JP2944083B2 - Laminate film - Google Patents
Laminate filmInfo
- Publication number
- JP2944083B2 JP2944083B2 JP63065236A JP6523688A JP2944083B2 JP 2944083 B2 JP2944083 B2 JP 2944083B2 JP 63065236 A JP63065236 A JP 63065236A JP 6523688 A JP6523688 A JP 6523688A JP 2944083 B2 JP2944083 B2 JP 2944083B2
- Authority
- JP
- Japan
- Prior art keywords
- film
- adhesive layer
- image
- weight
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】 〔産業上の利用分野〕 本発明はラミネートフィルムに関し、詳しくは、昇華
転写印字物の耐久性をあげるための保護材としてのラミ
ネートフィルムに関する。Description: TECHNICAL FIELD The present invention relates to a laminate film, and more particularly, to a laminate film as a protective material for improving the durability of a sublimation transfer print.
昇華性の分散染料を含有する染料層を有する熱転写シ
ートをサーマルヘッド等により画像信号に応じて点状に
加熱し染料を移行することにより画像を形成する試みが
行われている。Attempts have been made to form an image by heating a thermal transfer sheet having a dye layer containing a sublimable disperse dye by a thermal head or the like in a dot-like manner according to an image signal and transferring the dye.
しかしながら、この様な方法で形成された画像はプリ
ント後に印字面が露出しているため、表面のスクラッチ
性、染料の再昇華による他への汚染、染料の耐候性、耐
光性に問題があった。However, since the image formed by such a method has a printed surface exposed after printing, there are problems with the surface scratching property, contamination by others due to re-sublimation of the dye, weather resistance of the dye, and light resistance. .
本発明はこの様な転写画像が形成された画像形成層に
ラミネートをすることにより上記従来技術の欠点を解消
しえる優れたラミネートフィルムを提供することを目的
とするものである。An object of the present invention is to provide an excellent laminate film which can solve the above-mentioned disadvantages of the prior art by laminating an image forming layer on which such a transferred image is formed.
本発明は、（１）熱移行性染料を有する熱転写シート
から移行された染料により画像が形成された画像形成層
の表面をラミネートするラミネートフィルムであって、
シート状基材の一方の面に熱で接着性が発現する接着層
を設けてなり、該接着層がポリアミド系樹脂又は／及び
ポリエステル系樹脂で構成され且つ滑性剤を含み、該滑
性剤の添加量が接着層を構成する接着剤100重量部に対
し0.01〜20重量部である４ことを特徴とするラミネート
フィルム、を要旨とするものである。The present invention provides (1) a laminate film for laminating a surface of an image forming layer on which an image is formed by a dye transferred from a thermal transfer sheet having a heat transferable dye,
An adhesive layer which exhibits adhesiveness by heat is provided on one surface of the sheet-like substrate, and the adhesive layer is made of a polyamide-based resin or / and a polyester-based resin and contains a lubricating agent; Wherein the additive amount is 0.01 to 20 parts by weight with respect to 100 parts by weight of the adhesive constituting the adhesive layer.
以下、本発明の実施例を図面を参照して詳細に説明す
る。Hereinafter, embodiments of the present invention will be described in detail with reference to the drawings.
第１図において１はラミネートフィルムを示し、該ラ
ミネートフィルム１はシート状基材２の一方の面に接着
層３が設けられて構成されている。In FIG. 1, reference numeral 1 denotes a laminated film. The laminated film 1 is constituted by providing an adhesive layer 3 on one surface of a sheet-like substrate 2.
