JP2021178897A - Manufacturing method of organopolysiloxane crude rubber, and, silicone rubber composition using crude rubber - Google Patents
Manufacturing method of organopolysiloxane crude rubber, and, silicone rubber composition using crude rubber Download PDFInfo
- Publication number
- JP2021178897A JP2021178897A JP2020083666A JP2020083666A JP2021178897A JP 2021178897 A JP2021178897 A JP 2021178897A JP 2020083666 A JP2020083666 A JP 2020083666A JP 2020083666 A JP2020083666 A JP 2020083666A JP 2021178897 A JP2021178897 A JP 2021178897A
- Authority
- JP
- Japan
- Prior art keywords
- organopolysiloxane
- silicone rubber
- group
- formula
- rubber composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、オルガノポリシロキサン生ゴムの製造方法と、その生ゴムを用いたシリコーンゴム組成物とに関する。 The present invention relates to a method for producing an organopolysiloxane raw rubber and a silicone rubber composition using the raw rubber.
一般的にシリコーンゴムは耐候性、耐久性、耐熱性、生理不活性、着色性などに優れているため、建築材料、電気電子部品、事務機器、自動車部品、医療器具など様々な分野で使用されている。 Generally, silicone rubber has excellent weather resistance, durability, heat resistance, physiological inertness, coloring property, etc., so it is used in various fields such as building materials, electrical and electronic parts, office equipment, automobile parts, and medical equipment. ing.
シリコーンゴムは、シリコーンポリマーそのもの自体の強度が小さいため、煙霧質シリカ、沈降シリカなどの補強性シリカを配合したものが通常使用されている。しかし、シリコーンゴムの強度を増加させるために、シリコーンポリマーに補強性シリカを多量に添加すると、得られるシリコーンゴム組成物のウイリアムス可塑度が高くなりすぎ、かえって作業性に劣り、加工時の経済性を悪くしてしまう。更に、補強性シリカを高充填した場合、クレープハードニング性（可塑戻り）が非常に高くなるため、輸送保管後に、十分な粗練りが必要であったり、更には粗練り作業すらできないほどのクレープハードニングを生じることがある。 Since the strength of the silicone polymer itself is small, the silicone rubber usually contains a reinforcing silica such as fumigant silica or precipitated silica. However, if a large amount of reinforcing silica is added to the silicone polymer in order to increase the strength of the silicone rubber, the Williams plasticity of the obtained silicone rubber composition becomes too high, which is rather inferior in workability and economical in processing. Will make it worse. Furthermore, when the reinforcing silica is highly filled, the crepe hardening property (plastic return) becomes very high, so that sufficient crepe kneading is required after transportation and storage, and even crepe kneading work cannot be performed. May cause hardening.
クレープハードニング性は、分散剤を多く添加することにより抑えられ、改善され得る。しかし、分散剤を多く添加すると、シリコーンゴム組成物の表面のべたつきが増え、ロール粘着が大きくなって作業性が悪くなり、更に該組成物の硬化物の機械的強度も悪くなる。 The crepe hardening property can be suppressed and improved by adding a large amount of dispersant. However, when a large amount of dispersant is added, the stickiness of the surface of the silicone rubber composition increases, the roll adhesion becomes large, the workability deteriorates, and the mechanical strength of the cured product of the composition also deteriorates.
特許文献１では、長期保存してもウイリアムス可塑度の変化が少ないシリコーンゴムとして、オルガノポリシロキサン生ゴムと、吸着炭素量が２重量％以上で疎水化度が５０容積％以上である疎水性煙霧質シリカと、分散剤としてシラノール基含有低重合度ケイ素化合物とを用いている。オルガノポリシロキサン生ゴムの末端封鎖率の有効性を述べてはいるが、未封鎖率が８％と高く、十分な効果を得られているとは言い難い。 In Patent Document 1, as a silicone rubber having a small change in Williams plasticity even after long-term storage, an organopolysiloxane raw rubber and a hydrophobic fumigant having an adsorbed carbon content of 2% by weight or more and a hydrophobicity of 50% by volume or more are used. Silica and a silanol group-containing low polymerization degree silicon compound are used as a dispersant. Although the effectiveness of the terminal blockage rate of the organopolysiloxane raw rubber is stated, the unsealed rate is as high as 8%, and it cannot be said that a sufficient effect is obtained.
末端封鎖率の高いオルガノポリシロキサン生ゴムは、特許文献２、特許文献３等に記載された公知方法によって製造した場合、末端封止剤を用いても重合中に微量混入する水により末端基がシラノール基で停止したまま残ってしまうので、ヘキサオルガノジシラザンとトリオルガノクロロシランを大過剰に添加する必要があった。この場合、末端封鎖後に塩化アンモニウムが発生し、オルガノポリシロキサン生ゴムが白濁してしまい、上記シリコーンゴムの特性を満たせないものがある。発生した塩化アンモニウムを取り除くには、オルガノポリシロキサン生ゴムを大過剰の有機溶媒に溶解させ、水で洗浄する必要があるため、不経済であり実用的ではない。 When the organopolysiloxane raw rubber having a high end-sealing ratio is produced by the known methods described in Patent Documents 2, Patent Document 3, etc., the terminal group is silanol due to water mixed in a small amount during polymerization even if an end-sealing agent is used. Hexaorganodisilazane and triorganochlorosilane had to be added in large excesses as they remained stationary at the group. In this case, ammonium chloride is generated after the end is closed, and the organopolysiloxane raw rubber becomes cloudy, and some of the above-mentioned silicone rubber characteristics cannot be satisfied. In order to remove the generated ammonium chloride, it is necessary to dissolve the organopolysiloxane raw rubber in a large excess of organic solvent and wash it with water, which is uneconomical and impractical.
オルガノポリシロキサン生ゴムの製造において、重合触媒を失活させた後、Ｎ，Ｏ−ビス（トリアルキルシリル）アセトアミドを添加、混合して、生成物中のヒドロシリル基を低減させ、得られたオルガノポリシロキサン生ゴムを使用して、シリコーンゴム組成物を製造した時、シリコーンゴム組成物の経時によるクレープハードニング性が改善され、シリコーンゴム組成物の保存性が向上し、シリコーンゴム組成物使用時の作業性が改善できることが特許文献４に記載されている。しかし、末端封鎖後に取り除くのが困難なアセトアミドが発生してしまう問題があった。 In the production of organopolysiloxane raw rubber, after deactivating the polymerization catalyst, N, O-bis (trialkylsilyl) acetamide is added and mixed to reduce the hydrosilyl group in the product, and the obtained organopoly When a silicone rubber composition is produced using siloxane raw rubber, the crepe hardening property of the silicone rubber composition over time is improved, the storage stability of the silicone rubber composition is improved, and the work when using the silicone rubber composition is improved. It is described in Patent Document 4 that the property can be improved. However, there is a problem that acetamide, which is difficult to remove after the terminal blockage, is generated.
副生成物が残留しない方法として、環状オルガノポリシロキサンを熱分解型重合触媒の存在下、末端トリオルガノシリル基で封鎖された低分子量の直鎖状オルガノポリシロキサンと共に重合させ、重合終了後、減圧下で加熱して熱分解型重合触媒を失活させ、水分を除去する方法が特許文献５で開示されている。この方法は、末端単位のヒドロキシル基生成を防ぐとされているが、オルガノシリコーン生ゴムをトルエンに溶解させ、テトラメトキシシランとテトラプロピルチタネートの添加後の粘度変化を比較するだけで、末端封鎖率の具体的な記載はない。 As a method in which by-products do not remain, cyclic organopolysiloxane is polymerized with a low molecular weight linear organopolysiloxane sealed with a terminal triorganosilyl group in the presence of a pyrolysis type polymerization catalyst, and the pressure is reduced after the polymerization is completed. Patent Document 5 discloses a method of inactivating a pyrolysis type polymerization catalyst by heating underneath to remove water. This method is said to prevent the formation of hydroxyl groups in the terminal unit, but it is only necessary to dissolve organosilicone raw rubber in toluene and compare the changes in viscosity after the addition of tetramethoxysilane and tetrapropyl titanate. There is no specific description.
クレープハードニング性やシリコーンゴム組成物の加工性を向上したオルガノポリシロキサン生ゴムについて、末端封鎖率が１００％に近く、末端封鎖後に副生成物を容易に取り除ける方法はなかった。 With respect to the organopolysiloxane raw rubber having improved crepe hardening property and processability of the silicone rubber composition, the terminal closure rate was close to 100%, and there was no method for easily removing by-products after terminal closure.
本発明は、末端封鎖率が高く、副生成物の除去が容易なオルガノポリシロキサン生ゴムの製造方法、及びこの製造方法で得られたオルガノポリシロキサン生ゴムをベースポリマーとして用いた、経時におけるクレープハードニング性及び保存性が改善されたシリコーンゴム組成物を提供することを目的とする。 The present invention is a method for producing an organopolysiloxane raw rubber having a high terminal blockage rate and easy removal of by-products, and crepe hardening over time using the organopolysiloxane raw rubber obtained by this production method as a base polymer. An object of the present invention is to provide a silicone rubber composition having improved properties and storage stability.
本発明者は、上記目的を達成するため鋭意研究を重ねた結果、環状オルガノポリシロキサンをアルカリ性触媒の存在下で低分子量の直鎖状オルガノポリシロキサンと共に重合し、高分子量のオルガノポリシロキサン生ゴムを製造する場合、前記重合後、アルカリ性触媒を失活させてから、ジアルキルアミノビニルジアルキルシランを混合することにより、副生成物が残留せず、末端にヒドロキシル基をほとんど含まないオルガノポリシロキサン生ゴム（分子鎖両末端がビニルジアルキル基で封鎖されたオルガノポリシロキサン）が得られることを見出した。また、このようにして得られたオルガノポリシロキサン生ゴムをシリカ等の補強材と混練りし、シリコーンゴム組成物を製造した時、該シリコーンゴム組成物の硬化物（シリコーンゴム硬化物）の外観への影響がなく、シリコーンゴム組成物の経時におけるクレープハードニング性及び保存性が改善できることを見出し、本発明を完成した。 As a result of intensive studies to achieve the above object, the present inventor polymerizes a cyclic organopolysiloxane together with a low molecular weight linear organopolysiloxane in the presence of an alkaline catalyst to obtain a high molecular weight organopolysiloxane raw rubber. In the case of production, after deactivating the alkaline catalyst after the polymerization, the dialkylaminovinyldialkylsilane is mixed, so that no by-products remain and the organopolysiloxane raw rubber containing almost no hydroxyl group at the terminal (molecule). It has been found that an organopolysiloxane (organopolysiloxane) in which both ends of the chain are sealed with a vinyl dialkyl group) can be obtained. Further, when the organopolysiloxane raw rubber thus obtained is kneaded with a reinforcing material such as silica to produce a silicone rubber composition, the appearance of the cured product (silicone rubber cured product) of the silicone rubber composition is obtained. The present invention has been completed by finding that the crepe hardening property and storage stability of the silicone rubber composition over time can be improved without the influence of the above.
従って、本発明は、オルガノポリシロキサン生ゴムの製造方法、及び、その生ゴムを用いたシリコーンゴム組成物を提供するものである。 Therefore, the present invention provides a method for producing an organopolysiloxane raw rubber and a silicone rubber composition using the raw rubber.
