JP2920082B2 - Mark rope - Google Patents
Mark ropeInfo
- Publication number
- JP2920082B2 JP2920082B2 JP7049714A JP4971495A JP2920082B2 JP 2920082 B2 JP2920082 B2 JP 2920082B2 JP 7049714 A JP7049714 A JP 7049714A JP 4971495 A JP4971495 A JP 4971495A JP 2920082 B2 JP2920082 B2 JP 2920082B2
- Authority
- JP
- Japan
- Prior art keywords
- rope
- steel wire
- wire
- plating
- mark
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本発明は、外観識別できるマーク
ロープに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a mark rope capable of identifying its appearance.
【０００２】[0002]
【従来の技術】例えばクレーンで代表される荷役機械に
おいては、ワイヤロープは貨物の吊り上げ吊り下ろし要
素として重要な位置を占めている。荷役機械用ワイヤロ
ープには、繰り返し曲げによる摩耗が小さく断線を容易
に生じないこと、および腐食を容易に生じないことが要
求されている。2. Description of the Related Art In a cargo handling machine represented by a crane, for example, a wire rope occupies an important position as a lifting / hanging element of cargo. Wire ropes for cargo handling machines are required to have small wear due to repeated bending and not to easily cause disconnection and not to easily cause corrosion.
【０００３】荷役機械用ワイヤロープは、繰り返し使用
されるうちに外観目視検査では発見することができない
内部断線や内部腐食が徐々に進行し、劣化する。安全衛
生上の観点から、このようなロープの経年変化を適切に
把握し、使用開始時期等をロープごとに個別に管理する
必要がある。[0003] As the wire rope for cargo handling machines is repeatedly used, internal disconnection and internal corrosion, which cannot be found by visual inspection, gradually progress and deteriorate. From the viewpoint of safety and health, it is necessary to appropriately grasp the aging of such ropes and to manage the start of use and the like individually for each rope.
【０００４】また、ワイヤロープの直径や外部構成が同
じであると、材質が異なり破断強度が異なる異種ロープ
同士であっても同じように見え、外観から識別できな
い。そこで、各ロープごとに破断強度や内部構成を外観
から識別できるようにして管理する必要がある。従来は
異なる組成の潤滑剤を用いて伸線することにより素線に
着色したロープ（特開平１−１２７７５４号公報）、亜
鉛めっきした鋼線に着色樹脂材料を被覆したロープ（特
開平５−１７９５８７号公報）、素線を塗装着色したロ
ープ、側ストランドを塗装着色したロープ、あるいは心
鋼やロープ心に印糸等を撚り込んだロープがある。[0004] Further, if the wire ropes have the same diameter or the same external structure, different kinds of ropes having different materials and different breaking strengths look the same, and cannot be distinguished from the appearance. Therefore, it is necessary to manage the breaking strength and the internal structure of each rope so that they can be identified from the appearance. conventionally
Wire drawn by using lubricants of different composition
Colored rope (JP-A-1-127754)
A rope in which a tinted steel wire is coated with a colored resin material (special
JP-A-5-179587), a rope whose element wire is painted and colored, a rope whose side strands are painted and colored, or a rope in which a marking thread or the like is twisted into a core steel or a rope core.
【０００５】[0005]
【発明が解決しようとする課題】しかしながら、素線着
色ロープ及びストランド着色ロープは、クレーンシーブ
や他のロープ等と擦れ合うところでは著しい磨耗を受
け、着色樹脂被覆や着色塗料が剥がれるので、短時間で
識別不能になってしまう。このため、短い周期でロープ
を点検し、頻繁にロープを塗装する必要がある。また、
これらは製造コスト及び保守コストが高い。However, the wire-colored rope and the strand-colored rope are significantly worn when rubbed with crane sheaves or other ropes, and the colored resin coating and the colored paint are peeled off. It becomes indistinguishable. For this reason, it is necessary to inspect the rope in a short cycle and apply the rope frequently. Also,
These have high manufacturing and maintenance costs.
