JP3120544B2 - Information recording medium - Google Patents
Information recording mediumInfo
- Publication number
- JP3120544B2 JP3120544B2 JP04072013A JP7201392A JP3120544B2 JP 3120544 B2 JP3120544 B2 JP 3120544B2 JP 04072013 A JP04072013 A JP 04072013A JP 7201392 A JP7201392 A JP 7201392A JP 3120544 B2 JP3120544 B2 JP 3120544B2
- Authority
- JP
- Japan
- Prior art keywords
- infrared
- layer
- recording medium
- heat
- information recording
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本発明は不可視な情報を印字でき
る情報記録媒体に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an information recording medium on which invisible information can be printed.
【０００２】[0002]
【従来の技術】近年、株券・債券・小切手・通帳・宝ク
ジ・乗車券・回数券・定期券等の証券類の他、ＩＤカー
ド、クレジットカード、キャッシュカード、ギフトカー
ドなどのプラスチックカード、テレホンカードに代表さ
れるプリペイドカードといった金券に変わる証券関連商
品の発展はめざましい物があり、必然的にそれらの偽造
を効果的に防止する方法、および容易にそれらの真偽の
判別をおこなえる技術の重要性が非常に高まっている。2. Description of the Related Art In recent years, in addition to securities such as stock certificates, bonds, checks, passbooks, treasure lotteries, tickets, coupons, commuter passes, etc., plastic cards such as ID cards, credit cards, cash cards, gift cards, and telephones. There are remarkable developments in securities-related products such as prepaid cards, such as prepaid cards, which are remarkable, and inevitably the method of effectively preventing their counterfeiting and the importance of technology that can easily determine their authenticity. Sex is very high.
【０００３】そのようなセキュリティー性を目的とした
技術として幾つかの方法が提案されている。その一つに
磁気記録技術がある。しかしながら磁気記録された情報
は目視により解読はできないが、一般の磁気読み取り機
械の普及により、故意に記録情報を消去したり、書き換
えが可能なためこれらの危険性が高まっている。また、
バーコード、ＯＣＲ、ＭＩＣＲ等の手段をもって、情報
を記録する事も行なわれているが、このような手段では
コードを目視出来、偽造、改竄の対象になりえるため、
その危険性はまぬがれない。Several methods have been proposed as techniques for such security. One of them is a magnetic recording technology. However, although magnetically recorded information cannot be visually deciphered, these dangers have been increased because recorded information can be intentionally erased or rewritten due to the spread of general magnetic reading machines. Also,
Information is recorded by means such as a barcode, OCR, and MICR. However, such a means allows the code to be visually observed, and can be a target of forgery or tampering.
The danger is inevitable.
【０００４】[0004]
【発明が解決しようとする課題】そこで近年、赤外吸収
ロイコサーマルを中心とし記録された情報を赤外線を照
射した時、その反射率の差を検出器で読み取る事により
機械読み取りを行う提案がなされている。しかしなが
ら、前記記録情報は発色部が黒色、若しくは有濃色のも
のが殆どであるので、その情報を不可視な物とする為に
はプロセスインキを混ぜ合わせる事により作った墨イン
キ等で隠蔽する事が考えられている。Therefore, in recent years, there has been proposed a method of reading information recorded mainly on infrared absorption leucothermal by irradiating infrared rays with a detector to read a difference in reflectance with a detector to perform mechanical reading. ing. However, since most of the recorded information has a black or dark colored portion, in order to make the information invisible, it is necessary to hide the information with black ink or the like created by mixing process ink. Is considered.
【０００５】しかし、その隠蔽層を設けた場合、該隠蔽
層上に印刷を施すのが困難でありデザイン的にもあまり
見栄えの良いものとは言えず、部分的に隠蔽層を設ける
にしても、デザイン的に不自然な黒色のパターンがある
と、赤外線読み取り可能なコードがその下に隠されてい
る事を容易に想像させる結果となる為、改造・改竄のタ
ーゲットに成りやすいという欠点もあった。[0005] However, when the concealing layer is provided, it is difficult to print on the concealing layer, so that it cannot be said that the concealing layer has a very good appearance. However, if there is a black pattern that is unnatural in design, the result is that it is easy to imagine that the infrared readable code is hidden beneath it, and it has the disadvantage that it is easily targeted for modification and tampering. Was.