〔１〕
オルガノポリシロキサン生ゴムの製造方法であって、
（Ｉ）下記式（１）で示される環状オルガノシロキサンを、
アルカリ性触媒の存在下で、ジオルガノシロキサン単位が１〜２００の直鎖状オルガノシロキサンと共に重合する工程、
（ＩＩ）前記アルカリ性触媒を失活させる工程、
（ＩＩＩ）工程（ＩＩ）で得られたオルガノシロキサンと、下記式（２）
で示され、沸点が１６５℃以下であるジアルキルアミノビニルジアルキルシランとを混合する工程、及び
（ＩＶ）未反応のジアルキルアミノビニルジアルキルシラン、及び、副生成物を除去する工程、
を有する、下記式（４）
で示されるオルガノポリシロキサン生ゴムの製造方法。
〔２〕
（Ａ）下記式（４）
で示されるオルガノポリシロキサン生ゴム：１００質量部
（Ｂ）ＢＥＴ吸着法による比表面積が５０ｍ2／ｇ以上の補強性シリカ：１０〜１００質量部、及び
（Ｃ）硬化剤：有効量
を含有するシリコーンゴム組成物。
〔３〕
〔２〕に記載のシリコーンゴム組成物の硬化物。
[1]
Organopolysiloxane A method for producing raw rubber.
(I) The cyclic organosiloxane represented by the following formula (1)
The step of polymerizing with a linear organosiloxane with 1-200 diorganosiloxane units in the presence of an alkaline catalyst,
(II) Step of deactivating the alkaline catalyst,
(III) Organosiloxane obtained in step (II) and the following formula (2)
The step of mixing with the dialkylaminovinyldialkylsilane having a boiling point of 165 ° C. or lower, and (IV) the step of removing the unreacted dialkylaminovinyldialkylsilane and the by-products.
The following formula (4)
A method for producing an organopolysiloxane raw rubber shown by.
[2]
(A) The following formula (4)
Organopolysiloxane raw rubber represented by: 100 parts by mass (B) Reinforcing silica having a specific surface area of 50 m 2 / g or more by the BET adsorption method: 10 to 100 parts by mass, and (C) Hardener: Silicone containing an effective amount Rubber composition.
[3]
A cured product of the silicone rubber composition according to [2].
本発明は、末端封鎖率が高く、副生成物の除去が容易なオルガノポリシロキサン生ゴムの製造方法で、このようにして得られたオルガノポリシロキサン生ゴムをシリカ等の補強材と混練りし、シリコーンゴム組成物としたものは、該組成物を硬化したとき、外観への影響がなく、経時におけるクレープハードニング性及び保存性が改善されたものとなる。
なお本発明において末端封鎖率とは、オルガノポリシロキサンが末端封止剤によってトリオルガノシロキシ基に封鎖された封鎖率を示す。
The present invention is a method for producing an organopolysiloxane raw rubber having a high terminal blockage rate and easy removal of by-products. The organopolysiloxane raw rubber thus obtained is kneaded with a reinforcing material such as silica to form silicone. When the composition is cured, the rubber composition has no effect on the appearance and has improved crepe hardening property and storage stability over time.
In the present invention, the terminal blockade rate indicates the blockade rate at which organopolysiloxane is sealed to a triorganosyloxy group by a terminal capping agent.
［（Ａ）オルガノポリシロキサン生ゴム］
Ｉ．オルガノポリシロキサン生ゴムの重合工程
本発明は、環状オルガノシロキサンをアルカリ性触媒の存在下で低分子量の直鎖状オルガノシロキサンと共に重合して、高分子量のオルガノポリシロキサンを得るもので、このアルカリ性触媒によるオルガノポリシロキサンの重合方法は公知であり、例えば、環状オルガノシロキサン及び低分子量の直鎖状オルガノシロキサンに少量のアルカリ性触媒を添加し、１００〜１８０℃の加温下に平衡化反応させることによって行われる。
[(A) Organopolysiloxane raw rubber]
I. Polymerization process of organopolysiloxane raw rubber In the present invention, cyclic organosiloxane is polymerized together with low molecular weight linear organosiloxane in the presence of an alkaline catalyst to obtain a high molecular weight organopolysiloxane. A method for polymerizing a polysiloxane is known, and is performed, for example, by adding a small amount of an alkaline catalyst to a cyclic organosiloxane or a low molecular weight linear organosiloxane and allowing the equilibrium reaction to occur under heating at 100 to 180 ° C. ..
ここで、環状オルガノシロキサンは、下記式（１）で示されるものである。
式（１）中、Ｒ1は互いに独立に、炭素数１〜１０の非置換又は置換１価炭化水素基であり、特に炭素数１〜６のものが好ましい。炭素数１〜１０の非置換又は置換１価炭化水素基としては、例えば、メチル基、エチル基、ブチル基等のアルキル基、シクロヘキシル基、シクロペンチル基等のシクロアルキル基、ビニル基、アリル基等のアルケニル基、フェニル基、キシリル基等のアリール基、ベンジル基等のアラルキル基などやこれらの基の水素原子の一部又は全部がハロゲン原子、メルカプト基、グリシド基、（メタ）アクリロキシ基、アミノ基等で置換される基が挙げられる。ｍは３〜８の数であり、好ましくは３〜６の数である。 In the formula (1), R 1 is an unsubstituted or substituted monovalent hydrocarbon group having 1 to 10 carbon atoms independently of each other, and those having 1 to 6 carbon atoms are particularly preferable. Examples of the unsubstituted or substituted monovalent hydrocarbon group having 1 to 10 carbon atoms include an alkyl group such as a methyl group, an ethyl group and a butyl group, a cycloalkyl group such as a cyclohexyl group and a cyclopentyl group, a vinyl group and an allyl group. Alkenyl group, phenyl group, aryl group such as xylyl group, aralkyl group such as benzyl group, and some or all of the hydrogen atoms of these groups are halogen atom, mercapto group, glycid group, (meth) acryloxy group, amino. Examples thereof include a group substituted with a group or the like. m is a number of 3 to 8, preferably a number of 3 to 6.
上記環状オルガノシロキサンは、１種を単独で用いてもよく、２種類以上を併用してもよい。 The cyclic organosiloxane may be used alone or in combination of two or more.
低分子量の直鎖状オルガノシロキサンとしては、下記式（３）で示されるものが挙げられる。該低分子量の直鎖状オルガノシロキサンはオルガノポリシロキサン生ゴムの重合度を調節することができる。
式（３）中、Ｒ1は互いに独立に、炭素数１〜１０の非置換又は置換１価炭化水素基であり、Ｒ3は互いに独立に水酸基又はＲ1と同一のものである。上記直鎖状オルガノシロキサンは比較的低分子量が好ましく、具体的にはｎは１〜２００の数であり、好ましくは１〜１５０の数である。 In formula (3), R 1 is an unsubstituted or substituted monovalent hydrocarbon group having 1 to 10 carbon atoms independently of each other, and R 3 is independently the same as a hydroxyl group or R 1. The linear organosiloxane preferably has a relatively low molecular weight, and specifically, n is a number of 1 to 200, preferably a number of 1 to 150.
これらの出発原料となる環状オルガノシロキサンや低分子量の直鎖状オルガノシロキサンは、予め一部を蒸留又はシリカゲルなどの乾燥剤の使用により乾燥させることが好ましい。なお、低分子量の直鎖状オルガノシロキサンは、生成されるオルガノポリシロキサン生ゴムの重合度を決定する要因であり、所望の重合度に応じて環状オルガノシロキサンに対する比率を変動させればよい。 It is preferable to partially dry the cyclic organosiloxane or low molecular weight linear organosiloxane as a starting material in advance by distillation or using a desiccant such as silica gel. The low molecular weight linear organosiloxane is a factor that determines the degree of polymerization of the produced organopolysiloxane raw rubber, and the ratio to the cyclic organosiloxane may be varied according to the desired degree of polymerization.
本発明の製造方法で用いられるアルカリ性触媒としては、水酸化ナトリウム、水酸化カリウム、水酸化セシウムなどのアルカリ金属化合物又はそれらのシラノレートが例示される。また、これらのアルカリ性触媒は、酸性中和剤により失活させる場合があるが、１３０〜１５０℃の高温下において分解し、活性を失うもの（例えば、（ｎ−Ｃ4Ｈ9）4ＰＯＨなどの第４級ホスホニウム、（ＣＨ3）4ＮＯＨなどの第４級アンモニウム及びそれらのシラノレート等）を使用することもできる。 Examples of the alkaline catalyst used in the production method of the present invention include alkali metal compounds such as sodium hydroxide, potassium hydroxide and cesium hydroxide, or silanolates thereof. Further, these alkaline catalysts may be inactivated by an acidic neutralizing agent, but those that decompose at a high temperature of 130 to 150 ° C. and lose their activity (for example, (n-C 4 H 9 ) 4 POH, etc.) Quaternary phosphoniums, quaternary ammoniums such as (CH 3 ) 4 NOH and their silanolates, etc.) can also be used.
アルカリ触媒の配合量は、上記環状オルガノポリシロキサンと上記直鎖状オルガノポリシロキサンの総量に対し１〜１，０００ｐｐｍ、特に１０〜５００ｐｐｍとすることが好ましい。上記範囲内であると十分な重合度が得られ、副生成物の除去が困難にならず、得られたシロキサン生ゴム（硬化物）の外観やにおい、耐熱性、架橋特性などに悪影響が生じない。 The blending amount of the alkaline catalyst is preferably 1 to 1,000 ppm, particularly 10 to 500 ppm, based on the total amount of the cyclic organopolysiloxane and the linear organopolysiloxane. Within the above range, a sufficient degree of polymerization can be obtained, removal of by-products is not difficult, and the appearance, odor, heat resistance, cross-linking characteristics, etc. of the obtained siloxane raw rubber (cured product) are not adversely affected. ..
上記出発原料を用いた平衡化反応は、通常の条件で行うことができ、例えば１００〜１７０℃、好ましくは１１０〜１６５℃で、３０分〜６時間、好ましくは２〜５時間の反応条件で行うことができる。 The equilibration reaction using the above starting material can be carried out under normal conditions, for example, at 100 to 170 ° C., preferably 110 to 165 ° C., for 30 minutes to 6 hours, preferably 2 to 5 hours. It can be carried out.
ＩＩ．アルカリ性触媒を失活させる工程
上記平衡化反応後は、アルカリ性触媒を、酸性中和剤、例えば塩酸、エチレンクロルヒドリン、酢酸、二酸化炭素等で中和処理を行ったり、熱分解処理するなどして失活させる。
中和処理において、酸性中和剤の添加量は、アルカリ性触媒に対して２モル倍量以上とすることが好ましく、より好ましくは３倍以上である。
熱分解処理は、用いる触媒によるが、具体的には１２０〜２００℃、好ましくは１３０〜１８０℃で、３０分〜６時間、好ましくは１〜３時間行う。
中和処理及び熱分解処理は、常温で行うことが好ましい。
また、アルカリ性触媒の失活後、酸性中和剤の未反応分の低揮発分を溜去することが好ましい。該低揮発分を除去する方法としては、１３０〜１８０℃、好ましくは１４５〜１７０℃で、１〜２４時間、好ましくは３〜１２時間処理する。
上記低揮発分を除去する方法は常圧又は減圧下で行ってよく、減圧する場合の圧力は２０〜０．０１ｍｍＨｇ、好ましくは１０〜０．１ｍｍＨｇである。
II. Step to inactivate the alkaline catalyst After the equilibration reaction, the alkaline catalyst is neutralized with an acidic neutralizing agent such as hydrochloric acid, ethylene chlorhydrin, acetic acid, carbon dioxide, etc., or pyrolyzed. To deactivate.
