JP3129597B2 - Pressure-sensitive recording sheet - Google Patents
Pressure-sensitive recording sheetInfo
- Publication number
- JP3129597B2 JP3129597B2 JP06051485A JP5148594A JP3129597B2 JP 3129597 B2 JP3129597 B2 JP 3129597B2 JP 06051485 A JP06051485 A JP 06051485A JP 5148594 A JP5148594 A JP 5148594A JP 3129597 B2 JP3129597 B2 JP 3129597B2
- Authority
- JP
- Japan
- Prior art keywords
- pressure
- sensitive recording
- recording sheet
- electron
- paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本発明は感圧記録シート、特にバ
ーコード読取り用感圧記録シートに関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a pressure-sensitive recording sheet, and more particularly to a pressure-sensitive recording sheet for reading a bar code.
【０００２】[0002]
【従来の技術】感圧記録シートは、電子供与性有機発色
剤等を油に溶解し、その油滴をカプセル化したマイクロ
カプセルを主成分とする発色剤マイクロカプセル組成物
を基材の片面に塗布した上用紙、基材の片面には上記発
色剤と接触したとき発色する電子受容性顕色剤組成物を
塗布し、反対面には発色剤マイクロカプセル組成物を塗
布した中用紙、基材の片面に顕色剤を塗布した下用紙、
基材の同一面上発色剤マイクロカプセル組成物と顕色剤
組成物を塗布した自己発色紙、基材の一部に発色剤マイ
クロカプセル組成物あるいは顕色剤組成物をインキとし
て部分的に印刷したものなどがある。これらの感圧記録
シートは発色が得られるように組み合わせられるが、上
用紙・下用紙の複写セット、あるいは上用紙・下用紙の
間に中用紙を挟んだ多枚数の複写セットが一般的な組み
合わせである。感圧記録シートの組み合わせは、圧力に
より同時に多数枚の複写が得られることから、販売伝
票、配送伝票等の各種伝票類、あるいは契約書等に利用
されている。2. Description of the Related Art A pressure-sensitive recording sheet is prepared by dissolving an electron-donating organic color-forming agent or the like in oil, and coating a color-forming agent microcapsule composition mainly composed of microcapsules in which oil droplets are encapsulated on one surface of a substrate. On the coated upper paper, one side of the base material is coated with an electron-accepting developer composition that forms a color when it comes into contact with the above color former, and on the other side, a medium paper or base material coated with the color former microcapsule composition Paper with a developer applied to one side of
Self-coloring paper coated with a color former microcapsule composition and a color developer composition on the same surface of the substrate, and partially printed with a color former microcapsule composition or a color developer composition as ink on a part of the substrate And others. These pressure-sensitive recording sheets are combined so as to obtain color, but a common combination is a copy set of upper and lower sheets, or a large number of copy sets with middle sheets between upper and lower sheets. It is. The combination of pressure-sensitive recording sheets is used for various slips such as sales slips and delivery slips, or contracts, since many copies can be obtained simultaneously by pressure.
【０００３】一方近年、省力化の一環として、伝票類に
必要な情報をバーコードで付与し、そのバ−コ−ドをバ
ーコードリーダーで読取り、コンピュ−タ−に自動的に
入力する方法が盛んに行われている。感圧記録シートの
組み合わせによる伝票類においても、バ−コ−ドをドッ
トインパクトプリンターで印字し、発色したバ−コ−ド
画像をバーコードリーダーで入力する機会が多くなって
きた。On the other hand, in recent years, as a part of labor saving, a method has been proposed in which necessary information is added to slips using a barcode, the barcode is read by a barcode reader, and the information is automatically input to a computer. It is being actively performed. Even in slips formed by a combination of pressure-sensitive recording sheets, the bar code is printed by a dot impact printer, and a color bar code image is input by a bar code reader.
【０００４】[0004]
【発明が解決しようとする課題】しかしながら、バーコ
ード読取り装置に使用されている公知の感圧複写シート
を使用した場合、印字されたバーコードが太くなった
り、鮮明度が不十分なことから読取り率が低いという問
題があり、特に、複写されたバ−コ−ドにこの傾向が強
い。However, when a known pressure-sensitive copying sheet used in a bar code reader is used, the printed bar code becomes thicker or has insufficient sharpness. There is a problem that the rate is low, and this tendency is particularly strong in a copied bar code.
【０００５】[0005]
【課題を解決するための手段】そこで本発明者らは、こ
れら問題を解決するため種々検討を重ねた結果、基材と
してポリエステルから作られた合成紙を使用し、厚さ５
０μｍ以下，不透明度７０％以上の感圧記録シートを使
用することで、バーコードの読取り率が著しく改善され
ることを見出した。The inventors of the present invention have conducted various studies to solve these problems, and as a result, have used a synthetic paper made of polyester as a base material and having a thickness of 5%.
