JP3150645B2 - Electrostatic toner - Google Patents
Electrostatic tonerInfo
- Publication number
- JP3150645B2 JP3150645B2 JP15038297A JP15038297A JP3150645B2 JP 3150645 B2 JP3150645 B2 JP 3150645B2 JP 15038297 A JP15038297 A JP 15038297A JP 15038297 A JP15038297 A JP 15038297A JP 3150645 B2 JP3150645 B2 JP 3150645B2
- Authority
- JP
- Japan
- Prior art keywords
- toner
- developing
- alumina particles
- electrostatic charge
- particles
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【０００１】[0001]
【産業上の利用分野】本発明は、静電潜像を現像するた
めの静電荷現像用トナーに関し、特に現像ロールと感光
体ドラムとが接触した接触型の非磁性一成分現像方式に
好ましく使用するトナーに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a toner for developing an electrostatic latent image for developing an electrostatic latent image, and more particularly, it is preferably used in a contact type non-magnetic one-component developing system in which a developing roll and a photosensitive drum are in contact with each other. Related to toner.
【０００２】[0002]
【従来の技術】従来から行われている静電潜像とトナー
を用いて現像する方法を大別すると、トナー及びキャリ
アを主体とする二成分現像方法、あるいはトナーのみか
らなる一成分現像剤を用いる現像方法がある。一般に非
磁性トナーとキャリアを用いる二成分系現像剤による現
像方法は、一成分系現像剤による現像方法に比較して次
のような問題点がある。 トナーとキャリアとの混合比をコントロールするため
のトナー濃度センサーが必要である。 キャリアの耐久性に限界があり、長期間の使用に際し
てはトナーの補給だけではなく現像剤の交換が必要であ
る。 現像剤とトナーを混合する攪拌機構が必要であり現像
機が大型になり易い。 一方、磁性一成分系の現像剤による現像方法の問題点と
しては以下の点が挙げられる。 帯電部材が現像ロールあるいはブレードであり、キャ
リアを帯電部材として用いる場合に比較して帯電の安定
性に欠け帯電能力も弱い。 磁気ブラシを均一に形成するための現像機の精度が必
要である。 磁性トナーの場合、転写性および定着性の環境湿度へ
の依存性が大きいこと及び感光体への損傷性が大きいこ
との点において前記二成分系の非磁性トナーに比べて劣
る。 これらの問題点を総合的に考え、かつ装置の小型化等を
併せて考えると、非磁性一成分系トナーを用いる現像方
法が極めて有効であり、近年いくつかの現像方式が実用
化されている。2. Description of the Related Art Conventionally, a method of developing using an electrostatic latent image and toner is roughly classified into a two-component developing method mainly composed of toner and carrier, or a one-component developer consisting of only toner. There is a developing method to be used. Generally, a developing method using a two-component developer using a non-magnetic toner and a carrier has the following problems as compared with a developing method using a one-component developer. A toner concentration sensor for controlling the mixing ratio between the toner and the carrier is required. There is a limit to the durability of the carrier, and when used for a long time, it is necessary to replace not only the toner but also the developer. Since a stirring mechanism for mixing the developer and the toner is required, the size of the developing machine tends to increase. On the other hand, problems of the developing method using a magnetic one-component developer include the following. The charging member is a developing roll or a blade, and the charging stability is poor and the charging ability is weak as compared with the case where the carrier is used as the charging member. The precision of the developing machine for uniformly forming the magnetic brush is required. The magnetic toner is inferior to the two-component non-magnetic toner in that the transferability and the fixability are largely dependent on the environmental humidity and the damage to the photoconductor is large. Considering these problems comprehensively and also considering miniaturization of the apparatus, a developing method using a non-magnetic one-component toner is extremely effective, and several developing methods have been put into practical use in recent years. .
