JP2875349B2 - Postcard - Google Patents
PostcardInfo
- Publication number
- JP2875349B2 JP2875349B2 JP2140546A JP14054690A JP2875349B2 JP 2875349 B2 JP2875349 B2 JP 2875349B2 JP 2140546 A JP2140546 A JP 2140546A JP 14054690 A JP14054690 A JP 14054690A JP 2875349 B2 JP2875349 B2 JP 2875349B2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- adhesive
- postcard
- release agent
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】 (産業上の利用分野) この発明は、はがきに関し、特にたとえば、秘密事項
部分を郵送中においては隠し、正規の受け取り人が受け
取った後、その秘密事項部分を適宜見ることができる、
はがきに関する。Description: TECHNICAL FIELD The present invention relates to a postcard, and particularly relates to a postcard, for example, concealing a secret part during mailing and viewing the confidential part appropriately after receiving it by an authorized recipient. be able to,
About postcards.
(従来技術) 近年、銀行の預金残高などの通知などのように秘密事
項を記載した郵便物が増加しているが、秘密事項の記載
欄を郵送中は隠し、正規の受け取り人が受け取った後、
比較的簡単にその内容を見ることができるように形成さ
れたはがきを開発されている。(Prior art) In recent years, the number of mails containing confidential items, such as notices of bank balances, has increased. However, the confidential items are hidden during mailing, and after the legitimate recipient receives them. ,
Postcards have been developed that are formed so that their contents can be viewed relatively easily.
第10図は従来のこの種のはがきの部分断面図である。
このはがき1は官製はがき大に形成されたはがき台紙2
とこのはがき台紙2の一部に貼着された被覆材3を含
む。この被覆材3は基材4を含む。基材4の一方主面に
は接着剤層5から形成される。接着剤層5の一方主面に
は、アルミからなる隠ぺい層6が形成される。基材4と
隠ぺい層6は、接着剤層5によって接着される。隠ぺい
層6の一方主面には剥離剤層7が形成される。剥離剤層
7の一方主面には熱接着性樹脂層8が形成される。熱接
着性樹脂層8の一方主面にははがき台紙2が形成され
る。熱接着性樹脂層8は加熱されると溶融して、被覆材
3がはがき台紙2に貼着される。FIG. 10 is a partial sectional view of a conventional postcard of this type.
This postcard 1 is a postcard mount 2 formed into a large postcard.
And a covering material 3 attached to a part of the postcard mount 2. This covering material 3 includes a base material 4. An adhesive layer 5 is formed on one main surface of the substrate 4. On one main surface of the adhesive layer 5, a hiding layer 6 made of aluminum is formed. The base material 4 and the hiding layer 6 are adhered by the adhesive layer 5. On one main surface of the concealing layer 6, a release agent layer 7 is formed. On one main surface of the release agent layer 7, a heat-adhesive resin layer 8 is formed. The postcard backing paper 2 is formed on one main surface of the heat-adhesive resin layer 8. The heat-adhesive resin layer 8 is melted when heated, and the covering material 3 is adhered to the postcard mount 2.
(発明が解決しようとする課題) ところが、従来のはがきでは、さまざまな長所がある
代わりに被覆材を剥がす時、ビリビリ剥がれてしまい剥
がしにくかった。(Problems to be Solved by the Invention) However, conventional postcards have various advantages, but when peeling off the covering material, they peel off easily and are difficult to peel off.
しかも、このはがきは被覆材に指や爪を引っ掛けるも
のがないので、引き剥がしにくい。In addition, since this postcard has nothing to catch a finger or a nail on the covering material, it is difficult to peel it off.
それゆえに、この発明の主たる目的は、正規の受け取
り人において受け取った後比較的簡単に被覆材を引き剥
がし、その下部にある情報の内容を見ることができ、し
かも、被覆材を剥がす時じんわりと剥がれて剥がしやす
い、はがきを提供することである。Therefore, the main object of the present invention is to make it possible to peel off the covering material relatively easily after receiving it at a legitimate recipient, to see the contents of the information underneath, and to gradually remove the covering material. To provide a postcard that is easily peeled off.
