JP2022066412A - ポリイミドの製造方法 - Google Patents
ポリイミドの製造方法 Download PDFInfo
- Publication number
- JP2022066412A JP2022066412A JP2022033381A JP2022033381A JP2022066412A JP 2022066412 A JP2022066412 A JP 2022066412A JP 2022033381 A JP2022033381 A JP 2022033381A JP 2022033381 A JP2022033381 A JP 2022033381A JP 2022066412 A JP2022066412 A JP 2022066412A
- Authority
- JP
- Japan
- Prior art keywords
- diamine
- component
- polyimide
- less
- acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
本発明のポリイミドの製造方法において、前記ダイマージアミン組成物は、下記成分(a)~(c);
(a)ダイマージアミン;
(b)炭素数10~40の範囲内にある一塩基酸化合物の末端カルボン酸基を1級アミノメチル基又はアミノ基に置換して得られるモノアミン化合物;
(c)炭素数41~80の範囲内にある炭化水素基を有する多塩基酸化合物の末端カルボン酸基を1級アミノメチル基又はアミノ基に置換して得られるアミン化合物(但し、前記ダイマージアミンを除く);
について、
前記(a)成分の含有量が、前記ダイマージアミン組成物に対し、96重量%以上であり、
前記ダイマージアミン組成物のゲル浸透クロマトグラフィーを用いた測定におけるクロマトグラムの面積パーセントで、前記成分(b)及び(c)の合計が4%以下であることを特徴とする。
本発明の実施の形態に係るポリイミドに使用されるテトラカルボン酸無水物としては、例えば、3,3’、4,4’-ビフェニルテトラカルボン酸二無水物、ピロメリット酸二無水物、1,4-フェニレンビス(トリメリット酸モノエステル)二無水物、3,3’,4,4’-ジフェニルスルホンテトラカルボン酸二無水物、4,4’-オキシジフタル酸無水物、2,3',3,4'-ビフェニルテトラカルボン酸二無水物、2,2',3,3'-、2,3,3',4'-又は3,3',4,4'-ベンゾフェノンテトラカルボン酸二無水物、2,3',3,4'-ジフェニルエーテルテトラカルボン酸二無水物、ビス(2,3-ジカルボキシフェニル)エーテル二無水物、3,3'',4,4''-、2,3,3'',4''-又は2,2'',3,3''-p-テルフェニルテトラカルボン酸二無水物、2,2-ビス(2,3-又は3,4-ジカルボキシフェニル)-プロパン二無水物、ビス(2,3-又は3.4-ジカルボキシフェニル)メタン二無水物、ビス(2,3-又は3,4-ジカルボキシフェニル)スルホン二無水物、1,1-ビス(2,3-又は3,4-ジカルボキシフェニル)エタン二無水物、1,2,7,8-、1,2,6,7-又は1,2,9,10-フェナンスレン-テトラカルボン酸二無水物、2,3,6,7-アントラセンテトラカルボン酸二無水物、2,2-ビス(3,4-ジカルボキシフェニル)テトラフルオロプロパン二無水物、2,3,5,6-シクロヘキサン二無水物、1,2,5,6-ナフタレンテトラカルボン酸二無水物、1,4,5,8-ナフタレンテトラカルボン酸二無水物、2,3,6,7-ナフタレンテトラカルボン酸二無水物、4,8-ジメチル-1,2,3,5,6,7-ヘキサヒドロナフタレン-1,2,5,6-テトラカルボン酸二無水物、2,6-又は2,7-ジクロロナフタレン-1,4,5,8-テトラカルボン酸二無水物、2,3,6,7-(又は1,4,5,8-)テトラクロロナフタレン-1,4,5,8-(又は2,3,6,7-)テトラカルボン酸二無水物、2,3,8,9-、3,4,9,10-、4,5,10,11-又は5,6,11,12-ペリレン-テトラカルボン酸二無水物、シクロペンタン-1,2,3,4-テトラカルボン酸二無水物、ピラジン-2,3,5,6-テトラカルボン酸二無水物、ピロリジン-2,3,4,5-テトラカルボン酸二無水物、チオフェン-2,3,4,5-テトラカルボン酸二無水物、4,4’-ビス(2,3-ジカルボキシフェノキシ)ジフェニルメタン二無水物、2,2‐ビス〔4-(3,4‐ジカルボキシフェノキシ)フェニル〕プロパン二無水物、4,4’- (ヘキサフルオロイソプロピリデン)ジフタル酸無水物、p-フェニレンビス(トリメリット酸モノエステル酸無水物)、エチレングリコール ビスアンヒドロトリメリテート等の酸二無水物が挙げられる。この中でも特に2,2',3,3'-、2,3,3',4'-又は3,3',4,4'-ベンゾフェノンテトラカルボン酸二無水物を使用する場合は、分子骨格に存在するケトン基と、後述する成分(b)又は(c)のアミノ基が反応してC=N結合を形成する場合があり、本発明の効果を発現しやすい。
