JP2019536847A - アルジミン含有ガラス接合プライマー - Google Patents

アルジミン含有ガラス接合プライマー Download PDF

Info

Publication number
JP2019536847A
JP2019536847A JP2019520414A JP2019520414A JP2019536847A JP 2019536847 A JP2019536847 A JP 2019536847A JP 2019520414 A JP2019520414 A JP 2019520414A JP 2019520414 A JP2019520414 A JP 2019520414A JP 2019536847 A JP2019536847 A JP 2019536847A
Authority
JP
Japan
Prior art keywords
primer
primer composition
aldimine
composition according
primers
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP2019520414A
Other languages
English (en)
Other versions
JP7053599B2 (ja
Inventor
ニランジャン・マルヴァドカー
ダニエル・ピー・ソフィーア
ジェイミー・エム・ウェイシューン
Original Assignee
ダウ グローバル テクノロジーズ エルエルシー
ダウ グローバル テクノロジーズ エルエルシー
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ダウ グローバル テクノロジーズ エルエルシー, ダウ グローバル テクノロジーズ エルエルシー filed Critical ダウ グローバル テクノロジーズ エルエルシー
Publication of JP2019536847A publication Critical patent/JP2019536847A/ja
Application granted granted Critical
Publication of JP7053599B2 publication Critical patent/JP7053599B2/ja
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

