JPH0655897A - Application tape and method for protecting decorative pressure sensitive adhesive sheet using the same - Google Patents
Application tape and method for protecting decorative pressure sensitive adhesive sheet using the sameInfo
- Publication number
- JPH0655897A JPH0655897A JP21011892A JP21011892A JPH0655897A JP H0655897 A JPH0655897 A JP H0655897A JP 21011892 A JP21011892 A JP 21011892A JP 21011892 A JP21011892 A JP 21011892A JP H0655897 A JPH0655897 A JP H0655897A
- Authority
- JP
- Japan
- Prior art keywords
- adhesive sheet
- application tape
- sensitive adhesive
- decorative
- adherend
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、装飾用粘着シートを被
着体に転写させる目的のアプリケーションテープ及び該
アプリケーションテープを用いた装飾用粘着シートの保
護方法に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an application tape for transferring a decorative pressure-sensitive adhesive sheet onto an adherend and a method for protecting the decorative pressure-sensitive adhesive sheet using the application tape.
【０００２】[0002]
【従来の技術】従来より装飾を施すべき被着体上に装飾
用粘着シートを貼り付ける作業（装飾用粘着シートの転
写）を行う場合の補助手段としてアプリケーションテー
プが利用されている。2. Description of the Related Art Conventionally, an application tape has been used as an auxiliary means for adhering a decorative pressure-sensitive adhesive sheet onto an adherend to be decorated (transfer of the decorative pressure-sensitive adhesive sheet).
【０００３】例えば、剥離体上に粘着剤層を介して貼着
された装飾用粘着シートを用い、該装飾用粘着シートを
所定形状、例えば文字又は図柄にカッティングし、カッ
ティング形成された文字又は図柄部分の装飾用粘着シー
トのみを残して、不要部分の装飾用粘着シートを剥離体
から剥がし（通常カス取りと呼ばれる）、次いで、剥離
体上に残った上記文字又は図柄部分の装飾用粘着シート
における背面（粘着剤層とは反対面）を感圧性粘着剤層
が設けられたアプリケーションテープに強く貼着させ
る。アプリケーションテープと文字又は図柄部分の装飾
用粘着シートとの接合は、上記両者をお互いに圧着する
ことにより行われる。For example, a decorative pressure-sensitive adhesive sheet adhered on a peeling body via a pressure-sensitive adhesive layer is used, and the decorative pressure-sensitive adhesive sheet is cut into a predetermined shape, for example, a letter or a pattern, and the cut letter or pattern is formed. In the decorative pressure-sensitive adhesive sheet of the character or pattern part remaining on the peelable body, peel off the decorative pressure-sensitive adhesive sheet of the unnecessary portion from the peeling body, leaving only the decorative pressure sensitive adhesive sheet of the portion The back surface (the surface opposite to the adhesive layer) is strongly adhered to the application tape provided with the pressure sensitive adhesive layer. The joining of the application tape and the decorative pressure-sensitive adhesive sheet of the character or pattern portion is performed by pressure-bonding the both to each other.
【０００４】次いで、上記アプリケーションテープから
剥離体を引き剥がすことにより、上記文字又は図柄部分
の装飾用粘着シートが該アプリケーションテープに仮着
された状態、すなわち転着作業がなされることになる。Then, the peeling body is peeled off from the application tape, so that the decorative adhesive sheet for the characters or patterns is temporarily attached to the application tape, that is, the transfer operation is performed.
【０００５】その後、装飾を施すべきの被着体上に、上
記アプリケーションテープに仮着されている上記文字又
は図柄部分の装飾用粘着シートの粘着剤層面を該被着体
に貼り付けた後、該アプリケーションテープの上から押
し当てて圧着し、続いて上記アプリケーションテープを
被着体から引き剥がす。After that, after the pressure-sensitive adhesive layer surface of the decorative pressure-sensitive adhesive sheet of the character or pattern portion temporarily adhered to the application tape is adhered to the adherend to be decorated, The application tape is pressed onto the application tape for pressure bonding, and then the application tape is peeled off from the adherend.
