JP2022065196A - Outer package material for power storage device, and method for manufacturing outer package material for power storage device - Google Patents
Outer package material for power storage device, and method for manufacturing outer package material for power storage device Download PDFInfo
- Publication number
- JP2022065196A JP2022065196A JP2022029067A JP2022029067A JP2022065196A JP 2022065196 A JP2022065196 A JP 2022065196A JP 2022029067 A JP2022029067 A JP 2022029067A JP 2022029067 A JP2022029067 A JP 2022029067A JP 2022065196 A JP2022065196 A JP 2022065196A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- power storage
- base material
- storage device
- exterior material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、蓄電装置用外装材及び蓄電装置用外装材の製造方法に関する。 The present invention relates to an exterior material for a power storage device and a method for manufacturing an exterior material for a power storage device.
蓄電装置としては、例えば、リチウムイオン電池、ニッケル水素電池、及び鉛蓄電池等の二次電池、並びに電気二重層キャパシタ等の電気化学キャパシタが知られている。携帯機器の小型化又は設置スペースの制限等により蓄電装置のさらなる小型化が求められており、エネルギー密度が高いリチウムイオン電池が注目されている。リチウムイオン電池に用いられる外装材としては、従来は金属製の缶が用いられていたが、軽量で、放熱性が高く、低コストで作製できる多層フィルムが用いられるようになっている。 As the power storage device, for example, a secondary battery such as a lithium ion battery, a nickel hydrogen battery, and a lead storage battery, and an electric chemical capacitor such as an electric double layer capacitor are known. Due to the miniaturization of mobile devices or the limitation of installation space, further miniaturization of power storage devices is required, and lithium ion batteries having high energy density are attracting attention. Conventionally, metal cans have been used as exterior materials for lithium-ion batteries, but multilayer films that are lightweight, have high heat dissipation, and can be manufactured at low cost are now being used.
上記多層フィルムを外装材に用いるリチウムイオン電池では、内部への水分の浸入を防止するため、アルミニウム箔層を含む外装材により電池内容物(正極、セパレータ、負極、電解液等)を覆う構成が採用されている。このような構成を採用したリチウムイオン電池は、アルミラミネートタイプのリチウムイオン電池と呼ばれている。 In a lithium ion battery using the above-mentioned multilayer film as an exterior material, in order to prevent moisture from entering the inside, the battery contents (positive electrode, separator, negative electrode, electrolytic solution, etc.) are covered with an exterior material including an aluminum foil layer. It has been adopted. A lithium-ion battery adopting such a configuration is called an aluminum-laminated type lithium-ion battery.
アルミラミネートタイプのリチウムイオン電池は、例えば、外装材の一部に冷間成型によって凹部を形成し、該凹部内に電池内容物を収容し、外装材の残りの部分を折り返して縁部分をヒートシールで封止したエンボスタイプのリチウムイオン電池が知られている。(例えば、特許文献1参照)。このようなリチウムイオン電池では、冷間成型によって形成される凹部を深くするほど、より多くの電池内容物を収容できるため、エネルギー密度をより高くすることができる。 In an aluminum-laminated lithium-ion battery, for example, a recess is formed in a part of the exterior material by cold molding, the battery contents are housed in the recess, and the rest of the exterior material is folded back to heat the edge portion. An embossed type lithium-ion battery sealed with a seal is known. (See, for example, Patent Document 1). In such a lithium-ion battery, the deeper the recess formed by cold molding, the more battery contents can be accommodated, so that the energy density can be further increased.
しかしながら、特許文献1に記載された材料及び製造方法では、金属箔層とシーラント層との張り合わせや、張り合わせ後の巻取が適切に行えない等、加工適性が十分とは言えない場合がある。また、得られた外装材に対し深い凹部を形成しようとすると、外装材に破断が生じる場合がある。
However, the materials and manufacturing methods described in
本発明は上記事情に鑑みてなされたものであり、作製時の加工適性と作製後の深絞り成型性とに優れる蓄電装置用外装材、及び蓄電装置用外装材の製造方法を提供することを目的とする。 The present invention has been made in view of the above circumstances, and provides an exterior material for a power storage device and a method for manufacturing an exterior material for a power storage device, which are excellent in processing suitability at the time of production and deep drawing moldability after production. The purpose.
本発明は、少なくとも基材層、接着層、金属箔層、シーラント接着層及びシーラント層がこの順で積層された構造を有し、基材層は、160~200℃での熱処理後の、50%伸長時応力値が100~180MPaであり且つ熱収縮率が1~15%であるポリエステルフィルムからなる、蓄電装置用外装材を提供する。
50%伸長時応力値:基材層の4方向(0°(MD)、45°、90°(TD)、135°)に対し引張試験(試験片形状:JIS K7127に規定される5号型ダンベル状、チャック間距離:75mm、標点間距離:25mm、試験速度:50mm/min、温度:23℃)を行ったときの応力値の平均値である。
熱収縮率:基材層の4方向(0°(MD)、45°、90°(TD)、135°)に対する、熱処理前後での収縮率の平均値である。
The present invention has a structure in which at least a base material layer, an adhesive layer, a metal foil layer, a sealant adhesive layer and a sealant layer are laminated in this order, and the base material layer is 50 after heat treatment at 160 to 200 ° C. Provided is an exterior material for a power storage device, which is made of a polyester film having a% elongation stress value of 100 to 180 MPa and a heat shrinkage rate of 1 to 15%.
Stress value at 50% elongation: Tensile test (test piece shape: No. 5 type specified in JIS K7127) for 4 directions (0 ° (MD), 45 °, 90 ° (TD), 135 °) of the base material layer. It is an average value of stress values when dumbbell-shaped, distance between chucks: 75 mm, distance between gauge points: 25 mm, test speed: 50 mm / min, temperature: 23 ° C.).
Heat shrinkage rate: The average value of the shrinkage rate before and after the heat treatment in four directions (0 ° (MD), 45 °, 90 ° (TD), 135 °) of the base material layer.
蓄電装置用外装材の製造工程においては、複数の層を積層させるためにラミネート工程を必要とするものがある。このとき、一般的にはラミネート時にかかる熱、もしくは、接着剤乾燥時にかかる熱により基材層が熱劣化を起こし、絞り成型を行ったときに破れが生じる場合がある。一方、ラミネート時にかかる熱、もしくは、接着剤乾燥時にかかる熱による熱劣化をほぼ起こさないほど剛直な基材層の場合も、絞り成型を行ったときに破れが生じるおそれがある。また、仮に絞り成型性に優れていたとしても、金属箔層とシーラント層との張り合わせや、張り合わせ後の巻取が適切に行えない等、加工適性が十分とは言えない場合がある。本発明はこれらの問題点を解決するものである。 In the manufacturing process of the exterior material for a power storage device, there are some that require a laminating step in order to laminate a plurality of layers. At this time, in general, the heat applied during laminating or the heat applied during drying of the adhesive causes thermal deterioration of the base material layer, which may cause tearing when drawing and molding is performed. On the other hand, even in the case of a base material layer that is so rigid that heat deterioration due to heat applied during laminating or heat applied during adhesive drying may not occur, tearing may occur when drawing and molding is performed. Further, even if the drawing formability is excellent, it may not be possible to say that the processing suitability is sufficient because the metal foil layer and the sealant layer cannot be bonded properly and the winding after the bonding cannot be performed properly. The present invention solves these problems.
上記蓄電装置用外装材において、ポリエステルフィルムは、160℃での熱処理後の熱収縮率が1~5%であることが好ましい。これにより、作製時の加工適性と作製後の深絞り成型性とをさらに向上し易くなる。 In the exterior material for a power storage device, the polyester film preferably has a heat shrinkage rate of 1 to 5% after heat treatment at 160 ° C. This makes it easier to further improve the processability at the time of production and the deep drawability after production.
上記蓄電装置用外装材は、上記基材層と上記接着層との間に設けられた易接着処理層を更に備えていることが好ましい。これにより、基材層と接着層との間の密着性をより向上させることができるとともに、深絞り成型性をより向上させることができる。 It is preferable that the exterior material for a power storage device further includes an easy-adhesion-treated layer provided between the base material layer and the adhesive layer. As a result, the adhesion between the base material layer and the adhesive layer can be further improved, and the deep drawing moldability can be further improved.
上記蓄電装置用外装材において、上記易接着処理層が、ポリエステル樹脂、アクリル樹脂、ポリウレタン樹脂、エポキシ樹脂及びアクリルグラフトポリエステル樹脂からなる群より選択される少なくとも1種の樹脂を含む層であることが好ましい。これにより、基材層と接着層との間の密着性をより向上させることができるとともに、深絞り成型性をより向上させることができる。 In the exterior material for a power storage device, the easy-adhesion-treated layer may be a layer containing at least one resin selected from the group consisting of polyester resin, acrylic resin, polyurethane resin, epoxy resin and acrylic graft polyester resin. preferable. As a result, the adhesion between the base material layer and the adhesive layer can be further improved, and the deep drawing moldability can be further improved.
上記蓄電装置用外装材は、上記金属箔層の両面に設けられた腐食防止処理層を更に備えていることが好ましい。これにより、基材層と金属箔層との間の密着性をより向上させることができる。 It is preferable that the exterior material for the power storage device further includes corrosion prevention treatment layers provided on both sides of the metal foil layer. Thereby, the adhesion between the base material layer and the metal foil layer can be further improved.
上記蓄電装置用外装材において、上記腐食防止処理層が、希土類元素酸化物、及び、リン酸又はリン酸塩を含むことが好ましい。これにより、基材層と金属箔層との間の密着性をより向上させることができる。 In the exterior material for a power storage device, it is preferable that the corrosion prevention treatment layer contains a rare earth element oxide and phosphoric acid or a phosphate. Thereby, the adhesion between the base material layer and the metal foil layer can be further improved.
上記蓄電装置用外装材は、基材層上に、さらにコーティング層が積層された構造を有することができる。これにより、アクリル系PSAテープとの密着性が向上する。 The exterior material for a power storage device can have a structure in which a coating layer is further laminated on a base material layer. This improves the adhesion with the acrylic PSA tape.
上記蓄電装置用外装材において、コーティング層が、アクリル樹脂及びポリエステル樹脂からなる群より選択される少なくとも1種の樹脂を含む層であることが好ましい。これにより、アクリル系PSAテープとの密着性がより向上する。 In the exterior material for a power storage device, it is preferable that the coating layer is a layer containing at least one resin selected from the group consisting of an acrylic resin and a polyester resin. As a result, the adhesion with the acrylic PSA tape is further improved.
上記蓄電装置用外装材において、コーティング層の厚さが、0.05~3μmであることが好ましい。これにより、コーティング層を設けたとしても、絞り成型性の低下を抑制し易くなる。 In the exterior material for a power storage device, the thickness of the coating layer is preferably 0.05 to 3 μm. As a result, even if the coating layer is provided, it becomes easy to suppress the deterioration of the drawability.
本発明はまた、金属箔層の一方の面に、接着層を介して基材層を貼り合わせる工程、及び金属箔層の接着層とは反対側の面に、シーラント接着層を介してシーラント層を形成する工程、を備え、基材層は、160~200℃での熱処理後の、50%伸長時応力値が100~180MPaであり且つ熱収縮率が1~15%であるポリエステルフィルムからなる、蓄電装置用外装材の製造方法を提供する。
50%伸長時応力値:基材層の4方向(0°(MD)、45°、90°(TD)、135°)に対し引張試験(試験片形状:JIS K7127に規定される5号型ダンベル状、チャック間距離:75mm、標点間距離:25mm、試験速度:50mm/min、温度:23℃)を行ったときの応力値の平均値である。
熱収縮率:基材層の4方向(0°(MD)、45°、90°(TD)、135°)に対する、熱処理前後での収縮率の平均値である。
The present invention also has a step of adhering a base material layer to one surface of the metal foil layer via an adhesive layer, and a sealant layer via a sealant adhesive layer on a surface of the metal foil layer opposite to the adhesive layer. The substrate layer comprises a polyester film having a 50% elongation stress value of 100 to 180 MPa and a heat shrinkage of 1 to 15% after heat treatment at 160 to 200 ° C. , Provide a method for manufacturing an exterior material for a power storage device.
Stress value at 50% elongation: Tensile test (test piece shape: No. 5 type specified in JIS K7127) for 4 directions (0 ° (MD), 45 °, 90 ° (TD), 135 °) of the base material layer. It is an average value of stress values when dumbbell-shaped, distance between chucks: 75 mm, distance between gauge points: 25 mm, test speed: 50 mm / min, temperature: 23 ° C.).
Heat shrinkage rate: The average value of the shrinkage rate before and after the heat treatment in four directions (0 ° (MD), 45 °, 90 ° (TD), 135 °) of the base material layer.
本発明によれば、作製時の加工適性と作製後の深絞り成型性とに優れる蓄電装置用外装材、及び蓄電装置用外装材の製造方法を提供することができる。 INDUSTRIAL APPLICABILITY According to the present invention, it is possible to provide an exterior material for a power storage device and a method for manufacturing an exterior material for a power storage device, which are excellent in processing suitability at the time of production and deep drawing moldability after production.
以下、図面を参照しながら本発明の好適な実施形態について詳細に説明する。なお、図面中、同一又は相当部分には同一符号を付し、重複する説明は省略する。 Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the drawings. In the drawings, the same or corresponding parts are designated by the same reference numerals, and duplicate description will be omitted.
[蓄電装置用外装材]
図1は、本発明の蓄電装置用外装材の一実施形態を模式的に表す断面図である。図1に示すように、本実施形態の外装材(蓄電装置用外装材)10は、基材層11と、該基材層11の一方の面側に設けられた易接着処理層12と、該易接着処理層12の基材層11とは反対側に設けられた接着層13と、該接着層13の易接着処理層12とは反対側に設けられた、両面に腐食防止処理層15a及び15bを有する金属箔層14と、該金属箔層14の接着層13とは反対側に設けられたシーラント接着層16と、該シーラント接着層16の金属箔層14とは反対側に設けられたシーラント層17と、が順次積層された積層体である。ここで、腐食防止処理層15aは金属箔層14の接着層13側の面に、腐食防止処理層15bは金属箔層14のシーラント接着層16側の面に、それぞれ設けられている。外装材10は、基材層11の易接着処理層12とは反対側に、さらにコーティング層18を有していてもよい。外装材10は、基材層11(あるいはコーティング層18)が最外層、シーラント層17が最内層である。すなわち、外装材10は、基材層11を蓄電装置の外部側、シーラント層17を蓄電装置の内部側に向けて使用される。以下、各層について説明する。
[Exterior material for power storage device]
FIG. 1 is a cross-sectional view schematically showing an embodiment of an exterior material for a power storage device of the present invention. As shown in FIG. 1, the exterior material (exterior material for a power storage device) 10 of the present embodiment includes a
(基材層11)
基材層11は、蓄電装置を製造する際における後述する加圧熱融着工程における耐熱性及び他の蓄電装置から漏れ出した電解液に対する耐電解液性を外装材10に付与し、加工又は流通の際に起こり得るピンホールの発生を抑制するための層である。
(Base material layer 11)
The
基材層11は、以下に示す、160~200℃での熱処理後の、50%伸長時応力値が100~180MPaであり且つ熱収縮率が1~15%であるポリエステルフィルムからなる。
50%伸長時応力値:基材層の4方向(0°(MD)、45°、90°(TD)、135°)に対し引張試験(試験片形状:JIS K7127に規定される5号型ダンベル状、チャック間距離:75mm、標点間距離:25mm、試験速度:50mm/min、温度:23℃)を行ったときの応力値の平均値である。
熱収縮率:基材層の4方向(0°(MD)、45°、90°(TD)、135°)に対する、熱処理前後での収縮率の平均値である。
The
Stress value at 50% elongation: Tensile test (test piece shape: No. 5 type specified in JIS K7127) for 4 directions (0 ° (MD), 45 °, 90 ° (TD), 135 °) of the base material layer. It is an average value of stress values when dumbbell-shaped, distance between chucks: 75 mm, distance between gauge points: 25 mm, test speed: 50 mm / min, temperature: 23 ° C.).
Heat shrinkage rate: The average value of the shrinkage rate before and after the heat treatment in four directions (0 ° (MD), 45 °, 90 ° (TD), 135 °) of the base material layer.
