JP3053431B2 - Packaging material, manufacturing method and processing method - Google Patents
Packaging material, manufacturing method and processing methodInfo
- Publication number
- JP3053431B2 JP3053431B2 JP5501423A JP50142393A JP3053431B2 JP 3053431 B2 JP3053431 B2 JP 3053431B2 JP 5501423 A JP5501423 A JP 5501423A JP 50142393 A JP50142393 A JP 50142393A JP 3053431 B2 JP3053431 B2 JP 3053431B2
- Authority
- JP
- Japan
- Prior art keywords
- packaging material
- polymer
- water
- paper
- packaging
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【発明の詳細な説明】 技術分野 本発明は、古紙などの被包装物を包装する包装材、お
よびその製造方法、および処理方法に関するものであ
る。Description: TECHNICAL FIELD The present invention relates to a packaging material for packaging an article to be packaged, such as waste paper, and a method for producing and processing the same.
更に詳しくは、温水に溶解し得る高分子および／又は
その組成物などから成る包装材、およびその製造方法、
および該高分子が溶解する条件の水に包装物を接触させ
て該包装材を溶解せしめて解装して被包装物を回収する
処理方法に関するものである。More specifically, a packaging material comprising a polymer soluble in warm water and / or a composition thereof, and a method for producing the same,
The present invention also relates to a method for dissolving the packaging material, disassembling the packaging material, and recovering the packaged object by bringing the packaging material into contact with water in a condition in which the polymer is dissolved.
背景技術 従来、被包装物を包装する包装材に使用する高分子と
してのポリオレフィン、ポリエステル、ポリカーボネー
ト、ポリ塩化ビニル、ポリスチレン、ABSなどのプラス
チックスは物理的および化学的に優れた特性を有し、入
手も容易であるので広く大量に使用されているが、これ
らのプラスチックスは安定であるので、天然に放置され
てもなかなか劣化せずに留まり、自然を汚染したり破壊
したりする原因ともなり、又焼却すると高燃焼エネルギ
ーを有するので焼却炉を傷めたり、有害ガスが発生した
りするという問題がある。BACKGROUND ART Conventionally, plastics such as polyolefin, polyester, polycarbonate, polyvinyl chloride, polystyrene, and ABS, which are used as a packaging material for packaging an object to be packaged, have excellent physical and chemical properties, These plastics are widely used in large quantities because they are easily available.However, since these plastics are stable, they do not easily deteriorate even when left in nature, causing pollution and destruction of nature. In addition, when incinerated, it has a high combustion energy, so that there is a problem that the incinerator is damaged or harmful gas is generated.
一方、例えば、事業所、オフィス、各家庭等の様々な
発生源から回収される古紙などの被包装物は、省資源、
環境保全の立場から多量に回収され、再利用されている
が、その輸送のための包装法、包装材も、ビニール等、
針金、高分子製バンド、フィルム、ロープ等、形状、材
質ともに様々な形態をとっており、古紙を回収するため
には、これらの包装材はパルプ化される前に、人手によ
って除去されている。On the other hand, for example, packaged items such as waste paper collected from various sources such as offices, offices, and homes are resource-saving,
Large amounts are collected and reused from the standpoint of environmental protection.
Wires, polymer bands, films, ropes, etc. are in various shapes and materials, and in order to recover used paper, these packaging materials are manually removed before pulping. .
こような包装材は、包装材として機械的強度などの特
性に優れており、貯蔵や輸送途中の雨や水分、湿気等で
包装がほどけない、中性から弱酸性の水性媒体に安定な
材質を使用している。Such packaging materials have excellent mechanical strength and other properties as packaging materials, and cannot be unpacked due to rain, moisture, moisture, etc. during storage or transportation, and are stable in neutral to weakly acidic aqueous media. You are using
しかしながら、包装物として回収された古紙は水中で
パルプ化される際、包装材は異物となるためパルパーへ
の投入前に包装材を人手により除去する作業が必要とな
り、非常に多くの手間を必要とする。However, when waste paper recovered as a package is pulped in water, the packaging material becomes foreign matter, so it is necessary to manually remove the packaging material before putting it into the pulper, which requires a great deal of labor. And
また、包装材質が様々であるため、それらを解装する
道具も、ナイフ、カッター、ペンチ、はさみ等、その材
質に適したものを用意し、選択しながら処理作業すると
いうような、非常に煩雑なものである。また大きな包装
物ほど労力が必要である。In addition, since the packaging materials are various, tools for disassembling them are also very complicated, such as preparing knife, cutter, pliers, scissors, etc. suitable for the material and selecting and processing. It is something. Also, larger packages require more labor.
また、包装材ごとに包装物をパルパーに投入し、後段
のスクリーン、クリーナー等で包装材を除去することが
できるが、工程が煩雑となるため結局は異物を除去する
手間がかかるという問題がある。In addition, the packaging material can be put into a pulper for each packaging material, and the packaging material can be removed with a screen, a cleaner, or the like at a later stage. However, since the process is complicated, there is a problem that it takes time and effort to remove foreign substances. .
これらの問題に鑑み、クラフト紙表面上にパラフィン
ワックスとマレイン化石油樹脂を主体とした組成の水性
エマルジョンを常法により塗布する防湿包装用紙の製造
法（特開昭50−36711号公報）、主鎖構造を構成するブ
タジエン単位の50％以上が、1,2−結合を有する特殊な
ホモポリマー又はコポリマーを使用する方法（特公昭44
−24719号公報）、ワックス系エマルジョンを、高分子
熱硬化剤あるいは紙用湿潤強力剤、サイズ剤、硫酸バン
ドなどとパルプ中に添加して定着せしめた後、抄紙して
耐水性紙を製造する方法、合成ゴム系ラテックスとワッ
クス系エマルジョンを混合して塗工液として用いる方法
（特公昭55−22597号公報）などが提案されているが、
防湿性、防水性および故紙回収の容易さなどの点で、必
ずしも充分満足すべき効果が得られない。In view of these problems, a method for producing a moisture-proof packaging paper in which an aqueous emulsion having a composition mainly composed of paraffin wax and maleated petroleum resin is applied on the surface of kraft paper by a conventional method (Japanese Patent Application Laid-Open No. 50-36711). A method using a special homopolymer or copolymer in which 50% or more of the butadiene units constituting the chain structure have 1,2-bonds (Japanese Patent Publication No. Sho 44)
JP-A-24719), a wax-based emulsion is added to a pulp with a polymer thermosetting agent or a paper wetting agent, a sizing agent, a sulfuric acid band, and the like, fixed, and then made into paper to produce water-resistant paper. A method has been proposed in which a synthetic rubber-based latex and a wax-based emulsion are mixed and used as a coating liquid (Japanese Patent Publication No. 55-22597).
A sufficiently satisfactory effect cannot always be obtained in terms of moisture-proof property, waterproof property, and ease of collecting waste paper.
発明の開示 本発明の目的は、天然に放置されると微生物などによ
り分解され易いので自然を汚染したり破壊したりするこ
とがなく、又焼却しても高燃焼エネルギーや有害ガスが
発生せず、雨等の中性から弱酸性の水に対しては安定で
あり、強度、バリアー性、透明性、ヒートシール性、透
湿性、印刷性などの特性も充分に持つ上に、温水に溶解
し得るような高分子などから成る包装材を提供するこ
と、およびそのような包装材の製造方法を提供するこ
と、および包装物の包装をとく際の人手、手間のかから
ない処理方法を提供することである。DISCLOSURE OF THE INVENTION An object of the present invention is to prevent decomposition or destruction of nature because it is easily decomposed by microorganisms when left in nature, and does not generate high combustion energy or harmful gas even when incinerated. It is stable against neutral to weakly acidic water such as rain, has sufficient properties such as strength, barrier properties, transparency, heat sealability, moisture permeability, printability, and dissolves in warm water. By providing a packaging material made of a polymer or the like to be obtained, and by providing a method of manufacturing such a packaging material, and by providing a manual and labor-saving treatment method for unpacking a package. is there.
本発明者らは、鋭意検討の結果、古紙などの被包装物
の包装材としては、温水に溶解し得る高分子および／又
はその組成物などから成る包装材を使用すること、およ
びそのような高分子などから膜状物を作り包装材とした
り、そのような高分子などの水溶液を用いて原紙と積層
したものを包装材とする製造方法を提供すること、およ
びこの包装材を用いて被包装物を包装した包装物を解装
する時に、温水と接触させて包装材を溶解させるという
簡単な操作で処理できることにより上記諸問題を解決で
きることを見出し、本発明を成すに至った。The present inventors have conducted intensive studies and found that as a packaging material for articles to be packaged such as waste paper, a packaging material made of a polymer and / or a composition thereof soluble in hot water, and the like. To provide a production method in which a film is formed from a polymer or the like and used as a packaging material, or a material obtained by laminating a base paper using an aqueous solution of such a polymer or the like as a packaging material is provided. The present inventors have found that the above problems can be solved by a simple operation of dissolving the packaging material by bringing it into contact with hot water when unpacking the package in which the package is disassembled, and have accomplished the present invention.
