JP3098334B2 - Multi-prism sheet for liquid crystal display device and liquid crystal display device - Google Patents
Multi-prism sheet for liquid crystal display device and liquid crystal display deviceInfo
- Publication number
- JP3098334B2 JP3098334B2 JP04254861A JP25486192A JP3098334B2 JP 3098334 B2 JP3098334 B2 JP 3098334B2 JP 04254861 A JP04254861 A JP 04254861A JP 25486192 A JP25486192 A JP 25486192A JP 3098334 B2 JP3098334 B2 JP 3098334B2
- Authority
- JP
- Japan
- Prior art keywords
- liquid crystal
- crystal display
- display device
- prism
- prism sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【０００１】[0001]
【産業上の利用分野】本発明は、液晶テレビ、コンピュ
ータ用ディスプレイ等の液晶ディスプレイ等の液晶表示
装置、およびそれに使用されるマルチプリズムシートに
関するものであり、さらに詳しくは優れた輝度を有する
液晶表示装置に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a liquid crystal display device such as a liquid crystal display such as a liquid crystal television and a computer display , and a multi-prism sheet used therein . The present invention relates to a liquid crystal display device having luminance.
【０００２】[0002]
【従来の技術】液晶表示装置は、その軽量化や高精細化
等に伴って、ＯＡ機器やパーソナルコンピューター等に
広く使用されている。しかし、液晶自体は発光しないた
め、背面照明手段を用いて輝度の向上を図っている。一
方、最近では、カラー液晶テレビ等をはじめとして、液
晶表示装置のカラー化が進んでおり、さらなる輝度の向
上が要求されるようになっきている。このようなカラー
液晶表示素子においては、これまでの単色液晶表示装置
用の背面照明手段では十分な輝度を確保することができ
なくなってきている。そこで、背面照明手段の明るさを
向上させる試みがなされてきている。2. Description of the Related Art Liquid crystal display devices have been widely used in OA equipment, personal computers, etc., due to their lighter weight and higher definition. However, since the liquid crystal itself does not emit light, the luminance is improved by using a back-lighting unit. On the other hand, recently, colorization of liquid crystal display devices such as color liquid crystal televisions has been progressing, and further improvement in luminance has been demanded. In such a color liquid crystal display element, it has become impossible to secure sufficient luminance with the conventional back lighting means for a single color liquid crystal display device. Therefore, attempts have been made to improve the brightness of the backlight unit.
【０００３】[0003]
【発明が解決しようとする課題】しかし、背面照明手段
の明るさを向上させる方法では、発熱量の増大やコスト
アップ等の新たな問題点を伴っている。そこで、本発明
の目的は、背面照明手段の明るさの改良による発熱量の
増大等の問題点を伴うことなく、輝度の向上した液晶表
示装置を提供することにある。However, the method of improving the brightness of the backlight unit has new problems such as an increase in heat generation and an increase in cost. SUMMARY OF THE INVENTION It is an object of the present invention to provide a liquid crystal display device with improved brightness without problems such as an increase in the amount of heat generated by improving the brightness of the backlight unit.
【０００４】[0004]
【課題を解決するための手段】本発明者等は、このよう
な状況に鑑み、特定の形状を有し、特定の材料から構成
されるマルチプリズムシートを使用することによって液
晶表示装置の輝度を向上できることを見出し、本発明に
到達したものである。すなわち、本発明の液晶表示装置
は、背面照明手段の上に設置されたマルチプリズムシー
トと、このマルチプリズルシートの上に設置された液晶
表示素子とを備え、マルチプリズムシートのプリズム面
と液晶表示素子とが相対するように設置されている液晶
表示装置であって、前記マルチプリズムシートが、その
表面に頂角が６０〜９５゜で、ピッチが１００μｍ以下
である一連の細長い断面三角形状のプリズムが連続して
多数形成され、２５℃の弾性率が１００００〜５０００
０Ｋｇ／ｃｍ 2 の活性エネルギー線硬化型樹脂で成形さ
れていることを特徴とするものである。また、本発明の
マルチプリズムシートは、２５℃の弾性率が１００００
〜５００００Ｋｇ／ｃｍ 2 の活性エネルギー線硬化型樹
脂から形成され、その表面に頂角が６０〜９５゜で、ピ
ッチが１００μｍ以下である一連の細長い断面三角形状
のプリズムが連続して多数形成さてなることを特徴とす
ものである。 SUMMARY OF THE INVENTION In view of such a situation, the inventors of the present invention have a specific shape and are made of a specific material.