(課題を解決するための手段) この発明は、はがき台紙と、前記はがき台紙に貼着さ
れ、少なくともその一部分を被覆する被覆材とを含み、
前記被覆材は、基材の少なくともその表面の一部に剥離
剤層が形成され、前記剥離剤層の主面に、接着力調整層
が形成され、前記接着力調整層の主面に熱接着性樹脂層
が形成され、前記剥離剤層が形成された部分の基材は、
その一方端から他方端にかけて切目が形成され、前記切
目により基材が切り離し可能に形成され、前記被覆材
は、前記熱接着性樹脂層を溶融して前記はがき台紙に貼
着され、接着力調整層は、剥離剤層とは弱く接着され且
つ熱接着性樹脂層とは剥離剤層との接着強さと比して強
く接着されるとともに、貼着された基材を引き剥がすと
きに剥離剤層と接着力調整層とがじんわりと引き剥がさ
れるような組成のもので形成された、はがきである。(Means for Solving the Problems) The present invention includes a postcard mount, and a covering material attached to the postcard mount and covering at least a part thereof,
In the coating material, a release agent layer is formed on at least a part of the surface of the base material, an adhesive force adjustment layer is formed on a main surface of the release agent layer, and the adhesive material is thermally bonded to the main surface of the adhesive force adjustment layer. The conductive resin layer is formed, the base material of the portion where the release agent layer is formed,
A cut is formed from one end to the other end, and the base material is formed so as to be separable by the cut, and the coating material is applied to the postcard mount by melting the heat-adhesive resin layer and adjusting the adhesive force. The layer is weakly adhered to the release agent layer and strongly adhered to the heat-adhesive resin layer in comparison with the adhesive strength to the release agent layer, and when the adhered substrate is peeled off, the release agent layer is removed. This is a postcard formed of a composition such that the adhesive strength adjusting layer and the adhesive force adjusting layer are gradually peeled off.
(作用) 被覆材の裏面に形成された熱接着性樹脂層は、はがき
台紙の表面上にて、加熱され加圧されることにより、熱
接着性樹脂層を溶融してはがき台紙に貼着される。基材
と熱接着性樹脂層の間には、接着力調整層が形成されて
いるため、被覆材がはがき単片から剥がされる時、じん
わりと剥がれ剥がしやすい。(Function) The heat-adhesive resin layer formed on the back surface of the coating material is heated and pressed on the front surface of the postcard mount to melt the heat-adhesive resin layer and adhere to the postcard mount. You. Since the adhesive strength adjusting layer is formed between the base material and the heat-adhesive resin layer, the coating material is easily peeled off when peeled off from the post piece.
剥離剤層が形成された部分の基材は、その一方端から
他方端にかけて形成される切目により、比較的容易に引
き裂かれ、分離される。The base material at the portion where the release agent layer is formed is relatively easily torn and separated by a cut formed from one end to the other end.
(発明の効果) この発明によれば、被覆材をはがき台紙に貼着させる
のに熱接着性樹脂が用いられた場合、被覆材がはがき単
片から剥がされた後再接着させようと加熱され加圧され
ても、接着力調整層が基材と熱接着性樹脂の間に形成さ
れているため、じんわりと剥がれ剥がしやすい。(Effects of the Invention) According to the present invention, when a thermo-adhesive resin is used to attach a covering material to a postcard backing paper, the covering material is heated so as to be re-adhered after being peeled off from the postcard single piece. Even when the pressure is applied, the adhesive strength adjusting layer is formed between the base material and the heat-adhesive resin, so that the adhesive force adjusting layer is easily peeled off gradually.
そして、正規の受け取り人は、被覆材の基材に形成さ
れた切目により、容易に被覆材を引き裂き、はがき台紙
より被覆材を引き剥がすことができる。Then, the legitimate recipient can easily tear the coating material by the cuts formed in the base material of the coating material, and can peel off the coating material from the postcard mount.
この発明の上述の目的,その他の目的,特徴および利
点は、図面を参照して行う以下の実施例の詳細な説明か
ら一層明らかとなろう。The above and other objects, features and advantages of the present invention will become more apparent from the following detailed description of embodiments with reference to the drawings.
(実施例) 第1図は、この発明の一実施例であるはがきを示す斜
視図であり、第2図は第1図の線II−IIにおける部分断
面図である。(Embodiment) FIG. 1 is a perspective view showing a postcard according to an embodiment of the present invention, and FIG. 2 is a partial sectional view taken along line II-II in FIG.
このはがき10は、官製はがき大に形成されたはがき台
紙12とこのはがき台紙12の一部に貼着された被覆材14と
を含む。この被覆材14には切り離し用切目16が形成され
ている。The postcard 10 includes a postcard mount 12 formed into an official postcard size and a covering material 14 adhered to a part of the postcard mount 12. The coating material 14 has a cut 16 for cutting.
