JP2020073404A - Reel for anisotropic conductive film and anisotropic conductive film roll - Google Patents
Reel for anisotropic conductive film and anisotropic conductive film roll Download PDFInfo
- Publication number
- JP2020073404A JP2020073404A JP2019179345A JP2019179345A JP2020073404A JP 2020073404 A JP2020073404 A JP 2020073404A JP 2019179345 A JP2019179345 A JP 2019179345A JP 2019179345 A JP2019179345 A JP 2019179345A JP 2020073404 A JP2020073404 A JP 2020073404A
- Authority
- JP
- Japan
- Prior art keywords
- conductive film
- anisotropic conductive
- reel
- winding core
- winding
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、異方導電フィルム用リール、異方導電フィルム巻に関する。 The present invention relates to an anisotropic conductive film reel and an anisotropic conductive film winding.
従来、多数の電極を有する被接続部材同士を接続するための接着テープが用いられている。このような接着テープとして、例えば、異方導電テープ、導電テープがある。異方導電テープは、例えば、プリント配線基板、ＬＣＤ（液晶ディスプレイ）用ガラス基板、フレキシブルプリント基板等の基板にＩＣ、ＬＳＩといった半導体素子等を接続した場合、相対する接続部材の電極同士を導通状態とさせ、隣接する電極同士の絶縁状態を保持させることができる。また導電テープは、例えば、太陽電池セルにはんだ付き銅線を接続する際、相対する電極同士を導通させることができる。 Conventionally, an adhesive tape for connecting members to be connected having a large number of electrodes has been used. Examples of such an adhesive tape include an anisotropic conductive tape and a conductive tape. The anisotropic conductive tape, for example, when a semiconductor element such as an IC or LSI is connected to a substrate such as a printed wiring board, a glass substrate for an LCD (liquid crystal display), a flexible printed circuit board, or the like, the electrodes of opposing connecting members are in a conductive state. Therefore, the insulating state between the adjacent electrodes can be maintained. In addition, the conductive tape can electrically connect the opposing electrodes to each other when the copper wire with solder is connected to the solar cell, for example.
異方導電フィルムは、熱硬化性樹脂を含有する接着剤成分と、必要により配合される導電性粒子とを含み、ＰＥＴ（ポリエチレンテレフタレート）フィルム等の支持体（セパレータ）上に、フィルム状に形成され、テープ状にスリットされてから芯材に同一円心状に巻き付けてリール形状の細幅長尺テープ（巻重体）として製品化されていることが多い（例えば、特許文献１参照）。従来、異方導電フィルムとしては、高接着性でかつ高信頼性を示すエポキシ樹脂を用いた熱硬化性樹脂が用いられてきた（例えば、特許文献２参照）。また、アクリレート誘導体やメタアクリレート誘導体とラジカル重合開始剤である過酸化物を併用した、ラジカル硬化型接着剤が注目されている。ラジカル硬化は、反応活性種であるラジカルが反応性に富むため、短時間硬化が可能である（例えば、特許文献３参照）。 The anisotropic conductive film contains an adhesive component containing a thermosetting resin and conductive particles to be blended if necessary, and is formed into a film on a support (separator) such as a PET (polyethylene terephthalate) film. In many cases, the tape is slit into a tape shape and then wound around the core material in the same circular center shape to be commercialized as a reel-shaped narrow and long tape (rolled body) (for example, refer to Patent Document 1). Conventionally, as the anisotropic conductive film, a thermosetting resin using an epoxy resin having high adhesiveness and high reliability has been used (for example, refer to Patent Document 2). Further, radical curable adhesives in which an acrylate derivative or a methacrylate derivative and a peroxide which is a radical polymerization initiator are used in combination have attracted attention. In radical curing, radicals, which are reactive species, are highly reactive and can be cured in a short time (for example, see Patent Document 3).
ところで、近年、液晶ディスプレイに代表されるフラットパネルディスプレイの高精細化に伴い、低温接続可能な異方導電フィルムが要求されている。特に、液晶駆動用ＩＣドライバをフラットパネルディスプレイに直接実装するＣＯＧ（Ｃｈｉｐ ｏｎ Ｇｌａｓｓ）実装では、被熱膨張係数の差に起因する圧着後の被着体の収縮量が大きく異なるため、反りが発生するとともに、表示品質の低下が問題となる。 By the way, in recent years, with the increase in definition of flat panel displays typified by liquid crystal displays, there is a demand for anisotropic conductive films that can be connected at low temperatures. In particular, in COG (Chip on Glass) mounting in which the liquid crystal driving IC driver is directly mounted on the flat panel display, the amount of contraction of the adherend after pressure bonding due to the difference in the coefficient of thermal expansion is significantly different, so that warpage occurs. In addition, the deterioration of display quality becomes a problem.
従来の異方導電フィルムとしては、潜在性硬化剤とエポキシ樹脂を用いた熱硬化、アクリレート誘導体やメタアクリレート誘導体とラジカル重合開始剤である過酸化物を併用した熱硬化が行われているが、更なる低温接続を達成するために、紫外線照射によって活性化する潜在性硬化剤及びモノマを含有した異方導電フィルムは、加熱圧着時に比較的低温での接続が可能となっており、検討が進められている。 As the conventional anisotropic conductive film, heat curing using a latent curing agent and an epoxy resin, heat curing using a combination of an acrylate derivative or a methacrylate derivative and a peroxide that is a radical polymerization initiator is performed, In order to achieve even lower temperature connection, anisotropic conductive film containing latent curing agent and monomer that is activated by UV irradiation can be connected at a relatively low temperature during thermocompression bonding, and further study is underway. Has been.
ところで、紫外線照射によって活性化する潜在性硬化剤を含有した異方導電フィルムは、蛍光灯から発せられる微量な紫外線によってもモノマの重合開始成分が発生し、可視光下での保存安定性が悪化するため、紫外線を遮断した環境において取り扱う必要がある問題が生じる。 By the way, in the anisotropic conductive film containing a latent curing agent that is activated by ultraviolet irradiation, the polymerization initiation component of the monomer is generated even by a small amount of ultraviolet rays emitted from a fluorescent lamp, and the storage stability under visible light deteriorates. Therefore, there arises a problem that it must be handled in an environment where ultraviolet rays are blocked.