上記シート状基材としては、ポリエチレンフィルム、
ポリプロピレンフィルム、ポリ塩化ビニルフィルム、ポ
リ塩化ビニリデンフィルム、ポリビニルアルコールフィ
ルム、ポリエチレンテレフタレートフィルム、ポリカー
ボネートフィルム、ナイロンフィルム、ポリスチレンフ
ィルム、エチレン酢酸ビニル共重合体フィルム、エチレ
ンビニルアルコール共重合体フィルム、アイオノマー等
のプラスチックフィルムのうち、透明もしくは半透明の
もの（これらは有色透明もしくは有色半透明でもよい）
等が挙げられ、機械的装置により取り扱い時の破断防止
性や耐熱性を重視する場合には、ポリエチレンテレフタ
レートフィルム、ポリカーボネートフィルム、ナイロン
フィルムが好ましく、なかでもポリエチレンテレフタレ
ートフィルムが特に好ましい。As the sheet-like substrate, a polyethylene film,
Plastics such as polypropylene film, polyvinyl chloride film, polyvinylidene chloride film, polyvinyl alcohol film, polyethylene terephthalate film, polycarbonate film, nylon film, polystyrene film, ethylene vinyl acetate copolymer film, ethylene vinyl alcohol copolymer film, and ionomer Transparent or translucent films (these may be colored transparent or colored translucent)
When importance is placed on the prevention of breakage and heat resistance during handling by a mechanical device, a polyethylene terephthalate film, a polycarbonate film, and a nylon film are preferable, and a polyethylene terephthalate film is particularly preferable.
又、これらのフィルム中には紫外線吸収剤を含有させ
ることもでき、その具体例としてベンゾフェノン系、ヒ
ンダードアミン系、ベンゾトリアゾール系等が挙げら
れ、その添加量としてはフィルムを形成する樹脂100重
量部に対し、0.01〜20重量部程度であることが好まし
い。Further, in these films, an ultraviolet absorber can be contained, and specific examples thereof include benzophenone-based, hindered amine-based, benzotriazole-based, and the like, and the amount of addition is 100 parts by weight of the resin forming the film. On the other hand, it is preferably about 0.01 to 20 parts by weight.
このシート状基材の厚みは通常25〜200μｍ、好まし
くは75〜125μｍ程度である。The thickness of the sheet-form substrate is usually 25 to 200 μm, preferably about 75 to 125 μm.
又、接着層３は加熱することにより接着性が発現する
接着剤により構想されてなるものであり、この様な接着
剤としてはポリアミド系樹脂、ポリエステル系樹脂が挙
げられる。これらは単独で用いても混合して用いてもい
ずれでもよい。The adhesive layer 3 is conceived of an adhesive that exhibits adhesiveness when heated, and examples of such an adhesive include a polyamide resin and a polyester resin. These may be used alone or as a mixture.
実験例１〜３ 厚さ100μｍのポリエチレンテレフタレートフィルム
に斜線リバースコートにより、実験例１においてはポリ
アミド樹脂、実験例２においてはポリエステル樹脂、実
験例３においてはエチレン酢酸−ビニル共重合体樹脂を
用いて乾燥塗膜４μｍになるようにコーティングしてラ
ミネートフィルムを形成した。Experimental Examples 1 to 3 Polyethylene terephthalate films having a thickness of 100 μm were subjected to reverse coating using a polyamide resin in Experimental Example 1, a polyester resin in Experimental Example 2, and an ethylene acetate-vinyl copolymer resin in Experimental Example 3. Coating was performed to a dry coating film of 4 μm to form a laminate film.
このラミネートフィルムを用いて昇華転写印刷物に14
0℃、５秒の条件で加熱ラミネートした。得られた各積
層体の剥離強度、画像の滲みを測定した結果を第１表に
併せて示す。Sublimation transfer prints can be made using this laminate film.
Heat lamination was performed at 0 ° C. for 5 seconds. Table 1 also shows the results of measuring the peel strength and the bleeding of the image of each of the obtained laminates.
上記実験例の如く、ポリアミド系樹脂、ポリエステル
系樹脂はラミネートに際し、剥離強度が大きく即ち密着
性は良く、しかも画像の滲みを生じないという優れた特
性を有する。 As in the above experimental examples, the polyamide-based resin and the polyester-based resin have excellent peeling strength in lamination, that is, good adhesion, and have excellent characteristics of preventing image bleeding.
又、接着層３には必要に応じて、紫外線吸収剤、光安
定化剤、を添加することもできる。又、接着層３には滑
性剤を含んでいる。In addition, an ultraviolet absorber and a light stabilizer can be added to the adhesive layer 3 as necessary. The adhesive layer 3 contains a lubricant.
紫外線吸収剤、光安定化剤は画像形成層の転写画像の
耐光性を向上させるものであり、又、滑性剤はラミネー
トフィルム同士が使用前に接着してしまうのを防止する
効果がある。The ultraviolet absorber and the light stabilizer improve the light resistance of the transferred image of the image forming layer, and the lubricating agent has the effect of preventing the laminated films from adhering to each other before use.
