JP3002671B1 - Boron nitride and silicone oil composition using the same - Google Patents
Boron nitride and silicone oil composition using the sameInfo
- Publication number
- JP3002671B1 JP3002671B1 JP26962198A JP26962198A JP3002671B1 JP 3002671 B1 JP3002671 B1 JP 3002671B1 JP 26962198 A JP26962198 A JP 26962198A JP 26962198 A JP26962198 A JP 26962198A JP 3002671 B1 JP3002671 B1 JP 3002671B1
- Authority
- JP
- Japan
- Prior art keywords
- silicone oil
- boron nitride
- oil composition
- fluoroalkylsilane
- added
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
【要約】
【課題】潤滑性、離型性、摺動特性、放熱特性に優れる
シリコーンオイル組成物を提供する。
【解決手段】フルオロアルキルシランを添加した窒化硼
素を、シリコーンオイルに添加してなるシリコーンオイ
ル組成物。前記用途用の窒化硼素。An object of the present invention is to provide a silicone oil composition having excellent lubricating properties, releasing properties, sliding properties, and heat radiation properties. A silicone oil composition obtained by adding boron nitride containing fluoroalkylsilane to silicone oil. Boron nitride for said application.
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、窒化硼素にフルオ
ロアルキルシランを添加してなる窒化硼素であり、シリ
コーンオイルへの濡れ性を改善した窒化硼素に関する。
又、本発明は、前記窒化硼素をシリコーンオイルに添加
してなるシリコーンオイル組成物であり、金属の熱間加
工用の高温固体潤滑あるいは離型剤、更に摺動部分の潤
滑や発熱性電子・電気部品の放熱の用途に好適なシリコ
ーンオイル組成物に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to boron nitride obtained by adding fluoroalkylsilane to boron nitride, and to boron nitride having improved wettability to silicone oil.
Further, the present invention is a silicone oil composition obtained by adding the above-mentioned boron nitride to silicone oil, and includes a high-temperature solid lubrication or release agent for hot working of metal, lubrication of a sliding portion, and heat-generating electrons and heat. The present invention relates to a silicone oil composition suitable for use in heat radiation of electric components.
【０００２】[0002]
【従来の技術】シリコーンオイルに窒化硼素を添加した
シリコーンオイル組成物は公知であり、いろいろな分野
で使用されている。例えば、アルミニウム合金の押出成
形時の高温用固体潤滑剤や、アルミニウムダイキャスト
等の高温金型離型剤としては、従来の黒鉛粉末を添加し
たオイル組成物に替わって、高温での潤滑性や離型性を
改善する目的で、窒化硼素添加シリコーンオイル組成物
が提案され用いられている。また、従来のカーボンブラ
ック,ＰＴＦＥ等を添加した潤滑用シリコーンオイル組
成物や、酸化珪素、酸化亜鉛を添加した放熱用シリコー
ンオイル組成物において、前記潤滑性や熱伝導性を改善
する目的で、前記添加剤にかわって窒化硼素を用いたシ
リコーンオイル組成物が提案されている。2. Description of the Related Art Silicone oil compositions obtained by adding boron nitride to silicone oil are known and have been used in various fields. For example, as a high-temperature solid lubricant at the time of extrusion molding of an aluminum alloy, or as a high-temperature mold release agent such as aluminum die-casting, instead of the oil composition containing conventional graphite powder, lubricity at high temperatures and For the purpose of improving the releasability, a boron nitride-added silicone oil composition has been proposed and used. Further, conventional carbon black, a silicone oil composition for lubrication to which PTFE or the like is added, or a silicone oil composition for heat dissipation to which silicon oxide or zinc oxide is added, for the purpose of improving the lubricity or thermal conductivity, Silicone oil compositions using boron nitride instead of additives have been proposed.