It has been found that the use of a pressure-sensitive recording sheet having an opacity of not more than 0 μm and an opacity of not less than 70% significantly improves the barcode reading rate.
【０００６】すなわち、ポリエステルから作られた合成
紙を基材とし、その表面あるいは裏面に、マイクロカプ
セル組成物、あるいは顕色剤組成物を塗布し、厚さ５０
μｍ以下、不透明度７０％以上の感圧記録シートとする
ことで、ドットインパクトプリンターで印字したバーコ
ードの解像度、鮮明度が改善され、更に、転写性（複写
性）も改善される。従って、例えば、ポリエステルから
作られた合成紙を基材とした上用紙を通常の紙を基材と
した中用紙、下用紙と組み合わせると、２枚目の中用紙
あるいは下用紙に複写されたバーコード印字の太りが小
さく、均一な太さの鮮明度が改善されたバーコード像が
得られるので、読取り率が向上する。That is, a synthetic paper made of polyester is used as a base material, and a microcapsule composition or a color developer composition is applied to the front or back surface thereof, and a thickness of 50% is applied.
By using a pressure-sensitive recording sheet having a thickness of not more than μm and an opacity of not less than 70%, the resolution and sharpness of a barcode printed by a dot impact printer are improved, and the transferability (copyability) is also improved. Therefore, for example, when upper paper based on synthetic paper made of polyester is combined with middle paper based on ordinary paper and lower paper, a bar copied on the second middle paper or lower paper is used. Since a bar code image with a small thickness of code printing and improved sharpness of a uniform thickness is obtained, the reading rate is improved.
【０００７】また、ポリエステルから作られた合成紙を
基材とした感圧記録シートの不透明度を７０％以上にす
ることが必要で、不透明度が７０％未満の場合、その下
の印字画像の影響で、感圧記録シート上のバーコードの
読取り率が下がり、本発明の目的は達成されない。Further, it is necessary that the opacity of a pressure-sensitive recording sheet based on synthetic paper made of polyester be 70% or more. Due to the influence, the reading rate of the barcode on the pressure-sensitive recording sheet decreases, and the object of the present invention is not achieved.
【０００８】本発明の感圧記録シートは、基材にマイク
ロカプセル組成物あるいは顕色剤組成物を基材のそれぞ
れの面に別々に、あるいは同一面に重ねて塗布、乾燥し
て作成する。これら組成物は、公知の感圧記録シートに
使用されているものと同様に作成する。即ち、マイクロ
カプセル組成物は、油に溶解した電子供与性発色剤をマ
イクロカプセル化し、低圧破壊抑制剤、バインダ−など
とともに混合したものであり、顕色剤組成物は、顕色剤
とバインダ−などとともに混合したものであって、通常
水分散系の組成物である。これら組成物の塗布は、コ−
タ−により行われる。コ−タ−は、エアーナイフコータ
ー、ブレードコーター、カーテンコーター、ロッドコー
ター、ロールコーター等が使用される。本発明の組成物
は水系組成物として取り扱うことが適当なので、塗布後
の乾燥は、加熱乾燥が適当である。基材の耐熱性が不足
している場合には、乾燥ゾーン通過の際に基材が熱と張
力により伸びを生じ、塗工が出来なくなる。ポリエステ
ル系合成紙を基材とする本発明にあっては、ポリエステ
ル系合成紙の耐熱性が良好であり、水系組成物の加熱乾
燥に耐えられるので、コーターで問題なく塗工すること
が出来る。[0008] The pressure-sensitive recording sheet of the present invention is prepared by applying the microcapsule composition or the developer composition on the substrate separately or on the same surface of the substrate separately and drying. These compositions are prepared in the same manner as those used for known pressure-sensitive recording sheets. That is, the microcapsule composition is obtained by microencapsulating an electron-donating color former dissolved in oil and mixing it with a low-pressure destruction inhibitor, a binder, and the like. The developer composition comprises a developer and a binder. And the like, and is usually a water-dispersed composition. Coating of these compositions is
This is done by a charter. As the coater, an air knife coater, blade coater, curtain coater, rod coater, roll coater or the like is used. Since the composition of the present invention is suitably handled as an aqueous composition, drying after application is preferably performed by heating and drying. If the heat resistance of the substrate is insufficient, the substrate undergoes elongation due to heat and tension when passing through the drying zone, and coating cannot be performed. In the present invention using a polyester-based synthetic paper as a base material, the polyester-based synthetic paper has good heat resistance and can withstand heat-drying of an aqueous composition, so that it can be coated without any problem with a coater.