【０００６】一方、心綱やロープ心に印糸等を撚り込ん
だロープは、ロープ端部を剥いてみなければ内部の状態
は判別できないので、不便である。本発明は上記の課題
を解決するためになされたものであって、長期間にわた
って使用されたとしても寿命や種別を外観から容易に識
別することができるマークロープを提供することを目的
とする。On the other hand, a rope in which a marking thread or the like is twisted around a cord or a rope core is inconvenient because the internal state cannot be determined unless the end of the rope is peeled off. The present invention has been made to solve the above-described problem, and has as its object to provide a mark rope that can easily identify the life and type from the appearance even when used for a long period of time.
【０００７】[0007]
【課題を解決するための手段】本発明に係るマークロー
プは、ロープ心部と、このロープ心部の周囲に撚り合わ
された側ストランド部と、を備え、前記ストランド部は
複数本の無めっきの裸鋼線を多層撚りしてなり、このう
ち最外層の一部を溶融亜鉛めっき又は溶融亜鉛アルミニ
ウム合金めっきした識別鋼線とすることを特徴とする。A mark rope according to the present invention has a rope core and side strands twisted around the rope core.
Multiple unplated bare steel wires are twisted in multiple layers, and a part of the outermost layer is hot-dip galvanized or hot-dip aluminum
It is characterized in that it is a discriminated steel wire plated with an aluminum alloy .
【０００８】識別鋼線のめっきには亜鉛系、アルミニウ
ム系、鉛系など種々のものを採用することができるが、
とくに亜鉛系めっきであることが望ましい。亜鉛系めっ
きのうち溶融亜鉛めっき又は溶融亜鉛−アルミニウム合
金めっきであることが好ましい。なお、溶融亜鉛めっき
を用いる場合は、めっき付着量とめっき表面粗さ（外
観）とが重要な要素となるので、めっき浴の温度、線速
度、絞り量などを最適に制御する必要がある。Various types of plating such as zinc-based, aluminum-based, and lead-based can be used for plating the identification steel wire.
In particular, zinc plating is desirable. Among the zinc-based platings, hot-dip galvanization or hot-dip zinc-aluminum alloy plating is preferable. When hot-dip galvanizing is used, the amount of plating and the surface roughness (appearance) of the plating are important factors, so it is necessary to optimally control the temperature, linear velocity, amount of drawing, etc. of the plating bath.
【０００９】また、めっき層はできるだけ厚くするほう
が望ましい。ロープ内部でめっき層がアノードとして優
先的に溶け出し、周囲の裸鋼線が犠牲防食されるからで
ある。めっき付着量は５０〜４００ｇ／ｍ2 の範囲にす
ることが好ましく、８０〜２００ｇ／ｍ2 にすることが
より好ましい。It is desirable that the plating layer be as thick as possible. This is because the plating layer preferentially melts as an anode inside the rope, and the surrounding bare steel wire is sacrificed and protected. Coating weight is preferably in the range of 50 to 400 g / m 2, and more preferably to 80 to 200 g / m 2.
