JP3077549B2 - Fabric for wetsuit - Google Patents
Fabric for wetsuitInfo
- Publication number
- JP3077549B2 JP3077549B2 JP07028901A JP2890195A JP3077549B2 JP 3077549 B2 JP3077549 B2 JP 3077549B2 JP 07028901 A JP07028901 A JP 07028901A JP 2890195 A JP2890195 A JP 2890195A JP 3077549 B2 JP3077549 B2 JP 3077549B2
- Authority
- JP
- Japan
- Prior art keywords
- fabric
- tetron
- yarn
- knitted fabric
- denier
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本発明は、太陽光の電磁波エネル
ギーを吸収して、熱に変換する効果を有し、水中での運
動時に着用する衣料等に適する軽量かつ保温性に優れた
ウェットスーツ用積層構造布帛に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention has the effect of absorbing electromagnetic energy of sunlight and converting it into heat, and is a lightweight and excellent heat retaining suit suitable for clothing worn when exercising in water. The present invention relates to a laminated structure fabric for use.
【０００２】[0002]
【従来の技術】従来、水着やウェットスーツなど、水中
で運動を行う時に着用する衣服類は、動き易さが最も重
視されることから、伸びの良い編地を用いて身体にフィ
ットするように縫製される。このため、水中から上がっ
た後、身体と水着の間に水が滞留すると同時に、衣服自
体が多量の水を含むため、冷えによる不快感を感じる。
着用者に冷えによる不快感を与えない方法として、表面
と裏面に伸びの良い編地を、中層にクロロプレンゴムを
用いた３層構造のウェットスーツがある。これは、伸縮
性に富み、断熱性に優れるクロロプレンゴムを中層にボ
ンディングすることで冷え感を与えない効果を有するも
のである。2. Description of the Related Art Conventionally, clothes to be worn when exercising in water, such as swimwear and wet suits, are made to fit the body using a stretchy knitted fabric, since the ease of movement is of the utmost importance. It is sewn. Therefore, after getting out of the water, the water stays between the body and the swimsuit, and at the same time, the clothes themselves contain a large amount of water, so that the user feels discomfort due to the cold.
As a method of not giving a wearer discomfort due to cooling, there is a three-layer wet suit using a knitted fabric with good elongation on the front and back surfaces and chloroprene rubber as a middle layer. This has an effect of not giving a feeling of cooling by bonding chloroprene rubber which is rich in elasticity and excellent in heat insulation to the middle layer.
【０００３】しかし、この生地によるウェットスーツを
着用して泳いだ場合、表層と裏層の生地はポリアミド繊
維やポリエステル繊維からなる編地が多く使用されてい
るため、濡れた状態では多量の水を含み冷感を覚える。
そして保温力を高めるため、クロロプレンゴムの厚さを
増すと身体とのフィット感が悪くなると同時に動き易さ
が低下する。また、クロロプレンゴムは直方体状のもの
をスライス後ボンディング加工を行うので、通常の長尺
のシート状のものをボンディングする場合に比べ厚さの
バラつきが大きく、製品として使えない部分もある等の
種々の問題点がある。[0003] However, when swimming in a wet suit made of this fabric, a large amount of water is used in the wet state because the fabric of the surface layer and the back layer is made of a knitted fabric made of polyamide fiber or polyester fiber. I feel a sense of coolness.
When the thickness of the chloroprene rubber is increased to increase the heat retention, the fit with the body is deteriorated and the ease of movement is reduced. Also, since chloroprene rubber is subjected to bonding after slicing a rectangular parallelepiped, there is a large variation in thickness compared to the case of bonding a normal long sheet, and there are some parts that cannot be used as products. There is a problem.
【０００４】また、特開平５ー３１１５０２号公報で
は、太陽光熱変換能を有する布帛に撥水加工を施した速
乾水着が提案されている。これは速乾保温性に効果は見
られるが、生地が一重と薄いため、水中から上がった後
の環境が盛夏期よりも低温である場合の保温性効果は期
待できない。Japanese Patent Application Laid-Open No. 5-311502 proposes a quick-drying swimsuit in which a cloth having solar heat conversion ability is subjected to a water-repellent treatment. Although this has an effect on quick-drying heat retention, the effect of heat retention when the environment after rising from the water is lower than that in the midsummer season cannot be expected due to the single and thin dough.
【０００５】[0005]
【発明が解決しょうとする課題】本発明は、かかる従来
の水着やウェットスーツなどの問題点を解消し、水中で
の運動性を損なわず、水中から上がってからの身体の冷
感を軽減させるための優れたウェットスーツ用の太陽光
吸収保温性布帛を、低コストで提供するものである。SUMMARY OF THE INVENTION The present invention solves the problems of such conventional swimsuits and wet suits, and does not impair motility in water, and reduces the feeling of cooling of the body after getting out of water. The present invention provides an excellent sun-absorbing and heat-retaining fabric for a wet suit at a low cost.
【０００６】[0006]
【課題を解決するための手段】上記した目的を達成する
ため、本発明は、次の構成からなる。すなわち、中層を
形成する透明ストレッチフィルムの両面に編地を貼り合
わせてなる積層布帛であって、少なくとも片面の編地が
太陽光吸収性微粒子を１．５〜５．０重量％含有する合
成繊維マルチフィラメント糸条を２０〜１００％含む編
地であり、波長０．７６〜１．３μｍの電磁波の分光反
射率の最大値が４０％以下、目付が３６０〜６００ｇ／
ｍ2、伸長率がタテ、ヨコ共４０％以上であることを特
徴とするウェットスーツ用布帛である。このことにより
効率良く保温性が得られることから冷えによる不快感を
軽減するものである。To achieve the above-mentioned object, the present invention comprises the following constitution. That is, a synthetic fabric in which a knitted fabric is attached to both sides of a transparent stretch film forming a middle layer, wherein at least one side of the knitted fabric contains 1.5 to 5.0% by weight of sunlight-absorbing fine particles. A knitted fabric containing 20 to 100% of a multifilament yarn, the maximum value of the spectral reflectance of electromagnetic waves having a wavelength of 0.76 to 1.3 μm is 40% or less, and the basis weight is 360 to 600 g /
m 2, and wetsuit cloth, wherein the elongation rate is vertical, horizontal co-40%. As a result, heat retention can be efficiently obtained, so that discomfort due to cooling can be reduced.
【０００７】太陽光吸収性微粒子とは具体的にはカーボ
ン粉末（Ｃ）、チタン（Ｔｉ）、ジルコニウム（Ｚ
ｒ）、ハフニウム（Ｈｆ）、タンタル（Ｔａ）、シリコ
ン（Ｓｉ）、ホウ素（Ｂ）、などの金属の炭化物、ジル
コニウム（Ｚｒ）、シリコン（Ｓｉ）、クロム（Ｃ
ｒ）、鉄（Ｆｅ）、銅（Ｃｕ）、などの金属の酸化物、
アントラキノン化合物などの染料が挙げられ、粒子径は
５μｍ以下が好ましく、５μｍ以上になると製造不安定
となる。また、この微粒子をポリマー中に含有させる量
は１．５〜５．０重量％とするものであり、１．５重量
％未満では太陽光吸収効果が十分ではない。一方、この
含有料が５．０重量％を超える場合には、繊維の製造工
程通過性が悪く、かつ、繊維強度が低くなり使用に耐え
ないなどの問題が発生する。Specifically, the solar light absorbing fine particles include carbon powder (C), titanium (Ti), zirconium (Z
r), metal carbides such as hafnium (Hf), tantalum (Ta), silicon (Si), boron (B), zirconium (Zr), silicon (Si), chromium (C
r) oxides of metals such as iron (Fe), copper (Cu),
Dyes such as anthraquinone compounds are mentioned, and the particle diameter is preferably 5 μm or less, and if it is 5 μm or more, the production becomes unstable. The content of the fine particles in the polymer is 1.5 to 5.0% by weight. If the amount is less than 1.5% by weight, the sunlight absorbing effect is not sufficient. On the other hand, if the content exceeds 5.0% by weight, problems such as poor fiber passage in the production process and low fiber strength resulting in unacceptable use arise.
【０００８】本発明の編地を構成する原糸としては、ポ
リアミド系、ポリエステル系、ポリプロピレン系、など
の合成繊維マルチフィラメント糸条、またはより伸長率
を与えるためにこれらの合成繊維マルチフィラメント糸
条と交編させるポリウレタン弾性糸条を用いることがで
き、特に限定するものではない。The yarn constituting the knitted fabric of the present invention may be a synthetic fiber multifilament yarn of polyamide, polyester, polypropylene or the like, or a synthetic fiber multifilament yarn for giving a higher elongation. Polyurethane elastic yarns to be knitted can be used without any particular limitation.