新規なプライマー組成物は、アルジミン及び/又はエポキシ樹脂を含有し、このようなプライマーを作製するプロセスは、ガラス接合接着剤キットに使用される。

Description

本発明は、自動車関連用途、特にガラス接合用途において特有の特性を有する新しいプライマー組成物又は「プライマー」に関する。
典型的なガラス接合接着剤キットは、プライマー組成物及び湿気硬化型ウレタン接着剤を含む。ガラス接合プライマーは、典型的には、有機溶媒、有機シラン中間体、イソシアネートプレポリマー、フィルム形成剤、カーボンブラック、触媒及び安定剤を含有する。プライマーは、湿気硬化型ウレタン接着剤との良好な接合を可能にするためにガラスの表面を改質する。プライマー中のイソシアネートは、湿気硬化を受けて架橋熱硬化性ネットワークを生成し、これは、プライマーを周囲条件下で十分な耐久性を有するのに十分に堅牢にする。しかしながら、プライマーは、高温多湿条件を維持するのに十分な架橋密度を有さなければならない。これらの条件下において、前述の成分を含有する従来のプライマーは、架橋密度を失う傾向があり、これによりガラス表面から剥離する。従って、これは、高温多湿条件下でも十分な架橋密度を有するように新しいプライマーを開発するという要求である。
本発明の一態様では、本発明は、潜在的架橋剤として作用して改善された加水分解安定性をもたらす1つ以上のアルジミンを含有する新しいプライマーを提供する。本発明の別の態様では、これらの新しいプライマーは、カーボンブラックを含有しないか又は実質的に含まず、その耐久性を改善するための補強としてガラス接合プライマーに典型的に添加される。しかしながら、プライマーへのカーボンブラックの組み込みは、非常に時間及びエネルギーを消費する別の粉砕工程を必要とする。従って、カーボンブラックを除去することにより、製造の複雑さが簡素化され、全体的な費用が削減される。
本発明のプライマーは、典型的には、以下を含有する。
A)15〜45重量%、好ましくは20〜40重量%、より好ましくは25〜35重量%のアセトン及び/又はメチルエチルケトンなどの有機溶媒;
B)2〜10重量%、好ましくは2.5〜8重量%、より好ましくは3〜7重量%のジアルジミンなどのアルジミン;
C)2〜17重量%、好ましくは3〜15重量%、より好ましくは4〜12重量%のアルコキシシラン中間体、これは、その全体が参照により本明細書に組み込まれる米国特許第5,852,137号明細書において付加物としても知られ、これは、γ−メルカプトプロピルトリメトキシシランとヘキサメチレンジイソシアネート(HDI)ビウレットとの反応生成物であり、中間体の化学的性質及び製造は、米国特許第5,852,137号明細書、特に5列25行〜7列15行及び実施例に十分に記載及び教示されている。本発明で使用されるアルコキシシラン中間体は、同様にその全体が参照により本明細書に組み込まれる米国特許第5,238,993号明細書にも教示されており、米国特許第5,238,993号明細書の実施例1として開示されている;
D)0〜10重量%、好ましくは4〜8重量%、より好ましくは5〜7重量%のビスフェノールAのジグリシジルエーテル、D.E.R.(商標)332などのエポキシ樹脂;
E)15〜35重量%、好ましくは20〜33重量%、より好ましくは23〜30重量%のVITEL(登録商標)2301 BU(メチルエチルケトン中の40重量%溶液)などの非反応性フィルム形成樹脂;
F)18〜30重量%、好ましくは20〜28重量%、より好ましくは22〜26重量%の、Desmodur(登録商標)RFE、Desmodur(登録商標)HL及びPAPI(商標)20などの脂肪族及び芳香族ポリイソシアネートプレポリマー;
G)1〜3重量%、好ましくは1.5〜2.5重量%、より好ましくは2〜2.2重量%のオキサゾリジン含有化合物PARALOID(商標)QM−1007などの反応性改質剤;
H)0.1〜0.3重量%、好ましくは0.15〜0.25重量%、より好ましくは0.2〜0.22重量%のKKAT(登録商標)670などの触媒;及び
I)0.2〜0.5%、好ましくは0.25〜0.4重量%、より好ましくは0.3〜0.35重量%のマロン酸ジエチルなどのイソシアネート安定剤。
前述のように、本発明の全てのプライマーに対する特有の成分は、プライマーにおける1つ以上のアルジミンの使用である。アルジミンは、アルデヒドを第1級アミンと反応させてイミン官能基を形成することによって調製されるシッフ塩基である。アルジミンは、水分の存在下で加水分解を受けてアルデヒド及びアミンを放出する。次いで、この加水分解反応から放出されたアミンは、イソシアネート基又はエポキシ基と反応してプライマー被覆の架橋密度を増加させることができる。更に、アルジミンはまた、プライマーを安定化させることを促進し、プライマーの貯蔵寿命を延ばす。好ましい実施形態では、プライマーに使用されるアルジミンは、ジアルジミンである。
アルジミンに加えて、アミンとも反応することができるエポキシ樹脂も更なる靭性、耐久性及び防湿性を付与するためにプライマーに添加され得る。ビスフェノールAジグリシジルエーテルなどのエポキシ樹脂は、アミンで硬化したときに優れたバリヤー特性を与える。結果として、プライマーの加水分解安定性は、エポキシ樹脂が添加されたときに非常に改善される。エポキシ樹脂を含有するプライマーは、90℃の水に10日間浸漬した後の膨れに対する感受性が低い。ヒドロキシルがあるエポキシ樹脂は、プライマー組成物中にあるイソシアネートとの反応を引き起し、ゲル化をもたらす場合があることに留意することが重要である。従って、いかなるヒドロキシル官能基も有さないエポキシ樹脂を選択することが重要である。好ましい実施形態では、Olin Corporationから市販されているエポキシ樹脂DER 332をプライマー組成物に使用する。
プライマー中のアルジミン及びエポキシの存在は、プライマーのガラス接合強度を増大させ、また加水分解安定性を改良する。更に、本発明のプライマーを使用する、自動車用途に従来使用されている湿気硬化型ウレタン接着剤との結合速度は、従来のブラックミルド(black milled)プライマーのものと非常に類似している。しかしながら、いくつかの好ましい実施形態では、これらの新しいプライマーは、カーボンブラックを含有しないため、製造コストは、従来のブラックプライマーと比較して著しく低い。
以下の非限定的な実施例によって本発明を更に実証することができる。
表1は、本発明を実証するために実施例を作成するのに使用された様々な原料成分及びそれらの供給源を示す。
Figure 2019536847
表2は、本発明を実証するために調製された様々な実施例を要約した。実施例1〜6は、アルジミンを含有する本発明の試料であり、実施例7〜10は、アルジミンを含有しない比較試料である。
Figure 2019536847
更に、2つの市販のブラックプライマーも比較例として使用した。第1のプライマー、実施例11は、Dow Chemical Companyから市販されている、BETASEAL(商標)43520Aとして知られている市販の2段階ガラス接合プライマーであり、これは、カーボンブラックを含有するが、アルジミン又はエポキシ樹脂を含有しない。このプライマーは、溶媒系シランブレンドであるDow Chemical Companyから市販されているBETASEAL(商標)43518と併せて使用しなければならない。ガラス接合中、最初にBETASEAL(商標)43518をガラス面に塗布してガラス表面を調整する。次いで、BETASEAL(商標)43520Aを調整済みのガラス表面に塗布する。
