JP2021126674A - 9%Ni鋼溶接用被覆アーク溶接棒 - Google Patents
9%Ni鋼溶接用被覆アーク溶接棒 Download PDFInfo
- Publication number
- JP2021126674A JP2021126674A JP2020022616A JP2020022616A JP2021126674A JP 2021126674 A JP2021126674 A JP 2021126674A JP 2020022616 A JP2020022616 A JP 2020022616A JP 2020022616 A JP2020022616 A JP 2020022616A JP 2021126674 A JP2021126674 A JP 2021126674A
- Authority
- JP
- Japan
- Prior art keywords
- total
- core wire
- welding
- metal
- mass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
心線質量比=心線中の含有量%+被覆剤中の含有量%×被覆率%/100・・・式
(但し、心線中の含有量%は心線全質量に対する質量%、被覆剤中の含有量%は被覆剤全質量に対する質量%、被覆率は、当該9%Ni鋼溶接用被覆アーク溶接棒全質量に対する前記被覆剤の質量%)
心線質量比=心線中の含有量%+被覆剤中の含有量%×被覆率%/100・・・式
Siは、溶接金属中の耐気孔欠陥性を向上させる効果がある。心線質量比でSiが0.1%未満では、その効果が十分に得られず、気孔欠陥が発生しやすい。一方、心線質量比でSiが1.0%を超えると、割れが発生しやすくなる。従って、心線質量比でSiは0.1〜1.0%とする。なお、Siは、心線、金属Si、Fe−Si、Fe−Si−Mn等から添加できる。
Mnは、溶接金属の耐割れ性を向上させる効果がある。心線質量比でMnが1.5%未満であると、割れが発生しやすくなる。一方、心線質量比でMnが4.0%を超えると、溶接金属の靱性が低下する。従って、心線質量比でMnは1.5〜4.0%とする。なお、Mnは、心線、金属Mn、Fe−Mn、Fe−Si−Mn等から添加できる。
Crは、溶接金属の強度を向上させる効果がある。心線質量比でCrが8%未満では、溶接金属の強度が低下する。一方、心線質量比でCrが12%を超えると、溶接金属の靱性が低下する。従って、心線質量比でCrは8〜12%とする。なお、Crは、心線、金属Cr、Fe−Cr等の合金粉末から添加できる。
Moは、溶接金属の強度を向上させる効果がある。心線質量比でMoが2.5%未満では、溶接金属の強度が低下する。一方、心線質量比でMoが8.0%を超えると、溶接金属の靱性が低下する。従って、心線質量比でMoは2.5〜8.0%とする。なお、Moは、心線、金属Mo、Fe−Mo等から添加できる。
Nbは溶接金属の強度を向上させる効果がある。心線質量比でNbが0.5%未満では、溶接金属の強度が低下する。一方、心線質量比でNbが2.5%を超えると、溶接金属の靱性が低下する。従って、心線質量比でNbは0.5〜2.5%とする。なお、Nbは、心線、Fe−Nb等の合金粉から添加できる。
Taは、溶接金属の強度を向上させる効果がある。心線質量比でTaが0.05%未満では、溶接金属の強度が低下する。一方、心線質量比でTaが0.30%を超えると、溶接金属の靱性が低下する。従って、心線質量比でTaは0.05〜0.30%とする。なお、Taは、心線、金属Ta、Nb−Ta等から添加できる。
Tiは、合金に含まれる過剰な酸素を除去し、溶接金属の強度及び靱性を安定させる効果がある。心線質量比でTiが0.1%未満では、その効果は十分に得られず、溶接金属に気孔欠陥が発生しやすくなる。一方、心線質量比でTiが0.8%を超えると、溶接金属中に金属酸化物として多量に分布して強度及び靱性が低下する。従って、心線質量比でTiは0.1〜0.8%とする。なお、Tiは、心線、金属Ti、Fe−Ti等から添加できる。