本発明の請求項１は、40℃未満の水に対して不溶であ
るが、40℃以上の予め定められた温度に昇温することに
より、水に溶解する高分子を含む組成物から成る包装材
であって、該高分子が硼酸、硼砂、アゾ染料、レゾルシ
ノール、カテコール、フロログリシノール、サリシルア
ニリド、ガリックアシッド、ジヒドロキシ安息香酸、グ
リオキザールから選ばれる少なくとも１種を含むことを
特徴とする包装材である。Claim 1 of the present invention relates to a package comprising a composition containing a polymer which is insoluble in water below 40 ° C, but is soluble in water by raising the temperature to a predetermined temperature of 40 ° C or higher. A packaging material, wherein the polymer contains at least one selected from boric acid, borax, azo dye, resorcinol, catechol, phloroglicinol, salicylanilide, gallic acid, dihydroxybenzoic acid, and glyoxal. is there.
本発明の請求項２は、該高分子が変性ポリビニルアル
コールであることを特徴とする請求項１記載の包装材で
ある。A second aspect of the present invention is the packaging material according to the first aspect, wherein the polymer is a modified polyvinyl alcohol.
本発明の請求項３は、補強材として水溶性樹脂及び／
又は植物繊維を使用した該高分子組成物から成ることを
特徴とする請求項１あるいは請求項２記載の包装材であ
る。Claim 3 of the present invention provides a water-soluble resin and / or
The packaging material according to claim 1 or 2, wherein the packaging material is composed of the polymer composition using plant fiber.
本発明の請求項４は、請求項１記載の包装材が少なく
とも１層の原紙と積層されていることを特徴とする包装
材である。A fourth aspect of the present invention is a packaging material characterized in that the packaging material according to the first aspect is laminated with at least one layer of base paper.
本発明の請求項５は、請求項１に記載する高分子を含
む組成物から膜状物を作ることを特徴とする包装材の製
造方法である。A fifth aspect of the present invention is a method for producing a packaging material, comprising forming a film from the composition containing the polymer described in the first aspect.
本発明の請求項６は、請求項１に記載する高分子を含
む組成物を溶解した水溶液を、常法により原紙表面上に
塗布し、乾燥することを特徴とする包装材の製造方法で
ある。A sixth aspect of the present invention is a method for producing a packaging material, which comprises applying an aqueous solution in which the composition containing the polymer described in the first aspect is dissolved on the surface of a base paper by a conventional method, followed by drying. .
本発明の請求項７は、請求項１に記載する高分子を含
む組成物を溶解した水溶液を接着層として２枚以上の原
紙を積層した後、乾燥することを特徴とする包装材の製
造方法である。According to a seventh aspect of the present invention, there is provided a method for producing a packaging material, comprising laminating two or more base papers using an aqueous solution in which the composition containing the polymer according to the first aspect is dissolved as an adhesive layer, and drying. It is.
本発明の請求項８は、請求項１に記載の包装材あるい
は請求項４に記載の包装材の該高分子を含む組成物の面
に接着剤により原紙を積層することを特徴とする包装材
の製造方法である。According to an eighth aspect of the present invention, there is provided a packaging material characterized by laminating a base paper with an adhesive on a surface of a composition containing the polymer of the packaging material according to the first aspect or the packaging material according to the fourth aspect. It is a manufacturing method of.
本発明の請求項９は、該高分子が変性ポリビニルアル
コールであることを特徴とする請求項５から請求項８記
載のいずれかに記載の包装材の製造方法である。A ninth aspect of the present invention is the method for producing a packaging material according to any one of the fifth to eighth aspects, wherein the polymer is a modified polyvinyl alcohol.
本発明の請求項10は、請求項１あるいは請求項４に記
載する包装材により被包装物を包装した包装物を、該高
分子を溶解する条件の水と接触させることを特徴とする
処理方法である。According to a tenth aspect of the present invention, there is provided a processing method comprising contacting a package in which an object to be packaged is wrapped with the wrapping material according to the first or fourth aspect with water in a condition for dissolving the polymer. It is.
本発明の請求項11は、被包装物が古紙原料であること
を特徴とする請求項10記載の処理方法である。An eleventh aspect of the present invention is the processing method according to the tenth aspect, wherein the article to be packaged is a raw material for used paper.
本発明の請求項12は、請求項１あるいは請求項４に記
載する包装材が紐、帯、ロープ、バンド、テープから選
ばれる結束材であり、それにより被包装物を結束した包
装物を、該高分子を溶解する条件の水と接触させること
を特徴とする請求項10に記載の処理方法である。A twelfth aspect of the present invention is the packaging material according to the first or fourth aspect, wherein the packaging material is a binding material selected from a string, a band, a rope, a band, and a tape. 11. The treatment method according to claim 10, wherein the polymer is brought into contact with water under conditions for dissolving the polymer.
本発明において使用される、予め定められた温度未満
の水に対して不溶であるが、該温度以上に昇温すること
により、水に溶解する高分子としては、変性ポリビニル
アルコール、ポリビニルアルコール系、縮合系などの合
成樹脂、セルロース系などの天然高分子などであり、次
のようなものを挙げることができるが、これらに限定さ
れるものではない。The polymer used in the present invention is insoluble in water below a predetermined temperature, but as a polymer dissolved in water by raising the temperature to or above the temperature, modified polyvinyl alcohol, polyvinyl alcohol, It is a synthetic resin such as a condensation resin or a natural polymer such as a cellulosic resin. Examples thereof include, but are not limited to, the following.
（１）ポリ酢酸ビニルの加水分解物等の合成樹脂。(1) Synthetic resin such as hydrolyzate of polyvinyl acetate.
（２）ポリ酢酸ビニルの加水分解物等とグリセロールな
どとの混合物。(2) A mixture of a hydrolyzate of polyvinyl acetate and the like with glycerol and the like.
例えば、ポリ酢酸ビニルの加水分解物（ケン化度20〜
99.9モル％、好ましくは80〜90％、重合度1000〜3000、
好ましくは1500〜2500、温度15〜120℃、好ましくは20
〜85℃程度の水に溶解するもの）50〜95モル％とグリセ
ロール５〜50モル％を常温で混合したものを挙げること
ができる。For example, a hydrolyzate of polyvinyl acetate (a saponification degree of 20 to
99.9 mol%, preferably 80-90%, degree of polymerization 1000-3000,
Preferably 1500-2500, temperature 15-120 ° C, preferably 20
(Dissolved in water at about 85 ° C) 50 to 95 mol% and glycerol 5 to 50 mol% mixed at room temperature.
（３）カルボキシル基やアミノ基を含有するモノマーと
酢酸ビニルとの共重合物を加水分解した合成樹脂。(3) A synthetic resin obtained by hydrolyzing a copolymer of a monomer containing a carboxyl group or an amino group and vinyl acetate.
（４）ポリ酢酸ビニルの加水分解物等にポリビニルアル
コールをグラフト重合した共重合体。(4) A copolymer obtained by graft-polymerizing polyvinyl alcohol on a hydrolyzate of polyvinyl acetate or the like.
例えば、過酸化物触媒を用いて、50〜200℃の温度で
ポリ酢酸ビニルの加水分解物等にポリビニルアルコール
をグラフト重合することができる。For example, polyvinyl alcohol can be graft-polymerized to a hydrolyzate of polyvinyl acetate or the like at a temperature of 50 to 200 ° C. using a peroxide catalyst.
（５）カルボキシル基やアミノ基等の弱酸・弱塩基性基
を含むポリエチレンテレフタレートのような縮合型の合
成樹脂。(5) Condensation type synthetic resins such as polyethylene terephthalate containing a weak acid or weak basic group such as a carboxyl group or an amino group.
（６）アクリル系合成樹脂など。(6) Acrylic synthetic resin and the like.
（７）メチルセルロース、ヒドロキシエチルセルロー
ス、ヒドロキシプロピルメチルセルロース、カルボキシ
メチルセルロースなどを耐水化剤あるいは熱処理したセ
ルロース系天然高分子。(7) Cellulose-based natural polymers obtained by subjecting methylcellulose, hydroxyethylcellulose, hydroxypropylmethylcellulose, carboxymethylcellulose and the like to a water-resistant agent or heat-treated.
本発明でいう予め定められた温度とは、例えば本発明
の包装材が置かれたり、曝されたり環境の水の温度から
選択される特定の温度である。この環境水温度は、冬は
０℃あるいはそれ以下になり、夏は40℃あるいはそれ以
上になることもありうるので、これらの環境水温度の中
から10℃、25℃、40℃あるいはそれ以上の温度などを選
択して予め特定し、この特定温度未満の水に不溶であ
り、この特定温度以上の水に対しては溶解するような該
高分子を本発明の包装材に用いる。The predetermined temperature referred to in the present invention is, for example, a specific temperature selected from the temperature of water of the environment where the packaging material of the present invention is placed or exposed. This environmental water temperature is 0 ° C or lower in winter and may be 40 ° C or higher in summer. Therefore, among these environmental water temperatures, 10 ° C, 25 ° C, 40 ° C or higher The polymer is selected in advance by selecting the temperature and the like, and the polymer which is insoluble in water having a temperature lower than the specified temperature and soluble in water having a temperature higher than the specified temperature is used for the packaging material of the present invention.