【０００６】その際、アプリケーションテープの装飾用
粘着シート背面に対する粘着力は、装飾用粘着シートの
被着体に対する粘着力より低いため、アプリケーション
テープを被着体から引き剥がすと、文字又は図柄部分の
装飾用粘着シートのみが被着体の表面に貼着したまま残
存し、装飾用粘着シートにおけるカッティングされた文
字又は図柄部分の貼付、すなわち転写が完成する。この
様なシートの考案は、既に提案され知られている（例え
ば実公昭５７─４０２７０号公報）。At that time, since the adhesive force of the application tape to the rear surface of the decorative adhesive sheet is lower than the adhesive force of the decorative adhesive sheet to the adherend, when the application tape is peeled off from the adherend, the character or the pattern portion is removed. Only the decorative pressure-sensitive adhesive sheet remains attached to the surface of the adherend, and the cut character or pattern portion of the decorative pressure-sensitive adhesive sheet is stuck, that is, transferred. The invention of such a sheet has already been proposed and known (for example, Japanese Utility Model Publication No. 57-40270).
【０００７】又、表示シール等に仮着させ、その上から
塗装を施した場合のマスキングとしての目的で考案され
た透明性を有する保護シートも提案されている（実開昭
５５─６９９９号公報）。Also, a transparent protective sheet has been proposed, which is devised for the purpose of masking when it is temporarily attached to a display seal or the like and is coated on it (Japanese Utility Model Publication No. 55-6999). ).
【０００８】[0008]
【発明が解決しようとする課題】上述の様に、実公昭５
７─４０２７０号公報のものは、装飾用粘着シートを目
的の被着体に転写させる補助手段として使用されるが、
被着体への貼付け後における装飾用粘着シートの保護と
しては、耐侯性がなく使用出来なかった。又、実開昭５
５─６９９９号公報に記載のものは、塗装前に目的の装
飾用粘着シートに貼付けることにより、マスキングの機
能を果たすには有効であるが、その後、該装飾用粘着シ
ートの保護層として使用には、耐侯性の面で不可能であ
る。さらに、装飾用粘着シートを被着体に貼付ける転写
作業を果たす機能は有していない。[Problems to be Solved by the Invention] As mentioned above,
No. 7-40270 is used as an auxiliary means for transferring a decorative pressure-sensitive adhesive sheet to an intended adherend.
It could not be used because it had no weather resistance as a protection for the decorative pressure-sensitive adhesive sheet after being attached to an adherend. Also, the actual exploitation 5
The one described in JP-A-5-6999 is effective for fulfilling the function of masking by being stuck to the intended decorative pressure-sensitive adhesive sheet before coating, but thereafter used as a protective layer of the decorative pressure-sensitive adhesive sheet. It is impossible in terms of weather resistance. Furthermore, it does not have the function of performing the transfer operation of attaching the decorative pressure-sensitive adhesive sheet to the adherend.
【０００９】本発明は、以上の問題点を鑑みて、装飾用
粘着シートを貼付ける作業（転写）を行う場合の補助手
段としての機能を果たすと共に被着体に貼合わせてその
まま使用することにより、装飾用粘着シートの保護シー
トとしての機能を果たすアプリケーションテープを提供
することである。In view of the above problems, the present invention functions as an auxiliary means when performing a work (transfer) for sticking a decorative pressure-sensitive adhesive sheet, and by sticking it to an adherend and using it as it is. To provide an application tape that functions as a protective sheet for a decorative adhesive sheet.
【００１０】[0010]
【課題を解決するための手段】本発明は、上記課題を解
決するため鋭意研究を行った結果、上記目的を達成する
手段として本発明を完成させたものである。すなわち、
剥離体上に重ねられた所定形状の装飾用粘着シートを剥
離体から引き剥がし、目的の被着体に転写させるアプリ
ケーションテープであって、該アプリケーションテープ
基材が透明性を有し、且つ耐侯性向上材が含有されてな
ることを特徴とするアプリケーションテープである。The present invention has been completed as a means for achieving the above object as a result of earnest research to solve the above problems. That is,
An application tape in which a decorative pressure-sensitive adhesive sheet having a predetermined shape stacked on a peeling body is peeled from the peeling body and transferred to a target adherend, and the application tape base material has transparency and weather resistance. An application tape characterized by containing an improving material.
