- polarizing film
- film
- shape
- adhesive layer
- notch
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Links
- 239000012790 adhesive layer Substances 0.000 title claims abstract description 35
- 230000001681 protective effect Effects 0.000 claims abstract description 65
- 230000035939 shock Effects 0.000 abstract description 17
- 230000001788 irregular Effects 0.000 abstract description 5
- 239000010408 film Substances 0.000 description 190
- 239000010410 layer Substances 0.000 description 56
- 230000001070 adhesive effect Effects 0.000 description 45
- 239000000853 adhesive Substances 0.000 description 43
- 239000004820 Pressure-sensitive adhesive Substances 0.000 description 35
- 229920000642 polymer Polymers 0.000 description 27
- 229920002451 polyvinyl alcohol Polymers 0.000 description 21
- 239000004372 Polyvinyl alcohol Substances 0.000 description 20
- NLKNQRATVPKPDG-UHFFFAOYSA-M potassium iodide Chemical compound [K+].[I-] NLKNQRATVPKPDG-UHFFFAOYSA-M 0.000 description 18
- 238000000034 method Methods 0.000 description 17
- 229920005989 resin Polymers 0.000 description 16
- 239000011347 resin Substances 0.000 description 16
- -1 polyethylene terephthalate Polymers 0.000 description 15
- KGBXLFKZBHKPEV-UHFFFAOYSA-N boric acid Chemical compound OB(O)O KGBXLFKZBHKPEV-UHFFFAOYSA-N 0.000 description 14
- 229960002645 boric acid Drugs 0.000 description 14
- 235000010338 boric acid Nutrition 0.000 description 14
- 239000004327 boric acid Substances 0.000 description 14
- XLYOFNOQVPJJNP-UHFFFAOYSA-N water Substances O XLYOFNOQVPJJNP-UHFFFAOYSA-N 0.000 description 14
- 239000007864 aqueous solution Substances 0.000 description 13
- 238000004519 manufacturing process Methods 0.000 description 12
- 239000000463 material Substances 0.000 description 11
- 238000001035 drying Methods 0.000 description 10
- 238000004043 dyeing Methods 0.000 description 10
- 239000004973 liquid crystal related substance Substances 0.000 description 10
- 230000035882 stress Effects 0.000 description 9
- ZCYVEMRRCGMTRW-UHFFFAOYSA-N 7553-56-2 Chemical compound [I] ZCYVEMRRCGMTRW-UHFFFAOYSA-N 0.000 description 8
- 229910052740 iodine Inorganic materials 0.000 description 8
- 239000011630 iodine Substances 0.000 description 8
- 230000000052 comparative effect Effects 0.000 description 7
- 230000008602 contraction Effects 0.000 description 7
- 229920000139 polyethylene terephthalate Polymers 0.000 description 7
- 239000005020 polyethylene terephthalate Substances 0.000 description 7
- 239000008188 pellet Substances 0.000 description 6
- 229920001296 polysiloxane Polymers 0.000 description 6
- 239000002585 base Substances 0.000 description 5
- 210000004027 cell Anatomy 0.000 description 5
- 238000000576 coating method Methods 0.000 description 5
- 239000007788 liquid Substances 0.000 description 5
- 238000002156 mixing Methods 0.000 description 5
- 230000003287 optical effect Effects 0.000 description 5
- 238000006116 polymerization reaction Methods 0.000 description 5
- 238000012545 processing Methods 0.000 description 5
- 239000002904 solvent Substances 0.000 description 5
- 239000000758 substrate Substances 0.000 description 5
- YCKRFDGAMUMZLT-UHFFFAOYSA-N Fluorine atom Chemical compound [F] YCKRFDGAMUMZLT-UHFFFAOYSA-N 0.000 description 4
- NTIZESTWPVYFNL-UHFFFAOYSA-N Methyl isobutyl ketone Chemical compound CC(C)CC(C)=O NTIZESTWPVYFNL-UHFFFAOYSA-N 0.000 description 4
- 229920001893 acrylonitrile styrene Polymers 0.000 description 4
- 239000011248 coating agent Substances 0.000 description 4
- 239000011737 fluorine Substances 0.000 description 4
- 229910052731 fluorine Inorganic materials 0.000 description 4
- 238000010030 laminating Methods 0.000 description 4
- 239000000203 mixture Substances 0.000 description 4
- 229920006255 plastic film Polymers 0.000 description 4
- 239000002985 plastic film Substances 0.000 description 4
- 229920000728 polyester Polymers 0.000 description 4
- SCUZVMOVTVSBLE-UHFFFAOYSA-N prop-2-enenitrile;styrene Chemical compound C=CC#N.C=CC1=CC=CC=C1 SCUZVMOVTVSBLE-UHFFFAOYSA-N 0.000 description 4
- 239000000243 solution Substances 0.000 description 4
- 239000000126 substance Substances 0.000 description 4
- 239000004698 Polyethylene Substances 0.000 description 3
- 239000004743 Polypropylene Substances 0.000 description 3
- PPBRXRYQALVLMV-UHFFFAOYSA-N Styrene Chemical compound C=CC1=CC=CC=C1 PPBRXRYQALVLMV-UHFFFAOYSA-N 0.000 description 3
- 238000010521 absorption reaction Methods 0.000 description 3
- NIXOWILDQLNWCW-UHFFFAOYSA-N acrylic acid group Chemical group C(C=C)(=O)O NIXOWILDQLNWCW-UHFFFAOYSA-N 0.000 description 3