【０００６】以上の理由によりコードをデザイン的に不
自然な黒色にすることなく目視により確認できないもの
にする方法が望まれている。[0006] For the above reasons, there is a demand for a method of making the code unrecognizable visually without making the code unnatural black in design.
【０００７】また、株券・債券・小切手・通帳・宝クジ
・乗車券・回数券・定期券といった証券類の他、ＩＤカ
ード、クレジットカード、キャッシュカード、ギフトカ
ードなどのプラスチックカード、テレホンカードに代表
されるプリペイドカードといった金券に変わる証券関連
商品においては、改造・改竄に対するセキュリティー性
をより高くするために固定情報ではなく、それぞれの証
券関連商品毎の固有の可変情報である事が望まれてい
る。In addition to securities such as stock certificates, bonds, checks, passbooks, treasure lotteries, tickets, coupons, and commuter passes, plastic cards such as ID cards, credit cards, cash cards, gift cards, and telephone cards are representative. In securities-related products such as prepaid cards, which are replaced with cash vouchers, it is desired that the security-related products be not fixed information but variable information unique to each security-related product in order to enhance security against remodeling and tampering. .
【０００８】従って、本発明の目的はデザイン的に自然
な下地の白色に近いままで、しかも不可視な情報を印字
でき、かつ該不可視な情報として証券関連商品毎に固有
の可変情報を印字可能とし、改造・改竄に対するセキュ
リティー性を高くしうる情報記録媒体を提供することに
ある。Therefore, an object of the present invention is to make it possible to print invisible information while keeping the natural white background of the design and to print variable information unique to each securities-related product as the invisible information. Another object of the present invention is to provide an information recording medium capable of improving security against alteration and tampering.
【０００９】[0009]
【課題を解決するための手段】本発明者等は前記課題に
鑑みて鋭意研究の結果、本発明の上記目的は、基板上
に、少なくとも五二酸化リンを主成分とし、酸化鉄及び
／又は酸化銅を１．０重量％以上含む粉末リン酸塩ガラ
ス及びバインダーからなる赤外線吸収性インキ層、該赤
外線吸収性インキ層上に積層され、中空マイクロカプセ
ルを含有し、常温では赤外線透過率が低く、所定の温度
以上で赤外線透過率が増大する感熱記録層を有する情報
記録媒体を提供することにより、達成されることを見出
した。Means for Solving the Problems The inventors of the present invention have conducted intensive studies in view of the above-mentioned problems, and as a result, the object of the present invention is to provide a substrate comprising at least phosphorus pentoxide as a main component, iron oxide and / or oxide An infrared-absorbing ink layer composed of a powdered phosphate glass containing 1.0% by weight or more of copper and a binder, laminated on the infrared-absorbing ink layer, containing hollow microcapsules, and having a low infrared transmittance at room temperature; It has been found that this can be achieved by providing an information recording medium having a thermosensitive recording layer whose infrared transmittance increases at a predetermined temperature or higher.
【００１０】なお、中空マイクロカプセルの粒径が、
０．０５〜１μｍである事、感熱記録層に赤外光を透過
する黄緑色の染料又は顔料を添加する事、感熱記録層上
に、赤外線を透過すると共に、記録像の肉眼による識別
を不可能とする可視光線遮断層を有する事も含まれる。The particle size of the hollow microcapsules is
0.05 to 1 μm, addition of a yellow-green dye or pigment that transmits infrared light to the heat-sensitive recording layer, transmission of infrared light on the heat-sensitive recording layer, and impairment of the discrimination of the recorded image by the naked eye. It also includes having a visible light blocking layer that makes it possible.
【００１１】以下に、本発明を更に詳細に説明する。本
発明の情報記録媒体は、基体上に赤外線吸収性インキ層
を有しているが、該インキ層に用いられる赤外線吸収性
インキは粉末リン酸塩ガラス、バインダー及び溶剤から
成っている。Hereinafter, the present invention will be described in more detail. The information recording medium of the present invention has an infrared-absorbing ink layer on a substrate, and the infrared-absorbing ink used for the ink layer comprises powdered phosphate glass, a binder and a solvent.
【００１２】通常の粉末リン酸塩ガラスは、五二酸化リ
ンを主成分とし、酸化鉄及び／又は酸化銅を１．０〜
３．０重量％程度含むが、高い赤外線吸収性を必要とす
る場合は、酸化鉄及び酸化銅をそれぞれ２０重量％以上
含ませることが好ましい。An ordinary powdered phosphate glass contains phosphorus pentoxide as a main component and contains iron oxide and / or copper oxide in an amount of 1.0 to 1.0.
