JP3157107U - Disposable protective clothing - Google Patents
Disposable protective clothing Download PDFInfo
- Publication number
- JP3157107U JP3157107U JP2009008149U JP2009008149U JP3157107U JP 3157107 U JP3157107 U JP 3157107U JP 2009008149 U JP2009008149 U JP 2009008149U JP 2009008149 U JP2009008149 U JP 2009008149U JP 3157107 U JP3157107 U JP 3157107U
- Authority
- JP
- Japan
- Prior art keywords
- polyethylene
- sheath
- core
- composite sheet
- disposable protective
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
【課題】血液バリア性、ウィルスバリア性、通気性、柔軟性を併有する使い捨て防護服を提供する。【解決手段】本使い捨て防護服は、複合シートからなり、該複合シートは芯部がポリエチレンテレフタレートで構成されているとともに鞘部がポリエチレンで構成されている芯鞘複合繊維を構成繊維とし、構成繊維どうしが部分的に熱接着された不織布と、微多孔性ポリエチレンフィルム４とが積層されていることを特徴とする。【選択図】図１Disclosed is a disposable protective garment having both blood barrier properties, virus barrier properties, breathability, and flexibility. The disposable protective garment includes a composite sheet, and the composite sheet includes a core-sheath composite fiber having a core part made of polyethylene terephthalate and a sheath part made of polyethylene, and the constituent fiber. A non-woven fabric partially bonded with heat and a microporous polyethylene film 4 are laminated. [Selection] Figure 1
Description
本考案は、インフルエンザ対応などの際に用いられる使い捨て防護服に関する。 The present invention relates to a disposable protective garment used in the case of influenza response.
近年、有害物質から身体を守る観点から、インフルエンザ対応防護服や防塵対応防護服などの使い捨て防護服が用いられている。このような使い捨て防護服は、身体が皮膚呼吸するための空気に対する通気性と、身体をウィルスから防護するためウィルスバリア性を兼ね備えたものである。また、感染原因となる血液等の浸透を防止するための血液バリア性をも併有するものである。 In recent years, disposable protective clothing such as protective clothing for influenza and protective clothing for dust has been used from the viewpoint of protecting the body from harmful substances. Such disposable protective clothing combines air permeability for the body to breathe through the skin and virus barrier properties to protect the body from viruses. Moreover, it also has a blood barrier property for preventing the penetration of blood or the like that causes infection.
上記のような使い捨て防護服として、ポリエチレンの極細網状長繊維をランダムに積層したフラッシュ紡糸不織布からなるシートを用いたものが知られている。
このような不織布を用いた使い捨て防護服は軽くしなやかであり、強度もあるため有用である。しかしながら、ウィルスバリア性の点で、感染を防ぎ切れない場合があった。
As a disposable protective garment as described above, there is known one using a sheet made of a flash spun nonwoven fabric in which polyethylene ultrafine mesh long fibers are randomly laminated.
A disposable protective garment using such a non-woven fabric is useful because it is light, supple and strong. However, there are cases where infection cannot be prevented in terms of virus barrier properties.
上記のような問題を改善するために、ポリプロピレン単体の繊維から構成された不織布と、ポリエチレンやポリプロピレンなどのポリオレフィンから形成された微多孔性のフィルムを積層させたシートを用いて使い捨て防護服を形成することが検討されている。 In order to improve the above problems, a disposable protective garment is formed using a sheet of laminated non-woven fabric composed of fibers of polypropylene alone and a microporous film formed of polyolefin such as polyethylene or polypropylene. To be considered.
このような使い捨て防護服は、バリア性が高いため有用である。しかしながら、強度が弱いという問題点があった。従って、使い捨て防護服に要望される強度を得る場合には、厚みを厚くする必要があるため、ごわごわして着心地が悪いという欠点があった。 Such a disposable protective garment is useful because of its high barrier properties. However, there is a problem that the strength is weak. Accordingly, in order to obtain the strength required for the disposable protective garment, it is necessary to increase the thickness.
上記のように、血液や体液のバリア性、ウィルスバリア性、通気性、柔軟性を兼ね備えた使い捨て防護服は未だ得られていないのが現状である。 As described above, the present situation is that a disposable protective garment having a barrier property against blood and body fluid, a virus barrier property, air permeability, and flexibility has not yet been obtained.
