック粒は、
天然の多孔質鉱物材料粒であってもよい。天然の多孔質
鉱物材料としては、ゼオライト、パミスなどのいわゆる
天然の軽石が挙げられる。The ceramic particles used in the present invention are:
Natural porous mineral material particles may be used. Examples of the natural porous mineral material include so-called natural pumice such as zeolite and pumice.
【００２０】図２は、本発明による温灸パックの一例を
斜面図として示す。図示の温灸パックは、アラミド繊維
製の袋１にセラミック粒（図示せず）を充填収容してお
り、両端にアラミド繊維製の柄乃至取付具５を備えてい
る。但し、袋の中心部分の一定の領域７は、上下が縫い
合わされており、この部分には、セラミック粒は充填さ
れていない。この中心部分は、使用時に皮膚の過熱を防
止するために、必要に応じて設けるものであり、本発明
の必須の構成要素ではない。FIG. 2 is a perspective view showing an example of the hot moxibustion pack according to the present invention. The illustrated moxibustion pack includes an aramid fiber bag 1 filled with ceramic particles (not shown) and accommodates aramid fiber handles or attachments 5 at both ends. However, a certain area 7 in the center portion of the bag is sewn up and down, and this portion is not filled with ceramic grains. This central portion is provided as needed to prevent overheating of the skin during use, and is not an essential component of the present invention.
【００２１】図３は、本発明の温灸パックの他の一例を
斜面図として示す。図示の温灸パックも、アラミド繊維
製の袋１にセラミック粒（図示せず）を充填収容してお
り、両端にアラミド繊維製の柄乃至取付具９を備えてい
る。アラミド樹脂は、熱伝導性が極めて低いので、柄乃
至取付具９そのものが加熱により、皮膚に接触できない
程度の高温となることはない。FIG. 3 shows another example of the hot moxibustion pack of the present invention as a slanted view. The illustrated moxibustion pack also has a bag 1 made of aramid fiber filled with ceramic particles (not shown), and is provided with a handle or attachment 9 made of aramid fiber at both ends. Since the aramid resin has extremely low thermal conductivity, the handle or the attachment 9 itself does not reach a temperature high enough to prevent contact with the skin by heating.
【００２２】温灸パックの形状は、一切限定されず、使
用個所に応じて適宜選択することが出来る。また、必要
ならば、温灸パックにポリエステル樹脂製などの外カバ
ーを装着することもできる。The shape of the moxibustion pack is not limited at all, and can be appropriately selected according to the place of use. If necessary, an outer cover made of polyester resin or the like can be attached to the moxibustion pack.
【００２３】本発明による温灸パックを使用して、温灸
療法を実施する場合には、まず温灸パックを加熱する。
加熱装置としては、電磁波加熱装置を使用することが好
ましく、この場合には、家庭用の電子レンジを利用する
ことが出来るので、有利である。加熱装置としては、高
周波誘電加熱装置を使用することもできる。加熱温度
は、使用目的に応じて選択すれば良く、特に限定される
ものではないが、通常100〜250℃程度、好ましくは180
〜200℃程度である。加熱時間は、電子レンジなどの加
熱装置の加熱能力、所定の加熱温度などを考慮して決め
ることが出来る。例えば、粒径約3〜6mm程度、空隙率約
30％のホルンフェルスを主成分とする焼結多孔質セラミ
ック粒約1kgを容積1500ccのアラミド繊維製の袋に収容
した本発明温灸パックを出力0.5KWの家庭用電子レンジ
で加熱する場合、加熱時間を３〜１５分程度とすること
により100〜250℃というセラミック粒子温度が得られる
ことが見出された。この場合にも、加熱時間が30分程度
となると、セラミック粒の温度は、500℃以上となり、
アラミド繊維が炭化し始めて、破損することが判明し
た。When performing the hot moxibustion therapy using the hot moxibustion pack according to the present invention, the hot moxibustion pack is first heated.
As the heating device, it is preferable to use an electromagnetic wave heating device, and in this case, a household microwave oven can be used, which is advantageous. As the heating device, a high-frequency dielectric heating device can be used. The heating temperature may be selected according to the purpose of use, and is not particularly limited, but is usually about 100 to 250 ° C., preferably 180 ° C.
~ 200 ° C. The heating time can be determined in consideration of the heating capacity of a heating device such as a microwave oven, a predetermined heating temperature, and the like. For example, a particle size of about 3 to 6 mm, a porosity of about
When heating the moxibustion pack of the present invention, which contains about 1 kg of sintered porous ceramic particles mainly composed of 30% hornfels in a bag made of aramid fiber with a capacity of 1500 cc in a household microwave oven with an output of 0.5 KW, the heating time is reduced. It has been found that a ceramic particle temperature of 100 to 250 ° C. can be obtained by setting it to about 3 to 15 minutes. Also in this case, when the heating time is about 30 minutes, the temperature of the ceramic particles becomes 500 ° C or more,
It was found that the aramid fiber started to carbonize and was broken.