【０００９】編地を構成する合成繊維の糸形態として
は、モノフィラメントではなく、マルチフィラメントを
用いるものである。モノフィラメントの場合は肌触りが
悪く、着用感に劣るものである。マルチフィラメントの
フィラメント数としては、５〜１００フィラメントが好
ましく、単繊維繊度としては０．５〜１０デニールが好
ましい。また、単繊維の断面形状は特に限定されず、丸
断面、３角断面、その他異形断面などを用いることがで
きる。As the yarn form of the synthetic fibers constituting the knitted fabric, multifilaments are used instead of monofilaments. In the case of a monofilament, the feel is poor and the wearing feeling is inferior. The number of filaments of the multifilament is preferably 5 to 100 filaments, and the single fiber fineness is preferably 0.5 to 10 denier. In addition, the cross-sectional shape of the single fiber is not particularly limited, and a round cross section, a triangular cross section, or other irregular cross sections can be used.
【００１０】編地の種類としては丸編地であるシングル
丸編地、ダブル丸編地、経編地であるトリコット地、ラ
ッセル地の何れも用いることができ、特に限定するもの
ではない。太陽光吸収系微粒子を含有させた合成繊維マ
ルチフィラメント糸条の交編率は２０〜１００％とする
ものである。２０％未満の場合は太陽光吸収性に劣り、
狙いとする保温性に劣るものとなる。As the kind of the knitted fabric, any of a single circular knitted fabric as a circular knitted fabric, a double circular knitted fabric, a tricot fabric as a warp knitted fabric, and a Russell fabric can be used, and it is not particularly limited. The cross-knitting ratio of the synthetic fiber multifilament yarn containing the sun-absorbing fine particles is 20 to 100%. If it is less than 20%, the solar absorption is poor,
It is inferior in the intended heat retention.
【００１１】本発明の布帛では、上記の編地を少なくと
も片面に貼り合わせ、中層に透明なストレッチ性ポリウ
レタンフィルムをボンディングした積層構造とする。太
陽光吸収系微粒子を含有させた合成繊維マルチフィラメ
ント糸条を交編させた編地を片面のみに貼り合わせた３
層構造の場合、太陽光吸収性微粒子を含有しない通常の
合成繊維マルチフィラメント糸条からなる編地面を内側
または外側にして使用する。内側の編地片面の表面形状
としては平滑形状、凹凸形状のどちらでも良く、特に限
定されるものではない。The fabric of the present invention has a laminated structure in which the above knitted fabric is bonded to at least one surface and a transparent stretchable polyurethane film is bonded to the middle layer. 3. A knitted fabric obtained by cross-knitting a synthetic fiber multifilament yarn containing sunlight-absorbing fine particles is bonded to only one surface.
In the case of a layered structure, the knitted ground made of ordinary synthetic fiber multifilament yarn containing no sunlight-absorbing fine particles is used inside or outside. The surface shape of one surface of the inner knitted fabric may be any of a smooth shape and an uneven shape, and is not particularly limited.
【００１２】中層を形成するフィルムは透明で、かつ、
ストレッチ性を有することが重要である。透明であるこ
との必要性は下記のことによる。太陽光吸収系微粒子を
含有させた合成繊維マルチフィラメント糸条の混合され
た編地が、使用される表面に貼り合わされた場合は透明
である必要性はない。しかし、使用される裏面、すなわ
ち、肌面に貼り合わされた場合は、フィルムの透明性が
必要となる。これは、太陽光が表面に貼り合わされた編
地を形成するループ間の透間を通り、かつ、中層を形成
するフィルムを通過して裏面に貼り合わされた編地にま
で届き、太陽光吸収保温性効果を得るために、前記フィ
ルムの透明性が必要となる。透明性の尺度としては使用
するフィルムの光透過率で表現すれば光透過率７０％以
上が好ましい。The film forming the middle layer is transparent, and
It is important to have stretchability. The need for transparency is due to: When the knitted fabric in which the synthetic fiber multifilament yarn containing the solar light absorbing fine particles is mixed is bonded to the surface to be used, it is not necessary to be transparent. However, when the film is bonded to the back surface used, that is, the skin surface, the film needs to have transparency. This is because sunlight passes through the gaps between the loops forming the knitted fabric bonded to the front surface, reaches the knitted fabric bonded to the back surface through the film forming the middle layer, and absorbs sunlight. In order to obtain the effect, transparency of the film is required. As a measure of transparency, a light transmittance of 70% or more is preferable in terms of the light transmittance of the film used.
【００１３】フィルムのストレッチ性としては、フィル
ム単体の伸長率として１００％以上あることが好まし
い。伸長率が１００％以下の場合は、編地を貼り合わせ
た後の積層構造布帛の伸長率をタテ、ヨコ、共４０％以
上にすることは困難となる。また、フィルムの厚さは特
に限定されるものではないが、フィルムの破れを防ぐ一
方、布帛の厚さが過度に厚くなるのを防ぐ観点から５０
μｍ以下１０μｍ以上が好ましい。The stretchability of the film is preferably 100% or more as the elongation of the film alone. When the elongation rate is 100% or less, it is difficult to make the elongation rate of the laminated structure fabric after laminating the knitted fabrics equal to or more than 40% in the vertical, horizontal, and vertical directions. In addition, the thickness of the film is not particularly limited, but from the viewpoint of preventing the film from being broken and preventing the cloth from being excessively thickened.
It is preferably from 10 μm to 10 μm.
【００１４】本発明のウェットスーツ用布帛は、波長
０．７６〜１．３μｍの電磁波の分光反射率の最大値を
４０％以下、好ましくは３０％以下、さらに好ましくは
２０％以下とするものである。分光反射率の最大値が４
０％を超えると太陽光吸収効率が劣るものとなる。な
お、編地の場合、一般にこの分光反射率を５％未満とす
るのは困難である。The wet suit fabric of the present invention has a maximum spectral reflectance of 40% or less, preferably 30% or less, more preferably 20% or less, of the electromagnetic wave having a wavelength of 0.76 to 1.3 μm. is there. The maximum value of the spectral reflectance is 4
If it exceeds 0%, the sunlight absorption efficiency will be poor. In the case of a knitted fabric, it is generally difficult to reduce the spectral reflectance to less than 5%.
【００１５】本発明の貼り合わせた後の布帛の目付は３
６０〜６００ｇ／ｍ2とするものである。目付が３６０
ｇ／ｍ2未満の場合は目付が少なすぎ、狙った保温性が
得られない。一方、６００ｇ／ｍ2を超えると着用時に
重たく、身体とのフィット性も損なわれる。また、本発
明の布帛の伸長率は、タテ、ヨコ、共４０％以上とする
ものである。伸長率が４０％未満の場合は、身体にフィ
ットした状態で着用される水着やウェットスーツ等で
は、身体の動きが妨げられ、着用性に劣るものとなる。
この伸長率が高い程着用性に優れることになる。ポリウ
レタン弾性糸を混用した編地にして貼り合わせることに
より、より優れた伸長率を有する編地を得ることができ
好ましい。なお、一般に伸長率を１００％以上とするこ
とは困難である。The fabric weight after lamination of the present invention is 3
It is 60 to 600 g / m 2 . The basis weight is 360
If it is less than g / m 2 , the basis weight is too small and the desired heat retention cannot be obtained. On the other hand, if it exceeds 600 g / m 2 , it is heavy when worn, and the fit to the body is impaired. Further, the elongation percentage of the fabric of the present invention is set to 40% or more for both vertical and horizontal lengths. When the elongation rate is less than 40%, the movement of the body is hindered in a swimsuit, a wet suit, or the like that is worn in a state of fitting to the body, resulting in poor wearability.
The higher the elongation, the better the wearability. By knitting a knitted fabric mixed with polyurethane elastic yarn and bonding them together, a knitted fabric having a more excellent elongation rate can be obtained, which is preferable. In general, it is difficult to increase the elongation rate to 100% or more.
【００１６】この積層構造布帛に撥水加工を付与するこ
とにより、より速乾性等の着用快適性を得ることができ
好ましい。使用する撥水剤としては、シリコーン系撥水
剤、フッ素系撥水剤など通常の撥水剤を用いればよい。
また、撥水加工法も一般的に用いられている方法でよ
い。By applying a water-repellent treatment to this laminated structure fabric, wearing comfort such as quick drying can be obtained, which is preferable. As a water repellent to be used, a normal water repellent such as a silicone water repellent or a fluorine water repellent may be used.
In addition, a water repellent processing method may be a generally used method.