It contains about 3.0% by weight, but when high infrared absorption is required, it is preferable to contain 20% by weight or more of each of iron oxide and copper oxide.
【００１３】更に、本発明の赤外線吸収性インキは必要
に応じ、以下の化合物を含有する。 Ａｌ2 Ｏ3 ２．０〜１０．０重量％ Ｂ2 Ｏ3 １．０〜３０．０重量％ ＭｇＯ ３．０〜１０．０重量％ ＺｎＯ ０〜 ３．０重量％ Ｋ2 Ｏ ０〜１５．０重量％ ＢａＯ ０〜１０．０重量％ ＳｒＯ ０〜 １．０重量％ Ｎｉ，Ｃｏ，Ｓｅ 微量Further, the infrared absorbing ink of the present invention contains the following compounds as required. Al 2 O 3 2.0 to 10.0 wt% B 2 O 3 1.0~30.0 wt% MgO 3.0 to 10.0 wt% ZnO 0 to 3.0 wt% K 2 O 0 to 15 0.0% by weight BaO 0 to 10.0% by weight SrO 0 to 1.0% by weight Ni, Co, Se trace amount
【００１４】粉末リン酸塩ガラスは、上記得られたリン
酸塩ガラスを粉末化したものであり、本発明にはこれを
顔料としてインキ化したものを用いる。このような粉末
リン酸塩ガラスは溶剤を除くインキ組成物中に８０重量
％以下含まれることが好ましい。本発明の赤外線吸収性
インキに含まれるバインダーとしては、塩酢酸ビニル系
樹脂、飽和ポリエステル、ポリウレタンエラストマー等
が用いられる。上記バインダーは溶剤を除くインキ組成
物中に２０重量％以上含まれることが好ましい。The powdered phosphate glass is obtained by pulverizing the above-obtained phosphate glass, and in the present invention, the powdered phosphate glass is used as an ink. Such a powdered phosphate glass is preferably contained in the ink composition excluding the solvent in an amount of 80% by weight or less. As the binder contained in the infrared absorbing ink of the present invention, vinyl chloride acetate resin, saturated polyester, polyurethane elastomer and the like are used. The binder is preferably contained in the ink composition excluding the solvent in an amount of 20% by weight or more.
【００１５】更に本発明の赤外線吸収性インキには、上
記材料に加え消泡剤、滑剤等を含むこともできる。ま
た、上記赤外線吸収性インキに用いられる溶剤として
は、トルエン、メチルイソブチルケトン、キシレン、シ
クロヘキサノール、酢酸イソブチル、シクロヘキサノ
ン、メチルシクロヘキサノン、エチレングリコールモノ
ブチルエーテル等のグリコール誘導体等、又はこれらの
混合溶媒が挙げられる。Further, the infrared absorbing ink of the present invention may contain an antifoaming agent, a lubricant and the like in addition to the above materials. Examples of the solvent used in the infrared absorbing ink include toluene, methyl isobutyl ketone, xylene, cyclohexanol, isobutyl acetate, cyclohexanone, methyl cyclohexanone, glycol derivatives such as ethylene glycol monobutyl ether, and the like, or a mixed solvent thereof. Can be
【００１６】本発明において上記赤外線吸収インキ層上
には、中空マイクロカプセルを乳化分散する事により得
たエマルションを塗布乾燥することにより得られ、常温
では赤外線透過率が低く、所定の温度以上で赤外線透過
率が増大して、この赤外線透過率の差で記録像を構成す
る感熱記録層（以下、本発明の感熱記録層と称す）が設
けられる。In the present invention, the above-mentioned infrared absorbing ink layer is obtained by applying and drying an emulsion obtained by emulsifying and dispersing hollow microcapsules, and has a low infrared transmittance at ordinary temperature and an infrared transmittance at a predetermined temperature or higher. The transmittance increases, and a heat-sensitive recording layer (hereinafter, referred to as a heat-sensitive recording layer of the present invention) that forms a recorded image based on the difference in infrared transmittance is provided.
