JP2022042200A - Friction member, friction material composition, friction material, and vehicle - Google Patents
Friction member, friction material composition, friction material, and vehicle Download PDFInfo
- Publication number
- JP2022042200A JP2022042200A JP2020147510A JP2020147510A JP2022042200A JP 2022042200 A JP2022042200 A JP 2022042200A JP 2020147510 A JP2020147510 A JP 2020147510A JP 2020147510 A JP2020147510 A JP 2020147510A JP 2022042200 A JP2022042200 A JP 2022042200A
- Authority
- JP
- Japan
- Prior art keywords
- friction material
- fiber
- friction
- mass
- calcium sulfate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、摩擦部材、摩擦材組成物、摩擦材及び車両に関する。 The present invention relates to friction members, friction material compositions, friction materials and vehicles.
自動車等には、その制動のためにディスクブレーキパッド、ブレーキライニング等の摩擦材が使用されている。摩擦材は、ディスクロータ、ブレーキドラム等の対面材と摩擦することにより、制動の役割を果たす。そのため、摩擦材には、良好な摩擦係数、耐摩耗性（摩擦材の寿命が長いこと）等が要求される。 Friction materials such as disc brake pads and brake linings are used for braking in automobiles and the like. The friction material plays a role of braking by rubbing against a facing material such as a disc rotor and a brake drum. Therefore, the friction material is required to have a good friction coefficient, wear resistance (the life of the friction material is long), and the like.
摩擦材は繊維基材としてスチール繊維を３０～６０質量％含有するセミメタリック材と、スチール繊維を３０質量％未満含有するロースチール材と、スチール繊維を含有しないＮＡО（Non Asbestos Organic）材に大別される。ロースチール材、ＮＡＯ材等のスチール繊維の含有量が低い摩擦材は、相手材であるディスクロータへの攻撃性が低いため、ディスクロータの摩耗を抑制し、ブレーキ鳴きの発生を抑制できるという特徴を有する。一方、ロースチール材、ＮＡＯ材等は、スチール繊維の含有量が低いため、制動性能を十分に確保することが難しく、それを補うために、高温高速制動時の摩擦係数の低下抑制に高い効果を発揮する銅粉末、銅繊維等が使用されてきた。 Friction materials are large for semi-metallic materials containing 30 to 60% by mass of steel fibers as fiber base materials, low steel materials containing less than 30% by mass of steel fibers, and NAО (Non Asbestos Organic) materials containing no steel fibers. Be separated. Friction materials with a low content of steel fibers such as low steel material and NAO material have low aggression to the disc rotor, which is the mating material, and thus can suppress wear of the disc rotor and suppress the occurrence of brake squeal. Has. On the other hand, low steel materials, NAO materials, etc. have a low content of steel fibers, so it is difficult to secure sufficient braking performance. Copper powder, copper fiber, etc. have been used.
しかしながら、近年では、銅、銅合金等を含有する摩擦材は、制動時に発生する摩耗粉中に銅を含むため、河川、湖等を汚染する可能性が示唆されている。銅は、繊維、粉末等の形態で摩擦材に配合され、熱伝導率の付与に有効な成分である。銅を含有しない組成においては、熱伝導率が低下するため、高温での制動時に摩擦界面の熱が拡散せずに摩擦材の摩耗量が増大したり、制動時における分解ガスの量が多くなり耐フェード性が悪化したりするという問題が生じていた。 However, in recent years, it has been suggested that friction materials containing copper, copper alloys, etc. may contaminate rivers, lakes, etc. because copper is contained in the wear debris generated during braking. Copper is blended in the friction material in the form of fibers, powder, etc., and is an effective component for imparting thermal conductivity. In a composition that does not contain copper, the thermal conductivity decreases, so the heat at the friction interface does not diffuse during braking at high temperatures, increasing the amount of wear of the friction material and increasing the amount of decomposition gas during braking. There was a problem that the fade resistance deteriorated.
耐フェード性を向上させた摩擦材として、基材としてのロックウールを多めに含有させて気孔率を確保した摩擦材（例えば、特許文献１参照）が提案されている。
また、銅を含有しない組成において、高温高負荷での制動における耐摩耗性、摩擦係数の安定性を向上させた摩擦材として、鱗片状、柱状又は板状のトンネル状結晶構造のチタン酸塩と層状結晶構造のチタン酸塩とを併用した摩擦材（例えば、特許文献２参照）が提案されている。
As a friction material having improved fade resistance, a friction material in which a large amount of rock wool as a base material is contained to secure a porosity (see, for example, Patent Document 1) has been proposed.
In addition, as a friction material with improved wear resistance and friction coefficient stability during braking at high temperature and high load in a composition that does not contain copper, titanate having a scaly, columnar or plate-like tunnel-like crystal structure is used. A friction material (see, for example, Patent Document 2) in combination with a titanate having a layered crystal structure has been proposed.
特許文献１に記載の技術は耐フェード性の向上、特許文献２に記載の技術は銅を含有しない組成において、高温高速制動時の耐摩耗性、摩擦係数の安定性の向上を図ったものである。しかしながら、これらの摩擦材においても、耐フェード性と高温高速制動時の耐摩耗性との両立は未だ十分とは言えない。
The technique described in Patent Document 1 is intended to improve fade resistance, and the technique described in
本発明は、上記事情に鑑みなされたものであり、銅の含有量が０．５質量％未満、かつ、スチール繊維の含有量が２５質量％以下であっても、フェード時の摩擦係数と高温高速制動時の耐摩耗性が良好な摩擦材を有する摩擦部材、前記摩擦材を提供し得る摩擦材組成物、前記摩擦材、及び前記摩擦部材又は前記摩擦材を搭載した車両を提供することを課題とする。 The present invention has been made in view of the above circumstances, and even if the copper content is less than 0.5% by mass and the steel fiber content is 25% by mass or less, the friction coefficient at the time of fading and the high temperature are high. Provided are a friction member having a friction material having good wear resistance at high speed braking, a friction material composition capable of providing the friction material, the friction material, and a vehicle equipped with the friction member or the friction material. Make it an issue.
本発明者等は、上記目的を達成するために鋭意研究を重ねた結果、下記の本発明により当該課題を解決できることを見出した。すなわち、本発明は、下記［１］～［１５］に関する。
［１］摩擦材及び裏金を有する摩擦部材であって、
前記摩擦材は、銅の含有量が、前記摩擦材全量に対して０．５質量％未満、かつ、スチール繊維の含有量が、前記摩擦材全量に対して２５質量％以下であり、硫酸カルシウム繊維を、前記摩擦材全量に対して、１～２０質量％含有する、摩擦部材。
［２］前記硫酸カルシウム繊維の平均繊維長が、１～２００μｍである、上記［１］に記載の摩擦部材。
［３］前記硫酸カルシウム繊維の平均繊維径が、０．１～２０μｍである、上記［１］又は［２］に記載の摩擦部材。
［４］前記硫酸カルシウム繊維の平均アスペクト比（繊維長／繊維径）が、５～２００である、上記［１］～［３］のいずれかに記載の摩擦部材。
［５］前記硫酸カルシウム繊維が、II型無水石膏からなる繊維である、上記［１］～［４］のいずれかに記載の摩擦部材。
［６］前記摩擦材が、さらに、チタン酸塩を、前記摩擦材全量に対して、２～４０質量％含有する、上記［１］～［５］のいずれかに記載の摩擦部材。
［７］上記［１］～［６］のいずれかに記載の摩擦部材を搭載した車両。
［８］銅の含有量が０．５質量％未満、かつ、スチール繊維の含有量が２５質量％以下である摩擦材組成物であって、硫酸カルシウム繊維を、１～２０質量％含有する、摩擦材組成物。
［９］前記硫酸カルシウム繊維の平均繊維長が、１～２００μｍである、上記［８］に記載の摩擦材組成物。
［１０］前記硫酸カルシウム繊維の平均繊維径が、０．１～２０μｍである、上記［８］又は［９］に記載の摩擦材組成物。
［１１］前記硫酸カルシウム繊維の平均アスペクト比（繊維長／繊維径）が、５～２００である、上記［８］～［１０］のいずれかに記載の摩擦材組成物。
［１２］前記硫酸カルシウム繊維が、II型無水石膏からなる繊維である、上記［８］～［１１］のいずれかに記載の摩擦材組成物。
［１３］さらに、チタン酸塩を、２～４０質量％含有する、上記［８］～［１２］のいずれかに記載の摩擦材組成物。
［１４］上記［８］～［１３］のいずれかに記載の摩擦材組成物を含有してなる摩擦材。
［１５］上記［１４］に記載の摩擦材を搭載した車両。
As a result of diligent research to achieve the above object, the present inventors have found that the following invention can solve the problem. That is, the present invention relates to the following [1] to [15].
[1] A friction member having a friction material and a slush fund.