The present inventors have found that the brightness of a liquid crystal display device can be improved by using the multi-prism sheet described above, and have reached the present invention. That is, the liquid crystal display device of the present invention includes a multi-prism sheet was placed on top of the backlight unit, and a liquid crystal display device which is installed on the multi-pre-nozzle sheet, the prism surface of the multi prism sheet and liquid crystal and a liquid crystal display element is disposed so as to face
A display device, wherein the multi-prism sheet is
The surface has an apex angle of 60 to 95 ° and a pitch of 100 μm or less.
Is a series of elongated triangular prisms
Many are formed and the elastic modulus at 25 ° C. is 10,000 to 5000.
Molded with 0Kg / cm 2 active energy ray-curable resin
It is characterized by having been done. In addition, the present invention
The multi-prism sheet has an elastic modulus of 10,000 at 25 ° C.
Active energy ray-curable tree of up to 50,000 kg / cm 2
It is formed from fat and has a vertex angle of 60-95 ° on its surface.
Series of elongated triangular cross-sections with a notch of 100 μm or less
Characterized in that a large number of prisms are continuously formed.
Things.
【０００５】本発明の液晶表示装置について図１を用い
て説明する。図１は、本発明の液晶表示装置の一実施例
を示した部分断面図であり、図中１はマルチプリズムシ
ートで背面照明手段３の上に、マルチプリズムシート１
のプリズム面が上向きとなるように設置されている。そ
して、マルチプリズムシート１の上には、そのプリズム
面と相対するように液晶表示素子２が設置されている。
液晶表示素子２は、例えば、スペーサーにより一定の間
隔を隔てて設けられた２枚のガラス基板の間に液晶が充
填されて構成されている。さらに、この２枚の上下ガラ
ス基板のそれぞれの外面には偏光板が設けられており、
上部のガラス基板の内面にはカラーフィルター層と、こ
のカラーフィルター層の外面に内部電極が設けられ、下
部のガラス基板の内面には内部電極が設けられている。
内部電極は、微小な画素電極が多数縦横に配列されて構
成されている。また、カラーフィルター層は、赤、緑、
青の３色の色フィルターを、画素電極に対応させて配列
して、各々の画素を形成している。A liquid crystal display device of the present invention will be described with reference to FIG. FIG. 1 is a partial cross-sectional view showing an embodiment of the liquid crystal display device of the present invention. In FIG.
Is installed so that the prism surface of the lens faces upward. On the multi-prism sheet 1, a liquid crystal display element 2 is provided so as to face the prism surface.
The liquid crystal display element 2 is configured, for example, by filling a liquid crystal between two glass substrates provided at a predetermined interval by a spacer. Further, a polarizing plate is provided on each outer surface of the two upper and lower glass substrates,
A color filter layer is provided on the inner surface of the upper glass substrate, and internal electrodes are provided on the outer surface of the color filter layer. Internal electrodes are provided on the inner surface of the lower glass substrate.
The internal electrode is configured by arranging a large number of minute pixel electrodes vertically and horizontally. The color filter layers are red, green,
Three color filters of blue are arranged corresponding to the pixel electrodes to form each pixel.
【０００６】背面照明手段３は、図１に示したように、
光の入射面と出射面を有する板状の導光体５と蛍光灯等
の線状光源７を具備してなるものである。導光体５は、
一側端面を光入射面とし、該光入射面と略直角の光出射
面と、その反対面に位置する反射面から構成され、反射
面には反射膜６が形成され、必要に応じて光出射面ある
いは反射面に光量調整パターンが形成されている。導光
体５の光入射面に対向して、蛍光灯等の線状光源７が配
置されている。そして、導光板５の光入射面から入射し
た線状光源７からの入射光が、導光板５を通して、一部
は反射膜６に反射して光出射面から出射して、マルチプ
リズムシート１を通して液晶表示素子２の裏面側へ均一
に照射するようになっている。なお、背面照明手段３と
しては、図１に示した構造のものに限らず、通常使用さ
れている種々の背面照射手段を使用することができる。[0006] As shown in FIG.
Plate-shaped light guide 5 having a light incident surface and a light exit surface, a fluorescent lamp, and the like
The linear light source 7 is provided. The light guide 5 is
One end face is a light incident surface, and light is emitted substantially perpendicular to the light incident surface.
Surface, and a reflective surface located on the opposite side.
A reflection film 6 is formed on the surface, and a light exit surface is provided as necessary.
Alternatively, a light amount adjustment pattern is formed on the reflection surface. Light guide
A linear light source 7 such as a fluorescent lamp is arranged opposite the light incident surface of the body 5.