本発明は、上記課題の解決のためになされたものであり、異方導電フィルム用リールが紫外線を吸収することで、紫外線を遮光した環境以外においても、リールの巻芯に巻きつけられた異方導電フィルムの保存安定性が向上する異方導電フィルム用リール及び異方導電フィルム巻を提供することを目的とする。 The present invention has been made to solve the above-mentioned problems, and by absorbing the ultraviolet rays by the anisotropic conductive film reel, even in an environment other than the environment in which the ultraviolet rays are shielded, the anisotropic core wound on the reel core is different. An object of the present invention is to provide an anisotropic conductive film reel and an anisotropic conductive film winding in which the storage stability of the anisotropic conductive film is improved.
上記課題の解決のため、本発明に係る異方導電フィルム用リールは、巻芯と、前記巻芯の両側に互いに対向するように設けられた一対の側板と、を備え、前記一対の側板が、紫外線吸収剤を含有する。この異方導電フィルム用リールを用いることにより、紫外線照射によって活性化する潜在性硬化剤及びモノマを含有する異方導電フィルムを使用する場合にも、紫外線に対する保存安定性を向上することができる。 In order to solve the above problems, the reel for anisotropically conductive film according to the present invention includes a winding core and a pair of side plates provided so as to face each other on both sides of the winding core, and the pair of side plates is , Containing an ultraviolet absorber. By using this anisotropic conductive film reel, it is possible to improve the storage stability against ultraviolet rays even when an anisotropic conductive film containing a latent curing agent and a monomer that is activated by ultraviolet irradiation is used.
紫外線吸収剤は、トリアジン骨格、ベンゾトリアゾール骨格、或いはベンゾフェノン骨格を有する化合物を用いることができる。これにより、紫外線の遮光とリールの退色を両立することができる。 As the ultraviolet absorber, a compound having a triazine skeleton, a benzotriazole skeleton, or a benzophenone skeleton can be used. This makes it possible to both block the ultraviolet rays and fade the reel.
また、本発明は、異方導電フィルム用リールの巻芯に巻きつけられた異方導電フィルムを備える異方導電フィルム巻であって、前記異方導電フィルムは、テープ状の基材及びその一方面上に設けられた接着剤層を有し、少なくとも紫外線照射によって活性化する潜在性硬化剤及びモノマを含有する異方導電フィルム巻を提供する。これによって、紫外線に対する保存安定性が良好な、紫外線照射によって活性化する潜在性硬化剤及びモノマを含有する異方導電フィルム巻を得ることができる。 Further, the present invention is an anisotropic conductive film winding comprising an anisotropic conductive film wound around a winding core of an anisotropic conductive film reel, wherein the anisotropic conductive film is a tape-shaped base material and one of the same. Provided is an anisotropic conductive film winding having an adhesive layer provided on one side and containing at least a latent curing agent and a monomer which are activated by ultraviolet irradiation. As a result, it is possible to obtain an anisotropically conductive film winding containing a latent curing agent and a monomer which are activated by irradiation with ultraviolet rays and have good storage stability against ultraviolet rays.
本発明によれば、紫外線を遮光した環境以外においても、リールの巻芯に巻きつけられた異方導電フィルムの保存安定性が向上する異方導電フィルム用リール及び異方導電フィルム巻を提供することができる。 According to the present invention, there is provided an anisotropic conductive film reel and an anisotropic conductive film winding in which the storage stability of an anisotropic conductive film wound around a reel core is improved even in an environment other than the environment in which ultraviolet rays are shielded. be able to.
以下、図面を参照しながら、本発明に係る異方導電フィルム用リールの好適な実施形態について詳細に説明する。なお、図面の説明において同一の要素には同一の符号を付し、重複する説明を省略する。また、図示の便宜上、図面の寸法比率は説明のものと必ずしも一致しない。 Hereinafter, preferred embodiments of an anisotropic conductive film reel according to the present invention will be described in detail with reference to the drawings. In the description of the drawings, the same elements will be denoted by the same reference symbols, without redundant description. Further, for convenience of illustration, the dimensional ratios in the drawings do not necessarily match those described.
図１は、本発明に係る異方導電フィルム用リールの一実施形態を示す斜視図である。また、図２は、本発明に係る異方導電フィルム用リールの側板の内側面を示す正面図である。 FIG. 1 is a perspective view showing an embodiment of the anisotropic conductive film reel according to the present invention. FIG. 2 is a front view showing the inner surface of the side plate of the anisotropic conductive film reel according to the present invention.
図１，２に示すように、本実施形態における異方導電フィルム用リール１は、異方導電フィルム５が巻き付けられる筒状の巻芯２と、巻芯２の両端部において巻芯２を挟むように互いに対向して設けられた一対の側板３，３とを備えている。異方導電フィルム用リール１は、一対の側板３，３の協同によって、異方導電フィルム５の巻き崩れを防止するものであり、異方導電フィルム５を製造・供給・保存する際に用いられる。本実施形態における異方導電フィルム巻１０は、異方導電フィルム用リール１と、異方導電フィルム用リール１の巻芯２に巻き付けられた異方導電フィルム５と、を備えている。 As shown in FIGS. 1 and 2, in the anisotropic conductive film reel 1 according to the present embodiment, a cylindrical core 2 around which the anisotropic conductive film 5 is wound, and the core 2 is sandwiched between both ends of the core 2. As described above, the pair of side plates 3 and 3 are provided so as to face each other. The anisotropic conductive film reel 1 prevents the anisotropic conductive film 5 from collapsing due to the cooperation of the pair of side plates 3 and 3, and is used when the anisotropic conductive film 5 is manufactured, supplied and stored. .. The anisotropic conductive film winding 10 according to the present embodiment includes an anisotropic conductive film reel 1 and an anisotropic conductive film 5 wound around a winding core 2 of the anisotropic conductive film reel 1.