The friction material has a copper content of less than 0.5% by mass with respect to the total amount of the friction material, a steel fiber content of 25% by mass or less with respect to the total amount of the friction material, and calcium sulfate. A friction member containing 1 to 20% by mass of fibers with respect to the total amount of the friction material.
[2] The friction member according to the above [1], wherein the average fiber length of the calcium sulfate fiber is 1 to 200 μm.
[3] The friction member according to the above [1] or [2], wherein the calcium sulfate fiber has an average fiber diameter of 0.1 to 20 μm.
[4] The friction member according to any one of the above [1] to [3], wherein the average aspect ratio (fiber length / fiber diameter) of the calcium sulfate fiber is 5 to 200.
[5] The friction member according to any one of [1] to [4] above, wherein the calcium sulfate fiber is a fiber made of type II anhydrous gypsum.
[6] The friction member according to any one of [1] to [5] above, wherein the friction material further contains titanium salt in an amount of 2 to 40% by mass with respect to the total amount of the friction material.
[7] A vehicle equipped with the friction member according to any one of the above [1] to [6].
[8] A friction material composition having a copper content of less than 0.5% by mass and a steel fiber content of 25% by mass or less, which contains 1 to 20% by mass of calcium sulfate fibers. Friction material composition.
[9] The friction material composition according to the above [8], wherein the calcium sulfate fiber has an average fiber length of 1 to 200 μm.
[10] The friction material composition according to the above [8] or [9], wherein the calcium sulfate fiber has an average fiber diameter of 0.1 to 20 μm.
[11] The friction material composition according to any one of the above [8] to [10], wherein the average aspect ratio (fiber length / fiber diameter) of the calcium sulfate fiber is 5 to 200.
[12] The friction material composition according to any one of [8] to [11] above, wherein the calcium sulfate fiber is a fiber made of type II anhydrous gypsum.
[13] The friction material composition according to any one of the above [8] to [12], further containing 2 to 40% by mass of titanate.
[14] A friction material containing the friction material composition according to any one of the above [8] to [13].
[15] A vehicle equipped with the friction material according to the above [14].
本発明によれば、銅の含有量が０．５質量％未満、かつ、スチール繊維の含有量が２５質量％以下であっても、フェード時の摩擦係数と高温高速制動時の耐摩耗性が良好な摩擦材を有する摩擦部材、前記摩擦材を提供し得る摩擦材組成物、前記摩擦材、及び前記摩擦部材又は前記摩擦材を搭載した車両を提供することができる。 According to the present invention, even if the copper content is less than 0.5% by mass and the steel fiber content is 25% by mass or less, the friction coefficient at the time of fading and the wear resistance at the time of high temperature and high speed braking are obtained. It is possible to provide a friction member having a good friction material, a friction material composition capable of providing the friction material, the friction material, and a vehicle equipped with the friction member or the friction material.
以下、本発明の実施形態に係る摩擦部材、摩擦材組成物、摩擦材及び車両について詳細に説明する。但し、以下の実施形態において、その構成要素は、特に明示した場合を除き、必須ではない。数値及びその範囲についても同様であり、本発明を制限するものではない。 Hereinafter, the friction member, the friction material composition, the friction material, and the vehicle according to the embodiment of the present invention will be described in detail. However, in the following embodiments, the components are not essential unless otherwise specified. The same applies to the numerical values and their ranges, and does not limit the present invention.
本明細書中に記載されている数値範囲において、その数値範囲の上限値又は下限値は、実施例に示されている値に置き換えてもよい。さらに、本明細書において、摩擦材及び摩擦材組成物中の各成分の含有率は、各成分に該当する物質が複数種存在する場合には、特に断らない限り、摩擦材及び摩擦材組成物中に存在する当該複数種の物質の合計の含有率を意味する。
本明細書における記載事項を任意に組み合わせた態様も本発明に含まれる。
In the numerical range described in the present specification, the upper limit value or the lower limit value of the numerical range may be replaced with the value shown in the examples. Further, in the present specification, the content of each component in the friction material and the friction material composition is the friction material and the friction material composition unless otherwise specified, when a plurality of substances corresponding to the respective components are present. It means the total content of the multiple substances present in the substance.
The present invention also includes aspects in which the items described in the present specification are arbitrarily combined.
［摩擦部材、摩擦材、摩擦材組成物］
本実施形態に係る摩擦部材は、摩擦材及び裏金を有する摩擦部材であって、前記摩擦材は、銅の含有量が、前記摩擦材全量に対して０．５質量％未満、かつ、スチール繊維の含有量が、前記摩擦材全量に対して２５質量％以下であり、硫酸カルシウム繊維を、前記摩擦材全量に対して、１～２０質量％含有するものである。
[Friction member, friction material, friction material composition]
The friction member according to the present embodiment is a friction member having a friction material and a back metal, and the friction material has a copper content of less than 0.5% by mass with respect to the total amount of the friction material and is a steel fiber. Is 25% by mass or less with respect to the total amount of the friction material, and calcium sulfate fibers are contained in an amount of 1 to 20% by mass with respect to the total amount of the friction material.
本実施形態に係る摩擦材組成物は、銅の含有量が０．５質量％未満、かつ、スチール繊維の含有量が２５質量％以下である摩擦材組成物であって、硫酸カルシウム繊維を１～２０質量％含有するものであり、本実施形態の摩擦材は、本実施形態の摩擦材組成物を含有してなる摩擦材である。 The friction material composition according to the present embodiment is a friction material composition having a copper content of less than 0.5% by mass and a steel fiber content of 25% by mass or less, and contains calcium sulfate fiber of 1. The friction material of the present embodiment contains up to 20% by mass, and is a friction material containing the friction material composition of the present embodiment.
以下、本実施形態の摩擦部材が有する摩擦材、及び本実施形態の摩擦材組成物を含有してなる摩擦材（以下の説明においては、両者を「本実施形態の摩擦材」と称する。）について詳細に説明する。なお、本実施形態の摩擦材組成物に含有される各成分の種類、及びその製造方法は、下記の本実施形態の摩擦材と同様に説明されるものであり、その好適な態様もすべて同じである。摩擦材組成物中における各成分の含有量の好適範囲は、本実施形態の摩擦材で説明される好適範囲と同じであるが、含有量の基準は「摩擦材組成物全量」とする。 Hereinafter, the friction material contained in the friction member of the present embodiment and the friction material containing the friction material composition of the present embodiment (in the following description, both are referred to as "friction material of the present embodiment"). Will be described in detail. The types of each component contained in the friction material composition of the present embodiment and the method for producing the same are described in the same manner as the friction material of the present embodiment below, and all the preferred embodiments thereof are also the same. Is. The preferable range of the content of each component in the friction material composition is the same as the preferable range described by the friction material of the present embodiment, but the standard of the content is "the total amount of the friction material composition".
＜銅＞
本実施形態の摩擦材は、銅の含有量が、摩擦材全量に対して、０．５質量％未満である。
なお、本明細書において、「銅の含有量が、摩擦材全量に対して、０．５質量％未満」であるとは、銅の含有量が０質量％である場合も含む。
なお、上記の「銅」とは、例えば、繊維状、粉末状等の銅；銅合金、銅化合物などに含まれる銅元素である。
本実施形態の摩擦材が銅を含有する場合、その含有量は、摩擦材全量に対して、０．３質量％以下が好ましく、０．１質量％以下がより好ましく、０．０５質量％以下がさらに好ましい。
本実施形態の摩擦材は銅を含有しないものであってもよい。但し、本明細書において、銅を「含有しない」とは、銅を意図的に配合することを除外する規定であって、意図せずに銅が含まれる場合までを排除する規定ではない。
<Copper>
The friction material of the present embodiment has a copper content of less than 0.5% by mass with respect to the total amount of the friction material.
In the present specification, "the copper content is less than 0.5% by mass with respect to the total amount of the friction material" includes the case where the copper content is 0% by mass.
The above-mentioned "copper" is, for example, fibrous or powdery copper; a copper element contained in a copper alloy, a copper compound, or the like.
When the friction material of the present embodiment contains copper, the content thereof is preferably 0.3% by mass or less, more preferably 0.1% by mass or less, and 0.05% by mass or less with respect to the total amount of the friction material. Is even more preferable.
The friction material of the present embodiment may not contain copper. However, in the present specification, "not containing" copper is a provision excluding the intentional blending of copper, and is not a provision excluding the case where copper is unintentionally contained.