予め定められた温度の他の例としては、例えば本発明
の包装材が処理されるパルパーなどの処理水の温度であ
る。Another example of the predetermined temperature is, for example, the temperature of treated water such as pulper in which the packaging material of the present invention is treated.
なお該高分子の水への溶解温度は分子設計、結晶化度
制御、変性およびその程度、配合およびの割合などによ
り適宜決めるこができる。The dissolution temperature of the polymer in water can be appropriately determined by molecular design, control of crystallinity, modification and degree of modification, blending ratio, and the like.
これらの高分子は機械的強度などの特性に優れている
ばかりでなく、天然に放置されると微生物などにより分
解され易いので天然を汚染したり破壊したりすることが
なく、又焼却しても高燃焼エネルギーや有害ガスが発生
せず、雨等の中性から弱酸性の水性媒体に対しては安定
である上、上記のような温度条件の水と接触させると容
易に溶解する特性がある。These polymers not only have excellent properties such as mechanical strength, but also are not easily polluted by microorganisms when left in nature, so they do not pollute or destroy nature, and even when incinerated. It does not generate high combustion energy or harmful gases, is stable against neutral to weakly acidic aqueous media such as rain, and has the property of being easily dissolved when brought into contact with water under the above temperature conditions .
またこれらの高分子は、 1.透明性、光沢が良いので被包装材を引き立てる、 2.透湿性や吸湿性が大きいので、包装材に結露しない、
帯電しない、 3.伸びが大きいので、被包装材をストレッチラップする
ことができる、 4.ポリエチレンなどと同様にヒートシールできるので、
包装が容易、 5.前処理なしで例えばセロハンインキなどで印刷できる
ので美しく、商品価値を高めることができる、 6.剥離性があるので、ポリエステル、エポキシ樹脂など
の成型時の離型に用いることもできる、 7.引張強度、引裂強度などの機械的強度が大きい、 8.耐油性、耐溶剤性があり、鉱物油、動植物油、有機溶
剤などに対しておかされない、 9.接着剤で接着できる、 10.酸素、窒素、水素、炭酸ガス、香料などを透過し難
く、バリアー性に優れている、 11.熱可塑性であるため、成型は容易で通常の熱可塑性
樹脂と同様な方法により容易にフィルム状、シート状な
どの膜状物、あるいは袋状、帯状などにすることができ
る、などの特性がある。In addition, these polymers are: 1. Transparency and gloss are good to enhance the material to be packaged. 2. Due to their high moisture permeability and moisture absorption, they do not condense on the packaging material.
It is not charged, 3. It has a large elongation, so it can stretch-wrap the material to be wrapped, 4. It can be heat-sealed like polyethylene etc.
Easy packaging, 5. Can be printed with cellophane ink without pre-treatment, so it is beautiful and can enhance its commercial value. 6. Releasable, used for mold release when molding polyester, epoxy resin, etc. 7.High mechanical strength such as tensile strength, tear strength, etc. 8.It has oil and solvent resistance and is not damaged by mineral oil, animal and vegetable oils, organic solvents, etc. Yes, 10. It is hard to permeate oxygen, nitrogen, hydrogen, carbon dioxide, fragrance, etc., and has excellent barrier properties. 11. Because it is thermoplastic, molding is easy and easy by the same method as ordinary thermoplastic resin. Has the property that it can be formed into a film-like material such as a film or a sheet, or a bag-like or band-like material.
該フィルムやシートが更に帯状、テープ状、バンド
状、ロープ状にして結束材とし、工業用、機械用、家庭
用などの結束用として利用するこができる。また、該フ
ィルムやシートを自動結束撚り紐とすれば、パレット用
や水平自動結束機械用撚り紐として、びん、缶等のブラ
ケースや、段ボールケースのパレット積み、薬品、洗
剤、電気製品、塗料、機械部品のパレット積みなどの結
束、宅配物の結束、印刷物、農水産物の結束として最適
であり、引張り強度、引裂強度、耐衝撃性、耐摩耗性に
もすぐれ、上記高分子の溶解温度を変化させれば濡れて
も、湿っても、強度に変化は生ぜず、優れた結束材とな
る。The film or sheet can be further formed into a band, tape, band, or rope to form a binding material, which can be used for binding for industrial use, machine use, home use, and the like. In addition, if the film or sheet is used as an automatic binding twisting cord, as a pallet or a twisting cord for a horizontal automatic binding machine, bottles, cans and other bra cases, cardboard case pallet stacking, chemicals, detergents, electric products, paints Ideal for binding pallets of machine parts, binding home goods, binding printed matter, agricultural and marine products, and has excellent tensile strength, tear strength, impact resistance, and abrasion resistance. If it is changed, the strength does not change when wet or wet, and it becomes an excellent binding material.
また該高分子に補強材として水溶性樹脂を塗布、配
合、含浸、積層等の操作をほどこし、補強した高分子組
成物の包装材とすることができる。The polymer is subjected to operations such as application, blending, impregnation, lamination and the like of a water-soluble resin as a reinforcing material, so that a reinforced polymer composition packaging material can be obtained.
本発明で用いる水溶性樹脂は常温の水に溶解するもの
であれば特に限定されるものではなく、例えばメチルセ
ルロース、ヒドロキシエチルセルロース、ヒドロキシプ
ロピルメチルセルロース、カルボキシメチルセルロース
などのセルロース系、ポリビニルアルコールなどの合成
樹脂系などを挙げることができ、また市販の水溶性樹脂
を用いることができる。The water-soluble resin used in the present invention is not particularly limited as long as it is soluble in water at normal temperature. For example, cellulose resins such as methyl cellulose, hydroxyethyl cellulose, hydroxypropyl methyl cellulose and carboxymethyl cellulose, and synthetic resin resins such as polyvinyl alcohol And the like, and a commercially available water-soluble resin can be used.
また該高分子をパルプ等の植物繊維状物質から成るシ
ートに含浸させたり、フィルムを張り合わせる等の操作
をほどこし、該繊維状物シートに気密性・水密性を与え
た強度の高い高分子組成物の包装材とすることも、また
該高分子を植物繊維により補強した高分子組成物の包装
材とすることもできる。Further, the polymer is impregnated into a sheet made of a plant fibrous substance such as pulp, or a film is laminated, and the like is subjected to operations such as airtightness and watertightness of the fibrous material sheet. It can be used as a packaging material for products, or as a packaging material for a polymer composition in which the polymer is reinforced with plant fibers.
また該高分子に無機充填剤、顔料、香料、安定剤、そ
の他の充填剤や添加剤などを配合した高分子組成物とし
て用いることもできる。Further, the polymer can be used as a polymer composition in which an inorganic filler, a pigment, a fragrance, a stabilizer, other fillers and additives, etc. are blended.
該高分子や該高分子を含む組成物に硼酸や硼砂を含ま
せたり、該高分子や該高分子を含む組成物の水溶液に硼
酸や硼砂を含ませると、化学結合として適度に架橋する
などにより、上記の特性を損なうことなく透湿性を少な
くしたり、機械的強度やバリアー性などを向上すること
ができるので好ましい。When boric acid or borax is contained in the polymer or the composition containing the polymer, or when boric acid or borax is contained in an aqueous solution of the polymer or the composition containing the polymer, the polymer is appropriately crosslinked as a chemical bond. This is preferable because moisture permeability can be reduced without impairing the above characteristics, and mechanical strength and barrier properties can be improved.
また、該高分子や該高分子を含む組成物を溶解した水
溶液にさらに硼酸や硼砂を溶解すると、該高分子が部分
的に架橋結合されて水溶液の粘度が増大したり、ウエッ
トタック性が強くなりったりする効果もある。Further, when boric acid or borax is further dissolved in an aqueous solution in which the polymer or a composition containing the polymer is dissolved, the polymer is partially cross-linked to increase the viscosity of the aqueous solution or to have a strong wet tack property. There is also the effect of becoming.
硼酸や硼砂の配合量は、該高分子の分子量、分子構
造、反応温度などにより異なるので、特定することはで
きないが、あまり多量に使用するとゲル化するのでゲル
化しない範囲で使用することが好ましい。また、硼酸や
硼砂の配合量は、該高分子や該高分子を含む組成物と硼
酸や硼砂を溶解した水溶液を用いて、常法により原紙表
面上に塗布することができる範囲内か、この水溶液を用
いて、常法によりフィルムを製造することができる範囲
内とすることが好ましい。Since the amount of boric acid or borax varies depending on the molecular weight, molecular structure, reaction temperature and the like of the polymer, it cannot be specified. . The compounding amount of boric acid or borax is within the range that can be applied on the base paper surface by a conventional method using the polymer or a composition containing the polymer and an aqueous solution in which boric acid or borax is dissolved. It is preferable to use an aqueous solution within a range where a film can be produced by a conventional method.