巻芯２は、異方導電フィルム５を巻き付ける部分であり、巻芯２の軸方向の長さは、異方導電フィルム５の幅よりもわずかに長くなるように、異方導電フィルム５の幅に応じて適宜設定されている。また、巻芯２の中央部には、巻付装置又は繰出装置（不図示）の回転軸が挿入される軸穴４が設けられている。軸穴４は、例えば、断面円形状をなしており、巻付装置又は繰出装置の回転軸を軸穴４に差し込んだ状態で回転軸を駆動した場合に、空回りすることなく異方導電フィルム用リール１が回転するようになっている。巻芯２は、例えば、プラスチックからなり、異方導電フィルム５の幅と同様の厚さの円筒状をなしている。 The winding core 2 is a portion around which the anisotropic conductive film 5 is wound, and the width of the anisotropic conductive film 5 is set so that the axial length of the winding core 2 is slightly longer than the width of the anisotropic conductive film 5. It is set appropriately according to. A shaft hole 4 into which a rotary shaft of a winding device or a feeding device (not shown) is inserted is provided in the center of the winding core 2. The shaft hole 4 has, for example, a circular cross section, and when the rotary shaft of the winding device or the feeding device is driven into the shaft hole 4 and the rotary shaft is driven, the shaft hole 4 does not idle and is used for the anisotropic conductive film. The reel 1 is adapted to rotate. The winding core 2 is made of, for example, plastic and has a cylindrical shape having a thickness similar to the width of the anisotropic conductive film 5.
図３は、図１におけるＩＩＩ−ＩＩＩ線に沿った断面図である。図１〜３に示すように、側板３は、例えば、プラスチックからなり、円板状をなしている。巻芯２を介して隔てられた側板３，３間の距離Ｗ１は、異方導電フィルム５の幅よりもわずかに広くなるように、異方導電フィルム５の幅に応じて適宜設定されている。なお、側板３，３間の距離Ｗ１は、側板３の周縁側３ｂ側ほど広がる傾向にあるので、ここでいう側板３，３間の距離Ｗ１は、巻芯付近での測定値で定義している。通常、側板３，３間の距離Ｗ１は、異方導電フィルム５の幅に対して１０５％〜１２０％、より好ましくは１０７〜１１５％の幅で設定される。 FIG. 3 is a cross-sectional view taken along the line III-III in FIG. As shown in FIGS. 1 to 3, the side plate 3 is made of plastic, for example, and has a disc shape. The distance W1 between the side plates 3 and 3 separated by the winding core 2 is appropriately set according to the width of the anisotropic conductive film 5 so as to be slightly wider than the width of the anisotropic conductive film 5. .. Since the distance W1 between the side plates 3 and 3 tends to increase toward the peripheral edge side 3b of the side plate 3, the distance W1 between the side plates 3 and 3 here is defined by the measured value near the winding core. There is. Usually, the distance W1 between the side plates 3 and 3 is set to be 105% to 120%, and more preferably 107 to 115% of the width of the anisotropic conductive film 5.
側板３の厚さＷ２は、０．５ｍｍ〜５．０ｍｍ、好ましくは０．９ｍｍ〜３．０ｍｍ、より好ましくは１．０ｍｍ〜２．０ｍｍ程度となっている。また、側板３の径は、異方導電フィルム５が巻芯２に巻き付けられた際に側板３，３の周縁側３ｂから出ないように、巻き付ける異方導電フィルム５の長さや異方導電フィルム５が巻芯２に巻き付けられた巻重体の直径に応じて適宜設定される。本実施形態では、一対の側板３，３は、厚さＷ２及び径がそれぞれ同等となっている。また、一対の側板３，３の中央部分には、図１に示すように、それぞれ同径の断面円形の開口部３０，３０が設けられている。また、巻芯２は、側板３の内側面３ａにおいて、側板３，３の開口部３０，３０を囲むように固定されている。 The thickness W2 of the side plate 3 is 0.5 mm to 5.0 mm, preferably 0.9 mm to 3.0 mm, and more preferably 1.0 mm to 2.0 mm. The diameter of the side plate 3 is set such that the anisotropic conductive film 5 is wound around the core 2 so that the side plate 3 does not come out from the peripheral side 3b of the side plates 3 and 3 and the anisotropic conductive film 5 is wound. 5 is appropriately set according to the diameter of the wound body wound around the winding core 2. In the present embodiment, the pair of side plates 3 and 3 have the same thickness W2 and the same diameter. Further, as shown in FIG. 1, openings 30 and 30 having the same diameter and circular cross section are provided in the central portions of the pair of side plates 3 and 3, respectively. The winding core 2 is fixed on the inner side surface 3 a of the side plate 3 so as to surround the openings 30 of the side plates 3 and 3.
このような異方導電フィルム用リール１は、射出成形等によって巻芯２及び一対の側板３，３を一体的に成形してもよく、巻芯２及び一対の側板３，３を別々に成形し、これらを嵌合・接着することによって形成してもよい。巻芯２と側板３とを別体とした場合、巻き付ける異方導電フィルム５の長さに適した直径の側板３を適宜採用したり、異方導電フィルム５の幅に適した長さの巻芯２を適宜採用したりすることができるという利点がある。 In such an anisotropic conductive film reel 1, the core 2 and the pair of side plates 3 and 3 may be integrally molded by injection molding or the like, or the core 2 and the pair of side plates 3 and 3 may be molded separately. However, they may be formed by fitting and adhering them. When the winding core 2 and the side plate 3 are separate bodies, the side plate 3 having a diameter suitable for the length of the anisotropic conductive film 5 to be wound is appropriately adopted, or the winding having a length suitable for the width of the anisotropic conductive film 5 is adopted. There is an advantage that the core 2 can be appropriately adopted.
