JP2874828B2 - Photosensitive transfer sheet - Google Patents
Photosensitive transfer sheetInfo
- Publication number
- JP2874828B2 JP2874828B2 JP5348613A JP34861393A JP2874828B2 JP 2874828 B2 JP2874828 B2 JP 2874828B2 JP 5348613 A JP5348613 A JP 5348613A JP 34861393 A JP34861393 A JP 34861393A JP 2874828 B2 JP2874828 B2 JP 2874828B2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- transfer sheet
- photosensitive transfer
- photosensitive
- release layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本発明は、多色画像形成材料に関
するものであり、更に詳しくは、主として写真製版工程
で不可欠な校正作業に用いうるプレプレスカラープルー
フを得るために使用する感光性転写シートに関するもの
である。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a multicolor image forming material, and more particularly to a photosensitive transfer used for obtaining a prepress color proof which can be used mainly for a proofing work indispensable in a photomechanical process. It is about a sheet.
【０００２】[0002]
【従来の技術】カラー印刷における、印刷の仕上がりの
色・調子等をチェックするためのプレプレスカラープル
ーフに関しては、従来からその形態により主として、オ
ーバーレイ法およびサープリント法とがある。2. Description of the Related Art In color printing, a prepress color proof for checking the color and tone of a finished print is mainly classified into an overlay method and a surprint method depending on its form.
【０００３】オーバーレイ法は、各色分解原版を用い
て、着色感光剤を塗布した透明支持体に各色に応じプリ
ントし、白色のシート上に各色重ね合わせて校正を行な
うものである（USP3136637、USP3221553、USP332668
2）。この方法はプルーフを迅速に作ることができ、更
に２または３色を適当に組み合わせることによって分色
校正刷りとして利用することができる。しかしながら、
この種のタイプは各々の透明支持体をも重ね合わせるの
で、濁りを生じ、印刷機や校正機で刷った印刷物に比較
して感覚的に著しい差異を生じる。In the overlay method, each color separation master is printed in accordance with each color on a transparent support coated with a color sensitizer, and each color is superimposed on a white sheet for calibration (USP3136637, USP3221553, USP332668
2). This method can quickly produce a proof and can be used as a color proof by appropriately combining two or three colors. However,
Since this type also overlaps the respective transparent supports, turbidity is produced, and there is a noticeable difference in comparison to printed matter printed on a printing press or a proofing machine.
【０００４】サープリント方式による多色画像を形成す
る方法は種々提案されている。即ち、感圧接着剤による
方法は、主として支持体上に着色感光層、感圧接着層の
順で積層されており、接着層面を転写すべき白色ベース
台紙と十分加圧密着させて後支持体を剥がすことによ
り、着色感光層が接着層と共に台紙上に転写される。し
かる後該着色感光層の色調に応じた色分解原稿を密着露
光し、専用現像液で現像、乾燥して分解像を作る。この
上に更に上記とは異なった色について同じ操作を繰り返
して多色画像を形成する。（特公昭47-27441号公報）Various methods for forming a multicolor image by a surprint method have been proposed. That is, in the method using a pressure-sensitive adhesive, a colored photosensitive layer and a pressure-sensitive adhesive layer are mainly laminated on a support in this order. By peeling off, the colored photosensitive layer is transferred onto the backing paper together with the adhesive layer. Thereafter, a color separation document corresponding to the color tone of the colored photosensitive layer is exposed in close contact, developed with a dedicated developer, and dried to form a separation image. Further, the same operation is repeated for colors different from the above to form a multicolor image. (Japanese Patent Publication No. 47-27441)
【０００５】また、感圧接着剤を使用せず熱により転写
使用するものは種々提案されている。例えば支持体上に
ある温度以上で粘着性を示す着色光重合層を設けたもの
に原稿を重ね、密着露光すれば、露光部は粘着性を示さ
なくなるので未露光部のみ、紙ベースに転写するもの
（USP3203805）。または支持体上の着色重合層を露光現
像した後、着色画像を感熱接着剤を有するベースに熱転
写するもの（USP4304836）。または支持体／剥離層／着
色感光層からなるものを露光・現像し、着色画像を得た
後、感熱接着剤を該接着面もしくは受像面に塗布など
し、熱転写する方法などがある（USP3721557、特公昭46
-15326号公報、特公昭49-441号公報）。[0005] Further, there have been proposed various devices which use transfer by heat without using a pressure-sensitive adhesive. For example, if a document is overlaid on a support provided with a colored photopolymer layer exhibiting adhesiveness at a certain temperature or higher and exposed in close contact, only the unexposed portions are transferred to the paper base because the exposed portions no longer exhibit adhesiveness. Things (USP3203805). Alternatively, after exposing and developing a colored polymer layer on a support, a colored image is thermally transferred to a base having a heat-sensitive adhesive (USP4304836). Alternatively, there is a method of exposing and developing a support / release layer / colored photosensitive layer to obtain a colored image, applying a heat-sensitive adhesive to the bonding surface or the image receiving surface, and performing thermal transfer (USP3721557, Tokiko 46
-15326, JP-B-49-441).
【０００６】本発明の感光性転写シートが用いられる多
色画像形成方法は、透明支持体上に強く接着している透
明性の剥離層、剥離層から剥離可能である熱融着性の透
明な中間層、着色感光層が積層された感光性転写シート
を、(1) 陰画原稿を通して該感光材料を活性光線によ
り密着露光させた後、非露光部を現像処理し、画像を形
成する段階、(2) 該形成画像面を更に熱融着層を有す
る被転写材料の熱融着面と密着させ、加熱加圧させた
後、透明支持体を中間層から剥ぎとり、着色画像を中間
層と共に被転写材料に転写させる段階、で処理すること
からなり、段階(1) で着色感光層の色調の異なるものを
用意して、それぞれの色調に応じて、陰画原稿を選択
し、密着露光、現像処理し、画像を形成し、段階(2) で
それらのうちの特定の色調の着色画像を被転写材料に転
写した後、(3) 更に上記とは異なる色調の着色画像の
形成された感光材料の画像面を、段階(2) で得た被転写
材料の既転写面と密着させ、加熱加圧させた後、透明支
持体を中間層から剥ぎとり、着色画像を中間層と共に被
転写材料の既転写面上に転写させる段階、で処理するこ
とからなり、３色目以降は、段階(3) を繰り返すことを
特徴とする多色画像の形成方法である。The method for forming a multicolor image using the photosensitive transfer sheet of the present invention comprises a transparent release layer strongly adhered to a transparent support, and a heat-fusible transparent layer peelable from the release layer. An intermediate layer, a photosensitive transfer sheet having a colored photosensitive layer laminated thereon, (1) after closely exposing the photosensitive material with actinic light through a negative document, developing a non-exposed portion to form an image, 2) The formed image surface is further brought into close contact with the heat-fused surface of the material to be transferred having a heat-fused layer, and after heating and pressing, the transparent support is peeled off from the intermediate layer, and the colored image is coated together with the intermediate layer. In the step (1), different color tone of the colored photosensitive layer is prepared, a negative document is selected according to each color tone, and contact exposure and development processing are performed. And forming an image, and coloring certain tones of them in step (2) After transferring the image to the material to be transferred, (3) the image surface of the photosensitive material on which the colored image having a different color tone is formed is brought into close contact with the transferred surface of the material to be transferred obtained in step (2). After heating and pressurizing, the transparent support is peeled off from the intermediate layer, and the colored image is transferred together with the intermediate layer onto the already-transferred surface of the material to be transferred. This is a method for forming a multicolor image, characterized by repeating (3).
【０００７】この方法は、形成された画像を１色ずつ被
転写材料上に順次転写するので、４色の露光作業が同時
に行なえる為、作業時間を短縮できる利点を持ってい
る。According to this method, since the formed image is sequentially transferred one by one onto the material to be transferred, the exposure operation for four colors can be performed simultaneously, and thus the method has an advantage that the operation time can be reduced.
【０００８】しかし、この方法における感光性転写シー
トの着色感光層は、異なった色調を有すると共に、異な
った活性光線吸収特性の着色剤を含むため感度に差が生
じ、最適露光量が異なるという欠点があった。例えばブ
ラックの感光性転写シートは、ブラック顔料による活性
光線の吸収特性のため他の色調の感光性転写シートに比
べて、著しく感度が劣り、他の色と同等の画像強度を得
るためには、より多くの露光量が必要であった。そのた
め、４色の同時露光処理が可能であるという利点を十分
活かすことができなかった。[0008] However, the disadvantage of this method is that the colored photosensitive layer of the photosensitive transfer sheet has a different color tone and contains a colorant having a different absorption characteristic of active light, resulting in a difference in sensitivity and a different optimum exposure amount. was there. For example, a black photosensitive transfer sheet is significantly inferior in sensitivity to photosensitive transfer sheets of other colors due to absorption characteristics of actinic rays by a black pigment, and in order to obtain an image intensity equivalent to other colors, More exposure was needed. Therefore, the advantage that the simultaneous exposure processing of four colors is possible cannot be fully utilized.