このはがき台紙12の表面に、特にたとえば金融や保険
の案内などのような秘密事項などの画線構成部に形成さ
れた部分に貼着される、貼着材14について、主として第
2図に基づいて説明する。FIG. 2 mainly shows a sticking material 14 to be stuck to the surface of the postcard mount 12 and particularly to a portion formed in an image forming part such as a secret matter such as a financial or insurance guide. Will be explained.
この貼着材14は、たとえば紙,合成樹脂フィルムなど
の比較的柔軟で、手や鋏などで切断することが可能な素
材をもって形成された基材18を含む。The sticking material 14 includes a base material 18 formed of a relatively flexible material such as paper or a synthetic resin film, which can be cut with hands or scissors.
この基材18の一方主面には、接着剤層20が形成され
る。この接着剤層20を形成する接着剤としては、たとえ
ばポリ酢酸ビニルエマルジョンなどのエマルジョン,ラ
テックス接着剤や、水ガラス,カゼインなどの水溶性接
着剤や、ポリウレタンなどの溶剤系反応型接着剤などが
ある。On one main surface of the base material 18, an adhesive layer 20 is formed. Examples of the adhesive forming the adhesive layer 20 include an emulsion such as a polyvinyl acetate emulsion, a latex adhesive, a water-soluble adhesive such as water glass and casein, and a solvent-based reactive adhesive such as polyurethane. is there.
この接着剤層20の一方主面には、隠ぺい層22が形成さ
れる。この隠ぺい層22はアルミホイルなどの隠ぺい力を
有するフィルム材を接着剤層20の接着力をもって積層す
ることによって形成されるが、たとえば隠ぺい性のある
インクで印刷することによって形成してもよい。On one main surface of the adhesive layer 20, a hiding layer 22 is formed. The concealing layer 22 is formed by laminating a film material having a concealing force such as aluminum foil with the adhesive force of the adhesive layer 20, but may be formed by printing with a concealing ink, for example.
隠ぺい層22の表面の一部には、たとえばポリエチレ
ン,シリコン樹脂,フッソ樹脂,パラフィン,ワックス
などの剥離剤をコーティングしてなる剥離剤層24が形成
される。On a part of the surface of the concealing layer 22, a release agent layer 24 formed by coating a release agent such as, for example, polyethylene, silicone resin, fluorine resin, paraffin, or wax is formed.
隠ぺい層22の剥離剤層24側表面には、接着力調整層26
が形成される。An adhesive strength adjusting layer 26 is provided on the surface of the concealing layer 22 on the side of the release agent layer 24.
Is formed.
接着力調整層26の主面には、たとえば熱接着性樹脂
を、加熱しながら押し出しコーティングし、あるいは溶
剤に溶解させまたは水に分散させてグラビアまたはシル
クスクリーンなどの印刷をすることによって、熱接着性
樹脂層28が形成される。On the main surface of the adhesive strength adjusting layer 26, for example, a hot-adhesive resin is extruded and coated while heating, or is dissolved in a solvent or dispersed in water and printed by gravure or silk screen to thereby form a heat-adhesive resin. The conductive resin layer 28 is formed.
この熱接着性樹脂層28には、たとえば60℃ないし200
℃の温度で軟化,溶融し、はがき台紙12に完全に接着す
ることができるように形成される。For example, the heat-adhesive resin layer 28
It is softened and melted at a temperature of ° C., and is formed so that it can be completely adhered to the postcard backing paper 12.
切り離し用切目16は、剥離剤層24の左右両端の少し内
側に形成される。また、切り離し用切目16は、基材18,
接着剤層20,隠ぺい層22,剥離剤層24,接着力調整層26お
よび熱接着性樹脂層28の上下両端に形成される。The separating cuts 16 are formed slightly inside the left and right ends of the release agent layer 24. In addition, the cut 16 for separation is made of a base material 18,
The adhesive layer 20, the concealing layer 22, the release agent layer 24, the adhesive strength adjusting layer 26, and the heat adhesive resin layer 28 are formed on both upper and lower ends.