【００１７】すなわち、本発明の感熱記録層は乳化重合
法等で作成される粒径０．０５〜１μｍ程度の中空マイ
クロカプセルエマルションから構成される。かかる中空
マイクロカプセルが乳化分散されている感熱記録層は、
常温では赤外光の入射に対し中空マイクロカプセル内の
空気の存在により光の屈折率の変化が起こり、その結果
光の散乱が起こり赤外線透過率が低下する。これに対
し、所定以上の温度、即ち中空マイクロカプセルを形成
する樹脂のガラス転移点以上に加熱する事によりマイク
ロカプセルの破壊、融着が起こり、粒子−空気界面が減
少し光の散乱が抑制され透明化し、赤外光の透過率が増
大する。That is, the heat-sensitive recording layer of the present invention comprises a hollow microcapsule emulsion having a particle size of about 0.05 to 1 μm prepared by an emulsion polymerization method or the like. The heat-sensitive recording layer in which such hollow microcapsules are emulsified and dispersed,
At room temperature, the presence of air in the hollow microcapsules causes a change in the refractive index of light with respect to the incidence of infrared light. As a result, light is scattered and the infrared transmittance decreases. On the other hand, by heating above a predetermined temperature, that is, above the glass transition point of the resin forming the hollow microcapsules, breakage and fusion of the microcapsules occur, the particle-air interface decreases, and light scattering is suppressed. It becomes transparent, and the transmittance of infrared light increases.
【００１８】このようなマイクロカプセルを形成するた
めの壁材料としては、ガラス転移点温度が50℃〜150 ℃
程度のものが好ましく、ポリユレア、ポリエステル、ポ
リカーボネート、尿素−ホルムアルデヒド樹脂、メラミ
ン樹脂、ポリスチレン、スチレンメタクリレート共重合
体、ゼラチン、ポリビニルピロリドン、ポリビニルアル
コール等が挙げられ所望の透明化温度に応じて選択すれ
ば良い。The wall material for forming such microcapsules has a glass transition temperature of 50 ° C. to 150 ° C.
Polyurea, polyester, polycarbonate, urea-formaldehyde resin, melamine resin, polystyrene, styrene methacrylate copolymer, gelatin, polyvinylpyrrolidone, polyvinyl alcohol, etc. good.
【００１９】感熱記録層は、これらの乳化分散により得
られたエマルションとし、基板上の赤外線吸収性インキ
層上に、スクリーン印刷法、グラビア印刷法等の方法で
塗布乾燥することにより形成できる。なお、本発明の赤
外線吸収性インキ層は、組成により極薄い青緑色を呈す
る場合があり、この上に感熱記録層を設け、記録像を形
成する（感熱記録層を透明化）と、下層の赤外線吸収性
インキ層の極薄い青緑色が露出し、僅かなコントラスト
が生じ記録像が目視可能となる恐れがあるが、その場
合、感熱記録層に赤外光を透過する青緑色の染料又は有
色透明顔料を添加することにより、記録像が目視不可能
となる。The heat-sensitive recording layer can be formed by applying an emulsion obtained by emulsification and dispersion to the infrared-absorbing ink layer on the substrate by a method such as screen printing or gravure printing and drying. The infrared-absorbing ink layer of the present invention may exhibit an extremely light blue-green color depending on the composition. A heat-sensitive recording layer is provided on the ink-absorbing ink layer to form a recorded image (to make the heat-sensitive recording layer transparent). The extremely thin blue-green color of the infrared absorbing ink layer may be exposed, causing a slight contrast to make the recorded image visible.In such a case, a blue-green dye or colored material that transmits infrared light to the heat-sensitive recording layer The addition of the transparent pigment makes the recorded image invisible.