- 239000000654 additive Substances 0.000 description 3
- 125000000217 alkyl group Chemical group 0.000 description 3
- 239000003795 chemical substances by application Substances 0.000 description 3
- 239000012141 concentrate Substances 0.000 description 3
- 238000013461 design Methods 0.000 description 3
- 238000009792 diffusion process Methods 0.000 description 3
- 238000010438 heat treatment Methods 0.000 description 3
- 150000002596 lactones Chemical group 0.000 description 3
- 239000002346 layers by function Substances 0.000 description 3
- 239000012788 optical film Substances 0.000 description 3
- 229920000058 polyacrylate Polymers 0.000 description 3
- 229920000573 polyethylene Polymers 0.000 description 3
- 229920001155 polypropylene Polymers 0.000 description 3
- 238000002360 preparation method Methods 0.000 description 3
- 230000008569 process Effects 0.000 description 3
- 238000005406 washing Methods 0.000 description 3
- KDGNCLDCOVTOCS-UHFFFAOYSA-N (2-methylpropan-2-yl)oxy propan-2-yl carbonate Chemical compound CC(C)OC(=O)OOC(C)(C)C KDGNCLDCOVTOCS-UHFFFAOYSA-N 0.000 description 2
- XLPJNCYCZORXHG-UHFFFAOYSA-N 1-morpholin-4-ylprop-2-en-1-one Chemical compound C=CC(=O)N1CCOCC1 XLPJNCYCZORXHG-UHFFFAOYSA-N 0.000 description 2
- IJGRMHOSHXDMSA-UHFFFAOYSA-N Atomic nitrogen Chemical compound N#N IJGRMHOSHXDMSA-UHFFFAOYSA-N 0.000 description 2
- UIHCLUNTQKBZGK-UHFFFAOYSA-N Methyl isobutyl ketone Natural products CCC(C)C(C)=O UIHCLUNTQKBZGK-UHFFFAOYSA-N 0.000 description 2
- 239000004952 Polyamide Substances 0.000 description 2
- 239000004721 Polyphenylene oxide Substances 0.000 description 2
- VYPSYNLAJGMNEJ-UHFFFAOYSA-N Silicium dioxide Chemical compound O=[Si]=O VYPSYNLAJGMNEJ-UHFFFAOYSA-N 0.000 description 2
- BZHJMEDXRYGGRV-UHFFFAOYSA-N Vinyl chloride Chemical compound ClC=C BZHJMEDXRYGGRV-UHFFFAOYSA-N 0.000 description 2
- 239000003963 antioxidant agent Substances 0.000 description 2
- 229920005601 base polymer Polymers 0.000 description 2
- 238000006482 condensation reaction Methods 0.000 description 2
- 238000004132 cross linking Methods 0.000 description 2
- 210000002858 crystal cell Anatomy 0.000 description 2
- 229920001971 elastomer Polymers 0.000 description 2
- 239000005038 ethylene vinyl acetate Substances 0.000 description 2
- 239000011521 glass Substances 0.000 description 2
- 230000009477 glass transition Effects 0.000 description 2
- PNDPGZBMCMUPRI-UHFFFAOYSA-N iodine Chemical compound II PNDPGZBMCMUPRI-UHFFFAOYSA-N 0.000 description 2
- QQVIHTHCMHWDBS-UHFFFAOYSA-N isophthalic acid Chemical compound OC(=O)C1=CC=CC(C(O)=O)=C1 QQVIHTHCMHWDBS-UHFFFAOYSA-N 0.000 description 2
- 238000004898 kneading Methods 0.000 description 2
- 229910052751 metal Inorganic materials 0.000 description 2
- 239000002184 metal Substances 0.000 description 2
- 238000003801 milling Methods 0.000 description 2
- UUORTJUPDJJXST-UHFFFAOYSA-N n-(2-hydroxyethyl)prop-2-enamide Chemical compound OCCNC(=O)C=C UUORTJUPDJJXST-UHFFFAOYSA-N 0.000 description 2
- 230000002093 peripheral effect Effects 0.000 description 2
- 229920001200 poly(ethylene-vinyl acetate) Polymers 0.000 description 2
- 229920002647 polyamide Polymers 0.000 description 2
- 239000004417 polycarbonate Substances 0.000 description 2
- 229920000515 polycarbonate Polymers 0.000 description 2
- 229920001225 polyester resin Polymers 0.000 description 2
- 239000004645 polyester resin Substances 0.000 description 2
- 229920000570 polyether Polymers 0.000 description 2
- 229920006393 polyether sulfone Polymers 0.000 description 2
- 229920001721 polyimide Polymers 0.000 description 2
- 229920000098 polyolefin Polymers 0.000 description 2
- 229920002635 polyurethane Polymers 0.000 description 2
- 239000004814 polyurethane Substances 0.000 description 2
- 239000004800 polyvinyl chloride Substances 0.000 description 2
- 229920000915 polyvinyl chloride Polymers 0.000 description 2
- 238000010992 reflux Methods 0.000 description 2
- 239000005060 rubber Substances 0.000 description 2
- 238000007127 saponification reaction Methods 0.000 description 2
- 238000012360 testing method Methods 0.000 description 2
- 238000002834 transmittance Methods 0.000 description 2
- 239000006097 ultraviolet radiation absorber Substances 0.000 description 2
- JIAARYAFYJHUJI-UHFFFAOYSA-L zinc dichloride Chemical compound [Cl-].[Cl-].[Zn+2] JIAARYAFYJHUJI-UHFFFAOYSA-L 0.000 description 2
- RNFJDJUURJAICM-UHFFFAOYSA-N 2,2,4,4,6,6-hexaphenoxy-1,3,5-triaza-2$l^{5},4$l^{5},6$l^{5}-triphosphacyclohexa-1,3,5-triene Chemical compound N=1P(OC=2C=CC=CC=2)(OC=2C=CC=CC=2)=NP(OC=2C=CC=CC=2)(OC=2C=CC=CC=2)=NP=1(OC=1C=CC=CC=1)OC1=CC=CC=C1 RNFJDJUURJAICM-UHFFFAOYSA-N 0.000 description 1