【０００９】[0009]
【発明が解決しようとする課題】本発明は上記多色画像
形成方法において、異なった色調を有すると共に異なっ
た活性光線吸収特性の着色剤を含む各色感光層の感度を
同一にし、作業性を向上させると共に、より高精度のプ
レプレスカラープルーフを得るための多色画像形成材料
を提供することである。SUMMARY OF THE INVENTION According to the present invention, in the above-mentioned multicolor image forming method, the sensitivities of the respective color photosensitive layers having different color tones and containing a colorant having a different active light absorption characteristic are made the same to improve workability. It is another object of the present invention to provide a multicolor image forming material for obtaining a more accurate prepress color proof.
【００１０】[0010]
【課題を解決するための手段】本発明者らは、剥離層に
活性光線反射性物質を添加し、反射率を上げることによ
り着色感光層の感光速度が速くなることを発見した。す
なわち着色感光層を透過した活性光線（反応に使用され
なかった活性光線）を剥離層で反射させ、反射特性を変
化させることにより感光層の感度をコントロールできる
ことを見いだした。Means for Solving the Problems The present inventors have discovered that the actinic light-reflecting substance is added to the release layer to increase the reflectance, thereby increasing the photosensitive speed of the colored photosensitive layer. That is, it has been found that the sensitivity of the photosensitive layer can be controlled by reflecting the actinic rays transmitted through the colored photosensitive layer (actinic rays not used in the reaction) by the release layer and changing the reflection characteristics.
【００１１】つまり、透明支持体の一面に活性光線吸収
剤、帯電防止剤、塗膜形成性高分子樹脂からなる透明性
の活性光線吸収層が、および異なった一面に透明支持体
と強く接着している透明性の剥離層、剥離層から剥離可
能である熱融着性の透明な中間層、着色感光層が積層さ
れた本発明の感光性転写シートを、 （１） 陰画原稿を通して該感光材料を活性光線により
密着露光させた後、非露光部を現像処理し、画像を形成
する段階、 （２）該形成画像面を更に熱融着層を有する被転写材料
の熱融着面と密着させ、加熱加圧させた後、透明支持体
を中間層から剥ぎとり、着色画像を中間層と共に被転写
材料に転写させる段階、で処理することからなり、段階
（１）で着色感光層の色調の異なるものを用意して、そ
れぞれの色調に応じて、陰画原稿を選択し、密着露光、
現像処理し、画像を形成し、段階（２）でそれらのうち
の特定の色調の着色画像を被転写材料に転写した後、 （３） 更に上記とは異なる色調の着色画像の形成され
た感光材料の両像面を、段階（２）で得た被転写材料の
既転写面と密着させ、加熱加圧させた後、透明支持体を
中間層から剥ぎとり、着色画像を中間層と共に被転写材
料の既転写面上に転写させる段階、で処理することから
なり、３色目以降は、段階（３）を繰り返すことを特徴
とする多色画像の形成に際し、感光性転写シートの剥離
層が、活性光線反射性物質を含有するものである。本発
明の要旨とする所は、 （１） 透明支持体の一面に活性光線吸収剤、帯電防止
剤、塗膜形成性高分子樹脂からなる透明性の活性光線吸
収層が、および異なった一面に透明支持体と強く接着し
ている透明性の剥離層、剥離層から剥離可能である熱融
着性の透明な中間層、着色感光層が積層された感光性転
写シートにおいて、剥離層を形成する塗膜形成性高分子
樹脂中に活性光線反射性物質が含まれることを特徴とす
る感光性転写シート、 （２） 剥離層中の活性光線反射性物質が、種々の表面
処理が施された雲母系顔料、粉末アルミニューム、酸化
チタン、酸化亜鉛、硫酸バリウムのいずれか、あるいは
これらの混合物であることを特徴とする感光性転写シー
ト、 （３） 剥離層の活性光線（３６０ｎｍ）全反射率が１
５％以上であることを特徴とする感光性転写シート、 （４） 剥離層の塗膜形成性高分子樹脂がウレタン樹
脂、メラミン樹脂、フッ素樹脂、シリコン樹脂、ポリエ
ステル、ポリオレフィンのいずれかあるいはこれらの混
合物であることを特徴とする感光性転写シート、 （５） 中間層がポリエステル、エチレン−酢酸ビニル
共重合体、アクリル化合物のいずれかあるいはこれらの
混合物であることを特徴とする感光性転写シート、 （６） 着色感光層が下記一般式（Ｉ）または（ＩＩ） （但し上式中Ｒ１およびＲ２はそれぞれ互いに独立に、
水素原子またはアルキル基を表し、Ｙ−は酸の共役塩基
性イオン具体的にはＣｌ−，Ｂｒ−等のハロゲンのイオ
ンを示し、ｍは１〜６の整数を表し、ｎは０または１を
表す）で表される感光性樹脂と着色剤とからなることを
特徴とずる感光性転写シート、に存する。That is, a transparent active light-absorbing layer comprising an active light-absorbing agent, an antistatic agent and a film-forming polymer resin is adhered to one surface of the transparent support, and the transparent support is strongly adhered to a different surface. The photosensitive transfer sheet of the present invention, on which a transparent release layer, a heat-fusible transparent intermediate layer releasable from the release layer, and a colored photosensitive layer are laminated, (1) the photosensitive material is passed through a negative document Is exposed to actinic light, and then the unexposed area is developed to form an image. (2) The formed image surface is further brought into close contact with the heat-sealed surface of the transfer-receiving material having a heat-sealed layer. After the heating and pressurizing, the transparent support is peeled off from the intermediate layer, and the color image is transferred to the material to be transferred together with the intermediate layer. In the step (1), the color tone of the colored photosensitive layer is adjusted. Prepare different ones, according to each color tone, shade Select the document, contact exposure,
After developing, forming an image and transferring the colored image of a specific tone among them to the material to be transferred in step (2), (3) further forming a photosensitive image having a colored image of a different color from the above. After bringing both image surfaces of the material into close contact with the already-transferred surface of the material to be transferred obtained in step (2), applying heat and pressure, the transparent support is peeled off from the intermediate layer, and the colored image is transferred with the intermediate layer. In the step of transferring the material onto the already-transferred surface, the step (3) is repeated for the third and subsequent colors. In forming a multicolor image, the release layer of the photosensitive transfer sheet is It contains an actinic ray reflective substance. The gist of the present invention is as follows: (1) On one surface of a transparent support, there is provided a transparent active light-absorbing layer comprising an active light-absorbing agent, an antistatic agent and a film-forming polymer resin; A release layer is formed on a photosensitive transfer sheet in which a transparent release layer strongly adhered to a transparent support, a heat-fusible transparent intermediate layer that can be released from the release layer, and a colored photosensitive layer are laminated. A photosensitive transfer sheet characterized in that an actinic ray-reflective substance is contained in the film-forming polymer resin; A photosensitive transfer sheet characterized by being any one of a pigment, powdered aluminum, titanium oxide, zinc oxide, and barium sulfate, or a mixture thereof; (3) the active layer (360 nm) total reflectance of the release layer is 1
A photosensitive transfer sheet characterized by being at least 5%; (5) a photosensitive transfer sheet, wherein the intermediate layer is any one of polyester, ethylene-vinyl acetate copolymer, and an acrylic compound, or a mixture thereof; (6) The colored photosensitive layer has the following general formula (I) or (II) (Wherein R 1 and R 2 are each independently of the other
Represents a hydrogen atom or an alkyl group, Y − represents a conjugate basic ion of an acid, specifically a halogen ion such as Cl − or Br − , m represents an integer of 1 to 6, and n represents 0 or 1. Represented by a photosensitive resin and a colorant.
【００１２】以下本発明を更に詳しく説明する。本発明
の感光性転写シートに用いられる透明支持体としては、
ポリエチレンテレフタレート、ポリプロピレン、ポリエ
チレン、ポリ塩化ビニル、ポリスチレン、ポリカーボネ
ート、トリアセテートなどのプラスチックフィルムが適
しており、その中でも２軸延伸されたポリエチレンテレ
フタレートフィルムが強度、耐熱性、寸法安定性等にお
いて優れており好ましい。支持体の厚さは特に制限はな
いが50〜 150μｍ程度が適当である。Hereinafter, the present invention will be described in more detail. As the transparent support used in the photosensitive transfer sheet of the present invention,
Plastic films such as polyethylene terephthalate, polypropylene, polyethylene, polyvinyl chloride, polystyrene, polycarbonate, and triacetate are suitable, and among them, a biaxially stretched polyethylene terephthalate film is preferable because of its excellent strength, heat resistance, dimensional stability, and the like. . The thickness of the support is not particularly limited, but is suitably about 50 to 150 μm.