本考案の目的は、血液や体液のバリア性、ウィルスバリア性、通気性、柔軟性を併有した使い捨て防護服を提供することにある。 An object of the present invention is to provide a disposable protective garment having both barrier properties for blood and body fluids, virus barrier properties, breathability, and flexibility.
本考案者らは、上記課題を解決するために鋭意研究を重ねた結果、芯鞘型複合繊維から形成された不織布と、微多孔性ポリエチレンフィルムから得られた複合シートを用いることで、上記の課題を解決することを見出し、かかる知見に基づき本考案に到達した。 As a result of intensive studies to solve the above problems, the present inventors have used the nonwoven fabric formed from the core-sheath composite fiber and the composite sheet obtained from the microporous polyethylene film, and The present inventors have found that the problem can be solved and have arrived at the present invention based on such knowledge.
すなわち、本考案の要旨は、下記の通りである。
（１）複合シートからなる使い捨て防護服であって、該複合シートは芯部がポリエチレンテレフタレートで構成されているとともに鞘部がポリエチレンで構成されている芯鞘複合繊維を構成繊維とし構成繊維どうしが部分的に熱接着された不織布と、微多孔性ポリエチレンフィルムとが積層されていることを特徴とする使い捨て防護服。
That is, the gist of the present invention is as follows.
(1) A disposable protective garment composed of a composite sheet, wherein the composite sheet comprises a core-sheath composite fiber having a core part made of polyethylene terephthalate and a sheath part made of polyethylene as constituent fibers. A disposable protective garment characterized in that a partially heat-bonded nonwoven fabric and a microporous polyethylene film are laminated.
本考案によれば、血液や体液のバリア性、ウィルスバリア性、通気性、柔軟性を兼ね備えた使い捨て防護服を提供することが可能である。 According to the present invention, it is possible to provide a disposable protective garment having both blood and body fluid barrier properties, virus barrier properties, breathability, and flexibility.
以下、本考案を詳細に説明する。
本考案の使い捨て防護服は、不織布と、微多孔性ポリエチレンフィルムとが、積層されたシート（以下、単に「複合シート」と称する場合がある）から形成される。
Hereinafter, the present invention will be described in detail.
The disposable protective garment of the present invention is formed from a sheet in which a nonwoven fabric and a microporous polyethylene film are laminated (hereinafter, simply referred to as “composite sheet”).
上記複合シートの一例について、図１を用いて説明する。本考案の複合シート１は、接着剤３を介して、微多孔性ポリエチレンフィルム４の両面に不織布２が積層されている。または図２のように、微多孔性ポリエチレンフィルム４の片面に、接着剤３を介して不織布２が積層されている複合シート５も好ましいものである。不織布２は、芯部がポリエチレンテレフタレートで構成されているとともに鞘部がポリエチレンで構成されている芯鞘複合繊維から構成される。
An example of the composite sheet will be described with reference to FIG. The
鞘成分のポリエチレンは、芯成分のポリエチレンテレフタレートよりも、低い融点を有する。そのため、鞘成分を熱接着成分として確実に機能させるとともに、芯成分を繊維形態保持成分として確実に機能させることができる。 The sheath component polyethylene has a lower melting point than the core component polyethylene terephthalate. Therefore, while making a sheath component function reliably as a thermoadhesion component, a core component can be functioned reliably as a fiber form maintenance component.
芯成分のポリエチレンテレフタレートは、鞘成分のポリエチレンよりも高い融点を有する。また、結晶性があり、ポリマーの中でも強度が高いものであるため、鞘成分を熱により溶融させて熱接着を行う際に、溶融せずに所要の強度の繊維形態を確実に維持することができる。 The core component polyethylene terephthalate has a higher melting point than the sheath component polyethylene. In addition, since it has crystallinity and has high strength among polymers, when the sheath component is melted by heat to perform heat bonding, it is possible to reliably maintain the fiber form of the required strength without melting. it can.
