1288190 九、發明說明: 【發明所屬之技術領域】 本發明係關於一種含有石墨級碳愛平砂踏 反"、、聚酗纖維紗線編織 而成的石墨級碳黑聚醋纖維保溫織物,尤其是指一種庫用 於潛水衣、衝浪衣、外套、睡袋、棉被或護具之保溫織物, 可以有效保持穿著或使用者之體溫,本創作並且具有質 輕、抑菌、抗靜電之特點,屬於潛水衣、衝浪衣以及護且 之素材創新與功能提升之範疇。 〃1288190 IX. Description of the invention: [Technical field of the invention] The present invention relates to a graphite grade carbon black polyacetate insulation fabric which is woven from a graphite grade carbon Aiping sand tread ", and polyanthene fiber yarn, especially It refers to a kind of insulation fabric used for wetsuits, surf clothes, jackets, sleeping bags, quilts or protective gears. It can effectively maintain the body temperature of the wearer or user. This creation is characterized by light weight, antibacterial and antistatic. It belongs to the category of innovation and function enhancement of wetsuits, surf clothes and care. 〃
【先前技術】 潛水衣、衝浪衣等水上/水下運動服裝,長久以來因 呆溫性不良,使穿著者之活動時間受限,尤其是冬季氣、田 低時,’更會因體溫流失速度快而無法進行長時間之水'上〇 水下運動或作業,使得工作或運動因此而停止,更無法 興而歸。 & 在於運動、醫療或保健上使用之護具若能具有良好的 =功能’可以促進使用者之▲液循環,不僅使護具之功 月包提升’更可擴大其應用領域。 因此,尋找有效的保溫素材一直是潛水衣、衝浪衣、 外套、睡袋、棉被及護具製作領域之技術人M的主要課題, 傳、先方法是以厚重之毛巾布或磨毛/刷毛布做為潛水衣、 衡浪衣、護具之保溫㈣,不但保溫效果不佳、且織物厚 重丄増加穿著者之負擔、影響人體活動,肖人造橡膠海緯 貼合之布片不透氣,穿著時悶濕,容易滋生細菌。 1288190 【發明内容】 本發明提供一種新的石墨級碳黑聚酯纖維保溫織物, 可有效保持潛水衣、衝浪衣穿著者之體溫,延長其於水上 火下運動或作業時間,應用於睡袋、棉被或護具上,可 促進護具使用者之血液循環,並具有質輕、抑菌、抗靜電 之特性。 ' 本發明係利用石墨級碳黑聚酯纖維紗線與其他紗線編 織而成,其中石墨級碳黑聚酯纖維紗線需佔3〇%以上之比 例,經特殊染整加工製程處理,獲得具有保溫、質輕、抑 菌、、抗靜電之織物,可與人造橡膠海綿貼合,作為潛水衣、 衝浪衣、護具、睡袋或棉被之保溫素材,不僅質輕、穿著 舒適、而且保溫效能佳、可促進人體血液循環、具有抑菌、 抗靜電之功效。 【貫施方式】 本發明之石墨級碳黑聚酯纖維保溫織物,係指使用石 墨級碳黑聚自旨纖維紗線之比例佔以上所編織而成的織 物,經染整加工處理,具有保溫、抑菌、抗靜電之功能、, 可與橡膠海綿貼合’做為潛水衣、衝浪衣、外套、睡袋、 棉被及”蔓具之素材’與傳統保溫織物相較,有更優異之保 ’皿效果僅具有功能提升之進步性,更具有產業利用性。 v製%中之石墨級碳黑聚酯纖維紗線係指纖維中含 有石墨碳黑微粒之短纖或長絲紡製㈣之紗線。 上述製程中之編織可因組織設計之不同而產生各種類 型織物,如單面織物、雙面織物、羅紋織物、格子織物及 其他變化組織之織物。 上述製程中之执 用,包含精練、磨毛' 理加工處理為多項工程之組合應 第—至三圖說明,复:刷毛、後整理加工之任意組合,如 刷毛可職予織^精練具有清潔織物之作用,磨毛或 性,後整理加工且古a之表面’增加穿著舒適度與保溫 經上述與尺寸安定之功效。 到45〇…之間n/ 織物之碼重設定15〇〜 以75丹尸宽设定於45 inch到64 inch之間。 編織而成之輩I石墨級碳黑聚酯纖維紗線、4〇丹尼彈性紗 理加工處理,荠二織:,經磨毛工程、精練工程以及後整 針織布。1#寬56⑽、碼重mg/y之單面磨毛 以 7 5 ^ τι μ ^ 1、、及碳黑聚酯纖維紗線、75丹尼ΡΤΤ紗 理:而成之格子針織布,經磨毛工程、精練工程以及後整 處理,獲得幅寬54 inch、碼重225g/y之磨毛格子 針織布。 本發明以上兩項布種與傳統採用之保溫織物之性能比 ^表_所示’其中本發明保溫織物之表面溫差高達饥 與14 c ’顯示具有優異之保溫功效。 1288190 表一性能比較表 項目 羊毛 織物 耐隆 毛巾 織物 本發明 保溫織物 (單面磨毛 針織布) 本發明 保溫織物 (磨毛格子 針織布) 測試方法 保溫性 (表面溫度 差) 5°C 2°C 14°C 13°C 500W鹵素燈 照射10分鐘 抑菌率(%) <1% <1% 95% 95% AATCC 100-1998 摩擦帶 電壓 (V) 棉 — 2381 588 697 JIS L1094-1996 Method B 羊毛 — 2637 266 163 織物表面電阻 (Ω) ΙΟ10 1011 108 108 直接量測 綜上所述,本發明之保溫性優於傳統採用之保溫織 物,同時具有抑菌、抗靜電之功效,在產品應用功能上具 有創新進步性,在生產製造技術上具有產業利用價值,符 合專利法之規定。 【圖式簡單說明】 第一圖:係本發明之製造流程之一; 第二圖:係本發明之製造流程之二;以及 第三圖:係本發明之製造流程之三。 【主要元件符號說明】[Prior Art] Water/underwater sportswear such as wetsuits and surf suits have long been limited by the temperature of the wearer, especially when the weather is low in winter and low in the field. It is too fast to carry out long-term water's underwater movements or homework, so that work or exercise is stopped, and it is even more difficult to return. & If the protective gear used in sports, medical care or health care can have a good = function, it can promote the user's ▲ liquid circulation, which not only enhances the safety of the protective gear, but also expands its application area. Therefore, finding effective insulation materials has always been the main subject of technicians in the fields of wetsuits, surf clothes, coats, sleeping bags, quilts and protective gears. The first method is to use thick terry cloth or sanding/brushing cloth. As the insulation of wetsuits, Henglang clothes and protective gears (4), not only the insulation effect is not good, but also the fabric is thick and heavy, and the burden of the wearer is affected, which affects the human body activities. The fabric of the shawl of the artificial rubber is suitable for airtightness. It is stuffy and easy to breed bacteria. 