- OEPOKWHJYJXUGD-UHFFFAOYSA-N 2-(3-phenylmethoxyphenyl)-1,3-thiazole-4-carbaldehyde Chemical compound O=CC1=CSC(C=2C=C(OCC=3C=CC=CC=3)C=CC=2)=N1 OEPOKWHJYJXUGD-UHFFFAOYSA-N 0.000 description 1
- CBECDWUDYQOTSW-UHFFFAOYSA-N 2-ethylbut-3-enal Chemical compound CCC(C=C)C=O CBECDWUDYQOTSW-UHFFFAOYSA-N 0.000 description 1
- OLSDAJRAVOVKLG-UHFFFAOYSA-N 3-hydroxymandelic acid Chemical compound OC(=O)C(O)C1=CC=CC(O)=C1 OLSDAJRAVOVKLG-UHFFFAOYSA-N 0.000 description 1
- QTBSBXVTEAMEQO-UHFFFAOYSA-M Acetate Chemical compound CC([O-])=O QTBSBXVTEAMEQO-UHFFFAOYSA-M 0.000 description 1
- 239000004925 Acrylic resin Substances 0.000 description 1
- 229920000178 Acrylic resin Polymers 0.000 description 1
- 229920002284 Cellulose triacetate Polymers 0.000 description 1
- 239000004593 Epoxy Substances 0.000 description 1
- LFQSCWFLJHTTHZ-UHFFFAOYSA-N Ethanol Chemical compound CCO LFQSCWFLJHTTHZ-UHFFFAOYSA-N 0.000 description 1
- JOYRKODLDBILNP-UHFFFAOYSA-N Ethyl urethane Chemical compound CCOC(N)=O JOYRKODLDBILNP-UHFFFAOYSA-N 0.000 description 1
- 108010010803 Gelatin Proteins 0.000 description 1
- VVQNEPGJFQJSBK-UHFFFAOYSA-N Methyl methacrylate Chemical compound COC(=O)C(C)=C VVQNEPGJFQJSBK-UHFFFAOYSA-N 0.000 description 1
- 239000004677 Nylon Substances 0.000 description 1
- 239000004696 Poly ether ether ketone Substances 0.000 description 1
- 239000005062 Polybutadiene Substances 0.000 description 1
- 239000004695 Polyether sulfone Substances 0.000 description 1
- 239000004642 Polyimide Substances 0.000 description 1
- 239000004734 Polyphenylene sulfide Substances 0.000 description 1
- 239000004793 Polystyrene Substances 0.000 description 1
- NNLVGZFZQQXQNW-ADJNRHBOSA-N [(2r,3r,4s,5r,6s)-4,5-diacetyloxy-3-[(2s,3r,4s,5r,6r)-3,4,5-triacetyloxy-6-(acetyloxymethyl)oxan-2-yl]oxy-6-[(2r,3r,4s,5r,6s)-4,5,6-triacetyloxy-2-(acetyloxymethyl)oxan-3-yl]oxyoxan-2-yl]methyl acetate Chemical compound O([C@@H]1O[C@@H]([C@H]([C@H](OC(C)=O)[C@H]1OC(C)=O)O[C@H]1[C@@H]([C@@H](OC(C)=O)[C@H](OC(C)=O)[C@@H](COC(C)=O)O1)OC(C)=O)COC(=O)C)[C@@H]1[C@@H](COC(C)=O)O[C@@H](OC(C)=O)[C@H](OC(C)=O)[C@H]1OC(C)=O NNLVGZFZQQXQNW-ADJNRHBOSA-N 0.000 description 1
- 239000006096 absorbing agent Substances 0.000 description 1
- 125000002339 acetoacetyl group Chemical group O=C([*])C([H])([H])C(=O)C([H])([H])[H] 0.000 description 1
- BAPJBEWLBFYGME-UHFFFAOYSA-N acrylic acid methyl ester Natural products COC(=O)C=C BAPJBEWLBFYGME-UHFFFAOYSA-N 0.000 description 1
- 230000032683 aging Effects 0.000 description 1
- 125000003158 alcohol group Chemical group 0.000 description 1
- 239000003513 alkali Substances 0.000 description 1
- 150000001408 amides Chemical class 0.000 description 1
- 230000003373 anti-fouling effect Effects 0.000 description 1
- 230000003078 antioxidant effect Effects 0.000 description 1
- 239000002216 antistatic agent Substances 0.000 description 1
- 239000004760 aramid Substances 0.000 description 1
- 229920003235 aromatic polyamide Polymers 0.000 description 1
- 230000004888 barrier function Effects 0.000 description 1
- 230000015572 biosynthetic process Effects 0.000 description 1
- 239000002981 blocking agent Substances 0.000 description 1
- 239000001913 cellulose Substances 0.000 description 1
- 229920002678 cellulose Polymers 0.000 description 1
- 239000012461 cellulose resin Substances 0.000 description 1
- 230000008859 change Effects 0.000 description 1
- 239000003086 colorant Substances 0.000 description 1
- 238000004040 coloring Methods 0.000 description 1
- 150000001875 compounds Chemical class 0.000 description 1
- 239000000470 constituent Substances 0.000 description 1
- 229920001577 copolymer Polymers 0.000 description 1
- 238000003851 corona treatment Methods 0.000 description 1
- 229920005994 diacetyl cellulose Polymers 0.000 description 1
- 235000014113 dietary fatty acids Nutrition 0.000 description 1
- FRXGWNKDEMTFPL-UHFFFAOYSA-N dioctadecyl hydrogen phosphate Chemical compound CCCCCCCCCCCCCCCCCCOP(O)(=O)OCCCCCCCCCCCCCCCCCC FRXGWNKDEMTFPL-UHFFFAOYSA-N 0.000 description 1
- 238000007598 dipping method Methods 0.000 description 1
- WNAHIZMDSQCWRP-UHFFFAOYSA-N dodecane-1-thiol Chemical compound CCCCCCCCCCCCS WNAHIZMDSQCWRP-UHFFFAOYSA-N 0.000 description 1
- 230000000694 effects Effects 0.000 description 1
- 238000010894 electron beam technology Methods 0.000 description 1
- RTZKZFJDLAIYFH-UHFFFAOYSA-N ether Substances CCOCC RTZKZFJDLAIYFH-UHFFFAOYSA-N 0.000 description 1
- 238000011156 evaluation Methods 0.000 description 1