【００１１】及び、アプリケーションテープを剥離体上
に重ねられた所定形状の装飾用粘着シートに重ね合わ
せ、上記アプリケーションテープと装飾用粘着シートを
密着させた後、該所定形状の装飾用粘着シートを剥離体
から引き剥がし、目的の被着体に貼付ける際、耐侯性向
上材を含有するアプリケションテープを保護層として装
飾用粘着シートに重ね合わせた状態で被着体に貼付ける
ことを特徴とする装飾用粘着シートの保護方法である。
以下に本発明についての内容を詳細に説明する。本発
明のアプリケーションテープの構成は、基材層と粘着剤
層からなる。本発明におけるアプリケーションテープの
基材層としては、着色されていないで且つ全透過率が５
０％以上好ましくは、８０％以上を有する合成樹脂が使
用出来、その様な合成樹脂としては、ポリウレタン、ポ
リ塩化ビニル、ポリオレフィン、ポリエステル系樹脂等
が挙げられる。さらにアプリケーションテープとしての
基材物性の設計の容易さ及び成形加工性の容易さの点で
好ましくは、塩化ビニル系樹脂が挙げられる。基材層の
厚みとしては、３０〜１００μｍ使用上の使い易さか
ら、好ましくは４０〜８０μｍである。耐候性向上剤と
しては、紫外線による基材層の劣化、変色を防止出来る
もので透明性を阻害しないものが使用出来、通常の紫外
線吸収剤が好ましくは挙げられる。その例としては、例
えばベンゾフェノン系、ベンゾトリアゾール系、サリチ
ル酸エステル系およびシアノアクリレート系等の化合物
が挙げられる。さらにヒンダードアミン（ＨＡＬＳ）等
も配合することも出来る。上記紫外線吸収剤剤の添加量
としては、樹脂成分１００重量部に対して０．１〜１０
重量部、好ましくは０．５〜２重量部が良い。Further, the application tape is superposed on a decorative adhesive sheet having a predetermined shape which is laminated on the peeling body, and the application tape and the decorative adhesive sheet are brought into close contact with each other, and then the decorative adhesive sheet having the predetermined shape is peeled off. When peeled off from the body and applied to the target adherend, the application tape containing the weather resistance improving material is adhered to the adherend in a state of being overlapped with the decorative pressure-sensitive adhesive sheet as a protective layer. This is a method of protecting an adhesive sheet for decoration.
The details of the present invention will be described below. The constitution of the application tape of the present invention comprises a base material layer and an adhesive layer. The base layer of the application tape of the present invention is not colored and has a total transmittance of 5
A synthetic resin having 0% or more, preferably 80% or more can be used, and examples of such a synthetic resin include polyurethane, polyvinyl chloride, polyolefin and polyester resins. Further, from the viewpoint of easy design of physical properties of the substrate as an application tape and easy moldability, a vinyl chloride resin is preferable. The thickness of the base material layer is preferably 30 to 100 μm, and is preferably 40 to 80 μm from the viewpoint of ease of use. As the weather resistance improver, those that can prevent deterioration and discoloration of the base material layer by ultraviolet rays and do not impair transparency can be used, and ordinary ultraviolet absorbers are preferably mentioned. Examples thereof include compounds such as benzophenone-based, benzotriazole-based, salicylate-based and cyanoacrylate-based compounds. Further, hindered amine (HALS) and the like can be added. The amount of the ultraviolet absorber agent added is 0.1 to 10 parts by weight relative to 100 parts by weight of the resin component.
The amount is preferably 0.5 to 2 parts by weight.