In the neutralization treatment, the amount of the acidic neutralizing agent added is preferably 2 mol times or more, more preferably 3 times or more the amount of the alkaline catalyst.
The thermal decomposition treatment depends on the catalyst used, but specifically, it is carried out at 120 to 200 ° C., preferably 130 to 180 ° C. for 30 minutes to 6 hours, preferably 1 to 3 hours.
The neutralization treatment and the thermal decomposition treatment are preferably performed at room temperature.
Further, after deactivating the alkaline catalyst, it is preferable to distill off the low volatile content of the unreacted portion of the acidic neutralizing agent. As a method for removing the low volatile matter, treatment is carried out at 130 to 180 ° C., preferably 145 to 170 ° C. for 1 to 24 hours, preferably 3 to 12 hours.
The method for removing the low volatile matter may be carried out under normal pressure or reduced pressure, and the pressure when reduced pressure is 20 to 0.01 mmHg, preferably 10 to 0.1 mmHg.
ＩＩＩ．工程ＩＩで得られたオルガノシロキサンと、ジアルキルアミノビニルジアルキルシランとを混合する工程
本発明は、上記のようにアルカリ性触媒を失活させた後、得られたオルガノポリシロキサン生ゴムと、下記式（２）で示されるジアルキルアミノビニルジアルキルシランとを混合することを特徴とする。本発明において前記ジアルキルアミノビニルジアルキルシランは末端封止剤として作用する。
式（２）中、Ｒ2は互いに独立に、炭素数１〜５、好ましくは１〜４、更に好ましくは１〜３の非置換又は置換１価炭化水素基を表す。該１価炭化水素基としては、具体的には、メチル基、エチル基、プロピル基及びブチル基などのアルキル基が挙げられる。
上記ジアルキルアミノビニルジアルキルシランの具体例としては、ジメチルアミノビニルジメチルシラン（沸点：１０７℃）、ジエチルアミノビニルジメチルシラン（沸点：１２０℃）などが例示される。これらの沸点は１６５℃以下、好ましくは１６０℃以下、より好ましくは１５０℃以下である。沸点が１６５℃を超えると、工程ＩＶにおいて未反応のジアルキルアミノビニルジアルキルシランを取り除くことができず、シリコーンゴム組成物を硬化させる時に、硬化阻害を起こすことがある。
なお、上記ジアルキルアミノビニルジアルキルシランの沸点が１３０℃未満である場合には、オルガノポリシロキサン生ゴムの重合工程（上記工程Ｉ）における平衡化反応後に１００℃以下に冷却する工程か、又はアルカリ性触媒を失活させる工程（上記工程ＩＩ）における中和処理後又は熱分解処理後に１００℃以下に冷却する工程を設けることが好ましい。
In formula (2), R 2 independently represents an unsubstituted or substituted monovalent hydrocarbon group having 1 to 5 carbon atoms, preferably 1 to 4 carbon atoms, and more preferably 1 to 3 carbon atoms. Specific examples of the monovalent hydrocarbon group include alkyl groups such as a methyl group, an ethyl group, a propyl group and a butyl group.
Specific examples of the dialkylaminovinyldialkylsilane include dimethylaminovinyldimethylsilane (boiling point: 107 ° C.), diethylaminovinyldimethylsilane (boiling point: 120 ° C.), and the like. These boiling points are 165 ° C. or lower, preferably 160 ° C. or lower, and more preferably 150 ° C. or lower. If the boiling point exceeds 165 ° C., the unreacted dialkylaminovinyldialkylsilane cannot be removed in step IV, which may cause curing inhibition when the silicone rubber composition is cured.
When the boiling point of the dialkylaminovinyldialkylsilane is less than 130 ° C., a step of cooling to 100 ° C. or lower after the equilibration reaction in the polymerization step of the organopolysiloxane raw rubber (step I), or an alkaline catalyst is used. It is preferable to provide a step of cooling to 100 ° C. or lower after the neutralization treatment or the thermal decomposition treatment in the deactivation step (step II).
上記式（２）で示されるジアルキルアミノビニルジアルキルシランの添加量は、上記式（３）で示した低分子量の直鎖状オルガノシロキサンの等モル量〜５０モル倍量で十分であり、等モル量〜２０モル倍量程度でよい。また、その添加は、工程ＩＩでアルカリ性触媒を失活させた後であれば、低揮発分の溜去前又は溜去後を問わない。 As the addition amount of the dialkylaminovinyldialkylsilane represented by the above formula (2), an equimolar amount to 50 mol times the amount of the low molecular weight linear organosiloxane represented by the above formula (3) is sufficient. The amount may be about 20 mol times. Further, the addition thereof may be performed before or after the distillation of the low volatile component as long as it is after the alkaline catalyst is deactivated in the step II.
アルカリ性触媒が活性な状態で、上記式（２）で示されるジアルキルアミノビニルジアルキルシランを添加すると、かかるジアルキルアミノビニルアルキルシランが重合体の末端停止剤として作用し、所望の重合度を持つ生成物を得ることができない。 When the dialkylaminovinyldialkylsilane represented by the above formula (2) is added while the alkaline catalyst is active, the dialkylaminovinylalkylsilane acts as a terminal terminator of the polymer, and a product having a desired degree of polymerization is produced. Cannot be obtained.
かかるジアルキルアミノビニルジアルキルシランの添加後は、反応を完結させるため、室温〜１５０℃、好ましくは５０〜１３０℃で、１０分〜５時間、好ましくは３０分〜１時間の保温を行うことが好ましい。 After the addition of the dialkylaminovinyldialkylsilane, it is preferable to keep the temperature at room temperature to 150 ° C., preferably 50 to 130 ° C. for 10 minutes to 5 hours, preferably 30 minutes to 1 hour in order to complete the reaction. ..
ＩＶ．未反応のジアルキルアミノビニルジアルキルシラン、及び、副生成物の低揮発分を除去する工程
得られたオルガノポリシロキサン生ゴム中に、未反応のジアルキルアミノビニルジアルキルシラン、及び、副生成物のジアルキルアミンが残留すると、該オルガノポリシロキサン生ゴムを用いて得られたシリコーンゴム組成物に加硫剤を入れて硬化させる時に、硬化阻害を起こすことがある。その為、未反応のジアルキルアミノビニルジアルキルシラン、及び副生成物等の低揮発分を除去する必要がある。該低揮発分を除去する方法としては、１３０〜１８０℃、好ましくは１４５〜１７０℃で、３０分〜１２時間、好ましくは１〜６時間処理する。上記反応は常圧又は減圧下で行ってよく、減圧する場合は２０〜０．０１ｍｍＨｇ、好ましくは１０〜０．１ｍｍＨｇである。
副生成物のジアルキルアミンの沸点は、好ましくは１６５℃以下、より好ましくは１６０℃以下、さらに好ましくは１５０℃以下であると効率よく除去することができる。
IV. Step to remove unreacted dialkylaminovinyldialkylsilane and low volatile content of by-product In the obtained organopolysiloxane raw rubber, unreacted dialkylaminovinyldialkylsilane and by-product dialkylamine are contained. If it remains, it may cause curing inhibition when a vulcanizing agent is added to a silicone rubber composition obtained by using the organopolysiloxane raw rubber and cured. Therefore, it is necessary to remove unreacted dialkylaminovinyldialkylsilane and low volatile components such as by-products. As a method for removing the low volatile matter, treatment is carried out at 130 to 180 ° C., preferably 145 to 170 ° C. for 30 minutes to 12 hours, preferably 1 to 6 hours. The above reaction may be carried out under normal pressure or reduced pressure, and when the pressure is reduced, it is 20 to 0.01 mmHg, preferably 10 to 0.1 mmHg.
The boiling point of the by-product dialkylamine is preferably 165 ° C. or lower, more preferably 160 ° C. or lower, and even more preferably 150 ° C. or lower, so that it can be efficiently removed.
本発明で得られるオルガノポリシロキサン生ゴムは、下記式（４）で示される分子鎖両末端がビニルジアルキル基で封鎖されたオルガノポリシロキサンである。
式（４）中、Ｒ1は互いに独立に、炭素数１〜１０の非置換又は置換１価炭化水素基ある。１分子中、Ｒ1は、５０％以上がメチル基であることが好ましく、８０％以上がメチル基であることがより好ましく、側鎖アルケニル基及び末端アルケニル基以外のすべてのＲ1がメチル基であることが更に好ましい。このため、式（１）、式（３）の化合物を適宜選択することが好ましい。 In formula (4), R 1 is an unsubstituted or substituted monovalent hydrocarbon group having 1 to 10 carbon atoms independently of each other. In one molecule , 50% or more of R 1 is preferably a methyl group, 80% or more is more preferably a methyl group, and all R 1 except the side chain alkenyl group and the terminal alkenyl group are methyl groups. Is more preferable. Therefore, it is preferable to appropriately select the compounds of the formulas (1) and (3).
また、式（４）のオルガノポリシロキサン生ゴムは、１分子中に少なくとも２個のアルケニル基を有することが好ましく、上記式（４）及び（５）中、ケイ素原子に結合する基（即ち、式（４）におけるＲ1、式（５）におけるＲ2、及び末端ビニル基）のうち、０．００１〜２０％、特に０．０１〜１０％がアルケニル基であることが好ましい。このアルケニル基としては、好ましくはビニル基又はアリル基であり、特に好ましくはビニル基である。
なお、本発明において、アルケニル基含有量は以下に記載した測定条件で、日本電子（株）製４００ＭＨｚ−ＮＭＲ測定装置を用いて1Ｈ−ＮＭＲスペクトルによって測定した積分比から算出した値を指すものとする。
［測定条件］
・測定周波数：４００ＭＨｚ
・測定サンプル：ポリシロキサンの重クロロホルム２５質量％溶液を使用した。
・内部標準物質：クロロホルム
Further, the organopolysiloxane raw rubber of the formula (4) preferably has at least two alkenyl groups in one molecule, and in the above formulas (4) and (5), a group bonded to a silicon atom (that is, a formula). R 1 in (4), of the formula R 2 in (5), and terminal vinyl groups), it is preferable from 0.001 to 20%, in particular 0.01% to 10% is alkenyl group. The alkenyl group is preferably a vinyl group or an allyl group, and particularly preferably a vinyl group.
In the present invention, the alkenyl group content refers to a value calculated from an integral ratio measured by 1 H-NMR spectrum using a 400 MHz-NMR measuring device manufactured by JEOL Ltd. under the measurement conditions described below. And.
[Measurement condition]
・ Measurement frequency: 400MHz
-Measurement sample: A 25% by mass solution of deuterated chloroform of polysiloxane was used.