- 238000001704 evaporation Methods 0.000 description 1
- 230000008020 evaporation Effects 0.000 description 1
- 230000001747 exhibiting effect Effects 0.000 description 1
- 238000001125 extrusion Methods 0.000 description 1
- 238000007765 extrusion coating Methods 0.000 description 1
- 239000004744 fabric Substances 0.000 description 1
- 239000000194 fatty acid Substances 0.000 description 1
- 229930195729 fatty acid Natural products 0.000 description 1
- 150000004665 fatty acids Chemical class 0.000 description 1
- 239000003063 flame retardant Substances 0.000 description 1
- 239000011888 foil Substances 0.000 description 1
- 238000010528 free radical solution polymerization reaction Methods 0.000 description 1
- 229920000159 gelatin Polymers 0.000 description 1
- 239000008273 gelatin Substances 0.000 description 1
- 235000019322 gelatine Nutrition 0.000 description 1
- 235000011852 gelatine desserts Nutrition 0.000 description 1
- 239000012760 heat stabilizer Substances 0.000 description 1
- 239000012943 hotmelt Substances 0.000 description 1
- 229920001477 hydrophilic polymer Polymers 0.000 description 1
- 150000003949 imides Chemical class 0.000 description 1
- 238000007654 immersion Methods 0.000 description 1
- 239000003112 inhibitor Substances 0.000 description 1
- 239000003999 initiator Substances 0.000 description 1
- 230000001678 irradiating effect Effects 0.000 description 1
- 239000012948 isocyanate Substances 0.000 description 1
- 150000002513 isocyanates Chemical class 0.000 description 1
- 239000004816 latex Substances 0.000 description 1
- 229920000126 latex Polymers 0.000 description 1
- 239000000314 lubricant Substances 0.000 description 1
- 239000000155 melt Substances 0.000 description 1
- 230000004048 modification Effects 0.000 description 1
- 238000012986 modification Methods 0.000 description 1
- JTHNLKXLWOXOQK-UHFFFAOYSA-N n-propyl vinyl ketone Natural products CCCC(=O)C=C JTHNLKXLWOXOQK-UHFFFAOYSA-N 0.000 description 1
- 229910052757 nitrogen Inorganic materials 0.000 description 1
- 239000004745 nonwoven fabric Substances 0.000 description 1
- 125000003518 norbornenyl group Chemical group C12(C=CC(CC1)C2)* 0.000 description 1
- 239000002667 nucleating agent Substances 0.000 description 1
- 229920001778 nylon Polymers 0.000 description 1
- UHGIMQLJWRAPLT-UHFFFAOYSA-N octadecyl dihydrogen phosphate Chemical compound CCCCCCCCCCCCCCCCCCOP(O)(O)=O UHGIMQLJWRAPLT-UHFFFAOYSA-N 0.000 description 1
- 239000000123 paper Substances 0.000 description 1
- 239000000049 pigment Substances 0.000 description 1
- 239000004014 plasticizer Substances 0.000 description 1
- 230000010287 polarization Effects 0.000 description 1
- 229920003207 poly(ethylene-2,6-naphthalate) Polymers 0.000 description 1
- 229920003229 poly(methyl methacrylate) Polymers 0.000 description 1
- 229920002401 polyacrylamide Polymers 0.000 description 1
- 229920006122 polyamide resin Polymers 0.000 description 1
- 229920002857 polybutadiene Polymers 0.000 description 1
- 229920001083 polybutene Polymers 0.000 description 1
- 229920001707 polybutylene terephthalate Polymers 0.000 description 1
- 229920005668 polycarbonate resin Polymers 0.000 description 1
- 239000004431 polycarbonate resin Substances 0.000 description 1
- 150000004291 polyenes Chemical class 0.000 description 1
- 229920006267 polyester film Polymers 0.000 description 1
- 229920002530 polyetherether ketone Polymers 0.000 description 1
- 239000011112 polyethylene naphthalate Substances 0.000 description 1
- 239000009719 polyimide resin Substances 0.000 description 1
- 229920006254 polymer film Polymers 0.000 description 1
- 239000002952 polymeric resin Substances 0.000 description 1
- 239000004926 polymethyl methacrylate Substances 0.000 description 1
- 229920000306 polymethylpentene Polymers 0.000 description 1
- 239000011116 polymethylpentene Substances 0.000 description 1
- 229920005672 polyolefin resin Polymers 0.000 description 1
- 229920006324 polyoxymethylene Polymers 0.000 description 1
- 229920000069 polyphenylene sulfide Polymers 0.000 description 1
- 229920002223 polystyrene Polymers 0.000 description 1
- 229920006264 polyurethane film Polymers 0.000 description 1
- 229920000036 polyvinylpyrrolidone Polymers 0.000 description 1
- 239000001267 polyvinylpyrrolidone Substances 0.000 description 1
- 235000013855 polyvinylpyrrolidone Nutrition 0.000 description 1
- 239000011148 porous material Substances 0.000 description 1
- 239000000843 powder Substances 0.000 description 1
- 238000004080 punching Methods 0.000 description 1
- 238000007363 ring formation reaction Methods 0.000 description 1