基材層11の50%伸長時応力値(F50応力値)は、具体的には次のようにして測定することができる。すなわち、A4サイズにカットした基材層を、160~200℃の範囲内の任意の熱処理温度に保たれたオーブン中で30分間加熱する。その後、当該基材層の4方向(0°(MD)、45°、90°(TD)、135°)に対し、23℃(室温)にて引張試験(試験片形状:JIS K7127に規定される5号型ダンベル状、チャック間距離:75mm、標点間距離:25mm、試験速度:50mm/min)を行う。そして、4方向に対する測定結果の平均を取ることで、50%伸長時応力値を算出する。
Specifically, the stress value at 50% elongation (F50 stress value) of the
なお、基材層の縦方向及び横方向は、それぞれ基材層原反のMD方向(機械送り方向)及びTD方向(MD方向の垂直方向)に一致させるものとする。つまり、基材層11が二軸延伸フィルムからなる場合には、試験片の縦方向及び横方向はそれぞれフィルムの2つの延伸方向のいずれか一方に一致している。
The vertical direction and the horizontal direction of the base material layer shall be matched with the MD direction (machine feed direction) and the TD direction (vertical direction of the MD direction) of the base material layer raw fabric, respectively. That is, when the
上記のとおり測定される基材層11の50%伸長時応力値が100~180MPaの範囲にあることにより、加工適性に優れると共に、熱処理後においても深絞り成型が可能となる。この観点から、基材層11の50%伸長時応力値は110~170MPaであることが好ましい。
When the stress value at 50% elongation of the
基材層11の熱収縮率は、具体的には次のようにして測定することができる。すなわち、23℃にてA4サイズにカットした基材層を、160~200℃の範囲内の任意の熱処理温度に保たれたオーブン中で30分間加熱する。その後、当該基材層の4方向(0°(MD)、45°、90°(TD)、135°)の、23℃における長さを測定する。そして、下記式に従い各方向に対する熱収縮率を算出して、その平均値をとることで、熱収縮率を算出する。
熱収縮率(%)=[{熱処理前に測定された各方向の長さ(A4サイズ)-熱処理後に測定された各方向の長さ}/熱処理前に測定された各方向の長さ]×100
Specifically, the heat shrinkage rate of the
Heat shrinkage rate (%) = [{Length measured in each direction before heat treatment (A4 size) -Length measured in each direction after heat treatment} / Length in each direction measured before heat treatment] × 100
上記のとおり測定される基材層11の熱収縮率が1~15%の範囲にあることにより、金属箔層とシーラント層との張り合わせや、張り合わせ後の巻取を適切に行えるようになるため加工適性に優れると共に、良好な成形性をも有する外装材とすることができる。この観点から、基材層11の熱収縮率は1~8%であることが好ましい。
Since the heat shrinkage of the
基材層11は、160℃での熱処理後の熱収縮率が1~5%であることが好ましい。これにより、加工適性により優れる外装材とすることができる。この観点から、当該熱収縮率は、1~4%であることが好ましい。
The
基材層11のポリエステルフィルムを構成するポリエステル樹脂としては、上記の特性を満たし得るものであれば特に制限なく用いることができるが、例えばポリエチレンテレフタレート、ポリブチレンテレフタレート、ポリエチレンナフタレート、ポリブチレンナフタレート、共重合ポリエステル等が挙げられる。これらの中でも、深絞り成型性に優れるという観点から、共重合ポリエステルを好適に用いることができる。
The polyester resin constituting the polyester film of the
ポリエステルフィルムとしては、同時延伸、二軸延伸いずれの製法にて得られたものでも使用することができるが、より優れた深絞り成型性が得られる観点から、二軸延伸ポリエステルフィルムであることが好ましい。 As the polyester film, any one obtained by either simultaneous stretching or biaxial stretching can be used, but from the viewpoint of obtaining better deep drawing moldability, the biaxially stretched polyester film may be used. preferable.
二軸延伸フィルムにおける延伸方法としては、例えば、逐次二軸延伸法、チューブラー二軸延伸法、同時二軸延伸法等が挙げられる。二軸延伸フィルムは、より優れた深絞り成型性が得られる観点から、チューブラー二軸延伸法及び同時二軸延伸法により延伸されたものであることが好ましい。 Examples of the stretching method in the biaxially stretched film include a sequential biaxial stretching method, a tubular biaxial stretching method, and a simultaneous biaxial stretching method. The biaxially stretched film is preferably stretched by a tubular biaxial stretching method and a simultaneous biaxial stretching method from the viewpoint of obtaining more excellent deep drawing formability.
基材層11の厚さは、6~40μmであることが好ましく、10~30μmであることがより好ましい。基材層11の厚さが6μm以上であることにより、蓄電装置用外装材10の耐ピンホール性及び絶縁性を向上できる傾向がある。基材層11の厚さが40μmを超えると蓄電装置用外装材10の総厚が大きくなり、電池の電気容量を小さくしなければならない場合があるため望ましくない。
The thickness of the
(易接着処理層12)
易接着処理層12は、基材層11の一方の面側に設けられ、基材層11と接着層13との間に配置されている。易接着処理層12は、基材層11と接着層13との間の密着性を向上させ、ひいては基材層11と金属箔層14との間の密着性を向上させるための層である。蓄電装置用外装材10において、易接着処理層12は設けられていなくてもよい。その場合、基材層11と接着層13との間の密着性を向上させ、ひいては基材層11と金属箔層14との間の密着性を向上させるために、基材層11の接着層13側の面をコロナ処理してもよい。
(Easy Adhesive Treatment Layer 12)
The easy-adhesion-treated
易接着処理層12は、ポリエステル樹脂、アクリル樹脂、ポリウレタン樹脂、エポキシ樹脂及びアクリルグラフトポリエステル樹脂からなる群より選択される少なくとも1種の樹脂を含む層であることが好ましい。かかる易接着処理層12は、例えば、基材層11の一方の面上に、ポリエステル樹脂、アクリル樹脂、ポリウレタン樹脂、エポキシ樹脂及びアクリルグラフトポリエステル樹脂からなる群より選択される少なくとも1種の樹脂を主成分とする塗工剤を塗布して形成することができる。
The easy-adhesion-treated
<ポリエステル樹脂>
ポリエステル樹脂としては、接着性の点から、共重合成分を導入しガラス転移温度を低下させた共重合ポリエステルが好ましい。共重合ポリエステルは、塗工性の点から水溶性もしくは水分散性を有することが好ましい。このような共重合ポリエステルとしては、スルホン酸基又はそのアルカリ金属塩基からなる群より選択される少なくとも1種の基が結合した共重合ポリエステル(以下、「スルホン酸基含有共重合ポリエステル」という)を用いることが好ましい。
<Polyester resin>
As the polyester resin, a copolymerized polyester in which a copolymerization component is introduced to lower the glass transition temperature is preferable from the viewpoint of adhesiveness. The copolymerized polyester is preferably water-soluble or water-dispersible from the viewpoint of coatability. As such a copolymerized polyester, a copolymerized polyester in which at least one group selected from the group consisting of a sulfonic acid group or an alkali metal base thereof is bonded (hereinafter, referred to as “sulfonic acid group-containing copolymerized polyester”) is used. It is preferable to use it.
ここでスルホン酸基含有共重合ポリエステルとは、ジカルボン酸成分又はグリコール成分の一部にスルホン酸基又はそのアルカリ金属塩基からなる群より選択される少なくとも1種の基が結合したポリエステルをいい、中でも、スルホン酸基又はそのアルカリ金属塩基からなる群より選択される少なくとも1種の基を含有した芳香族ジカルボン酸成分を全酸成分に対して2~10モル%の割合で用いて調製した共重合ポリエステルが好ましい。 Here, the sulfonic acid group-containing copolymerized polyester means a polyester in which at least one group selected from the group consisting of a sulfonic acid group or an alkali metal base thereof is bonded to a part of a dicarboxylic acid component or a glycol component. , A copolymerization prepared by using an aromatic dicarboxylic acid component containing at least one group selected from the group consisting of a sulfonic acid group or an alkali metal base thereof at a ratio of 2 to 10 mol% with respect to the total acid component. Polyester is preferred.
このようなジカルボン酸の例としては、5-ナトリウムスルホイソフタル酸が好適である。この場合、他のジカルボン酸成分としては、テレフタル酸、イソフタル酸、フタル酸、p-β-オキシエトキシ安息香酸、2,6-ナフタレンジカルボン酸、4,4’-ジカルボキシジフェニル、4,4’-ジカルボキシベンゾフェノン、ビス(4-カルボキシフェニル)エタン、アジピン酸、セバシン酸、シクロヘキサン-1,4-ジカルボン酸等が挙げられる。 As an example of such a dicarboxylic acid, 5-sodium sulfoisophthalic acid is suitable. In this case, as other dicarboxylic acid components, terephthalic acid, isophthalic acid, phthalic acid, p-β-oxyethoxybenzoic acid, 2,6-naphthalenedicarboxylic acid, 4,4'-dicarboxydiphenyl, 4,4' -Dicarboxybenzophenone, bis (4-carboxyphenyl) ethane, adipic acid, sebacic acid, cyclohexane-1,4-dicarboxylic acid and the like can be mentioned.
スルホン酸基含有共重合ポリエステルを製造するためのグリコール成分としては、エチレングリコールが主として用いられ、この他に、プロピレングリコール、ブタンジオール、ネオペンチルグリコール、ジエチレングリコール、シクロヘキサンジメタノール、ビスフェノールAのエチレンオキサイド付加物、ポリエチレングリコール、ポリプロピレングリコール、ポリテトラメチレングリコール等を用いることができる。中でも、エチレングリコール、プロピレングリコール、ブタンジオール、ネオペンチルグリコール、ジエチレングリコール、シクロヘキサンジメタノール等を共重合成分として用いると、ポリスチレンスルホン酸塩との相溶性が向上するという点で好ましい。 Ethylene glycol is mainly used as a glycol component for producing a sulfonic acid group-containing copolymerized polyester, and in addition to this, ethylene oxide addition of propylene glycol, butanediol, neopentyl glycol, diethylene glycol, cyclohexanedimethanol, and bisphenol A is used. Articles, polyethylene glycol, polypropylene glycol, polytetramethylene glycol and the like can be used. Above all, it is preferable to use ethylene glycol, propylene glycol, butanediol, neopentyl glycol, diethylene glycol, cyclohexanedimethanol or the like as a copolymerization component in that compatibility with polystyrene sulfonate is improved.
また、ポリエステル樹脂としては、変性ポリエステル共重合体、例えば、ポリエステル、ウレタン、エポキシなどで変性したブロック共重合体、グラフト共重合体などを使用してもよい。本実施形態では、易接着処理層12と基材層11及び接着層13との間の密着性を向上させるために、易接着処理層12にポリエステル樹脂以外の樹脂を更に含有させてもよい。このような樹脂としては、例えば、ウレタン樹脂、アクリル樹脂などが挙げられる。
Further, as the polyester resin, a modified polyester copolymer, for example, a block copolymer modified with polyester, urethane, epoxy or the like, a graft copolymer or the like may be used. In the present embodiment, in order to improve the adhesion between the easy-adhesion-treated
<アクリル樹脂>
アクリル樹脂を構成するモノマー成分としては、例えば、アルキルアクリレート、アルキルメタクリレート(アルキル基としてはメチル基、エチル基、n-プロピル基、イソプロピル基、n-ブチル基、イソブチル基、t-ブチル基、2-エチルヘキシル基、ラウリル基、ステアリル基、シクロヘキシル基、フェニル基、ベンジル基、フェニルエチル基などが挙げられる);2-ヒドロキシエチルアクリレート、2-ヒドロキシエチルメタクリレート、2-ヒドロキシプロピルアクリレート、2-ヒドロキシプロピルメタクリレートなどのヒドロキシ基含有モノマー;アクリルアミド、メタクリルアミド、N-メチルアクリルアミド、N-メチルメタクリルアミド、N-メチロールアクリルアミド、N-メチロールメタクリルアミド、N,N-ジメチロールアクリルアミド、N-メトキシメチルアクリルアミド、N-メトキシメチルメタクリルアミド、N-フェニルアクリルアミドなどのアミド基含有モノマー;N,N-ジエチルアミノエチルアクリレート、N,N-ジエチルアミノエチルメタクリレートなどのアミノ基含有モノマー;グリシジルアクリレート、グリシジルメタクリレートなどのエポキシ基含有モノマー;アクリル酸、メタクリル酸およびそれらの塩(リチウム塩、ナトリウム塩、カリウム塩など)などのカルボキシル基、またはその塩を含有するモノマーなどを用いることができる。これらは1種を単独で用いてもよく、2種以上を用いて共重合させてもよい。更に、これらは上記以外の他のモノマーと併用することができる。
<Acrylic resin>
Examples of the monomer components constituting the acrylic resin include alkyl acrylates and alkyl methacrylates (alkyl groups include methyl group, ethyl group, n-propyl group, isopropyl group, n-butyl group, isobutyl group, t-butyl group, 2). -Ethylhexyl group, lauryl group, stearyl group, cyclohexyl group, phenyl group, benzyl group, phenylethyl group, etc.); 2-hydroxyethyl acrylate, 2-hydroxyethyl methacrylate, 2-hydroxypropyl acrylate, 2-hydroxypropyl Hydroxy group-containing monomers such as methacrylate; acrylamide, methacrylamide, N-methylacrylamide, N-methylmethacrylate, N-methylolacrylamide, N-methylolmethacrylate, N, N-dimethylolacrylamide, N-methoxymethylacrylamide, N -Amid group-containing monomers such as methoxymethylmethacrylate and N-phenylacrylamide; amino group-containing monomers such as N, N-diethylaminoethyl acrylate and N, N-diethylaminoethyl methacrylate; epoxy group-containing monomers such as glycidyl acrylate and glycidyl methacrylate. A carboxyl group such as acrylic acid, methacrylic acid and salts thereof (lithium salt, sodium salt, potassium salt, etc.), or a monomer containing the salt can be used. One of these may be used alone, or two or more thereof may be used for copolymerization. Furthermore, these can be used in combination with other monomers other than the above.
他のモノマーとしては、例えば、アリルグリシジルエーテルなどのエポキシ基含有モノマー;スチレンスルホン酸、ビニルスルホン酸およびそれらの塩(リチウム塩、ナトリウム塩、カリウム塩、アンモニウム塩など)などのスルホン酸基またはその塩を含有するモノマー;クロトン酸、イタコン酸、マレイン酸、フマル酸、およびそれらの塩(リチウム塩、ナトリウム塩、カリウム塩、アンモニウム塩など)などのカルボキシル基またはその塩を含有するモノマー;無水マレイン酸、無水イタコン酸などの酸無水物を含有するモノマー;ビニルイソシアネート、アリルイソシアネート、スチレン、ビニルメチルエーテル、ビニルエチルエーテル、ビニルトリスアルコキシシラン、アルキルマレイン酸モノエステル、アルキルフマル酸モノエステル、アクリロニトリル、メタクリロニトリル、アルキルイタコン酸モノエステル、塩化ビニリデン、酢酸ビニル、塩化ビニルなどを用いることができる。また、アクリル樹脂としては、変性アクリル共重合体、例えば、ポリエステル、ウレタン、エポキシなどで変性したブロック共重合体、グラフト共重合体などを使用してもよい。 Other monomers include, for example, epoxy group-containing monomers such as allylglycidyl ether; sulfonic acid groups such as styrene sulfonic acid, vinyl sulfonic acid and salts thereof (lithium salt, sodium salt, potassium salt, ammonium salt, etc.) or sulfonic acid groups thereof. Monomer containing salts; Sulfonic acid, itaconic acid, maleic acid, fumaric acid, and monomers containing carboxyl groups such as salts thereof (lithium salt, sodium salt, potassium salt, ammonium salt, etc.) or salts thereof; Malein anhydride. Monomer containing acid anhydrides such as acid, itaconic acid anhydride; vinyl isocyanate, allyl isocyanate, styrene, vinylmethyl ether, vinyl ethyl ether, vinyltris alkoxysilane, alkylmaleic acid monoester, alkyl fumolic acid monoester, acrylonitrile, Methacylonitrile, alkylitaconic acid monoester, vinylidene chloride, vinyl acetate, vinyl chloride and the like can be used. Further, as the acrylic resin, a modified acrylic copolymer, for example, a block copolymer modified with polyester, urethane, epoxy, or the like, a graft copolymer, or the like may be used.
本実施形態において用いられるアクリル樹脂のガラス転移点(Tg)は特に限定されるものではないが、好ましくは0~90℃であり、より好ましくは10~80℃である。Tgが低いと高温高湿下での密着性が低下したり、高いと延伸時にクラックが発生したりすることがあるため、それらを抑制する観点から、アクリル樹脂のTgは上記範囲内であることが好ましい。 The glass transition point (Tg) of the acrylic resin used in the present embodiment is not particularly limited, but is preferably 0 to 90 ° C, more preferably 10 to 80 ° C. If the Tg is low, the adhesion under high temperature and high humidity may decrease, and if the Tg is high, cracks may occur during stretching. Therefore, from the viewpoint of suppressing these, the Tg of the acrylic resin should be within the above range. Is preferable.
また、本実施形態において用いられるアクリル樹脂の重量平均分子量は10万以上であることが好ましく、30万以上であることがより好ましい。重量平均分子量が低いと耐湿熱性が低下する場合がある。本実施形態では、易接着処理層12と基材層11及び接着層13との間の密着性を向上させるために、易接着処理層12にアクリル樹脂以外の樹脂を更に含有させてもよい。このような樹脂としては、例えば、ポリエステル樹脂、ウレタン樹脂などが挙げられる。
Further, the weight average molecular weight of the acrylic resin used in the present embodiment is preferably 100,000 or more, more preferably 300,000 or more. If the weight average molecular weight is low, the moist heat resistance may decrease. In the present embodiment, in order to improve the adhesion between the easy-adhesion-treated
<ポリウレタン樹脂>
ポリウレタン樹脂としては、水系ポリウレタン樹脂が好ましい。水系ポリウレタン樹脂としては、粒子径が小さく、安定性が良好な点から、自己乳化型が好ましい。水系ポリウレタン樹脂の粒子径は、10~100nm程度にするとよい。本実施形態に用いる水系ポリウレタン樹脂は、そのガラス転移点(Tg)が40℃~150℃であることが望ましい。Tgが40℃以上であると塗工後ロール状に巻き取る際にブロッキングが発生することを十分に抑制できる傾向がある。一方、塗工後の乾燥温度よりTgが高すぎると均一な膜を形成し難いため、Tgは150℃以下であることが好ましい。
<Polyurethane resin>
As the polyurethane resin, a water-based polyurethane resin is preferable. As the water-based polyurethane resin, a self-emulsifying type is preferable because of its small particle size and good stability. The particle size of the water-based polyurethane resin is preferably about 10 to 100 nm. The water-based polyurethane resin used in this embodiment preferably has a glass transition point (Tg) of 40 ° C to 150 ° C. When Tg is 40 ° C. or higher, it tends to be possible to sufficiently suppress the occurrence of blocking when winding into a roll after coating. On the other hand, if Tg is too high than the drying temperature after coating, it is difficult to form a uniform film, so Tg is preferably 150 ° C. or lower.