別の比較用プライマーの例、実施例12は、同じくDow Chemical Companyから入手可能なBETAPRIME(商標)5504Gとして知られる市販の1段階プライマーであり、これは、カーボンブラックを含有するが、アルジミン又はエポキシ樹脂を含有しない。プライマーは、ガラス表面に直接塗布される。
全ての試料を以下の方法で調製した。本発明のガラス接合用プライマーは、2段階プロセスを用いて調製した。第1段階において、成分Cは、Desmodur(登録商標)N100(脂肪族ヘキサメチレンジイソシアネート系ポリイソシアネート)及びSILQUEST(登録商標)A189(γ−メルカプトプロピルトリメトキシシラン)とメチルエチルケトンとを組み合わせることによって調製して、70%固形分溶液を得た。Desmodur(登録商標)N100及びSILQUEST(登録商標)A189を添加して、3:1当量のイソシアネート及びメルカプト基を得た。次いで、FASCAT 4202(ジブチルスズジラウレート)触媒をブレンド物に添加した。全てのメルカプト基が消費されるまで溶液を60℃において反応容器中で反応させた。得られた反応生成物は、オルガノシラン中間体(表1の成分C)である。次に、表1に示した残りの成分をアルミニウム容器に添加した。オルガノシラン中間体を触媒(成分H)と共に添加した。次いで、成分を、舌圧子を用いて撹拌した。
比較例(実施例7〜10)を、アルジミンを添加せずに同様に調製した。
両方の種類の実施例のプライマーを使用して、3インチ×5インチのガラス基板上のプライマーの接着性能を検討した。プライマーを塗布する前にガラス基板をアセトン及びイソプロパノールで洗浄した。プライマーは、1ミルのドローダウンバーを用いて塗布した。プライマーを周囲条件下で必要な時間にわたって硬化させた。
本発明のプライマーの性能を、以下の試験方法を用いて評価した。
引っ掻き接着試験:接着試験は、直径1mmの半球状ステンレス鋼スクラッチヘッドを使用してガラス基板上にプライマーを被覆することによって実施した。プライマーを24時間硬化させた後、このスクラッチヘッドを用いてプライマー表面に引っ掻き傷を付けた。各試験について、常用荷重を200〜1000gで変動させることにより、8つの引っ掻き傷の組を付けた。ガラス表面からプライマーを除去するのに必要とされる最小の力は、プライマーとガラスとの間の接着力として報告した。
貯蔵安定性試験:アルミニウムボトルに保存した新たに調製したプライマーを54℃のオーブンに3日間入れた。3日後、ボトルをオーブンから取り出した。ゲル化したプライマーは、貯蔵安定性試験に合格しないが、ゲル化しないプライマーは、貯蔵安定性試験に合格する。
加水分解安定性試験:プライマーで被覆されたガラスを周囲条件下で7日間硬化させた。次いで、プライマーで被覆されたガラスを90℃の水浴中に10日間浸漬した。10日後、プライマーで被覆されたガラスを水浴から取り出し、4時間風乾した。最後に、このプライマーについて引っ掻き接着試験を行い、基材からプライマーを除去するのに必要とされる最小接着力を記録した。
クイックナイフ試験(SAE J1720):6.3mm(幅)×6.3mm(高さ)×100mm(長さ)の接着剤のビードを、プライマーで被覆された基材上に置いた。接着剤を23℃及び50%相対湿度の条件下で24時間硬化させた。次いで、硬化したビードを、180°の角度でビードの端部を引き戻しながら、45°の角度で基板までカミソリの刃で切断した。基板上において3mm毎にノッチを切った。接着破壊は、凝集破壊(CF)、即ち接着剤内で起こる接着破壊を1とし、プライマーに対する接着破壊(AFP)、即ちプライマー接着界面での破壊を2とし、ガラスへのプライマー破壊(PFG)、即ちプライマーガラス界面での破壊を3とした。
重ね剪断試験:プライマー試料を板ガラス上に被覆し、1時間乾燥させた。The Dow Chemical Companyから市販されているBETASEAL Expressの接着剤ビードを乾燥したプライマーに塗布した。次に、電着クーポンを重ね、アセンブリのビード上に置いた。重ね剪断試験前に接着剤を24時間硬化させた。2つの基板を5インチ/分の速度で引っ張ることによって重ね剪断を行った。2つの基板を引き離すために必要とされるピーク力及び接着破壊モードを記録した。
前述の全ての性能試験の結果を表3に要約する。
Figure 2019536847
表3は、本発明のプライマーの実施例及び比較例の性能を示す。実施例13を除く全てのプライマーは、24時間硬化後にガラス表面に対して良好な接着性を示した。これらのプライマーについての接着力の値は、機器の最大測定可能値(即ち1000g)を超える。比較すると、実施例13のプライマーは、比較的低い乾燥接着値(600g)を有し、これは、プライマーの遅い硬化速度論に起因し得る。
90℃の水に浸漬して10日後に行われた引っ掻き接着試験は、プライマーの加水分解安定性を実証する。90℃の水に浸漬して10日後の接着力の値を表3に示す。
本発明のプライマーが比較例よりもはるかに良好に機能することは明らかに確かである。エポキシ樹脂とアルジミンとの両方がプライマーの加水分解安定性を高めるために必要とされる。実施例1、2、3、4及び5のプライマーは、エポキシとアルジミンとの両方を含有し、プライマーを90℃の水に10日間浸漬した後に実施した引っ掻き試験で見られるように優れた加水分解安定性をもたらした。更に、アセンブリを90℃の水に10日間浸漬した後に行われた重ね剪断試験は、より良好な重ね剪断性能を得るためにアルジミンとエポキシとの両方の存在が必要であることを示している。アルジミンを含有するが、エポキシ樹脂を含有しない実施例6のプライマーは、引っ掻き試験から明らかなように室温で優れた接着性を示す。しかしながら、このプライマーの加水分解安定性は、実施例1〜5のプライマーと比較して僅かに低い。更に、このプライマーは、実施例1〜5のプライマーと比較してより重度の膨れを示す。エポキシとアルジミンとの両方が存在しない場合、プライマーは、より低い加水分解安定性を有する(実施例6、7、10及び11)。
更に、アルジミンは、プライマーを安定化させることを促進し、従ってプライマーの貯蔵安定性を高める。また、貯蔵安定性は、使用される触媒に依存する。実施例1、2及び3で使用されるように、Fomrez UL 28などのスズ触媒の場合、プライマーは、54℃ゲル試験に合格せず、より短い貯蔵寿命を示す。比較すると、実施例4及び5で使用されているように、KKAT 670などの非スズ触媒を含有するプライマーは、54℃ゲル試験に合格する可能性がより高い。しかしながら、たとえプライマーが触媒としてKKAT 670を含有するとしても、アルジミンが組成物中に存在しない場合、依然としてゲル試験に不合格となり得る。これは。実施例9及び10において明らかである。これらのプライマーの両方は、アルジミンを含有しないため、ゲル試験に不合格である。
湿気硬化型ウレタン接着剤との結合速度を評価するために、クイックナイフ試験を実施した。全てのプライマーは、7日間の接着剤硬化後のウレタン接着剤としてのBETASEAL Expressとの優れた結合時間(100%凝集破壊)を示す。アルジミン及び/又はエポキシの存在は、接着剤に対するプライマーの結合速度を損なわない。
また、本発明の好ましい態様では、プライマーは、ポリエーテルアミン(例えば、Huntsmanから市販されているJEFFAMINE D400)とベンズアルデヒドとの反応生成物であるIncozel BH(Incorezから市販されている)などのジアルジミンを含有する。