- 239000000377 silicon dioxide Substances 0.000 description 1
- 229920005573 silicon-containing polymer Polymers 0.000 description 1
- 239000007787 solid Substances 0.000 description 1
- 239000007921 spray Substances 0.000 description 1
- 239000003381 stabilizer Substances 0.000 description 1
- 150000003457 sulfones Chemical class 0.000 description 1
- 230000008961 swelling Effects 0.000 description 1
- 229920003002 synthetic resin Polymers 0.000 description 1
- 229920005992 thermoplastic resin Polymers 0.000 description 1
- 125000000391 vinyl group Chemical group [H]C([*])=C([H])[H] 0.000 description 1
- 229920002554 vinyl polymer Polymers 0.000 description 1
- 239000011592 zinc chloride Substances 0.000 description 1
- 235000005074 zinc chloride Nutrition 0.000 description 1
- 229960001939 zinc chloride Drugs 0.000 description 1
- NWONKYPBYAMBJT-UHFFFAOYSA-L zinc sulfate Chemical compound [Zn+2].[O-]S([O-])(=O)=O NWONKYPBYAMBJT-UHFFFAOYSA-L 0.000 description 1
- 229960001763 zinc sulfate Drugs 0.000 description 1
- 229910000368 zinc sulfate Inorganic materials 0.000 description 1
Images
Classifications
-
- H—ELECTRICITY
- H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
- H10K—ORGANIC ELECTRIC SOLID-STATE DEVICES
- H10K59/00—Integrated devices, or assemblies of multiple devices, comprising at least one organic light-emitting element covered by group H10K50/00
- H10K59/80—Constructional details
- H10K59/8791—Arrangements for improving contrast, e.g. preventing reflection of ambient light
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
- C09J201/00—Adhesives based on unspecified macromolecular compounds
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
- C09J7/00—Adhesives in the form of films or foils
- C09J7/20—Adhesives in the form of films or foils characterised by their carriers
-
- G—PHYSICS
- G02—OPTICS
- G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
- G02B5/00—Optical elements other than lenses
- G02B5/30—Polarising elements
-
- G—PHYSICS
- G02—OPTICS
- G02F—OPTICAL DEVICES OR ARRANGEMENTS FOR THE CONTROL OF LIGHT BY MODIFICATION OF THE OPTICAL PROPERTIES OF THE MEDIA OF THE ELEMENTS INVOLVED THEREIN; NON-LINEAR OPTICS; FREQUENCY-CHANGING OF LIGHT; OPTICAL LOGIC ELEMENTS; OPTICAL ANALOGUE/DIGITAL CONVERTERS
- G02F1/00—Devices or arrangements for the control of the intensity, colour, phase, polarisation or direction of light arriving from an independent light source, e.g. switching, gating or modulating; Non-linear optics
- G02F1/01—Devices or arrangements for the control of the intensity, colour, phase, polarisation or direction of light arriving from an independent light source, e.g. switching, gating or modulating; Non-linear optics for the control of the intensity, phase, polarisation or colour
- G02F1/13—Devices or arrangements for the control of the intensity, colour, phase, polarisation or direction of light arriving from an independent light source, e.g. switching, gating or modulating; Non-linear optics for the control of the intensity, phase, polarisation or colour based on liquid crystals, e.g. single liquid crystal display cells
- G02F1/133—Constructional arrangements; Operation of liquid crystal cells; Circuit arrangements
- G02F1/1333—Constructional arrangements; Manufacturing methods
- G02F1/1335—Structural association of cells with optical devices, e.g. polarisers or reflectors
-
- G—PHYSICS
- G09—EDUCATION; CRYPTOGRAPHY; DISPLAY; ADVERTISING; SEALS
- G09F—DISPLAYING; ADVERTISING; SIGNS; LABELS OR NAME-PLATES; SEALS
- G09F9/00—Indicating arrangements for variable information in which the information is built-up on a support by selection or combination of individual elements
- G09F9/30—Indicating arrangements for variable information in which the information is built-up on a support by selection or combination of individual elements in which the desired character or characters are formed by combining individual elements
-
- H—ELECTRICITY
- H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
- H05B—ELECTRIC HEATING; ELECTRIC LIGHT SOURCES NOT OTHERWISE PROVIDED FOR; CIRCUIT ARRANGEMENTS FOR ELECTRIC LIGHT SOURCES, IN GENERAL
- H05B33/00—Electroluminescent light sources
- H05B33/02—Details
-
- H—ELECTRICITY
- H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
- H10K—ORGANIC ELECTRIC SOLID-STATE DEVICES
- H10K59/00—Integrated devices, or assemblies of multiple devices, comprising at least one organic light-emitting element covered by group H10K50/00
- H10K59/80—Constructional details
- H10K59/87—Passivation; Containers; Encapsulations