・ Internal standard substance: Chloroform
上記式（４）のオルガノポリシロキサン生ゴムの重合度ｌは、３，０００以上の数、好ましくは３，０００〜１００，０００、より好ましくは３，０００〜５０，０００の高重合度（高粘度）であって、室温（２５℃）において自己流動性のない非液状のオルガノポリシロキサンである。
アルケニル基含有オルガノポリシロキサン生ゴムは、本発明の組成物の主剤（ベースポリマー）である。
重合度が３，０００未満であると、十分なゴム強度が得られない。
なお、この重合度は、ＧＰＣ（ゲルパーミエーションクロマトグラフィ）分析におけるポリスチレン換算の重量平均重合度として求められる。
The degree of polymerization l of the organopolysiloxane raw rubber of the above formula (4) is a number of 3,000 or more, preferably 3,000 to 100,000, and more preferably 3,000 to 50,000 with a high degree of polymerization (high viscosity). ), Which is a non-liquid organopolysiloxane having no self-fluidity at room temperature (25 ° C.).
The alkenyl group-containing organopolysiloxane raw rubber is the main agent (base polymer) of the composition of the present invention.
If the degree of polymerization is less than 3,000, sufficient rubber strength cannot be obtained.
The degree of polymerization is determined as a polystyrene-equivalent weight average degree of polymerization in GPC (gel permeation chromatography) analysis.
本発明中で言及する重量平均重合度とは、下記条件で測定したゲルパーミエーションクロマトグラフィ（ＧＰＣ）によるポリスチレンを標準物質として算出した値を指すこととする。
［測定条件］
・展開溶媒：トルエン
・流量：１ｍＬ／ｍｉｎ
・検出器：示差屈折率検出器（ＲＩ）
・カラム：ＫＦ−８０５Ｌ×２本（Ｓｈｏｄｅｘ社製）
・カラム温度：２５℃
・試料注入量：３０μＬ（濃度０．２質量％のトルエン溶液）
The weight average degree of polymerization referred to in the present invention refers to a value calculated using polystyrene by gel permeation chromatography (GPC) measured under the following conditions as a standard substance.
[Measurement condition]
・ Developing solvent: Toluene ・ Flow rate: 1 mL / min
-Detector: Differential refractometer (RI)
-Column: KF-805L x 2 (manufactured by Shodex)
-Column temperature: 25 ° C
-Sample injection amount: 30 μL (toluene solution with a concentration of 0.2% by mass)
本発明において末端封鎖率とは、分子鎖両末端が末端封止剤であるジアルキルアミノビニルジアルキルシランによってビニルジアルキルシロキシ基に封鎖された封鎖率を示す。通常は、主鎖がジオルガノシロキサン単位の繰り返しからなり、分子鎖両末端がビニルジアルキルシロキシ基で封鎖された、直鎖状のジオルガノポリシロキサンであって、少なくとも分子鎖両末端が９５％以上、好ましくは９７％以上、より好ましくは９８％以上封鎖されたものである。
末端封鎖率が９５％未満であると、得られたオルガノポリシロキサン生ゴムを用いてシリコーンゴム組成物とした際、該シリコーンゴム組成物に経時におけるクレープハードニングが生じ、シリコーンゴム組成物の保存性及び加工性が悪化する。
In the present invention, the terminal blockade rate indicates the blockade rate at which both ends of the molecular chain are sealed with a vinyldialkylsiloxy group by a dialkylaminovinyldialkylsilane which is a terminal sealant. Usually, the main chain consists of repeating diorganosiloxane units, and both ends of the molecular chain are sealed with vinyldialkylsiloxy groups, which is a linear diorganopolysiloxane with at least 95% or more of both ends of the molecular chain. , Preferably 97% or more, more preferably 98% or more.
When the terminal sealing ratio is less than 95%, when the obtained organopolysiloxane raw rubber is used to prepare a silicone rubber composition, the silicone rubber composition undergoes crepe hardening over time, and the silicone rubber composition has a shelf life. And workability deteriorates.
本明細書中で言及する末端封鎖率とは以下に記載した日本電子（株）製４００ＭＨｚ−ＮＭＲ測定装置を用いて29Ｓｉ−ＮＭＲスペクトルによって測定した積分比から算出した値を指すものとする。
［測定条件］
・測定周波数：４００ＭＨｚ
・測定サンプル：ポリシロキサンの重クロロホルム２５質量％溶液を使用した。
・内部標準物質：クロロホルム
The terminal blockage rate referred to in the present specification refers to a value calculated from an integral ratio measured by a 29 Si-NMR spectrum using a 400 MHz-NMR measuring device manufactured by JEOL Ltd. described below.
[Measurement condition]
・ Measurement frequency: 400MHz
-Measurement sample: A 25% by mass solution of deuterated chloroform of polysiloxane was used.
・ Internal standard substance: Chloroform
［シリコーンゴム組成物］
オルガノポリシロキサン生ゴムの製造方法により得られた上記式（４）で示されるオルガノポリシロキサン生ゴムを用いたシリコーンゴム組成物について説明する。
なお、本発明において、補強性フィラーの比表面積は、ＢＥＴ吸着法により測定された値である。シリコーンゴム組成物とは、室温（２５℃）において自己流動性のない高粘度で非液状のミラブル型シリコーンゴム組成物であって、ロールミル（例えば、二本ロールミルや三本ロールミル）などの混練機で剪断応力下に均一に混練することが可能なシリコーンゴム組成物を意味する。また、オルガノポリシロキサン生ゴムとは、その重合度が３，０００〜１００，０００の高重合度（高粘度）であって、室温（２５℃）において自己流動性のない非液状のミラブル型オルガノポリシロキサン成分であることを意味する。
[Silicone rubber composition]
A silicone rubber composition using the organopolysiloxane raw rubber represented by the above formula (4) obtained by the method for producing an organopolysiloxane raw rubber will be described.
In the present invention, the specific surface area of the reinforcing filler is a value measured by the BET adsorption method. The silicone rubber composition is a highly viscous, non-liquid, mirable silicone rubber composition that does not have self-fluidity at room temperature (25 ° C.), and is a kneader such as a roll mill (for example, a two-roll mill or a three-roll mill). Means a silicone rubber composition that can be kneaded uniformly under shear stress. Further, the organopolysiloxane raw rubber is a non-liquid mirable type organopoly having a degree of polymerization of 3,000 to 100,000 and a high degree of polymerization (high viscosity) and no self-fluidity at room temperature (25 ° C.). It means that it is a siloxane component.
（Ａ）成分のオルガノポリシロキサン生ゴムは、上記式（４）で示されるものであり、各種用途に使用することができ、特にシリコーンゴム組成物の主剤（ベースポリマー）として、下記に詳述する成分と組み合わせて用いることができる。
なお、前記オルガノポリシロキサン生ゴムは、シリコーンゴム組成物において１種単独で用いても、重合度や分子構造の異なる２種以上を組み合わせて用いてもよい。
（Ａ）成分のオルガノポリシロキサン生ゴムは、本発明のシリコーンゴム組成物中、１０〜９５質量％含有することが好ましく、２０〜９０質量％含有することがより好ましく、３０〜８０質量％含有することがさらに好ましい。
The organopolysiloxane raw rubber of the component (A) is represented by the above formula (4) and can be used for various purposes, and is described in detail below as a main agent (base polymer) of a silicone rubber composition. It can be used in combination with the ingredients.
The organopolysiloxane raw rubber may be used alone in the silicone rubber composition, or may be used in combination of two or more having different degrees of polymerization and molecular structure.
The organopolysiloxane raw rubber of the component (A) is preferably contained in an amount of 10 to 95% by mass, more preferably 20 to 90% by mass, and more preferably 30 to 80% by mass in the silicone rubber composition of the present invention. Is even more preferable.
［（Ｂ）補強性シリカ］
（Ｂ）成分の補強性シリカは、本発明のシリコーンゴム組成物の主剤（ベースポリマー）と混合されるものであり、得られるシリコーンゴム硬化物に対して優れた機械的特性を付与する成分として作用する。該補強性シリカは、沈降シリカ（湿式シリカ）でも、ヒュームドシリカ（乾式シリカ）でもよい。
[(B) Reinforcing silica]
The reinforcing silica of the component (B) is mixed with the main agent (base polymer) of the silicone rubber composition of the present invention, and is used as a component that imparts excellent mechanical properties to the obtained cured silicone rubber. It works. The reinforcing silica may be precipitated silica (wet silica) or fumed silica (dry silica).
本発明において（Ｂ）成分の補強性シリカのＢＥＴ法による比表面積は、５０ｍ2／ｇ以上であることが必要であり、好ましくは１００〜４００ｍ2／ｇである。この比表面積が５０ｍ2／ｇ未満であると（Ｂ）成分による補強効果が不十分となる場合がある。 In the present invention, the specific surface area of the reinforcing silica of the component (B) by the BET method needs to be 50 m 2 / g or more, preferably 100 to 400 m 2 / g. If this specific surface area is less than 50 m 2 / g, the reinforcing effect of the component (B) may be insufficient.
（Ｂ）成分の補強性シリカは、未処理の状態で使用しても、必要に応じてオルガノポリシロキサン、オルガノポリシラザン、クロロシラン、アルコキシシラン等の有機ケイ素化合物（シリカ表面処理剤）で表面処理（具体的には疎水化処理）されたものを使用してもよい。疎水化処理を施した補強性シリカを用いると、（Ａ）成分中への分散性や補強性の面で好ましい。このとき、予め粉体の状態で、シリカ表面処理剤により直接表面疎水化処理されたものを用いてもよいし、シリカ微粉末と（Ａ）成分との混合時にシリカ表面処理剤を添加して、加熱混合することにより、表面が疎水化処理されるようにしてもよい。 Even if the reinforcing silica of the component (B) is used in an untreated state, it is surface-treated with an organosilicon compound (silica surface treatment agent) such as organopolysiloxane, organopolysilazane, chlorosilane, and alkoxysilane, if necessary. Specifically, those that have been hydrophobized may be used. It is preferable to use reinforcing silica that has been hydrophobized in terms of dispersibility and reinforcing property in the component (A). At this time, a powder that has been directly surface-hydrophobicized with a silica surface treatment agent may be used, or a silica surface treatment agent is added when the silica fine powder and the component (A) are mixed. , The surface may be hydrophobized by heating and mixing.
このようなシリカ表面処理剤は、本発明のシリコーンゴム組成物の主剤（ベースポリマー）と混合されるものであり、具体的に、トリメチルクロロシラン、ジメチルジクロロシラン、及びメチルトリクロロシランなどのクロロシラン類；ヘキサメチルジシラザン、１，３−ジビニル−１，１，３，３−テトラメチルジシラザンのようなシラザン類等の公知の処理剤が挙げられる。シリカ表面処理剤の使用量は、表面未処理のシリカ微粉末１００質量部に対し、好ましくは５〜７５質量部、より好ましくは５〜６０質量部である。
上記補強性シリカは、１種単独で用いても、２種以上を組み合わせて用いてもよい。
Such a silica surface treatment agent is mixed with the main agent (base polymer) of the silicone rubber composition of the present invention, and specifically, chlorosilanes such as trimethylchlorosilane, dimethyldichlorosilane, and methyltrichlorosilane; Known treatment agents such as silazans such as hexamethyldisilazane and 1,3-divinyl-1,1,3,3-tetramethyldisilazane can be mentioned. The amount of the silica surface treatment agent used is preferably 5 to 75 parts by mass, and more preferably 5 to 60 parts by mass with respect to 100 parts by mass of the untreated silica fine powder.
The reinforcing silica may be used alone or in combination of two or more.
