JP2785515B2 - Antibacterial synthetic fiber and method for producing the same - Google Patents
Antibacterial synthetic fiber and method for producing the sameInfo
- Publication number
- JP2785515B2 JP2785515B2 JP3101585A JP10158591A JP2785515B2 JP 2785515 B2 JP2785515 B2 JP 2785515B2 JP 3101585 A JP3101585 A JP 3101585A JP 10158591 A JP10158591 A JP 10158591A JP 2785515 B2 JP2785515 B2 JP 2785515B2
- Authority
- JP
- Japan
- Prior art keywords
- silver
- antibacterial
- fiber
- zeolite
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【０００１】[0001]
【産業上の利用分野】本発明は、銀置換抗菌性ゼオライ
ト粒子を配合した合成繊維の色調を改善するために有効
な抗菌性合成繊維およびその製造方法に関するものであ
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an antibacterial synthetic fiber effective for improving the color tone of a synthetic fiber containing silver-substituted antibacterial zeolite particles and a method for producing the same.
【０００２】[0002]
【従来の技術】銀イオンで置換された抗菌性ゼオライト
を内部配合した繊維ならびにこれから得られた製品類
は、バクテリア、カビなどの微生物に対して優れた抗菌
作用を示すことが知られている（特公昭６３−５４０１
３号公報等）。2. Description of the Related Art It is known that fibers containing an antibacterial zeolite substituted with silver ions and products obtained therefrom have excellent antibacterial action against microorganisms such as bacteria and mold ( Tokiko 63-5401
No. 3 publication).
【０００３】また、銀イオンの他に、銅イオンや亜鉛イ
オンのような２価金属イオンも、銀イオンより効果が少
ないとはいえ相当な抗菌性と耐熱性を有するため、銀イ
オンと同時にゼオライトに吸着させた複合型の抗菌性ゼ
オライトで使用されることも多い。[0003] In addition to silver ions, divalent metal ions such as copper ions and zinc ions have considerable antibacterial properties and heat resistance even though they are less effective than silver ions. It is often used as a composite antibacterial zeolite that has been adsorbed on a surface.
【０００４】これら金属の１種以上を吸着させた金属置
換ゼオライトは通常の方法でポリマ中に配合され、繊維
やフィルム等に成形される。[0004] A metal-substituted zeolite having one or more of these metals adsorbed thereon is blended into a polymer by a usual method, and formed into a fiber or a film.
【０００５】[0005]
【発明が解決しようとする課題】ところが、従来の方法
で繊維を製造した場合、ゼオライト配合なしの繊維に比
べかなり色調が悪化するという問題があった。この色調
悪化は、銀とともに銅を担持させた抗菌性ゼオライトの
ように、銅が併存するポリマの場合に、特に大きく、染
色してもくすみのある色彩となるのであった。However, when the fiber is produced by the conventional method, there is a problem that the color tone is considerably deteriorated as compared with the fiber without zeolite. This deterioration in color tone was particularly large in the case of a polymer in which copper coexists, such as an antibacterial zeolite carrying copper together with silver, and the color became dull even when dyed.
【０００６】繊維の色調は、衣料用や内装用などの用途
では最も重視される要件の１つであり、その改善が強く
望まれていた。[0006] The color tone of the fiber is one of the most important requirements in applications such as clothing and interiors, and improvement thereof has been strongly desired.
【０００７】そこで、本発明は、上述のような従来技術
の欠点を解消し、色調の改善された銀置換ゼオライト系
抗菌性合成繊維、およびその製造方法を提供することを
主たる目的とする。Accordingly, an object of the present invention is to provide a silver-substituted zeolite-based antibacterial synthetic fiber having an improved color tone, which solves the above-mentioned disadvantages of the prior art, and a method for producing the same.