【００２０】本発明において可視光線遮断層とは、赤外
線センサーで読み取り可能な程度の赤外線を透過すると
共に、肉眼で記録像の識別が不可能な程度に可視光線を
遮断するものをいい、赤外線の透過率が可視光線の透過
率より大きいものはもちろん、赤外線センサーの感度が
優れていること等から、赤外線の透過率が可視光線の透
過率より小さいものであっても、肉眼で記録像が識別で
きず、赤外線センサーで識別できるものであればよい。
このような可視光線遮断層としては、ゼラチン膜、オラ
ゾールブラックＢ−Ｖやオラゾール２ＲＧ等の赤外線透
過性の染料を含む塗料、通常の紫外線硬化型プロセスイ
ンキ等が使用できる。プロセスインキを使用する場合に
は、可視領域の全ての波長の光が充分に遮断されるよう
に、イエロー、マゼンタ、シアンの三色を混合したグレ
ーまたは黒色のインキを使用することが望ましい。かか
る可視光線遮断層は、例えばスクリーン印刷法またはオ
フセット印刷法により紫外線硬化型プロセスインキを印
刷後、直ちに紫外線を照射して硬化させて形成すること
ができる。厚さは１μｍ以上あればよい。In the present invention, the visible light-blocking layer means a layer that transmits infrared light that can be read by an infrared sensor and blocks visible light so that a recorded image cannot be identified with the naked eye. The recorded image can be identified with the naked eye even if the transmittance of infrared rays is smaller than the transmittance of visible light because of the excellent sensitivity of the infrared sensor, as well as those with transmittance higher than that of visible light. Anything that can not be identified and can be identified by an infrared sensor may be used.
As such a visible light blocking layer, a gelatin film, a paint containing an infrared transmissive dye such as Orazole Black B-V or Orazole 2RG, or a usual ultraviolet curable process ink can be used. When a process ink is used, it is desirable to use a gray or black ink that is a mixture of three colors of yellow, magenta, and cyan so that light of all wavelengths in the visible region is sufficiently blocked. Such a visible light blocking layer can be formed, for example, by printing an ultraviolet curable process ink by a screen printing method or an offset printing method, and then immediately irradiating with ultraviolet light to cure the ink. The thickness may be 1 μm or more.
【００２１】また、サーマルヘッドの発熱による可視光
線遮断層の変形により光沢が変化し、この光沢の変化に
より肉眼で記録像が識別可能となることを防止するた
め、可視光線遮断層の上に、更に赤外線透過性で、耐熱
性の保護層を設けても良い。かかる耐熱製性保護層の素
材としては、アクリル樹脂、塩化ビニル樹脂、ニトロセ
ルロース、ヒドロキシセルロース、カルボキシメチルセ
ルロース、ポリビニルアルコール、スチレン−マレイン
酸共重合体、ポリエステル樹脂、ＡＢＳ樹脂等が使用で
き、これらをトルエン、キシレン等の溶剤に溶解または
分散してグラビア法、ロールコート法等により塗布乾燥
して耐熱性保護層を形成することができる。また熱硬化
型樹脂、紫外線硬化型樹脂、電子線硬化型樹脂などの硬
化型樹脂を使用してもよい。サーマルヘッドとこの耐熱
性保護層の間の滑り性を向上してサーマルヘッドのスム
ーズな走行を確保するため、耐熱性保護層はワックス等
の滑剤を含むものであってもよい。Further, in order to prevent the gloss from changing due to the deformation of the visible light blocking layer due to the heat generated by the thermal head, and to prevent the recorded image from being identifiable by the naked eye due to the change in the gloss, the visible light blocking layer is provided on the visible light blocking layer. Further, a heat-resistant protective layer that is infrared-transmissive and may be provided. Examples of the material for the heat-resistant protective layer include acrylic resin, vinyl chloride resin, nitrocellulose, hydroxycellulose, carboxymethylcellulose, polyvinyl alcohol, styrene-maleic acid copolymer, polyester resin, ABS resin and the like. A heat-resistant protective layer can be formed by dissolving or dispersing in a solvent such as toluene or xylene, and applying and drying by a gravure method, a roll coating method or the like. Further, a curable resin such as a thermosetting resin, an ultraviolet curable resin, and an electron beam curable resin may be used. The heat-resistant protective layer may contain a lubricant such as wax in order to improve the slipperiness between the thermal head and the heat-resistant protective layer to ensure smooth running of the thermal head.
【００２２】また、本発明に用いる基板には、用途に応
じて種々のものが使用できるが、例えば紙や、ＰＥＴ、
塩ビ等のプラスチック等が用いられる。本発明に係る情
報記録媒体は、上述のように、サーマルヘッドを走行さ
せながら、その発熱素子を選択的に発熱させて、感熱記
録層に記録像を形成することにより、情報を記録する。
感熱記録層が赤外線透過率が小さい状態にある時には、
サーマルヘッドにより中空マイクロカプセルのガラス転
移温度に加熱することにより、加熱された部位の赤外線
透過率が大きくなり、この赤外線透過率が大きい部位が
記録像を構成する。Various substrates can be used for the substrate according to the present invention, depending on the application. For example, paper, PET,
Plastics such as PVC are used. As described above, the information recording medium according to the present invention records information by forming a recording image on the heat-sensitive recording layer by selectively causing the heat-generating elements to generate heat while running the thermal head.