【００１７】次に、本発明における目付、伸長率、光透
過率、分光反射率、太陽光吸収保温性（生地裏温度）の
評価方法について延べる。 〈目付〉正確に２５ｃｍ×２５ｃｍの試験片を２枚採取
する。試験片を乾燥機で乾燥させた後、標準状態の室内
に放置する。水分平衡になったら重さを０．１ｇまで測
り、この測定値を１６倍して１ｍ2当たりの重さに換算
し、２枚を平均値し、整数位で表す。Next, the evaluation method of the basis weight, elongation rate, light transmittance, spectral reflectance and sunlight absorption and heat retention (backside temperature of fabric) in the present invention will be described. <Density> Two test pieces of exactly 25 cm × 25 cm are collected. After the test piece is dried with a dryer, it is left in a room in a standard state. When the water equilibrium is reached, the weight is measured to 0.1 g, the measured value is multiplied by 16 to be converted to the weight per 1 m 2 , and the two sheets are averaged and expressed as an integer.
【００１８】〈伸長率〉ＪＩＳ Ｌ １０１８法に準じ
て行い、定速伸長法のグラブ法で行った。測定手順とし
ては、１０ｃｍ×１５ｃｍの評価サンプルをタテ方向、
ヨコ方向にそれぞれ３枚ずつ採取する。自記記録装置付
定速伸長形引張試験機を用い、上下つかみとも表側は
２．５４ｃｍ×２．５４ｃｍ、裏側は２．５４ｃｍ×
５．０８ｃｍのものを取付け、つかみ間隔を７．６ｃｍ
として評価サンプルのたるみや、張力を除いて、つかみ
に固定する。引張速度１０ｃｍ／分で１．８ｋｇ加重時
まで引伸し、その時のつかみ間隔Ｄ1を計り、次式によ
り伸長率Ｌ（％）を求め、３枚の平均値で表す。 伸長率Ｌ（％）＝｛（Ｄ1−Ｄ）／Ｄ｝×１００ ここに、Ｄはつかみ間隔（ｍｍ）、Ｄ1は１．８ｋｇ加
重時まで引伸した時のつかみ間隔（ｍｍ）を表す。この
伸長率Ｌ（％）が大きいほど水着やウェットスーツで着
用した場合、身体にフィットして泳ぎ易いことを意味す
る。<Extension> The extension was performed according to the JIS L1018 method, and the grab method of the constant-speed extension was used. As a measurement procedure, the evaluation sample of 10 cm × 15 cm was set in the vertical direction,
Three samples are taken each in the horizontal direction. Using a constant-speed extension type tensile tester with a self-recording device, the upper and lower grips are 2.54 cm x 2.54 cm on the front side and 2.54 cm x on the back side.
Attach the one with 5.08cm and set the grip distance to 7.6cm
Fix the sample to the grip, excluding the slack and tension of the evaluation sample. Tensile speed of 10 cm / min until 1.8kg weight during stretching, weighed distance D 1 grasp at that time, determine the elongation L (%) by the following formula, expressed in three average values. Elongation ratio L (%) = {(D 1 −D) / D} × 100 Here, D represents the gripping interval (mm), and D 1 represents the gripping interval (mm) when stretched up to a load of 1.8 kg. . The larger the elongation rate L (%), the more the swimsuit or wet suit is worn by a swimsuit or wetsuit, which means that the swimsuit fits the body and is easier to swim.
【００１９】〈太陽光吸収保温性（生地裏温度）〉５℃
×６５％ＲＨの人工気象室環境下で、生地表面に６００
ｋｃａｌ／ｍ2・ｈｒの日射を２５分間あてる。このと
きの生地裏面温度を熱電対で測定する。 〈分光反射率〉５ｃｍ×５ｃｍの大きさに評価サンプル
を切り、同じ大きさの黒色台紙に貼り付ける。自己分光
光度計（日立（株）製Ｕ−３４００Ｓｐｅｃｔｒｏｐｈ
ｏｔｏｍｅｔｅｒ）を用いてサンプルに、光の波長０．
７６〜１．３０μｍの範囲で変化させながら光を当て、
その時の評価サンプルの反射率（％）を測定する。<Sunlight absorption and heat retention (cloth back temperature)> 5 ° C
X 600% on the fabric surface under the environment of 65% RH
Irradiate with kcal / m 2 · hr for 25 minutes. The back surface temperature of the dough at this time is measured with a thermocouple. <Spectral Reflectance> An evaluation sample is cut into a size of 5 cm × 5 cm, and is attached to a black mount of the same size. Self-spectrophotometer (U-3400 Spectroph manufactured by Hitachi, Ltd.)
The wavelength of light is set to 0.degree.
Light is applied while changing in the range of 76 to 1.30 μm,
The reflectance (%) of the evaluation sample at that time is measured.
【００２０】以下、実施例により、本発明について具体
的に説明する。なお、実施例における動き易さの判定基
準と表示は次のとおりである。 〈動き易さ〉 ◎：布帛は伸縮性が非常に優れ、着用しても非常に動き
易い ○：布帛は伸縮性に優れ、着用しても動き易い ×：布帛は伸縮性に劣り、着用したら動きにくい 〈水中から上がっての身体冷感〉 ◎：ほとんど感じない ○：さほど感じない ×：感じるHereinafter, the present invention will be specifically described with reference to examples. The criteria and display of the ease of movement in the embodiment are as follows. <Ease of movement> ◎: The fabric has excellent elasticity and is very easy to move even when worn ○: The fabric has excellent elasticity and is easy to move even when worn ×: The fabric is inferior in elasticity and when worn Difficult to move <Cool feeling when rising from the water> ◎: Almost no feeling ○: Not much felt ×: Feel
【００２１】[0021]
【実施例１】表地には、太陽光吸収系微粒子であるカー
ボンを２．５ｗｔ％含有させた東レ（株）製ポリエステ
ルフィラメント”テトロン”（５０デニール１８フィラ
メント）、東レ（株）製カチオン可染ポリエステルフィ
ラメント”テトロン”（５０デニール３６フィラメン
ト）と東レ・デュポン（株）製ポリウレタン弾性糸”オ
ペロン”２０デニールを使用し、２８ゲージのシングル
トリコット機で２枚筬にてフロント筬にカーボン含有”
テトロン”糸２０％、カチオン可染”テトロン”糸８０
％とし、バック筬に”オペロン”糸を配してハーフ組織
を編成した。これを”オペロン”交編品の通常染色法に
より、黒色に染色した編地を用いた。Example 1 Toray Co., Ltd. polyester filament "Tetron" (50 denier 18 filaments) containing 2.5% by weight of carbon, which is solar absorption fine particles, and cationic dyeing dye manufactured by Toray Co., Ltd. Using a polyester filament "Tetron" (50 denier 36 filament) and a polyurethane elastic yarn "Operon" 20 denier manufactured by Toray DuPont Co., Ltd., using a 28 gauge single tricot machine, two reeds contain carbon in the front reed. "
Tetron "20% yarn, cationic dyeable" Tetron "yarn 80
%, And an "operon" thread was arranged on the back reed to form a half structure. A knitted fabric dyed in black by the usual dyeing method of "Operon" mixed knitted product was used.
【００２２】中層には、厚さ２５μｍ、光透過率９７
％、伸長率タテ、ヨコ、共１７０％のポリウレタンフィ
ルムを使用した。裏地には、東レ（株）製カチオン可染
ポリエステルフィラメント”テトロン”（５０デニール
３６フィラメント）と東レ・デュポン（株）製ポリウレ
タン弾性糸”オペロン”２０デニールを使用し、２８ゲ
ージのシングルトリコット機で２枚筬にてフロント筬
に”テトロン”糸、バック筬に”オペロン”糸を配して
ハーフ組織を編成した。これを”オペロン”交編品の通
常染色法により、黒色に染色した編地を用いた。The middle layer has a thickness of 25 μm and a light transmittance of 97
%, Elongation percentage, horizontal, 170% for both polyurethane films. The lining is made of Toray's cationic dyeable polyester filament "Tetron" (50 denier 36 filaments) and Toray Dupont's polyurethane elastic yarn "Operon" 20 denier using a 28 gauge single tricot machine. A half reed was formed by arranging a "Tetron" thread on the front reed and an "Operon" thread on the back reed. A knitted fabric dyed in black by the usual dyeing method of "Operon" mixed knitted product was used.