硼酸や硼砂以外でも該高分子に対して硼酸や硼砂のよ
うに作用するものであれば使用することができる。この
ようなものの例としては、アゾ染料、レゾルシノール、
カテコール、フロログリシノール、サリシルアニリド、
ガリックアシッド、ジヒドロキシ安息香酸などを挙げる
ことができる。In addition to boric acid and borax, any substance that acts on the polymer like boric acid or borax can be used. Examples of such are azo dyes, resorcinols,
Catechol, phlorogrisinol, salicylanilide,
Garlic acid, dihydroxybenzoic acid and the like can be mentioned.
上記特性を保持する本発明の包装材は各種の包装に用
いることができる。The packaging material of the present invention having the above characteristics can be used for various types of packaging.
例えば、食品、容器、電気・電子製品、家具、工業用
部品、紙、古紙、木材、金属、ガラス、プラスチック
ス、セラミックス、鉱物油、動物植油、有機溶剤、香料
などなどの有機物や無機物の包装、被包装材が人体に接
触してはいけないもの、悪臭のあるもの、工場、事務
所、家庭の廃棄物、防虫を要するものなどの包装を挙げ
るこができる。For example, organic and inorganic substances such as foods, containers, electrical and electronic products, furniture, industrial parts, paper, waste paper, wood, metal, glass, plastics, ceramics, mineral oil, animal oil, organic solvents, fragrances, etc. Packaging and packaging materials that should not come into contact with the human body, those with foul odors, wastes from factories, offices, households, and those that require insect repellency can be mentioned.
さらに具体的に例示すると、牛乳パック、生ゴミなど
の回収に用いるフィルム袋、農薬の包装用フィルム袋、
化学薬品を包装するためのドラムなどの内装、内装袋あ
るいはバッグインボックスなど、新聞輸送用フィルム
袋；手提げ袋、セメント、カオリン、タルク、炭酸カル
シウムなどの袋、樹脂袋、粉粒体袋などとしての包装袋
あるいはラミ袋；ストレッチフィルム、シュリンクフィ
ルムなどのフィルム、温室用フィルムなどのフィルム；
新聞巻取包装用や平判包装用など紙および紙製品包装用
ラミネート紙；エアーキャップなどの空気セルを有する
フィルムやシート；発泡フィルムやシート；盛土、苗木
根包装用などのためのネット；本発明の包装材に用いら
れる該高分子及び／又は該高分子を含む組成物から成る
ラベル、あるいは印刷などを行ったラベルを、上記の本
発明の包装材に積層、貼合したものなどを挙げることが
できるが、本発明の主旨を逸脱しない限りこれらの用途
に限定されるものではない。More specifically, for example, a milk bag, a film bag used for collecting garbage, a film bag for packaging agricultural chemicals,
Film bags for transporting newspapers such as interiors such as drums for packaging chemicals, interior bags or bag-in-boxes; as handbags, bags of cement, kaolin, talc, calcium carbonate, etc., resin bags, granular bags, etc. Packaging bags or laminating bags; films such as stretch films and shrink films, films such as greenhouse films;
Laminated paper for paper and paper product packaging such as newspaper winding packaging and plain paper packaging; films and sheets having air cells such as air caps; foamed films and sheets; nets for embankment and seedling root packaging; books Labels formed by laminating and laminating a label comprising the polymer and / or a composition containing the polymer used for the packaging material of the invention, or a label on which printing or the like has been performed, on the packaging material of the invention described above, and the like. However, the present invention is not limited to these applications without departing from the gist of the present invention.
次に本発明の方法について詳述する。 Next, the method of the present invention will be described in detail.
本発明においては、該高分子及び／又は該高分子を含
む組成物などから上記のように常法によりシート、フィ
ルムなどの膜状物を作り包装材としたり、該高分子及び
／又は該高分子を含む組成物、あるいは更に硼酸や硼砂
を配合した水溶液を塗工液あるいは接着層形成液とし、
常法により原紙に塗工するか、常法により２枚以上の原
紙をウエットラミネートして包装材としたり、上記膜状
物、あるいは原紙に塗工して該高分子及び／又は該高分
子を含む組成物を積層したものの該高分子などの面に適
当な接着剤を用いて原紙を積層して包装材としてもよ
い。In the present invention, a film-like material such as a sheet or a film is formed from the polymer and / or a composition containing the polymer by a conventional method as described above to prepare a packaging material, or the polymer and / or the polymer. A composition containing a molecule, or an aqueous solution further containing boric acid or borax is used as a coating liquid or an adhesive layer forming liquid,
The base paper may be coated by a conventional method, or two or more base papers may be wet-laminated to form a packaging material by a conventional method, or the polymer and / or the polymer may be coated on the film-like material or the base paper. A base material may be laminated on the surface of the polymer or the like using a suitable adhesive to obtain a packaging material.
上記の水溶液中の該高分子の濃度は特に限定されるも
のではないが、15重量％以上であると粘度が高くなり塗
工性あるいは接着層形成性が悪くなり、５重量％以下で
あると皮膜形成が弱く、また得られる皮膜も物理的強度
が弱く所望の防湿性、防水性などが得られない。The concentration of the polymer in the above aqueous solution is not particularly limited, but if it is 15% by weight or more, the viscosity becomes high, and the coating property or the adhesive layer forming property deteriorates, and if it is 5% by weight or less. The film formation is weak, and the resulting film also has low physical strength, so that the desired moisture-proof and waterproof properties cannot be obtained.
上述の如き塗工液あるいは接着層形成液の塗工量は常
法により原紙に対し５〜100g/m2塗布する。この場合塗
工量が5g/m2以下では、ピンホール、繊維の毛羽立ち等
により充分な防湿防水効果を得ることができず、また、
100g/m2以上では不経済であり本発明の目的を達成でき
ないので好ましくない。The coating amount of the coating liquid or the adhesive layer forming liquid as described above is applied to the base paper by 5 to 100 g / m 2 by a conventional method. In this case, if the coating amount is 5 g / m 2 or less, a sufficient moisture-proof and waterproof effect cannot be obtained due to pinholes, fluffing of fibers, and the like.
If it is 100 g / m 2 or more, it is uneconomical and the object of the present invention cannot be achieved, which is not preferable.
以上の如く原紙上に塗工液を塗布した後、あるいは原
紙のウエットラミネートに用いた後、乾燥して製品を得
る。After applying the coating liquid on the base paper as described above, or after using it for wet lamination of the base paper, the product is obtained by drying.
前述の乾燥処理の温度は、本発明の方法により得られ
る製品の防湿、防水性を左右する重要は因子である。The temperature of the above-mentioned drying treatment is an important factor which affects the moisture-proof and waterproof properties of the product obtained by the method of the present invention.
即ち、本発明の塗工液あるいは接着層形成液の所定量
を塗布した後、常温〜130℃程度の温度、好ましくは70
℃〜120℃で乾燥すると、後述実施例の如く充分な防湿
性、接着性などが発現する。しかも、高温乾燥の場合
は、製造工程上加工速度を向上することがき、しかも安
定した防湿防水性の製品を大量生産し得ると言う効果が
ある。That is, after applying a predetermined amount of the coating liquid or the adhesive layer forming liquid of the present invention, the temperature is from room temperature to about 130 ° C., preferably 70 ° C.
Drying at a temperature of from about 120 ° C. to about 120 ° C. provides sufficient moisture-proof properties and adhesive properties as described in Examples below. In addition, in the case of high-temperature drying, there is an effect that the processing speed can be improved in the manufacturing process, and that a stable moisture-proof and waterproof product can be mass-produced.
以上の如く本発明の方法は、通常の熱可塑性樹脂に用
いられる成型法を用いたり、製紙工業に於いて実用化さ
れている合成ゴム系ラテックスなどの水性エマルジョン
を用いる通常の方法を用いて、該高分子及び／又は該高
分子を含む組成物からシート、フィルムなどの膜状物を
作り包装材としたり、上記高分子の水溶液を原紙上に塗
布したり、あるいは原紙のウエットラミネートに用いた
りした後、高温乾燥によって紙の折曲げ等によっても何
ら防湿、防水性が損なわれることのない包装材を生産す
ることができ、またこれらの包装材の該高分子側に公知
の適当な接着剤を用いて更に原紙を積層して包装材とす
ることができる。As described above, the method of the present invention uses a molding method used for an ordinary thermoplastic resin, or using an ordinary method using an aqueous emulsion such as a synthetic rubber latex practically used in the papermaking industry, From the polymer and / or a composition containing the polymer, a film-like material such as a sheet or a film is formed and used as a packaging material, an aqueous solution of the polymer is coated on base paper, or used for wet lamination of base paper. After that, it is possible to produce a packaging material in which the moisture resistance and waterproofness are not impaired even by folding the paper by drying at a high temperature, and a known suitable adhesive is attached to the polymer side of these packaging materials. And the base paper can be further laminated to form a packaging material.