（Ｂ）成分の補強性シリカの配合量は、（Ａ）成分のオルガノポリシロキサン１００質量部に対して１０〜１００質量部であり、好ましくは１０〜８０質量部であり、より好ましくは２０〜７０質量部である。この配合量が上記範囲を逸脱すると、得られるシリコーンゴム組成物の加工性が低下するだけでなく、該シリコーンゴム組成物の硬化物（シリコーンゴム硬化物）の機械的特性（引張り強度、引き裂き強度等）が不十分となるおそれがある。 The blending amount of the reinforcing silica of the component (B) is 10 to 100 parts by mass, preferably 10 to 80 parts by mass, and more preferably 20 to 100 parts by mass with respect to 100 parts by mass of the organopolysiloxane of the component (A). It is 70 parts by mass. If this blending amount deviates from the above range, not only the processability of the obtained silicone rubber composition is deteriorated, but also the mechanical properties (tensile strength, tear strength) of the cured product (silicone rubber cured product) of the silicone rubber composition are deteriorated. Etc.) may be insufficient.
［（Ｃ）硬化剤］
（Ｃ）成分の硬化剤は、本発明のシリコーンゴム組成物を硬化させ得るものであれば、特に限定されるものではなく、例えば下記の（Ｃ−１）付加反応硬化剤、及び／又は（Ｃ−２）有機過酸化物硬化剤が挙げられる。即ち、これらの硬化剤は、本発明のシリコーンゴム組成物において、（Ａ）成分のオルガノポリシロキサンと反応して架橋構造を形成し、本発明のシリコーンゴム硬化物を与えるものである。
[(C) Curing agent]
The curing agent for the component (C) is not particularly limited as long as it can cure the silicone rubber composition of the present invention. For example, the following (C-1) addition reaction curing agent and / or ( C-2) An organic peroxide curing agent can be mentioned. That is, these curing agents react with the organopolysiloxane of the component (A) to form a crosslinked structure in the silicone rubber composition of the present invention, and give the silicone rubber cured product of the present invention.
（Ｃ−１）付加反応硬化剤
付加反応硬化剤としては、オルガノハイドロジェンポリシロキサンとヒドロシリル化触媒とを組み合わせて用いることができる。
(C-1) Addition Reaction Curing Agent As the addition reaction curing agent, an organohydrogenpolysiloxane and a hydrosilylation catalyst can be used in combination.
オルガノハイドロジェンポリシロキサン
オルガノハイドロジェンポリシロキサンとしては、１分子中に、好ましくは２〜３００個、より好ましくは３〜２００個、更に好ましくは４〜１００個のケイ素原子に結合した水素原子（ＳｉＨ基）を含有すれば、直鎖状、環状、分枝状のいずれであってもよく、付加反応硬化型シリコーンゴム組成物の架橋剤として公知のオルガノハイドロジェンポリシロキサンを用いることができ、例えば、下記式（７）で表されるオルガノハイドロジェンポリシロキサンを用いることができる。
Ｒ6 aＨbＳｉＯ(4-a-b)/2 （７）
式（７）中、Ｒ6は互いに独立して、非置換又は置換の１価炭化水素基を示し、特に脂肪族不飽和結合を有さないものが好ましい。
なお、式（７）中、ａ、ｂは０≦ａ＜３、好ましくは１≦ａ≦２．２、０＜ｂ≦３、好ましくは０．００２≦ｂ≦１、０＜ａ＋ｂ≦３、好ましくは１．００２≦ａ＋ｂ≦３を満たす正数である。
Organohydrogenpolysiloxane As the organohydrogenpolysiloxane, hydrogen atoms (SiH) bonded to preferably 2 to 300, more preferably 3 to 200, still more preferably 4 to 100 hydrogen atoms in one molecule. As long as it contains a group), it may be linear, cyclic, or branched, and a known organohydrogenpolysiloxane can be used as a cross-linking agent for the addition reaction curable silicone rubber composition, for example. , Organohydrogenpolysiloxane represented by the following formula (7) can be used.
R 6 a H b SiO (4-ab) / 2 (7)
In the formula (7), R 6 represents an unsubstituted or substituted monovalent hydrocarbon group independently of each other, and is particularly preferably one having no aliphatic unsaturated bond.
In the formula (7), a and b are 0 ≦ a <3, preferably 1 ≦ a ≦ 2.2, 0 <b ≦ 3, preferably 0.002 ≦ b ≦ 1, 0 <a + b ≦ 3, It is preferably a positive number that satisfies 1.002 ≦ a + b ≦ 3.
前記オルガノハイドロジェンポリシロキサン中のＳｉＨ基は、分子鎖末端にあっても、分子鎖の途中にあっても、その両方にあってもよい。 The SiH group in the organohydrogenpolysiloxane may be at the end of the molecular chain, in the middle of the molecular chain, or both.
このようなオルガノハイドロジェンポリシロキサンとして、具体的には、例えば、１，１，３，３−テトラメチルジシロキサン、１，３，５，７−テトラメチルシクロテトラシロキサン、トリス（ハイドロジェンジメチルシロキシ）メチルシラン、トリス（ハイドロジェンジメチルシロキシ）フェニルシラン、メチルハイドロジェンシクロポリシロキサン、メチルハイドロジェンシロキサン・ジメチルシロキサン環状共重合体、両末端トリメチルシロキシ基封鎖メチルハイドロジェンポリシロキサン、両末端トリメチルシロキシ基封鎖ジメチルシロキサン・メチルハイドロジェンシロキサン共重合体、両末端ジメチルハイドロジェンシロキシ基封鎖ジメチルポリシロキサン、両末端ジメチルハイドロジェンシロキシ基封鎖ジメチルシロキサン・メチルハイドロジェンシロキサン共重合体、両末端トリメチルシロキシ基封鎖メチルハイドロジェンシロキサン・ジフェニルシロキサン共重合体、両末端トリメチルシロキシ基封鎖メチルハイドロジェンシロキサン・ジフェニルシロキサン・ジメチルシロキサン共重合体、両末端トリメチルシロキシ基封鎖メチルハイドロジェンシロキサン・メチルフェニルシロキサン・ジメチルシロキサン共重合体、両末端ジメチルハイドロジェンシロキシ基封鎖メチルハイドロジェンシロキサン・ジメチルシロキサン・ジフェニルシロキサン共重合体、両末端ジメチルハイドロジェンシロキシ基封鎖メチルハイドロジェンシロキサン・ジメチルシロキサン・メチルフェニルシロキサン共重合体、（ＣＨ3）2ＨＳｉＯ1/2単位と（ＣＨ3）3ＳｉＯ1/2単位とＳｉＯ4/2単位とからなる共重合体、（ＣＨ3）2ＨＳｉＯ1/2単位とＳｉＯ4/2単位とからなる共重合体、（ＣＨ3）2ＨＳｉＯ1/2単位とＳｉＯ4/2単位と（Ｃ6Ｈ5）3ＳｉＯ1/2単位とからなる共重合体などや、これらの化合物中のメチル基の一部又は全部を他のアルキル基や、フェニル基等に置換したものなどが挙げられる。このようなオルガノハイドロジェンポリシロキサンとしては、具体的に下記構造式の化合物を例示することができる。
これらのオルガノハイドロジェンポリシロキサンは、１種単独で用いても、２種以上を組み合わせて用いてもよい。
Specific examples of such an organohydrogenpolysiloxane include 1,1,3,3-tetramethyldisiloxane, 1,3,5,7-tetramethylcyclotetrasiloxane, and tris (hydrogendimethylsiloxy). ) Methylsilane, Tris (hydrogendimethylsiloxy) phenylsilane, methylhydrogencyclopolysiloxane, methylhydrogensiloxane / dimethylsiloxane cyclic copolymer, both-terminal trimethylsiloxy group blockage methylhydrogenpolysiloxane, both-terminal trimethylsiloxy group blockade Dimethylsiloxane / methylhydrogensiloxane copolymer, double-ended dimethylhydrogensiloxy group-blocked dimethylpolysiloxane, double-ended dimethylhydrogensiloxy group-blocked dimethylsiloxane / methylhydrogensiloxane copolymer, double-ended trimethylsiloxy group-blocked methylhydro Gensiloxane / diphenylsiloxane copolymer, double-ended trimethylsiloxy group-blocked methylhydrogensiloxane / diphenylsiloxane / dimethylsiloxane copolymer, double-ended trimethylsiloxy group-blocked methylhydrogensiloxane / methylphenylsiloxane / dimethylsiloxane copolymer, Both-ended dimethylhydrogensiloxy group-blocked methylhydrogensiloxane / dimethylsiloxane / diphenylsiloxane copolymer, both- ended dimethylhydrogensiloxy group-blocked methylhydrogensiloxane / dimethylsiloxane / methylphenylsiloxane copolymer, (CH 3) 2 Copolymer consisting of HSiO 1/2 unit and (CH 3 ) 3 SiO 1/2 unit and SiO 4/2 unit, (CH 3 ) 2 HSiO 1/2 unit and SiO 4/2 unit co-weight Combined, copolymers consisting of (CH 3 ) 2 HSiO 1/2 units, SiO 4/2 units and (C 6 H 5 ) 3 SiO 1/2 units, and some of the methyl groups in these compounds. Alternatively, those in which all of them are replaced with other alkyl groups, phenyl groups, or the like can be mentioned. Specific examples of such an organohydrogenpolysiloxane include compounds having the following structural formulas.
These organohydrogenpolysiloxanes may be used alone or in combination of two or more.
上記オルガノハイドロジェンポリシロキサンの配合量は、（Ａ）成分のオルガノポリシロキサン１００質量部に対し０．１〜４０質量部が好ましく、より好ましくは０．３〜２０質量部である。 The blending amount of the organohydrogenpolysiloxane is preferably 0.1 to 40 parts by mass, more preferably 0.3 to 20 parts by mass with respect to 100 parts by mass of the organopolysiloxane of the component (A).
また、上記オルガノハイドロジェンポリシロキサンは、（Ａ）成分中のケイ素原子に結合した脂肪族不飽和基（アルケニル基）に対するオルガノハイドロジェンポリシロキサン中のケイ素原子に結合した水素原子（ＳｉＨ基）のモル比（ＳｉＨ基／アルケニル基）が好ましくは０．５〜１０モル／モル、より好ましくは０．７〜５モル／モルとなるような量で配合することが望ましい。該モル比（ＳｉＨ基／アルケニル基）は、０．５モル／モル未満であると架橋が十分でなく、十分な機械的強度が得られない場合があり、また１０モル／モルを超えると硬化後の物理特性、特に耐熱性と圧縮永久歪性が悪くなる場合がある。 Further, the organohydrogenpolysiloxane is a hydrogen atom (SiH group) bonded to a silicon atom in the organohydrogenpolysiloxane with respect to an aliphatic unsaturated group (alkenyl group) bonded to a silicon atom in the component (A). It is desirable to mix in an amount such that the molar ratio (SiH group / alkenyl group) is preferably 0.5 to 10 mol / mol, more preferably 0.7 to 5 mol / mol. If the molar ratio (SiH group / alkenyl group) is less than 0.5 mol / mol, cross-linking may not be sufficient and sufficient mechanical strength may not be obtained, and if it exceeds 10 mol / mol, it is cured. Later physical characteristics, especially heat resistance and compression set, may deteriorate.