【０００９】本発明のポリエステル系合成紙は、ポリエ
ステルフィルムの内部に填料を内填したり、あるいは内
部に空隙（ボイド）を作成することによって不透明度を
高めると共に、ポリエステルの少なくとも片面に水溶性
高分子や熱可塑性水性エマルジョンを主成分とする塗料
を単独であるいは併用して塗布したり、これらに白色顔
料を混合して塗布するなどの方法により、水性インキ受
理性と筆記性を付与することにより、紙のように使用す
ることができるようにしたものである。[0009] The polyester synthetic paper of the present invention enhances the opacity by filling a filler inside the polyester film or forming voids (voids) inside the polyester film. By applying a coating containing a molecule or a thermoplastic aqueous emulsion as a main component alone or in combination, or by applying a mixture of white pigments to these to impart aqueous ink receptivity and writability. It can be used like paper.
【００１０】本発明において使用することができる電子
供与性発色剤は、顕色剤と反応してできる発色部が６２
０〜７２０ｎｍの波長領域に比較的大きな吸収を有する
ものを使用する必要があり、発色部がこの領域の吸収を
有するものであれば何でも良い。The electron-donating color-forming agent that can be used in the present invention has a color-forming portion formed by reaction with a color developer.
It is necessary to use a material having a relatively large absorption in a wavelength region of 0 to 720 nm, and any color-forming portion having an absorption in this region may be used.
【００１１】具体的には、次のような化合物を例示する
ことができる。 3,3-ビス［2-(4- ジメチルアミノフェニル)-2-(4- メト
キシフェニル）エチニル］4,5,6,7-テトラクロロフタリ
ド 3,3-ビス［2-2-ビス（4-ジメチルアミノフェニル）エチ
ニル］4,5,6,7-テトラクロロフタリド 3,3-ビス［2-2-ビス( 4-ジメチルアミノフェニル）エチ
ニル］-5--ピロリジノフタリド 3,3-ビス［2-2-ビス( 4-ジメチルアミノフェニル）エチ
ニル］-5- アザフタリド 3,3-ビス［2-(p- メトキシフェニル）-2-(p-ピロリジノ
フェニル）エチニル］4,5,6,7-テトラクロロフタリド 3,3-ビス［2-(p- メチルフェニル）-2-(p-ピロリジノフ
ェニル）エチニル］4,5,6,7-テトラクロロフタリド 3,3-ビス［2-（p-メトキシフェニル）-2-(p-ジメチルア
ミノフェニル）エチニル］4,5,6,7-テトラクロロフタリ
ド 6'- ［｛4-(4- アニリノ) アニリノ｝アニリノ］-2'-ク
ロル-3'-メチルスピロ［フタリド-3,9- キサンテン］ 3-(N-p- トリル-N- エチルアミノ）-7-(N-フェニル-N-
メチル）フルオラン6'- ｛4-(4- アニリノ) アニリノ｝
-2'-フェニルアミノ- ３' -メチルスピロ［フタリド-
3,9- キサンテン］ 6'- ジエチルアミノ-2- ｛4-(4- アニリノ) アニリノ｝
-2'-フェニルアミノ-３' - メチルスピロ［フタリド-3,
9- キサンテン］ 3-3-ビス（4 '-ジメチルアミノ-2- メトキシフェニル）
-4- アザフタリド、3-3 ビス（4 '-ジエチルアミノ-2-
エトキシフェニル）-4- アザフタリド 3,6-ジ(N - ジメチルアミノ）- フルオレン-9- スピロ
-3' -(6'- ジメチルアミノ）フタリド 3-ジエチルアミノ〔ａ〕（2,2-ジメチル-4- メチル）-
ピリジノ- フルオラン 3-(N-p- トリル-N- エチルアミノ）-(1'-N- エチル-2'
2'4'-トリメチル- ピリジル）-[a]- フルオランSpecifically, the following compounds can be exemplified. 3,3-bis [2- (4-dimethylaminophenyl) -2- (4-methoxyphenyl) ethynyl] 4,5,6,7-tetrachlorophthalide 3,3-bis [2-2-bis ( 4-dimethylaminophenyl) ethynyl] 4,5,6,7-tetrachlorophthalide 3,3-bis [2-2-bis (4-dimethylaminophenyl) ethynyl] -5-pyrrolidinophthalide 3, 3-bis [2-2-bis (4-dimethylaminophenyl) ethynyl] -5-azaphthalide 3,3-bis [2- (p-methoxyphenyl) -2- (p-pyrrolidinophenyl) ethynyl] 4, 5,6,7-tetrachlorophthalide 3,3-bis [2- (p-methylphenyl) -2- (p-pyrrolidinophenyl) ethynyl] 4,5,6,7-tetrachlorophthalide 3, 3-bis [2- (p-methoxyphenyl) -2- (p-dimethylaminophenyl) ethynyl] 4,5,6,7-tetrachlorophthalide 6 '-[{4- (4-anilino) anilino} Anilino] -2'-chloro-3'-methylspiro [phthalide-3,9- Santen] 3- (Np-tolyl -N- ethylamino)-7-(N-phenyl--N-
Methyl) fluoran 6 '-{4- (4-anilino) anilino}
-2'-Phenylamino-3'-methylspiro [phthalide-
