JP2974873B2 - Adhesive expanded polystyrene particles and expanded polystyrene moldings - Google Patents
Adhesive expanded polystyrene particles and expanded polystyrene moldingsInfo
- Publication number
- JP2974873B2 JP2974873B2 JP5084481A JP8448193A JP2974873B2 JP 2974873 B2 JP2974873 B2 JP 2974873B2 JP 5084481 A JP5084481 A JP 5084481A JP 8448193 A JP8448193 A JP 8448193A JP 2974873 B2 JP2974873 B2 JP 2974873B2
- Authority
- JP
- Japan
- Prior art keywords
- expanded polystyrene
- adhesive
- polystyrene particles
- volume
- molded article
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【０００１】[0001]
【産業上の利用分野】本発明は、栽培床、地面の覆い、
造花・切花の固定部材、インテリア・ディスプレイ用基
材、タタミ床、床材、壁材等の建築用の資材に用いられ
る粘着性発泡ポリスチレン粒子および発泡ポリスチレン
成形体に関するものである。The present invention relates to a cultivation floor, a ground covering,
The present invention relates to adhesive foamed polystyrene particles and foamed polystyrene moldings used as architectural materials such as fixing members for artificial flowers and cut flowers, base materials for interior displays, tatami floors, flooring materials, wall materials, and the like.
【０００２】[0002]
【従来の技術】従来より、魚箱、包装容器、インテリア
・ディスプレイ用基材、タタミ床、床材、壁材等には、
発泡ポリスチレンからなる発泡体成形品が広く使用され
ている。2. Description of the Related Art Conventionally, fish boxes, packaging containers, base materials for interior displays, tatami floors, flooring materials, wall materials, etc.
A foam molded article made of expanded polystyrene is widely used.
【０００３】上記発泡体成形品は、押出発泡体、また
は、ビーズ状の発泡ポリスチレンをそのまま、あるいは
予備発泡したものを所望の形状を有する金型に入れて、
熱加圧成形を行うことによって得られる。[0003] The above-mentioned foam molded article is prepared by extruding an extruded foam or bead-like expanded polystyrene as it is or pre-expanded into a mold having a desired shape.
It is obtained by performing hot pressing.
【０００４】また、上記発泡体成形品は、使用後その廃
棄物としての生成量も大量になっており、そこで、上記
発泡ポリスチレンからなる発泡体成形品の廃棄物の処理
方法の一つとして、廃棄物を粉砕して粒状あるいはチッ
プ状にしたもの（以下、発泡ポリスチレン粒子と称す
る）を所定形状に成形して再利用することが考えられて
いる。[0004] In addition, the above-mentioned foam molded article has a large amount of waste as a waste after use. Therefore, one of the methods of treating the waste of the foam molded article made of the expanded polystyrene is as follows. It has been considered to recycle waste by pulverizing waste into granules or chips (hereinafter referred to as expanded polystyrene particles) into a predetermined shape.
【０００５】[0005]
【発明が解決しようとする課題】そこで、上記の発泡ポ
リスチレン粒子から発泡体成形品を成形するには、上記
発泡ポリスチレン粒子に溶剤型接着剤を混合して成形す
る方法、発泡ポリスチレン粒子にエマルジョン接着剤の
みを混合して成形する方法等が考えられる。Therefore, in order to form a foam molded article from the above-mentioned expanded polystyrene particles, a method of mixing a solvent-type adhesive with the above-mentioned expanded polystyrene particles and forming the mixture is described below. For example, a method in which only the agent is mixed and molded is considered.
【０００６】しかしながら、発泡ポリスチレン粒子に溶
剤型接着剤を混合して成形する方法では、溶剤型接着剤
の接着力によって即座に発泡ポリスチレン粒子同士が接
着して固化し、さらに、発泡ポリスチレン粒子が溶解し
て収縮するので、その成形体は、所定の形状を維持する
ことができないという問題が生じる。[0006] However, in the method of mixing the foamed polystyrene particles with the solvent-based adhesive to form the foamed polystyrene particles, the foamed polystyrene particles are immediately adhered and solidified by the adhesive force of the solvent-based adhesive, and the foamed polystyrene particles are dissolved. As a result, the molded body cannot maintain a predetermined shape.
【０００７】また、発泡ポリスチレン粒子にエマルジョ
ン接着剤のみを混合して成形する方法では、エマルジョ
ン接着剤に含まれる多量の水分のために、発泡ポリスチ
レン粒子同士を接着させることができず、成形型内で加
圧成形しただけでは所定の形状を維持させることができ
ない。このため、発泡ポリスチレン粒子同士を接着させ
るには、上記の成形型内に加熱手段を設け、加圧成形時
に加熱して水分を蒸発させる必要がある。これによっ
て、発泡体成形品の成形工程が煩雑なものとなるので、
種々の形状の発泡体成形品を容易に成形することができ
ないという問題が生じる。Further, in the method of molding by mixing only the emulsion adhesive with the expanded polystyrene particles, the expanded polystyrene particles cannot be adhered to each other due to a large amount of water contained in the emulsion adhesive, so that the molding die cannot be used. However, it is not possible to maintain a predetermined shape only by pressure molding. For this reason, in order to adhere the expanded polystyrene particles to each other, it is necessary to provide a heating means in the above-mentioned molding die and to evaporate water by heating at the time of pressure molding. This makes the molding process of the foam molded article complicated,
There arises a problem that foam molded articles of various shapes cannot be easily molded.
【０００８】そこで、本発明は、鋭意研究を重ねた結
果、エマルジョン接着剤に、更に、微細連通気孔の無機
物体を混合することによって、上記問題点を解明でき得
ることを知見したものであり、その目的は、発泡ポリス
チレン粒子を容易に接着させることによって、種々の形
状の成形体を容易に成形することができる粘着性発泡ポ
リスチレン粒子およびこれによって得られた発泡ポリス
チレン成形体を提供することにある。Accordingly, the present inventors have conducted intensive studies and found that the above problem can be solved by further mixing an inorganic substance having fine pores with an emulsion adhesive. An object of the present invention is to provide an adhesive foamed polystyrene particle capable of easily molding molded articles of various shapes by easily adhering foamed polystyrene particles, and an expanded polystyrene molded article obtained thereby. .