上記のように高温乾燥が可能であり、且つ公知の大量
高速生産用加工機械を使用できる結果、加工速度を向上
することができ、安定した防湿防水性などに優れた包装
材を大量に効率良く生産できる効果がある。As described above, high-temperature drying is possible, and as a result of using a known processing machine for mass production at a high speed, the processing speed can be improved, and a large amount of packaging material having excellent moisture-proof and waterproof properties can be efficiently produced. There is an effect that can be produced.
本発明の処理方法について以下に説明する。 The processing method of the present invention will be described below.
本発明の包装材は、優れた包装材としての特性を示す
外に該高分子を溶解する水により、容易に分散離解する
ことができる。分散離解物は液状であり、繊維状物はそ
のままの形状で再利用することもでき、脱水などにより
運搬容易な形状にすることもできる。The packaging material of the present invention exhibits excellent properties as a packaging material and can be easily dispersed and defibrated with water that dissolves the polymer. The dispersed deflocculated product is in a liquid state, and the fibrous material can be reused as it is, or can be easily transported by dehydration or the like.
被包装物を回収する際に、この包装材を人手などによ
り除去することなく、該高分子を溶解することができる
水に接触させることにより溶解して除去することにより
被包装物を回収したり、後処理したりすることができ
る。When recovering the packaged object, without removing the packaging material by hand or the like, the packaged material can be recovered by dissolving and removing the polymer by contacting it with water capable of dissolving the polymer. Or post-processing.
また、紙や古紙の包装に用いて該高分子を溶解させる
が、除去することなく紙原料、古紙中に混在させること
により紙力などの特性を増強したり、改良したりするこ
とができる。Further, the polymer is dissolved in the packaging of paper or waste paper, but the properties such as paper strength can be enhanced or improved by mixing it in the paper raw material or waste paper without removing it.
また、下水道に流出した場合においても通常の下水処
理場において該高分子は液状化除去され環境も汚染する
ことは無い。In addition, even when the polymer is discharged into a sewer, the polymer is liquefied and removed in a normal sewage treatment plant, and does not pollute the environment.
本発明の包装材を用いて、被包装物としての古紙を包
装し、貯蔵、輸送などの後、古紙を回収するプロセスに
用いる例を次に説明する。The following describes an example of using the packaging material of the present invention to package used paper as an article to be packaged, and to use it in a process of collecting used paper after storage and transportation.
すなわち中性かつ常温の水に対して安定であり、温度
を調節することにより水に溶解する高分子及び／又は高
分子組成物などから成る包装材にて古紙原料を包装した
包装物を、パルプ化工程の前、あるいは工程内にて、該
包装材を溶解させる条件に調整した水と接触させて処理
する方法である。That is, a package in which the used paper material is packaged in a package made of a polymer and / or a polymer composition which is stable to neutral and normal temperature water and is soluble in water by adjusting the temperature is used as a pulp. Before or during the chemical conversion step, the packaging material is treated by contacting with water adjusted to conditions for dissolving the packaging material.
包装材と水の接触法は特に限定はないがパルパー投入
前のベルトコンベア上に水を噴霧する方法やパルパー内
で接触させパルプ化と同時に処理する方法等が好適であ
る。The method of contacting the packaging material with water is not particularly limited, but a method in which water is sprayed on a belt conveyor before the pulper is charged, a method in which the water is brought into contact in the pulper and treated simultaneously with pulping, and the like are preferable.
パルパーにおける離解用水としては抄紙白水を用いる
のが通例であり、パルパー内は高温酸性であることか
ら、このような条件で溶解する包装材を用いる。It is customary to use papermaking white water as the disintegration water in the pulper, and since the inside of the pulper is acidic at a high temperature, a packaging material that dissolves under such conditions is used.
上記の高分子の補強材として水溶性樹脂またはパルプ
などの植物繊維を用いることにより、高分子に任意の強
度と気密・水密性を持たせることができる上、人手をか
けることなく処理でき、且つ高分子などから成る包装材
自体も抄紙原料として利用されるので紙力増強効果を期
待できる。By using a water-soluble resin or a plant fiber such as pulp as a reinforcing material for the polymer, the polymer can be given any strength and airtightness / watertightness, and can be processed without human intervention, and Since the packaging material itself made of a polymer or the like is also used as a raw material for papermaking, an effect of enhancing paper strength can be expected.
以上説明したように、本願発明の包装材は温度を調整
することにより水溶性を調節できる高分子及び／又は該
高分子組成物から成る。As described above, the packaging material of the present invention comprises a polymer and / or a polymer composition whose water solubility can be adjusted by adjusting the temperature.
また該高分子の補強材として水溶性樹脂またはパルプ
等の繊維状物を用いることが好ましい。It is preferable to use a fibrous material such as a water-soluble resin or pulp as a reinforcing material for the polymer.
また、本発明は上記包装材の製造方法を提供する。該
高分子及び／又は該高分子、あるいは更に硼酸や硼砂を
含む組成物から常法によりシート、フィルムなどの膜状
物を作り包装材としたり、該高分子及び／又は該高分子
を含む組成物、あるいは更に硼酸や硼砂を配合した水溶
液を塗工液あるいは接着層形成液とし、常法により原紙
に塗工するか、常法により２枚以上の原紙をウエットラ
ミネートして包装材としたり、上記膜状物、あるいは原
紙に塗工して該高分子及び／又は該高分子を含む組成物
を積層したものの該高分子などの面に適当な公知の接着
剤を用いて原紙を積層して包装材とするものである。The present invention also provides a method for producing the above-mentioned packaging material. From the polymer and / or the polymer, or a composition further containing boric acid or borax, a film-like material such as a sheet or a film is formed by a conventional method to prepare a packaging material, or a composition containing the polymer and / or the polymer. The product, or an aqueous solution containing boric acid or borax as a coating solution or an adhesive layer forming solution, is applied to a base paper by a conventional method, or wet-laminated with two or more base papers by a conventional method to form a packaging material. The above-mentioned film-like material or base paper is coated and the polymer and / or a composition containing the polymer is laminated, and the base paper is laminated on a surface of the polymer or the like using an appropriate known adhesive. It should be a packaging material.
該高分子などを溶解した水溶液を使用して包装材を製
造する場合、塗工量を少なくしたり、あるいは接着層厚
さあるいは接着剤厚さを薄くすることができる上、包装
材は、防湿性・ガスバリアー性、耐油性、機械的特性、
気密性・水密性等に優れているので各種の包装その他の
目的に用いることができる。When a packaging material is produced using an aqueous solution in which the polymer or the like is dissolved, the amount of coating can be reduced, or the thickness of the adhesive layer or the adhesive can be reduced. Properties, gas barrier properties, oil resistance, mechanical properties,
Since it has excellent airtightness and watertightness, it can be used for various packaging and other purposes.
このような素材でできた包装材は該高分子を溶解する
水と接触することにより容易に液状化され、その後の操
作において再利用、回収運搬、下水道放流等の別を問わ
ずに処理は容易となる。The packaging material made of such a material is easily liquefied by being brought into contact with water in which the polymer is dissolved, and can be easily processed in subsequent operations regardless of reuse, collection and transportation, sewer discharge, etc. Becomes
本願発明における処理法は、単に該高分子を溶解する
水を包装物と接触させることにより該包装材を液状化
し、人手をかけずに処理するものである。In the treatment method of the present invention, the packaging material is liquefied simply by contacting water that dissolves the polymer with the package, and the treatment is performed without human intervention.
しかも処理工程以前の段階では包装材は、透明性、透
湿性、吸湿性、ヒートシール性、印刷性、剥離性、ガス
バリアー性、耐油性、機械的特性、気密性・水密性等に
優れているので各種の包装に用いることができる。In addition, prior to the processing step, the packaging material has excellent transparency, moisture permeability, moisture absorption, heat sealability, printability, peelability, gas barrier properties, oil resistance, mechanical properties, airtightness, watertightness, etc. Can be used for various types of packaging.
特に補強剤としてパルプを使った包装材を古紙原料の
包装に用い、包装材を適当な温度の水により液状化する
方法は最も省力効果の高い処理法と言える。In particular, a method in which a packaging material using pulp as a reinforcing agent is used for packaging used paper material and the packaging material is liquefied with water at an appropriate temperature can be said to be the most labor-saving treatment method.
これらは全て本発明において用いる温度の変化により
水に対する溶解性を調節し得る特殊な高分子の特性によ
るものである。These are all due to the properties of special polymers that can control solubility in water by changing the temperature used in the present invention.