本考案に使用する不織布は、芯部がポリエチレンテレフタレートで構成されているとともに鞘部がポリエチレンで構成されている芯鞘複合繊維から構成される。
芯部を構成するポリエチレンテレフタレートとしては、通常市販又は工業的に利用されているポリエチレンテレフタレートのうち、特に繊維用として市販され、利用されているものであれば特に限定されない。
The nonwoven fabric used in the present invention is composed of a core-sheath composite fiber having a core part made of polyethylene terephthalate and a sheath part made of polyethylene.
The polyethylene terephthalate constituting the core portion is not particularly limited as long as it is commercially available and used for fibers among polyethylene terephthalates usually commercially available or industrially used.
また、鞘部を構成するポリエチレンは、通常市販又は工業的に利用されているポリエチレンテレフタレートのうち、特に繊維用として市販され、利用されているものであれば特に限定されない。 Moreover, the polyethylene which comprises a sheath part will not be specifically limited if it is marketed and utilized especially for fiber use among the polyethylene terephthalate normally marketed or utilized industrially.
芯部と鞘部の質量比は、繊維同士の接着性の観点から、芯部／鞘部＝２／１〜１／２であることが好ましい。
本考案の防護服に用いられる不織布は、上記複合繊維によって構成されるが、構成繊維同士が熱接着により一体化したものであることが好ましく、特に熱エンボス加工により熱接着していることが好ましい。熱エンボス加工により熱接着している不織布は、熱接着部（不織布に形成された凹部）では熱と圧力が付与されているが、非熱接着部は熱や圧力の影響をほとんど受けていないため、柔軟性に優れ肌触りの良好な不織布となるからである。また、機械的特性も良好であり、形態安定性に優れるためである。
The mass ratio between the core part and the sheath part is preferably core part / sheath part = 2/1 to 1/2 from the viewpoint of the adhesiveness between the fibers.
The nonwoven fabric used in the protective garment of the present invention is composed of the above-mentioned composite fiber, but it is preferable that the constituent fibers are integrated by thermal bonding, and it is particularly preferable that they are thermally bonded by heat embossing. . Nonwoven fabrics that are thermally bonded by hot embossing are given heat and pressure at the thermal bonding part (recesses formed in the nonwoven fabric), but non-thermal bonding parts are hardly affected by heat or pressure. This is because the non-woven fabric has excellent flexibility and good touch. Moreover, it is because mechanical characteristics are also favorable and it is excellent in form stability.
本考案の防護服に用いられる不織布の製造方法の一例について説明する。まず、ポリエチレンテレフタレートとポリエチレンとを、該ポリエチレンテレフタレートが芯に配され、該ポリエチレンが鞘に配されるように、芯鞘型複合紡糸孔に供給し、溶融紡糸して芯鞘複合繊維を得る。次いで、該芯鞘複合繊維を、移動するコンベア上などに捕集して集積する。集積後は、エンボスロールなどに通して、部分的に熱圧接して、圧接部位で鞘部を軟化又は溶融させて、芯鞘複合繊維相互間を結合して不織布を得る。 An example of the manufacturing method of the nonwoven fabric used for the protective clothing of this invention is demonstrated. First, polyethylene terephthalate and polyethylene are supplied to a core-sheath-type composite spinning hole so that the polyethylene terephthalate is placed on the core and the polyethylene is placed on the sheath, and melt-spun to obtain a core-sheath composite fiber. Next, the core-sheath composite fiber is collected and collected on a moving conveyor or the like. After the accumulation, it is passed through an embossing roll or the like and partially heat-welded, and the sheath portion is softened or melted at the pressure-welding site to bond the core-sheath composite fibers together to obtain a nonwoven fabric.
また、不織布の目付けは、複合シートが用いられる防護服の具体的な用途に応じて適宜選択すればよく、本考案においては、柔軟性および強度の観点から、１０〜５０ｇ／ｍ２であることが好ましい。 The basis weight of the nonwoven fabric may be appropriately selected according to the specific use of the protective clothing in which the composite sheet is used. In the present invention, the basis weight is 10 to 50 g / m 2 from the viewpoint of flexibility and strength. Is preferred.