【０００８】[0008]
【課題を解決するための手段】この目的を達成するた
め、本発明は、繊維に対して０．０１〜２０重量％の銀
置換抗菌性ゼオライトと０．００１〜１．０重量％のハ
ロゲン化アルカリとを含有する抗菌性合成繊維からな
る。In order to achieve this object, the present invention relates to a method for producing a silver-substituted antibacterial zeolite of 0.01 to 20% by weight and a halogenation of 0.001 to 1.0% by weight based on fibers. It is made of antibacterial synthetic fiber containing alkali.
【０００９】そして、この抗菌性性合成繊維は、例え
ば、銀置換抗菌性ゼオライトをポリマの重合が完了する
前の段階で添加し、かつ、ハロゲン化アルカリを紡糸前
のポリマに添加することにより、ポリマに対して０．０
１〜２０重量％の銀置換抗菌性ゼオライトと０．００１
〜１．０重量％のハロゲン化アルカリとを含有するポリ
マ組成物とした後、紡糸して繊維とする方法によって製
造することができる。The antibacterial synthetic fiber is prepared by, for example, adding a silver-substituted antibacterial zeolite at a stage before polymerization of the polymer is completed, and adding an alkali halide to the polymer before spinning. 0.0 for polymer
1 to 20% by weight of silver-substituted antibacterial zeolite and 0.001
After preparing a polymer composition containing 組成 1.0% by weight of an alkali halide, it can be produced by spinning into a fiber.
【００１０】本発明で用いる銀置換ゼオライトとして
は、次のような物が挙げられる。The following are examples of the silver-substituted zeolite used in the present invention.
【００１１】銀置換する前のゼオライトは、ＳｉＯ2 と
Ａｌ2 Ｏ3 を主成分とした３次元骨格のアルミノケイ酸
塩であり、天然ゼオライト、合成ゼオライトのいずれを
も用いることができる。代表的なものとしては、チャバ
サイト（Chabazite)、クリノプチロライト（Clinoptilo
lite）、エリオナイト（Erionite）、フォージャサイト
（Faujasite)、モルデナイト（Mordenite)などの天然ゼ
オライト；Ａ型、Ｘ型、Ｙ型、モルデナイト型、ペンタ
シル型、フェリエライト型、ベータ型、ＺＳＭ−５型、
ＺＳＭ−１１型などの合成ゼオライトが適当である。溶
融紡糸における着色を抑え、粒子分散性を高めるために
は、ＳｉＯ2 ／Ａｌ2 Ｏ3 モル比が、例えば１５以上と
高いゼオライトの方が好ましい。The zeolite before silver substitution is an aluminosilicate having a three-dimensional skeleton containing SiO 2 and Al 2 O 3 as main components, and either a natural zeolite or a synthetic zeolite can be used. Typical examples are Chabazite and Clinoptilolite.
zeolites), natural zeolites such as Erionite, Faujasite, Mordenite; A type, X type, Y type, mordenite type, pentasil type, ferrierite type, beta type, ZSM-5 Type,
Synthetic zeolites such as ZSM-11 type are suitable. In order to suppress coloring in the melt spinning and enhance the particle dispersibility, zeolite having a high SiO 2 / Al 2 O 3 molar ratio of, for example, 15 or more is more preferable.
【００１２】これらゼオライトは、イオン交換反応によ
ってゼオライト中のアルカリあるいはアルカリ土類金属
と銀イオンとを置換して銀置換ゼオライトとすればよ
い。具体的には、水溶性銀化合物の溶液で処理すればよ
い。本発明で使用する銀置換ゼオライトは、銀イオンと
ともに他の金属イオン（銅、亜鉛など）が同時置換され
た複合型の抗菌性ゼオライトであってもよい。These zeolites may be replaced with silver ions by replacing the alkali or alkaline earth metal in the zeolite with silver ions by an ion exchange reaction. Specifically, the treatment may be performed with a solution of a water-soluble silver compound. The silver-substituted zeolite used in the present invention may be a composite antibacterial zeolite in which other metal ions (copper, zinc, etc.) are simultaneously substituted with silver ions.