また、本願発明の包装材を紐、帯、ロープ、バンド、
テープなどの結束材とすると、従来の紙バンドに比べて
数倍の強度があり、ポリエチレンフィルムやポリ塩化ビ
ニルフィルムに比較しても、その強度は強くすぐれてい
る。これらの材料の特性を表１に示す。In addition, the packaging material of the present invention can be used for a string, a band, a rope, a band,
When used as a binding material such as a tape, the binding strength is several times higher than that of a conventional paper band, and the strength is superior to a polyethylene film or a polyvinyl chloride film. Table 1 shows the properties of these materials.
発明を実施するための最良な形態 以下、本発明の効果を実施例を通じて、さらに具体的
に説明するが、本発明の主旨を逸脱しない限り実施例に
限定されるものではない。 BEST MODE FOR CARRYING OUT THE INVENTION Hereinafter, the effects of the present invention will be described more specifically with reference to examples, but the present invention is not limited to the examples unless departing from the gist of the present invention.
実施例１ 水75部、ポリ酢酸ビニル鹸化物（鹸化度98.5モル％、
重合度1100）20部、グリセロール1.4部、グリオキザー
ル0.6部を溶解した水溶液を100℃以下で乾燥させ約20ミ
クロン厚みのフィルムを作り、該フィルムとワンプ紙を
140℃で熱プレスしてラミネートし、気密・水密性の高
い包装材を得た（該フィルムは45℃の水に溶解する）。Example 1 75 parts of water, saponified polyvinyl acetate (a saponification degree of 98.5 mol%,
An aqueous solution in which 20 parts of polymerization degree 1100), glycerol 1.4 parts and glyoxal 0.6 parts are dissolved is dried at 100 ° C. or less to make a film having a thickness of about 20 μm.
Lamination was performed by hot pressing at 140 ° C. to obtain a highly airtight and watertight packaging material (the film was dissolved in water at 45 ° C.).
ミルクカートンの空箱をベーラーにより圧縮した被包
装物を該包装材により包装した包装物は常温の水にぬれ
ても安定であった。The package in which an empty box of the milk carton was compressed with a baler and the package was packaged with the packaging material was stable even when it was wet with water at room temperature.
この包装物は、そのままパルパー内に投入したとろ、
包装材ともども容易に離解され、紙料中に異物は見られ
なかった。When this package is put into the pulper as it is,
The packaging material was easily disaggregated, and no foreign matter was found in the stock.
パルパーに供給される離解用の抄紙白水はpH4.5〜5.
0、温度45℃である。The papermaking white water for disintegration supplied to the pulper has a pH of 4.5 to 5.
0, temperature 45 ° C.
抄紙白水中の包装物の割合は５重量％であった。 The proportion of the package in the papermaking white water was 5% by weight.
実施例２ 過酸化物触媒を用いて、100℃でポリ酢酸ビニルの加
水分解物にポリビニルアルコールをグラフト重合した共
重合体の水溶液を炭酸カルシウム含有紙に含浸させて高
分子含有紙を得た（該高分子は45℃の水に溶解する）。Example 2 Using a peroxide catalyst, an aqueous solution of a copolymer obtained by graft-polymerizing a polyvinyl alcohol hydrolyzate with polyvinyl alcohol at 100 ° C. was impregnated into calcium carbonate-containing paper to obtain a polymer-containing paper ( The polymer dissolves in water at 45 ° C).
この紙は中性の水に安定であり十分な水密性を有し
た。This paper was stable in neutral water and had sufficient watertightness.
この紙を50℃の水中に投入し攪拌すると容易に離解し
てパルプスラリーとなった。水中の紙の割合は５重量％
であった。When this paper was put into water at 50 ° C. and stirred, it was easily disintegrated to form a pulp slurry. 5% by weight of paper in water
Met.
このパルプスラリーを活性汚泥曝気槽に供給しても異
常は認められず、汚泥の脱水性は良好であった。Even when this pulp slurry was supplied to the activated sludge aeration tank, no abnormality was recognized, and the sludge dewaterability was good.
実施例３ 水10Kg、ガラス繊維（6GYD）3.75g、パルプ（NBKP）
1.85g、変性ポリビニルアルコール［鹸化度98.5モル
％、４％粘度26〜30cps（20℃）］（PVAと略す）（該PV
Aは50℃の水に溶解する）を6GYD/PVA＝67/33（重量比）
で下表に示す割合で配合し、パルパーにより3000rpm、
５分攪拌後、抄造し（80メッシュ金網）、3.5Kg/cm2で
プレスし、オートドライヤーで120℃、３分乾燥した。Example 3 Water 10 kg, glass fiber (6GYD) 3.75 g, pulp (NBKP)
1.85 g, modified polyvinyl alcohol [degree of saponification: 98.5 mol%, 4% viscosity: 26 to 30 cps (20 ° C)] (abbreviated as PVA) (the PV
A dissolves in 50 ° C water) 6GYD / PVA = 67/33 (weight ratio)
In the proportions shown in the table below, 3000 rpm by pulper,
After stirring for 5 minutes, the paper was made (80 mesh wire mesh), pressed at 3.5 kg / cm 2 , and dried at 120 ° C. for 3 minutes with an auto dryer.
得られたシートの強度を測定した結果を表２に示す。 Table 2 shows the results of measuring the strength of the obtained sheet.
強度測定法:TAPPI Ｔ−404,TS−66 （表２） PVA添加量（％） ０ 10 20 30 強度（Kg/cm） 0.25 2.75 4.30 5.50 実施例４ 古新聞紙を４つ折りにして高さ約50cmに積み上げたも
のを、実施例１と同様にして作ったフィルムをカットし
て幅40mm、厚さ30μｍの帯状の紐としたもので縦、横方
向に十分に結束した。Strength measurement method: TAPPI T-404, TS-66 (Table 2) PVA addition amount (%) 0 10 20 30 Strength (Kg / cm) 0.25 2.75 4.30 5.50 Example 4 Fold old newspaper and make it about 50 cm high The film formed in the same manner as in Example 1 was cut into a band-like string having a width of 40 mm and a thickness of 30 μm, which was sufficiently bound in the vertical and horizontal directions.
この包装物をそのまま、パルパーで処理したが、繊維
間結合を妨げることなく故紙の再生は可能であった。This package was treated with a pulper as it was, but it was possible to recycle waste paper without interfering with the interfiber bonding.
実施例５ 古週間紙を高さ約50cmに積み上げたものを、実施例１
と同様にして作ったフィルムをカットして幅40mm、厚さ
30μｍのバンド状の紐としたもので縦、横方向に十分に
結束した。Example 5 A stack of used weekly papers having a height of about 50 cm was used in Example 1.
Cut the film made in the same way as in the above, width 40mm, thickness
A 30 μm band-shaped cord was used and tied sufficiently in the vertical and horizontal directions.
この包装物をそのまま、パルパーで処理したが、繊維
間結合を妨げることなく故紙の再生は可能であった。This package was treated with a pulper as it was, but it was possible to recycle waste paper without interfering with the interfiber bonding.
比較例１ 20ミクロンのポリエチレンフィルムとワンプ紙を熱プ
レスしてラミネートし、気密・水密性の高い包装材を得
た。Comparative Example 1 A 20-micron polyethylene film and wamp paper were hot-pressed and laminated to obtain a highly airtight and watertight packaging material.
ミルクカートンの空箱をベーラーにより圧縮した被包
装物を該包装材により包装した包装物は水にぬれても安
定であった。The package in which an empty box of a milk carton was compressed with a baler and the package was packed with the packaging material was stable even when wet with water.
この包装物を、そのまま実施例１と同様にパルパー内
に投入したところ、包装材は全く離解されず、紙料中に
異物が残った。When this package was put into a pulper as it was in the same manner as in Example 1, the package was not disintegrated at all, and foreign matter remained in the stock.
実施例６ 水75部、ポリ酢酸ビニル鹸化物（鹸化度98.5モル％、
重合度1100）20部、グリセロール1.4部、グリオキザー
ル0.6部、あるいは更に硼酸又は硼砂0.2部を溶解した水
溶液を薄物ワンプ紙に塗工し、100℃以下で乾燥させ約2
3〜25ミクロン厚みのフィルムを積層した気密・水密性
の高い包装材を得た（該フィルムは45℃の水に溶解す
る）。Example 6 75 parts of water, saponified polyvinyl acetate (saponification degree: 98.5 mol%,
Polymerization degree 1100) 20 parts, glycerol 1.4 parts, glyoxal 0.6 parts or an aqueous solution in which boric acid or borax 0.2 parts is dissolved is applied to thin wamp paper, dried at 100 ° C. or less and dried for about 2 hours.
A highly air-tight and water-tight packaging material laminated with a film having a thickness of 3 to 25 microns was obtained (the film was dissolved in water at 45 ° C).
ミルクカートンの空箱をベーラーにより圧縮した被包
装物を該包装材により包装した包装物は常温の水にぬれ
ても安定であった。The package in which an empty box of the milk carton was compressed with a baler and the package was packaged with the packaging material was stable even when it was wet with water at room temperature.