本考案の防護服に使用する微多孔性ポリエチレンフィルムは、気体、水蒸気等は通すが、水（液体）は透さない程度の小孔を多数有する微多孔構造を有する公知のポリエチレンフィルムであれば特に限定されない。例えば、無機充填剤、有機充填剤などを含有するポリエチレンフィルムより該充填剤を溶剤で溶出して製造する微多孔性フィルムでもよい。または、無機充填剤、有機充填剤を含有するポリエチレン樹脂からなるシートを少なくとも一軸方向に延伸して微多孔構造を形成させて得られる微多孔性フィルムでもよい。 The microporous polyethylene film used in the protective garment of the present invention is a known polyethylene film having a microporous structure having a large number of small holes that allow gas, water vapor, etc. to pass through but not water (liquid). There is no particular limitation. For example, a microporous film produced by eluting the filler with a solvent from a polyethylene film containing an inorganic filler, an organic filler, or the like may be used. Or the microporous film obtained by extending | stretching the sheet | seat which consists of a polyethylene resin containing an inorganic filler and an organic filler at least to a uniaxial direction, and forming a microporous structure may be sufficient.
上記の微多孔性ポリエチレンフィルムを製造する方法としては、例えば、以下の方法が挙げられる。すなわち、ポリエチレン樹脂を、所定量の充填剤、各種添加剤とともに、混練押出成形機などを用いてペレット化し、このペレットを用いて、Ｔダイ押出成形機、インフレーション成形機を用いて製膜する。製膜されたフィルムは、少なくとも一軸方向に延伸される。延伸は多段階に行ってもよいし、二軸に延伸することもできる。この延伸によって、フィルムの強度が向上するとともに、微多孔が形成される。この延伸フィルムを熱処理することによって、フィルムの寸法安定性を向上させることができる。 Examples of the method for producing the microporous polyethylene film include the following methods. That is, a polyethylene resin is pelletized with a predetermined amount of filler and various additives using a kneading extrusion molding machine or the like, and the pellet is used to form a film using a T-die extrusion molding machine or an inflation molding machine. The formed film is stretched in at least a uniaxial direction. Stretching may be performed in multiple stages or biaxially. This stretching improves the strength of the film and forms micropores. By heat-treating this stretched film, the dimensional stability of the film can be improved.
微多孔性ポリエチレンフィルムのフィルム厚みは、特に限定されないが、柔軟性及びバリア性の観点から、通常、１５〜４０μｍであることが好ましい。
微多孔性ポリエチレンフィルムの透気度は、５０００〜１２０００ｇ／ｍ２・２４ｈｒであることが好ましい。
Although the film thickness of a microporous polyethylene film is not specifically limited, From a viewpoint of a softness | flexibility and barrier property, it is preferable that it is 15-40 micrometers normally.
The air permeability of the microporous polyethylene film is preferably 5000 to 12000 g / m 2 · 24 hr.
本考案の防護服に用いられる複合シートは、上述の芯鞘型複合繊維から構成される不織布とポリエチレン多孔性フィルムを、積層したものである。複合シートの構造としては、（不織布）／（微多孔性ポリエチレンフィルム）のような２層構造であってもよいし、（不織布）／（微多孔性ポリエチレンフィルム）／（不織布）のような３層構造であってもよい。 The composite sheet used in the protective clothing of the present invention is a laminate of a nonwoven fabric composed of the above-described core-sheath composite fiber and a polyethylene porous film. The structure of the composite sheet may be a two-layer structure such as (nonwoven fabric) / (microporous polyethylene film), or 3 such as (nonwoven fabric) / (microporous polyethylene film) / (nonwoven fabric). It may be a layer structure.
積層方法としては、接着剤を介して積層させる方法や、熱シール加工により積層させる方法が挙げられる。
上記の接着剤は、ホットメルト型接着剤が好ましく用いられる。ホットメルト型接着剤の中でも、接着性の観点から、ポリエチレン系接着剤が好ましい。
Examples of the laminating method include a method of laminating via an adhesive and a method of laminating by heat sealing.
As the adhesive, a hot melt adhesive is preferably used. Among the hot melt adhesives, a polyethylene adhesive is preferable from the viewpoint of adhesiveness.