【００１３】本発明の感光性転写シートに用いられる活
性光線吸収層は、塗膜形成性高分子からなり、更にハレ
ーションを防止するためにサリシレート系、ベンゾフェ
ノン系、ベンゾトリアゾール系等の紫外線吸収剤が添加
されている。そして、取り扱いの点から、導電性樹脂、
導電性粉末等の帯電防止剤も添加される。また、ブロッ
キング防止の為に、顔料を添加し表面をマット化しても
よい。これにより剥離層を通過した光がハレーションを
起して着色感光層に影響を与えドットゲインを太らせる
のを防止する。The actinic ray-absorbing layer used in the photosensitive transfer sheet of the present invention comprises a film-forming polymer, and further contains a salicylate-based, benzophenone-based, benzotriazole-based ultraviolet absorber to prevent halation. Has been added. And from the point of handling, conductive resin,
An antistatic agent such as a conductive powder is also added. In order to prevent blocking, a pigment may be added to make the surface matte. This prevents the light passing through the peeling layer from causing halation, affecting the colored photosensitive layer and increasing the dot gain.
【００１４】本発明の感光性転写シートに用いられる剥
離層は、ウレタン樹脂、メラミン樹脂、フッ素樹脂、シ
リコン樹脂、ポリエステル、ポリオレフィンのいずれか
あるいはこれらの混合系からなり、塗工厚は１〜10μ
ｍ、より好ましくは１〜５μｍが適している。また、剥
離層に顔料を添加してマット化することにより、その上
に塗設される中間層との間の剥離強度を安定化させるこ
とができる。更に、中間層と更にその上に塗設される着
色感光層にもマット化パターンが形成され、露光減圧時
に原稿と着色感光層との間の空気の抜けをスムーズにし
両者の密着性を良くすることも可能である。The release layer used in the photosensitive transfer sheet of the present invention is made of any one of urethane resin, melamine resin, fluororesin, silicone resin, polyester, polyolefin or a mixture thereof, and has a coating thickness of 1 to 10 μm.
m, more preferably 1 to 5 μm. Further, by adding a pigment to the release layer to form a mat, the peel strength between the release layer and the intermediate layer provided thereon can be stabilized. Further, a matted pattern is also formed on the intermediate layer and on the colored photosensitive layer further coated thereon, so that air can be smoothly evacuated between the original and the colored photosensitive layer when the exposure is decompressed, thereby improving the adhesion between the two. It is also possible.
【００１５】また、耐ブロッキング性能や中間受像シー
ト上で滑り性を向上させ、および中間受像シートに加熱
加圧により転写する際に受像シートと中間層の間の空気
が抜け易くなるよう両者間の密着性を向上させることが
できる。そして、添加顔料の種類、粒子サイズ、添加量
の選択によって、活性光線の反射特性を調整し、着色感
光層の感度をコントロールすることが可能である。Further, the anti-blocking performance and the slipperiness on the intermediate image-receiving sheet are improved, and the air between the image-receiving sheet and the intermediate layer is easily released when the image is transferred to the intermediate image-receiving sheet by heating and pressing. Adhesion can be improved. By selecting the type, the particle size, and the amount of the added pigment, it is possible to adjust the reflection characteristic of the actinic ray and control the sensitivity of the colored photosensitive layer.
【００１６】このような目的で使用される顔料として
は、表面処理が施された雲母系顔料、粉末アルミニュー
ム、酸化チタン、酸化亜鉛、硫酸バリウム、二酸化硅
素、炭酸カルシウム、アルミナ等の無機微粒子やポリエ
チレン、ポリプロピレン、ポリエチレンテレフタレー
ト、ポリスチロール、ポリカーボネート、アクリル酸エ
ステル樹脂、メタクリル酸樹脂、ポリアクリロニトリル
およびアクリロニトリルの共重合体等のプラスチックパ
ウダー、更に澱粉、セルロース等の微粉末がある。特に
着色感光層の高感度化には、表面処理が施された雲母系
顔料、粉末アルミニューム、酸化チタン、酸化亜鉛、硫
酸バリウムが適しており、剥離層の活性光線（360nm)全
反射率が15％以上、より好ましくは20％以上が望まし
い。顔料のサイズは0.01〜20μｍ、より好ましくは１〜
10μｍが適しており、それぞれの色調の着色感光層に応
じた剥離層を調製することにより各色調の感光性転写シ
ートの感度を同一化することができる。Examples of the pigment used for this purpose include surface-treated mica pigments, powdered aluminum, inorganic fine particles such as titanium oxide, zinc oxide, barium sulfate, silicon dioxide, calcium carbonate, and alumina. Plastic powders such as polyethylene, polypropylene, polyethylene terephthalate, polystyrene, polycarbonate, acrylate resin, methacrylic acid resin, polyacrylonitrile and copolymers of acrylonitrile, and fine powders such as starch and cellulose. In particular, surface-treated mica-based pigments, powdered aluminum, titanium oxide, zinc oxide, and barium sulfate are suitable for increasing the sensitivity of the colored photosensitive layer, and the active layer (360 nm) total reflectance of the release layer is suitable. 15% or more, more preferably 20% or more is desirable. The size of the pigment is 0.01 to 20 μm, more preferably 1 to 20 μm.
10 μm is suitable, and the sensitivity of the photosensitive transfer sheet of each color can be equalized by preparing a release layer corresponding to the colored photosensitive layer of each color.
【００１７】本発明の感光性転写シートに用いられる中
間層としては、水に不溶で色相および透明性を阻害する
ことなく、室温では非粘着性で熱により粘着性、融着性
となり、しかも室温では剥離層と容易に剥離可能で、か
つこの上に塗設される光により不溶化する着色感光層と
は、特に光不溶化後において十分なる密着性を有し、且
つ被転写シートとも十分な密着性を有する物質から選ば
れる。The intermediate layer used in the photosensitive transfer sheet of the present invention is non-adhesive at room temperature and becomes tacky and fusible by heat without being insoluble in water and hindering hue and transparency. And the colored photosensitive layer, which can be easily peeled off from the release layer and is insolubilized by light applied thereon, has sufficient adhesiveness especially after photoinsolubilization, and also has sufficient adhesiveness with the sheet to be transferred. Is selected from substances having
【００１８】例えば以下のような被膜形成性の高分子物
質が挙げられる。ポリアクリル酸エステルおよびアクリ
ル酸エステル共重合体、ポリメタアクリル酸エステルお
よびメタアクリル酸エステル共重合体、ポリアクリルア
マイドおよびアクリルアマイド共重合体、ポリ酢酸ビニ
ルおよび酢酸ビニル共重合体、ポリ塩化ビニルおよび塩
化ビニル共重合体、ポリ塩化ビニリデンおよび塩化ビニ
リデン共重合体、ポリスチレンおよびスチレン共重合
体、エチレンと酢酸ビニル、エチレンとアクリル酸エス
テル、エチレンと塩化ビニルエチレンとアクリル酸の如
き、エチレン共重合体、ポリビニルブチラール、ポリビ
ニルホルマールの如きポリビニルアセタール樹脂、ポリ
エステル樹脂、ナイロン、共重合ナイロンの如きポリア
ミド樹脂、合成ゴム、塩化ゴムの如き各種ゴム類、ポリ
エチレン、ポリプロピレンの如きポリオレフィン、セル
ロース誘導体、シェラック、各種ワックス類。For example, the following film-forming polymer substances can be mentioned. Polyacrylate and acrylate copolymer, polymethacrylate and methacrylate copolymer, polyacrylamide and acrylamide copolymer, polyvinyl acetate and vinyl acetate copolymer, polyvinyl chloride and Ethylene copolymers such as vinyl chloride copolymer, polyvinylidene chloride and vinylidene chloride copolymer, polystyrene and styrene copolymer, ethylene and vinyl acetate, ethylene and acrylate, ethylene and vinyl chloride ethylene and acrylic acid, Polyvinyl acetal resin such as polyvinyl butyral and polyvinyl formal, polyamide resin such as polyester resin, nylon and copolymerized nylon, various rubbers such as synthetic rubber and chlorinated rubber, and polyethylene such as polyethylene and polypropylene Olefins, cellulose derivatives, shellac, various waxes.