【０００９】[0009]
【課題を解決するための手段】請求項１記載の発明の粘
着性発泡ポリスチレン粒子は、発泡ポリスチレン粒子
と、エマルジョン接着剤１種または２種以上の混合接着
剤と、少なくとも、微細連通気孔を有する粉体状の無機
物質、または、連通気孔を有する短繊維状もしくは粒状
の有機物質とを混合してなることを特徴とするものであ
る。The pressure-sensitive adhesive expanded polystyrene particles according to the first aspect of the present invention have expanded polystyrene particles, one or more emulsion adhesives, and at least fine interconnected pores. It is characterized by being mixed with a powdery inorganic substance or a short-fiber or granular organic substance having continuous air holes.
【００１０】請求項２記載の発明の発泡ポリスチレン成
形体は、請求項１記載の粘着性発泡ポリスチレン粒子を
加圧成形してなることを特徴とするものである。A foamed polystyrene molded article according to a second aspect of the invention is characterized by being formed by pressure-forming the pressure-sensitive adhesive polystyrene particles according to the first aspect.
【００１１】ここで、上記発泡ポリスチレン粒子には、
発泡ポリスチレンに、プロパン、ブタン、ペンタン等の
発泡剤を配合してビーズ状にしたもの、もしくは発泡ポ
リスチレンの成形品等の使用後の廃棄物を粉砕して得ら
れる粒状あるいはチップ状にしたもの等（以下、発泡ポ
リスチレン粒子と称する）が使用されるが、廃棄物の処
理および有効利用という観点から、この使用後の廃棄物
から得られる発泡ポリスチレン粒子が好適に使用され
る。また、発泡ポリスチレン粒子の発泡倍率は特に限定
しないが、３０〜５０倍のものが使用される。Here, the expanded polystyrene particles include:
Expanded polystyrene mixed with a foaming agent such as propane, butane, pentane and the like to form beads, or granules or chips obtained by crushing used waste such as molded articles of expanded polystyrene, etc. (Hereinafter referred to as expanded polystyrene particles), and expanded polystyrene particles obtained from the used waste are preferably used from the viewpoint of waste treatment and effective utilization. Further, the expansion ratio of the expanded polystyrene particles is not particularly limited, but a expansion ratio of 30 to 50 times is used.
【００１２】尚、上記発泡ポリスチレン粒子は、軽量
化、弾力性を付与するとともに、独立気泡からなるた
め、成形体に保温・断熱性、防音性を付与するようにな
っている。The expanded polystyrene particles are not only lightweight and elastic, but also made of closed cells, so that the molded body is provided with heat retention, heat insulation, and sound insulation.
【００１３】また、上記エマルジョン接着剤には、大き
く分けてゴムラテックスと合成樹脂エマルジョンとがあ
る。このうち、上記ゴムラテックスの成分としては、天
然ゴム、合成ゴム等があり、一方、合成樹脂エマルジョ
ンの成分としては、ポリ酢酸ビニル、ポリエチレン、酢
酸ビニル・アクリル共重合体、ポリアクリル酸エステ
ル、スチレン・酢酸ビニル共重合体、スチレン・アクリ
ル共重合体等が挙げられる。The above-mentioned emulsion adhesives are roughly classified into rubber latex and synthetic resin emulsion. Among them, the rubber latex component includes natural rubber and synthetic rubber, while the synthetic resin emulsion component includes polyvinyl acetate, polyethylene, vinyl acetate / acrylic copolymer, polyacrylic acid ester, and styrene. -Vinyl acetate copolymer, styrene-acrylic copolymer, etc.
【００１４】そこで、発泡ポリスチレン粒子に１種類の
エマルジョン接着剤を配合する場合には、ゴムラッテク
ス接着剤を使用し、２種類以上のエマルジョン接着剤を
混合して配合する場合には、ゴムラテックス接着剤と合
成樹脂エマルジョン接着剤とを混合したものを使用する
のが好ましい。Therefore, when one kind of emulsion adhesive is mixed with the expanded polystyrene particles, a rubber latex adhesive is used, and when two or more kinds of emulsion adhesives are mixed and compounded, rubber latex adhesive is used. It is preferable to use a mixture of an agent and a synthetic resin emulsion adhesive.
【００１５】上記ゴムラテックスは、発泡ポリスチレン
粒子の接着剤として作用するものであり、その成分濃度
は、５〜５０重量％程度が好ましく、５重量％を超えて
濃度が低くなりすぎると、接着が不十分となり、所望の
粘着性発泡ポリスチレン粒子を得ることができず、これ
による成形体をも得ることが困難となる。逆に、５０重
量％を超えて濃度が高くなりすぎると、粘度が大きくな
って発泡ポリスチレン粒子との混合が不均一となり、こ
の場合においても、所望の粘着性発泡ポリスチレン粒子
を得ることができず、これによる成形体を安定して得る
ことが困難となる。The rubber latex acts as an adhesive for the expanded polystyrene particles, and its component concentration is preferably about 5 to 50% by weight, and if the concentration exceeds 5% by weight, the adhesion becomes too low. Insufficiently, it is not possible to obtain desired adhesive foamed polystyrene particles, and it is difficult to obtain a molded article by this. Conversely, if the concentration exceeds 50% by weight and the concentration is too high, the viscosity will increase and the mixing with the expanded polystyrene particles will be non-uniform. In this case also, the desired adhesive expanded polystyrene particles cannot be obtained. This makes it difficult to obtain a molded body stably.
【００１６】また、上記合成樹脂エマルジョンは、上記
ゴムラテックス接着剤と共に使用することが好ましく、
成形体の硬さ、および形状安定性を向上させるものであ
る。それゆえ、発泡ポリスチレン粒子に接着剤としてゴ
ムラッテクス接着剤のみを配合したものよりもゴムラテ
ックス接着剤に合成樹脂エマルジョンを配合した混合接
着剤を配合するのが好ましい。しかしながら、合成樹脂
エマルジョンの濃度が高くなれば、ゴムラテックス接着
剤による接着性を低下させることになるため、出来る限
り配合量を抑える必要がある。The above synthetic resin emulsion is preferably used together with the above rubber latex adhesive.