【０００３】[0003]
【発明が解決しようとする課題】しかし、シリコーンオ
イルに窒化硼素を充填する場合、窒化硼素表面とシリコ
ーンオイルの濡れが充分でなく、シリコーンオイル中の
窒化硼素の分散性が良好でないことから、シリコーンオ
イル組成物の粘度が高くなること、また、得られるシリ
コーンオイル組成物の特性について、充分な潤滑、離型
性、或いは摺動特性、放熱特性が十分に満足できるもの
ではないという問題がある。However, when the silicon oil is filled with boron nitride, the surface of the silicon nitride is not sufficiently wetted with the silicon oil and the dispersibility of the boron nitride in the silicone oil is not good. There is a problem that the viscosity of the oil composition becomes high, and that the properties of the obtained silicone oil composition are not sufficiently satisfactory in lubrication, release properties, sliding properties and heat radiation properties.
【０００４】本発明は、上記事情に鑑みてなされたもの
であり、シリコーンオイルに対する窒化硼素の濡れ性を
改善し、潤滑性、離型性、摺動特性、放熱特性等の特性
が十分に発揮されるシリコーンオイル組成物を提供する
ものである。[0004] The present invention has been made in view of the above circumstances, and improves the wettability of boron nitride with silicone oil, and fully exhibits properties such as lubricity, mold release, sliding properties, and heat radiation properties. The present invention provides a silicone oil composition to be used.
【０００５】[0005]
【課題を解決するための手段】本発明は、窒化硼素にフ
ルオロアルキルシランを添加してなることを特徴とする
シリコーンオイル添加用窒化硼素であり、好ましくは、
前記フルオロアルキルシランがトリメチルシラノール基
を有すること、更に好ましくは、前記窒化硼素の黒鉛化
指数が４．０以下である前記のシリコーンオイル添加用
窒化硼素である。The present invention is directed to a boron nitride for adding silicone oil, characterized by adding a fluoroalkylsilane to boron nitride.
Preferably, the fluoroalkylsilane has a trimethylsilanol group, more preferably the boron nitride for adding silicone oil, wherein the graphitization index of the boron nitride is 4.0 or less.
【０００６】又、本発明は、シリコーンオイルに、前述
のフルオロアルキルシランの添加された窒化硼素を添加
してなるシリコーンオイル組成物であり、更に、黒鉛、
二硫化モリブデンの１種以上を含有する前記シリコーン
オイル組成物であり、酸化珪素、酸化亜鉛、酸化アルミ
ニウム、カーボン、ＰＴＦＥ、リチウム石鹸の１種以上
を含有する前記のシリコーンオイル組成物である。[0006] The present invention also relates to the silicone oil described above.
Of boron nitride added with fluoroalkylsilane
A silicone oil composition, further comprising graphite,
A silicone oil composition containing at least one of molybdenum disulfide and the above-mentioned silicone oil composition containing at least one of silicon oxide, zinc oxide, aluminum oxide, carbon, PTFE, and lithium soap.
【０００７】[0007]
【発明の実施の形態】本発明のシリコーンオイル組成物
とは、シリコーンオイルに窒化硼素とフルオロアルキル
シランとを添加してなるオイル（粘度１００００ｃＳｔ
２５℃以下）、更に、必要に応じて、前記窒化硼素以外
の無機物質や増ちょう剤さらには添加剤を含ませた、粘
ちょう性を有するグリース状のものを総称している。BEST MODE FOR CARRYING OUT THE INVENTION The silicone oil composition of the present invention refers to an oil obtained by adding boron nitride and fluoroalkylsilane to a silicone oil (viscosity of 10,000 cSt).
(At 25 ° C. or lower) and, if necessary, a viscous grease-like material containing an inorganic substance other than boron nitride, a thickener, and an additive.
【０００８】窒化硼素については、立方晶、綾面体、六
方晶のそれぞれの結晶系に属するもの、或いはＰＢＮ、
ｔ−ＢＮ等いろいろなものが公知であるが、本発明で
は、六方晶の窒化硼素が好ましい。六方晶の窒化硼素
は、その結晶構造に由来して、高いアスペクト比の板
（或いは鱗片ともいう）の形状を有し、シリコーンオイ
ルに添加した際に、得られるシリコーンオイル組成物の
潤滑性や熱伝導率を格段に改善することができる。[0008] As for boron nitride, those belonging to the respective crystal systems of cubic, twilled, and hexagonal, or PBN,
Various materials such as t-BN are known, but hexagonal boron nitride is preferred in the present invention. Hexagonal boron nitride has a high aspect ratio plate (or scale) shape due to its crystal structure, and when added to silicone oil, the lubricating properties of the obtained silicone oil composition and Thermal conductivity can be significantly improved.