＜スチール繊維＞
本実施形態の摩擦材は、スチール繊維の含有量を低くすることで、ディスクロータへの攻撃性及びブレーキ鳴きの発生が抑制された組成を前提とし、当該組成において銅を使用せずとも十分な制動性能が得られる組成を見出した発明である。
そのため、本実施形態の摩擦材は、スチール繊維の含有量が、摩擦材全量に対して、２５質量％以下である。
なお、本明細書において、「スチール繊維の含有量が２５質量％以下」であるとは、スチール繊維の含有量が０質量％である場合も含む。
本実施形態の摩擦材がスチール繊維を含有する場合、その含有量は、特に限定されないが、ディスクロータの耐摩耗性及びブレーキ鳴きの発生を抑制するという観点から、摩擦材全量に対して、２０質量％以下が好ましく、１０質量％以下がより好ましく、１質量％以下がさらに好ましい。本実施形態の摩擦材はスチール繊維を含有しないものであってもよい。
<Steel fiber>
The friction material of the present embodiment is premised on a composition in which the aggression to the disc rotor and the occurrence of brake squeal are suppressed by lowering the content of the steel fiber, and it is sufficient without using copper in the composition. It is an invention that has found a composition that can obtain braking performance.
Therefore, the friction material of the present embodiment has a steel fiber content of 25% by mass or less with respect to the total amount of the friction material.
In addition, in this specification, "the content of a steel fiber is 25% by mass or less" includes the case where the content of a steel fiber is 0% by mass.
When the friction material of the present embodiment contains steel fibers, the content thereof is not particularly limited, but is 20 with respect to the total amount of the friction material from the viewpoint of suppressing the wear resistance of the disc rotor and the occurrence of brake squeal. It is preferably 1% by mass or less, more preferably 10% by mass or less, and even more preferably 1% by mass or less. The friction material of the present embodiment may not contain steel fibers.
＜硫酸カルシウム繊維＞
本実施形態の摩擦材は、硫酸カルシウム繊維を含有することで、フェード時の摩擦係数と高温高速制動時の耐摩耗性とを両立したものとなる。その原因は定かではないが次のように推測される。
硫酸カルシウム繊維は、摩擦材において補強作用を示す繊維形状を有する化合物であると共に、有機繊維と比べて強度に優れるため、摩擦材の機械強度を高めることができる。更に、硫酸カルシウム繊維は、高温に晒されても有機繊維より分解又は燃焼し難いため、高温高速制動時のような過酷な環境下でも、摩擦材に対する補強効果が失われず、ブレーキパッドの摩耗を抑制できたと考えられる。一方で、硫酸カルシウム繊維はモース硬度が高い材料ではないため、摩擦係数を含む他の物性に対して悪影響を及ぼすことなく、フェード時の摩擦係数と高温高速制動時の耐摩耗性とのバランスを向上できたものと考えられる。
本明細書における「硫酸カルシウム繊維」とは、最小長さに対する最大長さの比（アスペクト比）が５以上である硫酸カルシウムを意味する。
<Calcium sulfate fiber>
Since the friction material of the present embodiment contains calcium sulfate fibers, the friction coefficient at the time of fading and the wear resistance at the time of high-temperature high-speed braking are compatible. The cause is not clear, but it is presumed as follows.
Calcium sulfate fiber is a compound having a fiber shape that exhibits a reinforcing action in the friction material, and is superior in strength to organic fibers, so that the mechanical strength of the friction material can be increased. Furthermore, since calcium sulfate fibers are less likely to be decomposed or burned than organic fibers even when exposed to high temperatures, the reinforcing effect on the friction material is not lost even in a harsh environment such as during high temperature and high speed braking, and the brake pads are worn. It is probable that it could be suppressed. On the other hand, since calcium sulfate fiber is not a material with high moth hardness, it does not adversely affect other physical properties including the coefficient of friction, and balances the coefficient of friction during fading and wear resistance during high-temperature high-speed braking. It is considered that it could be improved.
As used herein, the term "calcium sulfate fiber" means calcium sulfate having a ratio (aspect ratio) of the maximum length to the minimum length of 5 or more.
硫酸カルシウムは、結晶水の存在形態に応じて、二水石膏（硫酸カルシウム二水和物）、半水石膏（硫酸カルシウム半水和物）及び無水石膏（硫酸カルシウム無水物）に大別され、硫酸カルシウム無水物は、更に、結晶系の違いによりI型、II型、III型に分類される。これらの中でも、本実施形態の摩擦材に含有される硫酸カルシウム繊維は、無水石膏（硫酸カルシウム無水物）からなる繊維であることが好ましく、吸水による摩擦係数の変動や体積変化に伴う摩擦材の膨張収縮を抑制する観点から、II型無水石膏からなる繊維であることがより好ましい。
硫酸カルシウム繊維を構成する硫酸カルシウムの種類は、１種を単独で用いてもよく、２種以上を併用してもよい。
Calcium sulfate is roughly classified into dihydrate gypsum (calcium sulfate dihydrate), hemihydrate gypsum (calcium sulfate hemihydrate) and anhydrous gypsum (calcium sulfate anhydride) according to the existence form of crystalline water. Calcium sulfate anhydride is further classified into type I, type II, and type III according to the difference in crystal system. Among these, the calcium sulfate fiber contained in the friction material of the present embodiment is preferably a fiber made of anhydrous gypsum (calcium sulfate anhydride), and the friction material due to fluctuation of friction coefficient due to water absorption and volume change. From the viewpoint of suppressing expansion and contraction, it is more preferable that the fiber is made of type II anhydrous gypsum.
As the type of calcium sulfate constituting the calcium sulfate fiber, one type may be used alone, or two or more types may be used in combination.
（繊維長）
硫酸カルシウム繊維の平均繊維長は、特に限定されないが、硫酸カルシウム繊維の分散性及びブレーキパッドの耐摩耗性の観点から、１～２００μｍが好ましく、３～１００μｍがより好ましく、５～５０μｍがさらに好ましく、１０～２０μｍが特に好ましい。
硫酸カルシウム繊維の最小繊維長は、０．１μｍ以上が好ましく、０．３μｍ以上がより好ましく、０．５μｍ以上がさらに好ましく、１μｍ以上が特に好ましい。
硫酸カルシウム繊維の最大繊維長は、１０００μｍ以下が好ましく、５００μｍ以下がより好ましく、２００μｍ以下がさらに好ましく、１００μｍ以下が特に好ましい。
硫酸カルシウム繊維の平均繊維長は、例えば、走査型電子顕微鏡（ＳＥＭ）等によって、任意の５０本の硫酸カルシウム繊維を観察して繊維長を測定し、それらの平均値として算出することができる。また、硫酸カルシウム繊維の最大繊維長及び最小繊維長は、平均繊維長の測定で観察した任意の５０本の硫酸カルシウム繊維のうちの最大繊維長及び最小繊維長を意味する。
(Fiber length)
The average fiber length of the calcium sulfate fiber is not particularly limited, but is preferably 1 to 200 μm, more preferably 3 to 100 μm, still more preferably 5 to 50 μm, from the viewpoint of the dispersibility of the calcium sulfate fiber and the wear resistance of the brake pad. 10 to 20 μm is particularly preferable.
The minimum fiber length of the calcium sulfate fiber is preferably 0.1 μm or more, more preferably 0.3 μm or more, further preferably 0.5 μm or more, and particularly preferably 1 μm or more.
The maximum fiber length of the calcium sulfate fiber is preferably 1000 μm or less, more preferably 500 μm or less, further preferably 200 μm or less, and particularly preferably 100 μm or less.
The average fiber length of calcium sulfate fibers can be calculated as an average value by observing any 50 calcium sulfate fibers with a scanning electron microscope (SEM) or the like and measuring the fiber length. Further, the maximum fiber length and the minimum fiber length of the calcium sulfate fiber mean the maximum fiber length and the minimum fiber length of any 50 calcium sulfate fibers observed in the measurement of the average fiber length.
（繊維径）
硫酸カルシウム繊維の平均繊維径は、特に限定されないが、硫酸カルシウム繊維の分散性及びブレーキパッドの耐摩耗性の観点から、０．１～２０μｍが好ましく、０．２～１０μｍがより好ましく、０．３～５μｍがさらに好ましく、０．５～２μｍが特に好ましい。
硫酸カルシウム繊維の最小繊維径は、０．０２μｍ以上が好ましく、０．０４μｍ以上がより好ましく、０．０７μｍ以上がさらに好ましく、０．１μｍ以上が特に好ましい。
硫酸カルシウム繊維の最大繊維径は、１００μｍ以下が好ましく、５０μｍ以下がより好ましく、３０μｍ以下がさらに好ましく、１０μｍ以下が特に好ましい。
硫酸カルシウム繊維の平均繊維径は、例えば、走査型電子顕微鏡（ＳＥＭ）等によって、任意の５０本の硫酸カルシウム繊維を観察して繊維径を測定し、それらの平均値として算出することができる。また、硫酸カルシウム繊維の最大繊維径及び最小繊維径は、平均繊維径の測定で観察した任意の５０本の硫酸カルシウム繊維のうちの最大繊維径及び最小繊維径を意味する。
(Fiber diameter)
The average fiber diameter of the calcium sulfate fiber is not particularly limited, but is preferably 0.1 to 20 μm, more preferably 0.2 to 10 μm, and 0. 3 to 5 μm is more preferable, and 0.5 to 2 μm is particularly preferable.