The purpose is to improve the hardness and shape stability of the molded body. Therefore, it is preferable to mix a rubber latex adhesive with a synthetic resin emulsion and a synthetic resin emulsion rather than a rubber latex adhesive alone as an adhesive with foamed polystyrene particles. However, when the concentration of the synthetic resin emulsion increases, the adhesiveness of the rubber latex adhesive decreases, so that it is necessary to reduce the compounding amount as much as possible.
【００１７】尚、ゴムラテックス接着剤としては、発泡
ポリスチレン粒子の接着性および粘着性等から考慮し
て、天然ゴムを使用した天然ゴムラッテクスが好まし
い。一方、合成樹脂エマルジョン接着剤としては、ゴム
ラテックスの接着性の低下に影響が比較的少ない、ポリ
酢酸ビニルが好ましい。As the rubber latex adhesive, natural rubber latex using natural rubber is preferable in consideration of the adhesiveness and tackiness of the expanded polystyrene particles. On the other hand, as the synthetic resin emulsion adhesive, polyvinyl acetate, which has relatively little effect on the decrease in the adhesion of the rubber latex, is preferable.
【００１８】また、上記発泡ポリスチレン粒子１００容
量部に対する上記エマルジョン接着剤１種または２種以
上の混合接着剤の配合量は、使用目的、発泡ポリスチレ
ン粒子の粒径等によって異なるが、概ね０．５〜２０容
量部の範囲内である。The blending amount of one or more of the above-mentioned emulsion adhesives with respect to 100 parts by volume of the expanded polystyrene particles varies depending on the purpose of use, the particle size of the expanded polystyrene particles, and the like. It is in the range of ２０20 parts by volume.
【００１９】但し、上記エマルジョン接着剤の配合量が
０．５容量部未満の場合には、接着強度が不十分にな
る。一方、２０容量部を上回る場合には、余剰の接着剤
が発泡ポリスチレン粒子間に入り込み、粘着性発泡ポリ
スチレン粒子同士が結合するので、後に所定形状の成形
体を得ることが困難となる。However, if the amount of the emulsion adhesive is less than 0.5 part by volume, the adhesive strength becomes insufficient. On the other hand, if it exceeds 20 parts by volume, the surplus adhesive enters between the expanded polystyrene particles, and the adhesive expanded polystyrene particles are bonded to each other, so that it is difficult to obtain a molded article having a predetermined shape later.
【００２０】また、上記微細連通気孔を有する粉体状の
無機物質としては、上記エマルジョン接着剤を吸収し、
粘着性発泡ポリスチレン粒子同士の結合を防止するもの
であり、例えば、ゼオライト、セビオライト、パーライ
ト、活性白土、硅藻土、石炭灰、活性炭、セメント、酸
化鉄、各種集塵灰からなる粉体が挙げられるが、脱臭
能、吸着能、吸水能、成分安定性等の点から、上記ゼオ
ライトのうち天然ゼオライトが好適に使用される。この
天然ゼオライトは、その大きな塩基置換容量により、土
壌中での肥効調整、ＰＨ調整等の機能をも有しているの
で、この天然ゼオライトを配合した発泡ポリスチレン粒
子は、そのまま土壌シート等として好適に使用すること
ができる。Further, as the powdered inorganic substance having the fine communicating holes, the powdery inorganic substance absorbs the emulsion adhesive,
It is intended to prevent the bonding between the adhesive expanded polystyrene particles, and examples thereof include zeolite, sebiolite, perlite, activated clay, diatomaceous earth, coal ash, activated carbon, cement, iron oxide, and powders composed of various dust ash. However, among the above zeolites, natural zeolites are preferably used in terms of deodorizing ability, adsorption ability, water absorbing ability, component stability and the like. Because this natural zeolite also has functions such as fertilizer effect adjustment and pH adjustment in soil due to its large base substitution capacity, expanded polystyrene particles containing this natural zeolite are suitable as soil sheets and the like as they are. Can be used for
【００２１】尚、上記無機物質の粒径は、０．０１μｍ
〜１．５ｍｍ程度が好ましく、また、その比表面積は、
エマルジョン接着剤を吸収するために、また、適正な脱
臭能、吸着能、吸水能等を発揮させるために、３０００
〜１０００００ｃｍ2 ／ｇ程度であることが好ましい
が、粒径、比表面積共にこれに限定するものではない。The particle size of the inorganic substance is 0.01 μm
About 1.5 mm is preferable, and the specific surface area is
In order to absorb the emulsion adhesive and to exhibit proper deodorizing ability, adsorption ability, water absorbing ability, etc., 3000
It is preferably about 100000 cm 2 / g, but both the particle size and the specific surface area are not limited thereto.
【００２２】但し、上記無機質の粉体の粒径が０．０１
μｍ以下、且つ、比表面積が１０００００ｃｍ2 ／ｇを
上回る場合は、発泡ポリスチレン粒子やエマルジョン接
着剤との混合が不均一となり、発泡ポリスチレン粒子間
の接着が不十分となる傾向にある。一方、粒径が１．５
ｍｍを上回り、且つ、比表面積が３０００ｃｍ2 ／ｇ未
満の場合は、上記無機物質の使用量が多くなるにつれ
て、無機物質が発泡ポリスチレン粒子の接着面に余剰に
入り込み、接着を困難なものとしている。これを無理に
接着させようとすれば、多量のエマルジョン接着剤が必
要となり、粘着性発泡ポリスチレン粒子の製造に係る費
用が増加するという問題が生じる。However, the particle diameter of the inorganic powder is 0.01
If it is not more than μm and the specific surface area exceeds 100,000 cm 2 / g, the mixing with the expanded polystyrene particles and the emulsion adhesive tends to be uneven, and the adhesion between the expanded polystyrene particles tends to be insufficient. On the other hand, when the particle size is 1.5
mm and the specific surface area is less than 3000 cm 2 / g, as the amount of the inorganic material used increases, the inorganic material excessively enters the bonding surface of the expanded polystyrene particles, making the bonding difficult. . If this is to be forcibly bonded, a large amount of an emulsion adhesive is required, which causes a problem that the cost for producing the sticky expanded polystyrene particles increases.