【０００９】六方晶の窒化硼素については、シリコーン
オイル組成物の高熱伝導率を達成する為に、高アスペク
ト比で、しかも結晶が発達したものが望ましい。六方晶
の窒化硼素の結晶の発達程度を知る指標としては、次の
黒鉛化指数が公知である。 黒鉛化指数＝（Ｉａ＋Ｉｂ）／Ｉｃ ここで、Ｉａは（１００）、Ｉｂは（１０１）、Ｉｃは
（１０２）のＸ線回折におけるピーク面積を示し、黒鉛
化指数が小さいほど結晶性は良好である。Regarding hexagonal boron nitride, in order to achieve high thermal conductivity of the silicone oil composition, it is desirable that the boron nitride has a high aspect ratio and a crystal is developed. The following graphitization index is known as an index for determining the degree of development of hexagonal boron nitride crystals. Graphitization index = (Ia + Ib) / Ic Here, Ia represents the peak area in X-ray diffraction of (100), Ib is (101), and Ic is (102). The smaller the graphitization index, the better the crystallinity. is there.
【００１０】本発明においては、黒鉛化指数が４．０以
下の窒化硼素に特定するときに、フルオロアルキルシラ
ンによる窒化硼素の樹脂への濡れ性の改善効果が一層達
成でき、その結果、シリコーンオイルと窒化硼素との混
練時の粘度を低くすることができるし、得られるシリコ
ーンオイル組成物も良好な潤滑特性を得る事ができる。
１．５以下がより好ましい範囲である。また、六方晶窒
化硼素の粒子の大きさについては、平均粒子径が５〜１
００μｍの範囲であることが好ましい。In the present invention, when boron nitride having a graphitization index of 4.0 or less is specified, the effect of improving the wettability of boron nitride to a resin by a fluoroalkylsilane can be further achieved. Can be reduced when kneaded with water and boron nitride, and the obtained silicone oil composition can also obtain good lubricating properties.
1.5 or less is a more preferred range. As for the size of the hexagonal boron nitride particles, the average particle diameter is 5 to 1%.
It is preferably in the range of 00 μm.
【００１１】本発明におけるフルオロアルキルシラン
は、化学式ＣＦ3 ＣＨ2 ＣＨ2 Ｓｉ（ＯＲ）3 、ＣＦ3
ＣＨ2 ＣＨ2 ＳｉＣｌ3 、ＣＦ3 （ＣＦ2 ）5 ＣＨ2 Ｃ
Ｈ2 ＳｉＣｌ3 、ＣＦ3 （ＣＦ2 ）5 ＣＨ2 ＣＨ2 Ｓｉ
（ＯＲ）3 、ＣＦ3 （ＣＦ2） 5 ＣＨ2 ＣＨ2 ＳｉＣ
ｌ3 、ＣＦ3 （ＣＦ2 ）7 ＣＨ2 Ｓｉ（ＯＲ）3 、ＣＦ
3 （ＣＦ2 ）7 ＣＨ2 ＳｉＭｅＣｌ2 、ＣＦ3 （ＣＦ
2 ）7 ＣＨ7 ＣＨ2 ＳｉＭｅ （ＯＲ）2 であらわせら
れるものである。ここで、Ｒは炭素数１〜１０程度のア
ルキル基を示す。The fluoroalkylsilane according to the present invention has a chemical formula of CF 3 CH 2 CH 2 Si (OR) 3 , CF 3
CH 2 CH 2 SiCl 3 , CF 3 (CF 2 ) 5 CH 2 C
H 2 SiCl 3 , CF 3 (CF 2 ) 5 CH 2 CH 2 Si
(OR) 3 , CF 3 (CF 2 ) 5 CH 2 CH 2 SiC
l 3 , CF 3 (CF 2 ) 7 CH 2 Si (OR) 3 , CF
3 (CF 2 ) 7 CH 2 SiMeCl 2 , CF 3 (CF
2 ) It can be represented by 7 CH 7 CH 2 SiMe (OR) 2 . Here, R represents an alkyl group having about 1 to 10 carbon atoms.