The minimum fiber diameter of the calcium sulfate fiber is preferably 0.02 μm or more, more preferably 0.04 μm or more, further preferably 0.07 μm or more, and particularly preferably 0.1 μm or more.
The maximum fiber diameter of the calcium sulfate fiber is preferably 100 μm or less, more preferably 50 μm or less, further preferably 30 μm or less, and particularly preferably 10 μm or less.
The average fiber diameter of calcium sulfate fibers can be calculated as an average value by observing any 50 calcium sulfate fibers with a scanning electron microscope (SEM) or the like and measuring the fiber diameter. Further, the maximum fiber diameter and the minimum fiber diameter of the calcium sulfate fiber mean the maximum fiber diameter and the minimum fiber diameter of any 50 calcium sulfate fibers observed in the measurement of the average fiber diameter.
（アスペクト比）
硫酸カルシウム繊維の平均アスペクト比（繊維長／繊維径）は、特に限定されないが、硫酸カルシウム繊維の分散性及びブレーキパッドの耐摩耗性の観点から、５～２００が好ましく、６～１００がより好ましく、８～５０がさらに好ましく、１０～２０が特に好ましい。
硫酸カルシウム繊維の平均アスペクト比（繊維長／繊維径）は、例えば、走査型電子顕微鏡（ＳＥＭ）等によって、任意の５０本の硫酸カルシウム繊維のアスペクト比を測定し、それらの平均値として算出することができる。
(aspect ratio)
The average aspect ratio (fiber length / fiber diameter) of the calcium sulfate fiber is not particularly limited, but is preferably 5 to 200, more preferably 6 to 100, from the viewpoint of dispersibility of the calcium sulfate fiber and wear resistance of the brake pad. , 8 to 50 are more preferable, and 10 to 20 are particularly preferable.
The average aspect ratio (fiber length / fiber diameter) of calcium sulfate fibers is calculated as an average value of 50 arbitrary calcium sulfate fibers measured by, for example, a scanning electron microscope (SEM) or the like. be able to.
本実施形態の摩擦材における硫酸カルシウム繊維の含有量は、特に限定されないが、フェード時の摩擦係数と高温高速制動時の耐摩耗性とを両立させる観点から、摩擦材全量に対して、１～２０質量％が好ましく、２～１５質量％がより好ましく、３～１０質量％がさらに好ましい。 The content of calcium sulfate fibers in the friction material of the present embodiment is not particularly limited, but is 1 to 1 to the total amount of the friction material from the viewpoint of achieving both a friction coefficient during fading and wear resistance during high-temperature and high-speed braking. 20% by mass is preferable, 2 to 15% by mass is more preferable, and 3 to 10% by mass is further preferable.
＜無機充填材、有機充填材、繊維基材、結合材＞
本実施形態の摩擦材は、無機充填材、有機充填材、上記硫酸カルシウム繊維を含む繊維基材及び結合材を含有するものであることが好ましい。
なお、本明細書において、硫酸カルシウム繊維以外の繊維基材を「他の繊維基材」と称する場合がある。単に「繊維基材」と称する場合、これは硫酸カルシウム繊維及び他の繊維基材を含む繊維基材全体を意味するものとする。
以下、各成分について、さらに詳細に説明する。
<Inorganic filler, organic filler, fiber base material, binder>
The friction material of the present embodiment preferably contains an inorganic filler, an organic filler, a fiber base material containing the calcium sulfate fiber, and a binder.
In addition, in this specification, a fiber base material other than calcium sulfate fiber may be referred to as "another fiber base material". When simply referred to as "fiber substrate", this shall mean the entire fiber substrate including calcium sulfate fibers and other fiber substrates.
Hereinafter, each component will be described in more detail.
＜無機充填材＞
無機充填材は、摩擦材の耐熱性、耐摩耗性、摩擦係数等を調整する摩擦調整材としての機能を発現し得るものを、目的に応じて適宜選択すればよい。なお、本実施形態においては「無機充填材」の定義に、繊維形状のもの（つまり、無機繊維）は含めない。
無機充填材は、１種を単独で用いてもよく、２種以上を併用してもよい。
<Inorganic filler>
As the inorganic filler, a material that can exhibit a function as a friction adjusting material for adjusting the heat resistance, wear resistance, friction coefficient, etc. of the friction material may be appropriately selected according to the purpose. In this embodiment, the definition of "inorganic filler" does not include fiber-shaped ones (that is, inorganic fibers).
As the inorganic filler, one kind may be used alone, or two or more kinds may be used in combination.
無機充填材としては、例えば、チタン酸カリウム（６－チタン酸カリウム、８－チタン酸カリウム）、チタン酸リチウムカリウム、チタン酸マグネシウムカリウム、チタン酸ナトリウム等のチタン酸塩；硫化錫、硫化鉄、硫化ビスマス、硫化モリブデン、硫化亜鉛、硫化アンチモン、硫化タングステン、硫化マンガン等の金属硫化物；天然黒鉛、人造黒鉛等の黒鉛；酸化鉄（III）、四酸化三鉄、酸化アルミニウム、酸化マグネシウム、酸化カルシウム、酸化ジルコニウム、酸化チタン、酸化亜鉛、酸化ビスマス、二酸化ケイ素等の金属酸化物又は非金属酸化物；鉄粉、錫粉、亜鉛粉、アルミニウム粉、これらの合金粉等の金属粉；硫酸バリウム、硫酸カルシウム等の金属硫酸塩；水酸化カルシウム等の金属水酸化物；ケイ酸ジルコニウム、ケイ酸カルシウム等の金属ケイ酸塩；炭酸ナトリウム、炭酸カルシウム、炭酸マグネシウム等の金属炭酸塩；コークス；マイカ、ドロマイト、バーミキュライト、タルク、クレー、ムライト、クロマイト、ゼオライト等の鉱物などが挙げられる。これらの中でも、チタン酸塩、金属硫化物、黒鉛、金属酸化物、非金属酸化物、金属ケイ酸塩、金属粉、硫酸バリウム及び水酸化カルシウムからなる群から選択される１種以上を含有することが好ましい。 Examples of the inorganic filler include titanates such as potassium titanate (6-potassium titanate, 8-potassium titanate), lithium potassium titanate, potassium magnesium titanate, sodium titanate; tin sulfide, iron sulfide, and the like. Metal sulfides such as bismuth sulfide, molybdenum sulfide, zinc sulfide, antimony sulfide, tungsten sulfide, manganese sulfide; graphite such as natural graphite and artificial graphite; iron (III) oxide, triiron tetroxide, aluminum oxide, magnesium oxide, oxidation Metallic or non-metal oxides such as calcium, zirconium oxide, titanium oxide, zinc oxide, bismuth oxide, silicon dioxide; metal powders such as iron powder, tin powder, zinc powder, aluminum powder, alloy powders thereof; barium sulfate , Metal sulfates such as calcium sulfate; Metal hydroxides such as calcium hydroxide; Metal silicates such as zirconium silicate and calcium silicate; Metal carbonates such as sodium carbonate, calcium carbonate, magnesium carbonate; Coke; Mica , Dolomite, vermiculite, talc, clay, sulfurite, chromite, minerals such as zeolite and the like. Among these, one or more selected from the group consisting of titanate, metal sulfide, graphite, metal oxide, non-metal oxide, metal silicate, metal powder, barium sulfate and calcium hydroxide is contained. Is preferable.
無機充填材の平均粒子径（Ｄ５０）は、材質に応じて適宜選択すればよいが、通常は、０．１～１００μｍの範囲で選択され、０．５～５０μｍであってもよく、１～３０μｍであってもよい。
なお、本明細書において、平均粒子径（Ｄ５０）は、レーザー回折粒度分布測定の方法を用いて測定したＤ５０の値（体積分布のメジアン径、累積中央値）を意味する。平均粒子径（Ｄ５０）は、例えば、レーザー回折／散乱式粒子径分布測定装置、商品名：ＬＡ－９２０（株式会社堀場製作所製）を用いて測定することができる。
以下、本実施形態の摩擦材が含有することが好ましい無機充填材について、より詳細に説明する。
The average particle size (D 50 ) of the inorganic filler may be appropriately selected depending on the material, but is usually selected in the range of 0.1 to 100 μm, and may be 0.5 to 50 μm. It may be up to 30 μm.
In the present specification, the average particle size (D 50 ) means the value of D 50 (median diameter of volume distribution, cumulative median value) measured by the method of laser diffraction particle size distribution measurement. The average particle size (D 50 ) can be measured using, for example, a laser diffraction / scattering type particle size distribution measuring device, trade name: LA-920 (manufactured by HORIBA, Ltd.).
Hereinafter, the inorganic filler preferably contained in the friction material of the present embodiment will be described in more detail.