また、本実施形態では、水系ポリウレタン樹脂とともに架橋剤を用いてもよい。水系ポリウレタンの架橋剤としては、水溶性エポキシ化合物等、汎用の水溶性架橋剤が使用できる。水溶性エポキシ化合物は、水への溶解性があり、2個以上のエポキシ基を有する化合物である。水溶性エポキシ化合物としては、例えば、エチレングリコール、ジエチレングリコール、トリエチレングリコール、ポリエチレングリコール、プロピレングリコール、ジプロピレングリコール、トリプロピレングリコール、ポリプロピレングリコール、1,4-ブタンジオール、1,6-ヘキサンジオール、ネオペンチルグリコール等のグリコール類1モルと、エピクロルヒドリン2モルとのエーテル化によって得られるポリエポキシ化合物、及び、フタル酸、テレフタル酸、アジピン酸、シュウ酸等のジカルボン酸類1モルとエピクロルヒドリン2モルとのエステル化によって得られるジエポキシ化合物等が挙げられる。但し、水溶性エポキシ化合物はこれらに限定されるものではない。 Further, in the present embodiment, a cross-linking agent may be used together with the water-based polyurethane resin. As the cross-linking agent for the water-based polyurethane, a general-purpose water-soluble cross-linking agent such as a water-soluble epoxy compound can be used. A water-soluble epoxy compound is a compound that is soluble in water and has two or more epoxy groups. Examples of the water-soluble epoxy compound include ethylene glycol, diethylene glycol, triethylene glycol, polyethylene glycol, propylene glycol, dipropylene glycol, tripropylene glycol, polypropylene glycol, 1,4-butanediol, 1,6-hexanediol, and neo. A polyepoxy compound obtained by etherification of 1 mol of glycols such as pentylene glycol and 2 mol of epichlorohydrin, and an ester of 1 mol of dicarboxylic acids such as phthalic acid, terephthalic acid, adipic acid and oxalic acid and 2 mol of epichlorohydrin. Examples thereof include diepylene compounds obtained by chemical conversion. However, the water-soluble epoxy compound is not limited to these.
これら水溶性架橋剤は、水系ポリウレタン樹脂と架橋し、塗膜の耐水性、耐溶剤性を向上し、易接着処理層12と基材層11及び接着層13との間の密着性向上にも寄与する。本実施形態では、易接着処理層12と基材層11及び接着層13との間の密着性を向上させるためにウレタン樹脂以外の樹脂を更に含有させてもよい。このような樹脂としては、例えば、ポリエステル樹脂、アクリル樹脂などが挙げられる。
These water-soluble cross-linking agents crosslink with the water-based polyurethane resin to improve the water resistance and solvent resistance of the coating film, and also to improve the adhesion between the easy-adhesion-treated
また、易接着処理層12は、例えば、主成分である上記樹脂と、多官能イソシアネート、多官能グリシジル化合物、メラミン系化合物等の硬化剤と、を含むように構成してもよい。このように、主成分である上記樹脂と、多官能イソシアネート、多官能グリシジル化合物、メラミン系化合物等の硬化剤と、を含むことにより、架橋構造を取り入れることが可能となるので、強硬な易接着処理層12を構成することができる。
Further, the easy-adhesion-treated
易接着処理層12を形成するために使用する塗工剤は、溶剤系でもよいし、水系でもよい。水系の主剤を用いた分散タイプ(ディスパージョン)は、分子量が大きく、分子間凝集力が向上して、易接着処理層12と基材層11及び接着層13との間の密着性に有効である。
The coating agent used to form the easy-adhesion-treated
易接着処理層12の厚さは、0.02~0.5μmであることが好ましく、0.04~0.3μmであることがより好ましい。易接着処理層12の厚さが0.02μm以上であると、均一な易接着処理層12を形成し易く、より十分な易接着効果が得られる傾向がある。一方、易接着処理層12の厚さが0.5μm以下であることにより、外装材10の深絞り成型性をより向上できる傾向がある。
The thickness of the easy-adhesion-treated
(接着層13)
接着層13は、基材層11と金属箔層14とを接着する層である。接着層13は、基材層11とは易接着処理層12を介して接着する。接着層13は、基材層11と金属箔層14とを強固に接着するために必要な密着力を有すると共に、冷間成型する際において、基材層11によって金属箔層14が破断されることを抑制するための追随性(部材が変形・伸縮したとしても、剥離することなく部材上に接着層13を確実に形成するための性能)も有する。
(Adhesive layer 13)
The
接着層13を構成する接着剤としては、例えば、ポリエステルポリオール、ポリエーテルポリオール、アクリルポリオール等のポリオールよりなる主剤と、芳香族系、脂肪族系等のイソシアネートよりなる硬化剤と、を有する二液硬化型のポリウレタン系接着剤を用いることができる。上記接着剤において、主剤の水酸基に対する硬化剤のイソシアネート基のモル比(=NCO/OH)は、1~10が好ましく、2~5がより好ましい。
The adhesive constituting the
上記ポリウレタン系接着剤は、塗工後、例えば40℃で4日以上のエージングを行うことで、主剤の水酸基と硬化剤のイソシアネート基との反応が進行し、基材層11と金属箔層14とのより強固な接着が可能となる。
After coating, the polyurethane adhesive is aged at 40 ° C. for 4 days or more to promote the reaction between the hydroxyl group of the main agent and the isocyanate group of the curing agent, and the
接着層13の厚さは、所望の接着強度、追随性、及び加工性等を得る観点から、1~10μmが好ましく、2~6μmがより好ましい。
The thickness of the
(金属箔層14)
金属箔層14としては、アルミニウム及びステンレス鋼等の各種金属箔が挙げられ、防湿性及び延展性等の加工性、並びにコストの面から、金属箔層14はアルミニウム箔であることが好ましい。アルミニウム箔は一般の軟質アルミニウム箔であってもよいが、耐ピンホール性及び成形時の延展性に優れる点から、鉄を含むアルミニウム箔であることが好ましい。
(Metal leaf layer 14)
Examples of the
鉄を含むアルミニウム箔(100質量%)において、鉄の含有量は、0.1~9.0質量%であることが好ましく、0.5~2.0質量%であることがより好ましい。鉄の含有量が0.1質量%以上であることにより、より優れた耐ピンホール性及び延展性を有する外装材10を得ることができる。鉄の含有量が9.0質量%以下であることにより、より柔軟性に優れた外装材10を得ることができる。
In the aluminum foil containing iron (100% by mass), the iron content is preferably 0.1 to 9.0% by mass, more preferably 0.5 to 2.0% by mass. When the iron content is 0.1% by mass or more, the
また、アルミニウム箔としては、所望の成型時の延展性を付与できる点から、焼鈍処理を施した軟質アルミニウム箔(例えば、JIS規格でいう8021材、8079材よりなるアルミニウム箔)がさらに好ましい。 Further, as the aluminum foil, a soft aluminum foil that has been annealed (for example, an aluminum foil made of 8021 material or 8079 material according to JIS standards) is further preferable from the viewpoint of imparting a desired ductility during molding.
金属箔層14に使用する金属箔は、所望の耐電解液性を得るために、例えば、脱脂処理が施されていることが好ましい。また、製造工程を簡便にするためには、上記金属箔としては、表面がエッチングされていないものが好ましい。上記脱脂処理としては、例えば、ウェットタイプの脱脂処理またはドライタイプの脱脂処理を用いることができるが、製造工程を簡便にする観点から、ドライタイプの脱脂処理が好ましい。
The metal foil used for the
上記ドライタイプの脱脂処理としては、例えば、金属箔を焼鈍処理する工程において、処理時間を長くすることで脱脂処理を行う方法が挙げられる。金属箔を軟質化するために施される焼鈍処理の際に、同時に行われる脱脂処理程度でも充分な耐電解液性が得られる。 Examples of the dry type degreasing treatment include a method of performing a degreasing treatment by lengthening the treatment time in the step of annealing the metal foil. Sufficient electrolytic solution resistance can be obtained even with the degreasing treatment performed at the same time as the annealing treatment applied to soften the metal foil.
また、上記ドライタイプの脱脂処理としては、上記焼鈍処理以外の処理であるフレーム処理及びコロナ処理等の処理を用いてもよい。さらに、上記ドライタイプの脱脂処理としては、例えば、金属箔に特定波長の紫外線を照射した際に発生する活性酸素により、汚染物質を酸化分解及び除去する脱脂処理を用いてもよい。 Further, as the dry type degreasing treatment, treatments other than the annealing treatment such as frame treatment and corona treatment may be used. Further, as the dry type degreasing treatment, for example, a degreasing treatment for oxidatively decomposing and removing contaminants by active oxygen generated when a metal foil is irradiated with ultraviolet rays having a specific wavelength may be used.
上記ウェットタイプの脱脂処理としては、例えば、酸脱脂処理、アルカリ脱脂処理等の処理を用いることができる。上記酸脱脂処理に使用する酸としては、例えば、硫酸、硝酸、塩酸、フッ酸等の無機酸を用いることができる。これらの酸は、1種を単独で使用してもよいし、2種以上を併用してもよい。また、アルカリ脱脂処理に使用するアルカリとしては、例えば、エッチング効果が高い水酸化ナトリウムを用いることができる。また、弱アルカリ系の材料及び界面活性剤等が配合された材料を用いて、アルカリ脱脂処理を行ってもよい。上記説明したウェットタイプの脱脂処理は、例えば、浸漬法、スプレー法により行うことができる。 As the wet type degreasing treatment, for example, a treatment such as an acid degreasing treatment or an alkaline degreasing treatment can be used. As the acid used for the acid degreasing treatment, for example, an inorganic acid such as sulfuric acid, nitric acid, hydrochloric acid, or hydrofluoric acid can be used. These acids may be used alone or in combination of two or more. Further, as the alkali used for the alkaline degreasing treatment, for example, sodium hydroxide having a high etching effect can be used. Further, the alkaline degreasing treatment may be performed using a weak alkaline material and a material containing a surfactant or the like. The wet type degreasing treatment described above can be performed by, for example, a dipping method or a spraying method.
金属箔層14の厚さは、バリア性、耐ピンホール性及び加工性の点から、9~200μmであることが好ましく、15~150μmであることがより好ましく、15~100μmであることが更に好ましい。金属箔層14の厚さが9μm以上であることにより、成型加工により応力がかかっても破断しにくくなる。金属箔層14の厚さが200μm以下であることにより、外装材の質量増加を低減でき、蓄電装置の重量エネルギー密度低下を抑制することができる。
The thickness of the
(腐食防止処理層15a,15b)
腐食防止処理層15a,15bは、電解液、又は、電解液と水分の反応により発生するフッ酸による金属箔層14の腐食を抑制する役割を果たす。また、腐食防止処理層15aは、金属箔層14と接着層13との密着力を高める役割を果たす。また、腐食防止処理層15bは、金属箔層14とシーラント接着層16との密着力を高める役割を果たす。腐食防止処理層15a及び腐食防止処理層15bは、同一の構成の層であってもよく、異なる構成の層であってもよい。なお、図1では、腐食防止処理層が金属箔層14の両面に形成されている場合を示したが、腐食防止処理層は金属箔層14の少なくとも一方の面に形成されていてもよい。
(Corrosion prevention treatment layers 15a and 15b)
The corrosion prevention treatment layers 15a and 15b play a role of suppressing corrosion of the
腐食防止処理層15a,15bは、例えば、腐食防止処理層15a,15bの母材となる層に対して、脱脂処理、熱水変成処理、陽極酸化処理、化成処理、腐食防止能を有するコーティング剤を塗工するコーティングタイプの腐食防止処理あるいはこれらの処理を組み合わせた腐食防止処理を実施することで形成することができる。 The corrosion prevention treatment layers 15a and 15b are coating agents having, for example, degreasing treatment, hydrothermal transformation treatment, anodic oxidation treatment, chemical conversion treatment, and corrosion prevention ability on the layer serving as the base material of the corrosion prevention treatment layers 15a and 15b. It can be formed by performing a coating type corrosion prevention treatment or a corrosion prevention treatment combining these treatments.
上述した処理のうち脱脂処理、熱水変成処理、陽極酸化処理、特に熱水変性処理及び陽極酸化処理は、処理剤によって金属箔(アルミニウム箔)表面を溶解させ、耐腐食性に優れる金属化合物(アルミニウム化合物(ベーマイト、アルマイト))を形成させる処理である。このため、このような処理は、金属箔層14から腐食防止処理層15a,15bまで共連続構造を形成している構造を得るために、化成処理の定義に包含されるケースもある。
Of the above-mentioned treatments, the degreasing treatment, the hydrothermal transformation treatment, the anodizing treatment, particularly the hydrothermal modification treatment and the anodizing treatment dissolve the surface of the metal foil (aluminum foil) with a treatment agent and are excellent in corrosion resistance. It is a process for forming an aluminum compound (boehmite, alumite). Therefore, such a treatment may be included in the definition of chemical conversion treatment in order to obtain a structure forming a co-continuous structure from the
脱脂処理としては、酸脱脂、アルカリ脱脂が挙げられる。酸脱脂としては上述した硫酸、硝酸、塩酸、フッ酸などの無機酸を単独あるいはこれらを混合して得られた酸脱脂を用いる方法などが挙げられる。また酸脱脂として、一ナトリウム二フッ化アンモニウムなどのフッ素含有化合物を上記無機酸で溶解させた酸脱脂剤を用いることで、金属箔層14の脱脂効果だけでなく不動態である金属のフッ化物を形成させることが可能であり、耐フッ酸性という点で有効である。アルカリ脱脂としては、水酸化ナトリウムなどを用いる方法が挙げられる。
Examples of the degreasing treatment include acid degreasing and alkaline degreasing. Examples of the acid degreasing include a method using acid degreasing obtained by using the above-mentioned inorganic acids such as sulfuric acid, nitric acid, hydrochloric acid, and hydrofluoric acid alone or in combination thereof. Further, as the acid degreasing, by using an acid degreasing agent in which a fluorine-containing compound such as monosodium difluoride is dissolved with the above-mentioned inorganic acid, not only the degreasing effect of the
上記熱水変成処理としては、例えば、トリエタノールアミンを添加した沸騰水中に金属箔層14を浸漬処理することで得られるベーマイト処理を用いることができる。上記陽極酸化処理としては、例えば、アルマイト処理を用いることができる。また、上記化成処理としては、例えば、クロメート処理、ジルコニウム処理、チタニウム処理、バナジウム処理、モリブデン処理、リン酸カルシウム処理、水酸化ストロンチウム処理、セリウム処理、ルテニウム処理、或いはこれらを2種以上組み合わせた処理を用いることができる。これらの熱水変成処理、陽極酸化処理、化成処理は、上述した脱脂処理を事前に施すことが好ましい。
As the hot water transformation treatment, for example, a boehmite treatment obtained by immersing the
なお、上記化成処理としては、湿式法に限らず、例えば、これらの処理に使用する処理剤を樹脂成分と混合し、塗布する方法を用いてもよい。また、上記腐食防止処理としては、その効果を最大限にすると共に、廃液処理の観点から、塗布型クロメート処理が好ましい。 The chemical conversion treatment is not limited to the wet method, and for example, a method in which a treatment agent used for these treatments is mixed with a resin component and applied may be used. Further, as the corrosion prevention treatment, a coating type chromate treatment is preferable from the viewpoint of maximizing the effect and waste liquid treatment.
腐食防止性能を有するコーティング剤を塗工するコーティングタイプの腐食防止処理に用いられるコーティング剤としては、希土類元素酸化物ゾル、アニオン性ポリマー、カチオン性ポリマーからなる群から選ばれる少なくとも1種を含有するコーティング剤が挙げられる。特に、希土類元素酸化物ゾルを含有するコーティング剤を用いる方法が好ましい。 The coating agent used for the coating type corrosion prevention treatment for applying a coating agent having corrosion prevention performance contains at least one selected from the group consisting of rare earth element oxide sol, anionic polymer, and cationic polymer. Examples include coating agents. In particular, a method using a coating agent containing a rare earth element oxide sol is preferable.