【０００３】非磁性一成分現像方式は、トナーを担持し
た現像ロールと感光体ドラムとが接触している装置がほ
とんどで、現像機には現像ロールに圧接されたブレード
やトナー供給ロールが接触して配置されている。この現
像方式によれば比較的容易にトナーを帯電させることが
可能であって、感光体ドラム表面上に現像されるトナー
の現像量も多いが、感光体ドラムの表面にトナーが融着
（以下、これをフィルミングという）しやすく、その部
分にトナーが現像されない潜像部分が生じ、その結果感
光体ドラム表面から転写された画像に文字抜けと呼ばれ
る画像欠損が発生するという問題を有していた。従来こ
のようなフィルミングに基づく問題を解決するため、ト
ナー粒子表面に例えばマグネタイト、カーボンブラッ
ク、酸化チタンあるいはセラミック等の無機微粉末を外
添し、感光体表面上を研磨してフィルミングの発生を防
止し画像品質を維持する方法が用いられていた。しかし
ながら、上記従来の無機微粉末は、感光体表面上に生じ
たトナーのフィルミングと同時に「膜削れ」と呼ばれる
感光体表面上を研磨し、この膜削れが生じた感光体表面
にはトナーが現像されなく、前記と同様に画像上に文字
抜けやカスレが生じる問題を有していた。In the non-magnetic one-component developing system, most of the devices have a developing roller carrying toner and a photosensitive drum in contact with each other. A developing machine is contacted with a blade or a toner supply roll pressed against the developing roll. It is arranged. According to this developing method, the toner can be charged relatively easily, and the amount of toner developed on the surface of the photoconductor drum is large. This is called filming), and a latent image portion where toner is not developed occurs in that portion. As a result, an image transferred from the surface of the photosensitive drum has an image defect called character omission. Was. Conventionally, in order to solve the problem based on such filming, an inorganic fine powder such as magnetite, carbon black, titanium oxide or ceramic is externally added to the toner particle surface, and the photoreceptor surface is polished to cause filming. A method has been used in which the image quality is prevented and the image quality is maintained. However, the above-mentioned conventional inorganic fine powder polishes the photoreceptor surface, which is called "film shaving", at the same time as the filming of the toner generated on the photoreceptor surface. There is a problem that the image is not developed and characters are missing or blurred on the image as described above.
【０００４】[0004]
【発明が解決しようとする課題】本発明は、前記従来の
静電荷現像用トナーの問題点を解決したものであり、感
光体表面へのトナーのフィルミングを防いで、且つ膜削
れが生じにくく、文字抜け等の問題のない画像を得るこ
とができる静電荷現像用トナーを提供することを目的と
するものである。SUMMARY OF THE INVENTION The present invention has been made to solve the above-mentioned problems of the conventional toner for developing an electrostatic charge, and prevents filming of the toner on the surface of the photoreceptor and hardly causes film shaving. It is another object of the present invention to provide an electrostatic charge developing toner capable of obtaining an image having no problem such as missing characters.
【０００５】[0005]
【課題を解決するための手段】本発明は、少なくとも結
着樹脂と着色剤を含有するトナー粒子の表面にＢＥＴ比
表面積とタップ密度が次の関係を有するアルミナ粒子を
付着させたことを特徴とする静電荷現像用トナーであ
る。The present invention is characterized in that alumina particles having a BET specific surface area and a tap density having the following relationship are adhered to the surface of toner particles containing at least a binder resin and a colorant. This is a toner for developing electrostatic charge.
【数３】 (Equation 3)
【０００６】以下、本発明について詳細に説明する。図
１は、本発明の静電荷現像用トナーが好適に使用される
接触型非磁性一成分現像方式の現像装置の概略構成図で
ある。図中、１は円筒状の感光体ドラム、２はホッパ
ー、３は静電荷現像用トナー、４ａはドクターブレード
などのトナー層厚規制部材、４ｂはトナー層厚規制部材
の固定部材、５は現像ロール、６はトナーの漏れ防止及
びかき落し部材、７は攪拌機である。この現像装置にお
いては、感光体ドラム１はＳｅや有機光半導体（ＯＰ
Ｃ）等が使用され、その表面に電子写真法によって静電
潜像が形成される。ホッパー２内には静電荷現像用トナ
ー３が収容されており、該トナーは、トナー層厚規制部
材４ａによって現像ロール５の表面上に一定の層厚にな
るように担持され、感光体ドラム１の表面に搬送され
る。その際静電荷現像用トナー３はトナー層厚規制部材
４ａによって摩擦帯電されるが、トナー層厚規制部材４
ａは、直流または交流電源に接続され、現像ロール５表
面上に形成されたトナー担持層とトナー層厚規制部材４
ａとの間に電界が発生するようにしてもよい。現像ロー
ル５表面上に形成されたトナー担持層と、感光体ドラム
１とは、１〜５ｍｍのニップ幅をもって接触して設置さ
れる。現像ロール５に担持された静電荷現像用トナー３
は、現像ロール５の回転により搬送されて静電潜像を有
する感光体ドラム１と接触し、静電潜像の顕像化が行わ
れる。Hereinafter, the present invention will be described in detail. FIG. 1 is a schematic configuration diagram of a contact-type non-magnetic one-component developing apparatus in which the electrostatic charge developing toner of the present invention is suitably used. In the figure, 1 is a cylindrical photosensitive drum, 2 is a hopper, 3 is a toner for developing electrostatic charge, 4a is a toner layer thickness regulating member such as a doctor blade, 4b is a fixing member of the toner layer thickness regulating member, and 5 is a developing member. A roll 6 is a member for preventing toner leakage and scraping, and 7 is a stirrer. In this developing device, the photosensitive drum 1 is made of Se or an organic optical semiconductor (OP).