【００１２】本発明に使用可能な塩化ビニル系樹脂シー
ト用の樹脂としては、通常使用されているカレンダ加工
法およびキャスト法により製造され、利用されるもので
あればであれば特に限定されるものではなく、上記塩化
ビニル樹脂としては、塩化ビニルホモポリマーの他に、
約３０重量％以下の共重合成分を含有する塩化ビニル共
重合体および塩化ビニルホモポリマーと塩化ビニル共重
合体とのブレンド物等が利用出来る。この様な共重合成
分の例としては、エチレン、プロピレン、ブテン、アク
リル酸エステル、塩化ビニリデン、ビニルエステル、ビ
ニルエーテル、酢酸ビニル等が挙げられる。The vinyl chloride resin sheet resin usable in the present invention is not particularly limited as long as it is produced and used by a commonly used calendering method and casting method. Instead of the vinyl chloride homopolymer, as the vinyl chloride resin,
A vinyl chloride copolymer containing about 30% by weight or less of a copolymerization component, a blend of a vinyl chloride homopolymer and a vinyl chloride copolymer, and the like can be used. Examples of such copolymerization component include ethylene, propylene, butene, acrylic acid ester, vinylidene chloride, vinyl ester, vinyl ether, vinyl acetate and the like.
【００１３】さらにこれら塩化ビニル系樹脂に、塩化ビ
ニル系樹脂以外のポリマー、例えばポリエチレン、ポリ
プロピレン、ブテン、アクリル樹脂、ポリ塩化ビニリデ
ン樹脂を約３０％以下の割合でブレンドした塩化ビニル
系樹脂ブレンド物も利用出来る。Further, a vinyl chloride resin blend obtained by blending these vinyl chloride resins with a polymer other than the vinyl chloride resin, for example, polyethylene, polypropylene, butene, acrylic resin, polyvinylidene chloride resin at a ratio of about 30% or less is also available. Available.
【００１４】上記使用可能な塩化ビニル系樹脂をシート
状に成形加工する場合は、該樹脂層中に耐侯性材料の他
に可塑剤、安定剤、抗酸化剤、滑剤等の添加剤を適宜選
択含有させることが出来る。When the above usable vinyl chloride resin is molded into a sheet, additives such as a plasticizer, a stabilizer, an antioxidant and a lubricant are appropriately selected in the resin layer in addition to the weather resistant material. It can be included.
【００１５】本発明のアプリケーションテープは、装飾
用粘着シートを被着体に貼付けた後、該装飾用粘着シー
トから引き剥がす必要がなくそのまま保護シートとして
使用するため、粘着剤層としては、室温において粘着性
を示し且つ、耐侯性を有するものであれば良く、通常の
アプリケーションテープの粘着剤層に必要な特性である
装飾用粘着シートの粘着剤が示す粘着力より低いレベル
の感圧性粘着剤に限定されるものではなく装飾用粘着シ
ートの粘着剤と同じものを使用出来る。例えば、ゴム系
粘着剤、アクリル粘着剤、ウレタン粘着剤、シリコン粘
着剤、酢酸ビニル粘着剤及びそれらの適当な混合系粘着
剤が挙げられるが透明性を保持するための耐侯性の点で
はアクリル粘着剤が好ましい。The application tape of the present invention does not need to be peeled off from the decorative pressure-sensitive adhesive sheet after it is attached to the adherend, and is used as it is as a protective sheet. Any pressure sensitive adhesive that exhibits adhesiveness and weather resistance can be used as a pressure-sensitive adhesive with a level lower than the adhesive strength of the adhesive for decorative adhesive sheets, which is a characteristic required for the adhesive layer of ordinary application tapes. It is not limited, and the same adhesive as the decorative adhesive sheet can be used. Examples include rubber-based adhesives, acrylic adhesives, urethane adhesives, silicone adhesives, vinyl acetate adhesives, and suitable mixed adhesives thereof, but acrylic adhesives in terms of weather resistance for maintaining transparency. Agents are preferred.