3,9-Xanthen] 6'-diethylamino-2- {4- (4-anilino) anilino}
-2'-phenylamino-3'-methylspiro [phthalide-3,
9-Xanthen] 3-3-bis (4'-dimethylamino-2-methoxyphenyl)
-4-azaphthalide, 3-3 bis (4'-diethylamino-2-
Ethoxyphenyl) -4-azaphthalide 3,6-di (N-dimethylamino) -fluorene-9-spiro
-3 '-(6'-dimethylamino) phthalide 3-diethylamino [a] (2,2-dimethyl-4-methyl)-
Pyridino-fluoran 3- (Np-tolyl-N-ethylamino)-(1'-N-ethyl-2 '
2'4'-trimethyl-pyridyl)-[a] -fluoran
【００１２】また、これと組み合わせて使用できる感圧
複写紙の分野で公知となっている従来の感圧染料として
下記の具体例を挙げることができる。 3,3-ビス-(P-ジメチルアミノフェニル)-6-ジメチルアミ
ノフタリド 3,3-ビス-(p-ジエチルアミノフェニル)-6-ジメチルアミ
ノフタリド 3,3-ビス（2-メチル-1- オクチル-3- インドリル）フタ
リド 3-(P- ジメチルアミノフェニル)-3-(1,2- ジメチルイン
ドール-3- イン) フタリド 3,3-ビス(1,2- ジメチルインドール-3- イン)-5-ジメチ
ルアミノフタリド 3,3-ビス-(p-ジエチルアミノフェニル)-6-n-プロピルア
ミノフタリド等のトリアリルメタン系染料 ベンゾイルロイコメチレンブルー、p-ニトロベンゾイル
ロイコメチレンブルー等のチアジン系染料 1,3,3-トリメチル-6- ニトロ- インドリノ- ベンゾスピ
ロピラン 3-メチル- スピロ- ジナフトピラン 3-フェニル- スピロ- ジナフトピラン 3-プロピル- スピロ- ジナフトピラン等のスピロ系染料 3-ジエチルアミノ-6- メチル-7- ジエチルアニリノフル
オラン 3-ジエチルアミノ-6- メチル-7- アニリノフルオラン 3-ジブチルアミノ-6- メチル-7- アニリノフルオラン 3-(N- エチル-N- イソペンチルアミノ）-6- メチル-7-
アニリノフルオラン 3-(N- シクロヘキシル-N- メチルアミノ）-6- メチル-7
- アニリノフルオラン 3-ジエチルアミノ-7-(m-トリフルオロメチルアニリノ）
フルオラン 3-ジエチルアミノ-7-(o-フルオロアニリノ）フルオラン 3-ジ-n- ブチルアミノ-7-(o-フルオロアニリノ）フルオ
ラン 3-ジエチルアミノ-7- ジベンジルアミノフルオラン 3-ジエチルアミノ-5- メチル-7- ジベンジルアミノフル
オラン等のフルオラン系染料Further, the following specific examples can be given as conventional pressure-sensitive dyes known in the field of pressure-sensitive copying paper which can be used in combination therewith. 3,3-bis- (P-dimethylaminophenyl) -6-dimethylaminophthalide 3,3-bis- (p-diethylaminophenyl) -6-dimethylaminophthalide 3,3-bis (2-methyl-1 -Octyl-3-indolyl) phthalide 3- (P-dimethylaminophenyl) -3- (1,2-dimethylindole-3-yne) phthalide 3,3-bis (1,2-dimethylindole-3-yne) Triarylmethane dyes such as -5-dimethylaminophthalide 3,3-bis- (p-diethylaminophenyl) -6-n-propylaminophthalide Thiazine dyes such as benzoyl leucomethylene blue and p-nitrobenzoyl leucomethylene blue Spiro dyes such as 1,3,3-trimethyl-6-nitro-indolino-benzospiropyran 3-methyl-spiro-dinaphthopyran 3-phenyl-spiro-dinaphthopyran 3-propyl-spiro-dinaphthopyran 3-diethylamino-6-methyl- 7- diethyla Rinofuruoran 3-diethylamino-6-methyl-7-anilinofluoran 3-dibutylamino-6-methyl-7-anilinofluoran 3- (N- ethyl--N--isopentylamino) -6-methyl-7-
Anilinofluoran 3- (N-cyclohexyl-N-methylamino) -6-methyl-7
-Anilinofluoran 3-diethylamino-7- (m-trifluoromethylanilino)
Fluoran 3-diethylamino-7- (o-fluoroanilino) fluoran 3-di-n-butylamino-7- (o-fluoroanilino) fluoran 3-diethylamino-7-dibenzylaminofluoran 3-diethylamino-5 -Fluoran dyes such as methyl-7-dibenzylaminofluoran
【００１３】これらの電子供与性発色剤をカプセル化す
る場合、通常油（疎水性媒体）に溶解し、これを芯物質
として用いる。疎水性媒体としては感圧複写紙の分野で
公知となっている下記のごとき物質が例示される。フェ
ニルキシリルエタン、フェニルキシリルエタン、フェニ
ルエチルフェニルエタン、フェニルブチルフェニルメタ
ンの如きジアリールアルカン、モノイソプロピルナフタ
リン、ジノイソプロピルナフタリンの如きアルキルナフ
タリン、イソプロピルビフェニール、ブチルビフェニー
ルおよび部分水素添加ターフェニール、及びこれらを主