【００２３】前記３種類の素材を用い、３層構造になる
ようにしてポリウレタン樹脂を用い貼り合わせ加工を行
った。この布帛の目付は４２３ｇ／ｍ2、伸長率はタテ
４５．０％、ヨコ４９．１％、電磁波の波長０．７６〜
１．３μｍにおける分光反射率の最大値が２４％、人工
気象室で、６００ｋｃａｌ／ｍ2・ｈｒの日射を２５分
間あてた時の生地裏温度が４７．２℃であった。この布
帛を用いてウェットスーツを作り、５名の男性により１
１月度の海中で着用評価を行ったところ、動き易く、か
つ、水中から上がっての身体冷感が少なく快適なもので
あった。Using the above three types of materials, a lamination process was performed using a polyurethane resin so as to form a three-layer structure. The basis weight of this fabric is 423 g / m 2 , the elongation percentage is 45.0% in the vertical direction, 49.1% in the horizontal direction, and the wavelength of the electromagnetic wave is 0.76 to
The maximum value of the spectral reflectance at 1.3 μm was 24%, and the back temperature of the fabric when exposed to solar radiation of 600 kcal / m 2 · hr for 25 minutes in an artificial weather chamber was 47.2 ° C. A wet suit is made using this cloth, and one
When the wearing evaluation was performed in the sea in January, it was easy to move, and it was comfortable with little body cold feeling when rising from the water.
【００２４】[0024]
【実施例２】表地には、太陽光吸収系微粒子であるカー
ボンを１．５ｗｔ％含有させた東レ（株）製ポリエステ
ルフィラメント”テトロン”（５０デニール１８フィラ
メント）、東レ（株）製カチオン可染ポリエステルフィ
ラメント”テトロン”（５０デニール３６フィラメン
ト）と東レ・デュポン（株）製ポリウレタン弾性糸”オ
ペロン”２０デニールを使用し、２８ゲージのシングル
トリコット機で２枚筬にて、フロント筬にカーボン含
有”テトロン”糸２０％、カチオン可染”テトロン”糸
８０％とし、バック筬に”オペロン”糸を配してハーフ
組織を編成した。これを”オペロン”交編品の通常染色
法により、黒色に染色した編地を用いた。Example 2 Toray Co., Ltd. polyester filament "Tetron" (50 denier 18 filaments) containing 1.5 wt% of carbon which is a solar light absorbing fine particle, and cationic dyeing dye manufactured by Toray Co., Ltd. Using polyester filament "Tetron" (50 denier 36 filament) and Toray DuPont polyurethane elastic yarn "Operon" 20 denier, using a 28 gauge single tricot machine with two reeds, the front reed contains carbon. " The tetron "20% yarn" and the cationic dyeable "tetron" yarn 80% were used, and the "operon" yarn was arranged on the back reed to form a half structure. A knitted fabric dyed in black by the usual dyeing method of "Operon" mixed knitted product was used.
【００２５】中層と裏地は、実施例１と同じものを用い
て３層構造になるようにポリウレタン樹脂を用い貼り合
わせ加工を行った。この布帛の目付は３６２ｇ／ｍ2、
伸長率はタテ４０．８％、ヨコ４８．２％、電磁波の波
長０．７６〜１．３μｍにおける分光反射率の最大値が
３８％、人工気象室で、６００ｋｃａｌ／ｍ2・ｈｒの
日射を２５分間あてた時の生地裏温度が４５．６℃であ
った。この布帛を用いてウェットスーツを作り、５名の
男性により１１月度の海中で着用評価を行ったところ、
動き易く、かつ、水中から上がっての身体冷感が少なく
快適なものであった。The middle layer and the lining were the same as in Example 1 and were laminated using a polyurethane resin so as to form a three-layer structure. The basis weight of this fabric is 362 g / m 2 ,
The elongation rate is 40.8% vertical, 48.2% horizontal, the maximum value of the spectral reflectance at an electromagnetic wave wavelength of 0.76 to 1.3 μm is 38%, and the artificial weather chamber emits 600 kcal / m 2 · hr of sunlight. The back temperature of the dough after 4 minutes was 45.6 ° C. When a wet suit was made using this cloth and evaluated by five men in the sea in November,
It was easy to move, and it was comfortable with little feeling of cold when rising from the water.
【００２６】[0026]
【実施例３】表地には、太陽光吸収系微粒子であるカー
ボンを５．０ｗｔ％含有させた東レ（株）製ポリエステ
ルフィラメント”テトロン”（５０デニール１８フィラ
メント）、東レ（株）製カチオン可染ポリエステルフィ
ラメント”テトロン”（５０デニール３６フィラメン
ト）と東レ・デュポン（株）製ポリウレタン弾性糸”オ
ペロン”２０デニールを使用し、２８ゲージのシングル
トリコット機で２枚筬にて、フロント筬にカーボン含
有”テトロン”糸２０％、カチオン可染”テトロン”糸
８０％とし、バック筬に”オペロン”糸を配してハーフ
組織を編成した。これを”オペロン”交編品の通常染色
法により、黒色に染色した編地を用いた。EXAMPLE 3 Toray Co., Ltd. polyester filament "Tetron" (50 denier 18 filaments) containing 5.0 wt% of carbon which is a solar absorbing fine particle, and cationic dyeing dye manufactured by Toray Co., Ltd. Using polyester filament "Tetron" (50 denier 36 filament) and Toray DuPont polyurethane elastic yarn "Operon" 20 denier, using a 28 gauge single tricot machine with two reeds, the front reed contains carbon. " The tetron "20% yarn" and the cationic dyeable "tetron" yarn 80% were used, and the "operon" yarn was arranged on the back reed to form a half structure. A knitted fabric dyed in black by the usual dyeing method of "Operon" mixed knitted product was used.
【００２７】中層と裏地は、実施例１と同じものを用い
て３層構造になるようにポリウレタン樹脂を用い貼り合
わせ加工を行った。この布帛の目付は４３１ｇ／ｍ2、
伸長率はタテ４０．６％、ヨコ４５．３％、電磁波の波
長０．７６〜１．３μｍにおける分光反射率の最大値が
１８％、人工気象室で、６００ｋｃａｌ／ｍ2・ｈｒの
日射を２５分間あてた時の生地裏温度が４８．４℃であ
った。この布帛を用いてウェットスーツを作り、５名の
男性により１１月度の海中で着用評価を行ったところ、
動き易く、かつ、水中から上がっての身体冷感がほとん
どなく快適なものであった。The middle layer and the lining were the same as in Example 1, and were laminated using a polyurethane resin so as to form a three-layer structure. The basis weight of this fabric is 431 g / m 2 ,
The elongation rate is 40.6% vertical, 45.3% horizontal, the maximum value of the spectral reflectance at an electromagnetic wave wavelength of 0.76 to 1.3 μm is 18%, and in an artificial weather room, the solar radiation of 600 kcal / m 2 · hr The back temperature of the dough after exposure for 25 minutes was 48.4 ° C. When a wet suit was made using this cloth and evaluated by five men in the sea in November,
It was easy to move, and there was almost no cold feeling when rising from the water.
【００２８】[0028]
【実施例４】表地には、太陽光吸収系微粒子であるカー
ボンを２．５ｗｔ％含有させた東レ（株）製ポリエステ
ルフィラメント”テトロン”（５０デニール１８フィラ
メント）、東レ・デュポン（株）製ポリウレタン弾性
糸”オペロン”２０デニールを使用し、２８ゲージのシ
ングルトリコット機で２枚筬にて、フロント筬にカーボ
ン含有”テトロン”糸、バック筬に”オペロン”糸を配
してハーフ組織を編成した。これを”オペロン”交編品
の通常染色法により、黒色に染色した編地を用いた。EXAMPLE 4 Toray Co., Ltd. polyester filament "Tetron" (50 denier 18 filaments) containing 2.5% by weight of carbon which is solar absorption fine particles, and polyurethane manufactured by Toray Dupont Co., Ltd. Using a 20-denier elastic thread "Operon", a half-knit was formed by arranging a carbon-containing "Tetron" thread on the front reed and an "Operon" thread on the back reed using a 28 gauge single tricot machine with two reeds. . A knitted fabric dyed in black by the usual dyeing method of "Operon" mixed knitted product was used.
【００２９】中層と裏地は、実施例１と同じものを用い
て３層構造になるようにポリウレタン樹脂を用い貼り合
わせ加工を行った。この布帛の目付は４６６ｇ／ｍ2、
伸長率はタテ４６．７％、ヨコ５０．５％、電磁波の波
長０．７６〜１．３μｍにおける分光反射率の最大値が
１５％、人工気象室で、６００ｋｃａｌ／ｍ2・ｈｒの
日射を２５分間あてた時の生地裏温度が４９．０℃であ
った。この布帛を用いてウェットスーツを作り、５名の
男性により１１月度の海中で着用評価を行ったところ、
動き易さに非常に優れ、かつ、水中から上がっての身体
冷感もほとんどなく快適なものであった。The middle layer and the lining were the same as in Example 1 and were bonded together using a polyurethane resin so as to form a three-layer structure. The basis weight of this fabric is 466 g / m 2 ,
The elongation rate is 46.7% vertical, 50.5% horizontal, the maximum value of the spectral reflectance at an electromagnetic wave wavelength of 0.76 to 1.3 μm is 15%, and in an artificial weather room, 600 kcal / m 2 · hr of solar radiation The back temperature of the dough when exposed for 25 minutes was 49.0 ° C. When a wet suit was made using this cloth and evaluated by five men in the sea in November,
It was very easy to move, and was comfortable with almost no cold feeling when rising from the water.