When the heat-sensitive recording layer has a low infrared transmittance,
By heating to the glass transition temperature of the hollow microcapsule by the thermal head, the infrared transmittance of the heated portion increases, and the portion having a high infrared transmittance constitutes a recorded image.
【００２３】記録像は可視光線遮断層により被覆されて
いるから、肉眼では識別できず、情報の秘密性が維持さ
れている。記録像を読む際には、波長700nm 以上の赤外
線レーザーを照射し、記録像からの反射光線を赤外線セ
ンサーにより感知すればよい。赤外線透過率の小さい部
位では入射した赤外線を反射散乱するが、赤外線透過率
の大きい部位では赤外線吸収性インキ層に入射光線が吸
収されて反射が生じないから、記録像の有無を識別する
ことができる。Since the recorded image is covered with the visible light blocking layer, it cannot be identified by the naked eye, and the confidentiality of the information is maintained. When reading a recorded image, an infrared laser having a wavelength of 700 nm or more may be irradiated, and reflected light from the recorded image may be detected by an infrared sensor. Although the incident infrared rays are reflected and scattered at the part with low infrared transmittance, the incident light is absorbed by the infrared absorbing ink layer and the reflection does not occur at the part with high infrared transmittance, so it is possible to identify the presence or absence of the recorded image. it can.
【００２４】[0024]
【作用】本発明の構成、特に本発明の感熱記録層を用い
ることにより、デザイン的に自由度の大きな白色に近い
下地の上に、不可視情報を感熱印字でき、また、これに
本発明の赤外線吸収性インキ層を組合わせることによ
り、赤外線を利用してその情報をよみとることが可能と
なる。更に、感熱記録層上に可視光線遮断層を組合わせ
ることにより、記録されたパターンの察知を困難にせし
め偽造、改竄防止をより確実に行なうことができる。According to the constitution of the present invention, in particular, by using the heat-sensitive recording layer of the present invention, invisible information can be heat-sensitive printed on a white base having a large degree of freedom in design. By combining the absorbent ink layer, the information can be read using infrared rays. Further, by combining the visible light blocking layer on the heat-sensitive recording layer, it becomes difficult to detect the recorded pattern, and forgery and tampering can be prevented more reliably.
【００２５】[0025]
【実施例】以下本発明の一実施例を図面を参照して具体
的に説明する。図１は本発明の情報記録媒体の１実施例
を示す断面図である。図１によれば本発明の情報記録媒
体は紙あるいはプラスチックからなる基板（１）上に下
記赤外線吸収性インキ層（２）、さらに下記の本発明の
感熱記録層（３）、その上の下記赤外透過のプロセスイ
ンキを印刷してなる可視光線遮断層（４）、その上に感
熱保護層として下記保護層（５）を積層してなる。DESCRIPTION OF THE PREFERRED EMBODIMENTS One embodiment of the present invention will be specifically described below with reference to the drawings. FIG. 1 is a sectional view showing one embodiment of the information recording medium of the present invention. According to FIG. 1, the information recording medium of the present invention comprises the following infrared-absorbing ink layer (2) on a substrate (1) made of paper or plastic, further the following thermosensitive recording layer (3) of the present invention, and the following A visible light blocking layer (4) formed by printing an infrared transmitting process ink, and the following protective layer (5) as a heat-sensitive protective layer are laminated thereon.
【００２６】・赤外線吸収性インキ層（２） Ｐ2 Ｏ5 ７８．０重量％，Ａｌ2 Ｏ3 ５．２重量％，Ｂ
ａＯ ９．０重量％，ＭｇＯ ５．４重量％，ＣｕＯ
１．７重量％，ＳｒＯ ０．０５重量％からなる混合物
を溶融しガラス化したものを粉砕し顔料とした。Infrared absorbing ink layer (2) 78.0% by weight of P 2 O 5 , 5.2% by weight of Al 2 O 3 , B
aO 9.0% by weight, MgO 5.4% by weight, CuO
A mixture consisting of 1.7% by weight and 0.05% by weight of SrO was melted and vitrified, and the mixture was pulverized to obtain a pigment.