希土類元素酸化物ゾルを含有するコーティング剤を用いる方法は、純粋なコーティングタイプの腐食防止処理であり、この方法を用いることで、一般的なコーティング方法でも金属箔層14に腐蝕防止効果を付与させることが可能である。また、希土類元素酸化物ゾルを用いて形成される層は、金属箔層14の腐蝕防止効果(インヒビター効果)を有し、かつ、環境側面的にも好適な材料である。
The method using a coating agent containing a rare earth element oxide sol is a pure coating type corrosion prevention treatment, and by using this method, the
希土類元素酸化物ゾルには、液体分散媒中に希土類元素酸化物の微粒子(例えば、平均粒径100nm以下の粒子)が分散されている。希土類元素酸化物としては、酸化セリウム、酸化イットリウム、酸化ネオジウム、酸化ランタン等が挙げられる。中でも、酸化セリウムが好ましい。これにより、金属箔層14との間の密着性をより向上させることができる。希土類元素酸化物ゾルの液体分散媒としては、例えば、水、アルコール系溶剤、炭化水素系溶剤、ケトン系溶剤、エステル系溶剤、エーテル系溶剤など各種溶媒を用いることができる。中でも、水が好ましい。腐食防止処理層15a,15bに含まれる希土類元素酸化物は1種を単独で又は2種以上を組み合わせて用いることができる。
In the rare earth element oxide sol, fine particles of the rare earth element oxide (for example, particles having an average particle size of 100 nm or less) are dispersed in a liquid dispersion medium. Examples of the rare earth element oxide include cerium oxide, yttrium oxide, neodymium oxide, lanthanum oxide and the like. Of these, cerium oxide is preferable. Thereby, the adhesion between the
希土類元素酸化物ゾルは、希土類元素酸化物粒子の分散を安定化させるために、分散安定化剤として、硝酸、塩酸、リン酸などの無機酸、酢酸、リンゴ酸、アスコルビン酸、乳酸などの有機酸、それらの塩等を含有することが好ましい。これらの分散安定化剤のうち、特にリン酸又はリン酸塩を用いることが好ましい。これにより、希土類元素酸化物粒子の分散安定化だけでなく、リチウムイオン電池用外装材の用途において、リン酸のキレート能力を利用した、金属箔層14との間の密着性向上、フッ酸の影響で溶出した金属物イオンを捕獲(不動態形成)することによる電解液耐性の付与、低温でもリン酸の脱水縮合起こし易いことによる希土類元素酸化物層の凝集力向上などの効果が期待できる。分散安定化剤として用いられるリン酸又はリン酸塩としては、例えば、オルトリン酸、ピロリン酸、メタリン酸、これらのアルカリ金属塩、アンモニウム塩などが挙げられる。中でも、トリメタリン酸、テトラメタリン酸、ヘキサメタリン酸、ウルトラメタリン酸などの縮合リン酸、あるいはこれらのアルカリ金属塩及びアンモニウム塩が、リチウムイオン電池用外装材としての機能発現に好ましい。特に、希土類元素酸化物ゾルを含むコーティング組成物を用いて、各種コーティング法により希土類酸化物を含む層を形成させる時の乾燥造膜性(乾燥能力、熱量)を考慮すると、低温での反応性に優れる剤が好ましく、低温での脱水縮合性に優れる点から、ナトリウム塩が好ましい。リン酸塩としては、水溶性の塩が好ましい。腐食防止処理層15a,15bに含まれるリン酸又はリン酸塩は、1種を単独で又は2種以上を組み合わせて用いることができる。
The rare earth element oxide sol is an inorganic acid such as nitric acid, hydrochloric acid and phosphoric acid, and an organic acid such as acetic acid, malic acid, ascorbic acid and lactic acid as a dispersion stabilizer in order to stabilize the dispersion of the rare earth element oxide particles. It is preferable to contain acids, salts thereof and the like. Of these dispersion stabilizers, it is particularly preferable to use phosphoric acid or phosphate. As a result, not only the dispersion stabilization of the rare earth element oxide particles but also the improvement of the adhesion with the
希土類元素酸化物ゾル中、リン酸あるいはその塩の配合量としては、希土類元素酸化物100質量部に対し、1質量部以上が好ましく、5質量部以上がより好ましい。1質量部以上であると、ゾルの安定化が良好であると共にリチウムイオン電池用外装材としての機能を満たすことが容易である。希土類元素酸化物100質量部に対するリン酸あるいはその塩の配合上限は、希土類元素酸化物ゾルの機能低下を伴わない範囲であればよく、希土類元素酸化物100質量部に対し、100質量部以下が好ましく、50質量部以下がより好ましく、20質量部以下がさらに好ましい。 The blending amount of phosphoric acid or a salt thereof in the rare earth element oxide sol is preferably 1 part by mass or more, more preferably 5 parts by mass or more, based on 100 parts by mass of the rare earth element oxide. When it is 1 part by mass or more, the sol is well stabilized and it is easy to satisfy the function as an exterior material for a lithium ion battery. The upper limit of the amount of phosphoric acid or a salt thereof for 100 parts by mass of the rare earth element oxide may be as long as it does not cause functional deterioration of the rare earth element oxide sol, and 100 parts by mass or less is 100 parts by mass with respect to 100 parts by mass of the rare earth element oxide. It is preferably 50 parts by mass or less, more preferably 20 parts by mass or less.
ただし、上述した希土類元素酸化物ゾルから形成される層は無機粒子の集合体であるため、乾燥キュアの工程を経ても、その層自身の凝集力は低い。そこで、この層の凝集力を補うために、アニオン性ポリマーで複合化させることが好適である。 However, since the layer formed from the above-mentioned rare earth element oxide sol is an aggregate of inorganic particles, the cohesive force of the layer itself is low even after the drying cure step. Therefore, in order to supplement the cohesive force of this layer, it is preferable to combine it with an anionic polymer.
アニオン性ポリマーとしては、カルボキシ基を有するポリマーが挙げられ、例えば、ポリ(メタ)アクリル酸(あるいはその塩)、あるいはポリ(メタ)アクリル酸を主成分として共重合した共重合体が挙げられる。該共重合体の共重合成分としては、アルキル(メタ)アクリレート系モノマー(アルキル基としては、メチル基、エチル基、n-プロピル基、i-プロピル基、n-ブチル基、i-ブチル基、t-ブチル基、2-エチルヘキシル基、シクロヘキシル基等。);(メタ)アクリルアミド、N-アルキル(メタ)アクリルアミド、N,N-ジアルキル(メタ)アクリルアミド(アルキル基としては、メチル基、エチル基、n-プ口ピル基、i-プロピル基、n-ブチル基、i-ブチル基、t-ブチル基、2-エチルヘキシル基、シクロヘキシル基等。)、N-アルコキシ(メタ)アクリルアミド、N,N-ジアルコキシ(メタ)アクリルアミド、(アルコキシ基としては、メトキシ基、エトキシ基、ブトキシ基、イソブトキシ基等。)、N-メチロール(メタ)アクリルアミド、N-フェニル(メタ)アクリルアミド等のアミド基含有モノマー;2-ヒドロキシエチル(メタ)アクリレート、2-ヒドロキシプロピル(メタ)アクリレート等の水酸基含有モノマー;グリシジル(メタ)アクリレート、アリルグリシジルエーテル等のグリシジル基含有モノマー;(メタ)アクリロキシプロピルトリメトキシシラン、(メタ)アクリロキシプロピルトリエ卜キシラン等のシラン含有モノマー;(メタ)アクリロキシプロピルイソシアネー卜等のイソシアネー卜基含有モノマー等が挙げられる。また、スチレン、α-メチルスチレン、ビニルメチルエーテル、ビニルエチルエーテル、マレイン酸、アルキルマレイン酸モノエステル、フマル酸、アルキルフマル酸モノエステル、イタコン酸、アルキルイタコン酸モノエステル、(メタ)アクリロニトリル、塩化ビニリデン、エチレン、プロピレン、塩化ビニル、酢酸ビニル、ブタジエン等が挙げられる。 Examples of the anionic polymer include polymers having a carboxy group, and examples thereof include poly (meth) acrylic acid (or a salt thereof) or a copolymer obtained by copolymerizing poly (meth) acrylic acid as a main component. As the copolymerization component of the copolymer, an alkyl (meth) acrylate-based monomer (as the alkyl group, a methyl group, an ethyl group, an n-propyl group, an i-propyl group, an n-butyl group, an i-butyl group, etc. t-Butyl group, 2-ethylhexyl group, cyclohexyl group, etc.); (meth) acrylamide, N-alkyl (meth) acrylamide, N, N-dialkyl (meth) acrylamide (alkyl groups include methyl group, ethyl group, etc.) n-Pulch pill group, i-propyl group, n-butyl group, i-butyl group, t-butyl group, 2-ethylhexyl group, cyclohexyl group, etc.), N-alkyl (meth) acrylamide, N, N- Dialkoxy (meth) acrylamide, amide group-containing monomers such as methoxy group, ethoxy group, butoxy group, isobutoxy group, etc., N-methylol (meth) acrylamide, N-phenyl (meth) acrylamide, etc.; Hydroxyl group-containing monomers such as 2-hydroxyethyl (meth) acrylate and 2-hydroxypropyl (meth) acrylate; glycidyl group-containing monomers such as glycidyl (meth) acrylate and allylglycidyl ether; (meth) acryloxypropyltrimethoxysilane, ( Examples thereof include silane-containing monomers such as acryloxypropyltrier xylan; and isociane group-containing monomers such as (meth) acryloxylpropylisocianate. In addition, styrene, α-methylstyrene, vinylmethyl ether, vinylethyl ether, maleic acid, alkylmaleic acid monoester, fumaric acid, alkylfumaric acid monoester, itaconic acid, alkylitaconic acid monoester, (meth) acrylonitrile, chloride. Examples thereof include vinylidene, ethylene, propylene, vinyl chloride, vinyl acetate, butadiene and the like.
アニオン性ポリマーは、希土類元素酸化物ゾルを用いて得られた腐食防止処理層15a,15b(酸化物層)の安定性を向上させる役割を果たす。これは、硬くて脆い酸化物層をアクリル系樹脂成分で保護する効果、及び、希土類酸化物ゾルに含まれるリン酸塩由来のイオンコンタミネーション(特にナトリウムイオン)を捕捉する(カチオンキャッチャー)効果によって達成される。つまり、希土類元素酸化物ゾルを用いて得られた腐食防止処理層15a,15b中に、特にナトリウム等のアルカリ金属イオン又はアルカリ土類金属イオンが含まれると、該イオンを含む場所を起点にして腐食防止処理層15a,15bが劣化し易くなる。そのため、アニオン性ポリマーによって希土類酸化物ゾルに含まれるナトリウムイオン等を固定化することで、腐食防止処理層15a,15bの耐性が向上する。 The anionic polymer plays a role of improving the stability of the corrosion prevention treatment layers 15a and 15b (oxide layers) obtained by using the rare earth element oxide sol. This is due to the effect of protecting the hard and brittle oxide layer with an acrylic resin component and the effect of capturing ion contamination (particularly sodium ions) derived from phosphate contained in the rare earth oxide sol (cation catcher). Achieved. That is, when the corrosion prevention treatment layers 15a and 15b obtained by using the rare earth element oxide sol contain alkali metal ions such as sodium or alkaline earth metal ions, the place containing the ions is the starting point. The corrosion prevention treatment layers 15a and 15b are likely to deteriorate. Therefore, by immobilizing sodium ions and the like contained in the rare earth oxide sol with the anionic polymer, the resistance of the corrosion prevention treatment layers 15a and 15b is improved.
アニオン系ポリマーと希土類元素酸化物ゾルと組み合わせた腐食防止処理層15a,15bは、金属箔層14にクロメート処理を施して形成した腐食防止処理層15a,15bと同等の腐食防止性能を有する。アニオン系ポリマーは、本質的に水溶性であるポリアニオン系ポリマーが架橋された構造であることが好ましい。該構造の形成に用いる架橋剤としては、例えば、イソシアネー卜基、グリシジル基、カルボキシ基、オキサゾリン基を有する化合物が挙げられる。さらにはシランカップリング剤を用いてシロキサン結合を有する架橋部位を導入することも可能である。
The corrosion prevention treatment layers 15a and 15b in which the anionic polymer and the rare earth element oxide sol are combined have the same corrosion prevention performance as the corrosion prevention treatment layers 15a and 15b formed by subjecting the
イソシアネー卜基を有する化合物としては、例えば、トリレンジイソシアネート、キシリレンジイソシアネートあるいはその水素添加物、ヘキサメチレンジイソシアネート、4,4’-ジフェニルメタンジイソシアネートあるいはその水素添加物、イソホロンジイソシアネー卜などのジイソシアネー卜類;あるいはこれらのイソシアネー卜類を、トリメチロールプロパンなどの多価アルコールと反応させたアダクト体、水と反応させることで得られたビューレッ卜体、あるいは三量体であるイソシアヌレート体などのポリイソシアネー卜類;あるいはこれらのポリイソシアネー卜類をアルコール類、ラクタム類、オキシム類などでブロック化させたブロックポリイソシアネー卜などが挙げられる。 Examples of the compound having an isocyanate group include tolylene diisocyanate, xylylene diisocyanate or a hydrogenated product thereof, hexamethylene diisocyanate, 4,4'-diphenylmethane diisocyanate or a hydrogenated product thereof, and diisocyanate such as isophorone diisocyanate. Kind; or poly such as an adduct compound obtained by reacting these isocyanates with a polyhydric alcohol such as trimethylolpropane, a burette compound obtained by reacting with water, or a trimeric isocyanate compound. Examples thereof include block polyisocyanates in which these polyisocyanates are blocked with alcohols, lactams, oximes and the like.
グリシジル基を有する化合物としては、例えば、エチレングリコール、ジエチレングリコール、トリエチレングリコール、ポリエチレングリコール、プロピレングリコール、ジプロピレングリコール、トリプロピレングリコール、ポリプロピレングリコール、1,4-ブタンジオール、1,6-ヘキサンジオール、ネオペンチルグリコール等のグリコール類とエピク口ルヒドリンを作用させたエポキシ化合物、グリセリン、ポリグリセリン、トリメチロールプロパン、ペンタエリスリ卜ール、ソルビ卜ール等の多価アルコール類とエピク口ルヒドリンを作用させたエポキシ化合物、フタル酸、テレフタル酸、シュウ酸、アジピン酸等のジカルボン酸とエピクロルヒドリンとを作用させたエポキシ化合物などが挙げられる。 Examples of the compound having a glycidyl group include ethylene glycol, diethylene glycol, triethylene glycol, polyethylene glycol, propylene glycol, dipropylene glycol, tripropylene glycol, polypropylene glycol, 1,4-butanediol, and 1,6-hexanediol. Epylene glycol on glycols such as neopentyl glycol and polyhydric alcohols such as glycerin, polyglycerin, trimethylolpropane, pentaerythryl, and sorbyl on which epic-mouth ruhydrin was allowed to act. Examples thereof include an epoxy compound, an epoxy compound obtained by reacting dicarboxylic acids such as phthalic acid, terephthalic acid, oxalic acid, and adipic acid with epichlorohydrin.
カルボキシ基を有する化合物としては、各種脂肪族あるいは芳香族ジカルボン酸などが挙げられ、さらにはポリ(メタ)アクリル酸及びポリ(メタ)アクリル酸のアルカリ(土類)金属塩を用いることも可能である。 Examples of the compound having a carboxy group include various aliphatic or aromatic dicarboxylic acids, and it is also possible to use poly (meth) acrylic acid and alkaline (earth) metal salts of poly (meth) acrylic acid. be.
オキサゾリン基を有する化合物としては、例えば、オキサゾリンユニットを2つ以上有する低分子化合物、あるいはイソプロペニルオキサゾリンのような重合性モノマーを用いる場合には、(メタ)アクリル酸、(メタ)アクリル酸アルキルエステル、(メタ)アクリル酸ヒドロキシアルキル等のアクリル系モノマーを共重合させた化合物が挙げられる。 Examples of the compound having an oxazoline group include a low molecular weight compound having two or more oxazoline units, or (meth) acrylic acid and (meth) acrylic acid alkyl ester when a polymerizable monomer such as isopropenyl oxazoline is used. , (Meta) A compound obtained by copolymerizing an acrylic monomer such as hydroxyalkyl acrylate.
シランカップリング剤としては、γ-グリシドキシプロピル卜リメトキシシラン、γ-グリシドキシプロピルトリエトキシシラン、β-(3,4-エポキシシクロヘキシル)エチルトリメトキシシラン、γ-クロロプロピルメトキシシラン、ビニルトリクロロシラン、γ-メルカプトプロピルトリメトキシシラン、γ-アミノプロピルトリエトキシシラン、N-β(アミノエチル)-γ-アミノプロピルトリメトキシシラン、γ-イソシアナートプロピルトリエトキシシランが挙げられ、特にアニオン性ポリマーとの反応性を考慮すると、エポキシシラン、アミノシラン、イソシアネートシランが好ましい。 Examples of the silane coupling agent include γ-glycidoxypropyl trimethoxysilane, γ-glycidoxypropyltriethoxysilane, β- (3,4-epoxycyclohexyl) ethyltrimethoxysilane, and γ-chloropropylmethoxysilane. Examples thereof include vinyl trichlorosilane, γ-mercaptopropyltrimethoxysilane, γ-aminopropyltriethoxysilane, N-β (aminoethyl) -γ-aminopropyltrimethoxysilane, and γ-isocyanatopropyltriethoxysilane, and particularly anion. Considering the reactivity with the sex polymer, epoxysilane, aminosilane, and isocyanatesilane are preferable.
架橋剤の配合量は、アニオン性ポリマー100質量部に対し、1~50質量部が好ましく、10~20質量部がより好ましい。架橋剤の比率がアニオン性ポリマー100質量部に対して1質量部以上であれば、架橋構造が充分に形成され易い。架橋剤の比率がアニオン性ポリマー100質量部に対して50質量部以下であれば、塗液のポットライフが向上する。 The blending amount of the cross-linking agent is preferably 1 to 50 parts by mass, more preferably 10 to 20 parts by mass with respect to 100 parts by mass of the anionic polymer. When the ratio of the cross-linking agent is 1 part by mass or more with respect to 100 parts by mass of the anionic polymer, the cross-linking structure is sufficiently likely to be formed. When the ratio of the cross-linking agent is 50 parts by mass or less with respect to 100 parts by mass of the anionic polymer, the pot life of the coating liquid is improved.
アニオン性ポリマーを架橋する方法は、上記架橋剤に限らず、チタニウム、ジルコニウム化合物を用いてイオン架橋を形成する方法等であってもよい。また、これらの材料は、腐食防止処理層15aを形成するコーティング組成物を適用してもよい。
The method for cross-linking the anionic polymer is not limited to the above-mentioned cross-linking agent, and may be a method for forming an ionic cross-link using a titanium or zirconium compound. Further, as these materials, a coating composition for forming the corrosion
以上説明した腐食防止処理層15a,15bにおいて、クロメート処理に代表される化成処理による腐食防止処理層15a,15bは、金属箔層14との傾斜構造を形成させるため、特にフッ酸、塩酸、硝酸、硫酸あるいはこれらの塩を配合した化成処理剤を用いて金属箔層14に処理を施し、次いでクロム系又はノンクロム系の化合物を作用させて化成処理層を金属箔層14に形成させる。しかし、上記化成処理は、化成処理剤に酸を用いていることから、作業環境の悪化及びコーティング装置の腐食を伴う。
In the corrosion prevention treatment layers 15a and 15b described above, the corrosion prevention treatment layers 15a and 15b by chemical conversion treatment represented by chromate treatment form an inclined structure with the
一方、前述したコーティングタイプの腐食防止処理層15a,15bは、クロメート処理に代表される化成処理とは異なり、金属箔層14に対して傾斜構造を形成させる必要がない。そのため、コーティング剤の性状は、酸性、アルカリ性、中性等の制約を受けることがなく、良好な作業環境を実現できる。加えて、クロム化合物を用いるクロメート処理は、環境衛生上、代替案が求められている点からも、コーティングタイプの腐食防止処理層15a,15bが好ましい。
On the other hand, unlike the chemical conversion treatment represented by the chromate treatment, the coating type corrosion prevention treatment layers 15a and 15b described above do not need to form an inclined structure with respect to the
腐食防止処理層15a,15bは、必要に応じて、さらにカチオン性ポリマーを積層した積層構造としてもよい。カチオン性ポリマーとしては、ポリエチレンイミン、ポリエチレンイミンとカルボン酸を有するポリマーとからなるイオン高分子錯体、アクリル主骨格に1級アミンをグラフ卜させた1級アミングラフトアクリル樹脂、ポリアリルアミンあるいはこれらの誘導体、アミノフェノール樹脂等が挙げられる。 The corrosion prevention treatment layers 15a and 15b may have a laminated structure in which a cationic polymer is further laminated, if necessary. Examples of the cationic polymer include polyethyleneimine, an ionic polymer complex composed of polyethyleneimine and a polymer having a carboxylic acid, a primary amine graft acrylic resin in which a primary amine is graphed on an acrylic main skeleton, polyallylamine or a derivative thereof. , Aminophenol resin and the like.