エンボス加工により複合シートを得る場合は、以下のような方法が挙げられる。すなわち、熱処理により、上記に説明した不織布の鞘部を構成するポリエチレンを溶融、または軟化させる。次いで、微多孔性ポリエチレンフィルムを積層し、熱をかけながらエンボスロールに通して、両者を融着一体化させて複合シートを得る。 When obtaining a composite sheet by embossing, the following methods are mentioned. That is, the polyethylene which comprises the sheath part of the nonwoven fabric demonstrated above is fuse | melted or softened by heat processing. Next, a microporous polyethylene film is laminated, passed through an embossing roll while applying heat, and both are fused and integrated to obtain a composite sheet.
上記の複合シートの目付は、特に限定されないが、強度及び柔軟性の観点から、４０〜７０ｇ／ｍ２であることが好ましい。
このような複合シートは、気体、水蒸気等は透すが、水（液体）は透さないという微多孔性ポリエチレンフィルムの性能を保持し、さらに不織布により補強されているため、機械的強度に優れる。また、本考案に用いられる不織布はヒートシール性にも優れるため、上記のような複合シートはヒートシール性にも優れている。
Although the fabric weight of said composite sheet is not specifically limited, From a viewpoint of intensity | strength and a softness | flexibility, it is preferable that it is 40-70 g / m < 2 >.
Such a composite sheet retains the performance of a microporous polyethylene film that allows gas, water vapor, etc. to pass through, but does not pass water (liquid), and is further reinforced with a nonwoven fabric, so it has excellent mechanical strength. . Moreover, since the nonwoven fabric used for this invention is excellent also in heat-sealability, the above composite sheets are also excellent in heat-sealability.
また、このような複合シートは上記した微多孔性ポリエチレンフィルムの性能が保持されているため、良好にウィルスバリア性を有するものとなる。
本考案の使い捨て防護服は、上記のような複合シートを適宜な方法で縫製することにより形成されるものである。そのため、高い血液バリア性、ウィルスバリア性、通気性、柔軟性を併有することができる。
Moreover, since such a composite sheet retains the performance of the above-described microporous polyethylene film, it has good virus barrier properties.
The disposable protective clothing of the present invention is formed by sewing the composite sheet as described above by an appropriate method. Therefore, it can have high blood barrier property, virus barrier property, air permeability, and flexibility.
以下、本考案を実施例により、さらに具体的に説明するが、本考案は実施例のみに限定されるものではない。
[評価方法]
以下に、実施例及び比較例の評価に用いた測定法を示す。
（１）引張強度試験
ＪＩＳ Ｔ ８１１５に準拠して測定した。
（２）血液バリア性（耐水性）
ＪＩＳ Ｔ ８０６０ 手順Ｄにて測定した。
（３）ウィルスバリア性
ＪＩＳ Ｔ ８０６１ 手順Ｄにて測定した。
（４）柔軟性（官能評価）
得られた試験片の手触りを評価した。以下の基準で評価した。
○：柔軟性があり、しなやかである。
×：柔軟性に劣り、ごわつきがある。
（実施例１）
ポリエチレンテレフタレートとポリエチレンを準備した。ポリエチレンテレフタレートが芯に配され、ポリエチレンが鞘に配されるように、且つ、両者の質量比が５０／５０となるようにして、芯鞘型複合紡糸孔に供給し、紡糸温度２９５℃、紡糸速度３０００ｍ／分で溶融紡糸を行った。溶融紡糸した後、吸引装置により引き取り細化し、吸引装置から排出された糸条を開繊した後、移動する捕集面上に芯鞘複合繊維（繊度：３．５ｄｔｅｘ）を集積させて不織ウェブを得た。この不織ウェブに、部分的に熱圧接処理を施して、目付が２６ｇ／ｃｍ２である不織布を得た。
Hereinafter, the present invention will be described more specifically with reference to examples. However, the present invention is not limited to the examples.
[Evaluation methods]
Below, the measuring method used for evaluation of an Example and a comparative example is shown.
(1) Tensile strength test It measured based on JIST8115.
(2) Blood barrier properties (water resistance)
Measured according to JIS T 8060 Procedure D.
(3) Virus barrier property Measured according to JIS T8061 Procedure D.
(4) Flexibility (sensory evaluation)
The feel of the obtained test piece was evaluated. Evaluation was made according to the following criteria.
○: Flexible and supple.
×: Inferior in flexibility and stiff.