Is placed. Then, incident light from the linear light source 7 incident from the light incident surface of the light guide plate 5 passes through the light guide plate 5, partially reflects on the reflection film 6 and exits from the light exit surface, and passes through the multi-prism sheet 1. Irradiation is uniformly performed on the back surface side of the liquid crystal display element 2. The backlight unit 3 is not limited to the one shown in FIG. 1, but may be any of various commonly used backlight units.
【０００７】マルチプリズムシート１は、樹脂板、シー
トあるいはフィルムから形成されており、その一方の表
面に一連の細長い断面三角形状のプリズムが連続して多
数形成されている。マルチプリズムシート１の部分断面
図を図２に示した。図中８は、合成樹脂からなる透明基
材であって、透明基材８の一方の表面にプリズム形状が
形成された合成樹脂からなるプリズム部９が一体に構成
されている。なお、本発明のマルチプリズムシート１
は、図２のように透明基材とレンズ部の２層構造として
もよいが、透明基材を用いないものでもよいし、透明基
材を剥離して使用する構造のものであってもよい。The multi-prism sheet 1 is formed from a resin plate, a sheet or a film, and a large number of a series of elongated prisms having a triangular cross section are continuously formed on one surface thereof. FIG. 2 shows a partial cross-sectional view of the multi-prism sheet 1. In the figure, reference numeral 8 denotes a transparent base made of a synthetic resin, and a prism portion 9 made of a synthetic resin having a prism shape formed on one surface of the transparent base 8 is integrally formed. The multi-prism sheet 1 of the present invention
May have a two-layer structure of a transparent base material and a lens portion as shown in FIG. 2, but may have no transparent base material, or may have a structure in which the transparent base material is peeled off and used. .
【０００８】本発明の液晶表示装置において、マルチプ
リズムシートの表面に形成されるプリズム部は、プリズ
ム頂角の角度θを６０〜９５゜の範囲に設定することが
重要である。これは、プリズム頂角の角度θが６０゜未
満では、指向性が顕著になり正面以外から見た場合には
画面が著しく暗くなるためえあり、逆に９５゜を超える
と光の集光性が低下し輝度向上効果が得られなくなった
り、プリズムシートの厚さによる光の吸収のために輝度
が低下するためである。[0008] In the liquid crystal display device of the present invention, multiplexed
Prism portions formed on the surface of the prism sheet, it is important to set the angle θ of the prism apex angle in the range of 60 to 95 °. This is the angle θ is 60 ° Not <br/> Mitsurude prism apex angle, there Tamee screen becomes remarkably dark when viewed from the other front face directed it becomes significant, more than 95 ° in the opposite This is because the light condensing property is reduced and the effect of improving brightness cannot be obtained, or the brightness is reduced due to light absorption due to the thickness of the prism sheet.
【０００９】プリズムのピッチａは、１００μｍ以下で
あることが好ましく、さらに好ましくは７０〜９０μｍ
の範囲である。これは、液晶表示装置のカラー化に伴
い、そのカラーフィルターのピッチが小さくなってきて
おり、画面のモアレ模様の発生を防止や画面の精細度を
向上の観点から、プリズムのピッチａも小さい方が好ま
しいためである。また、プリズムの凹凸の高さｂは、プ
リズム頂角の角度θとプリズムのピッチａの値によって
決定されるが、３０〜５０μｍの範囲であることが好ま
しい。さらに、プリズムシート１の厚さｃは、強度面か
らは厚い方が好ましく、光学的には光の吸収を抑えるた
め薄い方が好ましい。このため、使用する液晶表示装置
の画面の大きさ、使用条件等によって適度な厚さに設定
されるが、例えば、４〜１０インチ程度の画面の液晶表
示装置では数百μｍ以下程度の厚さであることが好まし
く、２００〜５００μ程度の範囲であれば、強度および
光学特性のバランスがとれて好ましい。The pitch a of the prism is preferably 100 μm or less, more preferably 70 to 90 μm.
Range. This is because the pitch of the color filter is becoming smaller with the colorization of the liquid crystal display device, and from the viewpoint of preventing the occurrence of moire patterns on the screen and improving the definition of the screen, the pitch a of the prism is also smaller. Is preferred. The height b of the irregularities of the prism is determined by the value of the angle θ of the prism apex angle and the pitch a of the prism, and is preferably in the range of 30 to 50 μm. Further, the thickness c of the prism sheet 1 is preferably thicker in terms of strength, and is preferably thinner optically to suppress light absorption. For this reason, an appropriate thickness is set depending on the size of the screen of the liquid crystal display device to be used, use conditions, etc. For example, a liquid crystal display device with a screen of about 4 to 10 inches has a thickness of about several hundred μm or less. Is preferably in the range of about 200 to 500 μm because the strength and the optical characteristics are balanced.