【００１６】さらに本発明におけるアプリケーションテ
ープの粘着剤層は、使用に至までは剥離シートで保護さ
れていても良い。使用可能な剥離シートとしては、支持
力を有し、且つ基材層の有する感圧性粘着剤層を剥離す
ることが可能な剥離層を表面に有しているものであれば
特に限定されるものでなく、例えば、不織布、合成繊
維、ネット、紙、プラスチックフィルム、又はポリエチ
レンフィルム等のポリオレフィンフィルムと紙との積層
物等の各種シート状体に、剥離層を形成するための材料
をコートしたものを好ましくは挙げることが出来る。Further, the adhesive layer of the application tape of the present invention may be protected by a release sheet until use. The release sheet that can be used is not particularly limited as long as it has a supporting force and has a release layer capable of releasing the pressure-sensitive adhesive layer of the base material layer on the surface. However, for example, various sheet-like bodies such as nonwoven fabrics, synthetic fibers, nets, papers, plastic films, or laminates of polyolefin films such as polyethylene films and papers, etc., coated with a material for forming a release layer. Can be preferably mentioned.
【００１７】この様にして作成したアプリケーションテ
ープの粘着剤層面を、所望の文字又は図柄にカッティン
グ形成されて剥離体上に残存している装飾用粘着シート
の少なくとも全体以上を覆う面積になる様に重ね合わ
せ、手あるいは圧着具により上記アプリケーションテー
プの上からなぞる様にして押し当てるこによりアプリケ
ーションテープと装飾用粘着シート背面を密着させる。The pressure-sensitive adhesive layer surface of the application tape prepared in this manner has an area covering at least the entire decorative pressure-sensitive adhesive sheet remaining on the peeling body after being cut into desired characters or patterns. The application tape and the rear surface of the adhesive sheet for decoration are brought into close contact with each other by stacking and pressing the application tape by tracing it over the application tape with a hand or a crimping tool.
【００１８】次いで、アプリケーションテープを剥離体
から引き剥がすことにより、文字又は図柄部分の装飾用
粘着シートを該剥離体から引き剥がし、装飾を施すべき
所望の被着体に貼付けた後、アプリケーションテープを
そのまま装飾用粘着シートの上に貼付したままにするこ
とにより被着体への貼付け作業、すなわち転写と共に装
飾用粘着シートの保護を可能とする。Next, by peeling off the application tape from the peeling body, the decorative pressure-sensitive adhesive sheet for characters or patterns is peeled off from the peeling body and attached to a desired adherend to be decorated, and then the application tape is applied. By leaving it stuck on the decorative pressure-sensitive adhesive sheet as it is, it is possible to protect the decorative pressure-sensitive adhesive sheet with the work of sticking it to an adherend, that is, transfer.
【００１９】[0019]
【作用】本発明によれば、基材が透明性を有すると共
に、耐侯性を有するアプリケーションテープとなる。According to the present invention, the application tape has a weather resistant property as well as a transparent base material.
【００２０】[0020]
（実施例）重合度１５００の塩化ビニル樹脂１００重量
部にアジピン酸エステル系高分子可塑剤（ＤＯＡ、積水
化学社製）、２５重量部、耐候性材料として、ベンゾフ
ェノン系紫外線吸収剤（ＴＩＮＡＶＩＮ３１２、チバガ
イギ製）、バリウム亜鉛系安定剤（ＢＺ１００Ｊ、勝田
化工社製）を配合したものをカレンダー法により、６０
μｍの厚みに成形した軟質塩化ビニル樹脂シートを基材
層（１）に、３０μｍのアクリル系粘着剤層（２）を形
成したものからなるアプリケーションテープ（４）を作
成した（図１）。この様にして作成したアプリケーショ
ンテープの全光線透過率を測定したところ８０％であっ
た。(Example) 100 parts by weight of a vinyl chloride resin having a degree of polymerization of 1500, 25 parts by weight of an adipic acid ester-based polymer plasticizer (DOA, manufactured by Sekisui Chemical Co., Ltd.), and a benzophenone-based ultraviolet absorber (TINAVIN312, Cibagaigi) as a weather resistant material. 60) by a calendering method and a barium-zinc stabilizer (BZ100J, manufactured by Katsuta Kako Co., Ltd.).
An application tape (4) was prepared by forming a 30 μm acrylic adhesive layer (2) on a substrate layer (1) of a soft vinyl chloride resin sheet molded to a thickness of μm (FIG. 1). The total light transmittance of the thus prepared application tape was measured and found to be 80%.