（チタン酸）
チタン酸塩としては、上記で挙げたものの中でも、摩擦係数の観点から６－チタン酸カリウム、８－チタン酸カリウムが好ましい。チタン酸塩は、非針状であることが好ましい。非針状のチタン酸塩とは、多角形、円、楕円等の形状を呈する板状チタン酸塩、不定形状のチタン酸塩等である。
本実施形態の摩擦材がチタン酸塩を含有する場合、その含有量は、特に限定されないが、摩擦材全量に対して、２～４０質量％が好ましく、１０～３５質量％がより好ましく、１５～３０質量％がさらに好ましい。
(Titanate)
Among the above-mentioned titanates, potassium 6-potassium titanate and potassium 8-titanate are preferable as the titanate from the viewpoint of the coefficient of friction. The titanate is preferably non-needle-shaped. The non-needle-shaped titanium salt is a plate-shaped titanium salt having a polygonal, circular, elliptical shape, or an indefinite shape.
When the friction material of the present embodiment contains titanium salt, the content thereof is not particularly limited, but is preferably 2 to 40% by mass, more preferably 10 to 35% by mass, and 15 by mass, based on the total amount of the friction material. ~ 30% by mass is more preferable.
（金属硫化物）
金属硫化物としては、上記で挙げたものの中でも、通常制動時の摩擦係数の安定性の観点から、硫化アンチモン、硫化錫、硫化鉄、硫化ビスマス、硫化モリブデン、硫化亜鉛が好ましく、硫化アンチモンがより好ましい。
本実施形態の摩擦材が金属硫化物を含有する場合、その含有量は、特に限定されないが、耐摩耗性及び摩擦係数の観点から、摩擦材全量に対して、０．５～１０質量％が好ましく、１～７質量％がより好ましく、２～５質量％がさらに好ましい。
(Metal sulfide)
Among the metal sulfides listed above, antimony sulfide, tin sulfide, iron sulfide, bismuth sulfide, molybdenum sulfide, and zinc sulfide are preferable, and antimony sulfide is more preferable, from the viewpoint of stability of the friction coefficient during normal braking. preferable.
When the friction material of the present embodiment contains a metal sulfide, the content thereof is not particularly limited, but is 0.5 to 10% by mass with respect to the total amount of the friction material from the viewpoint of wear resistance and friction coefficient. Preferably, 1 to 7% by mass is more preferable, and 2 to 5% by mass is further preferable.
（黒鉛）
本実施形態の摩擦材が黒鉛を含有する場合、その含有量は、特に限定されないが、耐摩耗性及び摩擦係数の観点から、摩擦材全量に対して、１～１５質量％が好ましく、２～１０質量％がより好ましく、３～８質量％がさらに好ましい。
(graphite)
When the friction material of the present embodiment contains graphite, the content thereof is not particularly limited, but is preferably 1 to 15% by mass, preferably 2 to 15% by mass, based on the total amount of the friction material, from the viewpoint of wear resistance and friction coefficient. 10% by mass is more preferable, and 3 to 8% by mass is further preferable.
（金属酸化物、非金属酸化物、金属ケイ酸塩）
金属酸化物、非金属酸化物及び金属ケイ酸塩としては、上記で挙げたものの中でも、酸化ジルコニウム、酸化マグネシウム、ケイ酸ジルコニウム、酸化アルミニウムが好ましく、酸化ジルコニウムがより好ましい。
本実施形態の摩擦材が、金属酸化物、非金属酸化物及び金属ケイ酸塩からなる群から選択される１種以上を含有する場合、その含有量は、特に限定されないが、耐摩耗性及び摩擦係数の観点から、摩擦材全量に対して、１７～４０質量％が好ましく、２０～３５質量％がより好ましく、２５～３２質量％がさらに好ましい。
(Metal oxides, non-metal oxides, metal silicates)
As the metal oxide, non-metal oxide and metal silicate, among those mentioned above, zirconium oxide, magnesium oxide, zirconium silicate and aluminum oxide are preferable, and zirconium oxide is more preferable.
When the friction material of the present embodiment contains one or more selected from the group consisting of metal oxides, non-metal oxides and metal silicates, the content thereof is not particularly limited, but wear resistance and abrasion resistance. From the viewpoint of the coefficient of friction, 17 to 40% by mass is preferable, 20 to 35% by mass is more preferable, and 25 to 32% by mass is further preferable with respect to the total amount of the friction material.
（金属粉）
金属粉としては、上記で挙げたものの中でも、亜鉛粉が好ましい。
本実施形態の摩擦材が金属粉を含有する場合、その含有量は、特に限定されないが、防錆性、耐摩耗性及び摩擦係数の観点から、摩擦材全量に対して、０．１～１０質量％が好ましく、０．５～５質量％がより好ましく、１～４質量％がさらに好ましい。
(Metal powder)
As the metal powder, zinc powder is preferable among those listed above.
When the friction material of the present embodiment contains metal powder, the content thereof is not particularly limited, but is 0.1 to 10 with respect to the total amount of the friction material from the viewpoint of rust resistance, wear resistance and friction coefficient. The mass% is preferable, 0.5 to 5% by mass is more preferable, and 1 to 4% by mass is further preferable.
（硫酸バリウム）
硫酸バリウムは摩擦材の体積を調整するための単なる充填材としての役割を果たすものである。つまり、硫酸バリウムの含有量は、他の成分の含有量に依存し、摩擦材を所定量とするための残部を硫酸バリウムで補充することができる。
(Barium sulfate)
Barium sulphate serves as a mere filler for adjusting the volume of the friction material. That is, the content of barium sulfate depends on the content of other components, and the balance for making the friction material a predetermined amount can be replenished with barium sulfate.
（水酸化カルシウム）
本実施形態の摩擦材が水酸化カルシウムを含有する場合、その含有量は、特に限定されないが、ｐＨを適度に調整する観点から、摩擦材全量に対して、０．５～１０質量％が好ましく、１～８質量％がより好ましく、２～５質量％がさらに好ましい。
(Calcium hydroxide)
When the friction material of the present embodiment contains calcium hydroxide, the content thereof is not particularly limited, but is preferably 0.5 to 10% by mass with respect to the total amount of the friction material from the viewpoint of appropriately adjusting the pH. 1 to 8% by mass is more preferable, and 2 to 5% by mass is further preferable.
本実施形態の摩擦材における無機充填材の合計含有量は、特に限定されないが、耐摩耗性及び摩擦係数の観点から、摩擦材全量に対して、４０～９０質量％が好ましく、５０～８５質量％がより好ましく、６０～７５質量％がさらに好ましい。 The total content of the inorganic filler in the friction material of the present embodiment is not particularly limited, but is preferably 40 to 90% by mass and 50 to 85% by mass with respect to the total amount of the friction material from the viewpoint of wear resistance and friction coefficient. % Is more preferable, and 60 to 75% by mass is further preferable.
＜有機充填材＞
有機充填材は、摩擦材の音振性能、耐摩耗性等を向上させるための摩擦調整材として含有されるものである。ここで、本実施形態においては、有機充填材の定義に、繊維形状のもの（つまり後述の有機繊維）は含めない。
<Organic filler>
The organic filler is contained as a friction adjusting material for improving the sound vibration performance, wear resistance and the like of the friction material. Here, in the present embodiment, the definition of the organic filler does not include those having a fiber shape (that is, organic fibers described later).
有機充填材としては、例えば、カシューダスト、ゴム成分等が挙げられ、カシューダストとゴム成分とを併用することが好ましい。
有機充填材は、１種を単独で用いてもよく、２種以上を併用してもよい。
Examples of the organic filler include cashew dust, a rubber component, and the like, and it is preferable to use cashew dust and a rubber component in combination.
As the organic filler, one kind may be used alone, or two or more kinds may be used in combination.
（カシューダスト）
カシューダストとしては、例えば、カシューナッツシェルオイルを重合及び硬化させたものを粉砕したものが挙げられる。カシューダストは、未変性のカシューダストであることが好ましい。
カシューダストは、一般的に、硬化反応に使用する硬化剤の種類に応じて、例えば、茶系、茶黒系、黒系等に分類される。
カシューダストの平均粒子径（Ｄ５０）は、特に限定されないが、分散性等の観点から、１０～７００μｍが好ましく、２０～５００μｍがより好ましく、３０～３５０μｍがさらに好ましい。
本実施形態の摩擦材がカシューダストを含有する場合、その含有量は、特に限定されないが、音振性能の観点から、摩擦材全量に対して、１～１５質量％が好ましく、２～１０質量％がより好ましく、４～８質量％がさらに好ましい。
(Cashew dust)
Examples of cashew dust include those obtained by polymerizing and hardening cashew nut shell oil and crushing it. The cashew dust is preferably unmodified cashew dust.
Cashew dust is generally classified into, for example, brown-based, brown-black-based, black-based, and the like, depending on the type of curing agent used in the curing reaction.
The average particle size (D 50 ) of cashew dust is not particularly limited, but is preferably 10 to 700 μm, more preferably 20 to 500 μm, and even more preferably 30 to 350 μm from the viewpoint of dispersibility and the like.