【００１０】上記のような構成による本発明の液晶表示
装置では、マルチプリズムシートのオウリズム面が液晶
表示素子と相対するように、マルチプリズムシートを背
面照射手段の上に設置したことにより、背面表示装置か
ら出射する光を液晶表示素子方向へ集中して出射するこ
とができるので、光源からの光を有効に活用できる輝度
の高い指向性に優れた液晶表示装置が得られるものであ
る。さらに、本発明においては、２枚あるいはそれ以上
のマルチプリズムシートを重ね合わせて使用することも
でき、さらなる輝度の向上を図るとともに、プリズムの
方向の組合せによって種々の指向性を持たせることがで
きる。しかし、マルチプリズムシートによる光量の損失
等を考慮すると、通常は１枚のマルチプリズムシートの
使用で十分である。In the liquid crystal display device of the present invention having the above-described structure, the multi-prism sheet is set on the back-side illuminating means so that the orismal surface of the multi-prism sheet faces the liquid crystal display element. Since the light emitted from the device can be concentrated and emitted in the direction of the liquid crystal display element, a liquid crystal display device with high luminance and excellent directivity capable of effectively utilizing the light from the light source can be obtained. Furthermore, in the present invention, two or more multi-prism sheets can be used in a superposed state, and furthermore, the luminance can be further improved, and various directivities can be provided by combining the directions of the prisms. . However, in consideration of the loss of the light amount due to the multi-prism sheet, it is usually sufficient to use one multi-prism sheet.
【００１１】本発明のマルチプリズムシートの製造方法
としては、合成樹脂を射出成形する方法、樹脂板と型と
を当接させて、これを加熱加圧することにより型の表面
形状を転写する押圧成形法、あるいは活性エネルギー線
硬化型樹脂組成物を表面凹凸を有する型内へ注入後、活
性エネルギー線を照射して硬化させる方法等のいずれの
方法も使用できるが、光学特性や生産性等の観点から活
性エネルギー線硬化型樹脂組成物を使用する方法が最も
好ましい。The method of manufacturing the multi-prism sheet according to the present invention includes a method of injection molding a synthetic resin, a method of pressing a resin plate and a mold in contact with each other, and transferring the surface shape of the mold by heating and pressing. Any method can be used, such as a method of injecting an active energy ray-curable resin composition into a mold having surface irregularities, and then irradiating with an active energy ray to cure the composition, but from the viewpoint of optical characteristics and productivity, etc. The most preferred method is to use an active energy ray-curable resin composition.
【００１２】以下、本発明のマルチプリズムシートの製
造方法について説明する。活性エネルギー線硬化型樹脂
組成物としては、不飽和ポリエステル−スチレン系、エ
ポキシ樹脂−ルイス酸系、ポリエン−チオール系、（メ
タ）アクリル酸エステル系等が挙げられる。中でも、透
明性の高い（メタ）アクリル酸エステル系が特に好まし
く、例えば、ポリエステル（メタ）アクリレート、エポ
キシ（メタ）アクリレート、ポリウレタン（メタ）アク
リレート等のプレポリマーと、単官能あるいは多官能の
（メタ）アクリレートモノマーとの組合せ等が挙げられ
る。これら樹脂は、単独あるいは組み合わせて使用する
ことができるが、得られるプリズムシートの弾性率等を
考慮して選択することが好ましい。特に、活性エネルギ
ー線硬化型樹脂の硬化後の２５℃における弾性率が１０
０００〜５００００ｋｇ／ｃｍ2の範囲にあるように調
整することが好ましい。これは、弾性率が１００００ｋ
ｇ／ｃｍ2 未満であると、プリズムシートが柔らかくな
り液晶表示装置に組込む際の取扱い性や作業性に劣ると
ともに、液晶表示素子とプリズム頂部とが接触する場合
にプリズム頂部に潰れが生じ画面上に影が現れるためで
ある。また、弾性率が５００００ｋｇ／ｃｍ2 を超える
と、プリズムシートが硬く脆くなり僅かの衝撃によって
破損するおそれがあるためである。Hereinafter, a method for manufacturing the multi-prism sheet of the present invention will be described. Examples of the active energy ray-curable resin composition include unsaturated polyester-styrene type, epoxy resin-Lewis acid type, polyene-thiol type, (meth) acrylate type and the like. Among them, a highly transparent (meth) acrylate ester type is particularly preferable. For example, a prepolymer such as polyester (meth) acrylate, epoxy (meth) acrylate, polyurethane (meth) acrylate and monofunctional or polyfunctional (meth) And acrylate monomers. These resins can be used alone or in combination, but it is preferable to select them in consideration of the elastic modulus of the obtained prism sheet. In particular, the elastic modulus at 25 ° C. of the active energy ray-curable resin after curing is 10%.