- H10K59/871—Self-supporting sealing arrangements
- H10K59/8722—Peripheral sealing arrangements, e.g. adhesives, sealants
Landscapes
- Physics & Mathematics (AREA)
- General Physics & Mathematics (AREA)
- Chemical & Material Sciences (AREA)
- Organic Chemistry (AREA)
- Optics & Photonics (AREA)
- Nonlinear Science (AREA)
- Mathematical Physics (AREA)
- Crystallography & Structural Chemistry (AREA)
- Engineering & Computer Science (AREA)
- Theoretical Computer Science (AREA)
- Liquid Crystal (AREA)
- Polarising Elements (AREA)
- Adhesive Tapes (AREA)
- Adhesives Or Adhesive Processes (AREA)
- Electroluminescent Light Sources (AREA)
Abstract
Description
前記偏光フィルムは、その外縁の長辺Lが60〜400mm及び短辺Wが30〜300mmであり、
前記偏光フィルムは、欠け部及び貫通孔から選択される少なくとも1種の異形部を1つ以上有しており、
前記欠け部は、前記偏光フィルムの外縁に設けられており、
前記欠け部の形は、直線、曲線、又はこれらの組合せにより構成されており、
前記欠け部の形を構成する2つの前記直線のなす角度θ1は90°以上180°未満であり、
前記欠け部が長辺L上にある場合、前記欠け部の形を構成する前記曲線の曲率半径R1は下記式(1)を満足し、
前記欠け部が短辺W上にある場合、前記欠け部の形を構成する前記曲線の曲率半径R1は下記式(2)を満足し、
前記欠け部が前記外縁の隅にある場合、前記欠け部の形を構成する前記曲線の曲率半径R1は0.2mm以上であり、
前記貫通孔は、前記偏光フィルムの平面内部に設けられており、
前記貫通孔の形は、直線、曲線、又はこれらの組合せにより構成されており、
前記貫通孔の形を構成する2つの前記直線のなす角度θ2は90°以上180°未満であり、
前記貫通孔の形を構成する前記曲線の曲率半径R2は0.6mm以上である、ことを特徴とする偏光フィルム、に関する。
R1<(L1−1)/2 (1)
L1:長辺L上における欠け部の長さ(mm)
R1<(W1−1)/2 (2)
W1:短辺W上における欠け部の長さ(mm)
本発明の偏光フィルムは、偏光子の片面又は両面に接着剤層を介して保護フィルムが設けられており、前記偏光フィルムは、その外縁の長辺Lが60〜400mm及び短辺Wが30〜300mmである(なお、長辺L>短辺Wである)。長辺L及び短辺Wの長さは、偏光フィルムの用途に応じて適宜調整する。例えば、長辺Lは100〜200mm、短辺Wは50〜100mmであってもよい。また、前記偏光フィルムは、欠け部及び貫通孔から選択される少なくとも1種の異形部を1つ以上有している。
偏光子は公知のものを特に制限なく使用することができるが、薄型化及びクラックの発生を抑える観点から厚みが10μm以下の偏光子を用いることが好ましい。偏光子の厚みは、より好ましくは8μm以下、更に好ましくは7μm以下、より更に好ましくは6μm以下である。一方、偏光子の厚みは2μm以上、さらには3μm以上であるのが好ましい。
特許第4751486号明細書、
特許第4751481号明細書、
特許第4815544号明細書、
特許第5048120号明細書、
国際公開第2014/077599号パンフレット、
国際公開第2014/077636号パンフレット、
等に記載されている薄型偏光子又はこれらに記載の製造方法から得られる薄型偏光子を挙げることができる。
とにより延伸による破断等の不具合なく延伸することが可能となる。
保護フィルムの材料としては、透明性、機械的強度、熱安定性、水分遮断性、等方性などに優れるものが好ましい。例えば、ポリエチレンテレフタレートやポリエチレンナフタレートなどのポリエステル系ポリマー、ジアセチルセルロースやトリアセチルセルロースなどのセルロース系ポリマー、ポリメチルメタクリレートなどのアクリル系ポリマー、ポリスチレンやアクリロニトリル・スチレン共重合体(AS樹脂)などのスチレン系ポリマー、ポリカーボネート系ポリマー等が挙げられる。また、ポリエチレン、ポリプロピレン、シクロ系ないしはノルボルネン構造を有するポリオレフィン、エチレン・プロピレン共重合体の如きポリオレフィン系ポリマー、塩化ビニル系ポリマー、ナイロンや芳香族ポリアミドなどのアミド系ポリマー、イミド系ポリマー、スルホン系ポリマー、ポリエーテルスルホン系ポリマー、ポリエーテルエーテルケトン系ポリマー、ポリフェニレンスルフィド系ポリマー、ビニルアルコール系ポリマー、塩化ビニリデン系ポリマー、ビニルブチラール系ポリマー、アリレート系ポリマー、ポリオキシメチレン系ポリマー、エポキシ系ポリマー、または上記ポリマーのブレンド物なども上記保護フィルムを形成するポリマーの例として挙げられる。
接着剤層は接着剤により形成される。接着剤の種類は特に制限されず、種々のものを用いることができる。前記接着剤層は光学的に透明であれば特に制限されず、接着剤としては、水系、溶剤系、ホットメルト系、活性エネルギー線硬化型等の各種形態のものが用いられるが、水系接着剤または活性エネルギー線硬化型接着剤が好適である。
異形部は、欠け部又は貫通孔である。
R1<(L1−1)/2 (1)
L1:長辺L上における欠け部の長さ(mm)
R1<(W1−1)/2 (2)
W1:短辺W上における欠け部の長さ(mm)
本発明の粘着剤層付き偏光フィルムは、前記偏光フィルムおよび粘着剤層を有する。
本発明の画像表示装置は、本発明の偏光フィルムまたは粘着剤層付き偏光フィルムを含むものであればよく、その他の構成については、従来の画像表示装置と同様のものを挙げることができる。前記偏光フィルムまたは粘着剤層付偏光フィルムは、画像表示セルに適用される。例えば、画像表示装置が液晶表示装置の場合には、前記偏光フィルムまたは粘着剤層付偏光フィルムは、画像表示セル(液晶セル)の視認側、バックライト側のいずれにも適用することができる。画像表示装置が有機EL表示装置の場合には、前記偏光フィルムまたは粘着剤層付偏光フィルムは、画像表示セルの視認側に適用することができる。本発明の画像表示装置は、前記偏光フィルムまたは粘着剤層付き偏光フィルムを含むため、高い信頼性を有するものである。
吸水率0.75%、Tg75℃の非晶質のイソフタル酸共重合ポリエチレンテレフタレート(IPA共重合PET)フィルム(厚み:100μm)基材の片面に、コロナ処理を施し、このコロナ処理面に、ポリビニルアルコール(重合度:4200、ケン化度:99.2モル%)及びアセトアセチル変性PVA(重合度:1200、アセトアセチル変性度:4.6%、ケン化度:99.0モル%以上、日本合成化学工業(株)製、商品名「ゴーセファイマーZ200」)を9:1の比で含む水溶液を25℃で塗布及び乾燥して、厚み11μmのPVA系樹脂層を形成し、積層体を作製した。
得られた積層体を、120℃のオーブン内で周速の異なるロール間で縦方向(長手方向)に2.0倍に自由端一軸延伸した(空中補助延伸処理)。
次いで、積層体を、液温30℃の不溶化浴(水100重量部に対して、ホウ酸を4重量部配合して得られたホウ酸水溶液)に30秒間浸漬させた(不溶化処理)。
次いで、液温30℃の染色浴に、偏光板が所定の透過率となるようにヨウ素濃度、浸漬時間を調整しながら浸漬させた。本実施例では、水100重量部に対して、ヨウ素を0.2重量部配合し、ヨウ化カリウムを1.0重量部配合して得られたヨウ素水溶液に60秒間浸漬させた(染色処理)。
次いで、液温30℃の架橋浴(水100重量部に対して、ヨウ化カリウムを3重量部配合し、ホウ酸を3重量部配合して得られたホウ酸水溶液)に30秒間浸漬させた(架橋処理)。
その後、積層体を、液温70℃のホウ酸水溶液(水100重量部に対して、ホウ酸を4.5重量部配合し、ヨウ化カリウムを5重量部配合して得られた水溶液)に浸漬させながら、周速の異なるロール間で縦方向(長手方向)に総延伸倍率が5.5倍となるように一軸延伸を行った(水中延伸処理)。
その後、積層体を液温30℃の洗浄浴(水100重量部に対して、ヨウ化カリウムを4重量部配合して得られた水溶液)に浸漬させた(洗浄処理)。
以上により、厚み5μmの偏光子を含む光学フィルム積層体を得た。得られた偏光子のホウ酸含有量は、20重量%であった。
N−ヒドロキシエチルアクリルアミド(HEAA)40重量部とアクリロイルモルホリン(ACMO)60重量部と光開始剤「IRGACURE 819」(BASF社製)3重量部を混合し、紫外線硬化型接着剤を調製した。
攪拌装置、温度センサー、冷却管、窒素導入管を備えた容量30Lの釜型反応器に、8,000gのメタクリル酸メチル(MMA)、2,000gの2−(ヒドロキシメチル)アクリル酸メチル(MHMA)、10,000gの4−メチル−2−ペンタノン(メチルイソブチルケトン、MIBK)、5gのn−ドデシルメルカプタンを仕込み、これに窒素を通じつつ、105℃まで昇温し、還流したところで、重合開始剤として5.0gのt−ブチルパーオキシイソプロピルカーボネート(カヤカルボンBIC−7、化薬アクゾ(株)製)を添加すると同時に、10.0gのt−ブチルパーオキシイソプロピルカーボネートと230gのMIBKからなる溶液を4時間かけて滴下しながら、還流下、約105〜120℃で溶液重合を行い、さらに4時間かけて熟成を行った。
得られた重合体溶液に、30gのリン酸ステアリル/リン酸ジステアリル混合物(Phoslex A−18、堺化学工業(株)製)を加え、還流下、約90〜120℃で5時間、環化縮合反応を行った。次いで、得られた重合体溶液を、バレル温度260℃、回転数100rpm、減圧度13.3〜400hPa(10〜300mmHg)、リアベント数1個、フォアベント数4個のベントタイプスクリュー二軸押出し機(φ=29.75mm、L/D=30)に、樹脂量換算で、2.0kg/hの処理速度で導入し、この押出し機内で、さらに環化縮合反応と脱揮を行い、押し出すことにより、ラクトン環含有重合体の透明なペレットを得た。