この包装物を、そのままパルパー内に投入したとこ
ろ、包装材はともども容易に離解され、紙料中に異物が
見られなかった。When this package was put into the pulper as it was, the package was easily disintegrated and no foreign matter was found in the stock.
パルパーに供給さる離解用の抄紙白水はpH4.5〜5.0、
温度45℃である。The papermaking white water for disintegration supplied to the pulper is pH 4.5-5.0,
The temperature is 45 ° C.
抄紙白水中の包装材の割合は５重量％であった。 The proportion of the packaging material in the papermaking white water was 5% by weight.
実施例７ 過酸化物触媒を用いて、100℃でポリ酢酸ビニルの加
水分解物等にポリビニルアルコールをグラフト重合した
共重合体、あるいは更にこの共重合体の２重量％の硼酸
又は硼砂を配合した水溶液を用いて、ウエットラミネー
ト法により炭酸カルシウム含有紙を積層した包装材を得
た（該高分子は45℃の水に溶解する）。Example 7 A copolymer in which polyvinyl alcohol was graft-polymerized to a hydrolyzate of polyvinyl acetate or the like at 100 ° C. using a peroxide catalyst, or 2% by weight of this copolymer, boric acid or borax was further compounded. Using the aqueous solution, a packaging material on which calcium carbonate-containing paper was laminated by a wet lamination method was obtained (the polymer was dissolved in water at 45 ° C).
この包装材は中性の水に安定であり十分な水密性を有
した。This packaging material was stable in neutral water and had sufficient watertightness.
この包装材を50℃の水中に投入し攪拌すると容易に離
解してパルプスラリーとなった。水中の紙の割合は５重
量％であった。When this packaging material was put into water at 50 ° C. and stirred, it was easily disintegrated to form a pulp slurry. The proportion of paper in water was 5% by weight.
このパルプスラリーを活性汚泥曝気槽に供給しても異
常は認められず、汚泥の脱水性は良好であった。Even when this pulp slurry was supplied to the activated sludge aeration tank, no abnormality was recognized, and the sludge dewaterability was good.
実施例８ 実施例７で用いた水溶液を用いて２枚のワンプ紙を積
層した。この積層包装材も実施例７の包装材と同様優れ
た強度特性と透湿性を有し、カールもなく、離解性にも
異常は認められなかった。Example 8 Two wamp papers were laminated using the aqueous solution used in Example 7. This laminated packaging material also had excellent strength properties and moisture permeability similarly to the packaging material of Example 7, no curl, and no abnormality in disaggregation.
また、実施例７で用いた水溶液を用いて作ったフィル
ムを公知の接着剤を用いて２枚のワンプ紙の間にサンド
イッチ状に積層した。この積層包装材も実施例７の包装
材と同様優れた強度特性と透湿性を有し、カールもな
く、離解性にも異常は認められなかった。Further, a film made by using the aqueous solution used in Example 7 was laminated in a sandwich manner between two wamp papers using a known adhesive. This laminated packaging material also had excellent strength properties and moisture permeability similarly to the packaging material of Example 7, no curl, and no abnormality in disaggregation.
実施例９〜12 厚紙厚さ、ラミネート膜厚を変化させ、実施例９は実
施例７と同様にしてウエットラミネート法により原紙を
積層した包装材を得た（該高分子は45℃の水に溶解す
る）。実施例10〜11では実施例７で用いた水溶液を用い
て実施例８と同様にしてサンドイッチ状に原紙と積層し
た包装材を得た。実施例12では実施例７で用いた水溶液
を用いて実施例７と同様にしてウエットラミネート法に
よりワンプ紙を積層し、該高分子側に公知の接着剤を用
いてワンプ紙を積層して包装材を得た。Examples 9 to 12 In Example 9, the thickness of the cardboard and the thickness of the laminate were changed, and in the same manner as in Example 7, a packaging material in which the base paper was laminated by a wet lamination method was obtained (the polymer was dissolved in water at 45 ° C). Dissolves). In Examples 10 to 11, the aqueous solution used in Example 7 was used to obtain a packaging material laminated with base paper in a sandwich manner in the same manner as in Example 8. In Example 12, the aqueous solution used in Example 7 was used to laminate the Wamp paper by wet lamination in the same manner as in Example 7, and the polymer side was laminated using a known adhesive to laminate the Wamp paper. Wood was obtained.
これらの包装材の引張強度および伸度、引き裂き強
度、透湿度、離解度、耐水性、摩擦係数を測定した。The tensile strength and elongation, tear strength, moisture permeability, degree of disaggregation, water resistance and coefficient of friction of these packaging materials were measured.
結果をまとめて表３に示す。 Table 3 summarizes the results.
比較例２ 20ミクロンのポリエチレンフィルムとワンプ紙を熱プ
レスしてラミネートし、気密・水密性の高い包装材を得
た。Comparative Example 2 A 20-micron polyethylene film and wamp paper were hot-pressed and laminated to obtain a highly airtight and watertight packaging material.
ミルクカートンの空箱をベーラーにより圧縮した被包
装物を該包装材により包装した包装物は水にぬれても安
定であった。The package in which an empty box of a milk carton was compressed with a baler and the package was packed with the packaging material was stable even when wet with water.
この包装物を、そのまま実施例１と同様にパルパー内
に投入したところ、包装材は全く離解されず、紙料中に
異物が残った。When this package was put into a pulper as it was in the same manner as in Example 1, the package was not disintegrated at all, and foreign matter remained in the stock.
比較例３ 25ミクロンのポリエチレンテレフタレートフィルムと
ワンプ紙を熱プレスしてラミネートし、気密・水密性の
高い包装材を得た。Comparative Example 3 A 25 micron polyethylene terephthalate film and wamp paper were hot-pressed and laminated to obtain a highly airtight and watertight packaging material.
ミルクカートンの空箱をベーラーにより圧縮した被包
装物を該包装材により包装した包装物は水にぬれても安
定であった。The package in which an empty box of a milk carton was compressed with a baler and the package was packed with the packaging material was stable even when wet with water.
この包装物を、そのまま実施例１と同様にパルパー内
に投入したところ、包装材は全く離解されず、紙料中に
異物が残った。When this package was put into a pulper as it was in the same manner as in Example 1, the package was not disintegrated at all, and foreign matter remained in the stock.
比較例４〜６ 比較例４〜６では、紙厚等の異なるワンプ紙について
同様に試験した。比較例５、６では、防湿性ワンプ紙を
用いた。Comparative Examples 4 to 6 In Comparative Examples 4 to 6, the same test was performed on wamp papers having different thicknesses. In Comparative Examples 5 and 6, moisture-proof wamp paper was used.
結果をまとめて表３に示す。 Table 3 summarizes the results.
試験法； 前処理方法、引張強度および伸度;JIS P8111に準ず
る。Test method: Pretreatment method, tensile strength and elongation; according to JIS P8111.
引裂き強度;JIS P8116に準ずる。Tear strength; according to JIS P8116.
透湿度;JIS Z0208（Ｂ法）に準ずる。Moisture permeability; according to JIS Z0208 (Method B).
摩擦係数;J.TAPPI.30−79に準ずる。Coefficient of friction; according to J.TAPPI.30-79.
離解度;50℃温水を入れた攪拌機付１リットルステンレ
ス容器（パルプ離解機）に1cm×1cmの試料を１枚入れ、
2000r.p.m.で試料が溶解する迄の時間（秒数）を測定し
た。Disintegration degree: One 1 cm × 1 cm sample was placed in a 1-liter stainless steel container (pulp disintegrator) equipped with a stirrer filled with hot water at 50 ° C.
The time (number of seconds) until the sample was dissolved was measured at 2000 rpm.
耐水性;50℃温水を入れた攪拌機付１リットルステンレ
ス容器（パルプ離解機）に1cm×1cmの試料を１枚入れ、
2000r.p.m.で試料が溶解する迄の時間を測定し、耐水性
を試験した。Water resistance; One 1 cm x 1 cm sample was placed in a 1-liter stainless steel container (pulp disintegrator) with a stirrer containing hot water at 50 ° C.
The time until the sample dissolved at 2000 rpm was measured, and the water resistance was tested.
結果を１（悪い）〜５（良い）で表す。 The results are expressed as 1 (bad) to 5 (good).
産業上の利用可能性 温度の変化により水に対する溶解性を調節し得る高分
子および／または補強材として水溶性樹脂や植物繊維を
含むこの高分子組成物などからなる本発明の包装材は、
通常の使用条件では十分な強度を持ち、透明性、透湿
性、吸湿性、ヒートシール性、印刷性、剥離性、ガスバ
リアー性、耐油性、気密性・水密性等の特性を保持する
ので各種の包装に用いることができる。 Industrial Applicability The packaging material of the present invention comprising a polymer capable of adjusting the solubility in water by a change in temperature and / or a polymer composition containing a water-soluble resin or a plant fiber as a reinforcing material,
Under normal use conditions, it has sufficient strength and retains properties such as transparency, moisture permeability, moisture absorption, heat sealability, printability, peelability, gas barrier properties, oil resistance, airtightness and watertightness, so various types Can be used for packaging.