成分とする疎水性媒体。When these electron-donating color formers are encapsulated, they are usually dissolved in oil (hydrophobic medium) and used as a core substance. Examples of the hydrophobic medium include the following substances which are known in the field of pressure-sensitive copying paper. Phenylxylylethane, phenylxylylethane, phenylethylphenylethane, diarylalkanes such as phenylbutylphenylmethane, alkylnaphthalenes such as monoisopropylnaphthalene and dinoisopropylnaphthalene, isopropylbiphenyl, butylbiphenyl and partially hydrogenated terphenyl, and the like. A hydrophobic medium containing as a main component.
【００１４】本発明で用いられるマイクロカプセルは従
来公知のコアセルベーション法（例えば米国特許280045
7 号、同2800458 号等に示される方法）、界面重合法
（例えば特開昭57-140638 号公報 同60-227828 号公報
等に示される方法） in-situ重合法（例えば特公昭51-9
079 号公報同53-84881等に示される方法）等の方法によ
り製造される。The microcapsules used in the present invention can be prepared by a conventionally known coacervation method (for example, US Pat. No. 280045).
7, 2800458, etc.), an interfacial polymerization method (for example, a method described in JP-A-57-140638 and 60-227828), an in-situ polymerization method (for example, Japanese Patent Publication No. 51-9)
No. 079, JP-A-53-84881).
【００１５】顕色剤と反応して６２０〜７２０ｎｍの波
長領域に大きな吸収を有する上記電子供与性発色剤は、
通常前記疎水性媒体中に２〜１０重量％程度溶解し、視
認濃度の向上が必要な場合は従来の電子供与性発色剤を
併せて溶解し、前記カプセル化法でマイクロカプセル化
される。このようにして得られたマイクロカプセルスラ
リーは常法に従い、生澱粉などのマイクロカプセルの低
圧破壊抑制材と共に適当量のバインダーにより支持体上
に１〜８ g／ｍ2 程度塗布される。The above-mentioned electron-donating color former which has a large absorption in the wavelength range of 620 to 720 nm by reacting with the color developer,
Usually, about 2 to 10% by weight is dissolved in the above-mentioned hydrophobic medium, and when the visual density is required to be improved, a conventional electron-donating color former is also dissolved together and microencapsulated by the above-mentioned encapsulation method. The microcapsule slurry thus obtained is applied on a support with a suitable amount of a binder together with a low-capacity destruction inhibitor for microcapsules, such as raw starch, in an amount of about 1 to 8 g / m 2 according to a conventional method.
【００１６】この際使用されるバインダーとしてはスチ
レン−ブタジエン共重合体エマルジョン，ポリアクリル
エマルジョン、アクリル−スチレン共重合体エマルジョ
ン、ポリエステルエマルジョン等の合成樹脂エマルジョ
ン、ポリビニ−ルアルコール、澱粉、セルロース誘導体
等の水溶性バインダーを挙げることが出来る。Examples of the binder used in this case include synthetic resin emulsions such as styrene-butadiene copolymer emulsion, polyacryl emulsion, acryl-styrene copolymer emulsion and polyester emulsion, polyvinyl alcohol, starch and cellulose derivatives. Water-soluble binders can be mentioned.
【００１７】また、顕色剤としては酸性白土、活性白
土、アタパルジャイト、ゼオライト、ベントナイト等の
天然固体酸、芳香族カルボン酸の金属塩、フェノールホ
ルムアルデヒド樹脂およびこれら金属塩、カルボキシル
化テルペンフェノ−ル樹脂の金属塩を主成分とするも
の、およびこれらの混合物等が挙げられる。Examples of the color developing agent include acid clay, activated clay, natural solid acids such as attapulgite, zeolite and bentonite, metal salts of aromatic carboxylic acids, phenol formaldehyde resins and these metal salts, and carboxylated terpene phenol resins. And mixtures thereof as a main component.