イオン高分子錯体を形成する「カルボン酸を有するポリマー」としては、例えば、ポリカルボン酸(塩)、ポリカルボン酸(塩)にコモノマーを導入した共重合体、カルボキシ基を有する多糖類等が挙げられる。ポリカルボン酸(塩)としては、例えば、ポリアクリル酸あるいはそのイオン塩などが挙げられる。カルボキシ基を有する多糖類としては、例えば、カルボキシメチルセルロースあるいはそのイオン塩などが挙げられる。イオン塩としては、アルカリ金属塩、アルカリ土類金属塩等が挙げられる。 Examples of the "polymer having a carboxylic acid" that forms an ionic polymer complex include polycarboxylic acid (salt), a copolymer in which a comonomer is introduced into the polycarboxylic acid (salt), and a polysaccharide having a carboxy group. Be done. Examples of the polycarboxylic acid (salt) include polyacrylic acid or an ionic salt thereof. Examples of the polysaccharide having a carboxy group include carboxymethyl cellulose or an ionic salt thereof. Examples of the ionic salt include alkali metal salts and alkaline earth metal salts.
1級アミングラフ卜アクリル樹脂は、アクリル主骨格に1級アミンをグラフ卜させた樹脂である。該アクリル主骨格としては、ポリ(メタ)アクリル酸など、上述したアクリルポリオールで用いられる各種モノマーが挙げられる。該アクリル主骨格にグラフ卜させる1級アミンとしては、エチレンイミン等が挙げられる。 The primary amine graph acrylic resin is a resin in which a primary amine is graphed on the acrylic main skeleton. Examples of the acrylic main skeleton include various monomers used in the above-mentioned acrylic polyols such as poly (meth) acrylic acid. Examples of the primary amine to be graphed on the acrylic main skeleton include ethyleneimine.
ポリアリルアミンまたはその誘導体としては、アリルアミン、アリルアミンアミド硫酸塩、ジアリルアミン、ジメチルアリルアミンなどの単独重合体あるいは共重合体を用いることが可能であり、さらに、これらのアミンはフリーのアミンでも酢酸あるいは塩酸による安定化物でも用いることが可能である。またさらに共重合体成分として、マレイン酸、二酸化イオウなどを用いることも可能である。さらには1級アミンを部分メトキシ化させることで熱架橋性を付与させたタイプも用いることが可能である。これらのカチオン性ポリマーは、1種単独で用いてもよく、2種以上を併用してもよい。カチオン性ポリマーとしては、上記の中でも、ポリアリルアミン及びその誘導体からなる群から選ばれる少なくとも1種が好ましい。 As the polyallylamine or a derivative thereof, homopolymers or copolymers such as allylamine, allylamine amide sulfate, diallylamine, and dimethylallylamine can be used, and these amines can be free amines by acetic acid or hydrochloric acid. Stabilized products can also be used. Further, it is also possible to use maleic acid, sulfur dioxide or the like as the copolymer component. Furthermore, it is also possible to use a type in which thermal crosslinkability is imparted by partially methoxylating a primary amine. These cationic polymers may be used alone or in combination of two or more. Among the above, the cationic polymer is preferably at least one selected from the group consisting of polyallylamine and its derivatives.
カチオン性ポリマーは、カルボキシ基、グリシジル基等のアミン/イミンと反応が可能な官能基を有する架橋剤と併用することが好ましい。カチオン性ポリマーと併用する架橋剤としては、ポリエチレンイミンとイオン高分子錯体を形成するカルボン酸を有するポリマーも使用でき、例えば、ポリアクリル酸あるいはそのイオン塩等のポリカルボン酸(塩)、あるいはこれにコモノマーを導入した共重合体、カルボキシメチルセルロースあるいはそのイオン塩等のカルボキシ基を有する多糖類等が挙げられる。 The cationic polymer is preferably used in combination with a cross-linking agent having a functional group capable of reacting with an amine / imine such as a carboxy group and a glycidyl group. As the cross-linking agent used in combination with the cationic polymer, a polymer having a carboxylic acid forming an ionic polymer complex with polyethyleneimine can also be used, for example, polyacrylic acid or a polycarboxylic acid (salt) such as an ionic salt thereof, or a polycarboxylic acid (salt) thereof. Examples thereof include a copolymer having a comonomer introduced therein, and a polysaccharide having a carboxy group such as carboxymethyl cellulose or an ionic salt thereof.
本実施形態においては、カチオン性ポリマーも腐食防止処理層15a,15bを構成する一構成要素として記載している。その理由は、リチウムイオン電池用外装材で要求される電解液耐性、フッ酸耐性を付与させるべく様々な化合物を用い鋭意検討を行った結果、カチオン性ポリマー自体にも、電解液耐性、耐フッ酸性を付与することが可能な化合物であることが判明したためである。この要因は、フッ素イオンをカチオン性基で捕捉する(アニオンキャッチャー)ことで、金属箔層14が損傷することを抑制しているためであると推測される。また、カチオン性ポリマーは、腐食防止処理層15bとシーラント接着層16の接着性の向上の点でも非常に好ましい。また、カチオン性ポリマーは、前述したアニオン性ポリマーと同様に水溶性であるため、上記架橋剤を用いて架橋構造を形成させることで耐水性を向上させることができる。このように、カチオン性ポリマーを用いても架橋構造を形成させることができることから、腐食防止処理層15a,15bの形成に希土類酸化物ゾルを用いた場合には、その保護層としてアニオン性ポリマーの代わりにカチオン性ポリマーを用いてもよい。
In this embodiment, the cationic polymer is also described as one component constituting the corrosion prevention treatment layers 15a and 15b. The reason for this is that as a result of diligent studies using various compounds to impart the electrolyte solution resistance and phosphoric acid resistance required for exterior materials for lithium-ion batteries, the cationic polymer itself also has electrolyte solution resistance and fluorine resistance. This is because it was found to be a compound capable of imparting acidity. It is presumed that this factor is because the
以上の内容から、上述したコーティングタイプの腐食防止処理の組み合わせの事例として、(1)希土類酸化物ゾルのみ、(2)アニオン性ポリマーのみ、(3)カチオン性ポリマーのみ、(4)希土類酸化物ゾル+アニオン性ポリマー(積層複合化)、(5)希土類酸化物ゾル+カチオン性ポリマー(積層複合化)、(6)(希土類酸化物ゾル+アニオン性ポリマー:積層複合化)/カチオン性ポリマー(多層化)、(7)(希土類酸化物ゾル+カチオン性ポリマー:積層複合化)/アニオン性ポリマー(多層化)、等が挙げられる。中でも(1)及び(4)~(7)が好ましく、(4)~(7)がより好ましい。また、腐食防止処理層15aの場合、腐食防止効果とアンカー効果(密着性向上効果)が一層で実現できることから、(6)が特に好ましい。また、腐食防止処理層15bの場合、シーラント層17側の電解液耐性をより保持し易くなることから、(6)及び(7)が特に好ましい。ただし、本実施形態は、上記組み合せに限られるわけではない。たとえば腐食防止処理の選択の事例として、カチオン性ポリマーは、後述するシーラント接着層16の説明で挙げる変性ポリオレフィン樹脂との接着性が良好であるという点でも非常に好ましい材料であることから、シーラント接着層16を変性ポリオレフィン樹脂で構成される場合においては、シーラント接着層16に接する面にカチオン性ポリマーを設ける(例えば、構成(5)及び(6)などの構成)といった設計が可能である。
From the above, as examples of the combination of coating type corrosion prevention treatments described above, (1) rare earth oxide sol only, (2) anionic polymer only, (3) cationic polymer only, (4) rare earth oxide Sol + anionic polymer (laminated composite), (5) rare earth oxide sol + cationic polymer (laminated composite), (6) (rare earth oxide sol + anionic polymer: laminated composite) / cationic polymer ( Multilayering), (7) (rare earth oxide sol + cationic polymer: laminated composite) / anionic polymer (multilayering), and the like. Among them, (1) and (4) to (7) are preferable, and (4) to (7) are more preferable. Further, in the case of the corrosion
ただし腐食防止処理層15a,15bは上述した層には限定されない。例えば、公知技術である塗布型クロメートのように、樹脂バインダー(アミノフェノール樹脂など)にリン酸とクロム化合物を配合した剤を用いて形成してもよい。該処理剤を用いれば、腐食防止機能と密着性を双方兼ね備えた層を形成することが可能になる。また、上述した化成処理層(脱脂処理、熱水変成処理、陽極酸化処理、化成処理、あるいはこれら処理の組み合わせにより形成した層)に対して、密着性を向上させるために、上述してきたカチオン性ポリマー及び/又はアニオン性ポリマーを用いて複合的な処理を施したり、あるいはこれらの処理の組み合わせに対して多層構造としてカチオン性ポリマー及び/又はアニオン性ポリマーを積層させたりすることも可能である。また、塗液の安定性を考慮する必要があるが、上述してきた希土類酸化物ゾルとカチオン性ポリマーあるいはアニオン性ポリマーとを事前に一液化して得られたコーティング剤を使用して腐食防止機能と密着性の両方を兼ね備えた層とすることができる。 However, the corrosion prevention treatment layers 15a and 15b are not limited to the above-mentioned layers. For example, it may be formed by using an agent in which a phosphoric acid and a chromium compound are mixed in a resin binder (aminophenol resin or the like), such as a coating type chromate which is a known technique. By using the treatment agent, it becomes possible to form a layer having both a corrosion prevention function and an adhesion. Further, in order to improve the adhesion to the above-mentioned chemical conversion treatment layer (layer formed by degreasing treatment, hydrothermal modification treatment, anodic oxidation treatment, chemical conversion treatment, or a combination of these treatments), the above-mentioned cationic property has been used. It is also possible to perform complex treatments with polymers and / or anionic polymers, or to laminate cationic and / or anionic polymers as a multilayer structure for a combination of these treatments. In addition, although it is necessary to consider the stability of the coating liquid, the corrosion prevention function is performed by using a coating agent obtained by preliminarily liquefying the above-mentioned rare earth oxide sol and a cationic polymer or an anionic polymer. It can be a layer having both adhesion and adhesion.
腐食防止処理層15a,15bの単位面積あたりの質量は0.005~0.200g/m2の範囲内が好ましく、0.010~0.100g/m2の範囲内がより好ましい。0.005g/m2以上であれば、金属箔層14に腐食防止機能を付与し易い。また、上記単位面積当たりの質量が0.200g/m2を超えても、腐食防止機能は飽和してあまり変らない。一方、希土類酸化物ゾルを用いた場合には、塗膜が厚いと乾燥時の熱によるキュアが不充分となり、凝集力の低下を伴うおそれがある。なお、上記内容では単位面積あたりの質量で記載しているが、比重がわかればそこから厚みを換算することも可能である。
The mass per unit area of the corrosion prevention treatment layers 15a and 15b is preferably in the range of 0.005 to 0.200 g / m 2 , and more preferably in the range of 0.010 to 0.100 g / m 2 . If it is 0.005 g / m 2 or more, it is easy to impart a corrosion prevention function to the
腐食防止処理層15a,15bの厚さは、腐食防止機能、及びアンカーとしての機能の点から、例えば10nm~5μmであることが好ましく、20~500nmであることがより好ましい。 The thickness of the corrosion prevention treatment layers 15a and 15b is preferably, for example, 10 nm to 5 μm, and more preferably 20 to 500 nm from the viewpoint of the corrosion prevention function and the function as an anchor.
(シーラント接着層16)
シーラント接着層16は、腐食防止処理層15bが形成された金属箔層14とシーラント層17を接着する層である。外装材10は、シーラント接着層16を形成する接着成分によって、熱ラミネート構成とドライラミネート構成に大きく分けられる。
(Sealant adhesive layer 16)
The
熱ラミネート構成におけるシーラント接着層16を形成する接着成分は、ポリオレフィン系樹脂を酸でグラフト変性した酸変性ポリオレフィン系樹脂であることが好ましい。酸変性ポリオレフィン系樹脂は、無極性であるポリオレフィン系樹脂の一部に極性基が導入されていることから、無極性のポリオレフィン系樹脂フィルム等で構成された場合のシーラント層17と、極性を有することが多い腐食防止処理層15bの両方に強固に密着することができる。また、酸変性ポリオレフィン系樹脂を使用することで、外装材10の電解液等の内容物に対する耐性が向上し、電池内部でフッ酸が発生してもシーラント接着層16の劣化による密着力の低下を防止し易い。
The adhesive component forming the
酸変性ポリオレフィン系樹脂のポリオレフィン系樹脂としては、例えば、低密度、中密度及び高密度のポリエチレン;エチレン-αオレフィン共重合体;ポリプロピレン;並びに、プロピレン-αオレフィン共重合体等が挙げられる。共重合体である場合のポリオレフィン樹脂は、ブロック共重合体であってもよく、ランダム共重合体であってもよい。また、ポリオレフィン樹脂としては、上記したものにアクリル酸若しくはメタクリル酸等の極性分子を共重合させた共重合体、又は、架橋ポリオレフィン等の重合体等も使用できる。ポリオレフィン系樹脂を変性する酸としては、カルボン酸、エポキシ化合物及び酸無水物等が挙げられ、無水マレイン酸であることが好ましい。シーラント接着層16に使用する酸変性ポリオレフィン系樹脂は、1種であってもよく、2種以上であってもよい。
Examples of the polyolefin-based resin of the acid-modified polyolefin-based resin include low-density, medium-density and high-density polyethylene; ethylene-α-olefin copolymer; polypropylene; and propylene-α-olefin copolymer. When it is a copolymer, the polyolefin resin may be a block copolymer or a random copolymer. Further, as the polyolefin resin, a copolymer obtained by copolymerizing the above-mentioned one with a polar molecule such as acrylic acid or methacrylic acid, or a polymer such as crosslinked polyolefin can also be used. Examples of the acid for modifying the polyolefin resin include carboxylic acid, epoxy compound, acid anhydride and the like, and maleic anhydride is preferable. The acid-modified polyolefin-based resin used for the
熱ラミネート構成のシーラント接着層16は、上記接着成分を押出し装置で押し出すことで形成できる。熱ラミネート構成のシーラント接着層16の厚さは2~50μmであることが好ましい。
The
ドライラミネート構成のシーラント接着層16を形成する接着成分としては、例えば、接着層13で挙げたものと同様の接着剤が挙げられる。この場合、電解液による膨潤及びフッ酸による加水分解を抑制するため、加水分解し難い骨格の主剤で、かつ架橋密度の向上が可能な組成となるように、接着剤の組成を設計することが好ましい。
Examples of the adhesive component forming the
架橋密度を向上させる場合、例えば、ダイマー脂肪酸、ダイマー脂肪酸のエステルもしくは水素添加物、ダイマー脂肪酸の還元グリコール、ダイマー脂肪酸のエステルもしくは水素添加物の還元グリコールを接着剤に添加するとよい。上記ダイマー脂肪酸は、各種不飽和脂肪酸を二量化させた酸であり、その構造としては、非環型、単環型、多環型、芳香環型が例示できる。 When improving the cross-linking density, for example, dimer fatty acid, ester or hydrogen additive of dimer fatty acid, reduced glycol of dimer fatty acid, ester of dimer fatty acid or reduced glycol of hydrogen additive may be added to the adhesive. The dimer fatty acid is an acid obtained by dimerizing various unsaturated fatty acids, and examples thereof include acyclic type, monocyclic type, polycyclic type, and aromatic ring type.
ダイマー脂肪酸の出発物質である脂肪酸は特に限定されない。また、このようなダイマー脂肪酸を必須成分として、通常のポリエステルポリオールで用いられるような二塩基酸を導入しても構わない。シーラント接着層16を構成する主剤に対する硬化剤としては、例えば、ポリエステルポリオールの鎖伸長剤としても使用できるイソシアネート化合物を用いることが可能である。これにより、接着剤塗膜の架橋密度が高まり、溶解性及び膨潤性の向上につながるとともに、ウレタン基濃度が高まることで基材密着性の向上も期待できる。
The fatty acid that is the starting material of the dimer fatty acid is not particularly limited. Further, with such a dimer fatty acid as an essential component, a dibasic acid as used in a normal polyester polyol may be introduced. As a curing agent for the main agent constituting the
ドライラミネート構成のシーラント接着層16は、エステル基及びウレタン基等の加水分解性の高い結合部を有しているので、より高い信頼性が求められる用途には、シーラント接着層16として熱ラミネート構成の接着成分を用いることが好ましい。例えば酸変性ポリオレフィン樹脂を、トルエン、メチルシクロヘキサン(MCH)等の溶剤にて溶解、あるいは、分散させた塗液に上述した各種硬化剤を配合し、塗布、乾燥させることでシーラント接着層16を形成する。
Since the
シーラント接着層16を押出成型により形成する場合、押出成型時に発生する応力等により、接着樹脂がMD方向(押出す方向)に配向し易い。この場合、シーラント接着層16の異方性を緩和するために、シーラント接着層16にエラストマーを配合してもよい。シーラント接着層16に配合するエラストマーとしては、例えば、オレフィン系エラストマー、スチレン系エラストマー等を用いることができる。
When the
上記エラストマーの平均粒径は、エラストマーと接着樹脂との相溶性が向上し、またシーラント接着層16の異方性を緩和する効果を向上させることが可能な粒径が好ましい。具体的には、上記エラストマーの平均粒径は、例えば、200nm以下が好ましい。
The average particle size of the elastomer is preferably a particle size capable of improving the compatibility between the elastomer and the adhesive resin and improving the effect of alleviating the anisotropy of the
なお、エラストマーの平均粒径は、例えば、電子顕微鏡により、エラストマー組成物の断面を拡大した写真を撮影し、その後、画像解析により、分散した架橋ゴム成分の平均粒径を測定することで求められる。上記エラストマーは、1種を単独で使用してもよいし、2種以上を併用して使用してもよい。 The average particle size of the elastomer can be determined by, for example, taking an enlarged photograph of the cross section of the elastomer composition with an electron microscope and then measuring the average particle size of the dispersed crosslinked rubber component by image analysis. .. The above-mentioned elastomer may be used alone or in combination of two or more.