C) and the like, and an electrostatic latent image is formed on the surface by electrophotography. The hopper 2 contains an electrostatic charge developing toner 3, and the toner is carried on the surface of the developing roll 5 by a toner layer thickness regulating member 4 a so as to have a constant layer thickness. Transported to the surface of At this time, the toner 3 for electrostatic charge development is frictionally charged by the toner layer thickness regulating member 4a.
a denotes a toner carrying layer and a toner layer thickness regulating member 4 connected to a DC or AC power source and formed on the surface of the developing roll 5.
An electric field may be generated between a and a. The toner carrying layer formed on the surface of the developing roll 5 and the photosensitive drum 1 are placed in contact with each other with a nip width of 1 to 5 mm. Toner 3 for electrostatic charge development carried on developing roll 5
Is transported by the rotation of the developing roll 5 and comes into contact with the photosensitive drum 1 having an electrostatic latent image, so that the electrostatic latent image is visualized.
【０００７】上記のように現像ロール５は、その表面上
にトナー担持層が形成され、内部には弾性ロールを有す
る２層構成となっている。トナー担持層は、バイアス電
圧が印加できるように導電性の材料よりなるか、または
導電性層を有するのが好ましい。該トナー担持層として
は、適度の弾性を備えた、肉薄樹脂層よりなり、例え
ば、含フッ素樹脂、シリコーン系樹脂、ポリエステル樹
脂、ポリカーボネート樹脂など、膜形成性を有する樹脂
が使用される。トナー担持層の厚さは、１０〜２００μ
ｍの範囲に形成される。また、弾性ロールを構成する弾
性材料としては、シリコーンゴム等の各種ゴム、スポン
ジゴム、ウレタンフォーム等が使用され、これらには導
電性粉末が含有されていてもよい。また、弾性ロールの
表面には導電性塗料が塗布されたものであってもよい。As described above, the developing roll 5 has a two-layer structure in which the toner carrying layer is formed on the surface and the elastic roll is provided inside. The toner carrying layer is preferably made of a conductive material or has a conductive layer so that a bias voltage can be applied. The toner carrying layer is composed of a thin resin layer having a suitable elasticity, and a resin having a film forming property such as a fluorine-containing resin, a silicone resin, a polyester resin, and a polycarbonate resin is used. The thickness of the toner carrying layer is 10 to 200 μm.
m. As the elastic material constituting the elastic roll, various rubbers such as silicone rubber, sponge rubber, urethane foam and the like are used, and these may contain a conductive powder. Further, the surface of the elastic roll may be coated with a conductive paint.
【０００８】本発明は上記の現像方式に好適に使用する
静電荷現像用トナーに関するもので、その特徴とすると
ころは、トナー粒子の表面にＢＥＴ比表面積とタップ密
度が次の関係を有するアルミナ粒子が付着されているこ
とにある。The present invention relates to a toner for electrostatic charge development suitably used in the above-mentioned developing method. The feature of the present invention is that alumina particles having a BET specific surface area and a tap density having the following relationship on the surface of the toner particles are provided. Is attached.
【数４】 本発明の特徴とするアルミナ粒子は、無水塩化アルミニ
ウムを高温（火炎）加水分解することにより製造された
超微粒子のアルミナ等であって、その表面はカップリン
グ処理剤で処理されていてもよい。アルミナ粒子のＢＥ
Ｔ比表面積（Ａ）とタップ密度（Ｂ）との関係がＡ／Ｂ
＜４×１０ -6 ｍ 5 ／ｇ 2 を満足するためには、アルミナ粒
子の形状を選択することによって調整することができる
し、またカップリング処理剤で処理する場合はカップリ
ング処理剤の種類、処理量によって調整することが可能
である。カップリング処理剤としては、ジメチルシリコ
ーン、メチルトリメトキシシラン、（３−アミノプロピ
ル）トリメトキシシラン、（３−アミノプロピル）トリ
エトキシシラン、｛３−（２−アミノエトキシアミノ）
プロピル｝トリエトキシシラン、｛３−（２−アミノエ
トキシアミノ）プロピル｝トリメトキシシラン、Ｃ8Ｆ
17ＳＯ2ＮＣ2Ｈ5（ＣＨ2）3Ｓｉ（ＣＨ3Ｏ）3等があげ
られる。 (Equation 4) The alumina particles featured in the present invention are ultrafine alumina or the like produced by subjecting anhydrous aluminum chloride to high-temperature (flame) hydrolysis, and the surface thereof may be treated with a coupling agent. BE of alumina particles
The relationship between T specific surface area (A) and tap density (B) is A / B
In order to satisfy <4 × 10 −6 m 5 / g 2 , the shape can be adjusted by selecting the shape of the alumina particles, and when treating with a coupling agent, the type of the coupling agent Can be adjusted according to the processing amount. Examples of the coupling agent include dimethyl silicone, methyltrimethoxysilane, (3-aminopropyl) trimethoxysilane, (3-aminopropyl) triethoxysilane, and {3- (2-aminoethoxyamino)}.