【００１０】[0010]
【作用】本発明に係るマークロープにおいては、識別鋼
線のみを溶融亜鉛めっき又は溶融亜鉛アルミニウム合金
めっき被覆しているので、使用初期においては無めっき
鋼線とめっき鋼線との光沢の違いを見分けることによ
り、亜鉛層又は亜鉛アルミニウム合金層が消失した後の
使用中期及び後期においては経年変化による色調の違い
を見分けることにより、識別鋼線を周囲の無めっきの裸
鋼線から目視で容易に識別できる。また、識別鋼線の溶
融亜鉛めっき又は溶融亜鉛アルミニウム合金めっきは鋼
線素地に対して深く食い込むＦｅ−Ｚｎ合金層又はＦｅ
−Ｚｎ−Ａｌ合金層が発達し、鋼線素地から容易に剥が
れない強固な被覆層を形成しているので、着色樹脂被覆
や塗料のように容易には剥がれず、長期間にわたり他の
ロープから確実に識別することができる。In the mark rope according to the present invention, since only the identification steel wire is galvanized or hot-dip zinc aluminum alloy <br/> plating coating, in the use initial free plating
By distinguishing the difference in luster between steel wire and plated steel wire
After the disappearance of the zinc layer or zinc aluminum alloy layer
Difference in color tone due to aging in the middle and late stages of use
By distinguishing each other, the identification steel wire can be easily visually identified from the surrounding unplated bare steel wire. In addition, melting of the identification steel wire
Galvanized or galvanized aluminum alloy plating is steel
Fe-Zn alloy layer or Fe that penetrates deeply into the wire base
-The Zn-Al alloy layer develops and is easily peeled from the steel wire substrate
Since forming a firm coating layer which is not, the colored resin-coated
It does not come off as easily as paint or paint and can be reliably distinguished from other ropes over a long period of time.
【００１１】[0011]
【実施例】以下、添付の図面を参照しながら本発明の実
施例について説明する。ここではクレーン等の荷役機械
に用いられるロープ心入りのワイヤロープ（ＩＷＲＣロ
ープ）の例について説明する。 （実施例１）図１に示す断面構成のＩＷＲＣ６×Ｗ（１
９）１６mm特種をマークロープとして作製した。この第
１実施例のマークロープ１０の心部には７×７構成のロ
ープ心が入れてあり、ロープ心の外周に６本の側ストラ
ンド１２がＺ撚りで撚り合わされている。側ストランド
１２は、１本の心線、６本の内周線、６本の外周太線、
６本の外周細線からなるＷ［１＋６＋（６＋６）］の構
成である。これら大小径１９本の裸鋼線１３をＳ撚りし
て側ストランド１２は形成されている。鋼線には、例え
ばＣ含有量が０．６０〜０．８６重量％，Ｍｎ含有量が
０．６０重量％以下の素線を熱処理し、伸線したものを
それぞれ用いた。ロープ外径１６mmの場合にロープピッ
チを約１００mmとし、側ストランド１２の撚りピッチを
約４２mmとした。Embodiments of the present invention will be described below with reference to the accompanying drawings. Here, an example of a wire rope (IWRC rope) with a rope core used for a cargo handling machine such as a crane will be described. (Example 1) IWRC6 × W (1
9) A 16 mm special type was manufactured as a mark rope. The mark rope 10 of the first embodiment has a 7 × 7 rope core in the core thereof, and six side strands 12 are twisted around the rope core in a Z twist. The side strands 12 include one core wire, six inner circumferential lines, six outer thick lines,
This is a configuration of W [1 + 6 + (6 + 6)] composed of six outer thin lines. The side strands 12 are formed by twisting these 19 large and small diameter bare steel wires 13 with S twist. As the steel wire, for example, a wire having a C content of 0.60 to 0.86% by weight and an Mn content of 0.60% by weight or less was heat-treated and drawn. When the rope outer diameter was 16 mm, the rope pitch was about 100 mm, and the twist pitch of the side strands 12 was about 42 mm.
【００１２】６本の側ストランド１２のうち１本の最外
周層には１本の識別鋼線１４が撚り込まれている。この
識別鋼線１４は外周太線のうちの１本にあたり、溶融亜
鉛めっきされている。図２に示すように、識別鋼線１４
がマークロープ１０の外観に表われる。 （実施例２）図３に示す断面構成のＩＷＲＣ６×Ｆｉ
（２５）２０mm特種をマークロープとして作製した。こ
の第２実施例のマークロープ２０の心部には７×７構成
のロープ心が入れてあり、ロープ心の外周に６本の側ス
トランド２２がＺ撚りで撚り合わされている。側ストラ
ンド２２は、１本の心線、６本の内周線、６本のフィラ
ー線、１２本の外周線からなるＦｉ［１＋６＋（６）＋
１２］の構成である。これら大小径２５本の裸鋼線２３
をＳ撚りして側ストランド２２は形成されている。鋼線
には、例えばＣ含有量が０．６０〜０．８６重量％，Ｍ
ｎ含有量が０．６０重量％以下の素線を熱処理し、伸線
したものをそれぞれ用いた。One identification steel wire 14 is twisted into one outermost layer of the six side strands 12. The identification steel wire 14 corresponds to one of the outer thick wires and is hot-dip galvanized. As shown in FIG.