シーラント接着層16にエラストマーを配合する場合、シーラント接着層16(100質量%)中に添加するエラストマーの配合量は、例えば、1~25質量%が好ましく、10~20質量%がより好ましい。エラストマーの配合量を1質量%以上とすることで、接着樹脂との相溶性が向上すると共に、シーラント接着層16の異方性を緩和する効果が向上する傾向がある。また、エラストマーの配合量を25質量%以下とすることで、シーラント接着層16が電解液によって膨潤することを抑制する効果が向上する傾向がある。
When the elastomer is blended in the
シーラント接着層16として、例えば、接着樹脂を有機溶媒に分散させたディスパージョンタイプの接着樹脂液を用いてもよい。
As the
シーラント接着層16の厚さは、熱ラミネート構成の場合には、2~50μmであることが好ましく、20~40μmであることがより好ましい。シーラント接着層16の厚さが2μm以上であることにより、金属箔層14とシーラント層17との十分な接着強度が得られ易く、50μm以下であることにより、外装材端面から内部の電池要素に浸入する水分量を低減し易くすることができる。また、シーラント接着層16の厚さは、ドライラミネート構成の場合には、1~5μmであることが好ましい。シーラント接着層16の厚さが1μm以上であることにより、金属箔層14とシーラント層17との十分な接着強度が得られ易く、5μm以下であることにより、シーラント接着層16の割れの発生を抑制することができる。
The thickness of the
(シーラント層17)
シーラント層17は、外装材10に対し、ヒートシールによる封止性を付与する層であり、蓄電装置の組み立て時に内側に配置されて熱融着される層である。シーラント層17としては、ポリオレフィン系樹脂、又はポリオレフィン系樹脂に無水マレイン酸等の酸をグラフト変性させた酸変性ポリオレフィン系樹脂からなる樹脂フィルムが挙げられる。中でも、水蒸気のバリア性を向上させ、ヒートシールによって過度に潰れることなく蓄電装置の形態を構成可能なポリオレフィン系樹脂が好ましく、ポリプロピレンが特に好ましい。
(Sealant layer 17)
The
ポリオレフィン系樹脂としては、例えば、低密度、中密度及び高密度のポリエチレン;エチレン-αオレフィン共重合体;ポリプロピレン;並びに、プロピレン-αオレフィン共重合体等が挙げられる。共重合体である場合のポリオレフィン樹脂は、ブロック共重合体であってもよく、ランダム共重合体であってもよい。これらポリオレフィン系樹脂は、1種を単独で使用してもよく、2種以上を併用してもよい。 Examples of the polyolefin-based resin include low-density, medium-density and high-density polyethylene; ethylene-α-olefin copolymer; polypropylene; and propylene-α-olefin copolymer. When it is a copolymer, the polyolefin resin may be a block copolymer or a random copolymer. One of these polyolefin resins may be used alone, or two or more thereof may be used in combination.
また、上記各タイプのポリプロピレン、すなわち、ランダムポリプロピレン、ホモポリプロピレン、ブロックポリプロピレンには、低結晶性のエチレン-ブテン共重合体、低結晶性のプロピレン-ブテン共重合体、エチレンとブテンとプロピレンの3成分共重合体からなるターポリマー、シリカ、ゼオライト、アクリル樹脂ビーズ等のアンチブロッキング剤(AB剤)、脂肪酸アマイド系のスリップ剤等を添加してもよい。 In addition, the above-mentioned types of polypropylene, that is, random polypropylene, homopolypropylene, and block polypropylene, include low-crystalline ethylene-butene copolymers, low-crystalline propylene-butene copolymers, and ethylene, butene, and propylene. An anti-blocking agent (AB agent) such as a tarpolymer composed of a component copolymer, silica, zeolite, or acrylic resin beads, a fatty acid amide-based slip agent, or the like may be added.
酸変性ポリオレフィン系樹脂としては、例えば、シーラント接着層16で挙げたものと同様のものが挙げられる。
Examples of the acid-modified polyolefin-based resin include those similar to those mentioned in the
シーラント層17は、単層フィルムであってもよく、多層フィルムであってもよく、必要とされる機能に応じて選択すればよい。例えば、防湿性を付与する点では、エチレン-環状オレフィン共重合体及びポリメチルペンテン等の樹脂を介在させた多層フィルムが使用できる。
The
また、シーラント層17は、難燃剤、スリップ剤、アンチブロッキング剤、酸化防止剤、光安定剤及び粘着付与剤等の各種添加材を含んでいてもよい。
Further, the
シーラント層17として、押出成型により形成した熱溶着性フィルムを使用する場合、該熱溶着性フィルムの押出し方向に配向傾向がある。このため、配向によるシーラント層17の異方性を緩和する観点から、熱溶着性フィルムにエラストマーを配合してもよい。これにより、蓄電装置用外装材10を冷間成型して凹部を形成する際にシーラント層17が白化することを抑制できる。
When a heat-weldable film formed by extrusion molding is used as the
シーラント層17を構成するエラストマーとしては、例えば、シーラント接着層16を構成するエラストマーとして例示した材料と同じ材料を用いることができる。シーラント層17が多層フィルム構造である場合、多層フィルム構造を構成する複数の層のうち、少なくとも1層がエラストマーを含むように構成してもよい。例えば、シーラント層17として、積層されたランダムポリプロピレン層/ブロックポリプロピレン層/ランダムポリプロピレン層よりなる3層積層構造の場合、エラストマーは、ブロックポリプロピレン層のみに配合してもよいし、ランダムポリプロピレン層のみに配合してもよいし、ランダムポリプロピレン層とブロックポリプロピレン層との両方に配合してもよい。
As the elastomer constituting the
また、シーラント層17に滑り性を付与するために、滑剤を含有させてもよい。このように、シーラント層17が滑剤を含有することで、冷間成型により、蓄電装置用外装材10に凹部を形成する際、蓄電装置用外装材10において延伸率の高い凹部の辺又は角となる部分が必要以上に延伸されることを抑制可能となる。これにより、金属箔層14とシーラント接着層16との間が剥離したり、シーラント層17とシーラント接着層16とにおいてクラックによる破断及び白化が生じたりすることを抑制することができる。
Further, in order to impart slipperiness to the
シーラント層17に滑剤を含有させる場合、シーラント層17(100質量%)中の滑剤の含有量は、0.001~0.5質量%が好ましい。滑剤の含有量が0.001質量%以上であると、冷間成型時にシーラント層17が白化することをより抑制できる傾向がある。また、滑剤の含有量が0.5質量%以下であると、シーラント層17の面と接触する他の層の面との間における密着強度の低下を抑制できる傾向がある。
When the
シーラント層17の厚さは、10~100μmであることが好ましく、20~60μmであることがより好ましい。シーラント層17の厚さが10μm以上であることにより、十分なヒートシール強度を得ることができ、100μm以下であることにより、外装材端部からの水蒸気の浸入量を低減することができる。
The thickness of the
(コーティング層18)
コーティング層18は、外装材10に対し、アクリル系PSA(Pressure Sensitive Adhesive)テープとの良好な密着性を付与する層である。外装材10を容器として備える蓄電装置は、アクリル系PSAテープを介してデバイスに載置される場合があるため、外装材10表面(すなわち基材層11側の面)が当該テープと良好に密着することが好ましい。なお、アクリル系PSAテープは、PETフィルム等の基材上にアクリル粘着剤層が積層されたものである。アクリル粘着剤としては、例えば水酸基を有するアクリル共重合体を主剤とし、イソシアネート系硬化剤を含むものが挙げられる。
(Coating layer 18)
The
コーティング層18としては、アクリル樹脂及びポリエステル樹脂からなる群より選択される少なくとも1種の樹脂を含む層であることが好ましい。
The
アクリル樹脂を構成するモノマー成分としては、例えば、アルキルアクリレート、アルキルメタクリレート(アルキル基としてはメチル基、エチル基、n-プロピル基、イソプロピル基、n-ブチル基、イソブチル基、t-ブチル基、2-エチルヘキシル基、ラウリル基、ステアリル基、シクロヘキシル基、フェニル基、ベンジル基、フェニルエチル基などが挙げられる);2-ヒドロキシエチルアクリレート、2-ヒドロキシエチルメタクリレート、2-ヒドロキシプロピルアクリレート、2-ヒドロキシプロピルメタクリレートなどのヒドロキシ基含有モノマー;アクリルアミド、メタクリルアミド、N-メチルアクリルアミド、N-メチルメタクリルアミド、N-メチロールアクリルアミド、N-メチロールメタクリルアミド、N,N-ジメチロールアクリルアミド、N-メトキシメチルアクリルアミド、N-メトキシメチルメタクリルアミド、N-フェニルアクリルアミドなどのアミド基含有モノマー;N,N-ジエチルアミノエチルアクリレート、N,N-ジエチルアミノエチルメタクリレートなどのアミノ基含有モノマー;グリシジルアクリレート、グリシジルメタクリレートなどのエポキシ基含有モノマー;アクリル酸、メタクリル酸およびそれらの塩(リチウム塩、ナトリウム塩、カリウム塩など)などのカルボキシル基、またはその塩を含有するモノマーなどを用いることができる。これらは1種を単独で用いてもよく、2種以上を用いて共重合させてもよい。更に、これらは上記以外の他のモノマーと併用することができる。 Examples of the monomer components constituting the acrylic resin include alkyl acrylates and alkyl methacrylates (alkyl groups include methyl group, ethyl group, n-propyl group, isopropyl group, n-butyl group, isobutyl group, t-butyl group, 2). -Ethylhexyl group, lauryl group, stearyl group, cyclohexyl group, phenyl group, benzyl group, phenylethyl group, etc.); 2-hydroxyethyl acrylate, 2-hydroxyethyl methacrylate, 2-hydroxypropyl acrylate, 2-hydroxypropyl Hydroxy group-containing monomers such as methacrylate; acrylamide, methacrylamide, N-methylacrylamide, N-methylmethacrylate, N-methylolacrylamide, N-methylolmethacrylate, N, N-dimethylolacrylamide, N-methoxymethylacrylamide, N -Amid group-containing monomers such as methoxymethylmethacrylate and N-phenylacrylamide; amino group-containing monomers such as N, N-diethylaminoethyl acrylate and N, N-diethylaminoethyl methacrylate; epoxy group-containing monomers such as glycidyl acrylate and glycidyl methacrylate. A carboxyl group such as acrylic acid, methacrylic acid and salts thereof (lithium salt, sodium salt, potassium salt, etc.), or a monomer containing the salt can be used. One of these may be used alone, or two or more thereof may be used for copolymerization. Furthermore, these can be used in combination with other monomers other than the above.
他のモノマーとしては、例えば、アリルグリシジルエーテルなどのエポキシ基含有モノマー;スチレンスルホン酸、ビニルスルホン酸およびそれらの塩(リチウム塩、ナトリウム塩、カリウム塩、アンモニウム塩など)などのスルホン酸基またはその塩を含有するモノマー;クロトン酸、イタコン酸、マレイン酸、フマル酸、およびそれらの塩(リチウム塩、ナトリウム塩、カリウム塩、アンモニウム塩など)などのカルボキシル基またはその塩を含有するモノマー;無水マレイン酸、無水イタコン酸などの酸無水物を含有するモノマー;ビニルイソシアネート、アリルイソシアネート、スチレン、ビニルメチルエーテル、ビニルエチルエーテル、ビニルトリスアルコキシシラン、アルキルマレイン酸モノエステル、アルキルフマル酸モノエステル、アクリロニトリル、メタクリロニトリル、アルキルイタコン酸モノエステル、塩化ビニリデン、酢酸ビニル、塩化ビニルなどを用いることができる。また、アクリル樹脂としては、変性アクリル共重合体、例えば、ポリエステル、ウレタン、エポキシなどで変性したブロック共重合体、グラフト共重合体などを使用してもよい。 Other monomers include, for example, epoxy group-containing monomers such as allylglycidyl ether; sulfonic acid groups such as styrene sulfonic acid, vinyl sulfonic acid and salts thereof (lithium salt, sodium salt, potassium salt, ammonium salt, etc.) or sulfonic acid groups thereof. Monomer containing salts; sulfonic acid, itaconic acid, maleic acid, fumaric acid, and monomers containing carboxyl groups such as salts thereof (lithium salt, sodium salt, potassium salt, ammonium salt, etc.) or salts thereof; maleine anhydride Monomer containing acid anhydrides such as acid, itaconic acid anhydride; vinyl isocyanate, allyl isocyanate, styrene, vinylmethyl ether, vinyl ethyl ether, vinyltris alkoxysilane, alkylmaleic acid monoester, alkyl fumolic acid monoester, acrylonitrile, Methacylonitrile, alkylitaconic acid monoester, vinylidene chloride, vinyl acetate, vinyl chloride and the like can be used. Further, as the acrylic resin, a modified acrylic copolymer, for example, a block copolymer modified with polyester, urethane, epoxy, or the like, a graft copolymer, or the like may be used.
ポリエステル樹脂としては、共重合成分を導入しガラス転移温度を低下させた共重合ポリエステルが好ましい。共重合ポリエステルは、塗工性の点から水溶性もしくは水分散性を有することが好ましい。このような共重合ポリエステルとしては、スルホン酸基又はそのアルカリ金属塩基からなる群より選択される少なくとも1種の基が結合した共重合ポリエステル(以下、「スルホン酸基含有共重合ポリエステル」という)を用いることが好ましい。 As the polyester resin, a copolymerized polyester in which a copolymerization component is introduced to lower the glass transition temperature is preferable. The copolymerized polyester is preferably water-soluble or water-dispersible from the viewpoint of coatability. As such a copolymerized polyester, a copolymerized polyester in which at least one group selected from the group consisting of a sulfonic acid group or an alkali metal base thereof is bonded (hereinafter, referred to as “sulfonic acid group-containing copolymerized polyester”) is used. It is preferable to use it.
ここでスルホン酸基含有共重合ポリエステルとは、ジカルボン酸成分又はグリコール成分の一部にスルホン酸基又はそのアルカリ金属塩基からなる群より選択される少なくとも1種の基が結合したポリエステルをいい、中でも、スルホン酸基又はそのアルカリ金属塩基からなる群より選択される少なくとも1種の基を含有した芳香族ジカルボン酸成分を全酸成分に対して2~10モル%の割合で用いて調製した共重合ポリエステルが好ましい。 Here, the sulfonic acid group-containing copolymerized polyester means a polyester in which at least one group selected from the group consisting of a sulfonic acid group or an alkali metal base thereof is bonded to a part of a dicarboxylic acid component or a glycol component. , A copolymerization prepared by using an aromatic dicarboxylic acid component containing at least one group selected from the group consisting of a sulfonic acid group or an alkali metal base thereof at a ratio of 2 to 10 mol% with respect to the total acid component. Polyester is preferred.
このようなジカルボン酸の例としては、5-ナトリウムスルホイソフタル酸が好適である。この場合、他のジカルボン酸成分としては、テレフタル酸、イソフタル酸、フタル酸、p-β-オキシエトキシ安息香酸、2,6-ナフタレンジカルボン酸、4,4’-ジカルボキシジフェニル、4,4’-ジカルボキシベンゾフェノン、ビス(4-カルボキシフェニル)エタン、アジピン酸、セバシン酸、シクロヘキサン-1,4-ジカルボン酸等が挙げられる。 As an example of such a dicarboxylic acid, 5-sodium sulfoisophthalic acid is suitable. In this case, as other dicarboxylic acid components, terephthalic acid, isophthalic acid, phthalic acid, p-β-oxyethoxybenzoic acid, 2,6-naphthalenedicarboxylic acid, 4,4'-dicarboxydiphenyl, 4,4' -Dicarboxybenzophenone, bis (4-carboxyphenyl) ethane, adipic acid, sebacic acid, cyclohexane-1,4-dicarboxylic acid and the like can be mentioned.
スルホン酸基含有共重合ポリエステルを製造するためのグリコール成分としては、エチレングリコールが主として用いられ、この他に、プロピレングリコール、ブタンジオール、ネオペンチルグリコール、ジエチレングリコール、シクロヘキサンジメタノール、ビスフェノールAのエチレンオキサイド付加物、ポリエチレングリコール、ポリプロピレングリコール、ポリテトラメチレングリコール等を用いることができる。中でも、エチレングリコール、プロピレングリコール、ブタンジオール、ネオペンチルグリコール、ジエチレングリコール、シクロヘキサンジメタノール等を共重合成分として用いると、ポリスチレンスルホン酸塩との相溶性が向上するという点で好ましい。 Ethylene glycol is mainly used as a glycol component for producing a sulfonic acid group-containing copolymerized polyester, and in addition to this, ethylene oxide addition of propylene glycol, butanediol, neopentyl glycol, diethylene glycol, cyclohexanedimethanol, and bisphenol A is used. Articles, polyethylene glycol, polypropylene glycol, polytetramethylene glycol and the like can be used. Above all, it is preferable to use ethylene glycol, propylene glycol, butanediol, neopentyl glycol, diethylene glycol, cyclohexanedimethanol or the like as a copolymerization component in that compatibility with polystyrene sulfonate is improved.