When the friction material of the present embodiment contains cashew dust, the content thereof is not particularly limited, but is preferably 1 to 15% by mass and 2 to 10% by mass with respect to the total amount of the friction material from the viewpoint of sound vibration performance. % Is more preferable, and 4 to 8% by mass is further preferable.
（ゴム成分）
ゴム成分としては、摩擦材に使用されている公知のものを使用することができ、例えば、天然ゴム、合成ゴム等が挙げられる。合成ゴムとしては、アクリロニトリル－ブタジエンゴム（ＮＢＲ）、アクリルゴム、イソプレンゴム、ポリブタジエンゴム（ＢＲ）、スチレンブタジエンゴム（ＳＢＲ）、シリコーンゴム、タイヤトレッドゴムの粉砕粉（ゴム粉と称することがある。）、ブチルゴム等が挙げられる。
本実施形態の摩擦材がゴム成分を含有する場合、その含有量は、特に限定されないが、摩擦材の弾性率、制振性、耐熱性、強度等の観点から、摩擦材全量に対して、０．１～１５質量％が好ましく、０．２～１０質量％がより好ましく、０．３～５質量％がさらに好ましい。
(Rubber component)
As the rubber component, known materials used for the friction material can be used, and examples thereof include natural rubber and synthetic rubber. As the synthetic rubber, acrylonitrile-butadiene rubber (NBR), acrylic rubber, isoprene rubber, polybutadiene rubber (BR), styrene butadiene rubber (SBR), silicone rubber, and crushed powder of tire tread rubber (rubber powder) may be used. ), Butyl rubber and the like.
When the friction material of the present embodiment contains a rubber component, the content thereof is not particularly limited, but from the viewpoint of elastic modulus, vibration damping property, heat resistance, strength, etc. of the friction material, the content thereof is relative to the total amount of the friction material. It is preferably 0.1 to 15% by mass, more preferably 0.2 to 10% by mass, still more preferably 0.3 to 5% by mass.
本実施形態の摩擦材における有機充填材の合計含有量は、特に限定されないが、音振性能、耐熱性及び摩擦材強度の観点から、摩擦材全量に対して、２～２０質量％が好ましく、４～１５質量％がより好ましく、６～１２質量％がさらに好ましい。 The total content of the organic filler in the friction material of the present embodiment is not particularly limited, but is preferably 2 to 20% by mass with respect to the total amount of the friction material from the viewpoint of sound vibration performance, heat resistance and friction material strength. 4 to 15% by mass is more preferable, and 6 to 12% by mass is further preferable.
＜他の繊維基材＞
他の繊維基材としては、例えば、有機繊維、硫酸カルシウム繊維以外の無機繊維等が挙げられる。他の繊維基材は、１種を単独で用いてもよく、２種以上を併用してもよい。
<Other fiber base materials>
Examples of other fiber base materials include organic fibers and inorganic fibers other than calcium sulfate fibers. As the other fiber base material, one type may be used alone, or two or more types may be used in combination.
－有機繊維－
本実施形態の摩擦材は、有機繊維を含有することが好ましい。有機繊維とは、有機物を主成分とする繊維状の材料である。
有機繊維としては、例えば、麻、木綿、アラミド繊維、セルロース繊維、アクリル繊維、フェノール樹脂繊維（架橋構造を有する）等が挙げられる。
有機繊維としては、耐熱性の観点から、アラミド繊維が好ましい。
-Organic fiber-
The friction material of the present embodiment preferably contains organic fibers. The organic fiber is a fibrous material containing an organic substance as a main component.
Examples of the organic fiber include hemp, cotton, aramid fiber, cellulose fiber, acrylic fiber, phenol resin fiber (having a crosslinked structure) and the like.
As the organic fiber, aramid fiber is preferable from the viewpoint of heat resistance.
本実施形態の摩擦材が有機繊維を含有する場合、その含有量は、特に限定されないが、摩擦材のせん断強度、耐クラック性、耐摩耗性等の観点から、摩擦材全量に対して、０．１～１０質量％が好ましく、０．５～６質量％がより好ましく、１～４質量％がさらに好ましい。 When the friction material of the present embodiment contains organic fibers, the content thereof is not particularly limited, but is 0 with respect to the total amount of the friction material from the viewpoint of shear strength, crack resistance, wear resistance, etc. of the friction material. .1 to 10% by mass is preferable, 0.5 to 6% by mass is more preferable, and 1 to 4% by mass is further preferable.
－硫酸カルシウム繊維以外の無機繊維－
硫酸カルシウム繊維以外の無機繊維としては、例えば、鉱物繊維、ガラス繊維、金属繊維、セラミック繊維、生分解性セラミック繊維、セピオライト（α型セピオライト及びβ型セピオライト）、アタパルジャイト、チタン酸カリウム繊維、シリカアルミナ繊維、耐炎化繊維等が挙げられる。これらの中でも、鉱物繊維が好ましい。
-Inorganic fibers other than calcium sulfate fibers-
Examples of inorganic fibers other than calcium sulfate fibers include mineral fibers, glass fibers, metal fibers, ceramic fibers, biodegradable ceramic fibers, sepiolite (α-type sepiolite and β-type sepiolite), attapulsite, potassium titanate fiber, and silica alumina. Examples include fibers and flame-resistant fibers. Among these, mineral fibers are preferable.
鉱物繊維は、スラグウール等の高炉スラグ；バサルトファイバー等の玄武岩；その他の天然岩石などを主成分として溶融紡糸した人造無機繊維である。
鉱物繊維としては、例えば、ＳｉＯ２、Ａｌ２Ｏ３、ＣａＯ、ＭｇＯ、ＦｅＯ、Ｎａ２Ｏ、これらの化合物を１種以上含有する鉱物繊維等が挙げられる。鉱物繊維としては、アルミニウム元素を含む鉱物繊維が好ましく、Ａｌ２Ｏ３を含有する鉱物繊維がより好ましく、Ａｌ２Ｏ３とＳｉＯ２とを含有する鉱物繊維がさらに好ましい。鉱物繊維は表面処理されていてもよいし、表面処理されていなくてもよく、表面処理された鉱物繊維と表面処理されていない鉱物繊維とを併用してもよい。
鉱物繊維の平均繊維長は、５００μｍ以下が好ましく、１００～４００μｍがより好ましく、１２０～３４０μｍがさらに好ましい。
The mineral fiber is an artificial inorganic fiber melt-spun with blast furnace slag such as slag wool; basalt such as basalt fiber; and other natural rocks as main components.
Examples of the mineral fiber include SiO 2 , Al 2 O 3 , CaO, MgO, FeO, Na 2 O, and mineral fiber containing one or more of these compounds. As the mineral fiber, a mineral fiber containing an aluminum element is preferable, a mineral fiber containing Al 2 O 3 is more preferable, and a mineral fiber containing Al 2 O 3 and SiO 2 is further preferable. The mineral fiber may be surface-treated or may not be surface-treated, and the surface-treated mineral fiber and the unsurface-treated mineral fiber may be used in combination.
The average fiber length of the mineral fiber is preferably 500 μm or less, more preferably 100 to 400 μm, still more preferably 120 to 340 μm.
本実施形態の摩擦材が硫酸カルシウム繊維以外の無機繊維を含有する場合、その含有量は、特に限定されないが、摩擦材全量に対して、０．１～１５質量％が好ましく、１～１０質量％がより好ましく、３～７質量％がさらに好ましい。 When the friction material of the present embodiment contains inorganic fibers other than calcium sulfate fibers, the content thereof is not particularly limited, but is preferably 0.1 to 15% by mass, preferably 1 to 10% by mass, based on the total amount of the friction material. % Is more preferable, and 3 to 7% by mass is further preferable.
本実施形態の摩擦材における繊維基材の合計含有量は、特に限定されないが、耐摩耗性及び摩擦係数の観点から、摩擦材全量に対して、２～３０質量％が好ましく、４～２５質量％がより好ましく、６～２０質量％がさらに好ましい。 The total content of the fiber base material in the friction material of the present embodiment is not particularly limited, but is preferably 2 to 30% by mass and 4 to 25% by mass with respect to the total amount of the friction material from the viewpoint of wear resistance and friction coefficient. % Is more preferable, and 6 to 20% by mass is further preferable.
＜結合材＞
結合材は、摩擦材に含有される有機充填材、繊維基材等を一体化して、強度を与えるものである。
結合材は、１種を単独で用いてもよく、２種以上を併用してもよい。
結合材としては、通常、摩擦材に用いられる熱硬化性樹脂を用いることができる。熱硬化性樹脂としては、例えば、フェノール樹脂、アクリルゴム変性フェノール樹脂、シリコーン変性フェノール樹脂、カシュー変性フェノール樹脂、エポキシ変性フェノール樹脂、アルキルベンゼン変性フェノール樹脂等の各種変性フェノール樹脂などが挙げられる。これらの中でも、フェノール樹脂が好ましい。フェノール樹脂としては、例えば、ストレートノボラックフェノール樹脂等が好ましく挙げられる。
<Binder>
The binder is a material that integrates the organic filler, fiber base material, etc. contained in the friction material to give strength.