【００１２】前記フルオロアルキルシランのうち、アル
キル基がメチル基のものは、窒化硼素との親和性が高
く、本発明の目的を達成する上で好ましい。即ち、ＣＦ
3 ＣＨ2 ＣＨ2 Ｓｉ（ＯＭｅ）3 、ＣＦ3 （ＣＦ2 ）5
ＣＨ2 ＣＨ2 Ｓｉ（ＯＭｅ） 3 、ＣＦ3 （ＣＦ2 ）7
ＣＨ2 ＣＨ2 Ｓｉ（ＯＭｅ）3 、ＣＦ3 （ＣＦ2 ）7Ｃ
Ｈ 2 ＣＨ2 ＳｉＭｅ（ＯＭｅ）2 であらわせられるも
のである。ここで、Ｍｅはメ チル基ＣＨ3 −を示す。[0012] Of the above fluoroalkylsilanes,
Those with a methyl kill group have high affinity for boron nitride.
It is preferable to achieve the object of the present invention. That is, CF
ThreeCHTwoCHTwoSi (OMe)Three, CFThree(CFTwo)Five
CHTwoCHTwoSi (OMe) Three , CFThree(CFTwo)7
CHTwoCHTwoSi (OMe)Three, CFThree(CFTwo)7C
HTwoCHTwoSiMe (OMe)TwoCan be exposed
It is. Here, Me is a methyl group CHThreeIndicates-.
【００１３】更に、本発明者らの実験的知見に基づけ
ば、前記フルオロアルキルシランのうちトリメチルシラ
ノール基を有するものが好ましく、特にＣＦ3 （Ｃ
Ｆ2 ）7 ＣＨ2 ＣＨ2 Ｓｉ（ＯＭｅ）3 は窒化硼素の分
散性が特に優れていて、好ましい。Further, based on the experimental findings of the present inventors, among the above fluoroalkylsilanes, those having a trimethylsilanol group are preferable, and particularly, CF 3 (C
F 2 ) 7 CH 2 CH 2 Si (OMe) 3 is preferable because boron nitride has particularly excellent dispersibility.
【００１４】フルオロアルキルシランの窒化硼素への添
加量については、０．１〜１０重量％が好ましい。０．
１重量％未満では、窒化硼素表面への処理効果が充分で
はないことがある。また、１０重量％を超えるとシリコ
ーンオイルの長期安定性等に悪影響を及ぼす恐れが生じ
ることがあるし、経済的にも不利である。窒化硼素に対
して、０．５〜５．０重量％が一層好ましい範囲であ
る。The amount of the fluoroalkylsilane added to boron nitride is preferably 0.1 to 10% by weight. 0.
If it is less than 1% by weight, the effect of treating the boron nitride surface may not be sufficient. If it exceeds 10% by weight, the long-term stability of the silicone oil may be adversely affected, which is economically disadvantageous. A more preferred range is 0.5 to 5.0% by weight based on boron nitride.
【００１５】フルオロアルキルシランの窒化硼素への添
加方法、或いは、フルオロアルキルシランの添加された
窒化硼素をシリコーンオイルに添加する方法について
は、従来公知の無機粉末の表面処理方法が適用できる。
例えば、窒化硼素とフルオロアルキルシランとを直接混
合する乾式法、フルオロアルキルシランを溶解させた溶
剤中に窒化硼素を添加し、充分に攪拌した後に取り出し
て乾燥させる湿式法、前記方法を組み合わせた方法等の
何れの方法にても行うことができる。A method for adding a fluoroalkylsilane to boron nitride, or a method for adding a fluoroalkylsilane to boron nitride
How to add boron nitride to silicone oil
A conventionally known surface treatment method for an inorganic powder can be applied.
For example, a dry method of mixing the boron nitride and the fluoroalkyl silane directly added boron nitride in a solvent to dissolve the fluoroalkyl silane, sufficiently wet type method of drying is taken out after stirring, a combination of the above methods Any method such as a method can be used.