【００１９】このほかこれらの高分子物質相互の混合
物、または他の高分子物質、可塑剤など他の物質との混
合系も使用できる。例えば室温で粘着性を示すものでも
該粘着性を防止することができる他物質との組合わせ
や、逆に加熱しても粘着性を示さないものでも、粘着性
付与物、可塑剤等との組合わせも考えられ、単一物質の
みならず、また支持体の種類等にもより必要に応じて種
々の組合わせが考えられ、またそれゆえ必ずしも上記物
質に限定されるものではない。In addition, a mixture of these high-molecular substances or a mixed system with another substance such as another high-molecular substance or a plasticizer can also be used. For example, a combination with another substance that can prevent the tackiness even if it shows tackiness at room temperature, or even a substance that does not show tackiness even when heated, a tackifier, a plasticizer and the like Combinations are also conceivable, and not only a single substance, but also various combinations depending on the type of the support, etc., as necessary, and therefore, are not necessarily limited to the above substances.
【００２０】支持体に塗設した剥離層上に中間層を積層
するには上記した高分子物質の溶液を通常の方法で剥離
層上に塗布し乾燥させるか、または、固体状の上記高分
子物質を熱溶融して塗布するか（ホットメルトコーティ
ング）更には上記高分子物質よりなるフィルムをラミネ
ートさせてもよい。中間層の厚さは 0.5〜10μｍ、より
望ましくは 0.5〜３μｍが好ましい。For laminating the intermediate layer on the release layer provided on the support, a solution of the above-mentioned polymer substance is applied on the release layer by a usual method and dried, or the solid polymer is used as the above-mentioned polymer. The material may be melted and applied (hot melt coating), or a film made of the above polymer material may be laminated. The thickness of the intermediate layer is preferably 0.5 to 10 μm, more preferably 0.5 to 3 μm.
【００２１】本発明の感光性転写シートに用いられる、
水に可溶で光により不溶化する着色感光層としては、従
来公知の感光性樹脂が利用でき、ネガ型の例としては下
記のものがある。 (1) クエン第二鉄アンモン、シュウ酸第二鉄アンモン
のような光により第一鉄イオンを与える感光性第二鉄塩
とゼラチン、ポリビニルアルコールの如き親水性樹脂か
ら成る組成物。 (2) ゼラチン、フィッシュグルー、アラビアゴム、ポ
リビニルアルコール、ポリアクリルアミド、カルボキシ
メチルセルロース、ヒドロキシメチルセルロース等の水
溶性樹脂と、ｐ−アミノジフェニルアミン、ベンジジ
ン、ジアニシジン、トルイソジンなどのジアミノ化合物
のテトラゾニウム塩、またはｐ−ジアゾフェニルアミン
とパラフォルムアルデヒドを縮合したジアゾ化合物とパ
ラフォルムアルデヒドを縮合したジアゾ樹脂からなる組
成物。 (3) ｐ−ジアゾジフェニルアミンの如きジアゾ化合物
とパラフォルムアルデヒドを縮合したジアゾ樹脂とから
なる組成物。 (4) ４，４′−ジアジドスチルベンゼン、２，２′−
ジスルホン酸ソーダの如きアジド化合物とポリアクリル
アミド、ポリビニルアルコール、ポリビニルピロリド
ン、ゼラチン等の水溶性樹脂からなる組成物。 (5) ４，４′−ジアジドスチルベンゼン、４，４′−
ジアジドカルコンなどのアジド化合物と環化ゴムからな
る組成物。 (6) ポリビニルアルコールの桂皮エステル酸エステ
ル、アリルアクリル酸エステルと５−ニトロアセナフテ
ン、１，２−ベンズアンスラキノンの如き増感剤とから
なる組成物。 (7) アクリルアミド、アクリル酸の如きビニルモノマ
ーと、セルロース誘導体およびポリビニルアルコール誘
導体と光重合開始剤からなる組成物。 (8) メチレンビスアクリルアミド、Ｎ，Ｎ′−ヘキサ
メチレンビスメタクリアミドの如きアクリルアミド類と
アルコール可溶性ナイロンおよび光重合開始剤からなる
組成物。 (9) アクリルアミド、アクリル酸の如きエチレン系不
飽和単量体とクエン第二鉄アンモンの如き感光性第二鉄
塩と親水性樹脂からなる組成物。 (10) ポリビニルアルコールにスチルビニリウム基、ス
チルバゾリウム基、スチルキノリウム基等の感光性基を
付加した変成ポリビニルアルコール組成物。Used in the photosensitive transfer sheet of the present invention,
As the colored photosensitive layer which is soluble in water and insolubilized by light, a conventionally known photosensitive resin can be used, and examples of the negative type are as follows. (1) A composition comprising a photosensitive ferric salt that gives ferrous ions by light such as ferric citrate ammonium and ferric oxalate, and a hydrophilic resin such as gelatin and polyvinyl alcohol. (2) Gelatin, fish glue, gum arabic, polyvinyl alcohol, polyacrylamide, carboxymethylcellulose, hydroxymethylcellulose, and other water-soluble resins, and p-aminodiphenylamine, benzidine, dianisidine, tetrazonium salts of diamino compounds such as tolisodin, or p- A composition comprising a diazo compound obtained by condensing diazophenylamine and paraformaldehyde and a diazo resin obtained by condensing paraformaldehyde. (3) A composition comprising a diazo compound such as p-diazodiphenylamine and a diazo resin obtained by condensing paraformaldehyde. (4) 4,4'-diazidostilbenzene, 2,2'-
A composition comprising an azide compound such as sodium disulfonate and a water-soluble resin such as polyacrylamide, polyvinyl alcohol, polyvinylpyrrolidone, and gelatin. (5) 4,4'-diazidostilbenzene, 4,4'-
A composition comprising an azide compound such as diazide chalcone and a cyclized rubber. (6) A composition comprising a cinnamate ester of polyvinyl alcohol, an allyl acrylate and a sensitizer such as 5-nitroacenaphthene and 1,2-benzanthraquinone. (7) A composition comprising a vinyl monomer such as acrylamide and acrylic acid, a cellulose derivative and a polyvinyl alcohol derivative, and a photopolymerization initiator. (8) A composition comprising acrylamides such as methylenebisacrylamide and N, N'-hexamethylenebismethacrylamide, an alcohol-soluble nylon, and a photopolymerization initiator. (9) A composition comprising an ethylenically unsaturated monomer such as acrylamide and acrylic acid, a photosensitive ferric salt such as ferric citrate ammonium, and a hydrophilic resin. (10) A modified polyvinyl alcohol composition obtained by adding a photosensitive group such as a stilvinylilium group, a stilbazolium group, and a stilquinolium group to polyvinyl alcohol.
【００２２】またポジ型の例としては、ナフトキノン−
（1.2)−ジアジドスルホン酸エステル等のキノンジアジ
ド化合物とアルカリ可溶性フェノールホルムアルデヒド
樹脂との組成物がある。上記感光樹脂は代表的な例であ
って、本発明は、これらに限定されるものではない。Examples of the positive type include naphthoquinone-
There is a composition of a quinonediazide compound such as (1.2) -diazidesulfonic acid ester and an alkali-soluble phenol formaldehyde resin. The above photosensitive resin is a typical example, and the present invention is not limited to these.
【００２３】着色剤については、水に分散可能な顔料、
水あるいはアルコール可溶性の染料など広範囲に選択で
きるが上記水溶性高分子物質や光不溶化剤、変性ポリビ
ニルアルコールとの混和性が良く、感光性、現像性等に
悪影響を及ぼさない物であることが必要であり、またそ
の色調については、写真製版における色校正の場合に
は、基本的にはシアン、マゼンタ、イエロー、ブラック
の４色であり、おのずと各々印刷インクのそれに近い色
のものが望まれる。着色剤の添加量は、その種類や着色
感光層の塗布量にもよるが、形成画像が被転写材料に転
写された後の該着色画像の所望の光学反射濃度により決
定されるべきである。As the colorant, pigments dispersible in water,
It can be selected from a wide range such as water or alcohol-soluble dyes, but it must have good miscibility with the above water-soluble polymer substance, photoinsolubilizer, and modified polyvinyl alcohol, and do not adversely affect photosensitivity and developability. The color tone is basically four colors of cyan, magenta, yellow, and black in the case of color proofing in photoengraving, and it is naturally desired that each color is close to that of the printing ink. The amount of the colorant to be added depends on the type and the amount of the colored photosensitive layer to be applied, but should be determined by the desired optical reflection density of the colored image after the formed image is transferred to the material to be transferred.