It is preferable to adjust so as to be in the range of 000 to 50,000 kg / cm 2 . This is because the elastic modulus is 10,000k
If it is less than g / cm 2 , the prism sheet becomes soft and the handling and workability when assembling into a liquid crystal display device are poor, and when the liquid crystal display element contacts the prism top, the prism top is crushed to cause a problem on the screen. This is because a shadow appears on the image. On the other hand, when the elastic modulus exceeds 50,000 kg / cm 2 , the prism sheet is hard and brittle, and may be damaged by a slight impact.
【００１３】上記したような活性エネルギー線硬化型樹
脂組成物を金型に塗布し、樹脂組成物の表面を平滑化し
た後、透明基材を重ね合わせ活性エネルギー線を照射し
て硬化させる。ここで、透明基材としては透明性の高い
ものであれば、厚さ、材料については特に限定されるも
のではないが、活性エネルギー線の透過性や取扱性等を
考慮した場合には、厚さ３ｍｍ以下のものが好ましい。
また、材料としては、例えば、アクリル樹脂、ポリカー
ボネート樹脂、ポリエステル樹脂、ポリスチレン樹脂、
フッ素樹脂、ポリイミド樹脂、これらの樹脂の混合物等
の合成樹脂あるいはガラス等が挙げられる。使用できる
活性エネルギー線としては、電子線、イオン線等の粒子
線、γ線、Ｘ線、紫外線、可視光線、赤外線等の電磁波
線等が挙げられるが、硬化速度や生産設備等の点から紫
外線が好ましい。After the active energy ray-curable resin composition as described above is applied to a mold and the surface of the resin composition is smoothed, the transparent substrates are overlapped and cured by irradiation with active energy rays. Here, as long as the transparent base material has high transparency, the thickness and the material are not particularly limited. Those having a thickness of 3 mm or less are preferable.
Further, as the material, for example, acrylic resin, polycarbonate resin, polyester resin, polystyrene resin,
Synthetic resins such as fluororesins, polyimide resins, mixtures of these resins, and the like, and glass are exemplified. Examples of usable active energy rays include particle beams such as electron beams and ion beams, electromagnetic rays such as γ-rays, X-rays, ultraviolet rays, visible rays, and infrared rays, and ultraviolet rays from the viewpoint of curing speed and production equipment. Is preferred.
【００１４】このようにして製造された透明基材上に活
性エネルギー線で硬化された樹脂組成物からなるマルチ
プリズムシートは、そのまま使用することもできるが、
透明基材を剥離して使用することもできる。The multi-prism sheet made of the resin composition cured on the transparent base material by the active energy ray can be used as it is.
The transparent substrate can be peeled off before use.
【００１５】[0015]
【実施例】以下、実施例によって本発明を具体的に説明
する。 実施例１ 成形後のプリズムのピッチが５０μｍ、プリズム頂角が
９０゜となるように予め設計された金型に、紫外線硬化
型樹脂組成物として以下の混合物を塗布し、その表面を
平滑化した後、厚さ５００μｍのポリカーボネートフィ
ルムを重ね合わせた。次いで、３２０〜３９０ｎｍの積
算紫外線照射量で１０００ｍＪ／ｃｍ2の紫外線を照射
して、紫外線硬化型樹脂組成物を硬化させた。その後、
金型から剥離してマルチプリズムシートを得た。The present invention will be specifically described below with reference to examples. Example 1 The following mixture was applied as a UV-curable resin composition to a mold previously designed such that the prism pitch after molding was 50 μm and the prism apex angle was 90 °, and the surface was smoothed. Thereafter, a polycarbonate film having a thickness of 500 μm was overlaid. Next, ultraviolet rays of 1000 mJ / cm 2 were irradiated at an integrated irradiation amount of 320 to 390 nm to cure the ultraviolet-curable resin composition. afterwards,
The multi-prism sheet was obtained by peeling from the mold.