ヒドロシリル化触媒
ヒドロシリル化触媒は、（Ａ）成分のアルケニル基とオルガノハイドロジェンポリシロキサンのケイ素原子結合水素原子（ＳｉＨ基）とを付加反応させる触媒である。
Hydrosilylation catalyst The hydrosilylation catalyst is a catalyst that causes an addition reaction between the alkenyl group of the component (A) and the silicon atom-bonded hydrogen atom (SiH group) of the organohydrogenpolysiloxane.
ヒドロシリル化触媒としては、白金族金属系触媒が挙げられ、白金族の金属単体とその化合物があり、これには従来、付加反応硬化型シリコーンゴム組成物の触媒として公知のものが使用できる。ヒドロシリル化触媒としては、例えば、シリカ、アルミナ又はシリカゲルのような担体に吸着させた微粒子状白金金属、塩化第二白金、塩化白金酸、塩化白金酸６水塩のアルコール溶液、パラジウム触媒、ロジウム触媒等が挙げられるが、白金又は白金化合物が好ましい。
これらのヒドロシリル化触媒は、１種単独で用いても、２種以上を組み合わせて用いてもよい。
Examples of the hydrosilylation catalyst include platinum group metal-based catalysts, which include platinum group metal alone and compounds thereof, and conventionally known catalysts for addition reaction curable silicone rubber compositions can be used. Examples of the hydrosilylation catalyst include fine particle platinum metal adsorbed on a carrier such as silica gel, alumina or silica gel, an alcohol solution of secondary platinum chloride, platinum chloride acid, and hexahydrate platinum chloride hexahydrate, a palladium catalyst, and a rhodium catalyst. Etc., but platinum or a platinum compound is preferable.
These hydrosilylation catalysts may be used alone or in combination of two or more.
ヒドロシリル化触媒の添加量は、付加反応を促進できればよく、通常、白金系金属量に換算して、（Ａ）成分のオルガノポリシロキサンに対して１質量ｐｐｍ〜１質量％の範囲で使用されるが、１０〜５００質量ｐｐｍの範囲が好ましい。この添加量が１質量ｐｐｍ未満であると、付加反応が十分促進されず、硬化が不十分である場合がある、一方、上記の添加量が１質量％を超えると、これより多く加えても反応性に対する影響が少なくなり、不経済となる場合がある。 The amount of the hydrosilylation catalyst added may be as long as it can promote the addition reaction, and is usually used in the range of 1% by mass to 1% by mass with respect to the organopolysiloxane of the component (A) in terms of the amount of platinum-based metal. However, the range of 10 to 500 mass ppm is preferable. If this addition amount is less than 1% by mass, the addition reaction may not be sufficiently promoted and curing may be insufficient, while if the above addition amount exceeds 1% by mass, even if a larger amount is added. It has less impact on reactivity and may be uneconomical.
（Ｃ−２）有機過酸化物硬化剤
（Ｃ−２）有機過酸化物硬化剤としては、例えば、ベンゾイルパーオキサイド、２，４−ジクロロベンゾイルパーオキサイド、ｐ−メチルベンゾイルパーオキサイド、ｏ−メチルベンゾイルパーオキサイド、２，４−ジクミルパーオキサイド、２，５−ジメチル−２，５−ビス（ｔ−ブチルパーオキシ）ヘキサン、ジ−ｔ−ブチルパーオキサイド、ｔ−ブチルパーベンゾエート、１，６−ヘキサンジオール−ビス−ｔ−ブチルパーオキシカーボネート等が挙げられる。
これらの有機過酸化物硬化剤は、１種単独で用いても、２種以上を組み合わせて用いてもよい。
(C-2) Organic Peroxide Hardener (C-2) Examples of the organic peroxide hardener include benzoyl peroxide, 2,4-dichlorobenzoyl peroxide, p-methylbenzoyl peroxide, and o-methyl. Benzoyl peroxide, 2,4-dicumyl peroxide, 2,5-dimethyl-2,5-bis (t-butylperoxy) hexane, di-t-butyl peroxide, t-butylperbenzoate, 1,6 -Hexanediol-bis-t-butylperoxycarbonate and the like can be mentioned.
These organic peroxide curing agents may be used alone or in combination of two or more.
上記有機過酸化物の配合量は、（Ａ）成分１００質量部に対して０．０１〜１０質量部、好ましくは１〜１０質量部、特に０．２〜５質量部が好ましい。配合量が少なすぎると硬化が不十分となる場合があり、多すぎると有機過酸化物の分解残渣によりシリコーンゴム硬化物が黄変する場合がある。 The blending amount of the organic peroxide is 0.01 to 10 parts by mass, preferably 1 to 10 parts by mass, and particularly preferably 0.2 to 5 parts by mass with respect to 100 parts by mass of the component (A). If the blending amount is too small, the curing may be insufficient, and if the blending amount is too large, the cured silicone rubber may turn yellow due to the decomposition residue of the organic peroxide.
本発明で得られる（Ｃ）硬化剤は、上記の（Ｃ−１）成分又は（Ｃ−２）成分を単独で使用することができるが、（Ｃ−１）付加反応硬化剤と（Ｃ−２）有機過酸化物硬化剤とを組み合わせた共加硫型の硬化剤として使用することもできる。この場合、（Ａ）成分に、（Ｃ−１）及び（Ｃ−２）成分を、それぞれの上記配合量の範囲内で組み合わせて配合して使用すればよい。 In the (C) curing agent obtained in the present invention, the above-mentioned (C-1) component or (C-2) component can be used alone, but the (C-1) addition reaction curing agent and (C-) can be used alone. 2) It can also be used as a co-vulcanization type curing agent in combination with an organic peroxide curing agent. In this case, the components (C-1) and (C-2) may be combined with the component (A) within the range of the above-mentioned blending amounts and used.
［（Ｄ）分散剤］
本発明では、上記成分に加え、必要に応じて、公知の分散剤を使用してもよい。該分散剤としては、具体的には、水、オルガノシロキサン化合物等が挙げられる。これらのなかでも、シラノール基を有するオルガノシロキサン化合物が好ましく、両末端基にシラノール基を有するオルガノシロキサン化合物がより好ましい。
これらの分散剤は１種単独で使用してもよいし、２種以上を併用してもよい。
本発明で用いられる分散剤の配合量は、（Ａ）成分１００質量部に対して、０．１〜５０質量部が好ましく、０．１〜３０質量部がより好ましい。
[(D) Dispersant]
In the present invention, in addition to the above components, known dispersants may be used, if necessary. Specific examples of the dispersant include water, an organosiloxane compound and the like. Among these, an organosiloxane compound having a silanol group is preferable, and an organosiloxane compound having a silanol group at both terminal groups is more preferable.
These dispersants may be used alone or in combination of two or more.
The blending amount of the dispersant used in the present invention is preferably 0.1 to 50 parts by mass, more preferably 0.1 to 30 parts by mass with respect to 100 parts by mass of the component (A).
［その他の任意成分］
本発明のシリコーンゴム組成物には、上述した成分に加え、必要に応じて、石英粉末、結晶性シリカ、珪藻土等の非補強性シリカ；アセチレンブラック、ファーネスブラック、チャンネルブラック等のカーボンブラック；着色剤；ベンガラ、酸化セリウム等の耐熱性向上剤；上記白金族金属触媒以外の白金化合物、酸化チタン、トリアゾール化合物等の難燃性向上剤；受酸剤；アルミナ、窒化ホウ素等の熱伝導率向上剤；離型剤；エチニルシクロヘキサノール等の反応制御剤等を添加してもよい。これらの任意成分は、１種単独で用いても、２種以上を組み合わせて用いてもよい。
[Other optional ingredients]
In the silicone rubber composition of the present invention, in addition to the above-mentioned components, if necessary, non-reinforcing silica such as quartz powder, crystalline silica, diatomaceous earth; carbon black such as acetylene black, furnace black, channel black; coloring; Agents; Heat resistance improvers such as red iron oxide and cerium oxide; Flame retardant improvers such as platinum compounds, titanium oxide and triazole compounds other than the platinum group metal catalysts; Acid receiving agents; Thermal conductivity improvement of alumina and boron nitride, etc. Agent; Mold release agent; Reaction control agent such as ethynylcyclohexanol may be added. These optional components may be used alone or in combination of two or more.
［製造方法］
本発明のシリコーンゴム組成物は、組成物を構成する成分をニーダー、バンバリーミキサー、二本ロールミル等の公知の混練機で混合することにより得ることができる。シリコーンゴム組成物として、上記（Ａ）〜（Ｃ）成分を含有する組成物を得る場合、（Ａ）成分と（Ｂ）成分とを混合して混合物（ベースコンパウンド）を得た後、該混合物に（Ｃ）成分を添加するのが好ましい。上記（Ａ）〜（Ｃ）成分を含有する組成物が更にその他の成分を含む場合には、（Ａ）成分と（Ｂ）成分とを混合して混合物（ベースコンパウンド）を得た後、その他の成分とを混合して混合物を得た後、該混合物に（Ｃ）成分を添加することが好ましい。
[Production method]
The silicone rubber composition of the present invention can be obtained by mixing the components constituting the composition with a known kneader such as a kneader, a Banbury mixer, or a two-roll mill. When a composition containing the above components (A) to (C) is obtained as a silicone rubber composition, the components (A) and (B) are mixed to obtain a mixture (base compound), and then the mixture is obtained. It is preferable to add the component (C) to. When the composition containing the above components (A) to (C) further contains other components, the component (A) and the component (B) are mixed to obtain a mixture (base compound), and then the other components are obtained. After mixing with the components of (C) to obtain a mixture, it is preferable to add the component (C) to the mixture.
本発明のシリコーンゴム組成物は、加熱硬化と同時に成形することにより、ゴム状の弾性体（シリコーンゴム硬化物）からなる成形物を得ることができる。
上記シリコーンゴム組成物を硬化させる方法については、特に制限はないが、上述した硬化剤の分解及びシリコーンゴム組成物の加硫に十分な熱をかける方法であればよい。硬化の温度条件については硬化方法にもよるが、通常８０〜４００℃、特に１００〜２００℃で３秒〜１６０分間、特に３秒〜２０分間である。また、その成形方法については、特に制限はなく、例えば、押し出し成形による連続加硫、プレス成形（加圧成形）、インジェクション成形等の成形方法を採用することができる。更に、必要に応じて、１５０〜２５０℃で１〜１０時間程度で二次加硫（ポストキュア）してもよい。
The silicone rubber composition of the present invention can be molded at the same time as heat curing to obtain a molded product made of a rubber-like elastic body (silicone rubber cured product).
The method for curing the silicone rubber composition is not particularly limited, but any method may be used as long as it is a method in which sufficient heat is applied to the above-mentioned decomposition of the curing agent and vulcanization of the silicone rubber composition. The temperature condition of curing depends on the curing method, but is usually 80 to 400 ° C., particularly 100 to 200 ° C. for 3 seconds to 160 minutes, particularly 3 seconds to 20 minutes. The molding method is not particularly limited, and for example, a molding method such as continuous vulcanization by extrusion molding, press molding (pressure molding), or injection molding can be adopted. Further, if necessary, secondary vulcanization (post-cure) may be performed at 150 to 250 ° C. for about 1 to 10 hours.