【００１３】銀イオンの置換量は、ゼオライトの構造、
ＳｉＯ2 ／Ａｌ2 Ｏ3 モル比などで変わるが、銀置換ゼ
オライトに対し０．１〜２０重量％の範囲が一般的であ
る。The substitution amount of silver ion is determined by the structure of zeolite,
Although it varies depending on the SiO 2 / Al 2 O 3 molar ratio and the like, the range is generally 0.1 to 20% by weight based on the silver-substituted zeolite.
【００１４】銀置換ゼオライトの合成繊維への配合量
は、置換されている銀量により変わるが、一般には繊維
に対して０．０１〜２０重量％が適当である。なかで
も、０．０５〜５重量％が好ましく、特に、０．１〜１
重量％が好ましい。その配合量が、少な過ぎれば抗菌効
果が不十分である。逆に、多過ぎれば繊維化することが
困難となるし、また、着色が大きくなるので染色された
繊維の色調が悪化し、商品価値が著しく低下する。The amount of the silver-substituted zeolite in the synthetic fiber varies depending on the amount of silver substituted, but generally, 0.01 to 20% by weight based on the fiber is appropriate. Among them, 0.05 to 5% by weight is preferable, and in particular, 0.1 to 1% by weight.
% By weight is preferred. If the amount is too small, the antibacterial effect is insufficient. Conversely, if the amount is too large, it becomes difficult to form fibers, and the coloration becomes large, so that the color tone of the dyed fibers deteriorates and the commercial value drops significantly.
【００１５】銀置換ゼオライトの合成繊維への配合方法
は、合成繊維原料を重合する時でもよいし、また、紡糸
前のいずれでもよいが、なかでも、ポリマの重合前や重
合途中のようなポリマ重合完了前の段階での添加がゼオ
ライト粒子をポリマ中に均一に微分散させるために好ま
しい。The method of blending the silver-substituted zeolite with the synthetic fiber may be at the time of polymerizing the synthetic fiber raw material or at any time before the spinning. Addition at a stage before the completion of the polymerization is preferable for uniformly finely dispersing the zeolite particles in the polymer.
【００１６】また、本発明では、繊維に対して０．００
１〜１．０重量％のハロゲン化アルカリを配合すること
が必要である。[0016] In the present invention, the content of the fiber is 0.00%.
It is necessary to add 1 to 1.0% by weight of an alkali halide.
【００１７】このハロゲン化アルカリは、例えば、ヨウ
化カリウム、ヨウ化ナトリウム、臭化カリウム、臭化ナ
トリウムで代表され、なかでも、ハロゲン化カリウムが
好ましい。The alkali halide is represented by, for example, potassium iodide, sodium iodide, potassium bromide, and sodium bromide, with potassium halide being preferred.
【００１８】このハロゲン化アルカリの配合量は、一般
に、繊維に対して０．００１〜１．０重量％であればよ
い。さらに、０．０１〜０．１重量％が好ましい。この
ハロゲン化アルカリの配合量が少な過ぎる場合は、十分
な色調改善効果か得られない。逆に多過ぎると、紡糸時
における製糸性が悪化するし、また、ハロゲン化アルカ
リの配合時に混合斑となり易く製品の色調斑の誘因とな
る。The compounding amount of the alkali halide may generally be 0.001 to 1.0% by weight based on the fiber. Further, 0.01 to 0.1% by weight is preferable. If the amount of the alkali halide is too small, a sufficient effect of improving color tone cannot be obtained. On the other hand, if the amount is too large, the spinnability during spinning is deteriorated, and mixing of the alkali halide is apt to occur, resulting in uneven color tone of the product.