巻芯２に巻き付けられる異方導電フィルム５は、例えば、フィルム状の基材６及びその一方面上に設けられた接着剤層８を有する異方導電フィルム５が細幅に切断されたものである。異方導電フィルム５は、例えば、相対する電極同士の導通状態を保ち、かつ隣接する電極同士の絶縁を保つように、電気的接続と機械的固着とを行う接続材料として使用される。異方導電フィルム５の長さは、通常は５０ｍ〜１０００ｍ程度であり、２００ｍ〜１０００ｍが好ましく、３００ｍ〜７００ｍがより好ましい。異方導電フィルム５の幅は、０．５ｍｍ〜１０ｍｍ、好ましくは０．５ｍｍ〜３．０ｍｍ、より好ましくは０．５ｍｍ〜２．０ｍｍ程度となっている。異方導電フィルム５の厚さは、５μｍ〜１００μｍ、好ましくは１０μｍ〜５０μｍ、より好ましくは１０μｍ〜３０μｍ程度となっている。なお、本実施形態では、基材６の厚さは、異方導電フィルム５の厚さと同程度となっている。また、本実施形態では、異方導電フィルム５の長さが３００ｍ以上となっている。 The anisotropic conductive film 5 wound around the winding core 2 is, for example, one obtained by cutting the anisotropic conductive film 5 having a film-shaped base material 6 and an adhesive layer 8 provided on one surface thereof into a narrow width. is there. The anisotropic conductive film 5 is used, for example, as a connecting material that performs electrical connection and mechanical fixing so that the electrodes facing each other are electrically connected and the electrodes adjacent to each other are insulated. The length of the anisotropic conductive film 5 is usually about 50 m to 1000 m, preferably 200 m to 1000 m, and more preferably 300 m to 700 m. The width of the anisotropic conductive film 5 is 0.5 mm to 10 mm, preferably 0.5 mm to 3.0 mm, and more preferably 0.5 mm to 2.0 mm. The thickness of the anisotropic conductive film 5 is 5 μm to 100 μm, preferably 10 μm to 50 μm, more preferably about 10 μm to 30 μm. In addition, in the present embodiment, the thickness of the base material 6 is approximately the same as the thickness of the anisotropic conductive film 5. Moreover, in this embodiment, the length of the anisotropic conductive film 5 is 300 m or more.
異方導電フィルム５は、巻芯２に巻き取る最初の部分（巻き始めの部分）が巻芯２に固定されている。この固定方法としては、周知の方法を使用できるが、例えば、粘着テープ、粘着剤により固定することができる。また、巻芯２に留め具や切り込み部を設けて固定することもできる。この中でも作業性の観点から粘着テープ又は粘着剤を使用して固定することが好ましい。 The anisotropic conductive film 5 is fixed to the winding core 2 at a first portion (a winding start portion) to be wound around the winding core 2. As this fixing method, a well-known method can be used. For example, it can be fixed with an adhesive tape or an adhesive. Further, the winding core 2 can be fixed by providing a fastener or a cut portion. Among these, it is preferable to use an adhesive tape or an adhesive for fixation from the viewpoint of workability.
基材６は、例えば、ポリエチレンテレフタレート、ポリエチレンナフタレート、ポリエチレンイソフタレート、ポリブチレンテレフタレート、ポリオレフィン、ポリアセテート、ポリカーボネート、ポリフェニレンサルファイド、ポリアミド、エチレン・酢酸ビニル共重合体、ポリ塩化ビニル、ポリ塩化ビニリデン、合成ゴム系、液晶ポリマー等からなる各種プラスチックテープ、又は、銅、アルミニウム等の金属箔を使用することが可能である。もっとも、基材６を構成する材質はこれらに限定されるものではない。また、基材６として、接着剤層８との当接面等に離型処理が施されたものを使用してもよい。基材６の一方面上に設けられた接着剤層８上に、更に接着剤層８を保護するためのカバーフィルムが積層されたものを使用しても構わない。 The base material 6 is, for example, polyethylene terephthalate, polyethylene naphthalate, polyethylene isophthalate, polybutylene terephthalate, polyolefin, polyacetate, polycarbonate, polyphenylene sulfide, polyamide, ethylene / vinyl acetate copolymer, polyvinyl chloride, polyvinylidene chloride, It is possible to use various plastic tapes made of synthetic rubber, liquid crystal polymer or the like, or metal foils such as copper and aluminum. However, the material forming the base material 6 is not limited to these. Further, as the base material 6, it is possible to use the base material 6 whose release surface is abutted against the adhesive layer 8. You may use what laminated | stacked the cover film for protecting the adhesive bond layer 8 further on the adhesive bond layer 8 provided on one surface of the base material 6.
接着剤層８は、少なくとも紫外線照射によって活性化する潜在性硬化剤及びモノマを含有し、必要により含有される導電粒子とを含んでなる接着剤組成物からなることが好ましい。接続後の耐熱性や耐湿性に優れていることから、架橋性材料の使用が好ましい。エポキシ樹脂を主成分として含有するエポキシ系接着剤は、接続作業性が良く、分子構造上接着性に優れている等の特徴から好ましい。また、アクリレートモノマを主成分として含有するアクリル系接着剤は、速硬化性が高く、短時間硬化性に優れる。 The adhesive layer 8 preferably comprises an adhesive composition containing at least a latent curing agent that is activated by irradiation with ultraviolet rays and a monomer, and optionally containing conductive particles. It is preferable to use a crosslinkable material because it has excellent heat resistance and moisture resistance after connection. An epoxy-based adhesive containing an epoxy resin as a main component is preferable because it has excellent workability in connection and excellent adhesiveness due to its molecular structure. An acrylic adhesive containing an acrylate monomer as a main component has high fast-curing property and excellent short-time curability.