【００２４】次いで、加熱された温灸パックを施術すべ
き個所（痛いところ、冷えているところ、凝っていると
ころなど）に接触させ、上述の柄または取付具により所
定の個所に固定して、必要な時間保持する。熱すぎると
感じられる場合には、温灸パックと施術個所との間にタ
オルなどを介在させても良く、或いは衣服の上から適用
しても良く、或いは温灸パック自体を温度調整用のカバ
ーで包んで使用しても良い。Next, the heated hot moxibustion pack is brought into contact with a place to be treated (a painful place, a cold place, a stiff place, etc.), and is fixed to a predetermined place by the above-mentioned handle or mounting tool. Hold for a good time. If it feels too hot, a towel may be interposed between the moxibustion pack and the treatment site, or it may be applied over clothing, or the moxibustion pack itself may be wrapped with a temperature control cover. You may use it.
【００２５】或いは、もぐさを使用する従来の灸におけ
ると同様に、温灸パックと皮膚との間に湿紙、濡れタオ
ル、ショウガ、ニンニクなどを介在させても良い。Alternatively, a wet paper, a wet towel, ginger, garlic, etc. may be interposed between the moxibustion pack and the skin as in the conventional moxibustion using moxa.
【００２６】[0026]
【発明の効果】本発明の温灸パックを使用する場合に
は、もぐさを使用する従来の温灸療法の欠点（資格を有
する灸師による施術の必要性、見栄えの悪さなど）を解
消することが出来る。When the moxibustion pack of the present invention is used, the drawbacks of the conventional moxibustion therapy using moxa (necessity of treatment by a qualified moxibustionist, poor appearance, etc.) can be solved. .
【００２７】多孔質のセラミック粒を使用するので、孔
内の湿気の存在により、電磁波による加熱が均一に進行
する。Since the porous ceramic particles are used, the heating by the electromagnetic wave proceeds uniformly due to the presence of moisture in the pores.
【００２８】加熱された多孔質セラミック粒は、その微
細な孔に含まれる空気のために、非多孔質セラミック粒
に比して、温度低下速度が約１／５程度と極めて小さい
ので、温灸効果が長期間持続する。[0028] The heated porous ceramic particles have an extremely small temperature decreasing rate of about 1/5 as compared with the non-porous ceramic particles due to the air contained in the fine pores. For a long time.
【００２９】また、アラミド繊維の熱伝導性が極めて低
いので、このことも、加熱された温灸パックの保温力を
長期にわたり維持するに役立つ。Further, since the heat conductivity of the aramid fiber is extremely low, this also helps to maintain the heat retaining power of the heated moxibustion pack for a long time.
【００３０】多孔質セラミックを収容する袋を構成する
アラミド繊維は、耐熱性に優れているので、電磁波によ
る加熱により劣化することはない。The aramid fiber constituting the bag for accommodating the porous ceramic is excellent in heat resistance and does not deteriorate due to heating by electromagnetic waves.
【００３１】[0031]
【実施例】以下に実施例を示し、本発明の特徴とすると
ころをより一層明確にする。EXAMPLES Examples are shown below to further clarify the features of the present invention.
【００３２】実施例１ 粒径3〜6mm程度、空隙率約40％のホルンフェルス／トル
マリン（８０／２０）からなる焼結セラミック粒1000ｇ
をアラミド繊維製の袋に収容して、本発明による温灸パ
ックを得た。Example 1 1000 g of sintered ceramic particles of hornfels / tourmaline (80/20) having a particle size of about 3 to 6 mm and a porosity of about 40%
Was stored in an aramid fiber bag to obtain a hot moxibustion pack according to the present invention.
【００３３】得られた温灸パックを家庭用電子レンジに
より出力2.5kwで８分間加熱し、200℃とした。The resulting moxibustion pack was heated to 200 ° C. for 8 minutes at 2.5 kW using a household microwave oven.
【００３４】加熱された温灸パックを空気中10℃で放置
したところ、最低温度部分の温度が60℃になるまで、約
１時間を要した。When the heated moxibustion pack was left at 10 ° C. in the air, it took about one hour until the temperature of the lowest temperature part reached 60 ° C.
【００３５】実施例２ 粒径1〜3mm程度、空隙率約30％のアルミナ／炭化珪素系
焼結多孔質セラミック粒1000ｇをアラミド繊維製の袋に
収容して得た本発明による温灸パックを家庭用電子レン
ジにより出力0.5kwで加熱して、時間の経過とともに上
昇する温度を測定した。結果は、図４に直線Ａとして示
す通りである。なお、袋中の多孔質粒子全体にわたり、
温度は殆ど同じであったので、一点の温度変化のみを示
した。Example 2 A hot and moxibustion pack according to the present invention obtained by accommodating 1000 g of alumina / silicon carbide sintered porous ceramic particles having a particle size of about 1 to 3 mm and a porosity of about 30% in a bag made of aramid fiber was used at home. Heating was performed with an output of 0.5 kw using a microwave oven, and the temperature rising with time was measured. The result is as shown as a straight line A in FIG. In addition, over the entire porous particles in the bag,
Since the temperatures were almost the same, only one temperature change was shown.