【００２４】光により不溶化する着色感光層には上記以
外にも暗反応を防止する為の安定化剤や該着色感光層を
剥離層面上に設けるに当たり、その塗工性改良の為のレ
ベリング剤や消泡剤、界面活性剤等を必要に応じて添加
することができる。また、該着色感光層を設けるに当た
り上記成分は主として水に溶解または分解して混合され
るが脱泡や塗工性改良を目的として、必要に応じてアル
コール類等の水に可溶性の有機溶剤を希釈剤として一部
使用することもできる。In the colored photosensitive layer which is insolubilized by light, in addition to the above, a stabilizer for preventing a dark reaction and a leveling agent for improving the coating property when the colored photosensitive layer is provided on the surface of the release layer. An antifoaming agent, a surfactant and the like can be added as needed. In providing the colored photosensitive layer, the above components are mainly dissolved or decomposed in water and mixed, but for the purpose of defoaming and improving coatability, a water-soluble organic solvent such as an alcohol is used as necessary. It can also be used partially as a diluent.
【００２５】該着色感光層の厚さは網諧調再現性など解
像度の点からできうる限り薄い方がよいが着色剤による
画像濃度との兼ね合いから 0.5〜５μｍ、より好ましく
は１〜３μｍが適している。上記着色感光層を離型面上
に塗設するに当たっては、従来公知のいかなる方法によ
ってもピンホール等が無く、均一な塗膜さえ得られれば
特に限定されるものではない。The thickness of the colored photosensitive layer is preferably as thin as possible from the viewpoint of resolution such as halftone reproducibility, but is preferably 0.5 to 5 μm, more preferably 1 to 3 μm in consideration of the image density by the colorant. I have. In applying the colored photosensitive layer on the release surface, there is no particular limitation as long as there is no pinhole or the like and a uniform coating film can be obtained by any conventionally known method.
【００２６】次に本発明に用いられる被転写材料につい
て説明する。支持体としては、紙、プラスチックフィル
ム、紙／プラスチック複合材料、ガラス板、金属板等を
挙げることができる。支持体上に密着して積層される熱
融着層に用いられる物質としては、室温では被粘着性で
熱により粘着性、融着性を示す物質、更に詳しくは、感
光性転写シートの中間層と露光現像後の着色感光層と熱
時相互融着しうる物質が選ばれるべきである。それらの
物質の例としては、感光性転写シートの中間層に用いら
れる物質と同様なものから選択されるが、この場合に
は、主として中間層と着色感光層との相互融着性を考慮
したうえで、単一物質に限らず混合系等から幅広く選択
する。受像シートの支持体に熱融着層を塗設するに当っ
ては、前記した高分子物質の溶液を通常の方法で支持体
上に塗布し乾燥させるか、または固状の前記高分子物質
を熱溶融して塗布するか（ホットメルトコーティング）
更には前記高分子物質からなるフィルムをラミネートさ
せてもよい。熱融着層の厚さは使用する樹脂にもよるが
３〜15μｍのものが好ましい。Next, the transfer material used in the present invention will be described. Examples of the support include paper, plastic films, paper / plastic composite materials, glass plates, metal plates, and the like. As the substance used for the heat-sealing layer that is closely adhered and laminated on the support, a substance which is tacky at room temperature and exhibits tackiness and fusing property by heat, more specifically, an intermediate layer of a photosensitive transfer sheet And a material which can mutually fuse with the colored photosensitive layer after exposure and development when heated. Examples of those substances are selected from the same substances as those used for the intermediate layer of the photosensitive transfer sheet. In this case, the mutual adhesion between the intermediate layer and the colored photosensitive layer is mainly considered. In addition, not only a single substance but also a wide selection from a mixed system or the like is available. In applying the heat-sealing layer to the support of the image receiving sheet, a solution of the above-described polymer substance is applied to the support by a usual method and dried, or the solid polymer substance is coated. Hot melt coating (hot melt coating)
Further, a film made of the above-mentioned polymer substance may be laminated. The thickness of the heat sealing layer depends on the resin used, but is preferably 3 to 15 μm.
【００２７】本発明の転写シートは、図１のようにまず
写真製版工程において得られる各分解色毎に網分解され
たフィルムを通して活性光線により密着露光させた後、
現像処理により画像を形成させる（段階１）。各分解色
に対応して、本発明の感光性転写シートを選ぶことによ
って（シアン版に対応したフィルムからはシアンに着色
した本発明感光性転写シートへ密着反転する）各々の着
色画像を有した感光性転写シートが得られる。ここで該
感光性転写シートの非画像部は中間層Ｂ−２が露出す
る。（受像シートの被転写材料の熱融着層Ｅは画像形成
後の着色感光層（画像部）Ｃ−１とも熱融着するも、こ
れのみでは完全ではなく、非画像部に露出された熱融着
性の中間層Ｂ−２との相互融着により、より完全に熱転
写される。）The transfer sheet of the present invention is first subjected to contact exposure with actinic rays through a net-decomposed film for each color obtained in the photomechanical process, as shown in FIG.
An image is formed by a development process (Step 1). By selecting the photosensitive transfer sheet of the present invention corresponding to each separation color (the film corresponding to the cyan printing plate was inverted to the photosensitive transfer sheet of the present invention colored in cyan) to have each colored image. A photosensitive transfer sheet is obtained. Here, the non-image portion of the photosensitive transfer sheet exposes the intermediate layer B-2. (The heat-fused layer E of the transfer material of the image-receiving sheet is also heat-sealed with the colored photosensitive layer (image portion) C-1 after image formation, but is not complete by itself, and the heat exposed to the non-image portion is not sufficient. Due to the mutual fusion with the fusible intermediate layer B-2, thermal transfer is more complete.)
【００２８】次に該感光性転写シートの画像面を被転写
材料の被転写面（熱融着層を有する面）と密着させ、加
熱加圧することにより感光性転写シートの中間層（未露
光部、非画像部）Ｂ−２と被転写材料の熱融着層Ｅが相
互融着を起こし（着色層の光不溶化部つまり画像部も被
転写材料の熱融着層と融着するがこの場合には一方が熱
融着性でないため、非画像部ほど強固な接着はできな
い）、しかる後に、該感光性転写シートの支持体Ａを剥
離層Ｂ−１と共に剥がすと分色画像は中間層Ｂ−２と共
に、被転写材料上に容易に強固に転写される（段階
２）。Next, the image surface of the photosensitive transfer sheet is brought into close contact with the transfer surface (the surface having a heat-sealing layer) of the material to be transferred, and heated and pressed to form an intermediate layer (unexposed portion) of the photosensitive transfer sheet. , Non-image portion) B-2 and the heat-fused layer E of the material to be transferred mutually fuse (the photo-insolubilized portion of the colored layer, ie, the image portion also fuses with the heat-fused layer of the material to be transferred). Cannot adhere as strongly as the non-image area because one of them is not heat-fusible). Thereafter, when the support A of the photosensitive transfer sheet is peeled off together with the release layer B-1, the color separation image becomes the intermediate layer B -2 is easily and firmly transferred onto the material to be transferred (Step 2).
【００２９】更に、上記転写画像の上に第２色目の着色
画像を熱転写するわけであるが、こ場合には１色目の転
写後の表面には熱融着性の中間層（第１色目の中間層Ｂ
−２）があるわけで１色目同様に容易にかつ強固に転写
しうる（段階３）。３色目以降も２色目と同様の結果で
順次異なった着色画像を中間層Ｂ−２と共に容易に転写
でき、最終的には被転写材料上に多色画像を形成するこ
とができる（段階４）。ここで本発明によって得られる
着色画像のそれぞれの色調（基本的にはシアン、マゼン
タ、イエロー、ブラック）、濃度を印刷インキのそれに
近いものを選ぶことによって最終印刷物に酷似した多色
画像が得られ、校正刷りに類似した色校正用として利用
されうる。Further, the colored image of the second color is thermally transferred on the above-mentioned transferred image. In this case, the surface after the transfer of the first color is provided on the heat-fusible intermediate layer (the first color). Middle layer B
-2), the image can be easily and firmly transferred as in the case of the first color (step 3). From the third color onward, sequentially different colored images can be easily transferred together with the intermediate layer B-2 with the same result as the second color, and finally a multicolor image can be formed on the material to be transferred (step 4). . Here, a multicolor image very similar to the final printed matter can be obtained by selecting a color tone (basically cyan, magenta, yellow, and black) and a density close to those of the printing ink of the colored image obtained by the present invention. Can be used for color proofing similar to proofing.