紫外線照射によって活性化する潜在性硬化剤は、紫外線照射によって酸、又はラジカルが発生するものが用いられ、接着剤層８に含有するモノマの種類によって適宜選ばれ、例えば、エポキシ樹脂系接着剤では酸を、アクリル系接着剤ではラジカルが発生する硬化剤が好適に用いられる。 As the latent curing agent that is activated by UV irradiation, those that generate an acid or a radical by UV irradiation are used and are appropriately selected depending on the type of the monomer contained in the adhesive layer 8. For example, in the epoxy resin adhesive, As the acid, a curing agent that generates radicals is preferably used in the acrylic adhesive.
導電粒子としては、例えば、Ａｕ、Ａｇ、Ｐｔ、Ｎｉ、Ｃｕ、Ｗ、Ｓｂ、Ｓｎ、はんだ等の金属やカーボンの粒子が挙げられる。また、非導電性のガラス、セラミック、プラスチック等を核とし、この核を上記の金属やカーボンで被覆した被覆粒子を使用してもよい。導電粒子の平均粒径は、分散性、導電性の観点から１μｍ〜３０μｍであることが好ましい。なお、導電粒子を絶縁層で被覆してなる絶縁被覆粒子を使用してもよく、隣接する電極同士の絶縁性を向上させる観点から導電粒子と絶縁性粒子とを併用してもよい。 Examples of the conductive particles include particles of metal such as Au, Ag, Pt, Ni, Cu, W, Sb, Sn and solder, and carbon particles. Further, coated particles in which a non-conductive glass, ceramic, plastic or the like is used as a core and the core is coated with the above metal or carbon may be used. The average particle diameter of the conductive particles is preferably 1 μm to 30 μm from the viewpoint of dispersibility and conductivity. It should be noted that insulating coated particles obtained by coating the conductive particles with an insulating layer may be used, or the conductive particles and the insulating particles may be used together from the viewpoint of improving the insulating property between adjacent electrodes.
導電粒子の配合割合は、接着剤層に含まれる接着剤成分１００体積部に対して、０．１〜３０体積部であることが好ましく、０．１〜１０体積部であることがより好ましい。この配合割合が０．１体積部以上であると対向する電極間の接続抵抗を低減することができ、３０体積部以下であると隣接する電極間の絶縁性が充分である。 The mixing ratio of the conductive particles is preferably 0.1 to 30 parts by volume, and more preferably 0.1 to 10 parts by volume with respect to 100 parts by volume of the adhesive component contained in the adhesive layer. When the mixing ratio is 0.1 volume part or more, the connection resistance between the opposing electrodes can be reduced, and when it is 30 volume parts or less, the insulating property between the adjacent electrodes is sufficient.
続いて、上述した巻芯２及び側板３の材質について説明する。 Next, the materials of the core 2 and the side plate 3 described above will be described.
上述した巻芯２及び、側板３の材質としては、プラスチック樹脂組成物からなることが好ましく、ポリエチレン、ポリプロピレン、ポリブタジエン、ポリエステル、ポリエチレンテレフタレート、ポリカーボネート、ポリ塩化ビニル、ポリスチレン、ポリ酢酸ビニル、アクリル樹脂、メタクリル樹脂、環状ポリオレフィン、ポリアセタール等の汎用プラスチックやエンジニアリングプラスチックなどから適宜選択することができるがこれらに限ったものではない。これら材質は１種を単独で又は２種以上を組み合わせて用いることができる。
室温での形状維持及び、成形性の観点から、ポリエステル、ポリエステルテレフタレート、ポリプロピレン、アクリル樹脂等が好適に用いられる。
The material of the winding core 2 and the side plate 3 described above is preferably made of a plastic resin composition, such as polyethylene, polypropylene, polybutadiene, polyester, polyethylene terephthalate, polycarbonate, polyvinyl chloride, polystyrene, polyvinyl acetate, acrylic resin, It can be appropriately selected from general-purpose plastics such as methacrylic resin, cyclic polyolefin, polyacetal, and engineering plastics, but is not limited thereto. These materials may be used alone or in combination of two or more.
From the viewpoint of shape retention at room temperature and moldability, polyester, polyester terephthalate, polypropylene, acrylic resin and the like are preferably used.
続いて、側板３に含有される紫外線吸収剤について説明する。 Next, the ultraviolet absorber contained in the side plate 3 will be described.
紫外線吸収剤は、紫外線を吸収する能力を有する化合物である。紫外線吸収剤は、主に光エネルギーを熱エネルギーに変換する機能を有すると言われる化合物である。
紫外線吸収剤としては、ベンゾフェノン類、ベンゾトリアゾール類、トリアジン類、ベンゾエート類、サリシレート類、シアノアクリレート類、蓚酸アニリド類、マロン酸エステル類、ホルムアミジン類、アクリロニトリル類等が挙げられる。これらは１種単独で又は２種以上を組み合わせて用いることができる。これらの中でも、ベンゾトリアゾール類、又は波長３８０〜４５０ｎｍにおけるモル吸光係数の最大値εｍａｘが１２００ｄｍ３・ｍｏｌ−１ｃｍ−１以下である紫外線吸収剤が好ましい。
A UV absorber is a compound that has the ability to absorb UV light. The ultraviolet absorber is a compound which is said to have a function of mainly converting light energy into heat energy.
Examples of the ultraviolet absorber include benzophenones, benzotriazoles, triazines, benzoates, salicylates, cyanoacrylates, anilide oxalates, malonates, formamidines, acrylonitriles and the like. These can be used alone or in combination of two or more. Among these, benzotriazoles or ultraviolet absorbers having a maximum molar extinction coefficient ε max at a wavelength of 380 to 450 nm of 1200 dm 3 · mol −1 cm −1 or less are preferable.