そして、被覆材14の先端部分にて、ライン状に熱接着
性樹脂層28と基材18の隠ぺい層22側とが直接接着するよ
うに、剥離材層24が形成されていないライン状接着部30
が存在する。剥離材層24が形成された部分では、基材18
と熱接着性樹脂層28とは弱く接着され、また、剥離剤層
24が形成されていないライン状接着部30では、基材18と
熱接着性樹脂層28とは強く接着される。そこで、切り離
し用切目16で切り離せばよい。Then, at the tip portion of the covering material 14, a line-shaped bonding portion where the release material layer 24 is not formed so that the heat-adhesive resin layer 28 and the concealing layer 22 side of the base material 18 are directly bonded in a line. 30
Exists. In the portion where the release material layer 24 is formed, the base material 18
And the heat-adhesive resin layer 28 are weakly adhered to each other.
In the linear bonding portion 30 where no 24 is formed, the base material 18 and the thermo-adhesive resin layer 28 are strongly bonded. Therefore, it is sufficient to cut off at the cutout 16 for separation.
そして、はがき台紙12の表面には、秘密事項などを記
載してなる情報部32が形成される。なお、情報部32が熱
接着性樹脂層28および接着力調整層26を通して透視し得
るようにするためには、熱接着性樹脂層28および接着力
調整層26が透明または半透明である必要性がある。Then, on the surface of the postcard mount 12, an information section 32 in which a secret matter or the like is described is formed. In order that the information section 32 can be seen through the thermoadhesive resin layer 28 and the adhesive strength adjusting layer 26, the thermoadhesive resin layer 28 and the adhesive strength adjusting layer 26 need to be transparent or translucent. There is.
熱接着性樹脂層28の表面において、被覆材14ははがき
台紙12に貼着される。On the surface of the heat-adhesive resin layer 28, the covering material 14 is adhered to the postcard mount 12.
第3図はこのはがき10を切り離し用切目16で切り離し
て、被覆材14を剥がした状態を示す。情報部32は熱接着
性樹脂層28および接着力調整層26を通して透視できるよ
うになっている。FIG. 3 shows a state in which the postcard 10 is cut off at a cutout 16 and the covering material 14 is peeled off. The information section 32 can be seen through the thermo-adhesive resin layer 28 and the adhesive force adjusting layer 26.
なお、基材18の例としては、前記実施例の他、合成
紙,セロハン,ポリエチレン,ポリエステルなどのフィ
ルムまたはアルミホイルなどを挙げられるが、この被覆
材14をはがき台紙12に貼着したときに、剥離剤層24が形
成された部位の接着力調整層26との接着力に抗してこの
被覆剤14が不用意に層間剥離しないように、比較的柔軟
なものを選択するのがよい。Examples of the base material 18 include synthetic paper, cellophane, polyethylene, polyester and other films or aluminum foil in addition to the above-described embodiment. When the covering material 14 is attached to the postcard mount 12, It is preferable to select a relatively flexible material so that the coating material 14 is not inadvertently delaminated against the adhesive force of the portion where the release agent layer 24 is formed with the adhesive force adjusting layer 26.
また、この基剤18としてアルミホイルなどのように隠
ぺい性に優れたものを選択した場合には、前記実施例の
ように、隠ぺい層22を形成しなくてもよい。When a material having excellent concealing properties such as aluminum foil is selected as the base 18, the concealing layer 22 may not be formed as in the above-described embodiment.
接着力調整層26の材料は、剥離剤層24との関係で選択
される。たとえば、剥離剤層24を形成する樹脂として、
ポリエチレンを選択した場合には、接着力調整層26の材
料としては、たとえば、ポリビニルメチルエーテル,ポ
リビニルエチルエーテル,ポリビニルイソブチルエーテ
ル,カルボキシ変成アクリル樹脂,ポリアミド樹脂,塩
素化ポリプロピレン,エチレン・アクリル酸共重合体,
エチレン・酢酸ビニル共重合体,エチレン・エチルアク
リレート樹脂,スチレン・ブタジエン・スチレンのブロ
ック共重合体,スチレン・イソプレン・スチレンのブロ
ック共重合体,ポリエステル樹脂,テルペン樹脂,ロジ
ン,エステルロジン,水添ロジン,重合ロジン,ブチラ
ール樹脂,石油樹脂などやポリエチレンワックス,パラ
フィンワックス,モンタンワックス,マイクロクリスタ
リンワックスなどのワックス類や塩化ビニル・酢酸ビニ
ル共重合体,ニトロセルロースなどが選択できる。そし
て、これら単体か、または2種類以上を混合したものを
コーティングして接着力調整層26とすることができる。The material of the adhesive force adjusting layer 26 is selected in relation to the release agent layer 24. For example, as a resin forming the release agent layer 24,
When polyethylene is selected, examples of the material of the adhesive strength adjusting layer 26 include polyvinyl methyl ether, polyvinyl ethyl ether, polyvinyl isobutyl ether, carboxy-modified acrylic resin, polyamide resin, chlorinated polypropylene, and ethylene / acrylic acid copolymer. Union,
Ethylene / vinyl acetate copolymer, ethylene / ethyl acrylate resin, styrene / butadiene / styrene block copolymer, styrene / isoprene / styrene block copolymer, polyester resin, terpene resin, rosin, ester rosin, hydrogenated rosin , Polymerized rosin, butyral resin, petroleum resin and the like, waxes such as polyethylene wax, paraffin wax, montan wax and microcrystalline wax, vinyl chloride / vinyl acetate copolymer, nitrocellulose and the like can be selected. The adhesive force adjusting layer 26 can be formed by coating a single material or a mixture of two or more thereof.