【００１６】フルオロアルキルシランを添加した窒化硼
素は、シリコーンオイル全組成物中に１体積％から５０
体積％添加されるのが一般的であるが、このとき同時に
黒鉛、二硫化モリブデン等の固体潤滑剤、ＰＴＦＥ、カ
ーボン、酸化珪素やリチウム石鹸等の増ちょう剤、酸化
アルミニウム、窒化珪素、酸化亜鉛、或いはＡｕ、Ａｇ
等の熱伝導率改善フィラーを添加してもよい。The boron nitride to which the fluoroalkylsilane is added can be used in an amount of 1% by volume to 50% in the total silicone oil composition.
In general, it is added at the same time by volume, but at the same time, a solid lubricant such as graphite and molybdenum disulfide, a thickener such as PTFE, carbon, silicon oxide and lithium soap, aluminum oxide, silicon nitride, and zinc oxide Or Au, Ag
And the like may be added.
【００１７】[0017]
【実施例】以下、実施例、比較例を基に、本発明を更に
詳細に説明する。 〔実施例１〕メタノール５０ｍｌにフルオロアルキルシ
ラン：ＣＦ3 （ＣＦ2 ）7 ＣＨ2 ＣＨ2 Ｓｉ（ＯＭｅ）
3 （東芝シリコーン社製、商品名：ＸＣ９５−４７０）
を２ 重量％添加した後、マイクロトラックで測定した
平均粒径が２０μｍであり、黒 鉛化係数が０．９８の
窒化硼素４０ｇを添加し、スターラーで２時間攪拌し
た。 その後、溶媒を９０℃の熱水で加熱して乾燥させ
た。The present invention will be described below in more detail with reference to examples and comparative examples. Example 1 Fluoroalkylsilane: CF 3 (CF 2 ) 7 CH 2 CH 2 Si (OMe) in 50 ml of methanol
3 (Toshiba Silicone Co., Ltd., trade name: XC95-470)
Was added, and 40 g of boron nitride having an average particle size of 20 μm measured by a Microtrac and a graphitization coefficient of 0.98 was added, and the mixture was stirred with a stirrer for 2 hours. Thereafter, the solvent was dried by heating with hot water of 90 ° C.
【００１８】シリコーンオイルとしてエポキシ変性シリ
コーンオイル（東レ・ダウコーニング社製：ＳＦ８４１
１）を用い、前述のフルオロアルキルシランで処理した
窒化硼素を２０体積％添加し、攪拌棒にて６０ｒｐｍで
３０ｍｉｎ攪拌してシリコーンオイル組成物とした。シ
リコーンオイル組成物の粘度を、温度４０℃、５ｒｐｍ
で５ｍｉｎ後の条件で、Ｂ型粘度計を用いて測定した。
この結果を表１に示した。Epoxy-modified silicone oil (manufactured by Dow Corning Toray: SF841) as the silicone oil
Using 1), 20% by volume of boron nitride treated with the above-mentioned fluoroalkylsilane was added, and the mixture was stirred with a stirring rod at 60 rpm for 30 minutes to obtain a silicone oil composition. The viscosity of the silicone oil composition was measured at a temperature of 40 ° C and 5 rpm.
And measured using a B-type viscometer under the conditions after 5 minutes.
The results are shown in Table 1.
【００１９】[0019]
【表１】 [Table 1]
【００２０】〔比較例１〕フルオロアルキルシラン処理
を行わないこと以外は、実施例１と同じ操作でシリコー
ンオイル組成物を作製し、粘度を測定した。この結果を
表１に示した。Comparative Example 1 A silicone oil composition was prepared in the same manner as in Example 1 except that the fluoroalkylsilane treatment was not performed, and the viscosity was measured. The results are shown in Table 1.
【００２１】〔比較例２、３〕表面処理剤として、エポ
キシ系シランカップリング剤（信越シリコーン社製、商
品名ＫＢＭ４０３）、アミノ系シランカップリング剤
（信越シリコーン社製、商品名ＫＢＭ６０３）を用いた
こと以外は実施例１と同じ操作でシリコーンオイル組成
物を作製し、粘度を測定した。この結果を表１に示し
た。[Comparative Examples 2 and 3] Epoxy silane coupling agents (trade name KBM403, manufactured by Shin-Etsu Silicone Co.) and amino silane coupling agents (trade name KBM603, manufactured by Shin-Etsu Silicone Co., Ltd.) were used as surface treatment agents. A silicone oil composition was prepared in the same manner as in Example 1 except that the viscosity was not changed, and the viscosity was measured. The results are shown in Table 1.