得られたラクトン環含有重合体について、ダイナミックTGの測定を行ったところ、0.17質量%の質量減少を検知した。また、このラクトン環含有重合体は、重量平均分子量が133,000、メルトフローレートが6.5g/10min、ガラス転移温度が131℃であった。
得られたペレットと、アクリロニトリル−スチレン(AS)樹脂(トーヨーAS AS20、東洋スチレン(株)製)とを、質量比90/10で、単軸押出機(スクリュー30mmφ)を用いて混練押出することにより、透明なペレットを得た。得られたペレットのガラス転移温度は127℃であった。
このペレットを、50mmφ単軸押出機を用い、400mm幅のコートハンガータイプTダイから溶融押出し、厚さ80μmのフィルムを作製した。なお、紫外線吸収剤(ADEKA社製、商品名:LA-F70)をペレット中の樹脂100重量部に対して0.66重量部供給しながら溶融押出した。作製したフィルムを、2軸延伸装置を用いて、150℃の温度条件下、2.0倍に延伸することにより、厚さ20μmの延伸フィルムを得た。この延伸フィルムの光学特性を測定したところ、全光線透過率が93%、面内位相差Δndが0.8nm、厚み方向位相差Rthが1.5nmであった。
上記光学フィルム積層体の偏光子(厚み:5μm)の表面に、上記紫外線硬化型接着剤を硬化後の接着剤層の厚さが0.1μmになるように塗布しながら、上記方法で作製した保護フィルムを貼合せたのち、活性エネルギー線として紫外線を照射して前記接着剤を硬化させた。その後、偏光子の片面に設けられた非晶性PET基材を剥離して、剥離した面に、輝度向上フィルム(住友スリーエム社製、APF−V3)を、粘着剤で貼合せた。さらに、前記保護フィルム上に粘着剤層(厚み:20μm)を形成して両面保護偏光フィルムを作製した。その後、長辺L130mm及び短辺W65mmの大きさで両面保護偏光フィルムを切り出した。その後、エンドミル加工により、図2に示すような欠け部(曲率半径R1:2.5mm、長さL1:12mm、最大深さD1:7mm)を両面保護偏光フィルムの長辺に1つ形成して、欠け部を有する両面保護偏光フィルムを作製した。
表1に記載の大きさの両面保護偏光フィルムを切り出し、表1に記載の形状の欠け部を形成した以外は、実施例1と同様の方法で欠け部を有する両面保護偏光フィルムを作製した。なお、実施例6の欠け部は図1に示すような形状であり、比較例3の欠け部は三角形である。
実施例1と同様の方法で表2に記載の大きさの両面保護偏光フィルムを作製した。その後、CO2レーザー加工により、図4に示すような円形の貫通孔を表2に記載の曲率半径R2で両面保護偏光フィルムに形成して、円形の貫通孔を有する両面保護偏光フィルムを作製した。
実施例1と同様の方法で表3に記載の大きさの両面保護偏光フィルムを作製した。その後、CO2レーザー加工により、図4に示すような矩形の貫通孔を表3に記載の大きさで両面保護偏光フィルムに形成して、矩形の貫通孔を有する両面保護偏光フィルムを作製した。
実施例1と同様の方法で表3に記載の大きさの両面保護偏光フィルムを作製した。その後、CO2レーザー加工により、角度θ2が60°、一辺が5mmの正三角形の貫通孔を両面保護偏光フィルムに形成して、正三角形の貫通孔を有する両面保護偏光フィルムを作製した。
実施例及び比較例で作製した欠け部又は貫通孔を有する両面保護偏光フィルムを0.5mm厚の無アルカリガラスに貼り合せてサンプルを作製した。当該サンプルに、−40℃(30分保持)⇔85℃(30分保持)のヒートショックを200サイクル又は50サイクル加えた。その後、前記偏光フィルムの欠け部又は貫通孔にクラック又は貫通クラックが発生しているか否かを光学顕微鏡にて確認した。
2:欠け部
3:外縁の隅
4、6:2つの直線が交わる部分
5:貫通孔
L:長辺
L1:長辺L上における欠け部の長さ
L2:長辺L方向における貫通孔の長さ
W:短辺
W1:短辺W上における欠け部の長さ
W2:短辺W方向における貫通孔の幅
D1:長辺Lからの欠け部の最大深さ
D2:短辺Wからの欠け部の最大深さ
θ1、θ2:2つの直線のなす角度
R1、R2:曲線の曲率半径
Claims (10)
- 偏光子の片面又は両面に接着剤層を介して保護フィルムが設けられている偏光フィルムであって、
前記偏光フィルムは、その外縁の長辺Lが60〜400mm及び短辺Wが30〜300mmであり、
前記偏光フィルムは、欠け部及び貫通孔から選択される少なくとも1種の異形部を1つ以上有しており、
前記欠け部は、前記偏光フィルムの外縁に設けられており、
前記欠け部の形は、直線、曲線、又はこれらの組合せにより構成されており、
前記欠け部の形を構成する2つの前記直線のなす角度θ1は90°以上180°未満であり、
前記欠け部が長辺L上にある場合、前記欠け部の形を構成する前記曲線の曲率半径R1は下記式(1)を満足し、
前記欠け部が短辺W上にある場合、前記欠け部の形を構成する前記曲線の曲率半径R1は下記式(2)を満足し、
前記欠け部が前記外縁の隅にある場合、前記欠け部の形を構成する前記曲線の曲率半径R1は0.2mm以上であり、
前記貫通孔は、前記偏光フィルムの平面内部に設けられており、
前記貫通孔の形は、直線、曲線、又はこれらの組合せにより構成されており、
前記貫通孔の形を構成する2つの前記直線のなす角度θ2は90°以上180°未満であり、
前記貫通孔の形を構成する前記曲線の曲率半径R2は0.6mm以上である、ことを特徴とする偏光フィルム。
R1<(L1−1)/2 (1)
L1:長辺L上における欠け部の長さ(mm)
R1<(W1−1)/2 (2)
W1:短辺W上における欠け部の長さ(mm) - 前記欠け部は、前記長辺L、前記短辺W、及び前記外縁の隅の少なくとも1箇所に設けられている請求項1に記載の偏光フィルム。
- 前記欠け部は、前記L1が100〜200mmである請求項1又は2に記載の偏光フィルム。
- 前記欠け部は、前記W1が50〜100mmである請求項1〜3のいずれかに記載の偏光フィルム。
- 前記欠け部は、前記長辺Lからの最大深さD1が2〜50mmである請求項1〜4のいずれかに記載の偏光フィルム。
- 前記欠け部は、前記短辺Wからの最大深さD2が2〜25mmである請求項1〜5のいずれかに記載の偏光フィルム。
- 前記貫通孔は、円形、楕円形、角丸長方形、四角形、又は五角以上の多角形である請求項1〜6のいずれかに記載の偏光フィルム。
- 前記偏光子の厚さは、10μm以下である請求項1〜7のいずれかに記載の偏光フィルム。
- 請求項1〜8のいずれかに記載の偏光フィルムおよび粘着剤層を有する粘着剤層付き偏光フィルム。
- 請求項1〜8のいずれかに記載の偏光フィルムまたは請求項9に記載の粘着剤層付偏光フィルムが、画像表示セルに配置されている画像表示装置。
Priority Applications (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2018117078A JP2019219528A (ja) | 2018-06-20 | 2018-06-20 | 偏光フィルム、粘着剤層付き偏光フィルム、及び画像表示装置 |
PCT/JP2019/024267 WO2019244923A1 (ja) | 2018-06-20 | 2019-06-19 | 偏光フィルム、粘着剤層付き偏光フィルム、及び画像表示装置 |
TW108121262A TWI732231B (zh) | 2018-06-20 | 2019-06-19 | 偏光薄膜、附黏著劑層之偏光薄膜及影像顯示裝置 |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2018117078A JP2019219528A (ja) | 2018-06-20 | 2018-06-20 | 偏光フィルム、粘着剤層付き偏光フィルム、及び画像表示装置 |
Publications (1)
Publication Number | Publication Date |
---|---|
JP2019219528A true JP2019219528A (ja) | 2019-12-26 |
Family
ID=68984064
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
JP2018117078A Pending JP2019219528A (ja) | 2018-06-20 | 2018-06-20 | 偏光フィルム、粘着剤層付き偏光フィルム、及び画像表示装置 |
Country Status (3)
Country | Link |
---|---|
JP (1) | JP2019219528A (ja) |
TW (1) | TWI732231B (ja) |
WO (1) | WO2019244923A1 (ja) |
Cited By (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN112289183A (zh) * | 2020-10-26 | 2021-01-29 | 武汉华星光电半导体显示技术有限公司 | 一种偏光片及显示面板 |
WO2021106341A1 (ja) * | 2019-11-29 | 2021-06-03 | 住友化学株式会社 | 偏光板 |
WO2022202371A1 (ja) * | 2021-03-24 | 2022-09-29 | 住友化学株式会社 | 偏光板および画像表示装置 |
JP7509823B2 (ja) | 2020-09-14 | 2024-07-02 | 日東電工株式会社 | 偏光板、偏光板の製造方法、位相差層付偏光板、ならびに、該偏光板または該位相差層付偏光板を含む画像表示装置 |
Families Citing this family (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPWO2022024796A1 (ja) * | 2020-07-29 | 2022-02-03 | ||
JPWO2022024798A1 (ja) * | 2020-07-29 | 2022-02-03 | ||
CN116134502A (zh) * | 2020-07-29 | 2023-05-16 | 日东电工株式会社 | 偏光板及包含该偏光板的图像显示装置 |
CN112093273A (zh) * | 2020-09-30 | 2020-12-18 | 京东方科技集团股份有限公司 | 一种保护膜及保护膜组件 |