Propyl} triethoxysilane, {3- (2-aminoethoxy) propyl} trimethoxy silane, C 8 F
17 SO 2 NC 2 H 5 (CH 2 ) 3 Si (CH 3 O) 3 and the like.
【０００９】本発明においてアルミナ粒子のＢＥＴ比表
面積を測定する方法としては、市販の高精度自動ガス吸
着装置（日本ベル社製、商品名ＢＥＬＳＯＲＰ２８）等
により測定する。この場合、ＢＥＴ比表面積は吸着ガス
として不活性ガスであるＮ2ガスを用いるものである。
具体的にはアルミナ粒子の表面に単分子層を形成するの
に必要な吸着量Ｖｍ（ｃｍ 3 ／ｇ）を測定し、次式にお
いてＢＥＴ比表面積Ｓ（ｍ2／ｇ）を求めることができ
る。 Ｓ＝４．３５×Ｖｍ（ｍ2／ｇ） また、タップ密度は細川ミクロン社製のパウダーテスタ
ーＴＹＰＥ ＰＴ−Ｅを用いて次の通り測定して得るも
のである。すなわち、パウダーテスターの測定用カップ
（内容積：１００ｃｍ3）にアルミナ粒子をすり切り一
杯入れ、１８０秒間タッピングを行う。このタッピング
時にアルミナ粒子は圧縮されるが、圧縮され減少した分
適宜補充する。タッピング終了後、余分なアルミナ粒子
をブレードですり切った後アルミナ粒子の重量（Ｗ）を
測定し、次の式によりタップ密度を得ることができる。 タップ密度＝Ｗ／（ｇ／１００ｃｍ3）In the present invention, as a method for measuring the BET specific surface area of the alumina particles, a commercially available high-precision automatic gas adsorption device (BELSORP28, manufactured by Bell Japan, Inc.) or the like is used. In this case, the BET specific surface area uses N 2 gas which is an inert gas as the adsorption gas.
Specifically, the amount of adsorption Vm ( cm 3 / g) required to form a monomolecular layer on the surface of the alumina particles is measured, and the BET specific surface area S (m 2 / g) can be obtained by the following equation. . S = 4.35 × Vm (m 2 / g) The tap density is obtained by using a powder tester TYPE PT-E manufactured by Hosokawa Micron as follows. That is, the alumina particles are put into a measuring cup (inner volume: 100 cm 3 ) of a powder tester, and the tapping is performed for 180 seconds. During the tapping, the alumina particles are compressed, and the compressed and reduced alumina particles are appropriately replenished. After completion of the tapping, excess alumina particles are cut off with a blade, and the weight (W) of the alumina particles is measured. The tap density can be obtained by the following equation. Tap density = W / (g / 100cm 3 )
【００１０】前記アルミナ粒子は、ＢＥＴ比表面積／タ
ップ密度が４×１０ -6 ｍ 5 ／ｇ 2 未満でなければならな
い。４×１０ -6 ｍ 5 ／ｇ 2 より大きい場合は、膜削れが発
生し画像のカスレが生じたり、流動性が低下して現像時
に補給トナーが十分補給されないために画像濃度の低下
等の問題が発生する。また、アルミナ粒子は上記関係を
満足させるため球形状のものが好ましく、球形状のアル
ミナ粒子は感光体表面上へのダメージが少なく、膜削れ
が生じにくいため好ましい。また、アルミナ粒子の体積
平均粒子径は０．２〜３μｍであることが好ましく、
０．２μｍ未満の場合はフィルミング防止効果が少な
く、３μｍより大きい場合はトナーの流動性が低下しや
すい。このような本発明に適用されるアルミナ粒子とし
ては住友化学社製のスミコランダムＡＡ−０．４やスミ
コランダムＡＡ−２等が上市されている。アルミナ粒子
の付着量はトナー粒子１００重量部に対して０．２〜
１．５重量部であることが好ましく、０．２重量部未満
ではトナーフィルミングへの研磨効果がなく、１．５重
量部より多い場合は膜削れが発生し画像のカスレが生じ
たり、高温高湿環境下において地カブリが多く発生する
等の問題が生じやすい。The alumina particles must have a BET specific surface area / tap density of less than 4 × 10 −6 m 5 / g 2 . If it is larger than 4 × 10 −6 m 5 / g 2 , problems such as a decrease in image density due to film shaving and blurring of the image or a decrease in fluidity and insufficient supply of replenishing toner during development. Occurs. Further, the alumina particles are preferably spherical in order to satisfy the above relationship, and the spherical alumina particles are preferable because damage to the surface of the photoreceptor is small and film abrasion hardly occurs. Further, the volume average particle diameter of the alumina particles is preferably 0.2 to 3 μm,
If it is less than 0.2 μm, the effect of preventing filming is small, and if it is more than 3 μm, the fluidity of the toner tends to be reduced. Examples of such alumina particles applicable to the present invention include Sumikoundum AA-0.4 and Sumikoundum AA-2 manufactured by Sumitomo Chemical Co., Ltd. The amount of alumina particles attached is 0.2 to 100 parts by weight of toner particles.