【００２７】・本発明の感熱記録層（３） アクリル系中空マイクロカプセル樹脂エマルション（平
均粒径0.5 μm ，固形分比33.6％）を10μの厚みに塗布
した。The thermosensitive recording layer (3) of the present invention Acrylic hollow microcapsule resin emulsion (average particle size: 0.5 μm, solid content ratio: 33.6%) was applied to a thickness of 10 μm.
【００２８】・可視光線遮断層形成用の赤外透過のプロ
セスインキ 黄色 紫外線硬化型イエローインキ マゼンタ色 紫外線硬化型マゼンタインキ シアン色 紫外線硬化型シアンインキ を用
いて印刷を行なった。Infrared transmitting process ink for forming a visible light blocking layer Yellow UV curable yellow ink Magenta UV curable magenta ink Cyan Color UV curable cyan ink was used for printing.
【００２９】・保護層（５） ＵＶ硬化型ハードコートを２〜５μｍの厚みに塗布し
た。Protective layer (5) A UV-curable hard coat was applied to a thickness of 2 to 5 μm.
【００３０】上記得られた記録媒体にサーマルヘッドを
用いてパターンを印字した。印字されたパターンは肉眼
で認識する事は出来なかったがＩＲスコープ（池上通信
社製）にて印字パターンを認識できた。A pattern was printed on the recording medium obtained above using a thermal head. The printed pattern could not be recognized with the naked eye, but the printed pattern could be recognized with an IR scope (Ikegami Tsushin Co., Ltd.).
【００３１】[0031]
【発明の効果】以上説明したように本発明によれば、デ
ザイン的に自由度の大きな白色に近い下地上に、不可視
情報を感熱印字でき、しかも赤外線を利用することによ
りその情報を読み取る事が可能である。As described above, according to the present invention, invisible information can be thermally printed on a white base having a large degree of freedom in design, and the information can be read by using infrared rays. It is possible.
【００３２】よって、記録されたパターンは察知する事
が難しいのみならず、偽造防止のためのパターンの存在
を察知される事がないため、偽造、改竄防止をより確実
に行なう事ができる。Therefore, not only is it difficult to detect the recorded pattern, but also the presence of a pattern for preventing forgery is not detected, so that forgery and falsification can be more reliably prevented.
【００３３】[0033]
【図１】本発明の情報記録媒体の一実施例の断面図を示
す。FIG. 1 is a sectional view of an embodiment of an information recording medium according to the present invention.
１ 基板 ２ 赤外線吸収性インキ層 ３ 感熱記録層 ４ 可視光線遮断層 ５ 保護層 DESCRIPTION OF SYMBOLS 1 Substrate 2 Infrared absorbing ink layer 3 Thermal recording layer 4 Visible light shielding layer 5 Protective layer
Claims (4)
分とし、酸化鉄及び／又は酸化銅を１．０重量％以上含
む粉末リン酸塩ガラス及びバインダーからなる赤外線吸
収性インキ層、該赤外線吸収性インキ層上に積層され、
中空マイクロカプセルを含有し、常温では赤外線透過率
が低く、所定の温度以上で赤外線透過率が増大する感熱
記録層を設けた事を特徴とする情報記録媒体。1. An infrared-absorbing ink layer comprising a phosphate glass powder and a binder containing at least phosphorus pentoxide as a main component and at least 1.0% by weight of iron oxide and / or copper oxide on a substrate. Laminated on the absorbent ink layer,
An information recording medium comprising a hollow microcapsule, a heat-sensitive recording layer having low infrared transmittance at room temperature and increasing infrared transmittance at a predetermined temperature or higher.
〜１μｍである事を特徴とする請求項１記載の情報記録
媒体。2. The hollow microcapsules having a particle size of 0.05
2. The information recording medium according to claim 1, wherein the thickness is from 1 to 1 [mu] m.
料又は顔料を添加する事を特徴とする請求項１又は２記
載の情報記録媒体。3. A process according to claim 1 or 2, wherein the information recording medium to the heat-sensitive recording layer, characterized in that the addition of blue-green dye or pigment that transmits infrared light.
に、記録像の肉眼による識別を不可能とする可視光線遮
断層を有する事を特徴とする請求項１又は２記載の情報
記録媒体。4. A heat-sensitive recording layer, while transmitting infrared rays, according to claim 1 or 2, wherein the information recording medium, characterized in that it has a visible light blocking layer that impossible identification by naked eye recorded images.