アクリル樹脂及びポリエステル樹脂は、それぞれ単独で用いても、二種以上を併用してもよい。また、これらの樹脂と、以下に例示する硬化剤とを併用してもよい。 The acrylic resin and the polyester resin may be used alone or in combination of two or more. Further, these resins may be used in combination with the curing agents exemplified below.
硬化剤としては特に制限はないが、例えばイソシアネート硬化剤が挙げられる。イソシアネートとしては、脂肪族イソシアネートや芳香族イソシアネートが挙げられるが、脂肪族イソシアネートが好ましい。脂肪族イソシアネート硬化剤は、芳香環を有しない2官能以上のイソシアネート化合物である。芳香環を有しないことにより紫外線によるベンゼン環のキノイド化が起きず、黄変を抑制できることからも、コーティング層のような最外層に適している。脂肪族イソシアネート硬化剤としては、メチレンジイソシアネート、イソプロピレンジイソシアネート、リジンジイソシアネート、2,2,4-もしくは2,4,4-トリメチルヘキサメチレンジイソシアネート、1,6-ヘキサメチレンジイソシアネート、メチルシクロヘキサンジイソシアネート、イソホロンジイソシアネート、4,4’-ジシクロヘキシルメタンジイソシアネート、イソプロピリデンジシクロヘキシル-4,4’-ジイソシアネート等が挙げられる。 The curing agent is not particularly limited, and examples thereof include an isocyanate curing agent. Examples of the isocyanate include aliphatic isocyanates and aromatic isocyanates, but aliphatic isocyanates are preferable. The aliphatic isocyanate curing agent is a bifunctional or higher functional isocyanate compound having no aromatic ring. Since it does not have an aromatic ring, the benzene ring does not become quinoid due to ultraviolet rays, and yellowing can be suppressed, so that it is suitable for the outermost layer such as a coating layer. Examples of the aliphatic isocyanate curing agent include methylene diisocyanate, isopropylene diisocyanate, lysine diisocyanate, 2,2,4- or 2,4,4-trimethylhexamethylene diisocyanate, 1,6-hexamethylene diisocyanate, methylcyclohexanediisocyanate, and isophorone diisocyanate. , 4,4'-Dicyclohexylmethane diisocyanate, isopropyridene dicyclohexyl-4,4'-diisocyanate and the like.
これらの中でも、脂肪族イソシアネート硬化剤としては、電解液耐性が向上することから、1,6-ヘキサメチレンジイソシアネート、イソホロンジイソシアネートが好ましい。特に、硬化剤の自己修復性能が向上することに加え、硬化剤のイソシアネート基とアクリル樹脂及びポリエステル樹脂が有する水酸基との反応性に優れるという観点からは、1,6-ヘキサメチレンジイソシアネートが好ましい。これにより優れた量産適性も得ることができる。 Among these, 1,6-hexamethylene diisocyanate and isophorone diisocyanate are preferable as the aliphatic isocyanate curing agent because the resistance to the electrolytic solution is improved. In particular, 1,6-hexamethylene diisocyanate is preferable from the viewpoint of improving the self-repairing performance of the curing agent and excellent reactivity between the isocyanate group of the curing agent and the hydroxyl groups of the acrylic resin and the polyester resin. As a result, excellent mass production suitability can be obtained.
また、硬化剤としてイソシアネートのアダクト体、ビューレット体又はイソシアヌレート体を用いることで、形成されるコーティング層の架橋密度がより向上し、優れたアルコール耐性及び電解液耐性も得ることができる。 Further, by using an isocyanate body, a burette body or an isocyanurate body as a curing agent, the crosslink density of the formed coating layer is further improved, and excellent alcohol resistance and electrolytic solution resistance can be obtained.
コーティング層18の厚さは、0.05~3μmであることが好ましい。コーティング層18の厚さが0.05μm以上であることにより、アクリル系PSAテープとの十分な密着性を得易く、3μm以下であることにより、コーティング層を設けたとしても、絞り成型性の低下を抑制し易くなる。
The thickness of the
[外装材の製造方法]
次に、外装材10の製造方法について説明する。なお、外装材10の製造方法は以下の方法に限定されない。
[Manufacturing method of exterior materials]
Next, a method for manufacturing the
外装材10の製造方法として、例えば、下記の工程S11~S14を有する方法が挙げられる。
工程S11:金属箔層14の一方の面上に腐食防止処理層15aを形成し、金属箔層14の他方の面上に腐食防止処理層15bを形成する工程。
工程S12:基材層11の一方の面上に易接着処理層12を形成し、積層体を得る工程。工程S13:腐食防止処理層15aの金属箔層14とは反対側の面と、上記積層体の易接着処理層12側の面とを、接着層13を介して貼り合わせる工程。
工程S14:腐食防止処理層15bの金属箔層14とは反対側の面上に、シーラント接着層16を介してシーラント層17を形成する工程。
工程S15:基材層11の易接着処理層12とは反対側の面に、コーティング層18を形成する工程。
As a method for manufacturing the
Step S11: A step of forming a corrosion
Step S12: A step of forming the easy-adhesion-treated
Step S14: A step of forming the
Step S15: A step of forming the
(工程S11)
工程S11では、金属箔層14の一方の面上に腐食防止処理層15aを形成し、金属箔層14の他方の面上に腐食防止処理層15bを形成する。腐食防止処理層15a及び15bは、それぞれ別々に形成されてもよく、両方が一度に形成されてもよい。具体的には、例えば、金属箔層14の両方の面に腐食防止処理剤(腐食防止処理層の母材)を塗布し、その後、乾燥、硬化、焼付けを順次行うことで、腐食防止処理層15a及び15bを一度に形成する。また、金属箔層14の一方の面に腐食防止処理剤を塗布し、乾燥、硬化、焼き付けを順次行って腐食防止処理層15aを形成した後、金属箔層14の他方の面に同様にして腐食防止処理層15bを形成してもよい。腐食防止処理層15a及び15bの形成順序は特に制限されない。また、腐食防止処理剤は、腐食防止処理層15aと腐食防止処理層15bとで異なるものを用いてもよく、同じのものを用いてもよい。上記腐食防止処理剤としては、例えば、塗布型クロメート処理用の腐食防止処理剤等を用いることができる。腐食防止処理剤の塗布方法は、特に限定されないが、例えば、グラビアコート法、グラビアリバースコート法、ロールコート法、リバースロールコート法、ダイコート法、バーコート法、キスコート法、コンマコート法等の方法を用いることができる。なお、金属箔層14として、未処理の金属箔層を用いてもよいし、ウェットタイプの脱脂処理又はドライタイプの脱脂処理により、脱脂処理を施した金属箔層を用いてもよい。
(Step S11)
In step S11, the corrosion
(工程S12)
工程S12では、基材層11の一方の面上に易接着処理層12を形成する。ここでは、易接着処理層12の形成方法の一例として、インラインコート法について説明する。始めに、易接着処理層12の主成分となる上記樹脂を分散剤で分散させた分散体を含有する水性塗布液を準備する。次いで、結晶配向が完了する前の熱可塑性樹脂フィルム(基材層11の母材)の一方の面に、上記水性塗布液を塗布する。次いで、塗布された上記水性塗布液を乾燥させ、その後、熱可塑性樹脂フィルムを少なくとも一軸方向に延伸させる。
(Step S12)
In step S12, the easy-adhesion-treated
次いで、熱処理により、熱可塑性樹脂フィルムの配向を完了させることで、基材層11の一方の面上に易接着処理層12が形成された積層体が得られる。このようなインラインコート法を用いて易接着処理層12を形成することで、基材層11と易接着処理層12との間の密着性が向上する。なお、易接着処理層12の形成方法は、上記方法に限定されることなく、いかなる方法を用いてもよい。また、易接着処理層12を形成するタイミングは、本実施の形態に限定されない。
Then, by completing the orientation of the thermoplastic resin film by heat treatment, a laminated body in which the easy-adhesion-treated
(工程S13)
工程S13では、腐食防止処理層15aの金属箔層14とは反対側の面と、上記積層体の易接着処理層12側の面とが、接着層13を形成する接着剤を用いてドライラミネーション等の手法で貼り合わせられる。工程S13では、接着性の促進のため、室温~100℃の範囲でエージング(養生)処理を行ってもよい。エージング時間は、例えば、1~10日である。
(Step S13)
In step S13, the surface of the corrosion
(工程S14)
工程S13後、基材層11、易接着処理層12、接着層13、腐食防止処理層15a、金属箔層14及び腐食防止処理層15bがこの順に積層された積層体の腐食防止処理層15bの金属箔層14とは反対側の面上に、シーラント接着層16を介してシーラント層17が形成される。シーラント層17は、ドライラミネーション及びサンドイッチラミネーション等によって積層されてもよく、シーラント接着層16とともに共押出し法によって積層されてもよい。シーラント層17は、接着性向上の点から、例えばサンドイッチラミネーションによって積層される、又は、シーラント接着層16とともに共押出し法によって積層されることが好ましく、サンドイッチラミネーションによって積層されることがより好ましい。
(Step S14)
After the step S13, the corrosion
(工程S15)
工程S14後、基材層11、易接着処理層12、接着層13、腐食防止処理層15a、金属箔層14、腐食防止処理層15b、シーラント接着層16及びシーラント層17がこの順に積層された積層体の、基材層11の易接着処理層12とは反対側の面上に、コーティング層18が形成される。形成方法は特に限定されないが、例えば、グラビアコート法、グラビアリバースコート法、ロールコート法、リバースロールコート法、ダイコート法、バーコート法、キスコート法、コンマコート法等が挙げられる。
(Step S15)
After step S14, the
以上説明した工程S11~S15により、外装材10が得られる。なお、外装材10の製造方法の工程順序は、上記工程S11~S15を順次実施する方法に限定されない。例えば、工程S12を行ってから工程S11を行う等、実施する工程の順序を適宜変更してもよい。
The
[蓄電装置]
次に、外装材10を容器として備える蓄電装置について説明する。蓄電装置は、電極を含む電池要素1と、上記電極から延在するリード2と、リード2を挟持しかつ電池要素1を収容する容器とを備え、上記容器は蓄電装置用外装材10から、シーラント層17が内側となるように形成される。上記容器は、2つの外装材をシーラント層17同士を対向させて重ね合わせ、重ねられた外装材10の周縁部を熱融着して得られてもよく、また、1つの外装材を折り返して重ね合わせ、同様に外装材10の周縁部を熱融着して得られてもよい。また、蓄電装置は、外装材20を容器として備えていてもよい。蓄電装置としては、例えば、リチウムイオン電池、ニッケル水素電池、及び鉛蓄電池等の二次電池、並びに電気二重層キャパシタ等の電気化学キャパシタが挙げられる。
[Power storage device]
Next, a power storage device including the
リード2は、シーラント層17を内側として容器を形成する外装材10によって挟持され、密封されている。リード2は、タブシーラントを介して、外装材10によって挟持されていてもよい。
The
[蓄電装置の製造方法]
次に、上述した外装材10を用いて蓄電装置を製造する方法について説明する。なお、ここでは、エンボスタイプ外装材30を用いて二次電池40を製造する場合を例に挙げて説明する。図2は上記エンボスタイプ外装材30を示す図である。図3の(a)~(d)は、外装材10を用いた片側成型加工電池の製造工程を示す斜視図である。二次電池40としては、エンボスタイプ外装材30のような外装材を2つ設け、このような外装材同士を、アライメントを調整しつつ、貼り合わせて製造される、両側成型加工電池であってもよい。また、エンボスタイプ外装材30は、外装材20を用いて形成されてもよい。
[Manufacturing method of power storage device]
Next, a method of manufacturing a power storage device using the above-mentioned
片側成型加工電池である二次電池40は、例えば、以下の工程S21~S25により製造することができる。
工程S21:外装材10、電極を含む電池要素1、並びに上記電極から延在するリード2を準備する工程。
工程S22:外装材10の片面に電池要素1を配置するための凹部32を形成する工程(図3(a)及び図3(b)参照)。
工程S23:エンボスタイプ外装材30の成型加工エリア(凹部32)に電池要素1を配置し、凹部32を蓋部34が覆うようにエンボスタイプ外装材30を折り返し重ねて、電池要素1から延在するリード2を挟持するようにエンボスタイプ外装材30の一辺を加圧熱融着する工程(図3(b)及び図3(c)参照)。
工程S24:リード2を挟持する辺以外の一辺を残し、他の辺を加圧熱融着し、その後、残った一辺から電解液を注入し、真空状態で残った一辺を加圧熱融着する工程(図3(c)参照)。
工程S25:リード2を挟持する辺以外の加圧熱融着辺端部をカットし、成型加工エリア(凹部32)側に折り曲げる工程(図3(d)参照)。
The
Step S21: A step of preparing an
Step S22: A step of forming a
Step S23: The
Step S24: One side other than the side holding the
Step S25: A step of cutting a pressurized heat-sealed side end portion other than the side holding the
(工程S21)
工程S21では、外装材10、電極を含む電池要素1、並びに上記電極から延在するリード2を準備する。外装材10は、上述した実施形態に基づき準備する。電池要素1及びリード2としては特に制限はなく、公知の電池要素1及びリード2を用いることができる。
(Step S21)
In step S21, the
(工程S22)
工程S22では、外装材10のシーラント層17側に電池要素1を配置するための凹部32が形成される。凹部32の平面形状は、電池要素1の形状に合致する形状、例えば平面視矩形状とされる。凹部32は、例えば矩形状の圧力面を有する押圧部材を、外装材10の一部に対してその厚み方向に押圧することで形成される。また、押圧する位置、すなわち凹部32は、長方形に切り出した外装材10の中央より、外装材10の長手方向の一方の端部に偏った位置に形成する。これにより、成型加工後に凹部32を形成していないもう片方の端部側を折り返し、蓋(蓋部34)とすることができる。
(Step S22)
In step S22, a
凹部32を形成する方法としてより具体的には、金型を用いた成型加工(深絞り成型)が挙げられる。成型方法としては、外装材10の厚さ以上のギャップを有するように配置された雌型と雄型の金型を用い、雄型の金型を外装材10とともに雌型の金型に押し込む方法が挙げられる。雄型の金型の押込み量を調整することで、凹部32の深さ(深絞り量)を所望の量に調整できる。外装材10に凹部32が形成されることにより、エンボスタイプ外装材30が得られる。このエンボスタイプ外装材30は、例えば図2に示すような形状を有している。ここで、図2(a)は、エンボスタイプ外装材30の斜視図であり、図2(b)は、図2(a)に示すエンボスタイプ外装材30のb-b線に沿った縦断面図である。
More specifically, as a method of forming the
(工程S23)
工程S23では、エンボスタイプ外装材30の成型加工エリア(凹部32)内に、正極、セパレータ及び負極等から構成される電池要素1が配置され。また、電池要素1から延在し、正極と負極にそれぞれ接合されたリード2が成型加工エリア(凹部32)から外に引き出される。その後、エンボスタイプ外装材30は、長手方向の略中央で折り返され、シーラント層17同士が内側となるように重ねられ、エンボスタイプ外装材30のリード2を挟持する一辺が加圧熱融着される。加圧熱融着は、温度、圧力及び時間の3条件で制御され、適宜設定される。加圧熱融着の温度は、シーラント層17を融解する温度以上であることが好ましい。
(Step S23)
In step S23, the
なお、シーラント層17の熱融着前の厚さは、リード2の厚さに対し40~80%であることが好ましい。シーラント層17の厚さが上記下限値以上であることにより、熱融着樹脂がリード2端部を十分充填できる傾向があり、上記上限値以下であることにより、二次電池40の外装材10端部の厚さを適度に抑えることができ、外装材10端部からの水分の浸入量を低減することができる。
The thickness of the
(工程S24)
工程S24では、リード2を挟持する辺以外の一辺を残し、他の辺の加圧熱融着が行われる。その後、残った一辺から電解液を注入し、残った一辺が真空状態で加圧熱融着される。加圧熱融着の条件は工程S23と同様である。
(Step S24)
In step S24, pressure heat fusion is performed on the other side, leaving one side other than the side holding the
(工程S25)
リード2を挟持する辺以外の周縁加圧熱融着辺端部がカットされ、端部からははみだしたシーラント層17が除去される。その後、周縁加圧熱融着部を成型加工エリア32側に折り返し、折り返し部42を形成することで、二次電池40が得られる。
(Step S25)
The peripheral pressure heat fusion side end portion other than the side holding the
以上、本発明の蓄電装置用外装材及び蓄電装置の製造方法の好ましい実施の形態について詳述したが、本発明はかかる特定の実施の形態に限定されるものではなく、特許請求の範囲内に記載された本発明の要旨の範囲内において、種々の変形・変更が可能である。 Although the preferred embodiment of the exterior material for the power storage device and the method for manufacturing the power storage device of the present invention has been described in detail above, the present invention is not limited to such a specific embodiment and is within the scope of the claims. Various modifications and changes are possible within the scope of the described gist of the present invention.
以下、実施例に基づいて本発明をより具体的に説明するが、本発明は以下の実施例に限定されるものではない。 Hereinafter, the present invention will be described in more detail based on Examples, but the present invention is not limited to the following Examples.