When the amount is less than 0.2 parts by weight, there is no polishing effect on toner filming. When the amount is more than 1.5 parts by weight, film abrasion occurs to cause image blurring or high temperature. In a high humidity environment, problems such as occurrence of a lot of ground fog are likely to occur.
【００１１】本発明においてアルミナ粒子をトナー粒子
表面に付着させる手段としては、トナーとアルミナ粒子
を混合した後、高速の剪断力を付与できる攪拌機で攪拌
することにより達成できる。例えばヘンシェルミキサ
ー、スーパーミキサー、タービュライザー、その他一般
的に粉体の表面改質機として使用されている奈良機械製
作所社のハイブリダイザー、ホソカワミクロン社のオン
グミル、ターボ工業社のターボミル等があげられる。そ
の際必要に応じてシリカ等の流動性改質剤を同時に添加
して付着させてもよい。In the present invention, the means for attaching the alumina particles to the surface of the toner particles can be achieved by mixing the toner and the alumina particles and then stirring the mixture with a stirrer capable of applying a high-speed shearing force. For example, a Henschel mixer, a super mixer, a turbulizer, a hybridizer of Nara Kikai Seisakusho, which is generally used as a surface reformer of powder, an ong mill of Hosokawa Micron, a turbo mill of Turbo Kogyo, etc. At that time, if necessary, a fluidity modifier such as silica may be simultaneously added and adhered.
【００１２】本発明の静電荷現像用トナーは上記で述べ
たアルミナ粒子を以下に述べるトナー粒子の表面に付着
させ作製することができる。すなわち、本発明を構成す
るトナー粒子は、結着樹脂、着色剤、電荷制御剤、その
他必要に応じて添加される添加剤を所定の配合にドライ
ブレンドし、この混合物をエクストルーダー、ロールミ
ル等を用いて溶融混練せしめ、得られた塊状体をジェッ
トミル等の機械的粉砕手段により粉砕して、所定の粒径
の粒子に分級して製造する。上記結着樹脂および着色剤
は、特に制限はなく、例えば結着樹脂としては、ポリス
チレン、ポリエステル、スチレン−アクリル酸エステル
共重合体、エチレン−塩化ビニル共重合体、エチレン−
酢酸ビニル共重合体、ポリアミド、ポリエチレン、マレ
イン酸樹脂、アクリル系樹脂、エポキシ樹脂、キシレン
樹脂、クマロン樹脂、ケトン樹脂、石油樹脂、フェノー
ル樹脂等が例示される。また、着色剤としては、例え
ば、カーボンブラック、アセチレンブラック、ランプブ
ラック、チャンネルブラック、ファーナルブルー、パー
マネントブルー、ニグロシンブルー、フタロシアニンブ
ルー、ローズベンガル、Ｃ．Ｉ．ピグメントレッド１２
２、Ｃ．Ｉ．ピグメントイエロー１２等が例示される。
これら着色剤は、結着樹脂１００重量部に対して１〜１
０重量部の範囲で適宜配合される。電荷制御剤として
は、従来使用されている電荷制御剤が使用できる。その
例としては、ニグロシン系染料、第四級アンモニウム
塩、トリフェニルメタン系、モノアゾ系金属錯体染料等
を挙げることができる。その他必要に応じて添加される
添加物として低分子量ポリオレフィン等を挙げることが
できる。また、流動性付与の目的で樹脂微粒子、疎水性
シリカ、コロイダルシリカ等をトナー粒子内部に含有す
ることもできる。本発明の静電荷現像用トナーは、前記
のとおり非磁性一成分現像方式に用いると極めて優れた
作用効果を奏するものであるが、この現像方式に限らず
キャリアと混合して二成分現像方式に用いたり、あるい
は前記トナー粒子内部に磁性粒子を含有させて磁性一成
分現像方式に用いたり、更に磁性粒子を含有した静電荷
現像用トナーをキャリアと混合して二成分現像方式に用
いても本願発明の作用効果を得ることができる。The toner for electrostatic charge development of the present invention can be produced by attaching the above-mentioned alumina particles to the surface of the following toner particles. That is, the toner particles constituting the present invention are obtained by dry blending a binder resin, a colorant, a charge control agent, and other additives to be added as required into a predetermined composition, and extruding the mixture into an extruder, a roll mill, or the like. The resulting mass is pulverized by a mechanical pulverizing means such as a jet mill and classified into particles having a predetermined particle size. The binder resin and the colorant are not particularly limited, and examples of the binder resin include polystyrene, polyester, styrene-acrylate copolymer, ethylene-vinyl chloride copolymer, and ethylene-
Examples include vinyl acetate copolymer, polyamide, polyethylene, maleic acid resin, acrylic resin, epoxy resin, xylene resin, coumarone resin, ketone resin, petroleum resin, phenol resin and the like. Examples of the coloring agent include carbon black, acetylene black, lamp black, channel black, farnal blue, permanent blue, nigrosine blue, phthalocyanine blue, rose bengal, C.I. I. Pigment Red 12
2, C.I. I. Pigment Yellow 12 and the like.