発明者の実験によれば、上述の実施例において、ポリ
エチレン層すなわち剥離剤層24に、塩素化ポリプロピレ
ンと塩化ビニル・酢酸ビニル共重合体の混合溶液を塗布
して、接着力調整層26を形成し、これらの配合比率を、
塩化ビニル・酢酸ビニル共重合体100部に対して塩素化
ポリプロピレン40部〜240部とした場合、塩素化ポリプ
ロピレン120部を配合したときに最も良好な結果が得ら
れた。According to the experiment of the inventor, in the above-described embodiment, a mixed solution of chlorinated polypropylene and vinyl chloride / vinyl acetate copolymer was applied to the polyethylene layer, that is, the release agent layer 24, to form the adhesion adjusting layer 26. And, these compounding ratios,
When the amount of chlorinated polypropylene was 40 to 240 parts based on 100 parts of vinyl chloride / vinyl acetate copolymer, the best results were obtained when 120 parts of chlorinated polypropylene were blended.
いずれにしても、接着力調整層26は、剥離剤層24とは
弱く接着され且つ熱接着性樹脂層28とは剥離剤層24との
接着強さと比して強く接着されるとともに、貼着された
基材18を引き剥がすときに剥離剤層24と接着力調整層26
とがじんわりと引き剥がされるような組成のもので形成
されることが必要である。In any case, the adhesive strength adjusting layer 26 is weakly adhered to the release agent layer 24 and strongly adhered to the heat-adhesive resin layer 28 as compared with the adhesive strength to the release agent layer 24. The release agent layer 24 and the adhesive strength adjusting layer 26
It must be formed of a composition that can be gradually peeled off.
また、上述の実施例において、ポリエチレン層すなわ
ち剥離剤層24に、スチレン・ブタジエン・スチレンのブ
ロック共重合体と塩化ビニル・酢酸ビニル共重合体との
混合溶液を塗布して、接着力調整層26を形成し、それら
の配合比率を、塩化ビニル・酢酸ビニル共重合体100部
に対してスチレン・ブタジエン・スチレンのブロック共
重合体1部〜40部とした場合、スチレン・ブタジエン・
スチレンのブロック共重合体10部を配合したときに最も
良好な結果が得られた。Further, in the above-described embodiment, a mixed solution of a block copolymer of styrene / butadiene / styrene and a vinyl chloride / vinyl acetate copolymer was applied to the polyethylene layer When the mixing ratio thereof is 1 part to 40 parts of a block copolymer of styrene / butadiene / styrene with respect to 100 parts of a vinyl chloride / vinyl acetate copolymer, styrene / butadiene /
The best results were obtained when 10 parts of a styrene block copolymer were blended.
前記熱接着性樹脂の例としては、EVA系の接着剤が選
択される。その組成は、EVA(エチレン−酢酸ビニル共
重合体樹脂),粘着付与剤,ワックス,抗酸化剤からな
り、補助的に可塑剤,充填剤が添加される場合がある。As an example of the heat-adhesive resin, an EVA-based adhesive is selected. Its composition is composed of EVA (ethylene-vinyl acetate copolymer resin), a tackifier, a wax, and an antioxidant, and a plasticizer and a filler may be added in some cases.
粘着付与剤としては、部分水添ロジンのグリセリンエ
ステル,ロジンのグリセリンエステル,ペンタエリスリ
トール変成ロジン,石油樹脂,αメチルスチレン/ビニ
ルトルエン共重合体,テルペン油重合体,テルペンフェ
ノール油重合体などがある。Examples of the tackifier include glycerin ester of partially hydrogenated rosin, glycerin ester of rosin, modified rosin pentaerythritol, petroleum resin, α-methylstyrene / vinyltoluene copolymer, terpene oil polymer, terpene phenol oil polymer and the like. .