【００３０】[0030]
【実施例５】表地には、太陽光吸収系微粒子である炭化
ジルコニウム（ＺｒＣ）を２．５ｗｔ％含有させた東レ
（株）製ポリエステルフィラメント”テトロン”（５０
デニール１８フィラメント）、東レ（株）製カチオン可
染ポリエステルフィラメント”テトロン”（５０デニー
ル３６フィラメント）と東レ・デュポン（株）製ポリウ
レタン弾性糸”オペロン”２０デニールを使用し、２８
ゲージのシングルトリコット機で２枚筬にて、フロント
筬にＺｒＣ含有”テトロン”糸２０％、カチオン可染”
テトロン”糸８０％とし、バック筬に”オペロン”糸を
配してハーフ組織を編成した。これを”オペロン”交編
品の通常染色法により、黒色に染色した編地を用いた。Example 5 A polyester filament "Tetron" (50%) manufactured by Toray Industries, Inc. containing 2.5% by weight of zirconium carbide (ZrC), which is a fine particle of solar absorption system, was placed on the outer surface.
Denier 18 filament), Toray Co., Ltd. cationic dyeable polyester filament "Tetron" (50 denier 36 filament) and Toray Dupont Co., Ltd. polyurethane elastic yarn "Operon" 20 denier are used.
With two reeds using a gauge single tricot machine, ZrC-containing "Tetron" yarn 20%, cationic dyeable on front reed
A half structure was knitted by arranging "Operon" yarns on a back reed with 80% of Tetron "yarns" and using the knitted fabric dyed black by the usual dyeing method of "Operon" mixed knitted articles.
【００３１】中層と裏地は、実施例１と同じものを用い
て３層構造になるようにポリウレタン樹脂を用い貼り合
わせ加工を行った。この布帛の目付は４５０ｇ／ｍ2、
伸長率はタテ４３．４％、ヨコ４７．９％、電磁波の波
長０．７６〜１．３μｍにおける分光反射率の最大値が
２８％、人工気象室で、６００ｋｃａｌ／ｍ2・ｈｒの
日射を２５分間あてた時の生地裏温度が４６．５℃であ
った。この布帛を用いてウェットスーツを作り、５名の
男性により１１月度の海中で着用評価を行ったところ、
動き易く、かつ、水中から上がっての身体冷感が少なく
快適なものであった。The middle layer and the backing were the same as in Example 1, and were laminated using a polyurethane resin so as to form a three-layer structure. The basis weight of this fabric is 450 g / m 2 ,
The elongation rate is 43.4% vertical, 47.9% horizontal, the maximum value of the spectral reflectance at an electromagnetic wave wavelength of 0.76 to 1.3 μm is 28%, and the artificial weather chamber emits 600 kcal / m 2 · hr of sunlight. The back temperature of the dough when exposed for 25 minutes was 46.5 ° C. When a wet suit was made using this cloth and evaluated by five men in the sea in November,
It was easy to move, and it was comfortable with little feeling of cold when rising from the water.
【００３２】[0032]
【実施例６】表地には、太陽光吸収系微粒子である酸化
第二銅（ＣｕＯ）を２．５ｗｔ％含有させた東レ（株）
製ポリエステルフィラメント”テトロン”（５０デニー
ル１８フィラメント）、東レ（株）製カチオン可染ポリ
エステルフィラメント”テトロン”（５０デニール３６
フィラメント）と東レ・デュポン（株）製ポリウレタン
弾性糸”オペロン”２０デニールを使用し、２８ゲージ
のシングルトリコット機で２枚筬にて、フロント筬にＣ
ｕＯ含有”テトロン”糸２０％、カチオン可染”テトロ
ン”糸８０％とし、バック筬に”オペロン”糸を配して
ハーフ組織を編成した。これを”オペロン”交編品の通
常染色法により、黒色に染色した編地を用いた。Embodiment 6 Toray Co., Ltd. containing 2.5 wt% of cupric oxide (CuO), which is a solar light absorbing fine particle, is included in the surface material.
Polyester filament “Tetron” (50 denier 18 filaments), Toray Co., Ltd. cationic dyeable polyester filament “Tetron” (50 denier 36
Filament) and Toray DuPont's polyurethane elastic yarn "Operon" 20 denier, using a 28 gauge single tricot machine with two reeds, C on the front reed
The uO-containing "Tetron" yarn was 20% and the cationic dyeable "Tetron" yarn was 80%, and the "Operon" yarn was arranged on the back reed to form a half structure. A knitted fabric dyed in black by the usual dyeing method of "Operon" mixed knitted product was used.
【００３３】中層と裏地は、実施例１と同じものを用い
て３層構造になるようにポリウレタン樹脂を用い貼り合
わせ加工を行った。この布帛の目付は４６１ｇ／ｍ2、
伸長率はタテ４８．７％、ヨコ５３．３％、電磁波の波
長０．７６〜１．３μｍにおける分光反射率の最大値が
３０％、人工気象室で、６００ｋｃａｌ／ｍ2・ｈｒの
日射を２５分間あてた時の生地裏温度が４６．０℃であ
った。この布帛を用いてウェットスーツを作り、５名の
男性により１１月度の海中で着用評価を行ったところ、
動き易さに非常に優れ、かつ、水中から上がっての身体
冷感が少なく快適なものであった。The middle layer and the backing were the same as in Example 1, and were laminated using a polyurethane resin so as to form a three-layer structure. The basis weight of this fabric is 461 g / m 2 ,
The elongation rate is 48.7% vertical, 53.3% horizontal, the maximum value of the spectral reflectance at a wavelength of 0.76 to 1.3 μm of the electromagnetic wave is 30%, and the solar radiation of 600 kcal / m 2 · hr in the artificial weather room. The backing temperature of the dough when exposed for 25 minutes was 46.0 ° C. When a wet suit was made using this cloth and evaluated by five men in the sea in November,
It was very easy to move, and had little body cold when coming out of the water and was comfortable.
【００３４】[0034]
【実施例７】表地には、太陽光吸収系微粒子であるカー
ボンを２．５ｗｔ％含有させた東レ（株）製ポリエステ
ルフィラメント”テトロン”（５０デニール１８フィラ
メント）、東レ（株）製カチオン可染ポリエステルフィ
ラメント”テトロン”（５０デニール３６フィラメン
ト）と東レ・デュポン（株）製ポリウレタン弾性糸”オ
ペロン”２０デニールを使用し、２８ゲージのシングル
トリコット機で２枚筬にて、フロント筬にカーボン含
有”テトロン”糸５０％、カチオン可染”テトロン”糸
５０％とし、バック筬に”オペロン”糸を配してハーフ
組織を編成した。これを”オペロン”交編品の通常染色
法により、黒色に染色した編地を用いた。Example 7 Polyester filament "Tetron" (50 denier 18 filament) manufactured by Toray Co., Ltd. containing 2.5% by weight of carbon which is solar absorption fine particles, and cationic dyeable dye manufactured by Toray Co., Ltd. Using polyester filament "Tetron" (50 denier 36 filament) and Toray DuPont polyurethane elastic yarn "Operon" 20 denier, using a 28 gauge single tricot machine with two reeds, the front reed contains carbon. " A 50% Tetron yarn and 50% cationic dyeable Tetron yarn were used, and an "Operon" yarn was arranged on the back reed to form a half structure. A knitted fabric dyed in black by the usual dyeing method of "Operon" mixed knitted product was used.
【００３５】中層と裏地は、実施例１と同じものを用い
て３層構造になるようにポリウレタン樹脂を用い貼り合
わせ加工を行った。この布帛の目付は５０７ｇ／ｍ2、
伸長率はタテ４１．２％、ヨコ４９．６％、電磁波の波
長０．７６〜１．３μｍにおける分光反射率の最大値が
１５％、人工気象室で、６００ｋｃａｌ／ｍ2・ｈｒの
日射を２５分間あてた時の生地裏温度が４９．３℃であ
った。この布帛を用いてウェットスーツを作り、５名の
男性により１１月度の海中で着用評価を行ったところ、
動き易く、かつ、水中から上がっての身体冷感がほとん
どなく快適なものであった。The middle layer and the backing were the same as in Example 1, and were laminated using a polyurethane resin so as to form a three-layer structure. The basis weight of this fabric is 507 g / m 2 ,
The elongation rate is 41.2% vertical, 49.6% horizontal, the maximum value of the spectral reflectance at an electromagnetic wave wavelength of 0.76 to 1.3 μm is 15%, and in an artificial weather chamber, the solar radiation of 600 kcal / m 2 · hr The back temperature of the dough when exposed for 25 minutes was 49.3 ° C. When a wet suit was made using this cloth and evaluated by five men in the sea in November,
It was easy to move, and there was almost no cold feeling when rising from the water.