【００２３】また、上記発泡ポリスチレン粒子１００容
量部に対する上記無機物質、または、有機物質の配合量
は、使用目的、発泡ポリスチレン粒子の粒径等によりそ
の都度異なるが、概ね０．１〜５０容量部が好ましく、
特に、無機物質では、０．１〜１５容量部が好ましい。The amount of the inorganic or organic substance per 100 parts by volume of the expanded polystyrene particles may vary depending on the purpose of use, the particle size of the expanded polystyrene particles, etc., but generally ranges from 0.1 to 50 parts by volume. Is preferred,
In particular, for an inorganic substance, 0.1 to 15 parts by volume is preferable.
【００２４】但し、上記無機質の配合量が０．１容量部
を下回る場合には、接着剤の助長作用が低減し、１５容
量部を上回る場合には、発泡ポリスチレン粒子間に無機
物質が余剰に入り込むので、何れの場合においても、発
泡ポリスチレン粒子の粘着性が不十分となる。従って、
これを用いて成形体を成形する場合、発泡ポリスチレン
粒子同士の接着が不十分となるので、成形体の形状安定
性が低下し、外圧等により容易に崩壊する恐れがある。
また、上記有機物質の配合量が０．１容量部を下回る場
合、または、５０容量部を上回る場合には、上記の無機
物質の場合と同じ理由から、発泡ポリスチレン粒子の粘
着性が不十分となる。However, when the amount of the inorganic material is less than 0.1 part by volume, the promoting action of the adhesive is reduced, and when the amount is more than 15 parts by volume, the inorganic material is excessively added between the expanded polystyrene particles. In any case, the adhesiveness of the expanded polystyrene particles becomes insufficient. Therefore,
When a molded article is molded using this, the adhesion between the expanded polystyrene particles becomes insufficient, so that the shape stability of the molded article is reduced, and the molded article may be easily collapsed by external pressure or the like.
When the amount of the organic substance is less than 0.1 part by volume, or when the amount is more than 50 parts by volume, the adhesiveness of the expanded polystyrene particles is insufficient for the same reason as the case of the inorganic substance. Become.
【００２５】また、上記連通気孔を有する短繊維状もし
くは粒状の有機物質としては、ピートモス等の天然有機
物質、バーク堆肥、油粕、籾殻、シイタケのホダ木、オ
ガクズ、およびコーヒー、サトウキビ、ビール等の絞り
粕の醗酵堆肥等が挙げられる。Examples of the short-fiber or granular organic substances having the continuous air holes include natural organic substances such as peat moss, bark compost, oil cake, rice husk, shiitake mushroom tree, sawdust, coffee, sugarcane, beer and the like. Fermentation compost of pomace cake and the like can be mentioned.
【００２６】尚、上記連通気孔を有する短繊維状もしく
は粒状の有機物質は、エマルジョン接着剤を吸収するた
めに、短繊維の場合、長さが０．１〜５ｍｍ程度、粒状
の場合、粒径が０．０１〜１ｍｍ程度が好ましいが、こ
れらの数値範囲に限定するものではない。The short-fiber or granular organic substance having the continuous air holes has a length of about 0.1 to 5 mm in the case of a short fiber and a particle size in the case of a granular material in order to absorb the emulsion adhesive. Is preferably about 0.01 to 1 mm, but is not limited to these numerical ranges.
【００２７】但し、短繊維状の有機物質の長さが０．１
ｍｍよりも短い場合、もしくは粒状の有機物質の粒径が
０．０１ｍｍよりも小さい場合には、発泡ポリスチレン
粒子または接着剤との混合が不均一となり、発泡ポリス
チレン粒子同士の接着が不十分となる傾向にある。一
方、短繊維状の有機物質の長さが５ｍｍよりも長い場
合、もしくは粒状の有機物質の粒径が１ｍｍよりも大き
い場合には、上記有機物質の使用量が多くなるととも
に、有機物質が接着面に余剰に入り込み、接着を困難な
ものとしている。したがって、これを無理に接着させよ
うとすれば、多量のエマルジョン接着剤が必要となり、
粘着性発泡ポリスチレン粒子の製造に係る費用が増加す
るとう問題が生じる。However, the length of the short fibrous organic substance is 0.1
mm, or when the particle size of the granular organic substance is smaller than 0.01 mm, the mixing with the expanded polystyrene particles or the adhesive becomes uneven, and the adhesion between the expanded polystyrene particles becomes insufficient. There is a tendency. On the other hand, when the length of the short fibrous organic substance is longer than 5 mm, or when the particle size of the granular organic substance is larger than 1 mm, the amount of the organic substance used increases and the organic substance adheres. The surface penetrates excessively, making bonding difficult. Therefore, if you try to forcibly adhere this, a large amount of emulsion adhesive is required,
A problem arises in that the cost associated with the production of sticky expanded polystyrene particles increases.
【００２８】また、上記有機物質として１種のみではな
く、例えば、有機顔料を添加することによって、所望す
る色調にすることができ、また、ポリビニルアルコール
を添加することによって、調湿機能を持たせることがで
きる等、各種機能を有する発泡ポリスチレン成形体にす
ることが可能となる。Further, not only one kind of the organic substance but also a desired color tone can be obtained by adding an organic pigment, for example, and a moisture control function can be provided by adding polyvinyl alcohol. For example, it is possible to obtain a foamed polystyrene molded article having various functions.
【００２９】また、発泡ポリスチレン粒子には、上述の
ように、微細連通気孔を有する無機物質粉体あるいは、
連通気孔を有する短繊維状もしくは粒状の有機物質の何
れか一方のみを配合しているが、これに限定することな
く、上記無機物質と有機物質とを混合したものを配合し
ても良い。As described above, the expanded polystyrene particles may be made of an inorganic material powder having fine communicating pores or
Although only one of the short-fiber or granular organic substances having continuous air holes is blended, the present invention is not limited to this, and a mixture of the above-mentioned inorganic substance and organic substance may be blended.
【００３０】また、本発明の粘着性発泡ポリスチレン粒
子および発泡ポリスチレン成形体は、以下のように製造
される。The adhesive foamed polystyrene particles and foamed polystyrene molded article of the present invention are produced as follows.