【００１９】このハロゲン化アルカリは、紡糸前のポリ
マに配合する方法が好ましく、その配合方法は、その特
性に応じた最適の方法を選択すればよい。例えば、繊維
形成に障害のない程度に微粉化できる化合物の場合は、
粉末状で繊維原料ポリマ（ペレット）とブレンドして十
分に混合した後に、紡糸に供すればよい。また、溶媒に
溶解できる化合物の場合は、溶解した濃厚液をポリマに
振り掛けた後乾燥する方法をとればよい。Preferably, the alkali halide is blended with the polymer before spinning, and the blending method may be selected from the most suitable method according to the characteristics. For example, in the case of a compound that can be pulverized to the extent that fiber formation is not impaired,
The powder may be blended with the fiber raw material polymer (pellet) and sufficiently mixed, and then subjected to spinning. In addition, in the case of a compound that can be dissolved in a solvent, a method in which the dissolved concentrated liquid is sprinkled on a polymer and then dried may be used.
【００２０】本発明の対象とする合成繊維は、特に限定
されないが、例えば、ポリアミド、ポリエステル、ポリ
アクリロニトリル、あるいはこれらの共重合体からなる
繊維が挙げられ、特に、ポリアミド繊維に本発明は好適
である。The synthetic fiber to be used in the present invention is not particularly limited, and examples thereof include a fiber made of polyamide, polyester, polyacrylonitrile, or a copolymer thereof. The present invention is particularly suitable for polyamide fiber. is there.
【００２１】適当なポリアミドとしては、ポリε−カプ
ロラクタム（ナイロン６）、ポリラウロラクタム（ナイ
ロン１２）、ジアミンとジカルボン酸からのポリアミ
ド、例えばポリヘキサメチレンアジパミド（ナイロン６
６）などが挙げられる。また、これらポリアミドと共重
合可能なジアミン−ジカルボン酸、ラクタム類とを共重
合してなるポリアミドも用い得る。Suitable polyamides include polyε-caprolactam (nylon 6), polylaurolactam (nylon 12), polyamides from diamines and dicarboxylic acids, such as polyhexamethylene adipamide (nylon 6).
6). Further, a polyamide obtained by copolymerizing a diamine-dicarboxylic acid and a lactam copolymerizable with these polyamides may also be used.
【００２２】これら合成繊維には、耐熱剤、耐光剤、分
散剤、制電剤などの通常の添加剤を同時に含有させても
よい。These synthetic fibers may contain ordinary additives such as a heat-resistant agent, a light-resistant agent, a dispersant, and an antistatic agent.
【００２３】これらポリマからの合成繊維の製造は、そ
のポリマに適した通常の方法によればよい。即ち、溶融
紡糸、湿式紡糸、乾式紡糸などの方法をとればよい。The production of synthetic fibers from these polymers may be carried out by a conventional method suitable for the polymer. That is, a method such as melt spinning, wet spinning, and dry spinning may be used.
【００２４】製糸して得られた抗菌性合成繊維は、その
ままフィラメント糸の状態で、仮撚加工や流体加工を施
したテキスチャードヤーンの状態で、ポリウレタン弾性
糸のカバリングに用いた被覆弾性糸の状態で、あるい
は、ステープル化し紡績した紡績糸の状態で布帛の製造
に用いられ、トリコット、丸編、織物、タフト織物な
ど、用途に応じた布帛製品とされる。The antibacterial synthetic fiber obtained by the spinning is used as a filament yarn in the state of a textured yarn which has been subjected to false twisting or fluid processing, and the coated elastic yarn used for covering the polyurethane elastic yarn. It is used in the production of a fabric in a state or in a state of a spun yarn that has been stapled and spun, and is a fabric product suitable for a use such as a tricot, a circular knit, a woven fabric, and a tufted woven fabric.