【００１６】 ファンクリルＦＡ−３２１Ｍ ４５重量部 （日立化成社製エチレンオキシド変性 ビスフェノールＡメタクリレート） ＮＫエステルＡ−ＢＰＥ−４ ２５重量部 （新中村化学社製エチレンオキシド変 性ビスフェノールＡジアクリレート） サートマー２８５ ３０重量部 （サートマー社製テトラヒドロフルフ リルアクリレート） ダロキュアー１１７３ ３重量部 （メルクジャパン社製２−ヒドロキシ −２−メチル−１−フェニルプロパ ン−１−オン） 表面輝度７０００ｃｄ／ｍ2 を有する背面照射手段を用
いた液晶表示装置を用いて、得られたマルチプリズムシ
ートを図１に示したように背面照射手段の上にプリズム
面が液晶表示素子に相対するように設置して、液晶画面
の表面輝度を測定した。その結果、２９０ｃｄ／ｍ2 の
表面輝度を有していた。なお、マルチプリズムシートを
使用しない場合の表面輝度は、２００ｃｄ／ｍ2 であっ
た。上記樹脂組成物を用いて、ガラスセルキャスト法で
２ｍｍの厚さの樹脂板を作成し、得られた樹脂板を幅１
０ｍｍ、長さ６０ｍｍに切断し、３２ｍｍの間隔に設置
した２点で支え３点曲げ試験を行った。その結果、２５
０００ｋｇ／ｃｍ2の曲げ弾性率を有していた。FANCRYL FA-321M 45 parts by weight (Ethylene oxide modified bisphenol A methacrylate manufactured by Hitachi Chemical Co., Ltd.) NK ester A-BPE-4 25 parts by weight (Shin Nakamura Chemical Co., Ltd. ethylene oxide modified bisphenol A diacrylate) Sartomer 285 30 parts by weight Part (tetrahydrofurfuryl acrylate manufactured by Sartomer Co., Ltd.) Darocure 1173 3 parts by weight (2-hydroxy-2-methyl-1-phenylpropan-1-one manufactured by Merck Japan Co., Ltd.) A back irradiation means having a surface luminance of 7000 cd / m 2 Using the used liquid crystal display device, the obtained multi-prism sheet was placed on the back-side illuminating means so that the prism surface was opposed to the liquid crystal display element as shown in FIG. It was measured. As a result, it had a surface luminance of 290 cd / m 2 . The surface luminance when the multi-prism sheet was not used was 200 cd / m 2 . Using the above resin composition, a resin plate having a thickness of 2 mm was prepared by a glass cell casting method, and the obtained resin plate was formed to have a width of 1 mm.
The test piece was cut into 0 mm and 60 mm in length, and supported at two points placed at an interval of 32 mm to perform a three-point bending test. As a result, 25
It had a flexural modulus of 000 kg / cm 2 .
【００１７】実施例２ 成形後のプリズムのピッチが５０μｍ、プリズム頂角が
７５゜となるように予め設計された金型を用いた以外
は、実施例１と同一の紫外線硬化型樹脂組成物を用い
て、同一の製造条件でマルチプリズムシートを得た。得
られたマルチプリズムシートを用いて、実施例１と同一
の方法で表面輝度を測定した。その結果、３００ｃｄ／
ｍ2 の表面輝度を有していた。Example 2 The same ultraviolet-curable resin composition as in Example 1 was used except that a mold was designed so that the prism pitch after molding was 50 μm and the prism apex angle was 75 °. A multi-prism sheet was obtained under the same manufacturing conditions. Using the obtained multi-prism sheet, the surface luminance was measured in the same manner as in Example 1. As a result, 300 cd /
It had a surface brightness of m 2 .
【００１８】実施例３ 成形後のプリズムのピッチが５０μｍ、プリズム頂角が
１００゜となるように予め設計された金型を用いた以外
は、実施例１と同一の紫外線硬化型樹脂組成物を用い
て、同一の製造条件でマルチプリズムシートを得た。得
られたマルチプリズムシートを用いて、実施例１と同一
の方法で表面輝度を測定した。その結果、２２０ｃｄ／
ｍ2 の表面輝度を有していた。Example 3 The same ultraviolet-curable resin composition as in Example 1 was used except that a mold designed so that the pitch of the prism after molding was 50 μm and the apex angle of the prism was 100 ° was used. A multi-prism sheet was obtained under the same manufacturing conditions. Using the obtained multi-prism sheet, the surface luminance was measured in the same manner as in Example 1. As a result, 220 cd /
It had a surface brightness of m 2 .