Appears on the appearance of the mark rope 10. (Embodiment 2) IWRC6 × Fi having a sectional structure shown in FIG.
(25) A special rope of 20 mm was produced as a mark rope. The mark rope 20 of the second embodiment has a 7 × 7 rope core in the center thereof, and six side strands 22 are twisted around the rope core in a Z twist. The side strand 22 is composed of Fi [1 + 6 + (6) +] including one core wire, six inner circumferential lines, six filler wires, and 12 outer circumferential lines.
12]. These large and small diameter 25 bare steel wires 23
Are S-twisted to form side strands 22. The steel wire has, for example, a C content of 0.60 to 0.86% by weight, M
A wire having an n content of 0.60% by weight or less was subjected to a heat treatment and then drawn.
【００１３】６本の側ストランド２２のうち１本の最外
周層には２本の識別鋼線２４ａ，２４ｂが撚り込まれて
いる。これらの識別鋼線２４ａ，２４ｂは外周線のうち
の２本にあたり、溶融亜鉛−アルミニウム合金めっきさ
れている。図４に示すように、識別鋼線２４ａ，２４ｂ
が２本並んでマークロープ２０の外観に表われる。 （実施例３）図５に示す断面構成のＩＷＲＣ６×ＳｅＳ
（３７）２８mm特種をマークロープとして作製した。こ
の第３実施例のマークロープ３０の心部には７×７構成
のロープ心が入れてあり、ロープ心の外周に６本の側ス
トランド３２がＺ撚りで撚り合わされている。側ストラ
ンド３２は、１本の心線、６本の内周線、１５本の中間
線、１５本の外周線からなるＳｅＳ（１＋６＋１５＋１
５）の構成である。これら大小径３７本の裸鋼線３３を
Ｓ撚りして側ストランド３２は形成されている。鋼線に
は、例えばＣ含有量が０．６０〜０．８６重量％，Ｍｎ
含有量が０．６０重量％以下の素線を熱処理し、伸線し
たものをそれぞれ用いた。Two identification steel wires 24a and 24b are twisted into one outermost layer of the six side strands 22. These identification steel wires 24a and 24b correspond to two of the outer peripheral wires, and are plated with a hot-dip zinc-aluminum alloy. As shown in FIG. 4, the identification steel wires 24a, 24b
Appear in the appearance of the mark rope 20 side by side. (Embodiment 3) IWRC6 × SeS having a sectional structure shown in FIG.
(37) A special rope of 28 mm was produced as a mark rope. The mark rope 30 of the third embodiment has a 7 × 7 rope core in the core thereof, and six side strands 32 are twisted around the rope core in a Z-twist. The side strand 32 is made of SeS (1 + 6 + 15 + 1) composed of one core wire, six inner circumferential lines, 15 middle lines, and 15 outer circumferential lines.
This is the configuration of 5). The side strands 32 are formed by S-twisting these 37 large and small diameter bare steel wires 33. For example, the steel wire has a C content of 0.60 to 0.86% by weight, Mn
A wire having a content of 0.60% by weight or less was heat-treated and drawn.
【００１４】６本の側ストランド３２のうち３本の最外
周層には１本の識別鋼線３４ａ，３４ｂ，３４ｃがそれ
ぞれ撚り込まれている。これらの識別鋼線３４ａ，３４
ｂ，３４ｃは外周線のうちの１本にあたり、溶融亜鉛め
っきされている。図６に示すように、識別鋼線３４ａ，
３４ｂ，３４ｃが適当な間隔をもってマークロープ２０
の外観に表われる。One identification steel wire 34a, 34b, 34c is twisted in each of the three outermost layers of the six side strands 32. These identification steel wires 34a, 34
b and 34c correspond to one of the outer peripheral lines and are hot-dip galvanized. As shown in FIG. 6, the identification steel wires 34a,
34b and 34c are provided with the mark rope 20 at appropriate intervals.