【００２２】〔実施例２〕マイクロトラックで測定した
平均粒径が７．６μｍであり、黒鉛化係数が１．３３の
窒化硼素粉を用いたこと以外は、実施例１と同じ操作で
シリコーンオイル組成物を作製し、粘度を測定した。こ
の結果を表２に示す。Example 2 The same procedure as in Example 1 was repeated except that a boron nitride powder having an average particle size of 7.6 μm measured by a Microtrac and a graphitization coefficient of 1.33 was used. A composition was prepared and the viscosity was measured. Table 2 shows the results.
【００２３】[0023]
【表２】 [Table 2]
【００２４】〔比較例４〕実施例２において、フルオロ
アルキルシラン処理を行わないこと以外は、実施例２と
同じ操作でシリコーンオイル組成物を作製し、粘度を測
定した。この結果を表２に示す。Comparative Example 4 A silicone oil composition was prepared in the same manner as in Example 2 except that the fluoroalkylsilane treatment was not performed, and the viscosity was measured. Table 2 shows the results.
【００２５】〔実施例３〕マイクロトラックで測定した
平均粒径が２０μｍであり、黒鉛化係数が０．９８の窒
化硼素粉を用い、実施例１と同じ方法にてフルオロアル
キルシランを添加した。前記窒化硼素をグリース状のリ
チウム石鹸系シリコーンオイル組成物中に１．５体積％
となる様に配合し、３段ロールミルにて混合した。Example 3 Fluoroalkylsilane was added in the same manner as in Example 1 using boron nitride powder having an average particle size of 20 μm measured by Microtrac and a graphitization coefficient of 0.98. 1.5% by volume of the boron nitride in a grease-like lithium soap-based silicone oil composition
And mixed by a three-stage roll mill.
【００２６】前記のシリコーンオイル組成物について、
シェル式四球式試験機を用い、ＡＳＴＭＤ４１７２に基
づいて、試験荷重：４０ｋｇｆ，回転速度：１２００ｒ
ｐｍ，グリース温度：７５℃，試験時間：６０ｍｉｎの
条件で摺動試験を行った後、摩耗痕径を測定した。この
結果を表３に示す。With respect to the above silicone oil composition,
Test load: 40 kgf, rotation speed: 1200 r based on ASTM D4172 using a shell-type four-ball testing machine
After performing a sliding test under the conditions of pm, grease temperature: 75 ° C., and test time: 60 minutes, the wear scar diameter was measured. Table 3 shows the results.
【００２７】[0027]
【表３】 [Table 3]
【００２８】〔比較例５〕フルオロアルキルシランを添
加しないこと以外は、実施例３と同じ操作でシリコーン
オイル組成物を作製し、摺動試験を実施した。この結果
を表３に示す。Comparative Example 5 A silicone oil composition was prepared in the same manner as in Example 3 except that no fluoroalkylsilane was added, and a sliding test was performed. Table 3 shows the results.
【００２９】〔実施例４〕マイクロトラックで測定した
平均粒径が１９μｍであり、黒鉛化係数が１．１８の窒
化硼素を用い、実施例１と同じ方法にてフルオロアルキ
ルシランを添加した。前記窒化硼素をグリース状のリチ
ウム石鹸系シリコーンオイル組成物中に５０体積％とな
る様に配合し、３段ロールミルにて混合し、シリコーン
オイル組成物の熱伝導率を定常法にて測定した。この結
果を表４に示す。Example 4 Fluoroalkylsilane was added in the same manner as in Example 1 using boron nitride having an average particle size of 19 μm measured by Microtrac and a graphitization coefficient of 1.18. The boron nitride was blended in a grease-like lithium soap-based silicone oil composition at 50% by volume, mixed with a three-stage roll mill, and the thermal conductivity of the silicone oil composition was measured by a steady-state method. Table 4 shows the results.