These colorants are used in an amount of 1 to 1 based on 100 parts by weight of the binder resin.
It is appropriately blended in a range of 0 parts by weight. As the charge control agent, a conventionally used charge control agent can be used. Examples thereof include nigrosine dyes, quaternary ammonium salts, triphenylmethane dyes, and monoazo metal complex dyes. Other additives that may be added as needed include low molecular weight polyolefins. Further, resin particles, hydrophobic silica, colloidal silica or the like may be contained in the toner particles for the purpose of imparting fluidity. As described above, the toner for electrostatic charge development of the present invention has an extremely excellent effect when used in the non-magnetic one-component developing system. However, the toner is not limited to this developing system but may be mixed with a carrier to form a two-component developing system. The present invention can be applied to a magnetic one-component developing method in which magnetic particles are contained inside the toner particles, or a toner for electrostatic charge development containing magnetic particles is mixed with a carrier and used in a two-component developing method. The operation and effect of the invention can be obtained.
【００１３】[0013]
【実施例】以下、実施例にしたがって本発明を説明する
がこれに限定されるものではない。なお、以下に記す部
とは重量部を示す。 ＜実施例１＞ 上記の配合で原料をスーパーミキサーで混合した後、エ
クストルーダーで１６５℃の温度で溶融混練し、ジェッ
トミル粉砕機で微粉砕して風力分級機で分級を行い、体
積平均粒子径が８．５μｍのトナー粒子を得た。次に該
トナー粒子１００重量部に対しアルミナ粒子Ａ（住友化
学社製 商品名：スミコランダムＡＡ−０．４）０．５
重量部及び疎水性シリカ（ヘキストジャパン社製 商品
名：ＨＶＫ−２１５０）０．６重量部をヘンシェルミキ
サーを使用して２分間撹拌混合しトナー粒子表面に付着
させ本発明の静電荷現像用トナーを得た。 ＜実施例２＞実施例１において、アルミナ粒子Ａを１．
５重量部に変更した以外は同様にして本発明の静電荷現
像用トナーを得た。The present invention will be described below with reference to examples, but the present invention is not limited to these examples. In addition, the part described below shows a weight part. <Example 1> After mixing the raw materials in the above-mentioned composition with a super mixer, melt kneading at a temperature of 165 ° C. with an extruder, finely pulverizing with a jet mill pulverizer and classifying with an air classifier, the volume average particle diameter is 8.5 μm Was obtained. Next, 0.5 parts of alumina particles A (trade name: Sumicorundum AA-0.4, manufactured by Sumitomo Chemical Co., Ltd.) are added to 100 parts by weight of the toner particles.
Parts by weight and 0.6 parts by weight of hydrophobic silica (trade name: HVK-2150, manufactured by Hoechst Japan Co., Ltd.) are stirred and mixed for 2 minutes using a Henschel mixer and adhered to the surface of the toner particles to prepare the toner for electrostatic charge development of the present invention. Obtained. <Example 2> In Example 1, alumina particles A were used in the same manner as in Example 1.
An electrostatic charge developing toner of the present invention was obtained in the same manner except that the amount was changed to 5 parts by weight.
【００１４】＜実施例３＞実施例１において、アルミナ
粒子Ａを０．２重量部に変更した以外は同様にして本発
明の静電荷現像用トナーを得た。 ＜実施例４＞実施例１において、アルミナ粒子Ａをアル
ミナ粒子Ｂ（住友化学社製 商品名：スミコランダムＡ
Ａ−２）０．５重量部に変更した以外は同様にして本発
明の静電荷現像用トナーを得た。Example 3 A toner for electrostatic charge development of the present invention was obtained in the same manner as in Example 1, except that the alumina particles A were changed to 0.2 parts by weight. <Example 4> In Example 1, alumina particles A were replaced with alumina particles B (trade name: Sumicorundum A manufactured by Sumitomo Chemical Co., Ltd.).
A-2) A toner for electrostatic charge development of the present invention was obtained in the same manner except that the amount was changed to 0.5 part by weight.