【００２５】これら布帛化までの工程で、この抗菌性合
成繊維は、他の合成繊維、例えば、通常のポリアミド繊
維、ポリエステル繊維、アクリル繊維；あるいは、綿、
ウールなどの天然繊維等と混用（例えば、混繊、混紡、
交編、混織等）して用いてもよいが、布帛製品における
本発明の抗菌性合成繊維の混率が１５％以上となるよう
に、布帛設計することが好ましい。混率が１５％未満と
少ない場合には、最終製品において十分な抗菌効果を発
揮することが困難である。In the process up to the formation of the fabric, the antibacterial synthetic fiber is made of another synthetic fiber such as ordinary polyamide fiber, polyester fiber, acrylic fiber;
Mixed with natural fibers such as wool (for example, mixed fiber, mixed spinning,
(Knitting, mixed weaving, etc.), but it is preferable to design the fabric such that the mixing ratio of the antibacterial synthetic fiber of the present invention in the fabric product is 15% or more. When the mixing ratio is as small as less than 15%, it is difficult to exhibit a sufficient antibacterial effect in the final product.
【００２６】このように用途に応じた方法で最終製品と
されるが、その最終製品とされるまでの任意の段階で、
必要に応じて染色され、さらに仕上げ加工されてもよ
い。As described above, the final product is formed by a method according to the application. At an arbitrary stage until the final product is obtained,
It may be dyed if necessary and further finished.
【００２７】その染料としては、合成繊維一般に用いら
れる染料、すなわち分散染料、酸性染料、含金染料、塩
基性染料、直接染料などが使用できる。As the dye, dyes generally used for synthetic fibers, that is, disperse dyes, acid dyes, gold-containing dyes, basic dyes, direct dyes and the like can be used.
【００２８】仕上げ加工としては、撥水、制電、柔軟加
工のような通常の仕上加工が挙げられる。Examples of the finishing include ordinary finishing such as water repellency, antistatic, and softening.
【００２９】[0029]
【作用】銀置換ゼオライトとともに配合されたハロゲン
化アルカリは、銀置換ゼオライトの配合に起因する色調
の悪化を大幅に抑制することができ、これは、次のよう
な理由によるものと考えられる。The alkali halide blended with the silver-substituted zeolite can significantly suppress the deterioration of the color tone caused by the blending of the silver-substituted zeolite, which is considered to be due to the following reasons.
【００３０】ハロゲン化アルカリを配合せずに銀置換ゼ
オライトのみを配合した場合では、銀置換ゼオライトか
ら遊離してポリマ中に存在する銀イオンが不安定である
ために還元や酸化されて金属銀や酸化銀となり易く、こ
れら金属銀や酸化銀がポリマ中に増加することによって
得られた繊維の色調悪化が生じる。When only the silver-substituted zeolite is compounded without the alkali halide, the silver ions released from the silver-substituted zeolite and present in the polymer are unstable, so that they are reduced or oxidized to form metallic silver or Silver oxide is liable to be produced, and the color tone of the obtained fiber is deteriorated due to the increase of these metallic silver and silver oxide in the polymer.
【００３１】ところが、銀置換ゼオライトとともにハロ
ゲン化アルカリを配合した繊維では、ハロゲン化アルカ
リがポリマ中の銀イオンの安定化に大きく寄与し、ポリ
マ中での金属銀や酸化銀の生成が抑制され、この結果、
得られた繊維の色調は大幅に改善される。However, in a fiber containing an alkali halide together with a silver-substituted zeolite, the alkali halide greatly contributes to stabilization of silver ions in the polymer, and the production of metallic silver and silver oxide in the polymer is suppressed. As a result,
The color tone of the fiber obtained is greatly improved.
【００３２】また、銀置換ゼオライトは、銅等の他の抗
菌性金属のみを置換含有するゼオライトに比し抗菌性が
はるかに優れているので、少量の使用で所望の抗菌効果
を得ることができるし、しかも、その抗菌性能は耐洗濯
性に優れているので、色調が重視される衣料用等に好適
である。Further, silver-substituted zeolites have much better antibacterial properties than zeolites substituted only with other antibacterial metals such as copper, so that a desired antibacterial effect can be obtained with a small amount of use. Moreover, since its antibacterial performance is excellent in washing resistance, it is suitable for clothing and the like where color tone is important.