Appears in the appearance of.
【００１５】次に、上記第１実施例のマークロープの製
造方法について説明する。 ［識別鋼線のめっき処理］素線を脱脂洗浄して伸線潤滑
剤などの異物を除去する。次いで、フラックス槽を通過
させ、素線に適量のフラックスを付着させる。フラック
スには塩化亜鉛（ＺｎＣｌ2 ）と塩化アンモニウム（Ｎ
Ｈ4 Ｃｌ）との複合塩を用いる。このような組成のフラ
ックスを用いることにより、めっき付着量が安定化し、
不めっき部の発生及びめっき表面の凹凸の発生が有効に
防止される。Next, a method of manufacturing the mark rope of the first embodiment will be described. [Plating treatment of identification steel wire] The wire is degreased and washed to remove foreign matter such as a wire drawing lubricant. Next, the flux is passed through a flux tank, and an appropriate amount of flux is attached to the strand. The flux includes zinc chloride (ZnCl 2 ) and ammonium chloride (N
H 4 Cl). By using a flux having such a composition, the amount of plating adhesion is stabilized,
The generation of non-plated portions and the generation of irregularities on the plating surface are effectively prevented.
【００１６】さらに、グリセリンやふすま等の有機発泡
剤を１．０〜１．５重量％添加してもよい。これらの添
加成分によって付着フラックスがめっき浴中で急速にガ
ス化されて有機発泡剤の気泡とともに鋼線から離脱しや
すくなり、めっき付着量が長期間にわたり安定化する。Further, an organic foaming agent such as glycerin or bran may be added in an amount of 1.0 to 1.5% by weight. With these additional components, the deposited flux is rapidly gasified in the plating bath, and is easily released from the steel wire together with the bubbles of the organic foaming agent, so that the deposited amount of the plating is stabilized for a long time.
【００１７】フラックス塗布後、鋼線を溶融亜鉛浴に通
過させ、上方に引上げ、絞り装置にて窒素ガスなどの非
酸化性ガスを吹き付けてめっき付着量を調整する。めっ
き浴の温度は例えば４５０±３０℃の範囲になるように
維持管理されている。めっき浴中の溶融金属は工業的純
亜鉛に若干量のＰｂを添加したものであることが望まし
い。After the flux is applied, the steel wire is passed through a molten zinc bath, pulled up, and a non-oxidizing gas such as nitrogen gas is blown by a squeezing device to adjust the amount of plating. The temperature of the plating bath is maintained and controlled, for example, in the range of 450 ± 30 ° C. It is desirable that the molten metal in the plating bath is one obtained by adding a small amount of Pb to industrial pure zinc.
【００１８】めっき付着量は、絞り装置での非酸化性ガ
スの噴射量と線速度の一方または双方によって制御す
る。めっき付着量５０〜４００ｇ／ｍ2 （好ましくは８
０〜２００ｇ／ｍ2 ）を目標とする場合に、一般に線速
度を毎分２０〜４５ｍの範囲とすることが望ましい。線
速度が毎分２０ｍを下回ると、所望のめっき付着量が確
保されず、不めっき部が生じるおそれがあり、線速度が
毎分４５ｍを上回ると、めっき付着量が過剰になるから
である。本実施例では平均めっき付着量１３０ｇ／ｍ2
のものを得た。 ［ロープ心の形成］線材をパテンチング処理をした後
に、５乃至１２回のダイス引きにより減面率８０〜９５
％の冷間伸線加工を行なうことによって所定の素線を得
る。The plating amount is controlled by one or both of the injection amount of the non-oxidizing gas and the linear velocity in the expansion device. Plating adhesion amount of 50 to 400 g / m 2 (preferably 8
When the target is 0 to 200 g / m 2 ), it is generally desirable to set the linear velocity in the range of 20 to 45 m / min. If the linear velocity is lower than 20 m / min, the desired amount of plating cannot be secured, and there is a possibility that an unplated portion may be generated. If the linear velocity is higher than 45 m / min, the amount of plating becomes excessive. In this embodiment, the average coating weight is 130 g / m 2.