【００３０】以上の説明から明らかなように、この方法
では、形成された画像を１色ずつ被転写材料上に順次転
写するので、シアン、マゼンタ、イエロー、ブラックな
どの各色の感光性転写シートの露光作業が同時に行なえ
る為、作業性に優れる。しかし、各色の感度差により最
適露光量が異なると、この利点を十分に活かすことがで
きない。本発明は、剥離層の反射特性により着色感光層
の感度のコントロールを可能にし、各色の露光作業が各
色の最適露光量で同時に行なえるようになった点は印刷
製版工程の作業性改善に寄与するところは極めて大きい
ものがある。As is apparent from the above description, in this method, the formed images are sequentially transferred one by one onto the material to be transferred, so that the photosensitive transfer sheet of each color such as cyan, magenta, yellow, and black is transferred. Excellent workability because exposure work can be performed at the same time. However, if the optimum exposure amount differs depending on the sensitivity difference of each color, this advantage cannot be fully utilized. The present invention makes it possible to control the sensitivity of the colored photosensitive layer by the reflection characteristics of the release layer, and the exposure work of each color can be performed simultaneously with the optimum exposure amount of each color, which contributes to the improvement in workability of the printing plate making process. There is something very big to do.
【００３１】[0031]
【実施例】本発明を更に明確にするため、以下実施例を
示すが本発明はこれに限定されるものではない。なお実
施例中の「部」は全て重量部を示す。The following examples are provided to further clarify the present invention, but the present invention is not limited thereto. Note that all “parts” in Examples are parts by weight.
【００３２】（実施例１） ＜活性光線吸収量形成液＞ サフトマーＳＴＨ−８７ 65部 （アクリル系導電性ポリマー：三菱油化（株）） テスファン３２２ 31部 （アクリルアミド共重合物：日立化成ポリマー（株）） サーモラックＦ１ 19部 （ポリエステル：綜研化学（株）） ドライヤー９００ 1.9部 （パラトルエンスルホン酸：日立化成ポリマー） チヌビン−１０９ ３部 （ベンゾトリアゾール系紫外線吸収剤：チバガイギー（株）） サイロイド３０８ 1.9部 （シリカ：水沢化学（株）） トルエン 100部 メチルエチルケトン 100部 エチルセルソロブ 48部(Example 1) <Active ray absorption amount forming liquid> 65 parts of Saftomer STH-87 (acrylic conductive polymer: Mitsubishi Yuka Co., Ltd.) 31 parts of tesfan 322 (acrylamide copolymer: Hitachi Chemical Polymer ( Co., Ltd.) Thermolac F1 19 parts (Polyester: Soken Chemical Co., Ltd.) Dryer 900 1.9 parts (Paratoluenesulfonic acid: Hitachi Chemical Co., Ltd.) Tinuvin-109 3 parts (Benzotriazole-based UV absorber: Ciba-Geigy Co., Ltd.) SILOID 308 1.9 parts (Silica: Mizusawa Chemical Co., Ltd.) Toluene 100 parts Methyl ethyl ketone 100 parts Ethyl cellolob 48 parts
【００３３】 ＜剥離層形成液−１＞ テスファイン３２２ 5部 （アクリルアミド共重合物：日立化成ポリマー（株）） ドライヤー９００ 0.6部 （パラトルエンスルホン酸：日立化成ポリマー（株）） リューロンＱｕ−６２８ 100部 （塩化ビニル−プロピオン酸ビニル共重合体：東ソー（株）） ミズカシールＳＫ−７ 0.8部 （シリカ：水沢化学（株）） トルエン 67部 メチルエチルケトン 67部 シクロヘキサノン 33部<Release Layer Forming Solution-1> 5 parts of Tesfine 322 (acrylamide copolymer: Hitachi Chemical Co., Ltd.) Dryer 900 0.6 parts (p-toluenesulfonic acid: Hitachi Chemical Co., Ltd.) Ryuron Qu-628 100 parts (vinyl chloride-vinyl propionate copolymer: Tosoh Corporation) Mizuka Seal SK-7 0.8 parts (silica: Mizusawa Chemical Co., Ltd.) Toluene 67 parts Methyl ethyl ketone 67 parts Cyclohexanone 33 parts
【００３４】 ＜剥離層形成液−２＞ テスファイン３２２ 5部 （アクリルアミド共重合物：日立化成ポリマー（株）） ドライヤー９００ 0.6部 （パラトルエンスルホン酸：日立化成ポリマー（株）） リューロンＱｕ−６２８ 100部 （塩化ビニル−プロピオン酸ビニル共重合体：東ソー（株）） ＩＲＩＯＤＩＮ−１１１ 17部 （雲母系顔料：メルクジャパン（株）） トルエン 36部 メチルエチルケトン 36部 シクロヘキサノン 18部<Release Layer Forming Solution-2> 5 parts of Tesfine 322 (acrylamide copolymer: Hitachi Chemical Co., Ltd.) Dryer 900 0.6 parts (paratoluenesulfonic acid: Hitachi Chemical Co., Ltd.) Ryuron Qu-628 100 parts (vinyl chloride-vinyl propionate copolymer: Tosoh Corporation) IRIODIN-111 17 parts (Mica pigment: Merck Japan KK) Toluene 36 parts Methyl ethyl ketone 36 parts Cyclohexanone 18 parts
【００３５】 ＜中間層形成液＞ バイロナールＭＤ−１１００ 91部 （ポリエステル：東洋紡（株）） バイロナールＭＤ−１４００ 78部 （ポリエステル：東洋紡（株）） 水 100部 イソプロピルアルコール 67部 ブチルセロソルブ 33部 ジメチルフォルムアミド 22部<Intermediate layer forming liquid> 91 parts of Vironal MD-1100 (polyester: Toyobo Co., Ltd.) 78 parts of Vironal MD-1400 (polyester: Toyobo Co., Ltd.) water 100 parts isopropyl alcohol 67 parts butyl cellosolve 33 parts dimethylformamide 22 parts
【００３６】 ＜着色感光層形成液＞ ブラック液 ＳＢＱ変性ＰＶＡ 10％水溶液 100部 （Ｎメチルスチルバゾリウム基1.25モル％導入、 平均重合度1700、ケン化度88％） 顔料分散液 4部 （カーボンブラック20％水分散） 水 100部 イソプロピルアルコール 10部<Coloring photosensitive layer forming solution> Black solution SBQ-modified PVA 10% aqueous solution 100 parts (N-methylstilbazolium group 1.25 mol% introduced, average polymerization degree 1700, saponification degree 88%) Pigment dispersion liquid 4 parts ( Carbon black 20% water dispersion) Water 100 parts Isopropyl alcohol 10 parts
【００３７】上記カーボンブラックの代わりにフタロシ
アニンブルー、パーマネントカーミンＦＢおよびパーマ
ネントイエローＨＲを用いてシアン、マゼンタ、イエロ
ー用の着色感光層液を同様に調整した。但し、イエロ
ー、シアン、マゼンタ、ブラックの顔料分散液は、以下
の配合でインキ練り機で３時間分散することにより得
た。 顔 料 20部 非イオン活性剤 1部 （ポリエチレングリコールアルキルフェニルエーテル主体） 水 80部Using phthalocyanine blue, permanent carmine FB and permanent yellow HR instead of the above carbon black, a colored photosensitive layer solution for cyan, magenta and yellow was similarly prepared. However, pigment dispersions of yellow, cyan, magenta, and black were obtained by dispersing with the following composition using an ink mill for 3 hours. Coatings 20 parts Nonionic surfactant 1 part (mainly polyethylene glycol alkyl phenyl ether) Water 80 parts
【００３８】活性光線吸収層形成液を２軸延伸した厚さ
100μｍのポリエチレンテレフタレートフィルムの片面
に、ロールコーターで塗布し 140℃１分間乾燥して、約
３μｍの活性光線吸収層を形成した。Thickness of biaxially stretched liquid for forming active light absorbing layer
One side of a 100 μm polyethylene terephthalate film was coated with a roll coater and dried at 140 ° C. for 1 minute to form an active light absorbing layer of about 3 μm.
【００３９】次に、活性光線吸収層とは異なる面に剥離
層形成液−１をロールコーターで塗布し、 140℃１分間
乾燥して、約３μｍの剥離層を形成した。得られた剥離
層の反射率を測定（日立 320 Spectrophotometer、 150
φ積分球付属装置使用）したところ８％（360nm)の全反
射率を示した。この剥離層の上に中間層形成液をロール
コーターで塗布し、 110℃１分間乾燥して、塗工量約１
μｍの中間層を形成した。更にこの上に着色感光層形成
液のイエロー液をロールコーターで塗布、乾燥して塗工
量約２μｍの着色感光層を形成しイエローの感光性転写
シートを得た。マゼンタ、シアンについても同様にして
着色感光層（塗工量約２μｍ）を形成し感光性転写シー
トを得た。Next, a release layer forming solution-1 was applied on a surface different from the active light absorbing layer by a roll coater and dried at 140 ° C. for 1 minute to form a release layer of about 3 μm. The reflectance of the obtained release layer was measured (Hitachi 320 Spectrophotometer, 150
(using a device attached to a φ-integrating sphere), and showed a total reflectance of 8% (360 nm). An intermediate layer forming liquid is applied on the release layer by a roll coater, dried at 110 ° C. for 1 minute, and applied in an amount of about 1
A μm intermediate layer was formed. Further, a yellow liquid of a colored photosensitive layer forming liquid was applied thereon by a roll coater and dried to form a colored photosensitive layer having a coating amount of about 2 μm, thereby obtaining a yellow photosensitive transfer sheet. A colored photosensitive layer (coating amount: about 2 μm) was similarly formed for magenta and cyan to obtain a photosensitive transfer sheet.