【００１８】本発明による上用紙、中用紙、下用紙、自
己発色紙などの感圧記録シ−トは、これらのみで感圧複
写セットを構成することもできるし、従来の感圧複写セ
ットの一部に本発明の感圧記録シートを組み入れて感圧
複写セットを構成しても良い。The pressure-sensitive recording sheets according to the present invention, such as upper paper, middle paper, lower paper, and self-coloring paper, can form a pressure-sensitive copy set by themselves, or can be a conventional pressure-sensitive copy set. A pressure-sensitive copying sheet may be partially incorporated to form a pressure-sensitive copying set.
【００１９】以下、本発明を実施例により詳細に説明す
る。本発明の効果は、本発明の感圧記録シートが上用紙
の場合に最も顕著に得られることから、以下の実施例に
おいては、本発明の感圧記録シートが上用紙の場合につ
いて行った。Hereinafter, the present invention will be described in detail with reference to examples. Since the effect of the present invention is most remarkable when the pressure-sensitive recording sheet of the present invention is an upper sheet, in the following examples, the case where the pressure-sensitive recording sheet of the present invention is an upper sheet was performed.
【００２０】[0020]
［実施例１］ （カプセル化）アクリル酸−スチレンスルホン酸−アク
リル酸エチル共重合体（モノマー比85：8 ：7 分子量約
24万）の 5％水溶液 180部に尿素10部レゾルシン12部を
溶解した後20％苛性ソーダでPH3.4 とし親水性液体とし
た。次いで620 〜720nm の波長領域に吸収のある感圧染
料として5.0 部の3-3 ビス（4 '-ジエチルアミノ-2- エ
トキシフェニル）-4- アザフタリドと、視認濃度向上の
ため通常感圧染料である3-ジエチルアミノ-6- メチル-7
- ジエチルアニリノフルオラン3.0 部と3,3-ビス（2-メ
チル-1- オクチル-3- インドリル）フタリド 1部とを混
合し 117部のジイソプロピルナフタレンに溶解した疎水
性液体 125部を、先に調製して得た親水性液体中に激し
く撹拌しながら添加し平均粒径5.0 μの乳化液を得た。
次いで37％ホルマリン液27部をこの乳化液に加え撹拌を
続けながら55℃に昇温しこの温度で３時間カプセル化反
応をさせた後、系の温度を40℃に下げ28％アンモニア水
溶液でPH7.5 に調整しカプセル化を完了した。[Example 1] (Encapsulation) Acrylic acid-styrenesulfonic acid-ethyl acrylate copolymer (monomer ratio: 85: 8: 7, molecular weight: approx.
(240,000) 5% aqueous solution (180 parts) Dissolve urea (10 parts) resorcin (12 parts) and adjust to PH3.4 with 20% caustic soda to obtain hydrophilic liquid. Then, 5.0 parts of 3-3 bis (4'-diethylamino-2-ethoxyphenyl) -4-azaphthalide as a pressure-sensitive dye having an absorption in the wavelength region of 620 to 720 nm, and a normal pressure-sensitive dye for improving the visual density. 3-diethylamino-6-methyl-7
-A mixture of 3.0 parts of diethylanilinofluoran and 1 part of 3,3-bis (2-methyl-1-octyl-3-indolyl) phthalide, and 125 parts of a hydrophobic liquid dissolved in 117 parts of diisopropylnaphthalene are added. Was added with vigorous stirring to the obtained hydrophilic liquid to obtain an emulsion having an average particle size of 5.0 μm.
Next, 27 parts of a 37% formalin solution was added to the emulsion, and the mixture was heated to 55 ° C. while stirring and allowed to undergo an encapsulation reaction at this temperature for 3 hours. Adjusted to .5 and completed encapsulation.
【００２１】（試験紙の作成）上で作成したマイクロカ
プセル分散液 150部に、澱粉粒子20部とポリアクリルエ
マルジョン30部を添加し濃度が25％になるように水を加
えて得られたマイクロカプセル組成物を塗料とした。基
材は、ポリエステル上に水溶性高分子とポリエステルエ
マルジョンの混合物を主成分として塗布した厚さ25μｍ
の合成紙（東洋紡（株）製クリスパーG2311 ）を用い、
塗布面と反対側の裏面に、前記マイクロカプセル塗料を
エアーナイフコーターにより5 ｇ／ｍ2 塗布し、熱風乾
燥して、上用紙の感圧記録シートを得た。この時の上用
紙は、厚さ33μｍ，不透明度77％であった。不透明度は
JIS P 8138のＡ法で測定し、上用紙の表面と裏面で測定
した不透明度の平均値を、本発明の不透明度とした。(Preparation of Test Paper) A microcapsule obtained by adding 20 parts of starch particles and 30 parts of a polyacryl emulsion to 150 parts of the microcapsule dispersion prepared above and adding water to a concentration of 25%. The capsule composition was used as a paint. The base material is a 25 μm thick coated on polyester with a mixture of water-soluble polymer and polyester emulsion as the main component.