ベンゾトリアゾール類としては、２−（２Ｈ−ベンゾトリアゾール−２−イル）−４−（１，１，３，３−テトラメチルブチル）フェノール（株式会社ＡＤＥＫＡ製；商品名：アデカスタブＬＡ−２９（「アデカスタブ」は、登録商標。））、２，２´−メチレンビス［６−（２Ｈ−ベンゾトリアゾール−２−イル）−４−（１，１，３，３−テトラメチルブチル）フェノール］（株式会社ＡＤＥＫＡ製；商品名：アデカスタブＬＡ−３１）、２−（２Ｈ−ベンゾトリアゾール−２−イル）−パラクレゾール（株式会社ＡＤＥＫＡ製；商品名：アデカスタブＬＡ−３２）、２−（２Ｈ−ベンゾトリアゾール−２−イル）−４，６−ビス（１−メチル−１−フェニルエチル）フェノール（ＢＡＳＦ社製；商品名：ＴＩＮＵＶＩＮ２３４（「ＴＩＮＵＶＩＮ」は、登録商標。））、２−（５−クロロ−２Ｈ−ベンゾトリアゾール−２−イル）−６−ターシャリーブチル−４−メチルフェノール（株式会社ＡＤＥＫＡ製；商品名：アデカスタブＬＡ−３６）等が挙げられるがこれらに限ったものではない。 As the benzotriazoles, 2- (2H-benzotriazol-2-yl) -4- (1,1,3,3-tetramethylbutyl) phenol (manufactured by ADEKA Corporation; trade name: ADEKA STAB LA-29 (" ADEKA STAB "is a registered trademark.)), 2,2'-methylenebis [6- (2H-benzotriazol-2-yl) -4- (1,1,3,3-tetramethylbutyl) phenol] (Ltd. ADEKA; trade name: ADEKA STAB LA-31), 2- (2H-benzotriazol-2-yl) -paracresol (manufactured by ADEKA; trade name: ADEKA STAB LA-32), 2- (2H-benzotriazole- 2-yl) -4,6-bis (1-methyl-1-phenylethyl) phenol (manufactured by BASF; trade name: TINUVIN234 (“TI "UVIN" is a registered trademark.), 2- (5-chloro-2H-benzotriazol-2-yl) -6-tert-butyl-4-methylphenol (manufactured by ADEKA Corporation; trade name: ADEKA STAB LA-36). ) And the like, but not limited to these.
トリアジン類としては、２−［４，６−ジ（２，４−キシリル）−１，３，５−トリアジン−２−イル］−５−オクチルオキシフェノール（ＢＡＳＦ社製；商品名：ＴＩＮＵＶＩＮ４１１Ｌ）、２−［４−［（２−ヒドロキシ−３−ドデシルオキシプロピル）オキシ］−４，６−ビス（２，４−ジメチルフェニル）−１，３，５−トリアジン／２−［４−［（２−ヒドロキシ−３−トリドデシルオキシプロピル）オキシ］−２−ヒドロキシフェニル］−４，６−ビス（２，４−ジメチルフェニル）−１，３，５−トリアジン（ＢＡＳＦ社製；商品名：ＴＩＮＵＶＩＮ４００）、２−（４，６−ジフェニル−１，３，５−トリアジン−２−イル）−５−（ヘキシルオキシ）フェノール（ＢＡＳＦ社製；商品名：ＴＩＮＵＶＩＮ１５７７）、［２−（４，６−ジフェニル−１，３，５−トリアジン−２−イル）−５−（２−（２−エチルヘキサノイルオキシ）エトキシ）フェノール（株式会社ＡＤＥＫＡ製；商品名：アデカスタブＬＡ−４６）、２，４，６−トリス（２−ヒドロキシ−４−ヘキシルオキシ−３−メチルフェニル）−１，３，５−トリアジン（株式会社ＡＤＥＫＡ製；商品名：アデカスタブＬＡ−Ｆ７０）等が挙げられるがこれらに限ったものではない。 Examples of triazines include 2- [4,6-di (2,4-xylyl) -1,3,5-triazin-2-yl] -5-octyloxyphenol (manufactured by BASF; trade name: TINUVIN411L), 2- [4-[(2-hydroxy-3-dodecyloxypropyl) oxy] -4,6-bis (2,4-dimethylphenyl) -1,3,5-triazine / 2- [4-[(2 -Hydroxy-3-tridodecyloxypropyl) oxy] -2-hydroxyphenyl] -4,6-bis (2,4-dimethylphenyl) -1,3,5-triazine (manufactured by BASF; trade name: TINUVIN400) , 2- (4,6-diphenyl-1,3,5-triazin-2-yl) -5- (hexyloxy) phenol (manufactured by BASF; trade name: TINUVIN1577), [2 (4,6-diphenyl-1,3,5-triazin-2-yl) -5- (2- (2-ethylhexanoyloxy) ethoxy) phenol (manufactured by ADEKA; trade name: ADEKA STAB LA-46) 2,2,6-tris (2-hydroxy-4-hexyloxy-3-methylphenyl) -1,3,5-triazine (manufactured by ADEKA Co., Ltd .; trade name: ADEKA STAB LA-F70) and the like. It is not limited to these.
ベンゾフェノン類としては、［２−ヒドロキシ−４−（オクチルオキシ）フェニル］（フェニル）メタノン（株式会社ＡＤＥＫＡ製；商品名：アデカスタブ１４１３）、［２−ヒドロキシ−４−（メトキシ）フェニル］（フェニル）メタノン（ケミプロ化成株式会社製；商品名：ＫＥＭＩＳＯＲＢ１１（「ＫＥＭＩＳＯＲＢ」は、登録商標。））、（２，４−ジヒドロキシフェニル）（フェニル）メタノン（ケミプロ化成株式会社製；商品名：ＫＥＭＩＳＯＲＢ１０）等が挙げられるがこれに限ったものではない。
これら紫外線吸収剤は１種を単独で又は２種以上を組み合わせて用いることができる。
Examples of benzophenones include [2-hydroxy-4- (octyloxy) phenyl] (phenyl) methanone (manufactured by ADEKA; trade name: ADEKA STAB 1413), [2-hydroxy-4- (methoxy) phenyl] (phenyl). Methanone (manufactured by Chemipro Kasei Co., Ltd .; trade name: KEMISORB11 (“KEMISORB” is a registered trademark)), (2,4-dihydroxyphenyl) (phenyl) methanone (manufactured by Chemipro Kasei Co., Ltd .; trade name: KEMISORB10), etc. Examples include but are not limited to:
These ultraviolet absorbers can be used alone or in combination of two or more.