【００１９】実施例４ 成形後のプリズムのピッチが５０μｍ、プリズム頂角が
６０゜となるように予め設計された金型を用いた以外
は、実施例１と同一の紫外線硬化型樹脂組成物を用い
て、同一の製造条件でマルチプリズムシートを得た。得
られたマルチプリズムシートを用いて、実施例１と同一
の方法で表面輝度を測定した。その結果、２９３ｃｄ／
ｍ2 の表面輝度を有していた。Example 4 The same ultraviolet-curable resin composition as in Example 1 was used except that a mold designed in advance so that the prism pitch after molding was 50 μm and the prism apex angle was 60 ° was used. A multi-prism sheet was obtained under the same manufacturing conditions. Using the obtained multi-prism sheet, the surface luminance was measured in the same manner as in Example 1. As a result, 293 cd /
It had a surface brightness of m 2 .
【００２０】[0020]
【００２１】比較例１ 成形後のプリズムのピッチが５０μｍ、プリズム頂角が
１００゜となるように予め設計された金型を用いた以外
は、実施例１と同一の紫外線硬化型樹脂組成物を用い
て、同一の製造条件でマルチプリズムシートを得た。得
られたマルチプリズムシートを用いて、実施例１と同一
の方法で表面輝度を測定した。その結果、１９６ｃｄ／
ｍ2 の表面輝度を有していた。Comparative Example 1 The same ultraviolet-curable resin composition as in Example 1 was used except that a mold designed in advance so that the prism pitch after molding was 50 μm and the prism apex angle was 100 ° was used. A multi-prism sheet was obtained under the same manufacturing conditions. Using the obtained multi-prism sheet, the surface luminance was measured in the same manner as in Example 1. As a result, 196 cd /
It had a surface brightness of m 2 .
【００２２】比較例２ 実施例１と同一のマルチプリズムシートを、プリズム面
が背面照射手段側に向くように設置した以外は、実施例
１と同一の方法で表面輝度を測定した。その結果、１９
５ｃｄ／ｍ2 の表面輝度を有していた。Comparative Example 2 The surface luminance was measured in the same manner as in Example 1 except that the same multi-prism sheet as in Example 1 was installed so that the prism face was directed toward the backside illuminating means. As a result, 19
It had a surface luminance of 5 cd / m 2 .
【００２３】[0023]
【発明の効果】本発明の液晶表示装置は、背面照射手段
の上にプリズム頂角の角度が特定の範囲にあるマルチプ
リズムシートを、そのプリズム面が液晶表示素子と相対
するように設置することによって、背面照射手段から出
射する光を液晶表示素子方向へ集中して出射することが
でき、光源からの光を有効に活用できる輝度の高い指向
性に優れたものであり、背面照射手段の別段の明るさの
向上を行うことなく、カラー液晶表示装置でも十分な輝
度を有するものである。According to the liquid crystal display device of the present invention, a multi-prism sheet having a prism apex angle within a specific range is provided on a backside illuminating means so that the prism surface faces the liquid crystal display element. The light emitted from the back illuminating means can be concentrated and emitted in the direction of the liquid crystal display element, and the light from the light source can be effectively used. The color liquid crystal display device has a sufficient luminance without improving the brightness of the display.
【図１】本発明の液晶表示装置の概略を示す断面図であ
る。FIG. 1 is a sectional view schematically showing a liquid crystal display device of the present invention.
【図２】本発明のマルチプリズムシートの一部を示す断
面図である。FIG. 2 is a sectional view showing a part of the multi-prism sheet of the present invention.