【００３６】[0036]
【実施例８】表地と中層には、実施例１と同じものを用
いた。裏地には、太陽光吸収系微粒子であるカーボンを
２．５ｗｔ％含有させた東レ（株）製ポリエステルフィ
ラメント”テトロン”（５０デニール１８フィラメン
ト）、東レ（株）製カチオン可染ポリエステルフィラメ
ント”テトロン”（５０デニール３６フィラメント）と
東レ・デュポン（株）製ポリウレタン弾性糸”オペロ
ン”２０デニールを使用し、２８ゲージのシングルトリ
コット機で２枚筬にて、フロント筬にカーボン含有”テ
トロン”糸２０％、カチオン可染”テトロン”糸８０％
とし、バック筬に”オペロン”糸を配してタテストライ
プ型の凹凸構造を編成した。これを”オペロン”交編品
の通常染色法により、黒色に染色した編地を用いた。Example 8 The same material as in Example 1 was used for the outer material and the middle layer. The lining has a polyester filament "Tetron" (50 denier 18 filament) manufactured by Toray Co., Ltd. containing 2.5% by weight of carbon, which is solar absorption fine particles, and a cation dyeable polyester filament "Tetron" manufactured by Toray Co., Ltd. (50 denier 36 filament) and Toray Dupont Co., Ltd. polyurethane elastic yarn "Operon" 20 denier, using a 28 gauge single tricot machine with 2 reeds, carbon front containing "Tetron" yarn 20% , 80% of cationic dyeable "Tetron" yarn
Then, "Operon" yarns were arranged on the back reed to form a vertical stripe type uneven structure. A knitted fabric dyed in black by the usual dyeing method of "Operon" mixed knitted product was used.
【００３７】前記３種類の素材を用い３層構造になるよ
うにポリウレタン樹脂を用い貼り合わせ加工を行った。
この布帛の目付は５９４ｇ／ｍ2、伸長率はタテ４０．
１％、ヨコ４３．９％、電磁波の波長０．７６〜１．３
μｍにおける分光反射率の最大値が２３％、人工気象室
で、６００ｋｃａｌ／ｍ2・ｈｒの日射を２５分間あて
た時の生地裏温度が４７．７℃であった。この布帛を用
いてウェットスーツを作り、５名の男性により１１月度
の海中で着用評価を行ったところ、動き易く、かつ、水
中から上がっての身体冷感がほとんどなく快適なもので
あった。A bonding process was performed using the above three types of materials and a polyurethane resin so as to form a three-layer structure.
The fabric has a basis weight of 594 g / m 2 and an elongation of 40.
1%, horizontal 43.9%, electromagnetic wave wavelength 0.76 to 1.3
The maximum value of the spectral reflectance at 23 μm was 23%, and the back temperature of the fabric when exposed to 600 kcal / m 2 · hr of solar radiation for 25 minutes in an artificial weather chamber was 47.7 ° C. A wet suit was made using this cloth, and when five men evaluated wearing it in the sea in November, it was easy to move, and it was comfortable with little feeling of cold when climbing out of the water.
【００３８】[0038]
【実施例９】実施例３で用いた生地を表裏逆使いとして
使用した。この布帛の目付は４３１ｇ／ｍ2、伸長率は
タテ４０．６％、ヨコ４５．３％、電磁波の波長０．７
６〜１．３μｍにおける分光反射率の最大値が３８％、
人工気象室で、６００ｋｃａｌ／ｍ2・ｈｒの日射を２
５分間あてた時の生地裏温度が４５．５℃であった。こ
の布帛を用いてウェットスーツを作り、５名の男性によ
り１１月度の海中で着用評価を行ったところ、動き易
く、かつ、水中から上がっての身体冷感が少なく快適な
ものであった。Example 9 The fabric used in Example 3 was used upside down. The basis weight of this cloth is 431 g / m 2 , the elongation is 40.6% in the vertical direction, 45.3% in the width, and the wavelength of the electromagnetic wave is 0.7.
The maximum value of the spectral reflectance at 6 to 1.3 μm is 38%,
In a climate chamber, the solar radiation of 600kcal / m 2 · hr 2
The back temperature of the dough after 4 minutes was 45.5 ° C. A wet suit was made using this cloth, and when five men evaluated wearing it in the sea in November, it was easy to move, and it was comfortable with little body cold feeling when rising from the water.
【００３９】実施例１ないし９の結果をまとめて表１
（Ａ，Ｂ）に示す。以下に比較例を具体的に説明する。The results of Examples 1 to 9 are summarized in Table 1.
(A, B). Hereinafter, a comparative example will be specifically described.
【００４０】［比較例１］表地と裏地にはウーリーナイ
ロン糸（７０デニール２４フィラメント）を使用し、２
８Ｇのシングル丸編機で天竺組織を編成した。中層には
厚さ１ｍｍのクロロプレンゴムを用いた。前記３種類の
素材を用い、３層構造になるようにポリウレタン樹脂を
用い貼り合わせ加工を行った。この布帛の目付は４７９
ｇ／ｍ2、伸長率はタテ４３．８％ヨコ５３．４％、電
磁波の波長０．７６〜１．３μｍにおける分光反射率の
最大値が４０％、人工気象室で６００ｋｃａｌ／ｍ2・
ｈｒの日射を２５分間あてた時の生地裏温度が４４．５
℃であった。この布帛を用いてウェットスーツを作り、
５名の男性により１１月度の海中での着用評価を行った
ところ、動き易さに優れるものの、水中から上がってか
らの身体冷感を感じる不快なものであった。[Comparative Example 1] A wooly nylon yarn (70 denier, 24 filaments) was used for the outer material and the lining.
The fabric was knitted with an 8G single circular knitting machine. A chloroprene rubber having a thickness of 1 mm was used for the middle layer. Using the above three types of materials, a bonding process was performed using a polyurethane resin so as to form a three-layer structure. The basis weight of this fabric is 479
g / m 2 , elongation rate is 43.8% vertical, 53.4% horizontal, the maximum value of the spectral reflectance at an electromagnetic wave wavelength of 0.76 to 1.3 μm is 40%, and 600 kcal / m 2 ··· in an artificial weather chamber.
The back temperature of the dough after 4 hours of sunshine exposure for 4 minutes is 44.5.
° C. Make a wet suit using this cloth,
When the evaluation of wearing in the sea in November was conducted by five men, it was uncomfortable to feel the coolness of the body after getting out of the water, although it was excellent in ease of movement.
【００４１】［比較例２］表地と裏地には、比較例１と
同じものを用いた。中層には厚さ３ｍｍのクロロプレン
ゴムを用いた。前記３種類の素材を用い、３層構造にな
るようにポリウレタン樹脂を用い貼り合わせ加工を行っ
た。この布帛の目付は９７２ｇ／ｍ2、伸長率はタテ４
４．０％ヨコ４８．５％、電磁波の波長０．７６〜１．
３μｍにおける分光反射率の最大値が４４％、人工気象
室で６００ｋｃａｌ／ｍ2・ｈｒの日射を２５分間あて
た時の生地裏温度が４３．７℃であった。この布帛を用
いてウェットスーツを作り、５名の男性により１１月度
の海中での着用評価を行ったところ、動きにくく、水中
から上がってからの身体冷感を感じる不快なものであっ
た。[Comparative Example 2] The same material as that of Comparative Example 1 was used for the outer material and the lining. Chloroprene rubber having a thickness of 3 mm was used for the middle layer. Using the above three types of materials, a bonding process was performed using a polyurethane resin so as to form a three-layer structure. The basis weight of this fabric is 972 g / m 2 and the elongation is
4.0% horizontal 48.5%, electromagnetic wave wavelength 0.76-1.
The maximum value of the spectral reflectance at 3 μm was 44%, and the back temperature of the fabric when exposed to solar radiation of 600 kcal / m 2 · hr for 25 minutes in an artificial weather chamber was 43.7 ° C. A wet suit was made using this cloth, and when five men evaluated wearing it in the sea in November, it was difficult to move, and it was unpleasant to feel the cold of the body after getting out of the water.