本発明方法で使用するダイマージアミン組成物は、下記成分(a)を含有するとともに、成分(b)及び(c)の量が制御されているものである。
(a)成分のダイマージアミンとは、ダイマー酸の二つの末端カルボン酸基(-COOH)が、1級のアミノメチル基(-CH2-NH2)又はアミノ基(-NH2)に置換されてなるジアミンを意味する。ダイマー酸は、不飽和脂肪酸の分子間重合反応によって得られる既知の二塩基酸であり、その工業的製造プロセスは業界でほぼ標準化されており、炭素数が11~22の不飽和脂肪酸を粘土触媒等にて二量化して得られる。工業的に得られるダイマー酸は、オレイン酸やリノール酸、リノレン酸などの炭素数18の不飽和脂肪酸を二量化することによって得られる炭素数36の二塩基酸が主成分であるが、精製の度合いに応じ、任意量のモノマー酸(炭素数18)、トリマー酸(炭素数54)、炭素数20~54の他の重合脂肪酸を含有する。また、ダイマー化反応後には二重結合が残存するが、本発明では、更に水素添加反応して不飽和度を低下させたものもダイマー酸に含めるものとする。
炭素数10~40の範囲内にある一塩基酸化合物は、ダイマー酸の原料に由来する炭素数10~20の範囲内にある一塩基性不飽和脂肪酸、及びダイマー酸の製造時の副生成物である炭素数21~40の範囲内にある一塩基酸化合物の混合物である。モノアミン化合物は、これらの一塩基酸化合物の末端カルボン酸基を1級アミノメチル基又はアミノ基に置換して得られるものである。
炭素数41~80の範囲内にある炭化水素基を有する多塩基酸化合物は、ダイマー酸の製造時の副生成物である炭素数41~80の範囲内にある三塩基酸化合物を主成分とする多塩基酸化合物である。また、炭素数41~80のダイマー酸以外の重合脂肪酸を含んでもよい。アミン化合物は、これらの多塩基酸化合物の末端カルボン酸基を1級アミノメチル基又はアミノ基に置換して得られるものである。
約2gのダイマージアミン組成物を200~250mLの三角フラスコに秤量し、指示薬としてフェノールフタレインを用い、溶液が薄いピンク色を呈するまで、0.1mol/Lのエタノール性水酸化カリウム溶液を滴下し、中和を行ったブタノール約100mLに溶解させる。そこに3~7滴のフェノールフタレイン溶液を加え、サンプルの溶液が薄いピンク色に変わるまで、0.1mol/Lのエタノール性水酸化カリウム溶液で攪拌しながら滴定する。そこへブロモフェノールブルー溶液を5滴加え、サンプル溶液が黄色に変わるまで、0.2mol/Lの塩酸/イソプロパノール溶液で攪拌しながら滴定する。
アミン価は、次の式(1)により算出する。
アミン価={(V2×C2)-(V1×C1)}×MKOH/m ・・・(1)
ここで、アミン価はmg-KOH/gで表される値であり、MKOHは水酸化カリウムの分子量56.1である。また、V、Cはそれぞれ滴定に用いた溶液の体積と濃度であり、添え字の1、2はそれぞれ0.1Mエタノール性水酸化カリウム溶液、0.2mol/Lの塩酸/イソプロパノール溶液を表す。さらに、mはグラムで表されるサンプル重量である。
重量平均分子量は、ゲル浸透クロマトグラフ(東ソー株式会社製、HLC-8220GPCを使用)により測定した。標準物質としてポリスチレンを用い、展開溶媒にテトラヒドロフランを用いた。
GPCは、20mgのダイマージアミン組成物を200μLの無水酢酸、200μLのピリジン及び2mLのTHFで前処理した100mgの溶液を、10mLのTHF(1000ppmのシクロヘキサノンを含有)で希釈し、サンプルを調製した。調製したサンプルを東ソー株式会社製、商品名;HLC-8220GPCを用いて、カラム:TSK-gel G2000HXL,G1000HXL,G1000HXL、 フロー量:1mL/min、カラム(オーブン)温度:40℃、注入量:50μLの条件で測定した。なお、シクロヘキサノンは流出時間の補正のために標準物質として扱った。
(a)メインピークで表される成分;
(b)メインピークにおけるリテンションタイムが遅い時間側の極小値を基準にし、それよりも遅い時間に検出されるGPCピークで表される成分;
(c)メインピークにおけるリテンションタイムが早い時間側の極小値を基準にし、それよりも早い時間に検出されるGPCピークで表される成分;
を検出した。
BTDA:3,3’,4,4’-ベンゾフェノンテトラカルボン酸二無水物