【００３６】一方、粒径1〜3mm程度のアルミナ／炭化珪
素系焼結非多孔質粒子1000ｇをアラミド繊維製の袋に収
容して得た比較品を上記と同様にして加熱した。温度
は、測定位置により大きな差があり、最高温度部の温度
は、直線Ｂとして示す通りであり、最低温度部の温度
は、直線Ｃとして示す通りであった。On the other hand, a comparative product obtained by storing 1000 g of alumina / silicon carbide sintered non-porous particles having a particle size of about 1 to 3 mm in a bag made of aramid fiber was heated in the same manner as described above. The temperature varied greatly depending on the measurement position. The temperature at the highest temperature portion was as shown as a straight line B, and the temperature at the lowest temperature portion was as shown as a straight line C.
【００３７】次いで、上記の本発明品を空気中10℃で放
置し、自然冷却させた。結果を図５に曲線Ａ′として示
す。なお、袋中の多孔質粒子表面と内部では、最大10程
度の温度差が認められたが、図５には、表面の温度を示
した。Next, the above-mentioned product of the present invention was allowed to stand in air at 10 ° C., and was naturally cooled. The result is shown as curve A 'in FIG. Although a temperature difference of up to about 10 was observed between the surface and the inside of the porous particles in the bag, FIG. 5 shows the surface temperature.
【００３８】また、上記の比較品を同様にして自然冷却
させた。最高温度部と最低温度部の結果を図５にそれぞ
れ曲線Ｂ′および曲線Ｃ′として示す。The above comparative product was naturally cooled in the same manner. The results of the highest temperature part and the lowest temperature part are shown in FIG. 5 as curves B 'and C', respectively.
【００３９】図４および図５に示す結果から、本発明品
が全体として均一に且つ急速に加熱できること、および
その冷却は均一に且つ長時間かけてゆっくりと行われる
ことが明らかである。It is clear from the results shown in FIGS. 4 and 5 that the product of the present invention can be uniformly and rapidly heated as a whole, and that the cooling is performed uniformly and slowly over a long period of time.
【００４０】これに対し、比較品では、加熱および冷却
に際して、大きな温度分布が存在していることが明らか
である。On the other hand, it is clear that the comparative product has a large temperature distribution during heating and cooling.
【図１】本発明による温灸パックの一例を示す断図面で
ある。FIG. 1 is a sectional view showing an example of a hot moxibustion pack according to the present invention.
【図２】本発明による温灸パックの形状の一例を示す斜
図面である。FIG. 2 is a perspective view showing an example of the shape of a hot moxibustion pack according to the present invention.
【図３】本発明による温灸パックの形状の他の一例を示
す斜図面である。FIG. 3 is a perspective view showing another example of the shape of the moxibustion pack according to the present invention.
【図４】本発明による温灸パックと比較例による温灸パ
ックの加熱状態を示すグラフである。FIG. 4 is a graph showing a heating state of a moxibustion pack according to the present invention and a moxibustion pack according to a comparative example.
【図５】本発明による温灸パックと比較例による温灸パ
ックの冷却状態を示すグラフである。FIG. 5 is a graph showing a cooling state of a moxibustion pack according to the present invention and a moxibustion pack according to a comparative example.
１…アラミド繊維製の袋状容器 ３…多孔質セラミック粒 ５…柄乃至取付具 ７…加熱防止部分 ９…柄乃至取付具 DESCRIPTION OF SYMBOLS 1 ... Aramid fiber bag-shaped container 3 ... Porous ceramic particles 5 ... Handle or fixture 7 ... Heat prevention part 9 ... Handle or fixture
Claims (3)
ック粒を収容してなる温灸パックであって、セラミック
粒がホルンフェルス/トルマリンからなる焼結多孔質セ
ラミック粒又はアルミナ/炭化珪素系焼結多孔質セラミ
ック粒であり、セラミック粒の空隙率が３０〜５０％で
ある温灸パック。1. A moxibustion pack comprising an aramid fiber container containing porous ceramic particles, wherein the ceramic particles are made of hornfels / tourmaline or are sintered porous ceramic particles or alumina / silicon carbide based sintered porous particles. quality ceramic particle der is, in the porosity of the ceramic particle is 30-50%
Oh Ru moxa pack.
ック粒を収容してなる温灸パックであって，セラミック
粒がホルンフェルス/トルマリンからなる焼結多孔質セ
ラミック粒又はアルミナ/炭化珪素系焼結多孔質セラミ
ック粒であり、セラミック粒の空隙率が３０〜５０％で
ある温灸パックを、電磁波により加熱することを特徴と
する温灸パックの加熱方法。2. A moxibustion pack in which porous ceramic particles are contained in a container made of aramid fiber, wherein the ceramic particles are hornfels / tourmaline or are sintered porous ceramic particles or alumina / silicon carbide based sintered porous. quality ceramic particle der is, in the porosity of the ceramic particle is 30-50%
The Oh Ru moxa pack, moxa pack heating method, characterized by heating by an electromagnetic wave.
ある請求項２に記載の温灸パックの加熱方法。3. The method for heating a moxibustion pack according to claim 2, wherein the means for heating by electromagnetic waves is a microwave oven.