ワックスとしては、パラフィンワックス,マイクロク
リスタリンワックス,低分子量ポリエチレンワックス,
フィッシャートロプシュワックス,カスターワックス,
塩素化パラフィンなどがある。Waxes include paraffin wax, microcrystalline wax, low molecular weight polyethylene wax,
Fischer-Tropsch wax, Custer wax,
Chlorinated paraffin and the like.
抗酸化剤としては、ヒンダードフェノール系化合物,
サリチル酸系化合物,ベンゾフェノン系化合物,ベンゾ
トリアゾール系化合物,燐系化合物,硫黄系化合物,有
機金属系化合物などがある。As antioxidants, hindered phenol compounds,
There are salicylic acid compounds, benzophenone compounds, benzotriazole compounds, phosphorus compounds, sulfur compounds, organometallic compounds, and the like.
前記実施例以外の熱接着性樹脂としては、スチレン−
ブタジエン−スチレン共重合樹脂,スチレン−イソブレ
ン−スチレン共重合樹脂,ポリエチレン,エチレン−エ
チルアクリレート共重合樹脂,エチレン−アクリル酸共
重合樹脂,エチレン−アクリル酸メチル共重合樹脂,エ
チレン−メチルメタクリレート共重合樹脂,エチレン−
メタクリル酸共重合樹脂,アイオノマー樹脂,ポリメチ
ルペンテン樹脂,エチレン−ビニルアルコール共重合樹
脂,塩化ビニリデン樹脂,塩ビ−酢ビ共重合樹脂,ポリ
アミド樹脂,スチレン−アクリル共重合樹脂,ポリスチ
レン樹脂,ポリアクリル酸共重合樹脂,ポリエステル樹
脂,ポリウレタン樹脂,ワックス類などが選択できる。
これらを印刷・塗工するときには、加熱しながら、ある
いは溶剤に溶解させ、または水に分散して適宜用いれば
よい。As the heat-adhesive resin other than the above examples, styrene-
Butadiene-styrene copolymer resin, styrene-isobrene-styrene copolymer resin, polyethylene, ethylene-ethyl acrylate copolymer resin, ethylene-acrylic acid copolymer resin, ethylene-methyl acrylate copolymer resin, ethylene-methyl methacrylate copolymer resin , Ethylene-
Methacrylic acid copolymer resin, ionomer resin, polymethylpentene resin, ethylene-vinyl alcohol copolymer resin, vinylidene chloride resin, vinyl chloride-vinyl acetate copolymer resin, polyamide resin, styrene-acryl copolymer resin, polystyrene resin, polyacrylic acid Copolymer resins, polyester resins, polyurethane resins, waxes and the like can be selected.
When printing or coating them, they may be used as appropriate while heating, or dissolved in a solvent, or dispersed in water.
熱接着性樹脂層28を加熱により溶融させることによっ
て、被覆材14ははがき台紙12に貼着される。はがき台紙
12の最適な位置に被覆材14が重ね合わされたことを確認
したときに初めて加熱すれば、被覆材14がはがき台紙12
の表面の最適な位置に正確に接着される。したがって、
感圧型接着剤を用いたときのように正確な位置に貼り付
けられないといういわゆる貼りミスは起こらない。The coating material 14 is adhered to the postcard backing paper 12 by melting the heat adhesive resin layer 28 by heating. Postcard mount
When heating is performed for the first time when it is confirmed that the covering material 14 has been superimposed on the optimal position of the 12, the covering material 14
It is precisely glued to the optimal position on the surface of the device. Therefore,
There is no so-called sticking error that the sticking cannot be performed at an accurate position as in the case of using a pressure-sensitive adhesive.
また、貼着材14には、切り離し用切目16が形成されて
いるので、万が一、正規の受け取り人でない第3者に内
容が見られても、その際に切り離し用切目16が破られて
いて、内容が見られたことが正規の受け取り人にわか
る。In addition, since the cutout 16 is formed on the adhesive material 14, the cutout 16 is broken even if the contents are seen by a third party who is not a regular recipient. , The legitimate recipient knows that the content has been seen.