DDA1:クローダジャパン株式会社製、商品名;PRIAMINE1075を蒸留精製したもの(a成分;97重量%、b成分:0.4%、c成分;2.1%、アミン価:206mg KOH/g)
DDA2:クローダジャパン株式会社製、商品名;PRIAMINE1074を蒸留精製したもの(a成分;96重量%、b成分:0%、c成分;3.6%、アミン価:210mg KOH/g)
DDA3:クローダジャパン株式会社製、商品名;PRIAMINE1074を蒸留精製したもの(a成分;96重量%、b成分:0%、c成分;3.9%、アミン価:210mg KOH/g)
DDA4:クローダジャパン株式会社製、商品名;PRIAMINE1074を蒸留精製したもの(a成分;96重量%、b成分:0%、c成分;3.7%、アミン価:208mg KOH/g)
DDA5:クローダジャパン株式会社製、商品名;PRIAMINE1075を蒸留精製したもの(a成分;97重量%、b成分:2.8%、c成分;1.0%、アミン価:210mg KOH/g)
NMP:N-メチル-2-ピロリドン
APB:1,3-ビス(3‐アミノフェノキシ)ベンゼン
BAPP:2,2-ビス[4-(4-アミノフェノキシ)フェニル]プロパン
1,3-BAC:1,3-ビス(アミノメチル)シクロヘキサン
BisDA:4,4‘-[プロパン―2,2-ジイルビス(1,4-フェニレンオキシ)]ジフタル酸二無水物(SABICイノベーティブプラスチックスジャパン合同会社製、商品名;BisDA-1000)
なお、上記DDA1~DDA5の分子量は下記式(1)により算出した。
分子量=56.1×2×1000/アミン価・・・(1)
1000mlのセパラブルフラスコに、55.55gのBTDA(0.17203モル)、94.45gのDDA1(0.17342モル)、210gのNMP及び140gのキシレンを装入し、40℃で1時間良く混合して、ポリアミド酸溶液を調製した。このポリアミド酸溶液を190℃に昇温し、4時間加熱、攪拌し、140gのキシレンを加えてイミド化を完結したポリイミド溶液1(固形分;30重量%、重量平均分子量;84,800)を調製した。
表1に示す原料組成とした他は、実施例1と同様にしてポリイミド溶液2~19を調製した。
Claims (5)
- テトラカルボン酸無水物成分と、ダイマー酸の二つの末端カルボン酸基が1級アミノメチル基又はアミノ基に置換されてなるダイマージアミンを主成分とするダイマージアミン組成物を含有するジアミン成分と、を反応させるポリイミドの製造方法であって、
前記ダイマージアミン組成物は、下記成分(a)~(c);
(a)ダイマージアミン;
(b)炭素数10~40の範囲内にある一塩基酸化合物の末端カルボン酸基を1級アミノメチル基又はアミノ基に置換して得られるモノアミン化合物;
(c)炭素数41~80の範囲内にある炭化水素基を有する多塩基酸化合物の末端カルボン酸基を1級アミノメチル基又はアミノ基に置換して得られるアミン化合物(但し、前記ダイマージアミンを除く);
について、
前記(a)成分の含有量が、前記ダイマージアミン組成物に対し、96重量%以上であり、
前記成分(b)及び(c)について、前記ダイマージアミン組成物のゲル浸透クロマトグラフィーを用いた測定におけるクロマトグラムの面積パーセントの比率(b/c)が1以上である場合、前記テトラカルボン酸無水物成分及び前記ジアミン成分のモル比(テトラカルボン酸無水物成分/ジアミン成分)を0.980以上0.992以下とすることによって、ポリイミドの重量平均分子量を67,820以上108,880以下の範囲内とし、
このとき、前記クロマトグラムの面積パーセントで、前記成分(b)及び(c)の合計が3.8%以下であり、
前記比率(b/c)が1未満である場合、前記テトラカルボン酸無水物成分及び前記ジアミン成分のモル比(テトラカルボン酸無水物成分/ジアミン成分)を0.992以上1.020以下とすることによって、ポリイミドの重量平均分子量を40,520以上84,800以下の範囲内とし、
このとき、前記クロマトグラムの面積パーセントで、前記成分(b)及び(c)の合計が2.5%以下であることを特徴とするポリイミドの製造方法。 - 前記(c)成分のクロマトグラムの面積パーセントが3%以下であることを特徴とする請求項1に記載のポリイミドの製造方法。
- 前記(c)成分のクロマトグラムの面積パーセントが2%以下であることを特徴とする請求項1に記載のポリイミドの製造方法。
- 前記ダイマージアミン組成物の原料を精製して前記ダイマージアミン組成物を得る工程を含む請求項1~3のいずれか1項に記載のポリイミドの製造方法。
- 前記ポリイミドの重量平均分子量が40,000~150,000の範囲内にあることを特徴とする請求項1~4のいずれか1項に記載のポリイミドの製造方法。