【００３１】まず、発泡ポリスチレン粒子に、エマルジ
ョン接着剤であるゴムラテックス接着剤または、ゴムラ
テックス接着剤と合成樹脂エマルジョン接着剤の混合接
着剤を加え、発泡ポリスチレン粒子表面に上記接着剤が
十分に塗布されるまで撹拌混合する。First, a rubber latex adhesive, which is an emulsion adhesive, or a mixed adhesive of a rubber latex adhesive and a synthetic resin emulsion adhesive is added to the expanded polystyrene particles, and the adhesive is sufficiently applied to the surface of the expanded polystyrene particles. Stir and mix until done.
【００３２】次いで、この混合物を撹拌しつつ、所定量
の微細連通気孔を有する粉体状の無機物質あるいは連通
気孔を有する短繊維状もしくは粒状の有機物質を添加
し、さらに、均一に撹拌混合して個々の粒子に分割され
た粘着性発泡ポリスチレン粒子を生成する。Next, while stirring the mixture, a predetermined amount of a powdery inorganic substance having fine communicating pores or a short fiber or granular organic substance having communicating pores is added, and the mixture is further uniformly stirred and mixed. To produce cohesive expanded polystyrene particles that are divided into individual particles.
【００３３】次に、この粘着性発泡ポリスチレン粒子を
指圧によって成形するか、もしくは所望する形状を有す
る成型容器にいれて指圧程度（０．３ｋｇ／ｃｍ2 ）以
上で加圧成形し、加圧状態を直ぐに開放して、所望の発
泡ポリスチレン成形体を得る。Next, the pressure-sensitive adhesive expanded polystyrene particles are molded by finger pressure, or placed in a molding container having a desired shape, and pressure-molded at about a finger pressure (0.3 kg / cm 2 ) or more. Is immediately released to obtain a desired foamed polystyrene molded article.
【００３４】尚、上記無機物質および有機物質は、何れ
か一方を添加しているが、上述したように、無機物質と
有機物質とを混合したものを添加してもよい。Although either one of the inorganic substance and the organic substance is added, a mixture of an inorganic substance and an organic substance may be added as described above.
【００３５】[0035]
【作用】請求項１記載の構成により、発泡ポリスチレン
粒子に混合された微細連通気孔を有する粉体状の無機物
質、または、連通気孔を有する短繊維状もしくは粒状の
有機物質によって、エマルジョン接着剤に含まれる水分
が吸収されるので、発泡ポリスチレン粒子は個々に分割
された状態で、その表面が、接着剤の初期乾燥状態と同
様な状態、つまり粘着状態となる。このことから、常温
でしかも僅かな圧力、例えば指圧（０．５ｋｇ／ｃ
ｍ2 ）程度の押圧力によっても発泡ポリスチレン粒子同
士を接着させることが可能となり、所望する形状にする
ために、高温高圧にする必要がなく、また、特別な金
型、加熱装置等を用いなくてもよく、粘着性発泡ポリス
チレン粒子の成形体を容易に成形することができる。According to the first aspect of the present invention, an emulsion adhesive is formed by mixing a powdered inorganic substance having fine open pores mixed with expanded polystyrene particles or a short fiber or granular organic substance having open pores. Since the contained moisture is absorbed, the expanded polystyrene particles are individually divided, and the surface thereof is in a state similar to the initial dry state of the adhesive, that is, a tacky state. From this, at room temperature and with a slight pressure, for example, acupressure (0.5 kg / c
m 2 ), the expanded polystyrene particles can be bonded to each other even with a pressing force of about m 2 ). In order to obtain a desired shape, there is no need to apply high temperature and high pressure, and there is no need to use a special mold or heating device. Alternatively, the molded article of the sticky expanded polystyrene particles can be easily molded.
【００３６】請求項２記載の構成により、請求項１記載
の粘着性発泡ポリスチレン粒子を加圧成形するだけで所
定の形状の成形体を得ることができる。また、粘着性発
泡ポリスチレン粒子に含まれる無機物質、または、有機
物質が、既にエマルジョン接着剤の水分を吸収した状態
となっているので、時間が経過すれば、さらに、エマル
ジョン接着剤の水分が乾燥して粘着性が増し発泡ポリス
チレン粒子同士の接着力がより強固なものとなる。これ
によって、外圧により容易に崩壊することなく、成形体
の形状を安定して維持することができる。According to the constitution of the second aspect, a molded article having a predetermined shape can be obtained only by pressure-forming the pressure-sensitive adhesive expanded polystyrene particles of the first aspect. In addition, since the inorganic or organic substance contained in the adhesive foamed polystyrene particles has already absorbed the moisture of the emulsion adhesive, the moisture of the emulsion adhesive further dries after a lapse of time. As a result, the adhesiveness increases, and the adhesive force between the expanded polystyrene particles becomes stronger. Thereby, the shape of the molded body can be stably maintained without easily collapsing due to external pressure.
【００３７】[0037]
【実施例】本発明の各実施例を以下に示す。EXAMPLES Examples of the present invention will be described below.
【００３８】〔実施例１〕発泡ポリスチレン粒子１００
容量部に、エマルジョン接着剤として、濃度１７．４重
量％の天然ゴムラテックス（商品名：ポリゾールＰＡ−
８、昭和高分子株式会社製）３．６容量部を加え、充分
に撹拌混合した。Example 1 Expanded polystyrene particles 100
In the volume part, as an emulsion adhesive, a natural rubber latex having a concentration of 17.4% by weight (trade name: Polysol PA-
8, 3.6 parts by volume, manufactured by Showa Polymer Co., Ltd.), and the mixture was sufficiently stirred and mixed.
【００３９】次に、生成した混合物を撹拌しつつ、微細
連通気孔を有する粉体状の無機物質として、粒径１μｍ
〜０．３ｍｍの天然ゼオライト（商品名：ＺＯ＃７０：
日東粉化工業株式会社製）１．６容量部を加えた後、さ
らに、充分撹拌混合して粘着性発泡ポリスチレン粒子を
得た。Next, while stirring the resulting mixture, a powdery inorganic substance having fine communicating pores having a particle size of 1 μm
~ 0.3 mm natural zeolite (trade name: ZO # 70:
After adding 1.6 parts by volume (manufactured by Nitto Powder Chemical Co., Ltd.), the mixture was further sufficiently stirred and mixed to obtain adhesive foamed polystyrene particles.