【００３３】また、請求項２の製造方法のように、銀置
換抗菌性ゼオライトをポリマの重合が完了する前の段階
で添加し、かつ、ハロゲン化アルカリを紡糸前のポリマ
に添加するという方法をとることにより、色調に優れた
抗菌性繊維を工業的に容易に得ることができる。Further, a method of adding the silver-substituted antibacterial zeolite at a stage before the polymerization of the polymer is completed and adding an alkali halide to the polymer before the spinning as in the production method of claim 2 is also provided. By taking this, an antibacterial fiber excellent in color tone can be industrially easily obtained.
【００３４】[0034]
【実施例】・ 実施例１ モルデナイト型ゼオライト粒子（ＳｉＯ2 ／Ａｌ2 Ｏ3
モル比が１７）を硝酸銀水溶液で処理して銀イオンを
７．５重量％含有する銀置換抗菌性ゼオライト粒子を得
た。EXAMPLES Example 1 Mordenite-type zeolite particles (SiO 2 / Al 2 O 3)
The molar ratio of 17) was treated with an aqueous silver nitrate solution to obtain silver-substituted antibacterial zeolite particles containing 7.5% by weight of silver ions.
【００３５】得られた銀置換ゼオライト粒子をナイロン
６の重合前の段階で０．３重量％添加し、常法どおり重
合して９８％硫酸相対粘度が２．７５の抗菌性ナイロン
６ペレットを得た。The obtained silver-substituted zeolite particles were added in an amount of 0.3% by weight before the polymerization of nylon 6, and polymerized in a usual manner to obtain antibacterial nylon 6 pellets having 98% sulfuric acid and a relative viscosity of 2.75. Was.
【００３６】得られた抗菌性ナイロン６ペレットを乾燥
した後、ヨウ化カリウムを、ポリマに対し、０．０１重
量％、０．０５重量％、０．５重量％、または、１．５
重量％添加し、十分に混合、乾燥した後、常法どおり溶
融紡糸して、３０デニール、６フィラメントのナイロン
６フィラメント糸を得た（ No.１、２）。After drying the obtained antibacterial nylon 6 pellets, potassium iodide was added to the polymer in an amount of 0.01% by weight, 0.05% by weight, 0.5% by weight, or 1.5% by weight.
% By weight, thoroughly mixed and dried, and then melt-spun in a conventional manner to obtain a 30-denier, 6-filament nylon 6 filament yarn (Nos. 1, 2).
【００３７】また、比較として、ハロゲン化アルカリを
添加しない以外は上記同様の方法で銀置換ゼオライトの
みを配合したナイロン６フィラメント糸を、また、銀置
換ゼオライトを添加しない以外は上記同様の方法でヨウ
化カリウム０．０５重量％のみを配合したナイロン６フ
ィラメント糸を、それぞれ得た（ No.３、４）。For comparison, a nylon 6 filament yarn blended with only silver-substituted zeolite was prepared in the same manner as above except that no alkali halide was added, and iodine was prepared in the same manner as above except that no silver-substituted zeolite was added. Nylon 6 filament yarns containing only 0.05% by weight of potassium iodide were obtained (Nos. 3 and 4).
【００３８】さらに比較として、銀置換ゼオライトも銅
化合物も添加しない以外は上記同様の方法で、ナイロン
６フィラメント糸を得た（ No.５）。For comparison, a nylon 6 filament yarn was obtained in the same manner as described above except that neither the silver-substituted zeolite nor the copper compound was added (No. 5).
【００３９】これらフィラメント糸を常法どおりに整経
し編立てして３２ゲージのハーフトリコットを編成し
た。These filament yarns were warped and knitted in a conventional manner to knit a 32-gauge half tricot.
【００４０】得られた編地について、抗菌性能の評価を
次のシェイク・フラスコ法によって行なった。The obtained knitted fabric was evaluated for antibacterial performance by the following shake flask method.