本発明の包装材の製造方法によると、通常の熱可塑性
樹脂に用いられる成型法を用いたり、製紙工業に於いて
実用化されている合成ゴム系ラテックスなどの水性エマ
ルジョンを用いる通常の方法を用いて、該高分子及び／
又は該高分子を含む組成物などからシート、フィルムな
どの膜状物を作り包装材としたり、上記高分子などの水
溶液を原紙上に塗布したり、あるいは原紙のウエットラ
ミネートに用いたりした後、高温乾燥によって包装材を
生産することができる結果、高加工速度で、安定した防
湿防水性などに優れた包装材を大幅に効率良く生産でき
る。According to the method for producing a packaging material of the present invention, a molding method used for a normal thermoplastic resin is used, or a normal method using an aqueous emulsion such as a synthetic rubber latex practically used in the papermaking industry is used. And the polymer and / or
Or, from the composition containing the polymer or the like, a film-like material such as a sheet and a film is used as a packaging material, or an aqueous solution of the above polymer or the like is applied on base paper, or after being used for wet lamination of the base paper, As a result of producing a packaging material by high-temperature drying, it is possible to produce a packaging material excellent in stable moisture-proof and water-proof properties at a high processing speed and efficiently.
また、包装不要となった時点で簡易な操作により包装
材を適当な温度の水により液状化することができるので
省力効果が高い。Further, when the packaging becomes unnecessary, the packaging material can be liquefied with water at an appropriate temperature by a simple operation, so that the power saving effect is high.
本発明の包装材を紙や古紙原料の包装に用いて、包装
材自体を抄紙原料として利用すると紙力増強効果があ
る。When the packaging material of the present invention is used for packaging paper or waste paper raw material, and the packaging material itself is used as a papermaking raw material, there is an effect of enhancing paper strength.
従来使用されているポリプロピレン、ポリエチレン製
の紐、撚り紐は包装用として使用した場合パルパー等で
不溶であり、除去する等故紙再生に障害を与えるという
問題があるが、本発明の包装材を紐として使用すると、
適当な温水により溶けて溶液となるので、紙や古紙原料
の結束、包装に使用して包装材自体を除去することなく
使用できる上、古紙原料として利用すると紙力増強効果
も期待することがてき、その産業上の利用価値は甚だ大
きい。Conventionally used polypropylene and polyethylene cords and twisted cords are insoluble in pulpers and the like when used for packaging, and there is a problem in that they may interfere with the recycling of waste paper, such as by removing them. When used as
Since it is dissolved by appropriate warm water to form a solution, it can be used for bundling and packaging paper and waste paper raw materials without removing the packaging material itself. Its industrial utility value is enormous.
───────────────────────────────────────────────────── フロントページの続き (72)発明者 佐藤 哲夫 東京都北区王子５丁目21番１号 十條製 紙株式会社技術開発センター内 (72)発明者 梅木 武光 東京都北区王子５丁目21番１号 十條製 紙株式会社技術開発センター内 (72)発明者 芦田 徹志 東京都北区王子５丁目21番２号 十條製 紙株式会社リキッドパッケージングセン ター内 (72)発明者 鈴木 新一 東京都北区王子５丁目21番２号 十條製 紙株式会社リキッドパッケージングセン ター内 (72)発明者 小林 裕 東京都千代田区神田東松下町28番地 株 式会社中村悳商会内 (72)発明者 原澤 重雄 東京都千代田区神田東松下町28番地 株 式会社中村悳商会内 (72)発明者 和井田 浩史 東京都足立区神明南２丁目16番９号 東 立化成工業株式会社内 (56)参考文献 特開 平２−108534（ＪＰ，Ａ) 特開 昭56−80457（ＪＰ，Ａ) 特開 昭51−12889（ＪＰ，Ａ) (58)調査した分野(Int.Cl.7，ＤＢ名) D21H 17/00 - 21/14 ──────────────────────────────────────────────────続 き Continuing on the front page (72) Inventor Tetsuo Sato 5-2-1-1, Oji, Kita-ku, Tokyo Inside the Technical Development Center, Jujo Paper Co., Ltd. (72) Takemitsu Umeki 5--21, Oji, Kita-ku, Tokyo No. 1 Jujo Paper Co., Ltd. Technology Development Center (72) Inventor Tetsushi Ashida 5-21-2 Oji, Kita-ku, Tokyo Jujo Paper Co., Ltd. Liquid Packaging Center (72) Inventor Shinichi Suzuki Tokyo 5-21-2 Oji Kita-ku Jujo Paper Co., Ltd. Liquid Packaging Center (72) Inventor Hiroshi Kobayashi 28 Kanda-Higashi Matsushita-cho, Chiyoda-ku, Tokyo Nakamura Shig Co., Ltd. (72) Inventor Harazawa Shigeo 28, Kanda-Higashimatsushita-cho, Chiyoda-ku, Tokyo Inside Nakamura Shig Co., Ltd. (72) Inventor Hiroshi Waida Shinmei-minami, Adachi-ku, Tokyo No. 16-9, Tohatsu Kasei Kogyo Co., Ltd. (56) References JP-A-2-108534 (JP, A) JP-A-56-80457 (JP, A) JP-A-51-12889 (JP, A) (58) Field surveyed (Int. Cl. 7 , DB name) D21H 17/00-21/14
Claims (12)
以上の予め定められた温度に昇温することにより、水に
溶解する高分子を含む組成物から成る包装材であって、
該高分子が硼酸、アゾ染料、レゾルシノール、カテコー
ル、フロログリシノール、サリシルアニリド、ガリック
アシッド、ジヒドロキシ安息香酸、グリオキザールから
選ばれる少なくとも１種を含むことを特徴とする包装
材。1. Insoluble in water below 40 ° C., but at 40 ° C.
By raising the temperature to the predetermined temperature, a packaging material comprising a composition containing a polymer soluble in water,
A packaging material characterized in that the polymer contains at least one selected from boric acid, azo dye, resorcinol, catechol, phloroglicinol, salicylanilide, gallic acid, dihydroxybenzoic acid, and glyoxal.
るこを特徴とする請求項１記載の包装材。2. The packaging material according to claim 1, wherein said polymer is a modified polyvinyl alcohol.
維を使用した該高分子組成物から成ることを特徴とする
請求項１あるいは請求項２記載の包装材。3. The packaging material according to claim 1, wherein the packaging material comprises the polymer composition using a water-soluble resin and / or vegetable fiber as a reinforcing material.
紙と積層されていることを特徴とする包装材。4. The packaging material according to claim 1, wherein the packaging material is laminated with at least one layer of base paper.
ら膜状物を作ることを特徴とする包装材の製造方法。5. A method for producing a packaging material, comprising forming a film from the composition containing the polymer according to claim 1.
溶解した水溶液を、常法により原紙表面上に塗布し、乾
燥することを特徴とする包装材の製造方法。6. A method for producing a packaging material, comprising applying an aqueous solution in which the composition containing the polymer according to claim 1 is dissolved on the surface of a base paper by a conventional method, and drying.
溶解した水溶液を接着層として２枚以上の原紙を積層し
た後、乾燥することを特徴とする包装材の製造方法。7. A method for producing a packaging material, comprising laminating two or more base papers using an aqueous solution in which the composition containing the polymer according to claim 1 is dissolved as an adhesive layer, and drying.
に記載の包装材の該高分子を含む組成物の面に接着剤に
より原紙を積層することを特徴とする包装材の製造方
法。8. The packaging material according to claim 1 or claim 4.
A method for producing a packaging material, comprising laminating a base paper on the surface of the composition containing the polymer of the packaging material according to 1 above with an adhesive.
ることを特徴とする請求項５から請求項８記載のいずれ
かに記載の包装材の製造方法。9. The method for producing a packaging material according to claim 5, wherein the polymer is a modified polyvinyl alcohol.
装材により被包装物を包装した包装物を、該高分子を溶
解する条件の水と接触させることを特徴とする処理方
法。10. A processing method comprising contacting a package in which a package is packaged with the packaging material according to claim 1 or 4 with water in a condition for dissolving the polymer.
する請求項10記載の処理方法。11. The processing method according to claim 10, wherein the object to be packaged is a raw material for used paper.
装材が紐、帯、ロープ、バンド、テープから選ばれる結
束材であり、それにより被包装物を結束した包装物を、
該高分子を溶解する条件の水と接触させることを特徴と
する請求項10に記載の処理方法。12. The packaging material according to claim 1 or 4, wherein the packaging material is a binding material selected from a string, a band, a rope, a band, and a tape.
11. The processing method according to claim 10, wherein the polymer is brought into contact with water under conditions that dissolve the polymer.