【００４０】この粘着性発泡ポリスチレン粒子１５０ｇ
を成型機の型枠（幅７．５ｃｍ×長さ１９．５ｃｍ×高
さ８．０ｃｍ＝容積１１７０ｃｍ3 ）に充填し、０．５
ｋｇ／ｃｍ2 の押圧力で２分間加圧し、その後、型枠か
ら取り外し、成形体を得た。この成形体の体積は、約１
５８７ｃｍ3 であった。また、加圧時の体積が１１７０
ｃｍ3 で加圧後の体積が約１５８７ｃｍ3 であるので、
この成形体の膨張倍率は、約１．３５６であった。150 g of the adhesive expanded polystyrene particles
Was filled into a mold frame (width 7.5 cm × length 19.5 cm × height 8.0 cm = volume 1170 cm 3 ) of a molding machine, and 0.5
Pressing was performed with a pressing force of kg / cm 2 for 2 minutes, and then removed from the mold to obtain a molded body. The volume of this compact is about 1
587 cm 3 . Further, the volume at the time of pressurization is 1170
Since the volume after pressing in cm 3 is about 1587 cm 3,
The expansion ratio of this molded product was about 1.356.
【００４１】さらに、上記成形体を６０℃に設定した乾
燥器内で一時間乾燥させた後、発泡ポリスチレン成形体
を得た。このとき、発泡ポリスチレン成形体の体積収縮
はなく、嵩密度は約０．０５ｇ／ｃｍ3 であった。Further, the molded article was dried in a dryer set at 60 ° C. for one hour to obtain a foamed polystyrene molded article. At this time, there was no volume shrinkage of the foamed polystyrene molded body, and the bulk density was about 0.05 g / cm 3 .
【００４２】〔実施例２〕発泡ポリスチレン粒子１００
容量部に、エマルジョン接着剤として、濃度２９．０重
量％の天然ゴムラテックス（商品名：ポリゾールＰＡ−
８、昭和高分子株式会社製）と濃度２４．０重量％のポ
リ酢酸ビニルエマルジョン（商品名：ポリゾール１３１
０、昭和高分子株式会社製）を１：１の割合で混合した
混合接着剤３．６容量部を加え、充分に撹拌混合した。Example 2 Expanded polystyrene particles 100
In the volume part, 29.0% by weight of natural rubber latex (trade name: Polysol PA-) was used as an emulsion adhesive.
8. Showa Polymer Co., Ltd.) and a polyvinyl acetate emulsion having a concentration of 24.0% by weight (trade name: Polysol 131)
And 3.6 parts by volume of a 1: 1 mixture of Showa Kogaku Co., Ltd.), and mixed thoroughly.
【００４３】次に、生成した混合物を撹拌しつつ、微細
連通気孔を有する粉体状の無機物質として、粒径１μｍ
〜０．３ｍｍの天然ゼオライト（商品名：ＺＯ＃７０：
日東粉化工業株式会社製）１．９容量部と黒色粉末顔料
０．３容量部を加えた後、さらに、充分撹拌混合して粘
着性発泡ポリスチレン粒子を得た。Next, while stirring the resulting mixture, a powdery inorganic substance having fine interconnected pores having a particle diameter of 1 μm
~ 0.3 mm natural zeolite (trade name: ZO # 70:
After adding 1.9 parts by volume of Nitto Powder Chemical Industry Co., Ltd. and 0.3 parts by volume of the black powder pigment, the mixture was sufficiently stirred and mixed to obtain adhesive foamed polystyrene particles.
【００４４】この粘着性発泡ポリスチレン粒子１７０ｇ
を前記実施例１で使用した成型機の型枠（容積：１１７
０ｃｍ3 ）に充填し、０．５ｋｇ／ｃｍ2 の押圧力で２
分間加圧し、その後、型枠から取り外し、成形体を得
た。この成形体の体積は、約１６３１ｃｍ3 であった。
また、加圧時の体積が１１７０ｃｍ3 で加圧後の体積が
約１６３１ｃｍ3 であるので、この成形体の膨張倍率
は、約１．３９４であった。170 g of the adhesive expanded polystyrene particles
Of the molding machine used in Example 1 (volume: 117)
It was filled in 0 cm 3), 2 by the pressing force of 0.5 kg / cm 2
For about one minute, and then removed from the mold to obtain a molded body. The volume of this compact was about 1631 cm 3 .
Further, since the volume at the time of pressurization was 1170 cm 3 and the volume after pressurization was about 1631 cm 3 , the expansion ratio of this molded product was about 1.394.
【００４５】さらに、上記成形体を６０℃に設定した乾
燥器内で一時間乾燥させた後、発泡ポリスチレン成形体
を得た。このとき、発泡ポリスチレン成形体の体積収縮
はなく、嵩密度は約０．０６ｇ／ｃｍ3 であった。Further, the molded article was dried in a dryer set at 60 ° C. for one hour to obtain a foamed polystyrene molded article. At this time, there was no volume shrinkage of the expanded polystyrene molded article, and the bulk density was about 0.06 g / cm 3 .
【００４６】〔実施例３〕発泡ポリスチレン粒子１００
容量部に、エマルジョン接着剤として、濃度１１．５重
量％の天然ゴムラテックス（商品名：ポリゾールＰＡ−
８、昭和高分子株式会社製）７．５容量部を加え、充分
に撹拌混合した。Example 3 Expanded polystyrene particles 100
A 11.5% by weight natural rubber latex (trade name: Polysol PA-) was used as an emulsion adhesive in the volume part.
8, manufactured by Showa Polymer Co., Ltd.), and 7.5 parts by volume were added thereto, followed by sufficiently stirring and mixing.
【００４７】次に、生成した混合物を撹拌しつつ、連通
気孔を有する短繊維状の有機物質として、繊維長さ０．
１〜５ｍｍのピートモス（カナダ産、見掛比重０．０
７）２０容量部を加えた後、さらに、充分撹拌混合して
粘着性発泡ポリスチレン粒子を得た。Next, while stirring the resulting mixture, a short fibrous organic substance having continuous air holes is used to obtain a fiber having a fiber length of 0.1 mm.
1-5mm peat moss (Canada, apparent specific gravity 0.0
7) After adding 20 parts by volume, the mixture was sufficiently stirred and mixed to obtain sticky expanded polystyrene particles.