【００４１】試料布帛に試験菌（黄色ブドウ状球菌 Sta
phylococcus aereus IFO12732 ）の懸濁緩衝液を注加
し、密閉容器中で１５０回／分、１時間振盪し、その振
盪後の生菌数を計測し、注加懸濁液の菌数に対する減少
率差（％）を求めた。A test bacterium (Staphylococcus aureus Sta.
phylococcus aereus IFO12732) was added thereto, and the mixture was shaken at 150 times / min for 1 hour in a closed container, and the number of viable cells after the shaking was counted. The difference (%) was determined.
【００４２】さらに、得られたハーフトリコットを、酸
性染料である“Nylusan Blue N-GFL”（サンド（株）
製）、０．８重量％owf.、９８℃、６０分間で染色し
た。Further, the obtained half tricot was used as an acid dye “Nylusan Blue N-GFL” (Sand Co., Ltd.).
), 0.8% by weight owf., 98 ° C, 60 minutes.
【００４３】得られた染色前の編地、及び染色後の編地
について、色調を、銀置換ゼオライトもヨウ化カリウム
も添加してない繊維（ No.５）を基準にした目視による
相対的判定によって評価した。The color tone of the obtained knitted fabric before dyeing and the knitted fabric after dyeing was visually judged relative to the fiber (No. 5) to which neither silver-substituted zeolite nor potassium iodide was added. Was evaluated by.
【００４４】[0044]
【表１】[Table 1]
【００４５】 表１に示すように、銀置換ゼオライトとともに、０．０
０１〜１．０重量％のハロゲン化アルカリを配合してな
る本発明の場合（ No.１、２）は、染色の前でも、染色
した製品でも、優れた色調を示した。[0045] As shown in Table 1, together with the silver-substituted zeolite, 0.0
In the case of the present invention (No. 1 and No. 2) in which the alkali halide was blended in an amount of from 01 to 1.0% by weight, excellent color tone was exhibited both before and after dyeing.
【００４６】これに対し、銀置換ゼオライトのみでハロ
ゲン化アルカリを配合しなかった場合（ No.３）は、色
調が劣っていた。On the other hand, when only the silver-substituted zeolite and no alkali halide were blended (No. 3), the color tone was inferior.
【００４７】また、銀置換ゼオライトを配合しなかった
場合（ No.４、５）は抗菌性能を得ることはできなかっ
た。When no silver-substituted zeolite was blended (Nos. 4 and 5), no antibacterial performance was obtained.
【００４８】・ 実施例２ 銀置換ゼオライトとして、ＳｉＯ2 ／Ａｌ2 Ｏ3 モル比
が１７．０のモルデナイト型ゼオライトを、硝酸銀と硫
酸銅水溶液で処理して、銀および銅がそれぞれ２．０重
量％、４．０重量％置換した複合型金属置換ゼオライト
を得、これを実施例１と同様の方法でナイロン６の重合
前の段階で０．７重量％添加し、硫酸相対粘度が２．７
２の変性ナイロン６ペレットを得た。次いで、実施例１
の No.２と同様に０．０５重量％のヨウ化カリウムを配
合し、溶融紡糸してナイロン６フィラメント糸を得た
（ No.６）。Example 2 As a silver-substituted zeolite, a mordenite-type zeolite having a SiO 2 / Al 2 O 3 molar ratio of 17.0 was treated with silver nitrate and an aqueous solution of copper sulfate to obtain silver and copper of 2.0 weight% each. %, 4.0% by weight of the composite metal-substituted zeolite was obtained, and 0.7% by weight was added in the same manner as in Example 1 before the polymerization of nylon 6 to obtain a sulfuric acid relative viscosity of 2.7.
2 modified nylon 6 pellets were obtained. Then, Example 1
As in No. 2 of No. 2, 0.05% by weight of potassium iodide was blended and melt-spun to obtain a nylon 6 filament yarn (No. 6).