As the binder, one type may be used alone, or two or more types may be used in combination.
As the binder, a thermosetting resin usually used as a friction material can be used. Examples of the thermosetting resin include various modified phenol resins such as phenol resin, acrylic rubber-modified phenol resin, silicone-modified phenol resin, cashew-modified phenol resin, epoxy-modified phenol resin, and alkylbenzene-modified phenol resin. Among these, phenol resin is preferable. As the phenol resin, for example, straight novolak phenol resin and the like are preferably mentioned.
本実施形態の摩擦材における結合材の含有量は、特に限定されないが、摩擦材強度及び音振性能の観点から、摩擦材全量に対して、２～２０質量％が好ましく、４～１５質量％がより好ましく、６～１２質量％がさらに好ましい。 The content of the binder in the friction material of the present embodiment is not particularly limited, but is preferably 2 to 20% by mass and 4 to 15% by mass with respect to the total amount of the friction material from the viewpoint of the friction material strength and the sound vibration performance. Is more preferable, and 6 to 12% by mass is further preferable.
＜その他の成分＞
本実施形態の摩擦材は、必要に応じて、上記各成分以外のその他の材料を含有していてもよいし、含有していなくてもよい。
本実施形態の摩擦材が上記その他の材料を含有する場合、その含有量としては、摩擦材全量に対して、それぞれ、例えば、０．０１～１０質量％であってもよく、０．１～５質量％であってもよい。
<Other ingredients>
The friction material of the present embodiment may or may not contain other materials other than the above-mentioned components, if necessary.
When the friction material of the present embodiment contains the above-mentioned other materials, the content thereof may be, for example, 0.01 to 10% by mass, or 0.1 to 10% by mass, respectively, with respect to the total amount of the friction material. It may be 5% by mass.
＜摩擦部材、摩擦材及び摩擦材組成物の製造方法＞
本実施形態の摩擦部材、摩擦材及び摩擦材組成物は、公知の方法により製造することができる。
具体的には、例えば、上記各成分をレーディゲ（登録商標）ミキサー、加圧ニーダー、アイリッヒ（登録商標）ミキサー等の混合機を用いて均一に混合して摩擦材組成物を得ることができる。そして、得られた摩擦材組成物を、成形金型にて必要に応じて予備成形した後、例えば、成形温度１３０～１６０℃、成形圧力２０～５０ＭＰａ、成形時間３～１０分間の条件で成形し、得られた成形物を１８０～２３０℃で３～５時間熱処理する方法により、摩擦材及び摩擦部材を得ることができる。なお、必要に応じて塗装、スコーチ処理、研磨処理等を行ってもよい。
<Manufacturing method of friction member, friction material and friction material composition>
The friction member, the friction material and the friction material composition of the present embodiment can be produced by a known method.
Specifically, for example, each of the above components can be uniformly mixed using a mixer such as a Raydige (registered trademark) mixer, a pressurized kneader, or an Erich (registered trademark) mixer to obtain a friction material composition. Then, the obtained friction material composition is premolded with a molding mold as necessary, and then molded under the conditions of, for example, a molding temperature of 130 to 160 ° C., a molding pressure of 20 to 50 MPa, and a molding time of 3 to 10 minutes. A friction material and a friction member can be obtained by a method of heat-treating the obtained molded product at 180 to 230 ° C. for 3 to 5 hours. If necessary, painting, scorch treatment, polishing treatment and the like may be performed.
本実施形態の摩擦材は、例えば、下記（１）～（３）の態様で用いられる。
（１）摩擦材のみの構成。
（２）裏金と、該裏金の上に形成させた、摩擦面となる本実施形態の摩擦材とを有する摩擦部材。
（３）上記（２）の構成において、裏金と摩擦部材との間に、裏金の接着効果を高めるための表面改質を目的としたプライマー層、裏金と摩擦部材の接着を目的とした接着層をさらに介在させた構成。
これらの中でも、上記（２）又は（３）のように摩擦部材として用いられることが好ましい。
裏金は、摩擦部材の機械的強度の向上のために用いるものであり、その材質としては、鉄、ステンレス等の金属；無機繊維強化プラスチック、炭素繊維強化プラスチック等の繊維強化プラスチックなどが挙げられる。
プライマー層及び接着層としては、通常、ブレーキシュー等の摩擦部材に用いられるものであればよい。
The friction material of the present embodiment is used, for example, in the following embodiments (1) to (3).
(1) Consists of only friction material.
(2) A friction member having a back metal and a friction material of the present embodiment, which is a friction surface formed on the back metal.
(3) In the configuration of (2) above, between the back metal and the friction member, a primer layer for the purpose of surface modification to enhance the adhesive effect of the back metal, and an adhesive layer for the purpose of adhering the back metal and the friction member. Is further intervened.
Among these, it is preferable to use it as a friction member as described in (2) or (3) above.
The back metal is used for improving the mechanical strength of the friction member, and examples thereof include metals such as iron and stainless steel; fiber reinforced plastics such as inorganic fiber reinforced plastics and carbon fiber reinforced plastics.
As the primer layer and the adhesive layer, those usually used for friction members such as brake shoes may be used.
図１を参照して本実施形態の摩擦部材の一実施態様について具体的に説明する。本実施形態の摩擦部材は、バックプレート１、本実施形態の摩擦材（図１の場合は上張り材とも称する。）２及び下張り材３から構成され、バックプレート１の摩擦材が配置される面１１（ここではバックプレート１の上面）に、下張り材３を介して摩擦材（上張り材）２が固着されたものである。本実施形態の摩擦材は、上記「上張り材」として用いることもできるし、上記「下張り材」として用いることもできるが、「上張り材」として用いることが好ましい。なお、「上張り材」とは、摩擦部材の摩擦面となる摩擦材であり、「下張り材」とは、摩擦部材の摩擦面となる摩擦材と裏金との間に介在する、摩擦材と裏金との接着部付近の剪断強度、耐クラック性向上を目的として配される層のことである。
An embodiment of the friction member of the present embodiment will be specifically described with reference to FIG. The friction member of the present embodiment is composed of a back plate 1, a friction material (also referred to as an upholstery material in the case of FIG. 1) 2 and an underlaying
本実施形態の摩擦材及び摩擦部材は、自動車等のディスクブレーキパッド、ブレーキライニングなどの摩擦材及び摩擦部材として好適である。
また、本実施形態の摩擦材は、目的形状に成形、加工、貼り付け等の工程を施すことにより、クラッチフェーシング、電磁ブレーキ、保持ブレーキ等の摩擦材としても使用することができる。
The friction material and friction member of the present embodiment are suitable as friction material and friction member for disc brake pads of automobiles and the like, brake linings and the like.
Further, the friction material of the present embodiment can also be used as a friction material for a clutch facing, an electromagnetic brake, a holding brake, etc. by subjecting a desired shape to a process such as molding, processing, and pasting.
［車両］
本発明は、本実施形態の摩擦材又は摩擦部材を搭載した車両も提供する。例えば、本実施形態の摩擦部材を、ディスクブレーキパッド、ブレーキライニング、クラッチフェーシング、電磁ブレーキ、保持ブレーキ等に用いた車両などが挙げられる。車両としては、例えば、大型自動車、中型自動車、普通自動車、大型特殊自動車、小型特殊自動車、大型自動二輪車、普通自動二輪車等の、自動四輪車及び自動二輪車を含む各種自動車が挙げられる。
[vehicle]
The present invention also provides a vehicle equipped with the friction material or the friction member of the present embodiment. For example, a vehicle in which the friction member of the present embodiment is used for a disc brake pad, a brake lining, a clutch facing, an electromagnetic brake, a holding brake, or the like can be mentioned. Examples of the vehicle include various automobiles including motorcycles and motorcycles such as large automobiles, medium-sized automobiles, ordinary automobiles, large special automobiles, small special automobiles, large two-wheeled vehicles, and ordinary two-wheeled vehicles.
以下、実施例を挙げて、本発明を具体的に説明するが、本発明は以下の実施例に限定されるものではない。 Hereinafter, the present invention will be specifically described with reference to examples, but the present invention is not limited to the following examples.
［ディスクブレーキパッドの作製］
＜実施例１～４及び比較例１～４＞
表１に示す配合比率（質量％）に従って材料を配合し、各摩擦材組成物を得た。
次に、この摩擦材組成物をレーディゲミキサー（株式会社マツボー製、商品名：レーディゲ（登録商標）ミキサーＭ２０）で混合し、得られた混合物を、成形プレス（株式会社テクノマルシチ製）を用いて鉄製の裏金（厚さ６ｍｍ）と共に加熱加圧成形した。得られた成形品を、２００℃で３．５時間熱処理し、ロータリー研磨機を用いて研磨し、５００℃で３分間のスコーチ処理を行って、
厚さ１０ｍｍ、投影面積５０ｃｍ２の摩擦材を有するディスクブレーキパッドを得た。
[Making disc brake pads]
<Examples 1 to 4 and Comparative Examples 1 to 4>
The materials were blended according to the blending ratio (% by mass) shown in Table 1 to obtain each friction material composition.