Example 1
Polyethylene terephthalate and polyethylene were prepared. Polyethylene terephthalate is placed on the core, polyethylene is placed on the sheath, and the mass ratio of both is 50/50, and is supplied to the core-sheath compound spinning hole, spinning temperature is 295 ° C., spinning Melt spinning was performed at a speed of 3000 m / min. After melt spinning, the material is taken up and refined by a suction device, and the yarn discharged from the suction device is opened. Got the web. This nonwoven web is subjected to a partial thermal compression treatment to obtain a nonwoven fabric having a basis weight is 26 g / cm 2.
得られた不織布の片面にホットメルト接着剤を３ｇ／ｍ２の量で溶融塗布し、その上から微多孔性ポリエチレンフィルム（三菱樹脂社製、品番「ＣＡＵ６０２０Ａ」）（厚み：２０μｍ、目付：２０ｇ／ｍ２）を貼り付けし、２層構造の複合シートを得た。 A hot melt adhesive was melt-coated on one side of the obtained nonwoven fabric in an amount of 3 g / m 2, and a microporous polyethylene film (manufactured by Mitsubishi Plastics, product number “CAU6020A”) (thickness: 20 μm, basis weight: 20 g) / M 2 ) was pasted to obtain a composite sheet having a two-layer structure.
得られた複合シートを各種測定に付した。
（比較例１）
比較例１のシートとして、ポリエチレン製フラッシュ紡糸不織布（目付：４５ｇ／ｍ２）を用意し、各種測定に付した。
（比較例２）
実施例１において用いた芯鞘複合繊維を用いた不織布に代えて、ポリプロピレン不織布（目付：３７ｇ／ｍ２）を用意し、このポリプロピレン不織布に実施例１と同様にして、片面にホットメルト接着剤を３ｇ／ｍ２の量で溶融塗布し、その上から微多孔性ポリエチレンフィルム（三菱樹脂社製、品番「ＣＡＵ６０２０Ａ」）（厚み：２０μｍ、目付：２０ｇ／ｍ２）を貼り付けし、２層構造の複合シートを得た。
The obtained composite sheet was subjected to various measurements.
(Comparative Example 1)
As a sheet of Comparative Example 1, a flash spun nonwoven fabric made of polyethylene (weight per unit area: 45 g / m 2 ) was prepared and subjected to various measurements.
(Comparative Example 2)
Instead of the nonwoven fabric using a core-sheath composite fibers used in Example 1, a polypropylene nonwoven fabric (basis weight: 37g / m 2) was prepared, in the same manner as in Example 1 to the polypropylene nonwoven fabric, hot-melt adhesive on one side Is applied in an amount of 3 g / m 2, and a microporous polyethylene film (manufactured by Mitsubishi Plastics, product number “CAU6020A”) (thickness: 20 μm, basis weight: 20 g / m 2 ) is pasted thereon to form two layers A composite sheet of structure was obtained.
得られた複合シートを各種測定に付した。
実施例および比較例で得られた評価結果を、表１に示す。
The obtained composite sheet was subjected to various measurements.
Table 1 shows the evaluation results obtained in Examples and Comparative Examples.
実施例１は、強度も十分であり、血液バリア性及びウィルスバリア性に優れるものであり、柔軟性に優れるものであった。
比較例１は、血液バリア性、柔軟性に優れていたが、ウィルスバリア性において劣っていた。
In Example 1, the strength was sufficient, the blood barrier property and the virus barrier property were excellent, and the flexibility was excellent.
Comparative Example 1 was excellent in blood barrier properties and flexibility, but was inferior in virus barrier properties.
比較例２は、耐水性、ウィルスバリア性に優れていたが、柔軟性において劣っていた。 Comparative Example 2 was excellent in water resistance and virus barrier properties, but was inferior in flexibility.
１ ３層構造の複合シート
２ 芯鞘複合繊維を構成繊維とする不織布
３ 接着剤
４ 微多孔性ポリエチレンフィルム
５ ２層構造の複合シート
DESCRIPTION OF
Claims (1)
A disposable protective garment comprising a composite sheet, wherein the composite sheet comprises a core-sheath composite fiber having a core part made of polyethylene terephthalate and a sheath part made of polyethylene, and the constituent fibers are partially A disposable protective garment characterized by laminating a non-woven fabric thermally bonded to a microporous polyethylene film.