紫外線吸収剤の配合量は、巻芯２及び側板３の材質として用いられるプラスチック樹脂組成物１００質量部に対して、好ましくは０．１〜５質量部、より好ましくは０．５〜３質量部である。紫外線吸収剤を含有させる方法としては、紫外線吸収剤を予めプラスチック樹脂組成物に配合してペレット化しておき、これを溶融押出等によって成形する方法、溶融押出成形時に直接、紫外線吸収剤を添加する方法、成形後の異方導電フィルム用リールに紫外線吸収剤を塗布する方法などが挙げられ、いずれの方法も使用できる。
なお、紫外線吸収剤は側板だけに含有されていてもよいし、巻芯及び側板に含有されていてもよい。
The blending amount of the ultraviolet absorber is preferably 0.1 to 5 parts by mass, more preferably 0.5 to 3 parts by mass with respect to 100 parts by mass of the plastic resin composition used as the material of the winding core 2 and the side plate 3. Is. As a method of incorporating the ultraviolet absorber, the ultraviolet absorber is preliminarily blended with the plastic resin composition and pelletized, and the mixture is molded by melt extrusion or the like, or the ultraviolet absorber is directly added during melt extrusion molding. Examples thereof include a method and a method of applying an ultraviolet absorber to the anisotropic conductive film reel after molding, and any method can be used.
The ultraviolet absorber may be contained only in the side plate, or may be contained in the core and the side plate.
以上、本発明の好適な実施形態について説明したが、本発明は、上記実施形態に限られるものではない。 Although the preferred embodiment of the present invention has been described above, the present invention is not limited to the above embodiment.
また、異方導電フィルム用リール１は、図２に示したように一対の側板３，３が巻芯２を挟むように互いに対向して設けられたものに限られない。例えば、巻芯２が一対の側板３，３の外側へ突出するように設けられていても構わない。また更に、一対の側板３，３は、厚さＷ２及び径がそれぞれ同等でなくても構わない。 Further, the anisotropic conductive film reel 1 is not limited to the one provided with the pair of side plates 3 and 3 facing each other so as to sandwich the winding core 2 as shown in FIG. For example, the winding core 2 may be provided so as to project to the outside of the pair of side plates 3 and 3. Furthermore, the pair of side plates 3 and 3 may not have the same thickness W2 and diameter.
また、上述した異方導電フィルム用リール１においては、接着剤層８が接着剤成分と、必要により含有される導電粒子を含んでいた異方導電フィルム５を巻き付けていたが、異方導電フィルム５の構成はこれに限られない。接着剤層８が接着剤成分からなり導電粒子を含まなくても構わない。また、接着剤層８に、導電粒子を異方導電テープよりも多く配合させ、異方性を有さない導電テープとしてもよい。上記以外の巻芯２に捲き付けられるテープとしては、ダイボンドフィルム、銀フィルム、半導体ウエハ加工用の接着フィルム等各種の電子材料用の接着フィルムを適用することができる。 Further, in the anisotropic conductive film reel 1 described above, the adhesive layer 8 is wound around the anisotropic conductive film 5 containing the adhesive component and the conductive particles optionally contained. The configuration of 5 is not limited to this. The adhesive layer 8 may be made of an adhesive component and may not contain conductive particles. Further, the adhesive layer 8 may be mixed with more conductive particles than the anisotropic conductive tape to provide a conductive tape having no anisotropy. As the tape wound around the core 2 other than the above, adhesive films for various electronic materials such as a die bond film, a silver film, and an adhesive film for processing a semiconductor wafer can be applied.
以下、本発明の好適な実施例について更に詳細に説明するが、本発明はこれらの実施例に限定されるものではない。 Hereinafter, preferred examples of the present invention will be described in more detail, but the present invention is not limited to these examples.
［参考例１］
硬化性成分として、脂環式エポキシ樹脂であるＣＥＬ２０２１Ｐ（株式会社ダイセル製、商品名）：２５質量部及びビスフェノールＡ型エポキシ樹脂であるＹＬ９８０（三菱化学株式会社製、商品名）：２５質量部と、光カチオン重合開始剤であるイルガキュア２５０（ＢＡＳＦ社製、商品名（「イルガキュア」は、登録商標））：３質量部とを用いた。バインダとして、フェノキシ樹脂ＹＰ−７０（新日鉄住金化学株式会社製、商品名）：５０質量部を用いた。また、ポリスチレンを核とする粒子の表面に厚さ０．２μｍのニッケル層を設け、このニッケル層の外側に厚さ０．０２μｍの金属層を設けることにより、平均粒径３μｍ、比重２．５の導電粒子を作製し、４０質量部を用いた。各成分を配合し、厚さ４０μｍのＰＥＴフィルムに塗工装置を用いて塗布し、７０℃、５分の熱風乾燥によって厚さが２０μｍの異方導電フィルムＡを得た。
[Reference Example 1]
As a curable component, CEL2021P (manufactured by Daicel Corporation, trade name) which is an alicyclic epoxy resin: 25 parts by mass and YL980 (manufactured by Mitsubishi Chemical Co., trade name) which is a bisphenol A type epoxy resin: 25 parts by mass And 3 parts by mass of Irgacure 250 (trade name (“Irgacure” is a registered trademark) manufactured by BASF) as a photocationic polymerization initiator. As the binder, 50 parts by mass of phenoxy resin YP-70 (trade name, manufactured by Nippon Steel & Sumikin Chemical Co., Ltd.) was used. Further, a nickel layer having a thickness of 0.2 μm is provided on the surface of particles having polystyrene as a nucleus, and a metal layer having a thickness of 0.02 μm is provided on the outside of the nickel layer, whereby an average particle diameter of 3 μm and a specific gravity of 2.5. 40 parts by mass of the conductive particles were prepared. Each component was mixed and applied to a PET film having a thickness of 40 μm by using a coating device, and dried by hot air at 70 ° C. for 5 minutes to obtain an anisotropic conductive film A having a thickness of 20 μm.