【００１５】＜比較例１＞実施例１において、アルミナ
粒子Ａをアルミナ粒子Ｃ（住友化学社製 商品名：ＡＫ
Ｐ−３０）０．５重量部に変更した以外は同様にして比
較用の静電荷現像用トナーを得た。 ＜比較例２＞実施例１において、アルミナ粒子Ａをアル
ミナ粒子Ｄ（住友化学社製 商品名：ＡＫＰ−３００
０）０．５重量部に変更した以外は同様にして比較用の
静電荷現像用トナーを得た。<Comparative Example 1> In Example 1, alumina particles A were replaced with alumina particles C (trade name: AK, manufactured by Sumitomo Chemical Co., Ltd.).
P-30) A comparative toner for developing electrostatic charge was obtained in the same manner except that the amount was changed to 0.5 part by weight. <Comparative Example 2> In Example 1, alumina particles A were replaced with alumina particles D (trade name: AKP-300, manufactured by Sumitomo Chemical Co., Ltd.).
0) A comparative electrostatic charge developing toner was obtained in the same manner except that the amount was changed to 0.5 parts by weight.
【００１６】＜比較例３＞実施例１において、アルミナ
粒子Ａをマグネタイト粒子（戸田工業社製 商品名：Ｍ
ＡＴ−３０５）０．５重量部に変更した以外は同様にし
て比較用の静電荷現像用トナーを得た。 ＜比較例４＞実施例１において、アルミナ粒子を付着し
ない以外は同様にして比較用の静電荷現像用トナーを得
た。Comparative Example 3 In Example 1, alumina particles A were replaced with magnetite particles (trade name: M, manufactured by Toda Kogyo KK)
AT-305) A comparative electrostatic charge developing toner was obtained in the same manner except that the amount was changed to 0.5 part by weight. Comparative Example 4 A comparative electrostatic developing toner was obtained in the same manner as in Example 1, except that no alumina particles were attached.
【００１７】前記実施例及び比較例で使用したアルミナ
粒子等の特性を表１に示す。Table 1 shows the characteristics of the alumina particles and the like used in the above Examples and Comparative Examples.
【表１】 [Table 1]
【００１８】次に上記各静電荷現像用トナーを、図１の
現像機構を有する市販の非磁性一成分現像方式のレーザ
ーファックス（三洋電機社製 商品名：ＳＰＦ−３１３
有機感光体を使用）を用いて、常温常湿（２０℃、６
５％ＲＨ）の環境下において２００００枚までプリント
を行い、その結果を表２に示した。なお、上記表におい
て、「画像濃度」はベタ画像をマクベス反射濃度計ＲＤ
−９１４で測定し、「地カブリ」は非画像部を日本電色
工業社製の色差計Ｚ−１００１ＤＰで測定した値であ
る。また、「文字抜け」とはＡ４の転写紙１頁に記号
「ｉ」を３０個印字し、該印字された記号を拡大鏡を用
いて目視で文字の欠損が発生しているかの確認を行い、
文字欠損が発生した記号の個数を記したものである。な
お、文字抜けは１５以下であれば実用範囲内である。ま
た、「画像カスレ」は、縦ラインのパターンでのライン
切れについて目視評価し、ライン切れの生じなかったも
のを○、ライン切れの生じたものを×とした。また、
「フィルミング」は感光体表面を目視にて観察し、フィ
ルミングが生じないで転写画像に問題がないものを○、
フィルミングは生じているが転写画像に問題がないもの
を△、フィルミングが生じ且つ転写画像に画像抜け等の
問題が生じたものを×とした。「膜削れ」は、キーエン
ス社製のレーザーフォーカス変位計ＬＴ−８０１０を用
い、現像に用いていない新品の感光体の表面厚さとの差
を示した。なお、実用上支障のない膜削れは５μｍ以下
である。Next, each of the above-mentioned toners for electrostatic charge development is supplied to a commercially available non-magnetic one-component developing laser facsimile having a developing mechanism shown in FIG. 1 (trade name: SPF-313, manufactured by Sanyo Electric Co., Ltd.).
Room temperature (20 ° C., 6
In an environment of 5% RH), printing was performed up to 20,000 sheets, and the results are shown in Table 2. In the above table, “image density” refers to a solid image taken by a Macbeth reflection densitometer RD.