【００４９】また、比較として、ヨウ化カリウムを配合
しなかった以外は上記と同様にして、ナイロン６フィラ
メント糸を得た（ No.７）。For comparison, a nylon 6 filament yarn was obtained in the same manner as above except that potassium iodide was not blended (No. 7).
【００５０】得られたフィラメント糸を、実施例１と同
様に、ハーフトリコットを編成し、染色して染色編地と
し、さらに、抗菌性能及び色調を評価した。In the same manner as in Example 1, the obtained filament yarn was knitted into a half tricot, dyed to obtain a dyed knitted fabric, and further evaluated for antibacterial performance and color tone.
【００５１】[0051]
【表２】[Table 2]
【００５２】 表２に示すように、ハロゲン化アルカリの併用による色
調改善効果は、銀とともに銅を置換した複合型の抗菌性
ゼオライトを配合した繊維の場合でも顕著なものであっ
た。[0052] As shown in Table 2, the effect of improving the color tone by the combined use of the alkali halide was remarkable even in the case of the fiber in which the composite antibacterial zeolite in which copper was replaced with silver was blended.
【００５３】[0053]
【発明の効果】本発明に係る抗菌性繊維とすると、銀置
換ゼオライトの配合による抗菌性繊維の色調を大幅に改
善することができるので、抗菌性能に優れ、かつ、色調
も良好な抗菌性繊維を得ることができる。According to the antibacterial fiber of the present invention, the color tone of the antibacterial fiber obtained by blending the silver-substituted zeolite can be greatly improved, so that the antibacterial fiber having excellent antibacterial performance and good color tone can be obtained. Can be obtained.
【００５４】この抗菌性能は、例えば、黄色フドウ状球
菌、大腸菌、枯草菌、肺炎棹菌、緑膿菌のようなバクテ
リア類、カンジタ菌、白癬菌のような真菌類（カビ）に
対し発揮される。This antibacterial performance is exerted against bacteria such as Staphylococcus aureus, Escherichia coli, Bacillus subtilis, Klebsiella pneumoniae and Pseudomonas aeruginosa, and fungi (molds) such as Candida and Trichophyton. You.
【００５５】本発明により得られる抗菌性繊維は、色調
が重視される用途、例えば、ランジェリー、下着類のよ
うな衣料品、ストッキングやソックスのような靴下製
品、室内装飾品類、などに有用である。The antibacterial fiber obtained by the present invention is useful for applications where color tone is important, for example, clothing such as lingerie and underwear, sock products such as stockings and socks, and upholstery. .
【００５６】また、請求項２の製造方法によると、この
抗菌性繊維を、工業的に容易に製造することができる。Further, according to the production method of the second aspect, the antibacterial fiber can be easily produced industrially.
Claims (2)
銀置換抗菌性ゼオライトと０．００１〜１．０重量％の
ハロゲン化アルカリとを含有することを特徴とする抗菌
性合成繊維。1. An antibacterial synthetic fiber containing 0.01 to 20% by weight of a silver-substituted antibacterial zeolite and 0.001 to 1.0% by weight of an alkali halide based on the fiber.
合が完了する前の段階で添加し、かつ、ハロゲン化アル
カリを紡糸前のポリマに添加することにより、ポリマに
対して０．０１〜２０重量％の銀置換抗菌性ゼオライト
と０．００１〜１．０重量％のハロゲン化アルカリとを
含有するポリマ組成物とした後、紡糸して繊維とするこ
とを特徴とする抗菌性合成繊維の製造方法。2. The method according to claim 1, wherein the silver-substituted antibacterial zeolite is added at a stage before the polymerization of the polymer is completed, and an alkali halide is added to the polymer before spinning, so that the weight of the polymer is 0.01 to 20% by weight. % Of a silver-substituted antibacterial zeolite and 0.001 to 1.0% by weight of an alkali halide, and then spun to obtain a fiber. .