Claims (10)

  1. プライマー組成物であって、前記組成物の総重量に基づいて、有機溶媒と、アルジミンと、アルコキシシランと、非反応性フィルム形成樹脂と、ポリイソシアネートプレポリマーと、反応性改質剤と、触媒と、イソシアネート安定剤とを含むプライマー組成物。
  2. 10重量%未満のエポキシ樹脂を更に含む、請求項1に記載のプライマー組成物。
  3. 前記エポキシ樹脂は、ビスフェノールAのジグリシジルエーテルである、請求項2に記載のプライマー組成物。
  4. カーボンブラックを実質的に含まないことを含む、請求項1に記載のプライマー組成物。
  5. 請求項1に記載のプライマー組成物は、カーボンブラックを含まない。
  6. 前記有機溶媒は、アセトン、メチルエチルケトン及びそれらの混合物の1つを含み、前記反応性改質剤は、オキサゾリジン含有化合物である、請求項1に記載のプライマー組成物。
  7. 前記イソシアネート安定剤は、マロン酸ジエチルを含む、請求項1に記載のプライマー組成物。
  8. 前記アルジミンは、ジアルジミンである、請求項1に記載のプライマー組成物。
  9. 前記アルジミンは、ポリエーテルアミンとベンズアルデヒドとの反応である、請求項8に記載のプライマー組成物。
  10. アルコキシシランは、γ−メルカプトプロピルトリメトキシシランとヘキサメチレンジイソシアネート(HDI)ビウレットとの反応生成物である、請求項1に記載のプライマー組成物。
JP2019520414A 2016-10-18 2017-10-02 アルジミン含有ガラス接合プライマー Active JP7053599B2 (ja)