The measurement was performed at −914, and “ground fog” was a value obtained by measuring the non-image portion with a color difference meter Z-1001DP manufactured by Nippon Denshoku Industries Co., Ltd. In addition, "missing characters" means that 30 symbols "i" are printed on one page of A4 transfer paper, and the printed symbols are visually checked with a magnifying glass to determine whether or not character loss has occurred. ,
This is the number of symbols with missing characters. Note that if the number of missing characters is 15 or less, it is within the practical range. As for “image blurring”, line breaks in the vertical line pattern were visually evaluated, and those without line breaks were evaluated as ○, and those with line breaks as x. Also,
"Filming" is to visually observe the surface of the photoreceptor,
A sample where filming occurred but there was no problem in the transferred image was rated as A, and a film where filming occurred and a problem such as image omission occurred in the transferred image was rated as x. “Film shaving” indicates a difference from the surface thickness of a new photoconductor not used for development, using a laser focus displacement meter LT-8010 manufactured by Keyence Corporation. In addition, film shaving that does not hinder practical use is 5 μm or less.
【００１９】[0019]
【表２】 [Table 2]
【００２０】上記表２の結果から明らかなように本発明
の静電荷現像用トナーは、初期から２００００枚後まで
画像濃度が１．３４以上と実用上十分あり、地カブリも
０．８３以下と実用上問題のない範囲であり、文字抜
け、画像カスレ及びフィルミングの発生も少なく実用上
問題のない結果であった。これに対し、比較例１及び２
は２００００枚プリント後の画像濃度が低く、感光体ド
ラムからの静電荷現像用トナーの転写性が悪いために文
字抜けが多く生じた。また、膜削れについても実施例の
ものよりも厚く削れ感光体表面へのダメージが大ききこ
とが確認され、その結果画像上に画像カスレが多く発生
した。また、比較例３及び４ではフィルミングが発生
し、文字抜けが多く、実用上問題のある結果であった。As is clear from the results shown in Table 2, the toner for electrostatic charge development of the present invention has a practically sufficient image density of 1.34 or more from the initial stage to after 20,000 sheets, and has a ground fog of 0.83 or less. This was within the range where there was no problem in practical use, and there were few occurrences of character omission, image blur and filming, and there was no problem in practical use. On the other hand, Comparative Examples 1 and 2
The image density after printing 20,000 sheets was low, and the lack of transferability of the toner for electrostatic charge development from the photosensitive drum caused many missing characters. Further, it was confirmed that the film was abraded thicker than that of the example, and the damage to the surface of the photoreceptor was large. Further, in Comparative Examples 3 and 4, filming occurred, many characters were missing, and the result was a problem in practical use.
【００２１】[0021]
【発明の効果】本発明の静電荷現像用トナーは、画像濃
度や地カブリといった基本的な画像特性を維持しながら
文字抜け及び画像カスレ等の画像欠損のない良好な画像
を得ることができる。また、感光体表面へのダメージが
少ないため、感光体の寿命が長く長期に渡り使用するこ
とができる効果を奏する。As described above, the toner for developing an electrostatic charge according to the present invention can obtain a good image without image defects such as missing characters and image blur while maintaining basic image characteristics such as image density and background fog. Further, since the damage to the surface of the photoreceptor is small, there is an effect that the life of the photoreceptor is long and the photoreceptor can be used for a long time.
【図１】本発明の静電荷現像用トナーが用いられる装置
の概略構成図である。FIG. 1 is a schematic configuration diagram of an apparatus using an electrostatic charge developing toner of the present invention.
１ 感光体ドラム ２ ホッパー ３ 静電荷現像用トナー ４ａ トナー層厚規制部材 ４ｂ 固定部材 ５ 現像ロール ６ トナーの漏れ防止及びかき落し部材 ７ 攪拌機 DESCRIPTION OF SYMBOLS 1 Photoreceptor drum 2 Hopper 3 Toner for electrostatic charge development 4a Toner layer thickness regulating member 4b Fixing member 5 Developing roll 6 Toner leakage prevention and scraping member 7 Stirrer
Claims (3)
トナー粒子の表面にＢＥＴ比表面積とタップ密度が次の
関係を有するアルミナ粒子を付着させたことを特徴とす
る静電荷現像用トナー。【数１】 1. A toner for electrostatic charge development, wherein alumina particles having a BET specific surface area and a tap density having the following relationship are attached to the surface of toner particles containing at least a binder resin and a colorant. (Equation 1)
トナー粒子の表面にＢＥＴ比表面積とタップ密度が次の
関係を有するアルミナ粒子を付着させたことを特徴とす
る非磁性一成分現像方式用の静電荷現像用トナー。【数２】 2. A non-magnetic one-component developing system characterized in that alumina particles having a BET specific surface area and a tap density having the following relationship are adhered to the surface of toner particles containing at least a binder resin and a colorant. For electrostatic charge development. (Equation 2)
０重量部に対して０．２〜１．５重量部であることを特
徴とする請求項１記載の静電荷現像用トナー。3. The toner particles having an adhesion amount of alumina particles of 10
2. The electrostatic charge developing toner according to claim 1, wherein the amount is 0.2 to 1.5 parts by weight with respect to 0 parts by weight.