Got something. [Formation of rope core] After the wire rod is subjected to the patenting treatment, the area reduction rate is 80 to 95 by die drawing 5 to 12 times.
% Is obtained by performing cold wire drawing.
【００１９】次に、７本の素線を撚り合わせて一次スト
ランドとする。更にこのような一次ストランドを７本撚
り合わせて、（７×７）のロープ心を得た。このような
ロープ心は次のようにつくられる。センタストランドと
なる一次ストランドをリールから巻き取り部の巻取機へ
向かって所定速度で引き出す。送給ラインにはボイスが
設けられており、このストランドの他に、ボイスに向か
ってリールから側ストランドとなる６本の一次ストラン
ドが引き出される。これら６本のストランドは、それぞ
れがＺ撚りに撚られたものであり、センタストランドの
外周にＺ撚りに撚り合わされてロープ心が得られる。 ［側ストランドの形成］１８本の裸鋼線１３及び１本の
識別鋼線（めっき鋼線）１４を撚り線機に送り、一括に
Ｓ撚りに撚り合わせ、Ｗ［１＋６＋（６＋６）］構成の
側ストランド１２を得た。 ［ロープの撚合］撚り線機はロープ心のリールスタンド
から巻き取り部の巻取機までの間に設けられ、連続送給
される各側ストランドに所定の張力が印加されるように
張力制御されている。撚り線機の中心にロープ心を通す
とともに、プレフォーム装置により側ストランド１２を
形付け（プレフォーム）し、これらをボイスによってロ
ープ心に上撚りする。撚り方向はＺ撚りである。ボイス
を出ると、ＩＷＲＣ６×Ｗ（１９）となる。Next, the seven strands are twisted to form a primary strand. Furthermore, seven such primary strands were twisted to obtain a (7 × 7) rope core. Such a rope core is made as follows. A primary strand serving as a center strand is drawn out from a reel toward a winder of a winding section at a predetermined speed. A voice is provided on the feed line, and in addition to this strand, six primary strands serving as side strands are drawn from the reel toward the voice. These six strands are each twisted in a Z twist, and are twisted in a Z twist around the center strand to obtain a rope core. [Formation of Side Strands] Eighteen bare steel wires 13 and one identification steel wire (plated steel wire) 14 are sent to a twisting machine and twisted together in an S twist to form a W [1 + 6 + (6 + 6)] configuration. The side strand 12 was obtained. [Rope twisting] A stranded wire machine is provided between the reel stand of the rope core and the winder of the winding section, and tension control is performed so that a predetermined tension is applied to each side strand continuously fed. Have been. The rope core is passed through the center of the stranding machine, and the side strands 12 are shaped (preformed) by a preforming device, and these are twisted onto the rope core by voice. The twist direction is Z twist. When leaving the voice, IWRC 6 × W (19) is obtained.
【００２０】[0020]
【発明の効果】本発明によれば、識別鋼線のみを溶融亜
鉛めっき又は溶融亜鉛アルミニウム合金めっき被覆して
いるので、使用初期は無めっき鋼線とめっき鋼線との光
沢の違いにより識別鋼線を周囲の無めっきの裸鋼線から
容易に識別できる。また、亜鉛層又は亜鉛アルミニウム
合金層が消失した後の使用中期及び後期は経年変化によ
る色調が違ってくるので、識別鋼線を周囲の無めっきの
裸鋼線から容易に識別できる。According to the present invention, only the identification steel wire is melted.