(基材層の用意)
基材層11として、表1の特性を有するポリエステルフィルム(いずれも厚さ25μm)を準備した。表1中、50%伸長時応力値及び熱収縮率は、それぞれ次のようにして測定した。
50%伸長時応力値(F50応力値):A4サイズにカットした各ポリエステルフィルムを、160~200℃の範囲内の任意の熱処理温度に保たれたオーブン中で30分間加熱した。その後、当該ポリエステルフィルムの4方向(0°(MD)、45°、90°(TD)、135°)に対し、引張試験(試験片形状:JIS K7127に規定される5号型ダンベル状、チャック間距離:75mm、標点間距離:25mm、試験速度:50mm/min、温度:23℃)を行った。そして、4方向に対する測定結果の平均を取ることで、50%伸長時応力値を算出した。
熱収縮率:23℃にてA4サイズにカットした各ポリエステルフィルムを、160~200℃の範囲内の任意の熱処理温度に保たれたオーブン中で30分間加熱した。その後、当該ポリエステルフィルムの4方向(0°(MD)、45°、90°(TD)、135°)の、23℃における長さを測定した。そして、下記式に従い各方向に対する熱収縮率を算出して、その平均値をとることで、熱収縮率を算出した。
熱収縮率(%)=[{熱処理前に測定された各方向の長さ(A4サイズ)-熱処理後に測定された各方向の長さ}/熱処理前に測定された各方向の長さ]×100
(Preparation of base material layer)
As the
50% Elongation Stress Value (F50 Stress Value): Each polyester film cut to A4 size was heated in an oven maintained at an arbitrary heat treatment temperature in the range of 160 to 200 ° C. for 30 minutes. After that, a tensile test (test piece shape: No. 5 dumbbell-shaped, chuck specified in JIS K7127) was performed in four directions (0 ° (MD), 45 °, 90 ° (TD), 135 °) of the polyester film. Distance between points: 75 mm, distance between gauge points: 25 mm, test speed: 50 mm / min, temperature: 23 ° C.). Then, the stress value at the time of 50% elongation was calculated by taking the average of the measurement results in four directions.
Heat shrinkage: Each polyester film cut to A4 size at 23 ° C. was heated in an oven maintained at an arbitrary heat treatment temperature in the range of 160 to 200 ° C. for 30 minutes. Then, the length of the polyester film in four directions (0 ° (MD), 45 °, 90 ° (TD), 135 °) was measured at 23 ° C. Then, the heat shrinkage rate was calculated in each direction according to the following formula, and the heat shrinkage rate was calculated by taking the average value.
Heat shrinkage rate (%) = [{Length measured in each direction before heat treatment (A4 size) -Length measured in each direction after heat treatment} / Length in each direction measured before heat treatment] × 100
(実施例1)
金属箔層14として、厚さ40μmの軟質アルミニウム箔8079材(東洋アルミニウム株式会社製)を準備した。次いで、金属箔層14の両面に、グラビアコートにより、溶媒として蒸留水を使用し、かつ固形分濃度10質量%に調整したポリリン酸ナトリウム安定化酸化セリウムゾル(腐食防止処理剤)を塗布した。このとき、酸化セリウム100質量部に対して、リン酸は10質量部とした。
(Example 1)
As the
次いで、塗布されたポリリン酸ナトリウム安定化酸化セリウムゾルを乾燥させた後、焼付け処理を順次行うことで、金属箔層14の一方の面に腐食防止処理層15aを形成し、他方の面に腐食防止処理層15bを形成した。焼き付け条件は、温度を150℃、処理時間を30秒とした。
Next, the applied sodium polyphosphate-stabilized cerium oxide sol is dried, and then the baking treatment is sequentially performed to form a corrosion
次いで、基材層11として表1に示すポリエステルフィルムを用い、基材層11の片面をコロナ処理した。
Next, using the polyester film shown in Table 1 as the
次いで、金属箔層14の腐食防止処理層15aの金属箔層14とは反対側の面に、接着層13として、ポリウレタン系接着剤を塗布した。次いで、ドライラミネート法により、接着層13を介して、金属箔層14と基材層11のコロナ処理された面とを接着させた。その後、基材層11、接着層13、腐食防止処理層15a、金属箔層14、及び腐食防止処理層15bからなる構造体を、温度が60℃の雰囲気中で6日間放置することで、エージング処理した。
Next, a polyurethane-based adhesive was applied as the
次に、シーラント接着層16を、シーラント接着層16の母材となる無水マレイン酸変性ポリプロピレン(三井化学社製、商品名:アドマー)を押出すことで形成した。このとき、シーラント接着層16の厚さは15μmとした。そして、熱ラミネーション装置を用いたサンドイッチラミネーション法により、シーラント接着層16を介して、腐食防止処理層15bに、シーラント層17となる厚さ30μmのポリオレフィンフィルム(無延伸ポリプロピレンフィルムのシーラント接着層16側の面をコロナ処理したフィルム)を160℃で張り合わせた(加熱圧着した)。これを巻き取ることで、ロール状の蓄電装置用外装材10を作製した。
Next, the
(実施例2、比較例1~6)
表1に記載のポリエステルフィルムを使用したこと以外は、実施例1と同様にして、蓄電装置用外装材10を作製した。
(Example 2, Comparative Examples 1 to 6)
The
(実施例3)
基材層11の片面をコロナ処理する代わりに基材層11の接着層13側の面に易接着処理層12を形成したこと以外は、実施例1と同様にして、蓄電装置用外装材10を作製した。易接着処理層12は、インラインコート法を用いて、基材層11の片面に、以下のとおり調製した易接着処理層12の母材となる塗工剤を固形分で0.1g/m2となるように塗工し、乾燥させることで形成した。易接着処理層12の厚さは約0.1μmであった。
(易接着処理層形成用塗工剤の調製)
易接着処理層形成用塗工剤として、下記組成の塗工剤を調製した。
塗工剤:東亞合成株式会社製の水溶性ポリエステル「アロンメルトPES-1000」に、ニホンポリウレタン工業株式会社製の自己乳化型ポリイソシアネート「アクアネート100」および日本触媒化学工業株式会社製の真球状シリカ微粒子「シーホスターKE-P30」(平均粒子径0.3μm)を95/5/0.5の配合比(質量比)で加え、水で希釈した。
(Example 3)
The
(Preparation of coating agent for forming an easy-adhesion treatment layer)
A coating agent having the following composition was prepared as a coating agent for forming an easy-adhesion-treated layer.
Coating agent: Water-soluble polyester "Aronmelt PES-1000" manufactured by Toa Synthetic Co., Ltd., self-emulsifying polyisocyanate "Aquanate 100" manufactured by Nihon Polyurethane Industry Co., Ltd., and spherical silica manufactured by Nippon Catalytic Chemical Industry Co., Ltd. Fine particles "Seahoster KE-P30" (average particle size 0.3 μm) were added at a blending ratio (mass ratio) of 95/5 / 0.5 and diluted with water.
(実施例4)
ポリリン酸ナトリウム安定化酸化セリウムゾルを用いて腐食防止処理層15a及び15bを形成する代わりに、クロメート処理を行って腐食防止処理層15a及び15bを形成したこと以外は、実施例1と同様にして、蓄電装置用外装材10を作製した。なお、クロメート処理は、金属箔層14の両面にフェノール樹脂、フッ化クロム化合物、及びリン酸からなる処理液を塗布して被膜を形成し、焼付けすることにより行った。
(Example 4)
In the same manner as in Example 1, except that the corrosion prevention treatment layers 15a and 15b were formed by chromate treatment instead of forming the corrosion prevention treatment layers 15a and 15b using the sodium polyphosphate stabilized cerium oxide sol. An
(実施例5~8、比較例7~12)
ポリエステルポリオールに硬化剤としてIPDIのイソシアヌレート体を配合した樹脂組成物を基材層11上に塗布し、加熱硬化することにより、基材層11上に、厚さ1.0μmのポリエステル系樹脂からなるコーティング層を形成したこと以外は、それぞれ実施例1~4及び比較例1~6と同様にして、蓄電装置用外装材10を作製した。
(Examples 5 to 8, Comparative Examples 7 to 12)
A resin composition containing an IPDI isocyanurate as a curing agent in a polyester polyol is applied onto the
(実施例9~12、比較例13~18)
アクリルポリオールに硬化剤としてHDIのアダクト体を配合した樹脂組成物を、基材層11上に塗布し、加熱硬化することにより、基材層11上に、厚さ1.0μmのアクリル系樹脂からなるコーティング層を形成したこと以外は、それぞれ実施例1~4及び比較例1~6と同様にして、蓄電装置用外装材10を作製した。
(Examples 9 to 12, Comparative Examples 13 to 18)
A resin composition containing an HDI adduct body as a curing agent in an acrylic polyol is applied onto the
(参考例1~2)
コーティング層の厚さを4.0μmにしたこと以外は、それぞれ実施例5及び9と同様にして、蓄電装置用外装材10を作製した。
(Reference Examples 1 and 2)
The
<加工適性の評価>
熱ラミネーション装置を用いたサンドイッチラミネーション法により、シーラント接着層16を介して、腐食防止処理層15bに、シーラント層17を張り合わせ、これを巻き取る際の加工適性について、以下の基準にて評価した。
A:張り合わせ及び巻取りのいずれも良好に行えた。
B:張り合わせ又は巻取りが良好に行えなかった。
C:張り合わせ及び巻取りのいずれも良好に行えなかった。
<Evaluation of processing suitability>
The
A: Both laminating and winding were performed well.
B: Laminating or winding could not be performed well.
C: Neither laminating nor winding was performed well.
<成型深度の評価>
各実施例及び比較例で作製した蓄電装置用外装材10について、深絞り成型が可能な成型深度を以下の方法で評価した。まず、蓄電装置用外装材10を、シーラント層17が上方を向くように成型装置内に配置した。成型装置の成型深さを6.0mm又は6.5mmに設定し、室温23℃、露点温度-35℃の環境下で冷間成型した。なお、パンチ金型には、70mm×80mmの長方形の横断面を有し、底面に1.00mmのパンチラジアス(RP)を有し、側面に1.00mmのパンチコーナーラジアス(RCP)を有するものを使用した。また、ダイ金型には、開口部上面に1.00mmのダイラジアス(RD)を有するものを使用した。冷間成型を行った部分の破断及びピンホールの有無を、外装材10にライトを照射しながら目視にて確認し、以下の基準にて成型深度の最大値(成型限界)を評価した。結果を表2に示す。
A:成型深度6.5mmでは破断及びピンホールのいずれも生じなかった。
B:成型深度6.5mmでは破断又はピンホールが生じたものの、成型深度6.0mmでは破断及びピンホールのいずれも生じなかった。
C:成型深度6.0mmで破断又はピンホールが生じた。
<Evaluation of molding depth>
With respect to the
A: At a molding depth of 6.5 mm, neither breakage nor pinholes occurred.
B: Although breakage or pinholes occurred at a molding depth of 6.5 mm, neither breakage nor pinholes occurred at a molding depth of 6.0 mm.
C: Breakage or pinhole occurred at a molding depth of 6.0 mm.
<層間密着性の評価>
各実施例及び比較例で作製した蓄電装置用外装材10について、基材層11と金属箔層14との間の密着性を以下の方法で評価した。まず、蓄電装置用外装材10を、シーラント層17が上方を向くように成型装置内に配置した。成型装置の成型深さを5mmに設定し、室温23℃、露点温度-35℃の環境下で冷間成型した。なお、パンチ金型には、70mm×80mmの長方形の横断面を有し、底面に1.00mmのパンチラジアス(RP)を有し、側面に1.00mmのパンチコーナーラジアス(RCP)を有するものを使用した。また、ダイ金型には、開口部上面に1.00mmのダイラジアス(RD)を有するものを使用した。
<Evaluation of interlayer adhesion>
With respect to the
次いで、冷間成型した外装材10を、1M六フッ化リン酸リチウム溶液(溶媒体積比=炭酸エチル:炭酸ジメチル:炭酸ジメチル=1:1:1)30mLが入った100mL容量のビーカーに入れた。次いで、外装材10が入ったビーカーを一斗缶内に封入して40℃の温度環境下に2時間置くことで、外装材10を電解液にさらした。その後、一斗缶内のビーカーから外装材10を取り出し、110℃のオーブン内、温度60℃湿度95%の環境下、又は、50℃の温水中に入れた。そして、その後の経時における外装材10の基材層11と金属箔層14との間の剥離の有無を目視にて確認し、基材層11と金属箔層14との間に剥離が確認されなかった期間の最大値(単位:週)を求めた。その結果に基づき、以下の評価基準により基材層11と金属箔層14との間の密着性を評価した。結果を表2に示す。
A:4週間後でも剥離が確認されなかった。
B:4週間後には剥離が確認された。
Next, the cold-molded
A: No peeling was confirmed even after 4 weeks.
B: Peeling was confirmed after 4 weeks.
<PSAテープ密着性>
各実施例及び比較例で作製した蓄電装置用外装材10について、基材層11(又はコーティング層18)とアクリル系PSAテープとの密着性を以下の方法で評価した。まず、支持体に、基材層11(又はコーティング層18)側が上面となるように蓄電装置用外装材10を貼り付けた。次に、基材層11(又はコーティング層18)上に、アクリル系PSAテープと剥離試験用の支持アルミニウム箔とを約20Nの力で貼り付けた。これを約1時間静置した後、基材層11(又はコーティング層18)とアクリル系PSAテープとの剥離強度(180度剥離、剥離速度は50mm/分)を測定し、以下の評価基準により評価をした。結果を表2に示す。
○:剥離強度が10N/15mm以上であった。
×:剥離強度が10N/15mm未満であった。
<PSA tape adhesion>
With respect to the
◯: The peel strength was 10 N / 15 mm or more.
X: The peel strength was less than 10 N / 15 mm.
表2に示した結果から、本実施例によれば、作製時の加工適性と作製後の深絞り成型性とに優れる蓄電装置用外装材を提供できることが理解される。 From the results shown in Table 2, it is understood that according to this embodiment, it is possible to provide an exterior material for a power storage device having excellent processing suitability at the time of production and deep drawing moldability after production.
1…電池要素、2…リード、10…外装材(蓄電装置用外装材)、11…基材層、12…易接着処理層、13…接着層、14…金属箔層、15a,15b…腐食防止処理層、16…シーラント接着層、17…シーラント層、18…コーティング層、30…エンボスタイプ外装材、32…成型加工エリア(凹部)、34…蓋部、40…二次電池。
1 ... Battery element, 2 ... Lead, 10 ... Exterior material (exterior material for power storage device), 11 ... Base material layer, 12 ... Easy adhesive treatment layer, 13 ... Adhesive layer, 14 ... Metal foil layer, 15a, 15b ... Corrosion Prevention treatment layer, 16 ... sealant adhesive layer, 17 ... sealant layer, 18 ... coating layer, 30 ... embossed type exterior material, 32 ... molding processing area (recess), 34 ... lid, 40 ... secondary battery.
Claims (10)
前記基材層は、160~200℃での熱処理後の、50%伸長時応力値が100~180MPaであり且つ熱収縮率が1~15%であるポリエステルフィルムからなる、蓄電装置用外装材。
50%伸長時応力値:基材層の4方向(0°(MD)、45°、90°(TD)、135°)に対し引張試験(試験片形状:JIS K7127に規定される5号型ダンベル状、チャック間距離:75mm、標点間距離:25mm、試験速度:50mm/min、温度:23℃)を行ったときの応力値の平均値である。
熱収縮率:基材層の4方向(0°(MD)、45°、90°(TD)、135°)に対する、熱処理前後での収縮率の平均値である。 It has a structure in which at least a base material layer, an adhesive layer, a metal foil layer, a sealant adhesive layer and a sealant layer are laminated in this order.
The base material layer is an exterior material for a power storage device, which is made of a polyester film having a stress value at 50% elongation of 100 to 180 MPa and a heat shrinkage rate of 1 to 15% after heat treatment at 160 to 200 ° C.
Stress value at 50% elongation: Tensile test (test piece shape: No. 5 type specified in JIS K7127) for 4 directions (0 ° (MD), 45 °, 90 ° (TD), 135 °) of the base material layer. It is an average value of stress values when dumbbell-shaped, distance between chucks: 75 mm, distance between gauge points: 25 mm, test speed: 50 mm / min, temperature: 23 ° C.).
Heat shrinkage rate: The average value of the shrinkage rate before and after the heat treatment in four directions (0 ° (MD), 45 °, 90 ° (TD), 135 °) of the base material layer.
前記金属箔層の前記接着層とは反対側の面に、シーラント接着層を介してシーラント層を形成する工程、を備え、
前記基材層は、160~200℃での熱処理後の、50%伸長時応力値が100~180MPaであり且つ熱収縮率が1~15%であるポリエステルフィルムからなる、
蓄電装置用外装材の製造方法。
50%伸長時応力値:基材層の4方向(0°(MD)、45°、90°(TD)、135°)に対し引張試験(試験片形状:JIS K7127に規定される5号型ダンベル状、チャック間距離:75mm、標点間距離:25mm、試験速度:50mm/min、温度:23℃)を行ったときの応力値の平均値である。
熱収縮率:基材層の4方向(0°(MD)、45°、90°(TD)、135°)に対する、熱処理前後での収縮率の平均値である。
The step of adhering the base material layer to one surface of the metal foil layer via the adhesive layer, and forming the sealant layer via the sealant adhesive layer on the surface of the metal foil layer opposite to the adhesive layer. With the process,
The base material layer is made of a polyester film having a stress value at 50% elongation of 100 to 180 MPa and a heat shrinkage rate of 1 to 15% after heat treatment at 160 to 200 ° C.
A method for manufacturing exterior materials for power storage devices.
Stress value at 50% elongation: Tensile test (test piece shape: No. 5 type specified in JIS K7127) for 4 directions (0 ° (MD), 45 °, 90 ° (TD), 135 °) of the base material layer. It is an average value of stress values when dumbbell-shaped, distance between chucks: 75 mm, distance between gauge points: 25 mm, test speed: 50 mm / min, temperature: 23 ° C.).
Heat shrinkage rate: The average value of the shrinkage rate before and after the heat treatment in four directions (0 ° (MD), 45 °, 90 ° (TD), 135 °) of the base material layer.