１ マルチプリズムシート ２ 液晶表示素子 ３ 背面照明手段 ８ 透明基材 ９ プリズム部 DESCRIPTION OF SYMBOLS 1 Multi-prism sheet 2 Liquid crystal display element 3 Back-lighting means 8 Transparent base material 9 Prism part
───────────────────────────────────────────────────── フロントページの続き (72)発明者 濱田 雅郎 愛知県名古屋市東区砂田橋四丁目１番60 号三菱レイヨン株式会社商品開発研究所 内 (72)発明者 大川 真 愛知県名古屋市東区砂田橋四丁目１番60 号三菱レイヨン株式会社商品開発研究所 内 (72)発明者 瀧川 高志 愛知県名古屋市東区砂田橋四丁目１番60 号三菱レイヨン株式会社商品開発研究所 内 (72)発明者 前沢 憲一 愛知県名古屋市東区砂田橋四丁目１番60 号三菱レイヨン株式会社商品開発研究所 内 合議体 審判長 東森 秀朋 審判官 稲積 義登 審判官 豊岡 静男 (56)参考文献 特開 平３−16032（ＪＰ，Ａ) 特開 平４−67016（ＪＰ，Ａ) 特開 平４−212125（ＪＰ，Ａ) 特開 平３−9838（ＪＰ，Ａ) 特開 平２−248215（ＪＰ，Ａ) 特開 平４−196288（ＪＰ，Ａ) 実開 平４−107201（ＪＰ，Ｕ) ──────────────────────────────────────────────────続 き Continuing on the front page (72) Inventor Masao Hamada 4-160, Sunadabashi, Higashi-ku, Nagoya-shi, Aichi Prefecture Inside Mitsubishi Rayon Co., Ltd. Product Development Laboratory (72) Inventor Makoto Okawa 4-chome, Sunadabashi, Higashi-ku, Nagoya-shi, Aichi Prefecture No. 1-60 Mitsubishi Rayon Co., Ltd. Product Development Laboratory (72) Inventor Takashi Takigawa 4-60 Sunadabashi, Higashi-ku, Nagoya-shi, Aichi Prefecture No. 1-60 Mitsubishi Rayon Co., Ltd. Product Development Laboratory (72) Inventor Kenichi Maezawa Aichi Prefecture 4-160, Sunadabashi, Higashi-ku, Nagoya-shi Mitsubishi Rayon Co., Ltd. Product Development Laboratory In-house panel Referee, Hidetomo Higashimori Referee, Yoshito Inazumi Referee, Shizuo Toyooka (56) References JP 3-16032 (JP, A) JP-A-4-67016 (JP, A) JP-A-4-212125 (JP, A) JP-A-3-9838 (JP, A) ) Patent Rights 2-248215 (JP, A) Patent Rights 4-196288 (JP, A) JitsuHiraku flat 4-107201 (JP, U)
Claims (4)
リズムシートと、このマルチプリズルシートの上に設置
された液晶表示素子とを備え、マルチプリズムシートの
プリズム面と液晶表示素子とが相対するように設置され
ている液晶表示装置であって、前記マルチプリズムシー
トが、その表面に頂角が６０〜９５゜で、ピッチが１０
０μｍ以下である一連の細長い断面三角形状のプリズム
が連続して多数形成され、２５℃の弾性率が１００００
〜５００００Ｋｇ／ｃｍ 2 の活性エネルギー線硬化型樹
脂で成形されていることを特徴とする液晶表示装置。And multi-prism sheet as claimed in claim 1] was placed on top of the backlight unit, and a liquid crystal display device which is installed on the multi-pre-nozzle sheet, the prism surface of the multi prism sheet and the liquid crystal display device A liquid crystal display device installed to face , wherein the multi-prism
The surface has an apex angle of 60-95 ° and a pitch of 10
A series of elongated triangular prisms with a cross section of 0 μm or less
Are continuously formed, and the elastic modulus at 25 ° C. is 10,000.
Active energy ray-curable tree of up to 50,000 kg / cm 2
A liquid crystal display device characterized by being molded with fat .
と該透明基材上に形成された活性エネルギー線硬化型樹
脂からなるプリズム部とからなることを特徴とする請求
項１記載の液晶表示装置。2. The method according to claim 1, wherein the multi-prism sheet includes a transparent substrate and an active energy ray-curable resin formed on the transparent substrate.
The liquid crystal display device according to claim 1, characterized in that comprising a fat or Ranaru prism unit.
０Ｋｇ／ｃｍ 2 の活性エネルギー線硬化型樹脂から形成
され、その表面に頂角が６０〜９５゜で、ピッチが１０
０μｍ以下である一連の細長い断面三角形状のプリズム
が連続して多数形成さてなることを特徴とする液晶表示
装置用マルチプリズムシート。 3. An elastic modulus at 25 ° C. of 10,000 to 5,000.
Formed from 0Kg / cm 2 active energy ray-curable resin
The surface has an apex angle of 60 to 95 ° and a pitch of 10
A series of elongated triangular prisms with a cross section of 0 μm or less
Liquid crystal display characterized by being formed continuously in large numbers
Multi prism sheet for equipment.
性エネルギー線硬化型樹脂からなるプリズム部とからな
ることを特徴とする請求項１記載の液晶表示装置用マル
チプリズムシート。 4. A transparent substrate and an active material formed on the transparent substrate.
With a prism part made of reactive energy ray-curable resin.
2. The liquid crystal display device according to claim 1, wherein
Chiprism sheet.