紫外線吸収剤としては上記シート状基材に含有させる
ものと同様のものが使用でき、その添加量としては接着
層を構成する接着層100重量部に対し、0.01〜20重量部
程度が好ましい。As the ultraviolet absorber, those similar to those contained in the above-mentioned sheet-like base material can be used, and the addition amount thereof is preferably about 0.01 to 20 parts by weight based on 100 parts by weight of the adhesive layer constituting the adhesive layer.
又、光安定化剤の具体例としてはホスファイト系光安
定化剤、ポペリジン系光安定化剤等が挙げられ、その添
加量としては接着層を構成する接着剤100重量部に対し
0.01〜10重量部であることが好ましい。Specific examples of the light stabilizer include a phosphite light stabilizer and a popridine light stabilizer, and the amount of the light stabilizer is 100 parts by weight of the adhesive constituting the adhesive layer.
It is preferably 0.01 to 10 parts by weight.
又、滑性剤の具体例としては、ポリエチレンワック
ス、アミドワックス、テフロンパウダー等の固形ワック
ス類或いはマイクロシリカ、酸化チタン、水酸化バリウ
ム等の無機充填剤が挙げられ、その添加量としては接着
層を構成する接着剤100重量部に対し0.01〜20重量部で
ある。Specific examples of the lubricant include solid waxes such as polyethylene wax, amide wax, and Teflon powder; and inorganic fillers such as microsilica, titanium oxide, and barium hydroxide. Is 0.01 to 20 parts by weight with respect to 100 parts by weight of the adhesive constituting the above.
接着層をシート状基材表面に形成する方法としては、
接着層を構成する接着剤及び要すれば紫外線吸収剤等の
他の添加剤を加熱溶融して公知の装置によりシート状基
材表面に塗布する所謂ホットメルトコートにより形成す
ることができ、或いは、上記接着剤等を溶剤に溶解或い
は分散させたものをロールコーティング、ダイコーティ
ング、ナイフコーティング、グラビアコーティング等の
公知の塗布方法により形成することができる。As a method of forming the adhesive layer on the sheet-like substrate surface,
It can be formed by so-called hot-melt coating in which the adhesive constituting the adhesive layer and, if necessary, other additives such as an ultraviolet absorber are heated and melted and applied to the surface of the sheet-like substrate by a known device, or The adhesive or the like dissolved or dispersed in a solvent can be formed by a known coating method such as roll coating, die coating, knife coating, or gravure coating.
接着層の厚さとしては１〜50μｍ程度であることが好
ましい。The thickness of the adhesive layer is preferably about 1 to 50 μm.
上記の様に構成されるラミネートフィルムは第２図に
示す如く、転写シートから移行した画像４が形成されて
なる画像形成層５の表面に接着層が当接する如く接着さ
れる。As shown in FIG. 2, the laminated film configured as described above is adhered so that the adhesive layer comes into contact with the surface of the image forming layer 5 on which the image 4 transferred from the transfer sheet is formed.
以下、参考例を挙げて本発明を更に詳細に説明する。 Hereinafter, the present invention will be described in more detail with reference to Reference Examples.
参考例 紫外線吸収剤を含有する厚さ100μｍのポリエチレン
テレフタレートフィルム（帝人製:HBタイプ）に斜線リ
バースコートによりナイロン樹脂（FS 175 SV 10）を乾
燥塗膜４μｍになるようにコーティングしてラミネート
フィルムを形成した。Reference Example A 100 μm thick polyethylene terephthalate film (manufactured by Teijin: HB type) containing an ultraviolet absorber is coated with a nylon resin (FS 175 SV10) by a diagonal reverse coat to a dry coating film of 4 μm to form a laminated film. Formed.
このラミネートフィルムを用いて昇華転写印刷物に14
0℃、５秒の条件で加熱ラミネートした。得られた積層
体は剥離強度が強く、転写後の画像の滲みも生じること
はなく、又、日光堅牢度も高い優れた積層体が得られ
た。Sublimation transfer prints can be made using this laminate film.