CN114170904A (zh) * | 2021-12-06 | 2022-03-11 | 合肥维信诺科技有限公司 | 显示模组及显示装置 |
Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2017047510A1 (ja) * | 2015-09-16 | 2017-03-23 | シャープ株式会社 | 異形状偏光板の製造方法 |
US20180003860A1 (en) * | 2016-06-30 | 2018-01-04 | Lg Display Co., Ltd. | Polarizer, Display Device Having the Polarizer, and Method of Fabricating the Polarizer |
JP2018025630A (ja) * | 2016-08-09 | 2018-02-15 | 日東電工株式会社 | 偏光板 |
JP2018092119A (ja) * | 2016-05-30 | 2018-06-14 | 住友化学株式会社 | 偏光板、画像表示装置及び偏光板の製造方法 |
-
2018
- 2018-06-20 JP JP2018117078A patent/JP2019219528A/ja active Pending
-
2019
- 2019-06-19 WO PCT/JP2019/024267 patent/WO2019244923A1/ja active Application Filing
- 2019-06-19 TW TW108121262A patent/TWI732231B/zh active
Patent Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2017047510A1 (ja) * | 2015-09-16 | 2017-03-23 | シャープ株式会社 | 異形状偏光板の製造方法 |
JP2018092119A (ja) * | 2016-05-30 | 2018-06-14 | 住友化学株式会社 | 偏光板、画像表示装置及び偏光板の製造方法 |
US20180003860A1 (en) * | 2016-06-30 | 2018-01-04 | Lg Display Co., Ltd. | Polarizer, Display Device Having the Polarizer, and Method of Fabricating the Polarizer |
JP2018025630A (ja) * | 2016-08-09 | 2018-02-15 | 日東電工株式会社 | 偏光板 |
Cited By (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2021106341A1 (ja) * | 2019-11-29 | 2021-06-03 | 住友化学株式会社 | 偏光板 |
JP7509823B2 (ja) | 2020-09-14 | 2024-07-02 | 日東電工株式会社 | 偏光板、偏光板の製造方法、位相差層付偏光板、ならびに、該偏光板または該位相差層付偏光板を含む画像表示装置 |
CN112289183A (zh) * | 2020-10-26 | 2021-01-29 | 武汉华星光电半导体显示技术有限公司 | 一种偏光片及显示面板 |
WO2022202371A1 (ja) * | 2021-03-24 | 2022-09-29 | 住友化学株式会社 | 偏光板および画像表示装置 |
Also Published As
Publication number | Publication date |
---|---|
WO2019244923A1 (ja) | 2019-12-26 |
TW202000819A (zh) | 2020-01-01 |
TWI732231B (zh) | 2021-07-01 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
WO2019244923A1 (ja) | 偏光フィルム、粘着剤層付き偏光フィルム、及び画像表示装置 | |
WO2019244916A1 (ja) | 偏光フィルム、粘着剤層付偏光フィルム、及び画像表示装置 | |
KR102199874B1 (ko) | 광학 필름, 박리 방법 및 광학 표시 패널의 제조 방법 | |
KR102338615B1 (ko) | 광학 필름, 박리 방법 및 광학 표시 패널의 제조 방법 | |
WO2017145607A1 (ja) | 偏光子、片保護偏光フィルム、粘着剤層付偏光フィルム並びに画像表示装置およびその連続製造方法 | |
JP2020190754A (ja) | 光学フィルム、剥離方法及び光学表示パネルの製造方法 | |
JP2023061955A (ja) | 光学フィルム及び光学表示パネル | |
JP2023025240A (ja) | 偏光フィルムロールの製造方法 | |
JP6767143B2 (ja) | 離型フィルムの剥離方法及び光学表示パネルの製造方法 | |
WO2019244915A1 (ja) | 偏光フィルム、粘着剤層付き偏光フィルム、及び画像表示装置 | |
JP6636367B2 (ja) | 透明樹脂層付の片保護偏光フィルムの製造方法、粘着剤層付偏光フィルムの製造方法、及び画像表示装置の製造方法 | |
CN107924016B (zh) | 单侧保护偏振膜、带粘合剂层的偏振膜及图像显示装置 | |
JP6771913B2 (ja) | 表面保護フィルム付偏光フィルム、及び偏光フィルムの製造方法 | |
JP2021002041A (ja) | 表面保護フィルム付偏光フィルム、及び偏光フィルムの製造方法 | |
JP2011227418A (ja) | 偏光板、その製造方法及びそれを用いたipsモード液晶表示装置 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
A621 | Written request for application examination |
Free format text: JAPANESE INTERMEDIATE CODE: A621 Effective date: 20190618 |
|
A131 | Notification of reasons for refusal |
Free format text: JAPANESE INTERMEDIATE CODE: A131 Effective date: 20190903 |
|
A521 | Request for written amendment filed |
Free format text: JAPANESE INTERMEDIATE CODE: A523 Effective date: 20191101 |
|
A02 | Decision of refusal |
Free format text: JAPANESE INTERMEDIATE CODE: A02 Effective date: 20200421 |
|
A521 | Request for written amendment filed |
Free format text: JAPANESE INTERMEDIATE CODE: A523 Effective date: 20200720 |
|
C60 | Trial request (containing other claim documents, opposition documents) |
Free format text: JAPANESE INTERMEDIATE CODE: C60 Effective date: 20200720 |
|
A911 | Transfer to examiner for re-examination before appeal (zenchi) |
Free format text: JAPANESE INTERMEDIATE CODE: A911 Effective date: 20200730 |
|
C21 | Notice of transfer of a case for reconsideration by examiners before appeal proceedings |
Free format text: JAPANESE INTERMEDIATE CODE: C21 Effective date: 20200731 |
|
A912 | Re-examination (zenchi) completed and case transferred to appeal board |
Free format text: JAPANESE INTERMEDIATE CODE: A912 Effective date: 20200821 |
|
C211 | Notice of termination of reconsideration by examiners before appeal proceedings |
Free format text: JAPANESE INTERMEDIATE CODE: C211 Effective date: 20200825 |
|
C22 | Notice of designation (change) of administrative judge |
Free format text: JAPANESE INTERMEDIATE CODE: C22 Effective date: 20201110 |
|
C23 | Notice of termination of proceedings |
Free format text: JAPANESE INTERMEDIATE CODE: C23 Effective date: 20210311 |
|
C03 | Trial/appeal decision taken |
Free format text: JAPANESE INTERMEDIATE CODE: C03 Effective date: 20210413 |
|
C30A | Notification sent |
Free format text: JAPANESE INTERMEDIATE CODE: C3012 Effective date: 20210413 |