Wは、溶接金属の靱性を低下させずに強度を改善する効果がある。心線質量比でWが0.5%未満であると、溶接金属の強度が得られない。一方、心線質量比でWが1.7%を超えると、溶接金属の強度が高くなりすぎて靭性が低下する。従って、心線質量比でWは0.5〜1.7%とする。なお、Wは、心線、金属W、WC等から添加できる。
Si酸化物は、スラグ剥離性を向上させる効果がある。Si酸化物のSiO2換算値の合計が4%未満では、アークが不安定になりスラグ剥離性が不良となる。一方、Si酸化物のSiO2換算値の合計が12%を超えると、溶融スラグの融点が過剰に下がるため、立向姿勢溶接でメタル垂れが発生してビード形状が不良となる。従って、Si酸化物は4〜12%とする。なお、Si酸化物は、珪砂、長石、水ガラス中の珪酸ソーダ及び珪酸カリウム等から添加できる。
金属弗化物は、アークの吹付け及びスラグの粘性、流動性を適正にし、溶接作業性を向上させる効果がある。金属弗化物の1種または2種以上の合計が12%未満では、その効果が得られずスラグ剥離性及びビード形状が不良となる。一方、金属弗化物の1種または2種以上の合計が25%以上を超えると、アークが不安定になりスパッタ発生量が多く、ビード形状も不良となる。さらに立向上進溶接でメタル垂れが発生しやすくなる。従って、金属弗化物の1種または2種以上の合計は12〜25%とする。なお、金属弗化物は、蛍石、弗化バリウム、弗化マグネシウム、弗化アルミニウム等から添加できる。
金属炭酸塩は、金属弗化物同様にアークの吹付け及びスラグの粘性、流動性を適正にし、溶接作業性を向上させる効果がある。金属炭酸塩の1種または2種以上の合計が13%未満では、その効果が得られず、アークが不安定となりビード形状が不良となる。一方、金属炭酸塩の1種または2種以上の合計が21%を超えると、アークが不安定でスパッタ発生量が多くなり、スラグ剥離性及びビード形状が不良となる。さらに立向上進溶接でメタル垂れが発生しやすくなる。従って、金属炭酸塩の1種または2種以上の合計は13〜21%とする。なお、金属炭酸塩は、炭酸カルシウム、炭酸マグネシウム、炭酸バリウム、炭酸マンガン、炭酸リチウム等から添加できる。
Na酸化物及びK酸化物は、アークを安定にする効果がある。Na酸化物及びK酸化物のNa換算値及びK換算値の合計が1%未満では、アークが不安定になりビード形状が不良となる。一方、Na酸化物及びK酸化物のNa換算値及びK換算値の合計が5%を超えると、アークが不安定でスパッタ発生量が多くなる。従って、Na酸化物及びK酸化物のNa換算値及びK換算値の合計は1〜5%とする。なお、Na酸化物及びK酸化物は、水ガラス中の珪酸ソーダ及び珪酸カリウム、長石等から添加できる。
2 溝
Claims (1)
- Niを95質量%以上含むNi基合金を心線とした、9%Ni鋼溶接用被覆アーク溶接棒において、前記心線と被覆剤の一方または両方の合計で、下記式に示す心線質量比で、
Si:0.1〜1.0%、
Mn:1.5〜4.0%、
Cr:8〜12%、
Mo:2.5〜8.0%、
Nb:0.5〜2.5%、
Ta:0.05〜0.30%、
Ti:0.1〜0.8%、
W:0.5〜1.7%を含有し、
前記被覆剤は、当該被覆剤全質量に対する質量%で、
Si酸化物のSiO2換算値の合計:4〜12%、
金属弗化物の1種または2種以上の合計:12〜25%、
金属炭酸塩の1種または2種以上の合計:13〜21%、
Na酸化物及びK酸化物のNa換算値及びK換算値の合計:1〜5%を含有し、
残部は前記心線中のNi及びFe分、前記被覆剤の鉄合金のFe分及び不可避不純物からなることを特徴とする9%Ni鋼溶接用被覆アーク溶接棒。
心線質量比=心線中の含有量%+被覆剤中の含有量%×被覆率%/100・・・式
(但し、心線中の含有量%は心線全質量に対する質量%、被覆剤中の含有量%は被覆剤全質量に対する質量%、被覆率は、当該9%Ni鋼溶接用被覆アーク溶接棒全質量に対する前記被覆剤の質量%)