Next, this friction material composition was mixed with a Ladyge mixer (manufactured by Matsubo Co., Ltd., trade name: Ladyge (registered trademark) mixer M20), and the obtained mixture was subjected to a molding press (manufactured by Technomarushichi Co., Ltd.). It was heat-press molded together with an iron backing metal (thickness 6 mm). The obtained molded product was heat-treated at 200 ° C. for 3.5 hours, polished using a rotary grinding machine, and scorch-treated at 500 ° C. for 3 minutes.
A disc brake pad having a friction material having a thickness of 10 mm and a projected area of 50 cm 2 was obtained.
実施例で用いた硫酸カルシウム繊維の詳細は以下の通りである。
（繊維長）
・平均繊維長：１６．２μｍ
・最大繊維長：８５．４μｍ
・最小繊維長：２．９μｍ
（繊維径）
・平均繊維径：１．１μｍ
・最大繊維径：５．４μｍ
・最小繊維径：０．１５μｍ
（アスペクト比）
・平均アスペクト比：１６．２
（結晶構造）
・結晶構造：II型無水石膏（不溶性無水石膏）
なお、上記の硫酸カルシウム繊維の平均繊維長、平均繊維径及び平均アスペクト比は、走査型電子顕微鏡（日本電子株式会社製、型番：ＪＳＭ－６０１０ＰＬＵＳ／ＬＡ）によって、任意の５０本の硫酸カルシウム繊維を観察し、各々について、繊維長、繊維径及びアスペクト比を測定し、それらの平均値として算出した。
また、硫酸カルシウム繊維の最大繊維長、最小繊維長、最大繊維径及び最小繊維径は、平均繊維長及び平均繊維径の測定で観察した任意の５０本の硫酸カルシウム繊維のうちの最大繊維長、最小繊維長、最大繊維径及び最小繊維径とした。
各実施例及び比較例で共通して使用されている上記以外の成分については、全ての実施例及び比較例で同じ材料を使用した。
The details of the calcium sulfate fiber used in the examples are as follows.
(Fiber length)
-Average fiber length: 16.2 μm
-Maximum fiber length: 85.4 μm
-Minimum fiber length: 2.9 μm
(Fiber diameter)
・ Average fiber diameter: 1.1 μm
-Maximum fiber diameter: 5.4 μm
-Minimum fiber diameter: 0.15 μm
(aspect ratio)
・ Average aspect ratio: 16.2
(Crystal structure)
-Crystal structure: Type II anhydrous gypsum (insoluble anhydrous gypsum)
The average fiber length, average fiber diameter, and average aspect ratio of the above calcium sulfate fibers can be determined by using a scanning electron microscope (manufactured by Nippon Denshi Co., Ltd., model number: JSM-6010PLUS / LA) to determine any 50 calcium sulfate fibers. Was observed, and the fiber length, fiber diameter, and aspect ratio were measured for each, and calculated as the average value thereof.
Further, the maximum fiber length, the minimum fiber length, the maximum fiber diameter and the minimum fiber diameter of the calcium sulfate fiber are the maximum fiber length of any 50 calcium sulfate fibers observed in the measurement of the average fiber length and the average fiber diameter. The minimum fiber length, maximum fiber diameter and minimum fiber diameter were set.
For components other than the above, which are commonly used in each Example and Comparative Example, the same material was used in all Examples and Comparative Examples.
［一般性能試験］
一般性能試験は、ＪＡＳＯ Ｃ４０６（一般性能試験）に準拠して実施した。具体的には、１／５スケールテスター（慣性３．０ｋｇ・ｍ２）と上記ディスクブレーキパッドから切り出した１９ｍｍ×４４ｍｍのテストピースを用い、第一フェード試験の平均摩擦係数μの最小値と第二フェード試験の平均摩擦係数μの最小値を求めた。結果を表１に示す。
[General performance test]
The general performance test was carried out in accordance with JASO C406 (general performance test). Specifically, using a 1/5 scale tester (inertia 3.0 kg ・ m 2 ) and a 19 mm × 44 mm test piece cut out from the disc brake pad, the minimum value of the average friction coefficient μ in the first fade test and the first The minimum value of the average friction coefficient μ in the two-fade test was determined. The results are shown in Table 1.
［高温高速制動試験］
上記一般性能試験を実施した後に、ローターの温度を５０℃以下まで冷却し、昇温制動後に１５０ｋｍ／ｈから５０ｋｍ／ｈまで減速度０．４Ｇで４０秒間隔の制動を１５回行い、試験後のブレーキパッド摩耗量を求めた。結果を表１に示す。
[High temperature high speed braking test]
After performing the above general performance test, the temperature of the rotor is cooled to 50 ° C. or lower, and after heating and braking, braking is performed 15 times at a deceleration of 0.4 G from 150 km / h to 50 km / h at intervals of 40 seconds. The amount of brake pad wear was calculated. The results are shown in Table 1.
表１から、硫酸カルシウム繊維を含有しない比較例１の摩擦材は、フェード試験における平均摩擦係数μの最小値が比較的良好であるが、高温高速制動時のブレーキパッド摩耗量が不十分であった。
比較例１の摩擦材を基準として、硫酸バリウムの一部をアラミド繊維に置換した比較例２の摩擦材は、高温高速制動時のブレーキパッド摩耗量は良好であるが、フェード試験における平均摩擦係数μの最小値が不十分であった。
また、比較例１の摩擦材を基準として、硫酸バリウムの一部を鉱物繊維に置換した比較例３の摩擦材は、フェード試験における平均摩擦係数μの最小値は比較的良好であるが、高温高速制動時のブレーキパッド摩耗量に劣っていた。
また、比較例１の摩擦材を基準として、チタン酸カリウムの一部を硫酸バリウムに置換した比較例４の摩擦材は、高温高速制動時のブレーキパッド摩耗量が著しく悪かった。
これに対して、比較例１の摩擦材を基準として、硫酸バリウムの一部を硫酸カルシウム繊維に置換した実施例１及び２、鉱物繊維を硫酸カルシウム繊維に置換した実施例３、チタン酸カリウムの一部を硫酸カルシウム繊維に置換した実施例４は、フェード試験における平均摩擦係数μの最小値、高温高速制動試験のブレーキパッド摩耗量が全て良好であり、これらを両立できていることが分かる。
From Table 1, the friction material of Comparative Example 1 containing no calcium sulfate fiber has a relatively good minimum value of the average friction coefficient μ in the fade test, but the amount of brake pad wear during high temperature and high speed braking is insufficient. rice field.
The friction material of Comparative Example 2 in which a part of barium sulfate is replaced with aramid fiber based on the friction material of Comparative Example 1 has a good amount of brake pad wear during high temperature and high speed braking, but the average friction coefficient in the fade test. The minimum value of μ was insufficient.
Further, the friction material of Comparative Example 3 in which a part of barium sulfate is replaced with mineral fibers based on the friction material of Comparative Example 1 has a relatively good minimum value of the average friction coefficient μ in the fade test, but has a high temperature. The amount of brake pad wear during high-speed braking was inferior.
Further, the friction material of Comparative Example 4 in which a part of potassium titanate was replaced with barium sulfate based on the friction material of Comparative Example 1 had a significantly poor amount of brake pad wear during high temperature and high speed braking.
On the other hand, with reference to the friction material of Comparative Example 1, Examples 1 and 2 in which a part of barium sulfate was replaced with calcium sulfate fiber, Example 3 in which mineral fiber was replaced with calcium sulfate fiber, and potassium titanate were used. In Example 4 in which a part of the calcium sulfate fiber was replaced, the minimum value of the average friction coefficient μ in the fade test and the amount of brake pad wear in the high-temperature high-speed braking test were all good, and it can be seen that both of these are compatible.
１ バックプレート
１１ バックプレートの摩擦材が配置される面
１２ バックプレートの他方の面
２ 摩擦材（上張り材）
３ 下張り材
1 Back
3 Underlaying material
Claims (15)
前記摩擦材は、銅の含有量が、前記摩擦材全量に対して０．５質量％未満、かつ、スチール繊維の含有量が、前記摩擦材全量に対して２５質量％以下であり、硫酸カルシウム繊維を、前記摩擦材全量に対して、１～２０質量％含有する、摩擦部材。 A friction member with a friction material and a slush fund.
The friction material has a copper content of less than 0.5% by mass with respect to the total amount of the friction material, a steel fiber content of 25% by mass or less with respect to the total amount of the friction material, and calcium sulfate. A friction member containing 1 to 20% by mass of fibers with respect to the total amount of the friction material.