Heat lamination was performed at 0 ° C. for 5 seconds. The obtained laminate had a high peel strength, did not cause bleeding of the image after transfer, and had an excellent laminate having high fastness to sunlight.
以上説明した如く、本発明ラミネートフィルムは、熱
移行性染料を有する熱転写シートから移行された染料に
より画像が形成された画像成形層の表面をラミネートす
るラミネートフィルムであって、シート状基材の一方の
面に熱で接着性が発現する接着層を設けてなるものであ
るから、画像形成層表面にラミネートした場合、転写画
像の表面スクラッチ性の改善、染料の再昇華による他へ
の汚染の防止、染料の耐候性の改善を図ることができ
る。As described above, the laminate film of the present invention is a laminate film for laminating the surface of an image forming layer on which an image has been formed with a dye transferred from a thermal transfer sheet having a heat transferable dye, and one of a sheet-like substrate. Is provided with an adhesive layer that exhibits adhesiveness by heat on the surface of the image forming layer, so that when it is laminated on the surface of the image forming layer, the surface scratching of the transferred image is improved, and the contamination of others due to dye sublimation is prevented. In addition, the weather resistance of the dye can be improved.
又、接着層がポリアミド系樹脂又は／及びポリエステ
ル系樹脂から構成されていため、画像形成層とラミネー
トフィルムの密着力が強く、フィルムの剥離が生じる様
な虞れはなく、又、接着後の転写画像が滲むことがなく
鮮明な画像を長期間維持できる。Further, since the adhesive layer is made of a polyamide-based resin and / or a polyester-based resin, the adhesion between the image forming layer and the laminate film is strong, and there is no fear that the film is peeled off. A clear image can be maintained for a long time without blurring the image.
又、接着層が滑性剤を接着層を構成する接着剤100重
量部に対し0.01〜20重量部含んでいるため、ラミネート
フィルム同士が使用前に接着してしまうのを良好に防止
できる。Further, since the adhesive layer contains the lubricant in an amount of 0.01 to 20 parts by weight based on 100 parts by weight of the adhesive constituting the adhesive layer, it is possible to prevent the laminated films from adhering to each other before use.
第１図はラミネートフィルムを示す縦断面図、第２図は
ラミネートフィルムを転写画像を有する画像形成層にラ
ミネートした状態を示す縦断面図である。 １……ラミネートフィルム ２……シート状基材 ３……接着層 ４……転写画像 ５……画像形成層FIG. 1 is a longitudinal sectional view showing a laminated film, and FIG. 2 is a longitudinal sectional view showing a state where the laminated film is laminated on an image forming layer having a transferred image. DESCRIPTION OF SYMBOLS 1 ... Laminated film 2 ... Sheet-shaped base material 3 ... Adhesive layer 4 ... Transfer image 5 ... Image forming layer
───────────────────────────────────────────────────── フロントページの続き (56)参考文献 特開 昭60−232949（ＪＰ，Ａ) 特開 昭56−24161（ＪＰ，Ａ) 特開 昭60−61853（ＪＰ，Ａ) 特開 昭62−214990（ＪＰ，Ａ) ──────────────────────────────────────────────────続 き Continuation of the front page (56) References JP-A-60-232949 (JP, A) JP-A-56-24161 (JP, A) JP-A-60-61853 (JP, A) JP-A Sho 62- 214990 (JP, A)
Claims (1)
行された染料により画像が形成された画像形成層の表面
をラミネートするラミネートフィルムであって、シート
状基材の一方の面に熱で接着性が発現する接着層を設け
てなり、該接着層がポリアミド系樹脂又は／及びポリエ
ステル系樹脂で構成され且つ滑性剤を含み、該滑性剤の
添加量が接着層を構成する接着剤100重量部に対し0.01
〜20重量部であることを特徴とするラミネートフィル
ム。1. A laminated film for laminating a surface of an image forming layer on which an image is formed by a dye transferred from a thermal transfer sheet having a heat transferable dye, which is adhered to one surface of a sheet-like substrate by heat. The adhesive layer is formed of a polyamide-based resin or / and a polyester-based resin and contains a lubricating agent, and the amount of the lubricating agent added to the adhesive layer 100 constitutes the adhesive layer. 0.01 parts by weight
A laminated film characterized by being in an amount of up to 20 parts by weight.