【００２１】次に、屋内装飾用粘着シート（商品名：ハ
ルカラー赤色、積水化学社製）にコンピュータカッティ
ングマシン（商品名：ハルジくん、積水化学社製）を用
い「ＡＢＣＤＥ」の文字を大きさ１５ｍｍ角にカッティ
ングした。次いで、上記カッティング形成された文字部
分の装飾用粘着シート（５）を残し、それ以外の不要部
分の装飾用粘着シートを手で、剥離体（６）から剥ぎ取
ることによりカス取りした後、上記作成のアプリケーシ
ョンテープを少なくとも、上記カッティング形成された
文字部分の装飾用粘着シート（５）より大きい面積にし
たものを剥離体（６）上に残った上記文字部分の装飾用
粘着シート（５）背面上に重ね合わせた後、圧着具
（３）で該アプリケーションテープ（４）上をなぞる様
にして両者を密着させた（図２）。次いで、アプリケー
ションテープ（４）を剥離体（６）から引き剥がすこと
により、文字部分の装飾用粘着シート（５）を剥離体
（６）から引き剥がし（図３）、スチール板（７）にア
プリケーションテープ（４）と共に貼付けた。（図４） この様にしてスチール板（６）に貼付けた文字部分の装
飾用粘着シート（５）とアプリケーションテープ（４）
の積層体を耐候性試験機（サンシャインウエザオメー
タ）により、装飾用粘着シート及びアプリケーションテ
ープの色劣化、基材劣化具合を評価したところ、１００
０時間経過しても全く変化していなかった。Next, a computer cutting machine (trade name: Haruji-kun, manufactured by Sekisui Chemical Co., Ltd.) was used for an indoor decorative adhesive sheet (trade name: Hal color red, manufactured by Sekisui Chemical Co., Ltd.), and a size of "ABCDE" was 15 mm. Cut into the corner. Then, the decorative pressure-sensitive adhesive sheet (5) for the cut character portion is left, and the unnecessary decorative pressure-sensitive adhesive sheet for the other unnecessary portions is removed by hand from the peeling body (6), At least the application tape prepared has a larger area than the decorative adhesive sheet (5) for the cut character portion, and the decorative adhesive sheet (5) for the character portion remaining on the peeling body (6) After superposing them on top of each other, the application tape (4) was traced with the crimping tool (3) to bring them into close contact with each other (FIG. 2). Then, by peeling off the application tape (4) from the peeling body (6), the decorative pressure-sensitive adhesive sheet (5) of the character portion is peeled off from the peeling body (6) (FIG. 3), and applied to the steel plate (7). It was attached together with the tape (4). (Fig. 4) The decorative adhesive sheet (5) for the character portion and the application tape (4) attached to the steel plate (6) in this way
The laminate was evaluated for color deterioration and base material deterioration of the decorative pressure-sensitive adhesive sheet and application tape by a weather resistance tester (Sunshine Weatherometer).
It did not change at all even after 0 hour.
【００２２】比較として通常使用されている延伸ポリプ
ロピレンフィルムを基材層として使用し、粘着剤層にア
クリル系粘着剤を使用したものをアプリケーションテー
プとして使用したこと以外は、実施例と同様の方法、内
容にて装飾用粘着シートの色劣化具合を評価したとこ
ろ、５００時間を経過したところで、アプリケーション
テープは黄変し、装飾用粘着シートの色劣化が見られ
た。As a comparative example, a stretched polypropylene film which is usually used is used as a base material layer, and an acrylic tape is used as an adhesive layer as an application tape. When the color deterioration of the decorative pressure-sensitive adhesive sheet was evaluated by the contents, the application tape turned yellow after 500 hours, and the color deterioration of the decorative pressure-sensitive adhesive sheet was observed.