Using synthetic paper (Crisper G2311 manufactured by Toyobo Co., Ltd.)
The above-mentioned microcapsule coating material was applied at 5 g / m 2 on the back surface opposite to the application surface by an air knife coater and dried with hot air to obtain a pressure-sensitive recording sheet of the upper paper. At this time, the upper sheet had a thickness of 33 μm and an opacity of 77%. Opacity is
The average value of the opacity measured by the method A of JIS P 8138 on the front and back surfaces of the upper paper was defined as the opacity of the present invention.
【００２２】（読取り率の測定）上で作成した試験シー
トのカプセル面と市販の下用紙（日本製紙（株）製NW50
BA）とを向いあわせ、ドットインパクトプリンター（富
士通（株）製 F9680M2）で一連のバーコード１００組
を印字し、一日後にバーコード検証機（RJS,INC製 イ
ンスペクターIIモデル200 ）用い、上用紙の表面（ドッ
トインパクト面）、及び下用紙の表面（複写面）につい
てバーコードの読取り率の測定を行った。読み取り率
は、上用紙、下用紙について、１回のスキャンで正しく
読み取れたバーコードの組みの数を測定し、全体の数
（ 100組）に対する割合（％）で表した。(Measurement of Reading Rate) The capsule surface of the test sheet prepared above and a commercially available lower paper (NW50 manufactured by Nippon Paper Industries Co., Ltd.)
BA), print a series of 100 barcodes with a dot impact printer (F9680M2, manufactured by Fujitsu Ltd.), and use a barcode verifier (RJS, INC, inspector II model 200) one day later to print on the top paper. The barcode reading rate was measured for the surface (dot impact surface) and the surface of the lower sheet (copying surface). The reading rate was obtained by measuring the number of barcode pairs that were correctly read in one scan for the upper sheet and the lower sheet, and expressed as a percentage (%) of the total number (100 pairs).
【００２３】［実施例２］基材として、ポリエステル上
に白色顔料とバインダ−を主成分とする塗料を塗布して
インク受理性を持たせた厚さ38μｍの合成紙（東洋紡
（株）製クリスパーG7911 ）を用いた他は実施例１と同
様にして、上用紙の感圧記録シートを得た。この上用紙
の厚さは49μ、不透明度は79％であった。Example 2 As a base material, a 38 μm thick synthetic paper (Crisper manufactured by Toyobo Co., Ltd.) obtained by applying a paint containing a white pigment and a binder as main components on polyester to give ink receptivity. G7911) was used in the same manner as in Example 1 to obtain an upper pressure-sensitive recording sheet. The thickness of the upper sheet was 49μ and the opacity was 79%.
【００２４】［実施例３］電子供与性発色剤として、62
0 〜720nm の波長領域に吸収のある3-3 ビス(2-4- ジメ
チルアミノフェニル)-2-(4- メトキシフェニル）エチニ
ル-4,5,6,7- テトラクロロフタリド6.0 部と、視認濃度
向上のため通常の電子供与性発色剤である3-ジエチルア
ミノ-6- メチル-7- ジエチルアニリノフルオラン3.0 部
とを使用した以外は、実施例１と同様にしてマイクロカ
プセル及び上用紙の感圧記録シートを得た。この上用紙
の厚さは32μｍ、不透明度は77％であった。Example 3 As an electron-donating color former, 62
6.0 parts of 3-3 bis (2-4-dimethylaminophenyl) -2- (4-methoxyphenyl) ethynyl-4,5,6,7-tetrachlorophthalide having an absorption in a wavelength range of 0 to 720 nm; Microcapsules and upper paper were prepared in the same manner as in Example 1 except that 3.0 parts of 3-diethylamino-6-methyl-7-diethylanilinofluoran, which is a usual electron-donating color developing agent, was used to improve the visual density. Was obtained. The thickness of the upper sheet was 32 μm, and the opacity was 77%.
【００２５】［実施例４］実施例３と同様のマイクロカ
プセルを、実施例１と同じ材質の厚さ33μｍの合成紙基
材上に、実施例１の方法で塗布して、上用紙の感圧記録
シートを得た。この上用紙の厚さは45μｍ、不透明度は
86％であった。Example 4 The same microcapsules as in Example 3 were applied to a 33 μm thick synthetic paper substrate of the same material as in Example 1 by the method of Example 1, and A pressure recording sheet was obtained. The thickness of the paper is 45μm, and the opacity is
86%.