【００３０】[0030]
【表４】 [Table 4]
【００３１】〔比較例６〕フルオロアルキルシランを添
加しないこと以外は、実施例２と同じ方法でシリコーン
オイル組成物を作製し、熱伝導率を測定した。この結果
を表４に示す。Comparative Example 6 A silicone oil composition was prepared in the same manner as in Example 2 except that no fluoroalkylsilane was added, and the thermal conductivity was measured. Table 4 shows the results.
【００３２】[0032]
【発明の効果】本発明の窒化硼素は、シリコーンオイル
に対する濡れ性が改善されているので、窒化硼素を添加
したときのシリコーンオイル組成物の粘度上昇が低く抑
えられる特徴を有する。また、本発明のシリコーンオイ
ル組成物は、シリコーンオイルに対する濡れ性の改善さ
れた窒化硼素を含有することにより、窒化硼素が高配合
することができるので、潤滑性、離型性、摺動特性、熱
伝導性等の特性を一層発揮できるという特徴を有してい
る。また、本発明のシリコーンオイル組成物は、前記摺
動特性に優れ、自動車用等速ジョイント用グリースとし
ても十分に使用できる。The boron nitride of the present invention has an improved wettability with respect to silicone oil, and thus has the characteristic that the increase in viscosity of the silicone oil composition when boron nitride is added is suppressed to a low level. In addition, the silicone oil composition of the present invention contains boron nitride having improved wettability with respect to silicone oil, so that boron nitride can be highly blended, so that lubricity, mold release properties, sliding properties, It has the feature that it can further exhibit properties such as thermal conductivity. Further, the silicone oil composition of the present invention is excellent in the above-mentioned sliding properties and can be sufficiently used as grease for a constant velocity joint for automobiles.
───────────────────────────────────────────────────── フロントページの続き (56)参考文献 特開 平11−71521（ＪＰ，Ａ) 特開 平９−215705（ＪＰ，Ａ) 特開 平７−215705（ＪＰ，Ａ) (58)調査した分野(Int.Cl.7，ＤＢ名) C01B 21/064 ＣＡ（ＳＴＮ)────────────────────────────────────────────────── ─── Continuation of the front page (56) References JP-A-11-71521 (JP, A) JP-A-9-215705 (JP, A) JP-A-7-215705 (JP, A) (58) Field (Int. Cl. 7 , DB name) C01B 21/064 CA (STN)
Claims (7)
してなることを特徴とするシリコーンオイル組成物用窒
化硼素。1. A boron nitride for a silicone oil composition comprising a fluoroalkylsilane added to boron nitride.
シラノール基を有することを特徴とする請求項１記載の
シリコーンオイル組成物用窒化硼素。2. The boron nitride for a silicone oil composition according to claim 1, wherein said fluoroalkylsilane has a trimethylsilanol group.
こと特徴とする請求項１または請求２項記載のシリコー
ンオイル組成物用窒化硼素。3. The boron nitride for a silicone oil composition according to claim 1, wherein the graphitization index of the boron nitride is 4.0 or less.
載されたいずれかのシリコーンオイル組成物用窒化硼素
を添加してなることを特徴とするシリコーンオイル組成
物。4. The silicone oil according to claim 1, wherein
Any of the above-listed boron nitride for silicone oil compositions
Silicone oil composition characterized by comprising the addition of.
加してなることを特徴とする請求項４記載のシリコーン
オイル組成物。5. The silicone oil composition according to claim 4, wherein at least one of graphite and molybdenum disulfide is added.
ブラック、ＰＴＦＥ(ポリテトラフルオロエチレン）、
リチウム石鹸の１種以上を添加してなることを特徴とす
る請求項４又は請求項５記載のシリコーンオイル組成
物。6. Silicon oxide, zinc oxide, alumina, carbon black, PTFE (polytetrafluoroethylene),
The silicone oil composition according to claim 4 or 5 , wherein one or more lithium soaps are added.
請求項４又は請求項５記載のシリコーンオイル組成物。7. It is for a constant velocity joint.
The silicone oil composition according to claim 4 or claim 5 .