【００４０】これとは別に、活性光線吸収層の反対面に
剥離層形成液−２をロールコーターで塗布し 140℃１分
間乾燥して、約３μｍの剥離層を形成した。同様に反射
率を測定したところ35％（360nm)の全反射率が得られ
た。この剥離層の上に中間層形成液をロールコーターで
塗布し、 110℃１分間乾燥して、塗工量約１μｍの中間
層を形成した。更にこの上に着色感光層形成液のブラッ
ク液をロールコーターで塗布、乾燥して塗工量約２μｍ
の着色感光層を形成しブラックの感光性転写シートを得
た。Separately, a release layer forming solution-2 was applied to the opposite surface of the active light absorbing layer using a roll coater and dried at 140 ° C. for 1 minute to form a release layer of about 3 μm. When the reflectance was measured in the same manner, a total reflectance of 35% (360 nm) was obtained. An intermediate layer forming liquid was applied on the release layer by a roll coater and dried at 110 ° C. for 1 minute to form an intermediate layer having a coating amount of about 1 μm. Further, a black liquid of the colored photosensitive layer forming liquid was applied thereon by a roll coater and dried to obtain a coating amount of about 2 μm.
Was formed to obtain a black photosensitive transfer sheet.
【００４１】このようにして作られたブラック用感光性
転写シートの着色感光面にブラック（スミ）版用の色分
解網ネガフィルムを密着させ、２KWの高圧水銀灯で１ｍ
の距離から15秒間露光を与え、その後被露光部を１kg／
cm2 に加圧したノズルから噴出する常温水で水洗溶去
し、水切りの後約50℃の温風で乾燥し、ブラックに着色
したネガ−ポジ画像を得た。同様にシアン、マゼンタ、
イエローについても各々対応する色分解網ネガフィルム
を用い、それぞれ上記と同様の操作を行ないシアン、マ
ゼンタ、イエローに着色したネガ−ポジ画像を得た。何
れも、15秒の同一露光量で各色調同等の優れた網点再現
性が得られた。A color separation net negative film for a black (sumi) plate is brought into close contact with the colored photosensitive surface of the thus-prepared black photosensitive transfer sheet, and a 1 Km high-pressure mercury lamp of 2 KW is applied.
Exposure for 15 seconds from the distance of
Water was removed by washing with normal temperature water jetted from a nozzle pressurized to cm 2 , water was removed, and after drying with hot air at about 50 ° C., a black-colored negative-positive image was obtained. Similarly, cyan, magenta,
With respect to yellow, a negative-positive image colored cyan, magenta, and yellow was obtained by performing the same operation as above using the corresponding color separation net negative films. In each case, excellent halftone dot reproducibility equivalent to each color tone was obtained with the same exposure amount of 15 seconds.
【００４２】更に、坪量 129.7ｇ／ｍ2 のコート紙を支
持体として、その片面に塩化ビニルと塩化ビニリデンの
共重合体のトルエン／酢酸エチル溶液を塗布、乾燥して
６μｍの厚さの熱融着層を形成して被転写材料を得た。
この被転写材料の熱融着層面に、前記ポジ画像を有する
ブラック用感光性転写シートの画像面を重ね、 100℃に
加熱したローラーで押圧してから、感光性転写シートの
支持体を剥離層と中間層の間から剥離すると、着色画像
は中間層と共に被転写材料の被転写面上に容易に転写さ
れた。転写時の密着性は良好であった。次いで、被転写
材料上に転写されたブラック画像上に、前記シアン、マ
ゼンタ、イエロー画像を順次同様な操作で熱転写するこ
とにより、コート紙上に４色からなる多色画像を得た。
これは最終印刷物に酷似した高精度のプレプレスカラー
プルーフであった。Further, using a coated paper having a basis weight of 129.7 g / m 2 as a support, a toluene / ethyl acetate solution of a copolymer of vinyl chloride and vinylidene chloride was applied to one side of the coated paper, dried and dried to a thickness of 6 μm. A transfer material was obtained by forming a fusion layer.
The image surface of the photosensitive transfer sheet for black having the positive image is superimposed on the surface of the heat-sealing layer of the material to be transferred, pressed with a roller heated to 100 ° C., and then the support of the photosensitive transfer sheet is peeled off. When peeled from between the and the intermediate layer, the colored image was easily transferred onto the transfer surface of the transfer material together with the intermediate layer. Adhesion during transfer was good. Next, the cyan, magenta, and yellow images were successively thermally transferred onto the black image transferred onto the transfer material by the same operation, thereby obtaining a multicolor image of four colors on coated paper.
This was a high precision prepress color proof very similar to the final print.
【００４３】（実施例２）実施例１の剥離層形成液−２
のパール顔料の添加量を以下のように変えた他は、全て
実施例１と同様に行なった。Example 2 Release Layer Forming Solution-2 of Example 1
All were performed in the same manner as in Example 1 except that the amount of the pearl pigment was changed as follows.
【００４４】 ＜剥離層形成液−２＞ テスファイン３２２ 5部 （アクリルアミド共重合物：日立化成ポリマー（株）） ドライヤー９００ 0.6部 （パラトルエンスルホン酸：日立化成ポリマー（株）） リューロンＱｕ−６２８ 100部 （塩化ビニル−プロピオン酸ビニル共重合体：東ソー（株）） ＩＲＩＯＤＩＮ−１１１ 10部 （パール顔料：メルクジャパン（株）） トルエン 36部 メチルエチルケトン 36部 シクロヘキサノン 18部<Release Layer Forming Solution-2> 5 parts of Tesfine 322 (acrylamide copolymer: Hitachi Chemical Co., Ltd.) Dryer 900 0.6 parts (paratoluenesulfonic acid: Hitachi Chemical Co., Ltd.) Ryuron Qu-628 100 parts (vinyl chloride-vinyl propionate copolymer: Tosoh Corporation) IRIODIN-111 10 parts (Pearl pigment: Merck Japan K.K.) Toluene 36 parts Methyl ethyl ketone 36 parts Cyclohexanone 18 parts
【００４５】実施例１同様に上記剥離層形成液−２をブ
ラック用感光性転写シートに用いたところ、得られた剥
離層の全反射率は22％（360nm)で、20秒の同一露光量で
各色調同等の網点再現性が得られた。被転写材料上に形
成された多色画像は最終印刷物に酷似した高精度のプレ
プレスカラープルーフであった。When the above release layer forming liquid-2 was used for a photosensitive transfer sheet for black in the same manner as in Example 1, the total reflectance of the obtained release layer was 22% (360 nm), and the same exposure amount for 20 seconds was used. As a result, halftone dot reproducibility equivalent to each color tone was obtained. The multicolor image formed on the transfer material was a high-precision prepress color proof that closely resembled the final print.
【００４６】実施例１同様に上記剥離層形成液−２をブ
ラック用感光性転写シートに用いたところ、得られた剥
離層の全反射率は22％（360nm)で、20秒の同一露光量で
各色調同等の網点再現性が得られた。被転写材料上に形
成された多色画像は最終印刷物に酷似した高精度のプレ
プレスカラープルーフであった。When the above release layer forming liquid-2 was used for a photosensitive transfer sheet for black in the same manner as in Example 1, the total reflectance of the obtained release layer was 22% (360 nm), and the same exposure amount for 20 seconds was obtained. As a result, halftone dot reproducibility equivalent to each color tone was obtained. The multicolor image formed on the transfer material was a high-precision prepress color proof that closely resembled the final print.
【００４７】（実施例３）実施例１の剥離層形成液−２
の顔料を以下のように変えた他は、全て実施例１と同様
に行なった。Example 3 Release Layer Forming Solution-2 of Example 1
All were carried out in the same manner as in Example 1, except that the following pigment was changed.