以下に、実施例及び比較例を挙げて、本発明を更に具体的に説明するが、本発明はこれら実施例に限定されるものではない。 Hereinafter, the present invention will be described in more detail with reference to Examples and Comparative Examples, but the present invention is not limited to these Examples.
下記の例において、オルガノポリシロキサン生ゴムに含まれるシラノール基における水酸基（シラノール性水酸基）の含有量（質量％）は、日本電子（株）製４００ＭＨｚ−ＮＭＲ測定装置を用いて、29Ｓｉ−ＮＭＲにおける検出スペクトルの積分値から算出した。 In the following example, the content (% by mass) of the hydroxyl group (silanol hydroxyl group) in the silanol group contained in the organopolysiloxane raw rubber is 29 Si-NMR using a 400 MHz-NMR measuring device manufactured by JEOL Ltd. It was calculated from the integrated value of the detection spectrum.
下記の例において、重量平均重合度は、下記条件で測定したゲルパーミエーションクロマトグラフィ（ＧＰＣ）によるポリスチレンを標準物質として算出した値である。
［測定条件］
・展開溶媒：トルエン
・流量：１ｍＬ／ｍｉｎ
・検出器：示差屈折率検出器（ＲＩ）
・カラム：ＫＦ−８０５Ｌ×２本（Ｓｈｏｄｅｘ社製）
・カラム温度：２５℃
・試料注入量：３０μＬ（濃度０．２質量％のトルエン溶液）
In the following example, the weight average degree of polymerization is a value calculated using polystyrene by gel permeation chromatography (GPC) measured under the following conditions as a standard substance.
[Measurement condition]
・ Developing solvent: Toluene ・ Flow rate: 1 mL / min
-Detector: Differential refractometer (RI)
-Column: KF-805L x 2 (manufactured by Shodex)
-Column temperature: 25 ° C
-Sample injection amount: 30 μL (toluene solution with a concentration of 0.2% by mass)
［実施例１］
オルガノポリシロキサン生ゴム（Ｉ）の合成
撹拌機、還流冷却器、滴下ロート及び温度計を備えた３Ｌセパラブルフラスコに、オクタメチルシクロテトラシロキサン１８００ｇ、１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン０．７２ｇ及び１，３，５，７−テトラメチル−１，３，５，７−テトラビニルシクロシロキサン２．６ｇからなる混合物に、１０％水酸化テトラ−ｎ−ブチルホスホニウムのジメチルポリシロキサネート３ｇを添加し、１１０℃で１時間重合反応した。
重合反応後、１５０℃で２時間加熱撹拌し、水酸化テトラ−ｎ−ブチルホスホニウムを熱分解させた。１００℃まで冷却後、ジメチルアミノビニルジメチルシラン（末端封鎖剤１、沸点１０７℃）１．５７ｇを添加し、１００℃で１時間保温した。反応物を１４０〜１５０℃、２ｍｍＨｇ以下でおよそ５時間減圧し、低揮発分を溜去した。得られたオルガノポリシロキサン生ゴムは、重量平均重合度が８，０００で末端封鎖率が９９％以上である無色透明なオルガノポリシロキサン生ゴム（Ｉ）１，６２０ｇであった。
上記「オルガノポリシロキサン生ゴム（Ｉ）」１００質量部、（Ｂ）ＢＥＴ比表面積２
００ｍ2／ｇのヒュームドシリカ（商品名「アエロジル２００」、日本アエロジル（株）製）４０質量部、ヘキサメチルジシラザン５質量部と水１質量部をニーダーにて混練りし、１７０℃にて２時間加熱処理して「ベースコンパウンド１」を調製した。
上記「ベースコンパウンド１」１００質量部に対し、両末端がトリメチルシロキシ基で封鎖され側鎖にＳｉ−Ｈ基を平均２０個有するメチルハイドロジェン・ジメチルポリシロキサン（平均重合度３８、Ｓｉ−Ｈ基量０．００７４モル／ｇ）０．９１質量部、白金触媒（Ｐｔ濃度１質量％）０．０５質量部、反応制御剤としてエチニルシクロヘキサノール０．０４質量部を混合し、「シリコーンゴム組成物１」を調製した。組成物全体の総Ｓｉ−Ｈ基量と総ビニル基量のモル比（Ｓｉ−Ｈ基／ビニル基）は４．７である。
シリコーンゴム組成物１を成形圧力７．８ＭＰａ（８０ｋｇｆ／ｃｍ2）、１２０℃、１０分のプレスキュア（一次加硫）後、オーブン内で２００℃、４時間のポストキュア（二次加硫）を行って、１００ｍｍ角、厚さ２ｍｍのシート状の「シリコーンゴム硬化物１」を得た。
[Example 1]
Synthesis of Organopolysiloxane Raw Rubber (I) In a 3L separable flask equipped with a stirrer, a reflux condenser, a dropping funnel and a thermometer, 1800 g of octamethylcyclotetrasiloxane, 1,3-divinyl-1,1,3,3 10% tetra-n-butylphosphonium hydroxide in a mixture consisting of 0.72 g of tetramethyldisiloxane and 2.6 g of 1,3,5,7-tetramethyl-1,3,5,7-tetravinylcyclosiloxane 3 g of dimethylpolysiloxanate was added, and the polymerization reaction was carried out at 110 ° C. for 1 hour.
After the polymerization reaction, the mixture was heated and stirred at 150 ° C. for 2 hours to thermally decompose tetra-n-butylphosphonium hydroxide. After cooling to 100 ° C., 1.57 g of dimethylaminovinyldimethylsilane (terminal sealant 1, boiling point 107 ° C.) was added, and the mixture was kept warm at 100 ° C. for 1 hour. The reaction product was depressurized at 140 to 150 ° C. and 2 mmHg or less for about 5 hours to remove low volatile components. The obtained organopolysiloxane raw rubber was 1,620 g of colorless and transparent organopolysiloxane raw rubber (I) having a weight average degree of polymerization of 8,000 and a terminal sealing ratio of 99% or more.
100 parts by mass of the above "organopolysiloxane raw rubber (I)", (B) BET specific surface area 2
Knead 40 parts by mass of 00m 2 / g fumed silica (trade name "Aerosil 200", manufactured by Nippon Aerosil Co., Ltd.), 5 parts by mass of hexamethyldisilazane and 1 part by mass of water with a kneader, and bring to 170 ° C. The mixture was heat-treated for 2 hours to prepare "Base Compound 1".
Methylhydrogen-dimethylpolysiloxane (average polymerization degree 38, Si—H group) having 20 Si—H groups on the side chain with both ends sealed with trimethylsiloxy groups with respect to 100 parts by mass of the above “base compound 1”. Amount 0.0074 mol / g) 0.91 part by mass, platinum catalyst (Pt concentration 1% by mass) 0.05 part by mass, and 0.04 part by mass of ethynylcyclohexanol as a reaction control agent were mixed to form a "silicone rubber composition". 1 ”was prepared. The molar ratio (Si—H group / vinyl group) of the total Si—H group amount and the total vinyl group amount of the entire composition is 4.7.
Silicone rubber composition 1 is pre-cured (primary vulcanization) at a molding pressure of 7.8 MPa (80 kgf / cm 2 ), 120 ° C. for 10 minutes, and then post-cured (secondary vulcanization) at 200 ° C. for 4 hours in an oven. A sheet-shaped "silicone rubber cured product 1" having a size of 100 mm square and a thickness of 2 mm was obtained.
［実施例２］
オルガノポリシロキサン（ＩＩ）の合成
実施例１において末端封鎖剤を、ジエチルアミノビニルジメチルシラン（末端封鎖剤２、沸点１２０℃）１．８９ｇに変更したところ、重量平均重合度が６，０００で末端封鎖率が９９％以上である無色透明なオルガノポリシロキサン生ゴム（ＩＩ）を１，６１０ｇ得ることができた。
（Ａ）オルガノポリシロキサン生ゴム（Ｉ）をオルガノポリシロキサン生ゴム（ＩＩ）に変更し、（Ｂ）ＢＥＴ比表面積２００ｍ2／ｇのヒュームドシリカを、ＢＥＴ比表面積が１３０ｍ2／ｇで、表面が疎水処理化されたヒュームドシリカ（アエロジルＲ−９７２、日本アエロジル（株）製）４０質量部に変更し、それ以外は実施例１と同様にして「ベースコンパウンド２」及び「シリコーンゴム組成物２」を得た。得られた「シリコーンゴム組成物２」を実施例１と同じ条件で硬化させ、１００ｍｍ角、厚さ２ｍｍのシート状の「シリコーンゴム硬化物２」を得た。
[Example 2]
Synthesis of Organopolysiloxane (II) In Example 1, when the terminal blocking agent was changed to 1.89 g of diethylaminovinyldimethylsilane (terminal blocking agent 2, boiling point 120 ° C.), the weight average degree of polymerization was 6,000 and the terminal sealing was performed. It was possible to obtain 1,610 g of colorless and transparent organopolysiloxane raw rubber (II) having a rate of 99% or more.
(A) Organopolysiloxane raw rubber (I) was changed to organopolysiloxane raw rubber (II), and (B) fumed silica with a BET specific surface area of 200 m 2 / g was used, with a BET specific surface area of 130 m 2 / g and a surface surface. Change to 40 parts by mass of hydrophobically treated fumed silica (Aerosil R-972, manufactured by Nippon Aerosil Co., Ltd.), and otherwise in the same manner as in Example 1, "Base Compound 2" and "Silicone Rubber Composition 2". I got. The obtained "silicone rubber composition 2" was cured under the same conditions as in Example 1 to obtain a 100 mm square, 2 mm thick sheet-shaped "silicone rubber cured product 2".
［実施例３］
オルガノポリシロキサン（ＩＩＩ）の合成
撹拌機、還流冷却器、滴下ロート及び温度計を備えた３Ｌセパラブルフラスコに、オクタメチルシクロテトラシロキサン１８００ｇ、１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン０．７２ｇ及び１，３，５，７−テトラメチル−１，３，５，７−テトラビニルシクロシロキサン２．６ｇからなる混合物に、１０％水酸化カリウムのジメチルポリシロキサネート０．６ｇを添加し、１５０℃で４時間重合反応した。重合反応後、エチレンクロルヒドリン０．４ｇを追加し、１５０℃で２時間中和処理を行った後、１００℃まで冷却後、ジメチルアミノビニルジメチルシラン（末端封鎖剤１、沸点１０７℃）１．５７ｇを添加し、１時間保温してから１４０〜１５０℃の保温／減圧下で２ｍｍＨｇ以下になるまでおよそ５時間、低揮発分を溜去した。得られたオルガノポリシロキサン生ゴムは、重量平均重合度が８，０００で末端封鎖率が９９％以上である無色透明なオルガノポリシロキサン生ゴム（ＩＩＩ）を１，６１５ｇ得ることができた。
（Ａ）オルガノポリシロキサン生ゴム（Ｉ）をオルガノポリシロキサン生ゴム（ＩＩＩ）に変更し、（Ｂ）ＢＥＴ比表面積２００ｍ2／ｇのヒュームドシリカ（商品名「アエロジル２００」、日本アエロジル（株）製）１０質量部をニーダーにて混練りし、１７０℃にて２時間加熱処理して「ベースコンパウンド３」を調製した。それ以外は実施例１と同様にして「シリコーンゴム組成物３」を得た。得られた「シリコーンゴム組成物３」を実施例１と同じ条件で硬化させ、１００ｍｍ角、厚さ２ｍｍのシート状の「シリコーンゴム硬化物３」を得た。
[Example 3]
Synthesis of Organopolysiloxane (III) In a 3L separable flask equipped with a stirrer, reflux condenser, dropping funnel and thermometer, 1800 g of octamethylcyclotetrasiloxane, 1,3-divinyl-1,1,3,3- Dimethylpolysiloxanate of 10% potassium hydroxide in a mixture consisting of 0.72 g of tetramethyldisiloxane and 2.6 g of 1,3,5,7-tetramethyl-1,3,5,7-tetravinylcyclosiloxane. 0.6 g was added, and the polymerization reaction was carried out at 150 ° C. for 4 hours. After the polymerization reaction, 0.4 g of ethylene chlorhydrin was added, neutralized at 150 ° C. for 2 hours, cooled to 100 ° C., and then dimethylaminovinyldimethylsilane (terminal sealant 1, boiling point 107 ° C.) 1 .57 g was added, and after keeping the temperature for 1 hour, the low volatile matter was distilled off for about 5 hours until the temperature became 2 mmHg or less under the heat retention / reduced pressure of 140 to 150 ° C. As the obtained organopolysiloxane raw rubber, 1,615 g of colorless and transparent organopolysiloxane raw rubber (III) having a weight average degree of polymerization of 8,000 and a terminal sealing ratio of 99% or more could be obtained.