【００２３】[0023]
【発明の効果】本発明のアプリケーションテープを、剥
離体上の装飾用粘着シートに重ね合わせた後、上記アプ
リケーションテープと装飾用粘着シートを密着させた
後、該装飾用粘着シートを剥離体から引き剥がし、目的
の被着体に貼付けることにより、装飾用粘着シートを転
写することが出来る。The application tape of the present invention is superposed on a decorative pressure-sensitive adhesive sheet on a peeling body, and after the application tape and the decorative pressure-sensitive adhesive sheet are brought into close contact with each other, the decorative pressure-sensitive adhesive sheet is pulled from the peeling body. The decorative pressure-sensitive adhesive sheet can be transferred by peeling it off and attaching it to the intended adherend.
【００２４】又、装飾用粘着シートを目的の被着体に貼
付けた後、アプリケーションテープを引き剥がさない
で、装飾用粘着シート上に重ね合わせた状態で被着体に
貼付けることにより、耐候性を有しない装飾用粘着シー
トの耐候性を改善する効果が得られ、さらには装飾用粘
着シートの表面に対する接触等による傷付きを防止する
ことが出来る。After the decorative pressure-sensitive adhesive sheet is applied to the intended adherend, the application tape is not peeled off, and the decorative adhesive sheet is laminated on the adherend to be adhered to the adherend. It is possible to obtain the effect of improving the weather resistance of the decorative pressure-sensitive adhesive sheet that does not have the above-mentioned property, and further it is possible to prevent scratches due to contact with the surface of the decorative pressure-sensitive adhesive sheet.
【図１】 は本発明のアプリケーションテープの斜視図
である。FIG. 1 is a perspective view of an application tape of the present invention.
【図２】 は本発明において、アプリケーションテープ
の使用状態を示す断面図である。FIG. 2 is a sectional view showing a usage state of an application tape in the present invention.
【図３】 は本発明において、装飾用粘着シートの転着
状態を示す斜視図である。FIG. 3 is a perspective view showing a transfer state of the decorative pressure-sensitive adhesive sheet in the present invention.
【図４】 は本発明において、アプリケーションテープ
の使用状態を示す斜視図である。FIG. 4 is a perspective view showing a usage state of an application tape in the present invention.
１ アプリケーションテープの基材層 ２ アプリケーションテープの粘着剤層 ３ 圧着具 ４ アプリケーションテープ ５ 文字部分の装飾用粘着シート ６ 剥離体 ７ スチール板 1 Base layer of application tape 2 Adhesive layer of application tape 3 Crimping tool 4 Application tape 5 Adhesive sheet for decorative characters 6 Peeling body 7 Steel plate
フロントページの続き (51)Int.Cl.5 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｇ０９Ｆ 3/10 7028−5Ｇ Continuation of front page (51) Int.Cl. 5 Identification number Office reference number FI technical display location G09F 3/10 7028-5G
Claims (2)
着シートを剥離体から引き剥がし、目的の被着体に転写
させるアプリケーションテープであって、該アプリケー
ションテープ基材が透明性を有し、且つ耐侯性向上剤が
含有されてなる合成樹脂からなることを特徴とするアプ
リケーションテープ。1. An application tape for peeling a decorative pressure-sensitive adhesive sheet having a predetermined shape, which is laminated on a peeling body, from the peeling body and transferring it to an intended adherend, wherein the application tape base material is transparent. And an application tape comprising a synthetic resin containing a weather resistance improver.
られた所定形状の装飾用粘着シートに重ね合わせ、上記
アプリケーションテープと装飾用粘着シートを密着させ
た後、該所定形状の装飾用粘着シートを剥離体から引き
剥がし、目的の被着体に貼付ける際、耐侯性向上剤を含
有するアプリケションテープを保護層として装飾用粘着
シートに重ね合わせた状態で被着体に貼付けることを特
徴とする装飾用粘着シートの保護方法。2. An application tape is superposed on a decorative adhesive sheet having a predetermined shape, which is laminated on a peeling body, and the application tape and the decorative adhesive sheet are brought into close contact with each other, and then the decorative adhesive sheet having the predetermined shape is peeled off. When peeled off from the body and attached to the target adherend, the application tape containing the weather resistance improver is attached to the adherend in a state of being superimposed on the decorative pressure-sensitive adhesive sheet as a protective layer. How to protect decorative adhesive sheets.