【００４８】さらに、根腐れ防止用に天然ゼオライト細
粒（粒径０．３〜１ｍｍ程度）を加えて、押圧してシー
トに成形して、人工土壌シートとして有用であり、特に
軽量化が臨まれる屋上スペース等の緑化用に効果を発揮
する。Further, natural zeolite fine granules (particle size: about 0.3 to 1 mm) are added to prevent root rot and pressed to form a sheet, which is useful as an artificial soil sheet. It is effective for greening rooftop spaces.
【００４９】〔実施例４〕 発泡ポリスチレン粒子１００容量部に、エマルジョン接
着剤１種として、濃度１３．５重量％の天然ゴムラテッ
クス（商品名：ポリゾールＰＡ−８、昭和高分子株式会
社製）６．０容量部を加え、充分に撹拌混合した。[0049] Example 4 100 parts by volume expanded polystyrene particles as emulsion adhesive one, a concentration 13.5% by weight of natural rubber latex (trade name: Polysol PA-8, Showa Kobunshi Co., Ltd.) 6 Then, the mixture was stirred and mixed thoroughly.
【００５０】次に、生成した混合物を撹拌しつつ、微細
連通気孔を有する粉体状の無機物粉体として、粒径１μ
ｍ〜０．３ｍｍの天然ゼオライト（商品名：ＺＯ＃７
０：日東粉化工業株式会社製）１．５容量部と、連通気
孔を有する短繊維状の有機物質として、繊維長さ０．１
〜５ｍｍのピートモス（カナダ産、見掛比重０．０７）
１０容量部を加えた後、さらに、十分撹拌混合して粘着
性発泡ポリスチレン粒子を得た。Next, while stirring the resulting mixture, a powdery inorganic powder having fine interconnected pores having a particle size of 1 μm was obtained.
m to 0.3 mm natural zeolite (trade name: ZO # 7)
0: manufactured by Nitto Powder Chemical Co., Ltd.) 1.5 volume parts and a fiber length of 0.1 as a short fibrous organic substance having continuous air holes.
~ 5mm peat moss (Canada, apparent specific gravity 0.07)
After adding 10 parts by volume, the mixture was further sufficiently stirred and mixed to obtain sticky expanded polystyrene particles.
【００５１】この粘着性発泡ポリスチレン粒子は、既に
細粒の天然ゼオライトが混合されているので、シート状
に加圧成形して人工土壌シートとして使用することが可
能であり、特に軽量化が臨まれる屋上スペース等の緑化
用に効果を発揮する。Since the viscous expanded polystyrene particles have already been mixed with fine natural zeolite, they can be pressed into a sheet and used as an artificial soil sheet. It is effective for greening rooftop spaces.
【００５２】以上の各実施例によれば、発泡ポリスチレ
ン粒子の粒度、接着剤の濃度および配合比、無機物質、
有機物質の種類、粒度、配合比等を広範囲に変化させる
こが可能である。According to the above embodiments, the particle size of the expanded polystyrene particles, the concentration and the mixing ratio of the adhesive, the inorganic substance,
It is possible to change the type, particle size, compounding ratio, etc. of the organic substance in a wide range.
【００５３】また、上記のような粘着性発泡ポリスチレ
ン粒子は、常温で、しかも僅かな圧力で簡単に所定形状
の成形体を成形することができるので、例えば、利用者
は、粘土や石膏のように簡単に成形体を成形することが
できる。Further, since the above-mentioned adhesive foamed polystyrene particles can easily form a molded article having a predetermined shape at normal temperature and with a slight pressure, for example, a user may use a material such as clay or gypsum. The molded body can be easily formed.
【００５４】また、造成地法面緑化に使用する場合に
は、芝等の種子を混合し、通気性・耐水性を有する樹脂
を表面にコーテイングしたシート状にして使用すれば、
風雨によって流出することがなく、短期間で法面の緑化
を行うことができる。Further, in the case of using for greening the slope of the land, the seeds such as turf are mixed, and a resin having air permeability and water resistance is coated on the surface to be used.
The slope can be greened in a short period of time without flowing out due to wind and rain.
【００５５】また、建築内装資材として使用する場合に
は、発泡ポリスチレン自体の特性と粒子間空隙により、
優れた保温断熱性、防音性、弾力性を発揮する。また、
上記の特性に加えて通気性を有するタタミ床としても有
用である。When used as a building interior material, the properties of the expanded polystyrene itself and the voids between the particles cause
Demonstrates excellent heat insulation, sound insulation, and elasticity. Also,
It is also useful as a tatami floor having air permeability in addition to the above characteristics.
【００５６】また、インテリア・ディスプレイ用基材と
して使用する場合には、軽量で成形が簡単なため、優れ
たデザインを容易に具象化することができ、また、搬入
・搬出、製作・撤去を容易に行うことができるので、こ
れらに係る費用を低減することができる。When used as a substrate for an interior display, it is lightweight and easy to mold, so that an excellent design can be easily embodied, and loading / unloading, production / removal is easy. Therefore, the cost for these can be reduced.
【００５７】また、軽量で、且つ、保温性、通気性、保
水性に優れているので、育苗用、ハウス栽培用、貸し鉢
用等の土壌シートとしても有用である。Further, since it is lightweight and excellent in heat retention, air permeability and water retention, it is also useful as a soil sheet for raising seedlings, cultivating houses, renting pots and the like.
【００５８】尚、上記粘着性発泡ポリスチレン粒子は、
上記の利用分野に限定されることなく、これら以外に
も、その成形体の使用目的等に応じて、例えば小石、木
片等の発泡ポリスチレン粒子以外の部材を含有して成形
体を成形することも可能である。例えば、成形体に適度
な重量が必要な場合には、粘着性発泡ポリスチレン粒子
に、例えば小石を含有させて成形したものが使用され
る。The above adhesive foamed polystyrene particles are
Without being limited to the above-mentioned application fields, in addition to these, depending on the intended use of the molded article, for example, it is also possible to mold a molded article containing members other than expanded polystyrene particles such as pebbles and wood chips. It is possible. For example, when an appropriate weight is required for the molded article, a molded article obtained by adding, for example, pebbles to adhesive foamed polystyrene particles is used.