(A) Organopolysiloxane raw rubber (I) was changed to organopolysiloxane raw rubber (III), and (B) fumed silica with a BET specific surface area of 200 m 2 / g (trade name "Aerosil 200", manufactured by Nippon Aerosil Co., Ltd.) ) 10 parts by mass was kneaded with a kneader and heat-treated at 170 ° C. for 2 hours to prepare "Base Compound 3". A "silicone rubber composition 3" was obtained in the same manner as in Example 1 except for the above. The obtained "silicone rubber composition 3" was cured under the same conditions as in Example 1 to obtain a 100 mm square, 2 mm thick sheet-shaped "silicone rubber cured product 3".
［比較例１］
オルガノポリシロキサン（ＩＶ）の合成
実施例１において末端封鎖剤を使わなかった結果、重量平均重合度が５，０００で末端封鎖率が９３％である無色透明なオルガノポリシロキサン生ゴム（ＩＶ）を１，６００ｇ得ることができた。
（Ａ）オルガノポリシロキサン生ゴム（Ｉ）をオルガノポリシロキサン生ゴム（ＩＶ）に変更し、それ以外は実施例１と同様にして「ベースコンパウンド４」及び「シリコーンゴム組成物４」を得た。得られたシリコーンゴム組成物４を実施例１と同じ条件で硬化させ、１００ｍｍ角、厚さ２ｍｍのシート状の「シリコーンゴム硬化物４」を得た。
[Comparative Example 1]
Synthesis of Organopolysiloxane (IV) As a result of not using an end-sealing agent in Example 1, a colorless and transparent organopolysiloxane raw rubber (IV) having a weight average degree of polymerization of 5,000 and an end-sealing ratio of 93% was obtained. , 600 g could be obtained.
(A) Organopolysiloxane raw rubber (I) was changed to organopolysiloxane raw rubber (IV), and "base compound 4" and "silicone rubber composition 4" were obtained in the same manner as in Example 1 except for the above. The obtained silicone rubber composition 4 was cured under the same conditions as in Example 1 to obtain a 100 mm square, 2 mm thick sheet-shaped "silicone rubber cured product 4".
［比較例２］
オルガノポリシロキサン（Ｖ）の合成
実施例１において末端封鎖剤を、ジメチルビニルクロロシラン（末端封鎖剤５−１、沸点８２℃）２．９２ｇと１，３−ジビニル−１，１，３，３−テトラメチルジシラザン（末端封鎖剤５−２、沸点１７０℃）２．２５ｇの混合物に変更したところ、重量平均重合度が６，０００で末端封鎖率が９９％以上である白濁したオルガノポリシロキサン生ゴム（Ｖ）を１，６１５ｇ得ることができた。
実施例１において（Ａ）オルガノポリシロキサン生ゴム（Ｉ）をオルガノポリシロキサン生ゴム（Ｖ）に変更し、それ以外は実施例１と同様にして「ベースコンパウンド５」及び「シリコーンゴム組成物５」を得た。得られた「シリコーンゴム組成物５」を実施例１と同じ条件で硬化させ、１００ｍｍ角、厚さ２ｍｍのシート状の「シリコーンゴム硬化物５」を得た。
[Comparative Example 2]
Synthesis of Organopolysiloxane (V) In Example 1, the terminal blocking agent was dimethylvinylchlorosilane (terminal blocking agent 5-1, boiling point 82 ° C.) 2.92 g and 1,3-divinyl-1,1,3,3-. When changed to a mixture of 2.25 g of tetramethyldisilazane (terminal sealant 5-2, boiling point 170 ° C.), a cloudy organopolysiloxane raw rubber having a weight average degree of polymerization of 6,000 and an end seal ratio of 99% or more. It was possible to obtain 1,615 g of (V).
In Example 1, (A) the organopolysiloxane raw rubber (I) was changed to the organopolysiloxane raw rubber (V), and otherwise, the "base compound 5" and the "silicone rubber composition 5" were used in the same manner as in Example 1. Obtained. The obtained "silicone rubber composition 5" was cured under the same conditions as in Example 1 to obtain a 100 mm square, 2 mm thick sheet-shaped "silicone rubber cured product 5".
［比較例３］
オルガノポリシロキサン（ＶＩ）の合成
実施例１において末端封鎖剤を、ジ−ｎ−オクチルアミノビニルジメチルシラン（末端封鎖剤７、沸点２００℃以上）３．９４ｇに変更したところ、重量平均重合度が６，０００で末端封鎖率が９７％である無色透明なオルガノポリシロキサン生ゴム（ＶＩ）を１，６３０ｇ得た。
実施例１において（Ａ）オルガノポリシロキサン生ゴム（Ｉ）をオルガノポリシロキサン生ゴム（ＶＩ）に変更し、それ以外は実施例１と同様にして「ベースコンパウンド６」及び「シリコーンゴム組成物６」を得た。得られた「シリコーンゴム組成物６」を実施例１と同じ条件で硬化をおこなったが、完全に硬化させることができず、「シリコーンゴム硬化物６」を得ることができなかった。
[Comparative Example 3]
Synthesis of Organopolysiloxane (VI) In Example 1, when the terminal sequestering agent was changed to 3.94 g of di-n-octylaminovinyldimethylsilane (terminal sequestering agent 7, boiling point 200 ° C. or higher), the weight average degree of polymerization was increased. A colorless and transparent organopolysiloxane raw rubber (VI) having a terminal blockage rate of 97% at 6,000 was obtained in an amount of 1,630 g.
In Example 1, (A) the organopolysiloxane raw rubber (I) was changed to the organopolysiloxane raw rubber (VI), and otherwise, the "base compound 6" and the "silicone rubber composition 6" were used in the same manner as in Example 1. Obtained. The obtained "silicone rubber composition 6" was cured under the same conditions as in Example 1, but could not be completely cured, and "silicone rubber cured product 6" could not be obtained.
可塑度試験
実施例１〜３及び比較例１〜３で調製したベースコンパウンドについて、ＪＩＳ Ｋ ６２４９：２００３に準拠して可塑度試験をおこない、初期のウイリアムス可塑度を測定した。更に４０℃、７日間経過した後、組成物を練り返すことなく３０分放冷して、ウイリアムス可塑度を測定し、その差から可塑度変化を求めた。
Plasticity test The base compounds prepared in Examples 1 to 3 and Comparative Examples 1 to 3 were subjected to a plasticity test according to JIS K 6249: 2003, and the initial Williams plasticity was measured. After a further lapse of 40 ° C. for 7 days, the composition was allowed to cool for 30 minutes without kneading, and the Williams plasticity was measured, and the change in plasticity was determined from the difference.
外観
実施例１〜３及び比較例１〜３で調製したシリコーンゴム硬化物について、外観を確認した。
Appearance The appearance of the cured silicone rubber prepared in Examples 1 to 3 and Comparative Examples 1 to 3 was confirmed.
上記の実施例１〜３及び比較例１〜３の各例の試験用ゴムシート（シリコーンゴム硬化物）について、上記の各項目で測定した物性値を表１に示す。
本発明は、末端封鎖率が高く、副生成物の除去が容易なオルガノポリシロキサン生ゴムの製造方法で、このようにして得られたオルガノポリシロキサン生ゴムをシリカ等の補強材と混練りし、シリコーンゴム組成物を製造した時、該シリコーンゴム組成物の硬化物（シリコーンゴム硬化物）の外観への影響がなく、シリコーンゴム組成物の経時におけるクレープハードニング性が改善され、シリコーンゴム組成物の保存性を著しく向上させることができた。 The present invention is a method for producing an organopolysiloxane raw rubber having a high terminal blockage rate and easy removal of by-products. The organopolysiloxane raw rubber thus obtained is kneaded with a reinforcing material such as silica to form silicone. When the rubber composition is manufactured, there is no effect on the appearance of the cured product (silicone rubber cured product) of the silicone rubber composition, the crepe hardening property of the silicone rubber composition over time is improved, and the silicone rubber composition is improved. The storage stability could be significantly improved.
Claims (3)
（Ｉ）下記式（１）で示される環状オルガノシロキサンを、
アルカリ性触媒の存在下で、ジオルガノシロキサン単位が１〜２００の直鎖状オルガノシロキサンと共に重合する工程、
（ＩＩ）前記アルカリ性触媒を失活させる工程、
（ＩＩＩ）工程（ＩＩ）で得られたオルガノシロキサンと、下記式（２）
で示され、沸点が１６５℃以下であるジアルキルアミノビニルジアルキルシランとを混合する工程、及び
（ＩＶ）未反応のジアルキルアミノビニルジアルキルシラン、及び、副生成物を除去する工程、
を有する、下記式（４）
で示されるオルガノポリシロキサン生ゴムの製造方法。 Organopolysiloxane A method for producing raw rubber.
(I) The cyclic organosiloxane represented by the following formula (1)
The step of polymerizing with a linear organosiloxane with 1-200 diorganosiloxane units in the presence of an alkaline catalyst,
(II) Step of deactivating the alkaline catalyst,
(III) Organosiloxane obtained in step (II) and the following formula (2)
The step of mixing with the dialkylaminovinyldialkylsilane having a boiling point of 165 ° C. or lower, and (IV) the step of removing the unreacted dialkylaminovinyldialkylsilane and the by-products.
The following formula (4)
A method for producing an organopolysiloxane raw rubber shown by.
で示されるオルガノポリシロキサン生ゴム：１００質量部
（Ｂ）ＢＥＴ吸着法による比表面積が５０ｍ2／ｇ以上の補強性シリカ：１０〜１００質量部、及び
（Ｃ）硬化剤：有効量
を含有するシリコーンゴム組成物。 (A) The following formula (4)
Organopolysiloxane raw rubber represented by: 100 parts by mass (B) Reinforcing silica having a specific surface area of 50 m 2 / g or more by the BET adsorption method: 10 to 100 parts by mass, and (C) Hardener: Silicone containing an effective amount Rubber composition.