1288190 SUMMARY OF THE INVENTION The present invention provides a new graphite grade carbon black polyester fiber insulation fabric, which can effectively maintain the body temperature of a wetsuit and a surf wearer, and prolong its movement or working time under water fire, and is applied to sleeping bags and cotton. The quilt or the protective device can promote the blood circulation of the user of the protective device, and has the characteristics of light weight, antibacterial and antistatic. The invention utilizes graphite grade carbon black polyester fiber yarn and other yarns to be woven, wherein the graphite grade carbon black polyester fiber yarn accounts for more than 3% of the proportion, and is processed by a special dyeing and finishing process to obtain It has thermal insulation, light weight, antibacterial and antistatic fabric. It can be laminated with synthetic rubber sponge. It can be used as a heat preservation material for wetsuit, surf clothing, protective gear, sleeping bag or quilt. It is not only light, comfortable, but also warm. Good performance, can promote blood circulation, antibacterial and antistatic effects. [Comprehensive application method] The graphite-grade carbon black polyester fiber thermal insulation fabric of the present invention refers to a fabric which is woven by using the proportion of the graphite-grade carbon black poly-spinning fiber yarn, which is dyed and finished, and has heat preservation. , antibacterial, anti-static function, can be combined with rubber sponge 'as a wetsuit, surf clothing, jacket, sleeping bag, quilt and "vine material" compared with traditional insulation fabric, there is better protection 'The effect of the dish is only the improvement of the function and the industrial utilization. The graphite grade carbon black polyester fiber yarn in the % system refers to the staple fiber or filament spinning containing the graphite carbon black particles in the fiber (4) Yarns. The weaving in the above process can produce various types of fabrics due to different tissue design, such as single-faced fabrics, double-faced fabrics, ribbed fabrics, tartan fabrics and other fabrics with varying textures. The application in the above process includes refining. , sanding 'processing and processing as a combination of a number of projects should be the first - to three figures to illustrate, complex: any combination of bristles, finishing, such as bristles can be woven to refine the role of cleaning fabrics, Hair or sex, finishing and processing and the surface of ancient a 'increased wearing comfort and heat preservation through the above and dimensional stability. Between 45 〇... between n / fabric weight setting 15 〇 ~ set at 75 dan Between 45 inch and 64 inch. Weaved generation I graphite grade carbon black polyester yarn, 4 inch Danny elastic yarn processing, 荠二织:, sanding engineering, refining engineering and finishing knitting Cloth. 1# width 56 (10), code weight mg / y single-side sanding with 7 5 ^ τι ^ ^ 1, and carbon black polyester fiber yarn, 75 denier yarn: a plaid knitted fabric, Grinding engineering, refining engineering and post-finishing treatment, obtaining a woven woven fabric with a width of 54 inches and a weight of 225g/y. The performance ratio of the above two kinds of fabrics and the traditionally used thermal insulation fabrics are shown in Table _ 'Where the surface temperature difference of the insulation fabric of the invention is as high as hunger and 14 c' shows excellent heat preservation effect. 1288190 Table 1 performance comparison table item wool fabric thorn towel fabric The invention insulation fabric (single-faced sanding knitted fabric) Fabric (grinding woven fabric) Test method Insulation (surface temperature difference) 5 °C 2 °C 14 °C 13 °C 500W halogen lamp irradiation for 10 minutes inhibition rate (%) <1% <1% 95% 95% AATCC 100-1998 Friction With voltage (V) cotton — 2381 588 697 JIS L1094-1996 Method B Wool — 2637 266 163 Fabric surface resistance (Ω) ΙΟ10 1011 108 108 Direct measurement As described above, the insulation of the present invention is superior to the conventional insulation. The fabric has the effects of antibacterial and antistatic, and has innovative and progressive functions in product application. It has industrial utilization value in manufacturing technology and conforms to the provisions of the Patent Law. BRIEF DESCRIPTION OF THE DRAWINGS The first drawing is one of the manufacturing processes of the present invention; the second drawing is the second manufacturing process of the present invention; and the third drawing is the third manufacturing process of the present invention. [Main component symbol description]