【００５９】〔比較例〕前記実施例１において、無機物
質の混合を除いて、他を同条件として発泡ポリスチレン
粒子からなる混合物およびその成形体を得ることを試み
た。すなわち、発泡ポリスチレン粒子１００容量部に、
エマルジョン接着剤として、濃度１７．４重量％の天然
ゴムラテックス（商品名：ポリゾールＰＡ−８、昭和高
分子株式会社製）３．６容量部を加え、充分に撹拌混合
して混合物を得た。COMPARATIVE EXAMPLE In Example 1, an attempt was made to obtain a mixture of expanded polystyrene particles and a molded article thereof under the same conditions except for the mixing of the inorganic substance. That is, to 100 parts by volume of expanded polystyrene particles,
As an emulsion adhesive, 3.6 parts by volume of a natural rubber latex (trade name: Polysol PA-8, manufactured by Showa Polymer Co., Ltd.) having a concentration of 17.4% by weight was added, and the mixture was sufficiently stirred and mixed to obtain a mixture.
【００６０】この得られた混合物１５０ｇを実施例１と
同様の成型機（１１７０ｃｍ3 ）に充填し、０．５ｋｇ
／ｃｍ2 の押圧力で２分間加圧し、その後、型枠から取
り外した。しかし、直ぐに膨張崩壊し、成形体を形成す
るこができなかった。また、成型機の型枠内面には、多
量の接着剤及び発泡ポリスチレン粒子が付着残留した状
態となっていた。150 g of the obtained mixture was charged into the same molding machine (1170 cm 3 ) as in Example 1, and 0.5 kg
/ Cm 2 for 2 minutes and then removed from the mold. However, it immediately expanded and collapsed, and a molded article could not be formed. In addition, a large amount of adhesive and expanded polystyrene particles remained on the inner surface of the mold frame of the molding machine.
【００６１】尚、前記実施例１では、成形後の型枠内に
は接着剤および発泡ポリスチレン粒子の付着残留はみら
れなった。このことにより、微細連通気孔を有する粉体
状の無機物質を適正量（発泡ポリスチレン粒子１００容
量部に対して０．１〜１５容量部）添加することで、上
記無機物質が接着剤を余剰なく吸着することができ、吸
着された接着剤は、発泡ポリスチレン粒子同士の接着の
みに使用されることができるので、型枠内に接着剤の付
着残留を無くすことができる。In Example 1, no adhesive residue and no expanded polystyrene particles remained in the mold after molding. Thus, by adding an appropriate amount of a powdery inorganic substance having fine interconnected pores (0.1 to 15 parts by volume with respect to 100 parts by volume of the expanded polystyrene particles), the inorganic substance does not have excess adhesive. Since the adhesive that can be adsorbed and the adsorbed adhesive can be used only for adhesion between the expanded polystyrene particles, it is possible to eliminate the adhesive remaining in the mold.
【００６２】[0062]
【発明の効果】請求項１記載の発明の粘着性発泡ポリス
チレン粒子は、以上のように、発泡ポリスチレン粒子
と、エマルジョン接着剤１種または２種以上の混合接着
剤と、少なくとも、微細連通気孔を有する粉体状の無機
物質、または、連通気孔を有する短繊維状もしくは粒状
の有機物質とを混合してなることを特徴とする構成であ
る。As described above, the pressure-sensitive adhesive expanded polystyrene particles according to the first aspect of the present invention are characterized in that expanded polystyrene particles, one or more emulsion adhesives, and at least fine interconnected pores are formed. The composition is characterized by being mixed with a powdered inorganic substance or a short fibrous or granular organic substance having continuous air holes.
【００６３】それゆえ、微細連通気孔を有する粉体状の
無機物質または連通気孔を有する短繊維状もしくは粒状
の有機物質が、エマルジョン接着剤の水分を吸収するの
で、上記構成の発泡ポリスチレン粒子は、適度に粘着性
を有し、常温でしかも僅かな押圧力によって簡単に種々
の形状に成形体を成形することかできるという効果を奏
する。Therefore, the powdered inorganic substance having the fine pores or the short fiber or granular organic substance having the fine pores absorbs the moisture of the emulsion adhesive. This has an effect that it has moderate adhesiveness and can easily form molded articles into various shapes at room temperature and with a small pressing force.
【００６４】請求項２記載の発明の発泡ポリスチレン成
形体は、以上のように、請求項１記載の粘着性発泡ポリ
スチレン粒子を加圧成形してなることを特徴とする構成
である。The foamed polystyrene molded article according to the second aspect of the present invention is characterized by being formed by pressure-forming the pressure-sensitive adhesive polystyrene particles according to the first aspect as described above.
【００６５】それゆえ、上記構成の発泡ポリスチレン成
形体は、粘着性発泡ポリスチレン粒子から容易に成形さ
れ、時間経過に伴ってエマルジョ接着剤に含有される水
分が蒸発するので、粘着性が増大し、発泡ポリスチレン
粒子同士の接着力が増大する。これによって、外圧によ
っても崩壊しにくくなり、形状を安定して維持すること
ができるという効果を奏する。Therefore, the expanded polystyrene molded article having the above structure is easily formed from the adhesive expanded polystyrene particles, and the water contained in the emuljo adhesive evaporates over time, so that the adhesiveness increases. The adhesive force between the expanded polystyrene particles increases. As a result, there is an effect that it is difficult to collapse even by external pressure, and the shape can be stably maintained.
Claims (2)
着剤１種または２種以上の混合接着剤と、少なくとも、
微細連通気孔を有する粉体状の無機物質、または、連通
気孔を有する短繊維状もしくは粒状の有機物質とを混合
してなることを特徴とする粘着性発泡ポリスチレン粒
子。1. An expanded polystyrene particle, one or more emulsion adhesives, and at least one mixed adhesive,
Adhesive expanded polystyrene particles characterized by being mixed with a powdery inorganic substance having fine communicating pores or a short fiber or granular organic substance having communicating pores.
子を加圧成形してなることを特徴とする発泡ポリスチレ
ン成形体。2. A foamed polystyrene molded product obtained by pressure-molding the pressure-sensitive adhesive polystyrene foam particles according to claim 1.