［参考例２］
硬化性成分として、ラジカル重合性化合物であるＵＡ５５００（根上工業株式会社製、商品名）：２５質量部及びＭ３１３（新中村化学工業株式会社製、商品名）：２５質量部と、光ラジカル重合開始剤であるイルガキュアＯＸＥ０２（ＢＡＳＦ社製、商品名）：３質量部とを用いた。バインダとして、フェノキシ樹脂ＹＰ−７０（新日鉄住金化学株式会社製、商品名）：５０質量部を用いた。また、ポリスチレンを核とする粒子の表面に厚さ０．２μｍのニッケル層を設け、このニッケル層の外側に厚さ０．０２μｍの金属層を設けることにより、平均粒径３μｍ、比重２．５の導電粒子を作製し、４０質量部を用いた。各成分を配合し、厚さ４０μｍのＰＥＴフィルムに塗工装置を用いて塗布し、７０℃、５分の熱風乾燥によって厚さが２０μｍの異方導電フィルムＢを得た。
[Reference Example 2]
As a curable component, a radical polymerizable compound, UA5500 (manufactured by Negami Kogyo Co., Ltd., trade name): 25 parts by mass and M313 (Shin Nakamura Chemical Co., Ltd., trade name): 25 parts by mass, and radical photopolymerization initiation Irgacure OXE02 (manufactured by BASF, trade name): 3 parts by mass as an agent. As the binder, 50 parts by mass of phenoxy resin YP-70 (trade name, manufactured by Nippon Steel & Sumikin Chemical Co., Ltd.) was used. Further, a nickel layer having a thickness of 0.2 μm is provided on the surface of particles having polystyrene as a nucleus, and a metal layer having a thickness of 0.02 μm is provided on the outside of the nickel layer, whereby an average particle diameter of 3 μm and a specific gravity of 2.5. 40 parts by mass of the conductive particles were prepared. Each component was mixed and applied to a PET film having a thickness of 40 μm by using a coating device, and dried with hot air at 70 ° C. for 5 minutes to obtain an anisotropic conductive film B having a thickness of 20 μm.
［実施例１〜６及び比較例１，２］
表１に示す紫外線吸収剤を、リールを構成する樹脂１００質量部に対して３質量部配合した条件で異方導電フィルム用リール及び異方導電フィルム巻を作製した後、異方導電フィルム巻を蛍光灯下にて２４時間横置きした場合における、異方導電フィルムの保存安定性を評価した。保存安定性は、異方導電フィルムの赤外吸収スペクトルを測定し、エポキシの転化率を測定することにより評価した。なお、異方導電フィルムとしては、上記で作製した異方導電フィルムＡ及び異方導電フィルムＢを用いた。評価結果を表１に示す。
[Examples 1 to 6 and Comparative Examples 1 and 2]
After producing the reel for anisotropic conductive film and the anisotropic conductive film winding under the condition that 3 parts by mass of the ultraviolet absorber shown in Table 1 was mixed with 100 parts by mass of the resin constituting the reel, the anisotropic conductive film winding was performed. The storage stability of the anisotropic conductive film was evaluated when it was left horizontally for 24 hours under a fluorescent lamp. The storage stability was evaluated by measuring the infrared absorption spectrum of the anisotropic conductive film and measuring the conversion of epoxy. As the anisotropic conductive film, the anisotropic conductive film A and the anisotropic conductive film B produced above were used. The evaluation results are shown in Table 1.
表１に示すように、紫外線吸収剤を配合しない比較例１及び２に示す異方導電フィルム用リールに巻きつけられた異方導電フィルム巻は、２４時間後にモノマがそれぞれ３０％及び３２％エポキシ転化したが、紫外線吸収剤を配合した実施例１〜６に示す異方導電フィルム用リールに巻きつけられた異方導電フィルム巻は、２４時間後もエポキシ転化率が５％以下であり良好な保存安定性を示した。 As shown in Table 1, the anisotropic conductive film wound around the reels for anisotropic conductive film shown in Comparative Examples 1 and 2 containing no ultraviolet absorber had monomers of 30% and 32% epoxy after 24 hours, respectively. Although converted, the anisotropic conductive film wound around the anisotropic conductive film reels shown in Examples 1 to 6 containing the ultraviolet absorber had an epoxy conversion rate of 5% or less even after 24 hours, which was good. It showed storage stability.
１ 異方導電フィルム用リール
１０ 異方導電フィルム巻
２ 巻芯
３ 側板
３ａ 側板の内側面
３ｂ 側板の周縁側
３０ 側板の開口部
４ 軸穴
５ 異方導電フィルム
６ 基材
８ 接着剤層
Ｗ１ 側板間の距離
Ｗ２ 側板の厚さ
DESCRIPTION OF SYMBOLS 1 Anisotropic conductive film reel 10 Anisotropic conductive film winding 2 Core 3 Side plate 3a Side plate inner side surface 3b Side plate peripheral edge side 30 Side plate opening 4 Shaft hole 5 Anisotropic conductive film 6 Base material 8 Adhesive layer W1 Side plate Distance between W2 Side plate thickness
Claims (3)
前記一対の側板は、紫外線吸収剤を含有する、異方導電フィルム用リール。 A reel for an anisotropic conductive film, comprising: a winding core; and a pair of side plates provided so as to face each other on both sides of the winding core,
The pair of side plates is an anisotropic conductive film reel containing an ultraviolet absorber.
It is an anisotropic conductive film winding provided with the anisotropic conductive film wound around the said core of the anisotropic conductive film reel as described in any one of Claim 1 or 2, Comprising: The said anisotropic conductive film is An anisotropic conductive film winding comprising a tape-shaped base material and an adhesive layer provided on one surface thereof, and containing at least a latent curing agent and a monomer which are activated by irradiation with ultraviolet rays.