【００４２】［比較例３］表地には太陽光吸収系微粒子
であるカーボンを０．５ｗｔ％含有させた東レ（株）製
ポリエステルフィラメント”テトロン”（５０デニール
１８フィラメント）、東レ（株）製カチオン可染ポリエ
ステルフィラメント”テトロン”（５０デニール３６フ
ィラメント）と東レ・デュポン（株）製ポリウレタン弾
性糸”オペロン”２０デニールを使用し、２８ゲージの
シングルトリコット機で２枚筬にて、フロント筬にカー
ボン含有”テトロン”糸５０％、カチオン可染”テトロ
ン”糸５０％とし、バック筬に”オペロン”糸を配して
ハーフ組織を編成した。これを”オペロン”交編品の通
常染色法により黒色に染色した編地を用いた。中層には
実施例１と同じものを用いた。裏地には実施例８と同じ
ものを用いた。[Comparative Example 3] Polyester filament "Tetron" (50 denier 18 filament) manufactured by Toray Co., Ltd. containing 0.5% by weight of carbon, which is a solar absorbing fine particle, on the outer material, and cation manufactured by Toray Co., Ltd. Using a dyeable polyester filament "Tetron" (50 denier 36 filament) and Toray DuPont polyurethane elastic yarn "Operon" 20 denier, use a 28 gauge single tricot machine with two reeds and carbon on the front reed. The "Tetron" yarn content was 50%, the cationic dyeable "Tetron" yarn was 50%, and the "Operon" yarn was arranged on the back reed to form a half structure. A knitted fabric which was dyed black by an ordinary dyeing method of "Operon" mixed knitted product was used. The same material as in Example 1 was used for the middle layer. The same backing as in Example 8 was used.
【００４３】前記３種類の素材を用い、３層構造になる
ようにポリウレタン樹脂を用い貼り合わせ加工を行っ
た。この布帛の目付は５９９ｇ／ｍ2、伸長率はタテ５
５．８％ヨコ４６．２％、電磁波の波長０．７６〜１．
３μｍにおける分光反射率の最大値が５３％、人工気象
室で６００ｋｃａｌ／ｍ2・ｈｒの日射を２５分間あて
た時の生地裏温度が４１．６℃であった。この布帛を用
いてウェットスーツを作り、５名の男性により１１月度
の海中での着用評価を行ったところ、動き易さに優れる
ものの、水中から上がってからの身体冷感を感じる不快
なものであった。Using the above three types of materials, a bonding process was performed using a polyurethane resin so as to form a three-layer structure. The basis weight of this fabric is 599 g / m 2 and the elongation is
5.8% horizontal 46.2%, electromagnetic wave wavelength 0.76-1.
The maximum value of the spectral reflectance at 3 μm was 53%, and the back temperature of the fabric when exposed to solar radiation of 600 kcal / m 2 · hr for 25 minutes in an artificial weather chamber was 41.6 ° C. A wet suit was made using this fabric, and the evaluation of wearing in the sea in November by five men was performed. there were.
【００４４】［比較例４］表地には太陽光吸収系微粒子
であるカーボンを２．５ｗｔ％含有させた東レ（株）製
ポリエステルフィラメント”テトロン”（５０デニール
１８フィラメント）、東レ（株）製カチオン可染ポリエ
ステルフィラメント”テトロン”（５０デニール３６フ
ィラメント）と東レ・デュポン（株）製ポリウレタン弾
性糸”オペロン”２０デニールを使用し、２８ゲージの
シングルトリコット機で２枚筬にて、フロント筬にカー
ボン含有”テトロン”糸１５％、カチオン可染”テトロ
ン”糸８５％とし、バック筬に”オペロン”糸を配して
ハーフ組織を編成した。中層と裏地には実施例１と同じ
ものを用いた。[Comparative Example 4] Polyester filament "Tetron" (50 denier 18 filaments) manufactured by Toray Co., Ltd. containing 2.5% by weight of carbon, which is a solar absorption fine particle, and cation manufactured by Toray Co., Ltd. Using a dyeable polyester filament "Tetron" (50 denier 36 filament) and Toray DuPont polyurethane elastic yarn "Operon" 20 denier, use a 28 gauge single tricot machine with two reeds and carbon on the front reed. The "Tetron" yarn content was 15%, the cationic dyeable "Tetron" yarn was 85%, and the "Operon" yarn was arranged on the back reed to form a half structure. The same thing as Example 1 was used for the middle layer and the lining.
【００４５】前記３種類の素材を用い、３層構造になる
ようにポリウレタン樹脂を用い貼り合わせ加工を行っ
た。この布帛の目付は４６３ｇ／ｍ2、伸長率はタテ４
２．４％ヨコ４８．３％、電磁波の波長０．７６〜１．
３μｍにおける分光反射率の最大値が４３％、人工気象
室で６００ｋｃａｌ／ｍ2・ｈｒの日射を２５分間あて
た時の生地裏温度が４３．２℃であった。この布帛を用
いてウェットスーツを作り、５名の男性により１１月度
の海中での着用評価を行ったところ、動き易さに優れる
ものの、水中から上がってからの身体冷感を感じる不快
なものであった。Using the above three types of materials, a bonding process was performed using a polyurethane resin so as to form a three-layer structure. The basis weight of this fabric was 463 g / m 2 , and the elongation was
2.4% horizontal 48.3%, electromagnetic wave wavelength 0.76-1.
The maximum value of the spectral reflectance at 3 μm was 43%, and the back temperature of the fabric when exposed to solar radiation of 600 kcal / m 2 · hr for 25 minutes in an artificial weather chamber was 43.2 ° C. A wet suit was made using this fabric, and the evaluation of wearing in the sea in November by five men was performed. there were.
【００４６】［比較例５］表地には太陽光吸収系微粒子
であるカーボンを２．５ｗｔ％含有させた東レ（株）製
ポリエステルフィラメント”テトロン”（５０デニール
１８フィラメント）、東レ（株）製カチオン可染ポリエ
ステルフィラメント”テトロン”（５０デニール３６フ
ィラメント）と東レ・デュポン（株）製ポリウレタン弾
性糸”オペロン”２０デニールを使用し、２８ゲージの
シングルトリコット機で２枚筬にて、フロント筬にカー
ボン含有”テトロン”糸５０％、カチオン可染”テトロ
ン”糸５０％とし、バック筬に”オペロン”糸を配して
ハーフ組織を編成した。中層と裏地には実施例１と同じ
ものを用いた。[Comparative Example 5] Polyester filament "Tetron" (50 denier 18 filament) manufactured by Toray Co., Ltd. containing 2.5% by weight of carbon, which is a solar absorption fine particle, and cation manufactured by Toray Co., Ltd. Using a dyeable polyester filament "Tetron" (50 denier 36 filament) and Toray DuPont polyurethane elastic yarn "Operon" 20 denier, use a 28 gauge single tricot machine with two reeds and carbon on the front reed. The "Tetron" yarn content was 50%, the cationic dyeable "Tetron" yarn was 50%, and the "Operon" yarn was arranged on the back reed to form a half structure. The same thing as Example 1 was used for the middle layer and the lining.
【００４７】前記３種類の素材を用い、３層構造になる
ようにポリウレタン樹脂を用い貼り合わせ加工を行っ
た。この布帛の目付は３４３ｇ／ｍ2、伸長率はタテ５
３．６％ヨコ５５．１％、電磁波の波長０．７６〜１．
３μｍにおける分光反射率の最大値が２０％、人工気象
室で６００ｋｃａｌ／ｍ2・ｈｒの日射を２５分間あて
た時の生地裏温度が４６．３℃であった。この布帛を用
いてウェットスーツを作り、５名の男性により１１月度
の海中での着用評価を行ったところ、動き易さに優れる
ものの、ウエアの生地が薄すぎるために、水中から上が
ってからの身体冷感を感じる不快なものであった。Using the above three types of materials, a bonding process was performed using a polyurethane resin so as to form a three-layer structure. The basis weight of this fabric was 343 g / m 2 and the elongation was
3.6% horizontal 55.1%, electromagnetic wave wavelength 0.76-1.
The maximum value of the spectral reflectance at 3 μm was 20%, and the back temperature of the fabric when exposed to solar radiation of 600 kcal / m 2 · hr for 25 minutes in an artificial weather chamber was 46.3 ° C. A wet suit was made using this fabric, and the evaluation of wearing in the sea in November by five men was performed. She was uncomfortable feeling cold.