本発明によれば、接着力調整層26が基材18と熱接着性
樹脂層28の間に形成されているため、被覆材14がはがき
台紙12から剥がされる時、じんわりと剥がれ剥がしやす
い。According to the present invention, since the adhesive force adjusting layer 26 is formed between the base material 18 and the heat-adhesive resin layer 28, when the covering material 14 is peeled off from the postcard backing paper 12, it is easily peeled off.
第4図は、この発明の他の実施例を示す要部断面図で
あり、第5図は、第4図に示す実施例においてはがき台
紙12から被覆材14を剥がした状態を示す要部断面図であ
る。FIG. 4 is a cross-sectional view of a main part showing another embodiment of the present invention. FIG. 5 is a cross-sectional view of a main part showing a state where the covering material 14 is peeled off from the postcard backing sheet 12 in the embodiment shown in FIG. FIG.
この実施例では、被覆材14の先端部分にて、ライン状
に熱接着性樹脂層28と隠ぺい層22とが直接接着するよう
に、剥離剤層24および接着力調整層26が形成されていな
いライン状接着部30が存在する。このような構成によっ
ても、切り離し用切目16で切り離すことによって、容易
に被覆材14をはがき台紙12から剥がすことができる。In this embodiment, the release agent layer 24 and the adhesive strength adjusting layer 26 are not formed so that the heat-adhesive resin layer 28 and the concealing layer 22 are directly bonded in a line at the tip portion of the covering material 14. There is a linear bonding portion 30. Even with such a configuration, the coating material 14 can be easily peeled off from the postcard backing paper 12 by being separated at the separation cut 16.
第6図は、この発明のさらに他の実施例を示す要部断
面図である。この実施例では、特に、基材18,接着剤層2
0,隠ぺい層22,剥離剤層24,接着力調整層26および熱接着
性樹脂層28の上下両端に、剥離剤層24の縁に沿って、切
り離し用切目16aおよび切り離し用切目16bが形成され、
さらに切り離し用切目16aの内側に切り離し用切目16cが
形成される。FIG. 6 is a sectional view of a principal part showing still another embodiment of the present invention. In this embodiment, in particular, the base material 18, the adhesive layer 2
0, a separating cut 16a and a separating cut 16b are formed on the upper and lower ends of the concealing layer 22, the release agent layer 24, the adhesive strength adjusting layer 26, and the heat adhesive resin layer 28 along the edge of the release agent layer 24. ,
Further, a separation cut 16c is formed inside the separation cut 16a.
第6図に示す実施例では、切り離し用切目16aおよび1
6cの間の基剤18が、第7図に示すように、切り離せるよ
うになっている。なお、この切り離し用切目16aおよび1
6cの間の基材18の先端に、指あるいは爪を引っ掛けやす
くするために凹みを形成してもよく、あるいは指で摘み
やすくするために凸片を形成してもよい。In the embodiment shown in FIG. 6, the separating cuts 16a and 1
The base 18 during 6c is detachable as shown in FIG. Note that the cuts 16a and 1
A recess may be formed at the tip of the base material 18 between 6c to make it easy for a finger or a nail to be hooked, or a convex piece may be formed to make it easy to pick with a finger.
第8図は、この発明の別の実施例を示す要部平面図で
ある。この実施例では、特に、多数の切目34が被覆材14
の周囲に沿って形成される。また、それぞれの切目34
は、被覆材14を引き剥がす方向に見て隣合った切目34の
一部が重なるように、直線状の切目部分36aと円弧状の
切目部分36bとで構成される。このようにすれば、貼着
材14の中央部分が容易に引き剥がされる。FIG. 8 is a main part plan view showing another embodiment of the present invention. In this embodiment, in particular, a number of cuts 34
Is formed along the periphery of. In addition, each cut 34
Is composed of a straight cut portion 36a and an arc-shaped cut portion 36b such that adjacent cuts 34 overlap in the direction in which the covering material 14 is peeled off. By doing so, the central portion of the adhesive material 14 can be easily peeled off.
第9図は、第8図に示す実施例の変形例を示す要部平
面図である。この実施例では、特に、被覆材14を引き剥
がす方向に見て隣合った切目34の一部が重なるように、
基材18の周囲に直線状の各切目34が斜めに形成される。
このようにしても、被覆材14の中央部分が容易に引き剥
がされる。なお、第8図に示す実施例では、はがき台紙
12の一部に、被覆材14が貼着されているが、この実施例
のように、はがき台紙12全体に被覆材14が貼着されても
よい。FIG. 9 is a plan view of an essential part showing a modification of the embodiment shown in FIG. In this embodiment, in particular, so that part of the adjacent cuts 34 viewed in the direction of peeling the coating material 14 overlap,
Each linear cut 34 is formed obliquely around the base material 18.