【００２６】［比較例１］実施例１と同じ材質の厚さ50
μｍの合成紙基材を用いた他は、実施例１と同様にして
上用紙の感圧記録シートを得た。この上用紙の厚さは55
μｍ、不透明度は90％であった。[Comparative Example 1] The same material 50 as in Example 1 having a thickness of 50
An upper pressure-sensitive recording sheet was obtained in the same manner as in Example 1 except that a synthetic paper substrate of μm was used. The top paper thickness is 55
μm, opacity was 90%.
【００２７】［比較例２］実施例１で用いた厚さ25μｍ
の合成紙基材（東洋紡（株）製クリスパーG2311）の代
わりに、同じ材質で不透明度が低い厚さ38μｍのポリエ
ステル系合成紙（東洋紡（株）製クリスパーH2311 ）を
使用した以外は、実施例１と同様に処理した。この上用
紙の厚さは44μｍ、不透明度は60％であった。Comparative Example 2 The thickness of 25 μm used in Example 1
Example 2 except that the synthetic paper base material (Crisper G2311 manufactured by Toyobo Co., Ltd.) was replaced by a 38 μm-thick polyester synthetic paper (Crispar H2311 manufactured by Toyobo Co., Ltd.) of the same material and low opacity. The same treatment as in No. 1. The thickness of the upper sheet was 44 μm, and the opacity was 60%.
【００２８】［比較例３］基材として厚さ30μｍのポリ
プロピレンから作られた合成紙を使用し、実施例１のマ
イクロカプセル塗料を実施例１と同様にしてエアーナイ
フコーターで塗工を行おうとしたところ、乾燥ゾーン通
過の際、基材が流れ方向に伸びるためテンションをかけ
ることが出来ず、塗工することは出来なかった。Comparative Example 3 A microcapsule paint of Example 1 was coated with an air knife coater in the same manner as in Example 1 using synthetic paper made of polypropylene having a thickness of 30 μm as a base material. As a result, when passing through the drying zone, the substrate was stretched in the flow direction, so that tension could not be applied and coating could not be performed.
【００２９】実施例と比較例の結果を表１に示す。Table 1 shows the results of Examples and Comparative Examples.
【００３０】[0030]
【表１】 [Table 1]
【００３１】[0031]
【発明の効果】本発明の感圧記録シートを使用すること
により、バーコードの読取り率が向上する。By using the pressure-sensitive recording sheet of the present invention, the bar code reading rate is improved.
───────────────────────────────────────────────────── フロントページの続き (56)参考文献 特開 平７−125422（ＪＰ，Ａ) 特開 平５−177925（ＪＰ，Ａ) 特開 昭49−130742（ＪＰ，Ａ) 特開 平４−212882（ＪＰ，Ａ) 特公 昭54−28766（ＪＰ，Ｂ２) ──────────────────────────────────────────────────続 き Continuation of the front page (56) References JP-A-7-125422 (JP, A) JP-A-5-177925 (JP, A) JP-A-49-130742 (JP, A) JP-A-4- 212882 (JP, A) JP-B 54-28766 (JP, B2)
Claims (3)
マイクロカプセルと電子受容性顕色剤を、それぞれ又は
同時に塗布し、圧力による電子供与性発色剤と電子受容
性顕色剤との発色反応を利用した感圧記録シートにおい
て、該基材がポリエステルフィルムから作られた合成紙
であって、かつその合成紙を使用した感圧記録シートの
厚さが５０μｍ以下、不透明度７０％以上であることを
特徴とするバーコード読取り用感圧記録シート。1. A microcapsule containing an electron-donating color developing agent and an electron-accepting color developing agent are respectively or simultaneously applied onto a substrate, and the electron-donating color forming agent and the electron-accepting color developing agent are applied under pressure. Wherein the base material is a synthetic paper made of a polyester film , and the thickness of the pressure-sensitive recording sheet using the synthetic paper is 50 μm or less, and the opacity is 70%. A pressure-sensitive recording sheet for reading barcodes, characterized in that:
与性発色剤を含有したマイクロカプセルを塗布した上用
紙である請求項１記載の感圧記録シ−ト。2. The pressure-sensitive recording sheet according to claim 1, wherein the pressure-sensitive recording sheet is an upper paper on which microcapsules containing an electron-donating color former are coated on the back surface of a substrate.
に有意の吸収があるものである、請求項１あるいは２に
記載の感圧記録シ−ト。3. An electron-donating color former having a wavelength of 620 to 720 nm.
3. A pressure-sensitive recording sheet according to claim 1, wherein the pressure-sensitive recording sheet has significant absorption.