【００４８】［比較例６］表地と中層には、実施例６と
同じものを用いた。裏地には、実施例８と同じものを用
いた。前記３種類の素材を用い、３層構造になるように
ポリウレタン樹脂を用い貼り合わせ加工を行った。この
布帛の目付は７０２ｇ／ｍ2、伸長率はタテ４３．６％
ヨコ４７．２％、電磁波の波長０．７６〜１．３μｍに
おける分光反射率の最大値が２１％、人工気象室で６０
０ｋｃａｌ／ｍ2・ｈｒの日射を２５分間あてた時の生
地裏温度が４８．２℃であった。この布帛を用いてウェ
ットスーツを作り、５名の男性により１１月度の海中で
の着用評価を行ったところ、水中から上がってからの身
体冷感はさほど感じないものの、ウエアの生地が重す
ぎ、動きにくいため、不快なものであった。Comparative Example 6 The same material as in Example 6 was used for the outer material and the middle layer. The same lining as in Example 8 was used. Using the above three types of materials, a bonding process was performed using a polyurethane resin so as to form a three-layer structure. The basis weight of this fabric is 702 g / m 2 , and the elongation is 43.6% vertical
Horizontal 47.2%, maximum value of spectral reflectance at electromagnetic wave wavelength 0.76 to 1.3 μm is 21%, 60 in artificial climate chamber
The backside temperature of the dough when exposed to 0 kcal / m 2 · hr for 25 minutes was 48.2 ° C. A wet suit was made using this fabric, and five men evaluated wearing it in the sea in November, but although they did not feel much cold after rising from the water, the fabric of the wear was too heavy, It was uncomfortable because it was hard to move.
【００４９】［比較例７］表地と中層は、比較例６と同
じものを用いた。裏地には、比較例４と同じものを用い
た。前記３種類の素材を用い、３層構造になるようにポ
リウレタン樹脂を用い貼り合わせ加工を行った。この布
帛の目付は５１７ｇ／ｍ2、伸長率はタテ２２．４％ヨ
コ２８．３％、電磁波の波長０．７６〜１．３μｍにお
ける分光反射率の最大値が２０％、人工気象室で６００
ｋｃａｌ／ｍ2・ｈｒの日射を２５分間あてた時の生地
裏温度が４８．０℃であった。この布帛を用いてウェッ
トスーツを作り、５名の男性により１１月度の海中での
着用評価を行ったところ、水中から上がってからの身体
冷感はさほど感じないものの、ウエアの生地の伸長率が
低すぎるために動きにくく、不快なものであった。[Comparative Example 7] The same material as that of Comparative Example 6 was used for the surface material and the middle layer. The same backing as that of Comparative Example 4 was used. Using the above three types of materials, a bonding process was performed using a polyurethane resin so as to form a three-layer structure. The basis weight of this fabric is 517 g / m 2 , the elongation is 22.4% vertical, 28.3% horizontal, the maximum value of the spectral reflectance at an electromagnetic wave wavelength of 0.76 to 1.3 μm is 20%, and 600% in an artificial weather chamber.
The backside temperature of the dough when exposed to kcal / m 2 · hr for 25 minutes was 48.0 ° C. Using this fabric, a wet suit was made, and the evaluation of wearing in the sea in November by five men showed that although the body did not feel much cold after coming out of the water, the elongation rate of the clothing fabric was low. It was uncomfortable because it was too low to move.
【００５０】比較例１ないし比較例７の結果をまとめて
表２（Ｃ，Ｄ）に示す。表１、表２から明らかなごと
く、本発明品は、従来のクロロプレンゴム使用品よりも
軽量であり、身体とのフィット感に優れる。また、保温
性に関する評価項目のほとんどで本発明が従来品より優
れているのも明らかである。The results of Comparative Examples 1 to 7 are summarized in Table 2 (C, D). As is clear from Tables 1 and 2, the product of the present invention is lighter than the conventional product using chloroprene rubber, and is excellent in the fit to the body. It is also clear that the present invention is superior to the conventional product in most of the evaluation items relating to the heat retention.
【００５１】[0051]
【発明の効果】本発明は、水着やウェットスーツ、ドラ
イスーツなどに使用する場合、従来品並のストレッチ性
を保持したまま、生地目付厚さが従来品より小さい。こ
れは従来品より軽量かつ身体とのフィット感に優れてい
ると言える。しかも、泳いだ後の速乾性、保温性という
着用快適感をも従来品をしのいでいる。本発明ではこれ
らの優れた特徴を有する布帛を提供することができる。According to the present invention, when used in swimwear, wet suits, dry suits, etc., the basis weight of the fabric is smaller than that of the conventional product while maintaining the stretchability of the conventional product. It can be said that this is lighter and has a better fit with the body than conventional products. Moreover, it also outperforms conventional products in the feeling of wearing comfort such as quick drying and warmth after swimming. According to the present invention, a fabric having these excellent characteristics can be provided.
【００５２】[0052]
【表１】ーＡー [Table 1] -A-
【００５３】ーＢー 注：（１）表面基布編組織のＴＨ：トリコットハーフ （２）貼り合わせ加工のＡ ：太陽光吸収繊維交編地 （３） ” Ｂ ：ポリウレタンフィルム （４） ” Ｃ ：通常ハーフ組織 （５） ” Ｄ ：太陽光吸収繊維交編凹凸構造-B- Note: (1) TH of the surface base fabric knitting structure: tricot half (2) A of the bonding process: sun-absorbing fiber cross knitted fabric (3) "B: polyurethane film (4)" C: normal half structure (5 ) ”D: Sunlight absorbing fiber interwoven knitted uneven structure
【００５４】[0054]
【表２】ーＣー [Table 2] -C-
【００５５】ーＤー 注：（１）表面基布編組織のＴＨ：トリコットハーフ （２）貼り合わせ加工のＡ ：太陽光吸収繊維交編地 （３） ” Ｂ ：ポリウレタンフィルム （４） ” Ｃ ：通常ハーフ組織 （５） ” Ｄ ：太陽光吸収繊維交編凹凸構造 （６） ” Ｅ ：ウーリーナイロン天竺編地 （７） ” Ｆ ：クロロプレンゴム（厚さ１ｍｍ） （８） ” Ｇ ：クロロプレンゴム（厚さ３ｍｍ） （９） ” Ｊ ：トリコット凹凸構造編地-D- Note: (1) TH of the surface base fabric knitting structure: tricot half (2) A of the bonding process: sun-absorbing fiber cross knitted fabric (3) "B: polyurethane film (4)" C: normal half structure (5 ) "D: Sunlight absorbing fiber interwoven knitted uneven structure (6)""E: Woolly nylon knitted fabric (7)""F: Chloroprene rubber (thickness 1mm) (8)" G: Chloroprene rubber (thickness 3mm) ( 9) "J: Tricot uneven structure knitted fabric
───────────────────────────────────────────────────── フロントページの続き (58)調査した分野(Int.Cl.7，ＤＢ名) B63C 11/04 A41D 31/00 - 31/02 A41D 13/00 B32B 1/00 - 35/00 ──────────────────────────────────────────────────続 き Continued on the front page (58) Fields surveyed (Int. Cl. 7 , DB name) B63C 11/04 A41D 31/00-31/02 A41D 13/00 B32B 1/00-35/00
Claims (2)
両面に編地を貼り合わせてなる積層布帛であって、少な
くとも片面の編地が太陽光吸収性微粒子を１．５〜５．
０重量％含有する合成繊維マルチフィラメント糸条を２
０〜１００％含む編地であり、波長０．７６〜１．３μ
ｍの電磁波の分光反射率の最大値が４０％以下、目付が
３６０〜６００ｇ／ｍ2、伸長率がタテ、ヨコ共４０％
以上であることを特徴とするウェットスーツ用布帛。1. A laminated fabric comprising a transparent stretch film forming an intermediate layer and a knitted fabric attached to both sides, wherein at least one side of the knitted fabric contains 1.5 to 5.
2% synthetic fiber multifilament yarn containing 0% by weight
It is a knitted fabric containing 0 to 100% and has a wavelength of 0.76 to 1.3 μm.
m, the maximum value of the spectral reflectance of the electromagnetic wave is 40% or less, the basis weight is 360 to 600 g / m 2 , and the elongation is 40% for both vertical and horizontal.
A wet suit fabric characterized by the above.
（Ｃ）、チタン（Ｔｉ）、ジルコニウム（Ｚｒ）、ハフ
ニウム（Ｈｆ）、タンタル（Ｔａ）、シリコン（Ｓ
ｉ）、ホウ素（Ｂ）、などの金属の炭化物、ジルコニウ
ム（Ｚｒ）、シリコン（Ｓｉ）、クロム（Ｃｒ）、鉄
（Ｆｅ）、銅（Ｃｕ）、などの金属の酸化物、アントラ
キノン化合物などの染料の中から選ばれたものであり、
粒径が５μｍ以下であることを特徴とする請求項１記載
のウェットスーツ用布帛。2. The solar light absorbing fine particles include carbon powder (C), titanium (Ti), zirconium (Zr), hafnium (Hf), tantalum (Ta), and silicon (S).
i), oxides of metals such as boron (B), metal carbides such as zirconium (Zr), silicon (Si), chromium (Cr), iron (Fe), copper (Cu), and anthraquinone compounds Selected from dyes,
The wet suit fabric according to claim 1, wherein the particle size is 5 µm or less.