Even in this case, the central portion of the covering material 14 can be easily peeled off. In the embodiment shown in FIG.
Although the covering material 14 is adhered to a part of the 12, the covering material 14 may be adhered to the entire postcard mount 12 as in this embodiment.
第1図は、この発明の一実施例におけるはがきを示す斜
視図であり、第2図は、第1図の線II−IIにおける部分
断面図である。 第3図は、はがき台紙から被覆材を剥がした状態を示す
部分断面図である。 第4図は、この発明の他の実施例を示す要部断面図であ
り、第5図は、第4図に示す実施例においてはがき台紙
から被覆材を剥がした状態を示す要部断面図である。 第6図は、この発明のさらに他の実施例を示す要部断面
図であり、第7図は、第6図に示す実施例においてはが
き台紙から被覆材を剥がした状態を示す要部断面図であ
る。 第8図は、この発明の別の実施例を示す要部平面図であ
る。 第9図は、第8図に示す実施例の変形例を示す要部平面
図である。 第10図は、従来のこの種のはがきの部分断面図である。 図において、10ははがき、12ははがき台紙、14は被覆
材、16は切り離し用切目、18は基材、24は剥離剤層、26
は接着力調整層、28は熱接着性樹脂層を示す。FIG. 1 is a perspective view showing a postcard according to an embodiment of the present invention, and FIG. 2 is a partial sectional view taken along line II-II in FIG. FIG. 3 is a partial cross-sectional view showing a state in which the covering material has been peeled off from the postcard mount. FIG. 4 is a cross-sectional view of a main part showing another embodiment of the present invention, and FIG. 5 is a cross-sectional view of a main part showing a state in which the covering material is peeled off from the postcard sheet in the embodiment shown in FIG. is there. FIG. 6 is a cross-sectional view of a main part showing still another embodiment of the present invention, and FIG. 7 is a cross-sectional view of a main part showing a state in which the covering material is peeled off from the postcard sheet in the embodiment shown in FIG. It is. FIG. 8 is a main part plan view showing another embodiment of the present invention. FIG. 9 is a plan view of an essential part showing a modification of the embodiment shown in FIG. FIG. 10 is a partial cross-sectional view of a conventional postcard of this type. In the figure, 10 is a postcard, 12 is a postcard mount, 14 is a covering material, 16 is a cutting cut, 18 is a base material, 24 is a release agent layer, 26
Denotes an adhesive force adjusting layer, and 28 denotes a thermoadhesive resin layer.
Claims (1)
覆する被覆材とを含み、 前記被覆材は、基材の少なくともその表面の一部に剥離
剤層が形成され、前記剥離剤層の主面に、接着力調整層
が形成され、前記接着力調整層の主面に熱接着性樹脂層
が形成され、前記剥離剤層が形成された部分の基材は、
その一方端から他方端にかけて切目が形成され、前記切
目により基材が切り離し可能に形成され、 前記被覆材は、前記熱接着性樹脂層を溶融して前記はが
き台紙に貼着され、 接着力調整層は、剥離剤層とは弱く接着され且つ熱接着
性樹脂層とは剥離剤層との接着強さと比して強く接着さ
れるとともに、貼着された基材を引き剥がすときに剥離
剤層と接着力調整層とがじんわりと引き剥がされるよう
な組成のもので形成された、 はがき。1. A postcard mount, and a coating material attached to the postcard mount and covering at least a part thereof, wherein the coating material has a release agent layer formed on at least a part of the surface of a base material. An adhesive strength adjustment layer is formed on the main surface of the release agent layer, a heat-adhesive resin layer is formed on the main surface of the adhesive force adjustment layer, and the base material on which the release agent layer is formed is
A cut is formed from one end to the other end, and the base material is formed so as to be separable by the cut, and the coating material is applied to the postcard mount by melting the heat-adhesive resin layer, and adjusting the adhesive force. The layer is weakly adhered to the release agent layer and strongly adhered to the heat-adhesive resin layer in comparison with the adhesive strength to the release agent layer, and the release agent layer is peeled off when the adhered substrate is peeled off. A postcard formed of such a composition that the adhesive strength adjusting layer and the adhesive strength adjusting layer are gradually peeled off.