【００４８】 ＜剥離層形成液−２＞ テスファイン３２２ 5部 （アクリルアミド共重合物：日立化成ポリマー（株）） ドライヤー９００ 0.6部 （パラトルエンスルホン酸：日立化成ポリマー（株）） リューロンＱｕ−６２８ 100部 （塩化ビニル−プロピオン酸ビニル共重合体：東ソー（株）） ＦＡ−５５Ｗ 30部 （酸化チタン：古河機械金属（株）） トルエン 36部 メチルエチルケトン 36部 シクロヘキサノン 18部<Release Layer Forming Solution-2> 5 parts of Tesfine 322 (acrylamide copolymer: Hitachi Chemical Co., Ltd.) Dryer 900 0.6 parts (paratoluenesulfonic acid: Hitachi Chemical Co., Ltd.) Ryuron Qu-628 100 parts (vinyl chloride-vinyl propionate copolymer: Tosoh Corporation) FA-55W 30 parts (titanium oxide: Furukawa Kikai Metals Co., Ltd.) Toluene 36 parts Methyl ethyl ketone 36 parts Cyclohexanone 18 parts
【００４９】実施例１同様に上記剥離層形成液−２をブ
ラック用感光性転写シートに用いたところ、得られた剥
離層の全反射率は20％（360nm)で、20秒の同一露光量で
各色調同等の網点再現性が得られた。被転写材料上に形
成された多色画像は最終印刷物に酷似した高精度のプレ
プレスカラープルーフであった。When the above-mentioned release layer forming liquid-2 was used for a photosensitive transfer sheet for black in the same manner as in Example 1, the total reflectance of the obtained release layer was 20% (360 nm), and the same exposure amount for 20 seconds was obtained. As a result, halftone dot reproducibility equivalent to each color tone was obtained. The multicolor image formed on the transfer material was a high-precision prepress color proof that closely resembled the final print.
【００５０】（比較例１）実施例１の剥離層形成液−１
をブラック、シアン、マゼンタ、イエローの全ての色調
の感光性転写シートに用いた他は実施例１と同様に行な
ったところ、15秒の同一露光量で各色調同等の網点再現
性を得ることはできなかった。Comparative Example 1 Release Layer Forming Solution-1 of Example 1
Was performed in the same manner as in Example 1 except that the photosensitive transfer sheet of all colors of black, cyan, magenta, and yellow was used. The same halftone dot reproducibility was obtained with the same exposure amount of 15 seconds. Could not.
【００５１】以上の結果を表１および表２にまとめた。
表２に示される剥離層の全反射率（％）を有する感光性
転写シートを用いることにより、表１の特性を有する網
点再現可能な露光量（秒）が得られた。表１から分るよ
うに実施例１〜３はブラック、シアン、マゼンタ、イエ
ロー、各色共通の露光量を有するのに対し、比較例１で
は各色共通の露光量が存在しない。The above results are summarized in Tables 1 and 2.
By using a photosensitive transfer sheet having the total reflectance (%) of the release layer shown in Table 2, an exposure amount (second) capable of reproducing halftone dots having the characteristics shown in Table 1 was obtained. As can be seen from Table 1, Examples 1 to 3 have an exposure amount common to black, cyan, magenta and yellow, and each color, whereas Comparative Example 1 has no exposure amount common to each color.
【００５２】[0052]
【表１】 [Table 1]
【００５３】[0053]
【表２】 [Table 2]
【００５４】[0054]
【発明の効果】本発明の感光性転写シートは剥離層に活
性光線反射性物質を添加し、反射特性を調節することに
より、着色感光層の感度コントロールを可能にした。こ
れにより、各色調の感光性転写シートの感度を同一化す
ることができ、作業性が向上し、より安定した高精度の
プレプレスカラープルーフを得こるとができた。According to the photosensitive transfer sheet of the present invention, the sensitivity of the colored photosensitive layer can be controlled by adding an actinic light reflective substance to the release layer and adjusting the reflection characteristics. As a result, the sensitivity of the photosensitive transfer sheet of each color can be made the same, the workability is improved, and a more stable and accurate prepress color proof can be obtained.
【図１】図１は本発明の方法を段階を追って模式的に示
したものである。FIG. 1 schematically shows the method of the present invention step by step.
Ａ−１ 感光性転写シートの透明支持体 Ａ−２ 感光性転写シートの活性光線吸収層 Ｂ−１ 感光性転写シートの剥離層 Ｂ−２ 感光性転写シートの中間層 Ｃ−１〜Ｃ−４ 露光・現像後の感光性転写シートの各
着色画像 Ｄ 被転写材料の支持体 Ｅ 被転写材料の熱融着層A-1 Transparent support of photosensitive transfer sheet A-2 Active light absorbing layer of photosensitive transfer sheet B-1 Release layer of photosensitive transfer sheet B-2 Intermediate layer of photosensitive transfer sheet C-1 to C-4 Each colored image of the photosensitive transfer sheet after exposure and development D Support of transfer material E Thermally fused layer of transfer material
───────────────────────────────────────────────────── フロントページの続き (56)参考文献 特開 平３−144647（ＪＰ，Ａ) 特開 平２−308253（ＪＰ，Ａ) 特開 平４−358151（ＪＰ，Ａ) 特開 平５−273759（ＪＰ，Ａ) 特開 昭61−286858（ＪＰ，Ａ) 特開 平４−199056（ＪＰ，Ａ) 特開 昭61−213843（ＪＰ，Ａ) 特開 昭63−253941（ＪＰ，Ａ) 特開 平１−282542（ＪＰ，Ａ) (58)調査した分野(Int.Cl.6，ＤＢ名) G03F 7/004 G03F 7/105 G03F 7/11 ──────────────────────────────────────────────────続 き Continuation of the front page (56) References JP-A-3-144647 (JP, A) JP-A-2-308253 (JP, A) JP-A-4-358151 (JP, A) JP-A-5-358 273759 (JP, A) JP-A-61-286858 (JP, A) JP-A-4-199056 (JP, A) JP-A-61-213843 (JP, A) JP-A-63-253941 (JP, A) JP-A-1-282542 (JP, A) (58) Fields investigated (Int. Cl. 6 , DB name) G03F 7/004 G03F 7/105 G03F 7/11
Claims (5)
剤、帯電防止剤、塗膜形成性高分子樹脂からなる透明性
の活性光線吸収層が積層され、該透明支持体の他方の面
に透明支持体に強く接着している透明性の剥離層、該剥
離層から剥離可能である熱融着性の透明な中間層および
着色感光層が順次積層された感光性転写シートにおい
て、該剥離層を形成する塗膜形成性高分子樹脂中に活性
光線反射性物質を含有せしめたことを特徴とする感光性
転写シート。1. A transparent active light-absorbing layer comprising an active light-absorbing agent, an antistatic agent, and a film-forming polymer resin is laminated on one surface of a transparent support, and the other surface of the transparent support is provided. In a photosensitive transfer sheet in which a transparent release layer strongly adhered to a transparent support, a heat-fusible transparent intermediate layer releasable from the release layer and a colored photosensitive layer are sequentially laminated, A photosensitive transfer sheet comprising an actinic light-reflective substance contained in a film-forming polymer resin for forming a layer.
の表面処理を施された雲母系顔料、粉末アルミニュー
ム、酸化チタン、酸化亜鉛、硫酸バリウムのいずれか、
あるいはこれらの混合物であることを特徴とする請求項
１記載の感光性転写シート。2. The actinic ray-reflecting substance in the release layer is selected from the group consisting of mica pigments, powdered aluminum, titanium oxide, zinc oxide and barium sulfate, each of which has been subjected to various surface treatments.
2. The photosensitive transfer sheet according to claim 1, wherein the photosensitive transfer sheet is a mixture thereof.
率が１５％以上であることを特徴とする請求項１または
２記載の感光性転写シート。3. The photosensitive transfer sheet according to claim 1, wherein the release layer has a total reflectance of actinic rays (360 nm) of 15% or more.
ン樹脂、メラミン樹脂、フッ素樹脂、シリコン樹脂、ポ
リエステル、ポリオレフィンのいずれかあるいはこれら
の混合物であることを特徴とする請求項１〜３のいずれ
か１項記載の感光性転写シート。4. The film-forming polymer resin of the release layer is any one of a urethane resin, a melamine resin, a fluororesin, a silicone resin, a polyester and a polyolefin or a mixture thereof. The photosensitive transfer sheet according to any one of the above items.
ビニル共重合体、アクリル化合物のいずれかあるいはこ
れらの混合物であることを特徴とする請求項１〜４のい
ずれか１項記載の感光性転写シート。5. The photosensitive transfer sheet according to claim 1, wherein the intermediate layer is any one of polyester, ethylene-vinyl acetate copolymer, and acrylic compound, or a mixture thereof. .