Since the lead-plated or hot-dip zinc aluminum alloy-plated coating, using the initial light with plated steel wire with non-plated steel wire
Due to the difference between the swaths, the identification steel wire can be easily identified from the surrounding unplated bare steel wire. Also, zinc layer or zinc aluminum
To use the medium-term and late aging after the alloy layer is lost
Since the color tone is different, the identification steel wire can be easily identified from the surrounding unplated bare steel wire.
【００２１】また、識別鋼線の溶融亜鉛めっき又は溶融
亜鉛アルミニウム合金めっきは鋼線素地に対して深く食
い込むＦｅ−Ｚｎ合金層又はＦｅ−Ｚｎ−Ａｌ合金層が
発達し、鋼線素地から容易に剥がれない強固な層を形成
しているので、着色樹脂被覆や塗料のように容易には剥
がれず、長期間にわたり他のロープから確実に識別する
ことができる。とくにクレーンシーブや他のロープ等と
擦れ合い著しい磨耗を受けるところであっても、長時間
にわたって寿命や種別を外観から容易に識別することが
できる。このため、短い周期でロープを点検したり、頻
繁にロープを塗装する必要がなく、保守点検コストが大
幅に低減される。Also, hot-dip galvanizing or hot-dipping of the identification steel wire
Zinc-aluminum alloy plating eats deep into steel wire base
Fe-Zn alloy layer or Fe-Zn-Al alloy layer
Develops and forms a strong layer that does not easily come off the steel wire substrate , so it does not come off as easily as colored resin coatings or paints, and is reliably distinguished from other ropes for a long time be able to. In particular, even in places where they are rubbed against crane sheaves or other ropes and are subject to significant wear, their life and type can be easily identified from the appearance over a long period of time. For this reason, it is not necessary to inspect the rope in a short cycle or to paint the rope frequently, and the maintenance and inspection cost is greatly reduced.
【図１】本発明の第１実施例に係るマークロープを示す
横断面図。FIG. 1 is a cross-sectional view showing a mark rope according to a first embodiment of the present invention.
【図２】第１実施例のマークロープの一部を示す外観
図。FIG. 2 is an external view showing a part of the mark rope of the first embodiment.
【図３】本発明の第２実施例に係るマークロープを示す
横断面図。FIG. 3 is a cross-sectional view showing a mark rope according to a second embodiment of the present invention.
【図４】第２実施例のマークロープの一部を示す外観
図。FIG. 4 is an external view showing a part of a mark rope according to a second embodiment.
【図５】本発明の第３実施例に係るマークロープを示す
横断面図。FIG. 5 is a cross-sectional view showing a mark rope according to a third embodiment of the present invention.
【図６】第３実施例のマークロープの一部を示す外観図
である。FIG. 6 is an external view showing a part of a mark rope according to a third embodiment.
１０，２０，３０…マークロープ １２，２２，３２…側ストランド １３，２３，３３…裸鋼線（不めっき鋼線） １４，２４ａ，２４ｂ，３４ａ，３４ｂ，３４ｃ…識別
鋼線（めっき鋼線）。10, 20, 30 ... mark rope 12, 22, 32 ... side strand 13, 23, 33 ... bare steel wire (unplated steel wire) 14, 24a, 24b, 34a, 34b, 34c ... identification steel wire (plated steel wire) ).
Claims (1)
撚り合わされた側ストランド部と、を備え、 前記側ストランド部は複数本の無めっきの裸鋼線を多層
撚りしてなり、このうち最外層の一部を溶融亜鉛めっき
又は溶融亜鉛アルミニウム合金めっき被覆した識別鋼線
とすることを特徴とするマークロープ。1. A rope core portion, and a side strand portion twisted around the rope core portion, wherein the side strand portion is formed by twisting a plurality of unplated bare steel wires in multiple layers. Part of the outermost layer is hot-dip galvanized
A mark rope characterized by being an identification steel wire coated with a galvanized aluminum alloy .